Vacuum annealing phenomena in ultrathin TiD y /Pd bi-layer films evaporated on Si(100) as studied by TEM and XPS

Using a combination of TEM and XPS, we made an analysis of the complex high-temperature annealing effect on ultrathin titanium deuteride (TiD _y ) films evaporated on a Si(100) substrate and covered by an ultrathin palladium layer. Both the preparation and annealing of the TiD _y /Pd bi-layer films were performed in situ under UHV conditions. It was found that the surface and bulk morphology of the bi-layer film as well as that of the Si substrate material undergo a microstructural and chemical conversion after annealing and annealing-induced deuterium evolution from the TiD _y phase. Energy-filtered TEM (EFTEM) mapping of cross-section images and argon ion sputter depth profiling XPS analysis revealed both a broad intermixing between the Ti and Pd layers and an extensive inter-diffusion of Si from the substrate into the film bulk area. Segregation of Ti at the Pd top layer surface was found to occur by means of angle-resolved XPS (ARXPS) and the EFTEM analyses. Selected area diffraction (SAD) and XPS provided evidence for the formation of a new PdTi₂ bimetallic phase within the top region of the annealed film. Moreover, these techniques allowed to detect the initial stages of TiSi phase formation within the film–substrate interlayer.     

Microstructural and chemical transformation of thin Ti/Pd and TiD<Subscript><Emphasis Type="BoldItalic">y</Emphasis></Subscript>/Pd bilayer films induced by vacuum annealing

Using a combination of scanning electron microscopy, transmission electron microscopy (TEM), X-ray diffraction and X-ray photoelectron spectroscopy (XPS), we made a comparative study of the high-temperature annealing impact on thin titanium deuteride (TiD _y ) films covered by an ultrathin Pd layer, and on Ti/Pd bilayer films. The bilayer films were prepared under ultrahigh vacuum conditions and were in situ annealed using the same annealing procedure. It was found that the surface and the bulk morphology of both films undergo different annealing-induced transformations, leading to an extensive intermixing between the Ti and Pd layers and the formation of a new PdTi₂ bimetallic phase. Energy-filtered TEM imaging and energy-dispersive X-ray spectrometry analysis, as well as XPS depth profiling all provided evidence of a different distribution of Pd and Ti in the annealed TiD _y /Pd film compared with the annealed Ti/Pd film. Our results show that thermal decomposition of TiD _y , as a consequence of annealing the TiD _y /Pd film, modifies the intermixing process, thereby promoting Ti diffusion into the Pd-rich top layer of the TiD _y film and thus providing a more likely path for the formation of the PdTi₂ phase than in an annealed Ti/Pd film. Figure Figure Microstructural and chemical characterisation of thin TiDy/Pd film after annealing     

Application of TEM and XPS in the interpretation of the kinetics of deuterium evolution from ultrathin TiD<Subscript><Emphasis Type="BoldItalic">y</Emphasis></Subscript>/Pd films evaporated on quartz

The kinetics of thermal evolution of deuterium from ultrathin TiD _y /Pd bilayer films has been studied by means of thermal desorption mass spectrometry (TDMS). Using a combination of transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy, we made a study of the complex structural and chemical transformations of the TiD _y /Pd film as a result of TDMS-induced evolution of deuterium and simultaneous annealing of this film. Both preparation and TDMS processing of the TiD _y /Pd bilayer films were performed in situ under UHV conditions. It was found that the high-temperature TDMS processing of an ultrathin TiD _y /Pd film, which was carried out in a relatively short time, leads to a significant film structure transformation. Energy-filtered TEM mapping of cross-section images and EDX analysis revealed extensive interdiffusion of Ti and Pd within the Ti–Pd bi-layer film. This process leads to a progressive change in chemical composition within the surface and subsurface area of the film during the TDMS processing. As the temperature of TDMS heating increases, segregation of Ti at the Pd top layer surface becomes significant. As a result, the kinetics of deuterium desorption is progressively changed during TDMS; at lower temperatures, the kinetics is limited by recombinative processes at the Pd surface, at temperatures beyond 500 K, it becomes dominated by interdiffusion of Ti into the Pd surface.     

Palladium-doped polyimides: An X-ray photoelectron study

Five polyimide films prepared from 3,3′,4,4′-benzophenone tetracarboxylic acid'dianhydride (BTDA) and diamines, 4,4′-oxydianiline (ODA), 3,3′-diaminobenzophenone (DABP), or 3,3′-diaminodiphenylcarbinol (DADPC) and doped with Li₂PdCl₄ (LTP) or Pd[(CH₃)₂S]₂Cl₂ (PDS) were selected for a detailed x-ray photoelectron spectroscopic (XPS) study to determine the oxidation state of palladium and the relative distribution of this and other elements in these films, especially as they relate to electrical resistivity. XPS shows that Pd in the films is present as a mixture of zero and +2 valence states. Films that contain lithium as part of the dopant all show that metal is present as Li⁺ and Li₂O, a fact that may have a bearing on film electrical properties. An Auger electron spectroscopic (AES) or XPS profiling was performed on two of the electrically conductive films. A film doped with PDS reveals a majority of palladium at the surface as Pd(0) and much smaller amounts in film bulk as a mixture of Pd(0) and Pd(II). Film behavior is similar to a metal-vapor deposited film. An LTP doped film, by contrast, exhibits a homogeneous composition with a mixture of Pd(0) and Pd(II). These studies support others that use chemical etching on the film surfaces. Scanning electron microscopy (SEM) has been used to provide surface evaluations.     

SEM and AES depth profile studies of thin titanium and titanium oxide films covered by nanoscale evaporated Au layers

Thin titanium and titanium oxide films, both covered by ultra-thin gold layers, have been compared with titanium films after analysis, using a combination of SEM and AES. The Ti films were prepared under UHV conditions by evaporation on a glass substrate. The Ti oxide layers were prepared in situ by precisely controlled oxygen sorption at 298 K on Ti film. Both Ti and Ti oxide films were then covered in situ by a very thin Au layer. Analysis was performed in a separate system after long-term exposure of the films to air. SEM analysis revealed a much smaller size grain on the Au coated Ti films than on Ti films not coated with a Au layer. The thin gold layers covering the Ti surface prevent an extensive air interaction with Ti film. The analysis of the features of the Ti Auger spectra during the sputter profile measurements allow to characterise the chemical nature of Ti-oxide formed in Ti/Au interface region. Received: 7 September 1998 / Revised: 14 January 1999 / Accepted: 2 February 1999     

ZIF-8原位负载Pd纳米粒子及其在Suzuki-Miyaura反应中的应用(英文)

将PdCl2与ZIF-8的反应原料ZnO和2-甲基咪唑按照一定的比例,采用机械化学法原位将Pd2+负载在ZIF-8上(Pd2+/ZIF-8)。然后用NaBH4将Pd2+/ZIF-8进行还原,得到均匀分散的Pd纳米颗粒(Pd/ZIF-8)。通过XRD、N2吸附、透射电镜、ICP-AES、XPS等对Pd/ZIF-8的结构、形貌、价态等进行了表征。结果表明用机械化学法原位制备的Pd/ZIF-8具有分散均匀、容易大量制备的优点。该催化剂不仅能高效催化Suzuki-Miyaura交叉偶联反应,并且能够多次循环利用。     

Layer‐by‐layer assembly of {chitosan/Pd}n multilayer film based on in‐situ photochemical reduction with excellent electrocatalytic properties

Chitosan/palladium {CTS/Pd}_n composite multilayer film was assembled based on layer‐by‐layer self‐assembly technique and in‐situ photo‐chemical reduction reaction, in which the CTS plays the role of a photo‐reduction agent and an assembly reagent. Transmission electron microscopy (TEM) shows that spherical Pd nanoparticles with diameter of 20 nm are well‐dispersed in the composite multilayer films, and the size of Pd nanoparticles increased gradually with the extension of illumination time. Besides, the {CTS/Pd}_n composite multilayer film exhibits linear, uniform and regular layer‐by‐layer growth. Furthermore, the {CTS/Pd}_n composite multilayer film presents an excellent catalytic properties for oxygen reduction, and it has potential application in energy, chemical synthesis and biological processes. Copyright © 2015 John Wiley & Sons, Ltd.     

Hierarchical TiO2 microspheres supported ultrasmall palladium Nanocrystals: A highly efficient catalyst for Suzuki reaction

A hierarchical titanium dioxide microspheres-supported palladium catalyst (Pd/TiO₂-350) was prepared and characterized using BET, XRD, XPS, SEM, EDX, and TEM analyses. An ICP-OES analysis of Pd/TiO₂-350 further confirmed the successful Pd immobilization on TiO₂ with a palladium loading of 0.1 mmol g^?1. Pd/TiO₂-350 efficiently catalyzed the Suzuki-Miyaura reaction of aryl iodides with arylboronic acids to give the corresponding biaryl derivatives in good to excellent yields. After the reaction, the catalyst was recovered by centrifugation and reused three times without significant loss of its catalytic activity. Moreover, the loading of palladium species further decreased to 0.001 mol%, and the total turnover number and turnover frequency of the catalyst reached as high as 99 000 and 0.57 s^?1, respectively.     

Preparation of thin films comprising palladium nanoparticles by a solid-liquid interface reaction technique

A new approach to the formation of palladium nanoparticulate films with diameter between 6 and 50 nm by the solid-liquid interface reaction technique (SLIRT) has been presented. A solid film of palladium nitrate was formed by the modified spin coating method. This film is subsequently immersed in a reducing solution to initiate a reaction at the interface and ultimately transforms it to a palladium metal film. The kinetics of palladium reduction has been studied by UV-visible spectroscopy. The characterization of the palladium film has been performed by various physicochemical techniques such as XRD, ED, XPS, SEM, EDX, TEM, and UV-visible spectroscopy. The texture and morphology of the materials has been investigated by atomic force microscopy (AFM). At a constant palladium nitrate concentration, the average diameter of palladium nanoparticles decreases with an increase of hydrazine concentration. The effect of concentration of hydrazine on the particle size has been discussed. The palladium film formation mechanism has been proposed for the SLIRT.     

X-ray photoelectron spectroscopy-based valence band spectra of passive films on titanium

Titanium (Ti) is always covered by thin passive films. Thus, valence band (VB) spectra, obtained using X-ray photoelectron spectroscopy (XPS), are superpositions of the VB spectra of passive films and that of the metallic Ti substrate. In this study, to obtain the VB spectra only of passive films, angular resolution (for eliminating the substrate Ti contribution) and argon ion sputtering (for removing passive films) were used along with XPS. The passive film on Ti was determined to consist of a very thin TiO₂layer with small amounts of Ti₂O₃, TiO, hydroxyl groups, and water with a thickness of 5.9 nm. The VB spectra of Ti were deconvoluted into four peak components: a peak at ~1 eV, attributed to the Ti metal substrate; a broad peak in the 3–10 eV range, mainly attributed to O 2p (~6 eV) and O 2p-Ti 3d hybridized states (~8 eV), owing to the π (non-bonding) and σ (bonding) orbitals in the passive oxide film; and a peak at ~13 eV, attributed to the 3σ orbital of O 2p as OH⁻or H₂O. The VB region spectrum between approximately 3 and 14 eV from Ti is originating from the passive film on Ti. In particular, characterization of VB spectrum obtained with a takeoff angle of less than 24° is effective to obtain VB spectrum only from the passive film on Ti. The property as n-type semiconductor of the passive film on Ti is probably higher than that of rutile TiO₂ceramics.     

Sol-Gel Preparation and Characterization of Ag-TiO2 Nanocomposite Thin Films

Ag-TiO₂ thin films were prepared with a sol-gel route, using titanium isopropoxide and silver nitrate as precursors, at 0.03 and 0.06 Ag/Ti nominal atomic ratios. After drying at 80°C, the films were fired at 300°C and 500°C for 30 min. The films were analysed by X-ray diffraction (XRD) with glancing angle, and X-ray photoelectron spectroscopy (XPS), with depth profiling of the concentration. XPS analysis showed the presence of C and N as impurities in the nanocomposite films. Their concentration decreased with increasing the firing temperature. Chemical state analysis showed that Ag was present in metallic state, except for the very outer layer where it was present as Ag⁺. For the films prepared with a Ag/Ti concentration of 0.06, depth profiling measurements of the film fired at 300°C showed a strong Ag enrichment at the outer surface, while composition remained almost constant within the rest of the film, at 0.019. For the films heated to 500°C, two layers were found, where the Ag/Ti ratios were 0.015 near the surface and 0.026 near the substrate.     

Photo-Induced Hydrophilicity of TiO<Subscript>2</Subscript> Films Deposited on Stainless Steel via Sol-Gel Technique

The photo-induced hydrophilicity of TiO₂ films deposited on stainless steel substrates and silicon wafers using two different sol-gel routes has been investigated. The results indicate that crystalline titanium oxide films with excellent hydrophilic properties can be obtained on silicon wafer with both routes. XPS and XRD data reveal that films deposited on stainless steel exhibit crystallization features similar to those of films deposited on silicon wafers, and only differ by their oxidation degree owing to a TiO₂ reduction process associated to a diffusion of iron ions during deposition of the acidic sol and/or high temperature post-treatment. Consequently, hydrophilic properties of films deposited on stainless steel are inhibited. The deposition of a SiO_x barrier layer at the film/substrate interface allows preventing such a detrimental substrate influence. A low temperature deposition route of the TiO₂ film associated to the presence of a barrier layer yields best results in preventing iron contamination of the films.     

Dissolution of oxygen in polycrystalline palladium at $${P_{{O_2}}}$$= 100 Pa and temperatures of 500 to 950 K

The dissolution of oxygen in polycrystalline palladium Pd(poly) at an O₂ pressure of 100 Pa and temperatures of 500–950 K has been investigated by temperature-programmed desorption. At 500 K, the process yields a surface palladium film that includes an oxide-like reconstructed structure on a rarefied metal surface layer. At this temperature, palladium sorbs ~2 monolayers (ML) of oxygen. At 600–800 K, palladium dissolves up to ~140 ML of oxygen as a result of O₂ chemisorption on the surface of the oxide film, penetration of O_ads atoms under the oxide film, and their diffusion into the metal bulk. The dependence of the amount of oxygen sorbed by Pd(poly) (n) on the time of exposure to an O₂ atmosphere is described by a nearparabolic function, n = at^b, indicating that oxygen atoms diffuse in the metal lattice. The activation energy of this diffusion, Е _dif, is ~83.5 kJ/mol. At high temperatures (800–950 K), palladium sorbs much less oxygen (≤10 ML). This is due to the complete decomposition of the surface oxide film, a process that markedly hampers the insertion of Oads atoms under the surface layer of the metal.     

Synthesis and structure of poly-3,4-ethylenedioxythiophene film with the inclusions of palladium nanoparticles

By chemical deposition of ultrafine particles of metallic palladium on the polymer matrix of poly-3,4-ethylenedioxythiophene (PEDOT) composite PEDOT/Pd films were obtained. The conditions of synthesis of the composite films in dependence on the duration of exposure of the reduced form of PEDOT film in a solution of palladium chloride, its concentration and the film thickness were studied. By the methods of scanning electron microscopy (SEM) and transmission electron microscopy (TEM) it was shown that in the process of the synthesis of the composite films the nanosized palladium particles of predominantly quasispherical shape precipitated on the globular structure of the polymer. The size of the palladium nanoparticles in the composite PEDOT film and the nature of their distribution over the film bulk were revealed. An increase in the duration of deposition of the palladium nanoparticles on the film was shown to lead to an increase in their size and in the density of particles in the film.     

Photoelectrochemical Properties of Sol-Gel Processed Ag-TiO2 Nanocomposite Thin Films

Ag-TiO₂ thin films were prepared with a sol-gel route, using titanium isopropoxide and silver nitrate as precursors, at 0, 0.03 and 0.06 Ag/Ti nominal atomic ratios. After drying at 80°C, the films were fired at 300°C, 500°C, and 600°C for 30 min and 5 h. Glancing angle X-ray diffraction (XRD) analysis and X-ray photoelectron spectroscopy (XPS), with depth profiling of the concentration, were used to study the films. XPS analysis showed the presence of C and N as impurities in the nanocomposite films. Their concentration decreased with increasing the firing temperature. Chemical state analysis showed that Ag was present in metallic state, except for the outer layer where it was present as Ag⁺. For the films prepared with a Agt/Ti concentration of 0.06, depth profiling measurements of the film fired at 300°C showed a strong Ag enrichment at the outer surface, while composition remained almost constant within the rest of the film, at Ag/Ti atomic ratio of 0.02. Two layers were found for the films heated to 500°C, where the Ag/Ti ratios were 0.015 near the surface and 0.03 near the substrate. The photoelectrochemical properties of Ag-TiO₂ were studied for thin films deposited on ITO substrates. Photocurrents of Ag-TiO₂ nanocomposite electrodes fired at 300°C were observed even at visible light, for wavelengths longer than 400 nm.     

Stability studies of an electrochemically formed [C60]fullerene-palladium two-component film

The stability of C₆₀ and palladium two-component films, C₆₀/Pd, has been investigated. The effect of different polymerization conditions on the electrochemical stability of the film upon prolonged potential cycling has been studied. Stable voltammetric behavior was observed for polymers formed at potentials less negative than the potential of third C₆₀ reduction step. The incorporation of palladium particles into the structure of C₆₀/Pd polymers increases the polymer stability. The C₆₀/Pd films are doped with supporting electrolyte cations during reduction. The size of these cations is a crucial factor in determining the stability of the film. A strong solvent effect on the potential stability of the film was also observed. The wildest range of stable voltammetric properties was found for acetonitrile and N,N-dimethylformamide. No effect of the temperature on the film stability was observed. The results reported in this work allow for the determination of the optimal conditions for the formation of stable C₆₀/Pd films.     

Induction of titanium reduction using pyrrole and polypyrrole in the ionic liquid ethyl-methyl-imidazolium bis(trifluoromethanesulphonyl)amide

The electrowinning of titanium currently involves high temperature processing and quite extreme condition. As part of a project investigating the use of ionic liquids to refine titanium, we have investigated the use of a polymeric nucleating agent to assist the electro-deposition of the metal. Initial attempts focussed on polypyrrole coatings on the working electrode. These were unsuccessful due to the low conductivity of the conducting polymer in the IL at the reductive potentials required to deposit the titanium. However, it was found that pyrrole was a very successful additive able to induce deposition of titanium species from a TiCl₄ containing ionic liquid electrolyte ([emim][Ntf₂]). Well characterised titanium containing polypyrrole co-deposits have been achieved, when pyrrole was introduced, however bulk metallic titanium was not observed. The presence of titanium species in these deposits was confirmed by XPS. It is thought that the growing pyrrole oligomers form nucleation sites either in situ at the electrode–liquid interface or as a thin film on the electrode allowing co-precipitation of reduced Ti species from solution.     

One-pot deposition of palladium on hybrid TiO2 nanoparticles and catalytic applications in hydrogenation

One-pot deposition of Pd onto TiO(2) has been achieved through directly contacting palladium(II) salt with nanosized functionalized TiO(2) support initially obtained by sol-gel process using titanium isopropoxide and citric acid. Citrate groups act as functional moieties able to directly reduce the Pd salt avoiding any further reducing treatment. Various palladium salts (Na(2)PdCl(4) and Pd(NH(3))(4)Cl(2)·H(2)O) and titanium to citrate (Ti/CA) ratios (20, 50, and 100) were used in order to study the effect of the nature of the precursor and of the citrate content on the final Pd particle size and catalytic properties of the as-obtained Pd/TiO(2) systems. Characterization was performed using N(2) adsorption-desorption isotherms, ICP-AES, FTIR, XRD, XPS, and TEM. The as-obtained hybrid Pd/TiO(2) catalysts were tested in the selective hydrogenation (HYD) of an α,β-unsaturated aldehyde, i.e. cinnamaldehyde. Citrate-free Pd/TiO(2)-based catalysts present lower selectivity into saturated alcohol. However, citrate-functionalized Pd/TiO(2) catalyst seems to control the selectivity, the particle size and dispersion of Pd NPs leading to high intrinsic activity.     

Preparation of nano-sized Pt metal particles by photo-assisted deposition (PAD) on transparent Ti-containing mesoporous silica thin film

We have investigated a novel technique for the preparation of nano-sized Pt metals on Ti-containing mesoporous silica (TMS) thin film by photo-assisted deposition (PAD). The transparent TMS thin film was prepared on a quartz plate through sol—gel/spin coating. XRD, UV-Vis and Ti K-edge XAFS measurements revealed the formation of isolated Ti oxide species with a tetrahedral-coordination geometry in the silica framework. Deposition of Pt metal precursor on TMS thin film under UV-light irradiation, followed by reduction with molecular hydrogen, afforded a transparent thin film (Pt/TMS). The formation of highly dispersed nano-sized Pt metals having narrow size distributions was determined by Pd L_III-edge XANES and TEM analysis. The TMS and Pt/TMS thin films have been demonstrated to exhibit a strong hydrophilic property, even before UV irradiation, compared to the common mesoporous silica and TiO₂ thin films. After UV-light irradiation, the contact angle of water droplet on the TMS and Pt/TMS thin films became extremely lower, indicating the appearance of the photo-induced super-hydrophilic property.     

Photocatalytic Nanocomposite Films Fabricated by Layer‐by‐Layer Self‐assembly of TiO2 Nanoparticles and Lignosulfonates

Photocatalytic multilayer nanocomposite films composed of anatase TiO₂ nanoparticles and lignosulfonates (LS) were fabricated on quartz slides by the layer‐by‐layer (LBL) self‐assembly technique. X‐ray photoelectron spectroscopy (XPS), UV‐vis spectroscopy and atomic force microscopy (AFM) were used to characterize the TiO₂/LS multilayer nanocomposite films. Moreover, the photocatalytic properties (decomposition of methyl orange and bacteria) of multilayer nanocomposite films were investigated. XPS results indicated that the intensities of titanium and sulfur peaks increased with the LBL deposition process. A linear increase in absorbance at 280 nm was found by UV‐Vis spectroscopy, suggesting that stepwise multilayer growth occurs on the substrate and this deposition process is highly reproducible. AFM images showed that quartz slide was completely covered by TiO₂ nanoparticles when a 10‐bilayer multilayer film was formed. The decomposition efficiency of methyl orange by TiO₂/LS multilayer films under the same UV irradiation time increased linearly with the number of TiO₂ layers, and the results of decomposition of bacteria under UV irradiation showed that TiO₂/LS multilayer nanocomposite films exhibited excellent decomposition activity of bacteria (Escherichia coil).