Electrical properties of SrBi2(Nb0.5Ta0.5)2O9 ceramics

Aurivillius SrBi₂(Nb_0.5Ta_0.5)₂O₉ (SBNT 50/50) ceramics were prepared using the conventional solid-state reaction method. Scanning electron microscopy was applied to investigate the grain structure. The XRD studies revealed an orthorhombic structure in the SBNT 50/50 with lattice parameters a=5.522 Å, b=5.511 Å and c=25.114 Å. The dielectric properties were determined by impedance spectroscopy measurements. A strong low frequency dielectric dispersion was found to exist in this material. Its occurrence was ascribed to the presence of ionized space charge carriers such as oxygen vacancies. The dielectric relaxation was defined on the basis of an equivalent circuit. The temperature dependence of various electrical properties was determined and discussed. The thermal activation energy for the grain electric conductivity was lower in the high temperature region (T>303.6 °C, E_a−ht=0.47 eV) and higher in the low temperature region (T<303.6 °C, E_a−lt=1.18 eV).     

Influence of Ce doping on electrical and thermal properties of La0.7−xCexCa0.3MnO3 (0.0≤x≤0.7) manganites

The effect of Ce-doping on structural, magnetic, electrical and thermal transport properties in hole-doped manganites La_0.7−xCe_xCa_0.3MnO₃ (0.0≤x≤0.7) is investigated. The structure of the compounds was found to be crystallized into orthorhombically distorted perovskite structure. dc Susceptibility versus temperature curves reveal various magnetic transitions. For x≤0.3, ferromagnetic regions (FM) were identified and the magnetic transition temperature (T_C) was found to be decreasing systematically with increasing Ce concentration. The electrical resistivity ρ(T) separates the well-define metal-semiconducting transition (T_MS) for low Ce doping concentrations (0.0≤x≤0.3) consistent with magnetic transitions. For the samples with 0.4≤x≤0.7, ρ(T) curves display a semiconducting behavior in both the high temperature paramagnetic (PM) phase and low temperature FM or antiferromagnetic phase. The electron–phonon and electron–electron scattering processes govern the low temperature metallic behavior, whereas small polaron hopping model is found to be operative in PM phases for all samples. These results were broadly corroborated by thermal transport measurements for metallic samples (x≤0.3) in entire temperature range we investigated. The complicated temperature dependence of Seebeck coefficient (S) is an indication of electron–magnon scattering in the low temperature magnetically ordered regime. Specific heat measurements depict a broadened hump in the vicinity of T_C, indicating the existence of magnetic ordering and magnetic inhomogeneity in the samples. The observation of a significant difference between ρ(T) and S(T) activation energies and a positive slope in thermal conductivity κ(T) implying that the conduction of charge carriers were dominated by small polaron in PM state of these manganites.     

Effects of Cr doping in bilayered manganite LaSr2Mn2O7: Resistivity, thermoelectric power, and thermal conductivity

Systematic studies of resistivity, thermoelectric power, and thermal conductivity have been performed on polycrystalline bilayered manganites LaSr₂Mn_2−xCr_xO₇ (0≤x≤0.2). It is found that the temperature dependence of both Seebeck coefficient S(T) and resistivity ρ(T) in the high temperature region follows the small polaron transport mechanism for all the samples. But in the low temperature region, variable-range-hopping (VRH) model matches the experimental data better. In addition, the maximum of absolute S(T) at low temperatures is gradually suppressed for the sample with Cr-doping level of x>0.04, implying that a new FM order probably arises. With decreasing the temperatures further, S(T) has a sign change and becomes positive for the sample with Cr-doping level of x>0.04, indicating that there may occur a variation of the type of charge carrier. As to thermal conduction κ(T), the low-temperature peak is suppressed due to Cr-doping. The variation of κ(T) is analyzed based on the combined effect due to the suppression of local Mn³⁺O₆ Jahn-Teller (JT) lattice distortion because of the substitution of Cr³⁺ ions for Mn³⁺ ions, which results in the increase in thermal conduction, and the introduction of the disorder due to Cr-doping, which contributes to the decrease in thermal conduction.     

Thermal conductivity of La0.67(CaxSr1−x)0.33MnO3 (x=0, 0.5, 1) and La0.6Y0.07Ca0.33MnO3 pellets between 10 and 300 K

Thermal conductivity (λ) of nanocrystalline La_0.67(Ca_xSr_1−x)_0.33MnO₃ (x=0, 0.5, 1) and La_0.6Y_0.07Ca_0.33MnO₃ pellets prepared by a novel ‘pyrophoric’ method have been studied between the temperature range 10 and 300 K. Our data show that the magnitude of thermal conductivity is strongly influenced by the ion substitutions at La-site. The analysis of the thermal conductivity data indicates that the thermal transport is governed largely by phonons scattering in these systems and the electronic contribution is as small as 0.2-1% of total thermal conductivity (λ_total). At low temperatures (<90 K) 2D like lattice defects contribute to the phonon scattering dominantly and its strength increases with increasing Sr content and also with partial substitution of La by Y. Depending upon the composition of the samples, the magnon thermal conductivity contributes 2-15% of λ_total close to T_C. In the paramagnetic regime the unusual increase in λ_total keeps signature of large dynamic lattice distortion.     

High pressure behaviour of KHSO4 studied by electrical impedance spectroscopy

Measurements of the electrical conductivity were performed in KHSO₄ at pressures between 0.5 and 2.5 GPa and in the temperature range 120-350 °C by the use of the impedance spectroscopy. The temperatures of the α-β phase transition (T_Tr) and of the melting (T_m), determined from the Arrhenius plots ln(σT) vs. 1/T, increase with pressure up to 1.5 GPa having dT/dP∼+45 K/GPa. Above the pressure 1.5 GPa, the pressure dependencies of T_Tr and T_m are negative dT/dP∼−45 K/GPa. At pressures above 0.5 GPa, the reversible decomposition of KHSO₄ into K₃H(SO₄)₂+H₂SO₄ (and probably into K₅H₃(SO₄)₄+H₂SO₄) affects the electrical conductivity of KHSO₄, with the typical values of the protonic electrical conductivity, c. 10⁻¹ S/cm at 2.5 GPa.     

Mössbauer spectroscopic study of the thermal spin crossover in [Fe(II)(isoxazole)6](ClO4)2

The ⁵⁷Fe Mössbauer spectroscopy of mononuclear [Fe(II)(isoxazole)₆](ClO₄)₂ has been studied to reveal the thermal spin crossover of Fe(II) between low-spin (S=0) and high-spin (S=2) states. Temperature-dependent spin transition curves have been constructed with the least-square fitted data obtained from the Mössbauer spectra measured at various temperatures between 84 and 270 K during a cooling and heating cycle. This compound exhibits an unusual temperature-dependent spin transition behaviour with T_C(↓)=223 and T_C(↑)=213 K occurring in the reverse order in comparison to those observed in SQUID observation and many other spin transition compounds. The compound has three high-spin Fe(II) sites at the highest temperature of study of which two undergo spin transitions. The compound seems to undergo a structural phase transition around the spin transition temperature, which plays a significant role in the spin crossover behaviour as well as the magnetic properties of the compound at temperatures below T_C. The present study reveals an increase in high-spin fraction upon heating in the temperature range below T_C, and an explanation is provided.     

H nuclear magnetic resonance study of the ferroelastic and superionic phase transitions of (NH4)4LiH3(SO4)4 single crystals

We investigated the temperature dependences of the line shape, spin-lattice relaxation time, T₁, and spin-spin relaxation time, T₂, of the ¹H nuclei in (NH₄)₄LiH₃(SO₄)₄ single crystals. On the basis of the data obtained, we were able to distinguish the “ammonium” and “hydrogen-bond” protons in the crystals. For both the ammonium and hydrogen-bond protons in (NH₄)₄LiH₃(SO₄)₄, the curves of T₁ and T₂ versus temperature changed significantly near the ferroelastic and superionic phase transitions at T_C (=232 K) and T_S (=405 K), respectively. In particular, near T_S, the ¹H signal due to the hydrogen-bond protons abruptly narrowed and the T₂ value for these protons abruptly increased, indicating that these protons play an important role in this superionic phase transition. The marked increase in the T₂ of the hydrogen-bond protons above T_S indicates that the breaking of O-H?O bonds and the formation of new H-bonds with HSO₄^- contribute significantly to the high-temperature conductivity of (NH₄)₄LiH₃(SO₄)₄ crystals.     

Synthesis and physical characterization of superconductivity-magnetism crossover compound RuSr2EuCeCu2O10−δ

We carefully studied the nonsuperconducting sample of the magneto-superconducting RuSr₂(Eu_1−xCe_x)Cu₂O_10−δ series with composition RuSr₂EuCeCu₂O_10−δ. This compound seems to exhibit a complex magnetic state as revealed by host of techniques like resistivity, thermopower, magnetic susceptibility, and MR measurements. The studied compound exhibited ferromagnetic like M(H) loops at 5, 20, and 50 K, and semiconductor like electrical conduction down to 5 K, with −MR^7 T of up to 4% at low temperatures. The −MR^7 T decreases fast above 150 K and monotonically becomes close to zero above say 230 K. Below, 150 K −MR^7 T decreases to around 3% monotonically down to 75 K, with further increase to 4% at around 30 K and lastly having a slight decrease below this temperature. The thermopower S(T) behavior closely followed the −MR^7 T steps in terms of d(S/T)/dT slopes. Further, both MR^7 T steps and d(S/T)/dT slopes are found in close vicinity to various magnetic ordering temperatures (T_mag) of this compound.     

Magnetic properties of RPd5Al2 (R=Y, Ce, Pr, Nd, Sm, Gd)

Polycrystalline samples of a new rare-earth series RPd₅Al₂ crystallizing in the tetragonal ZrNi₂Al₅-type structure have been prepared. Their physical properties by electrical resistivity ρ, magnetic susceptibility χ, magnetization M and specific heat C_p measurements are reported. The ingots are composed of elongated grains preferentially aligned in the c direction; therefore, measurements were conducted parallel and perpendicular to the grains. Antiferromagnetic ordering appears in R=Ce, Nd, Gd, and Sm at low temperatures. CePd₅Al₂ has two AFM transitions at 4.1 and 2.9 K and ρ(T) indicates a Kondo metal behavior with large anisotropy. In PrPd₅Al₂ no magnetic transition was observed down to 0.4 K. The C_p(T) shows a broad peak around 13 K due to the CEF effect, suggesting a non-magnetic singlet ground state. In NdPd₅Al₂, χ(T) shows anisotropy and the C_p(T) shows a sharp peak at 1.2 K. The magnetic entropy at 3 K is very close to Rln2, indicating a Kramers doublet ground state. In SmPd₅Al₂, C_p(T) shows a magnetic transition at 1.7 K. C_p(T) for GdPd₅Al₂ shows a peak at 6 K, followed by a broad anomaly around 3 K. Within this series, T_N's for CePd₅Al₂ and NdPd₅Al₂ clearly deviate from the relation predicted by de Gennes scaling, which is ascribed to the CEF effect.     

Superconducting properties in Rh17S15 under magnetic field and pressure

We have studied superconducting properties by measuring the electrical resistivity and magnetization for a single crystal of Rh₁₇S₁₅ with a superconducting transition temperature T_c=5.4 K. The upper critical field H_c2(0) and the lower critical field H_c1(0) were obtained as 20.5 and 0.0033 T, respectively. Correspondingly, the coherence length and the penetration depth were estimated to be 40 and 4900 Å, respectively, indicating that Rh₁₇S₁₅ is a typical type-II superconductor with strong correlations of conduction electrons with a 4d-electron character of Rh atoms. The present electron correlations are formed to be enhanced with increasing pressure.     

Effects of Cr doping in electron-doped manganites La0.9Te0.1MnO3

The effects of Cr doping on Mn sites in the electron-doped manganites La_0.9Te_0.1MnO₃ have been studied by preparing the series La_0.9Te_0.1Mn_1−xCr_xO₃ (0.05≤x≤0.20). Upon Cr doping, both the Curie temperature T_C and magnetization M are suppressed. The resistivity measurements indicate that there exists a weak metal-insulator (M-I) transition for the sample with x=0.05, with an increase in the doping level, the M-I transition disappears and the resistivity increases. Thermopower S(T) exhibits a maximum near T_C for all samples. By fitting the S(T) and ρ(T) curves, it is found that the temperature dependences of both S(T) and ρ(T) in the high temperature paramagnetic (PM) region follow the small polaron conduction (SPC) mechanism for all samples. The fitting parameters obtained imply changes of both the average-hopping distance of the polarons and the polaron concentration with Cr doping in our studied samples. In the case of the thermal conductivity κ(T), the variation of κ(T) is analyzed based on the combined effects due to the suppression of the local Mn³⁺O₆ Jahn-Teller (JT) lattice distortion because of the substitution of Cr³⁺ for Mn³⁺ ions, which results in the increase in κ, and the introduction of the disorder due to Cr-doping, which contributes to the decrease in κ.     

Thermal and magnetic properties of DyB62 at low temperatures

Temperature dependences of heat capacity C_P(T) and magnetization M(T) of an icosahedral dysprosium boride (DyB₆₂) single crystal have been experimentally investigated in the temperature range of 2-300 K. The magnetic susceptibility χ(T) of DyB₆₂ follows Curie-Weiss law with a paramagnetic Curie temperature of −3.7 K, which implies that the antiferromagnetic interactions are dominant in this material and suggests the possibility of magnetic ordering at low temperatures. This conjecture is supported by the temperature dependence of heat capacity C_P(T), which decreases upon heating from 2 to 7 K. The heat capacity of DyB₆₂ at 2 K is analyzed as a sum of magnetic, Debye, two-level system and soft atomic potential components.     

The effects of elements doping on transport and thermoelectric properties of Sr3Ti2O7

The Ruddlesden–Popper (RP) phase compounds (Sr_0.95R_0.05)₃Ti₂O₇ (R=Er, Y, Dy, Gd, Eu, Sm, Nd and La) were prepared, and their transport and thermoelectric properties were investigated. The results indicate that high-T electrical resistivity ρ (300 K<T<1000 K) increases monotonically with temperature and basically has a relation ρ∝T^M, with M varying from 0.91 to 1.92 at temperatures T>~650 K, suggesting acoustic phonon scattering is dominant. At low temperatures (5 K<T<300 K), ρ for (Sr_0.95R_0.05)₃Ti₂O₇ (R=Nd and La) decreases monotonously with decreasing temperature, whereas ρ for (Sr_0.95R_0.05)₃Ti₂O₇ (R=Er, Y, Dy, Gd, Eu and Sm) decreases first, and then increases instead as T decreases to a critical temperature T_c. Moreover, electrical conductivity σ∝T^1/2 holds at lower temperatures, indicating that the electron–electron interaction caused by the presence of disorder dominates the transport process at the low temperatures. Besides, experiments show that at T<~400 K the lattice thermal conductivity of the doped compounds basically decreases with increase of the atomic mass of dopants. Generally, the figure of merit (ZT) at 1000 K increases first, and then decreases with the increase of the dopants' ionic radius, and the largest ZT is achieved in (Sr_0.95Gd_0.05)₃Ti₂O₇ mainly owing to its lower lattice thermal conductivity.     

Superconductivity in porous MgB2

Porous magnesium diboride samples have been prepared by the heat treatment of a pressed mixture of Mg and MgB₂ powders. It was found that linked superconducting structure is formed down to the minimum normalized density γ_c=d/d₀≅0.16 (percolation threshold), where d is the density of MgB₂ averaged over the sample, d₀=2.62 g/cm³ is the X-ray density. Lattice parameters and critical temperature of the porous sample decrease with increasing porosity (decreasing γ) and T_c2≅32 K is minimal at γ_c. The grain boundaries in the porous samples are transparent for the current and J_c∼3×10⁵ A/cm² in self field at T=20 K in the samples with γ∼0.24.     

Room temperature magnetic entropy change and magnetoresistance in La0.70(Ca0.30−xSrx)MnO3:Ag 10% (x=0.0−0.10)

The magnetic and magnetocaloric properties of polycrystalline La_0.70(Ca_0.30−xSr_x)MnO₃:Ag 10% manganite have been investigated. All compositions are crystallized in single phase orthorhombic Pbnm space group. Both, the insulator–metal transition temperature (T^IM) and Curie temperature (T_c) are observed at 298 K for x=0.10 composition. Though both T^IM and T_c are nearly unchanged with Ag addition, the MR is increased. The MR at 300 K is found to be as large as 31% with magnetic field change of 1 T, whereas it reaches up to 49% at magnetic field of 3 T for the La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample. The maximum entropy change (ΔS_Mmax) at near its T_c (300.5 K) is 7.6 J kg⁻¹ K⁻¹ upon the magnetic field change of 5 T. The La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample having good MR (31%^1 T, 49%^3 T) and reasonable change in magnetic entropy (7.6 J kg⁻¹.K⁻¹, 5 T) at 300 K can be a potential magnetic refrigerant material at ambient temperatures.     

Heat generation ability in AC magnetic field of nano MgFe2O4-based ferrite powder prepared by bead milling

Nanosized MgFe₂O₄-based ferrite powder having heat generation ability in an AC magnetic field was prepared by bead milling and studied for thermal coagulation therapy applications. The crystal size and the particle size significantly decreased by bead milling. The heat generation ability in an AC magnetic field improved with the milling time, i.e. a decrease in crystal size. However, the heat generation ability decreased for excessively milled samples with crystal sizes of less than 5.5 nm. The highest heat ability (ΔT=34 °C) in the AC magnetic field (370 kHz, 1.77 kA/m) was obtained for fine MgFe₂O₄ powder having a ca. 6 nm crystal size (the samples were milled for 6-8 h using 0.1 mm ? beads). The heat generation of the samples was closely related to hysteresis loss, a B-H magnetic property. The reason for the high heat generation properties of the samples milled for 6-8 h using 0.1 mm ? beads was ascribed to the increase in hysteresis loss by the formation of a single domain. Moreover, the improvement in heating ability was obtained by calcination of the bead-milled sample at low temperature. In this case, the maximum heat generation (ΔT=41 °C) ability was obtained for a ca. 11 nm crystal size sample was prepared by crystal growth during the sample calcination. On the other hand, the ΔT value for Mg_0.5Ca_0.5Fe₂O₄ was synthesized using a reverse precipitation method decreased by bead milling.     

Analysis of low temperature specific heat in Nd0.5Sr0.5MnO3 and R0.5Ca0.5MnO3 (R=Nd,Sm, Dy and Ho) compounds

We report on the specific heat C(T) of doped manganites Nd_0.5Sr_0.5MnO₃, Nd_0.5Ca_0.5MnO₃, Sm_0.5Ca_0.5MnO₃, Dy_0.5Ca_0.5MnO₃ and Ho_0.5Ca_0.5MnO₃ in the temperature range 2?T?300 K using modified rigid ion model (MRIM). The present specific heat results are in general satisfactory agreement with experimental data except at very low temperatures (i.e. T?12 K). Also a sharp peak observed in the experimental results for these compounds around 5 K could not be revealed by our computed results as they arise due to Schottky-like anomaly. Besides, we have reported the cohesive and the thermal properties of these compounds. The results obtained by us are discussed in detail.     

Effect of Pb on the electrical properties of a-Ge20Se80 glasses

The present paper reports the effect of Pb impurity (low ∼2 at% and high ∼10 at%) on the ac conductivity (σ_ac) of a-Ge₂₀Se₈₀ glass. Frequency-dependent ac conductance and capacitance of the samples over a frequency range ∼100 Hz to 50 kHz have been taken in the temperature range ∼268 to 358 K. At frequency 2 kHz and temperature 298 K, the value of σ_ac increases at low as well as at higher concentration of Pb. σ_ac is proportional to ω^s for undoped and doped samples. The value of frequency exponent (s) decreases as the temperature increases. The static permittivity (ε_s) increases at both Pb concentrations. These results have been explained on the basis of some structural changes at low and higher concentration of Pb impurity.     

Structural,electrical transport,and magnetic properties of Ni1−xZnxFe2O4

Structural, electrical, and magnetic properties of Ni_1−xZn_xFe₂O₄ (x=0.2, 0.4) samples sintered at various temperatures have been investigated thoroughly. The bulk density of the Ni_0.8Zn_0.2Fe₂O₄ samples increases as the sintering temperature (T_s) increases from 1200 to 1300 °C and above 1300 °C the bulk density decreases slightly. The Ni_0.6Zn_0.4Fe₂O₄ samples show similar behavior of changes to that of Ni_0.8Zn_0.2Fe₂O₄ samples, except that the bulk density is found to be the highest at 1350 °C. The DC electrical resistivity, ρ(T)$\rho (T)$, decreases as the temperature increases indicating that the samples have semiconductor-like behavior. As the Zn content increases, the Curie temperature (T_c), resistivity, and the activation energy decrease while the magnetization, initial permeability, and the relative quality factor (Q) increases. A Hopkinson peak is obtained near T_c in the real part of the initial permeability vs. temperature curves. The ferrite with higher permeability has a relatively lower resonance frequency. The initial permeability and magnetization of the samples has been found to correlate with density, average grain sizes. Possible explanation for the observed structural, magnetic, and changes of resistivity behavior with various Zn content are discussed.     

Exotic superconducting state embedded in the hidden order state of URu2Si2

The heavy-fermion compound URu₂Si₂ has mystified researchers since the superconducting state (T_c = 1.45 K) is embedded within the enigmatic ‘‘hidden order” phase (T_h = 17.5 K). Here, we report charge and thermal transport measurements on ultraclean single crystals of URu₂Si₂ with very large residual-resistivity-ratio down to 30 m K (∼T_c/50), which reveal a number of unprecedented superconducting properties. The results provide strong evidence for a new type of unconventional superconductivity with two distinct gaps having different nodal topology. We propose a gap function with chiral d-wave form Δ(k) = Δ₀k_z(k_x + ik_y). We also demonstrate that a distinct flux line lattice melting transition with outstanding characters occurs well below the upper critical fields even at sub-Kelvin temperature. The intriguing superconducting state of URu₂Si₂ adds a unique and exciting example to the list of unconventional superconductors.