Fabrication and photocatalytic property of TiO<Subscript>2</Subscript> nanofibers

TiO₂ nanofibers were prepared from tetrabutyl titanate sol precursors by using electrospun method. X-ray diffraction (XRD) and atomic force microscope (AFM) were used to characterize their crystal structure and morphology feature. The results demonstrated that TiO₂ nanofibers possessed anatase phase and the average diameter of TiO₂ nanofibers was about 150 nm. The photocatalytic property of TiO₂ nanofibers was evaluated for the photodecomposition of methyl orange solution. And TiO₂ nanofibers exhibited high photocatalytic activities with transfer efficiency about 100% after 20 min.     

Visible-light-driven photocatalytic degradation of microcystin-LR by Bi-doped TiO<Subscript>2</Subscript>

Bi-doped nano-crystalline TiO₂ (Bi–TiO₂) has been synthesized by sonocrystallization at low temperature. The Bi–TiO₂ materials have narrower bandgaps than pristine TiO₂, which endow them with significant visible light absorption. Accordingly, these materials had enhanced photocatalytic activity in the degradation of organic dye pollutants and the cyanotoxin microcystin-LR (MC-LR) under visible irradiation. It was found that degradation of MC-LR is rather efficient. After irradiation with visible light for 12 h the original MC-LR was removed completely, and 78% of the organic carbon was mineralized into CO₂ after irradiation for 20 h. The hydroxyl radical (·OH) is the major active species responsible for the degradation reaction. Identified intermediates primarily originate from attack of ·OH radicals on the double bonds between C4 and C5 (C6 and C7) of Adda and the ethylenic bond of Mdha in MC-LR. Some peptide bonds are also broken with longer irradiation time.     

TiO<Subscript>2</Subscript> nanofibers embedding single crystalline TiO<Subscript>2</Subscript> nanowires

Epitaxially grown titanium dioxide (TiO₂) nanofibers embedding single crystalline TiO₂ nanowires (NWs) were successfully fabricated by electropinning poly(vinyl pyrrolidone)/ethanol solutions mixed with hydrothermally synthesized TiO₂ NWs and titanium isopropoxide precursors and subsequently calcinating the electrospun nanofibers. Utilizing scanning electron microscopy (SEM) and transmission electron microscopy (TEM), the morphologies of TiO₂ NWs and nanofibers were investigated. High resolution TEM (HR-TEM) and selected area electron diffraction (SAED) allowed us to indentify the fact that, during the calcination process under the optimized condition, titanium isopropoxide precursors were epitaxially crystallized on the surface of single crystalline TiO₂ NWs. Based on the X-ray diffraction (XRD) experiments, it was also realized that the crystalline structure of hydrothermally synthesized TiO₂ NWs and epitaxially crystallized TiO₂ nanofibers is anatase and that TiO₂ composite nanofibers embedding TiO₂ NWs exhibited a higher crystallinity than the pristine TiO₂ nanofibers. Additionally, ultraviolet visible (UV–Vis) spectra of nanofibers indicated that optical properties of TiO₂ nanofibers can be tuned by introducing the single crystalline TiO₂ NWs.     

Optimized photocatalytic degradation of pefloxacin by TiO<Subscript>2</Subscript>/UV process

The photocatalytic degradation of pefloxacin was studied using modified TiO₂ as a photocatalyst. The effect of various parameters such as the amount of the photocatalyst, the initial concentration of pefloxacin, initial pH value on the process were investigated, and the optimal conditions were determined. The optimal amount of the photocatalyst is 0.3 g/L. The photodegradation rate of pefloxacin decreases with the increase of initial concentration. Alkaline medium is favorable for the photocatalytic degradation process. The primary photo-degradation products were analyzed by HPLC-ESI-MS/MS and thus the process mechanism was discussed.     

Preparation of nanocrystalline TiO<Subscript>2</Subscript> powders for photocatalytic oxidation of phenol

Nanocrystalline TiO₂ powders in the anatase, rutile, and mixed phases prepared by hydrolysis of TiCl₄ solution were of ultrafine size (<7.2 nm) with high specific surface areas in the range 167 to 388 m²/g. In the photocatalytic degradation of phenol as model reaction, the photocatalytic properties of TiO₂ nanoparticles were evaluated by use of UV–vis absorption spectroscopy and total organic carbon (TOC) content. The synthetic mixed-phase TiO₂ powder calcined at 400 °C had higher activity than pure anatase or rutile; it degraded more than 90% phenol to CO₂ (evaluated by TOC) after irradiation with near UV light for 90 min at a catalyst loading of 0.4 g/L. The TOC results indicated that rutile TiO₂ crystallites of particle size 7.2 nm resulted in much better photocatalytic performance than particles of larger size. This result suggested that some intermediates, not determined by UV–vis absorption spectroscopy, existed in the solution after the photocatalytic process over the rutile TiO₂ photocatalysts of larger crystallite size.     

Microstructure of SiO<Subscript>2</Subscript>/TiO<Subscript>2</Subscript> hybrid electrospun nanofibers and their application in dye degradation

SiO₂/TiO₂ hybrid nanofibers were prepared by electrospinning and applied for photocatalytic degradation of methylene blue (MB). The phase structure, specific surface area, and surface morphologies of the SiO₂/TiO₂ hybrid nanofibers were characterized through thermogravimetry (TG), X-ray diffraction (XRD) analysis, Brunauer–Emmett–Teller (BET) analysis, scanning electron microscopy (SEM), etc. XRD measurements indicated that doping of silica into TiO₂ nanofibers can delay the phase transition from anatase to rutile and decrease the grain size. SEM and BET characterization proved that silica doping can remarkably enhance the porosity of the SiO₂/TiO₂ hybrid nanofibers. The MB adsorption capacity and photocatalytic activity of the SiO₂/TiO₂ hybrid nanofibers were distinguished experimentally. It was found that, although increased silica doping content could enhance the MB adsorption capacity, the intrinsic photocatalytic activity gradually dropped. The SiO₂ (10 %)/TiO₂ composite nanofibers exhibited the highest MB degradation rate, being superior to SiO₂ (20 %)/TiO₂ or pure TiO₂.     

Three-dimensional hierarchical CeO<Subscript>2</Subscript> nanowalls/TiO<Subscript>2</Subscript> nanofibers heterostructure and its high photocatalytic performance

Combining the versatility of electrospinning technique and hydrothermal growth of nanostructures enabled the fabrication of hierarchical CeO₂/TiO₂ nanofibrous mat. The as-prepared hierarchical heterostructure consisted of CeO₂ nanowalls growing on the primary TiO₂ nanofibers. Interestingly, not only were secondary CeO₂ nanowalls successfully grown on TiO₂ nanofibers substrates, but also the CeO₂ nanowalls were uniformly distributed without aggregation on TiO₂ nanofibers. The photocatalytic studies suggested that the CeO₂/TiO₂ heterostructures showed enhanced photocatalytic efficiency compared with bare TiO₂ nanofibers under UV light irradiation.     

Preparation and photocatalytic activity of TiO<Subscript>2</Subscript> films with Ni nanoparticles

Titania thin films were synthesized by sol–gel dip-coating method with metallic Ni nanoparticles synthesized separately from an organometallic precursor Ni(COD)₂ (COD = cycloocta-1,5-diene) in presence of 1,3-diaminopropane as a stabilizer. Titania was obtained from a titanium isopropoxide precursor solution in presence of acetic acid. A Ni/TiO₂ sol system was used to coat glass substrate spheres (6, 4 and 3 mm diameter sizes), and further heat treatment at 400 °C was carried out to promote the crystallization of titania. XRD analysis of the TiO₂ films revealed the crystallization of the anatase phase. Transmission Electron Microscopy (TEM) and High Resolution TEM studies of Ni nanoparticles before mixing with the TiO₂ solution revealed the formation of Ni nanostructures with an average size of 5–10 nm. High-angle annular dark-field images of the Ni/TiO₂ system revealed well-dispersed Ni nanoparticles supported on TiO₂ and confirmed by AFM analysis. The photocatalytic activity of the Ni/TiO₂ films was evaluated in hydrogen evolution from the decomposition of ethanol using a mercury lamp for UV light irradiation. Titania films in presence of Ni nanoparticles show higher efficiency in their photocatalytic properties in comparison with TiO₂.     

Influence of ThO<Subscript>2</Subscript> on the photocatalytic activity of TiO<Subscript>2</Subscript>

Microcomposites consisting of TiO₂ (or Ce-doped TiO₂) and ThO₂ (0.5–2% of the TiO₂ mass) are produced by sol-gel synthesis of TiO₂ in presence of ThO₂. X-ray diffraction study reveals the effects of ThO₂ (compared to the ThO₂-free TiO₂, obtained by the same method) on the anatase interplanar distances, crystallites size and phase composition. The photocatalytic tests in presence of the composites under UV irradiation reveal an increase of the Malachite Green degradation rate constant. The effect depends on the Th relative content, temperature of annealing of the catalyst and addition of other doping agent. The highest photocatalytic activity is observed for TiO₂ obtained at 550°C and containing 1% ThO₂. The composite exhibits activity in dark, also. The presence of Ce⁴⁺ ions is not an obligatory requirement for the realization of the ThO₂ effect. The reported results suggest that the radioactivity of the Th and/or its decay products is one of the main factors responsible for the increased photocatalytic activity of TiO₂.      

Nanosized TiO<Subscript>2</Subscript> particles decorated on SiO<Subscript>2</Subscript> spheres (TiO<Subscript>2</Subscript>/SiO<Subscript>2</Subscript>): synthesis and photocatalytic activities

Nanosized TiO₂ and nano-anatase TiO₂ decorated on SiO₂ spherical core shells were synthesized by using a sol–gel method. The synthesized pure TiO₂ nano particle and TiO₂ grafted on SiO₂ sphere with various ratios have been characterized for their structure and morphologies by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectrophotometry (FTIR) and transmission electron microscopy (TEM). Their surface areas were measured using the BET method. The photocatalytic activity of all nanocomposites was investigated using methylene blue as a model pollutant. The synthesized TiO₂/SiO₂ particles appeared to be more efficient in the degradation of methylene blue pollutant, as compared to pure TiO₂ particles.     

Influence of MnO<Subscript>2</Subscript> on the photocatalytic activity of P-25 TiO<Subscript>2</Subscript> in the degradation of methyl orange

Influences of α-MnO₂, β-MnO₂, and δ-MnO₂ on the photocatalytic activity of Degussa P-25 TiO₂ have been investigated through the photocatalytic degradation of methyl orange. The TiO₂ photocatalyst, before and after being contaminated by MnO₂, was characterized by UV-visible diffuse reflectance spectroscopy (UV-vis DRS), photoluminescence (PL), and X-ray photoelectron spectroscopy (XPS). The results showed that photocatalytic activity of TiO₂ could be inhibited significantly or completely deactivated due to the presence of even a small amount of MnO₂ particles. It was found that the poisoning effect varied with the crystal phases of MnO₂ and the effect was in the order δ-MnO₂ >α-MnO₂ >β-MnO₂. The poisoning effect was attributed to the formation of heterojunctions between MnO₂ and TiO₂ particles. The heterojunctions changed the chemical state of Ti⁴⁺ and O²⁻ sites in the crystalline phase of TiO₂. MnO₂ in contact with TiO₂ particles also broadens the band-gap of TiO₂, which decreases UV absorption of TiO₂. It can also create some deep impurity energy levels serving as photoelectron-photohole recombination center, which accelerates the electron-hole recombination. Supported by the National Natural Science Foundation of China (Grant No. 20477009) and the Natural Science Foundation of Hebei Province (Grant No. E2005000183)     

Effects of TiO<Subscript>2</Subscript> surface fluorination on photocatalytic degradation of methylene blue and humic acid

Photocatalytic degradation (PCD) reactions of cationic methylene blue (MB) and anionic humic acid (HA) were studied in naked TiO₂ and fluorinated TiO₂ (F-TiO₂) suspensions in order to investigate how the modification of the TiO₂ surface functional group influenced PCD reactions. Adsorption behaviors of MB and HA in the naked TiO₂ followed a typical pH-dependent electrostatic interaction mechanism. On the other hand, those in the F-TiO₂ were markedly changed and even showed a reversed dependence in specific pH ranges due to surface fluoride interrupting the interaction of substrates and surface titanol groups. PCD rates of MB (k _MB) and its N-demethylation (Δλ _max) were significantly increased by surface fluorination below circum-neutral pH range, in particular, by a factor of 12 and 54 at pH 2, respectively. In the case of HA, the fluorination had an insignificant effect on its degradation rate but appeared to change its degradation behavior. It has been suggested that, although the primary effect of fluorination enhances the photocatalytic production of hydroxyl radicals, the change in electrostatic interaction with substrates could affect PCD as well.     

Assessment of operating parameters for photocatalytic degradation of a textile dye by Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>/TiO<Subscript>2</Subscript>/clinoptilolite nanocatalyst using Taguchi experimental design

In the current study, a nanophotocatalyst doped with of TiO₂ and Fe₂O₃ nanoparticles supported on Iranian clinoptilolite was synthesized and characterized by XRD, XRF, SEM, and EDX analyses. The results suggested the successful loading of TiO₂ and Fe₂O₃ nanoparticles onto the surface of clinoptilolite. The SEM images confirmed the average size of nanoparticles deposited on zeolite, which was about 20–40 nm. Furthermore, application of the synthesized photocatalyst in photocatalytic degradation of Acid Black 172 dye was studied using the Taguchi method and the chosen parameters were as follows: pH (2–7), dye concentration (50–200 mg/l), irradiation time (30–120 min), and catalyst dosage (0.5–1.5 g/l). The results indicate that dye concentration, pH, and irradiation time are respectively the most effective factors in these experiments while with the minimum dosage of the catalyst (0.5 g/l), up to 90 % removal efficiency could be achieved. The optimum value for each parameter was pH = 2, dye concentration = 50 mg/l, catalyst dosage = 1 g/l and irradiation time = 60 min, and the dye removal efficiency reached up to 100 % at these optimal conditions. Furthermore, after five-times recycling and reusing the catalyst, the efficiency of the photocatalytic degradation was reduced from 91.5 to 65.9 %, which is still an acceptable value.     

Photocatalytic degradation of dichloroacetyl chloride adsorbed on TiO<Subscript>2</Subscript>

Dichloroacetyl chloride (DCAC) attracted our attention as an intermediate product of the photocatalytic degradation of trichloroethylene (TCE). The adsorption and photocatalytic reaction of DCAC on TiO₂ have been investigated by FTIR spectroscopy. The influence of the surface structure of several TiO₂s on the reaction mechanism was discussed in order to understand the complete degradation mechanism of TCE as well as DCAC. DCAC was transformed into dichloroacetic acid (DCAA) on the relatively hydrophobic TiO₂ surface by the small amount of the water molecules weakly adsorbed on the surface. This DCAA was degraded to phosgene, CO₂, and CO during UV irradiation. For the hydrophilic TiO₂, DCAC was mainly transformed into the dichloroacetate anion. UV irradiation allowed this species to produce chloroform in addition to phosgene, CO₂, and CO. It is suggested that DCAC easily reacts with the Ti–OH group on the hydrophilic TiO₂ and forms the bidentate titanium chelate of dichloroacetate, which efficiently degrades into chloroform.     

Solvothermal synthesis and photocatalytic activity of S-doped TiO<Subscript>2</Subscript> and TiS<Subscript>2</Subscript> powders

The photocatalytic activity of S-doped TiO₂ powder depends on the S content. To synthesize S-doped TiO₂ powders with high S content, solvothermal processes were used in this work. The S-doped TiO₂ powder contains 2.0 M% sulfur and has an absorption edge of 460 nm (2.7 eV). The pure TiS₂ powder also synthesized by a solvothermal process has an absorption edge of 595 nm (2.08 eV) and broad absorption above 595 nm. The photocatalysis experiments indicate that the degradation of methyl orange is associated with the light adsorption edge. The photocatalytic activity is much larger for the pure TiS₂ powder than for partially S-doped TiO₂ powder.     

Preparation of Nb<Subscript>2</Subscript>O<Subscript>5</Subscript> and N co-doped TiO<Subscript>2</Subscript> photocatalysts and their enhanced photocatalytic activities under visible light

Niobium pentaoxide (Nb₂O₅) and nitrogen co-doped TiO₂ photocatalysts were prepared by mechanical alloying with Nb₂O₅, TiO₂ and urea as raw materials. The pure TiO₂ powders of Degussa P25 were chosen as precursor. Chemical and physical properties of the Nb₂O₅ and N co-doped TiO₂ photocatalysts were investigated, including XRD patterns, XPS spectra, DRS spectra, FT-IR spectra and N₂ adsorption-desorption isotherms. Experiments on photodegradation of methylene blue (MB) and sulfosalicylic acid (SSA) under visible light were carried out to evaluate the photoactivities of the prepared samples, and the chemical oxygen demand (COD) analysis was also conducted as a comparison.     

Enhancement of photocatalytic H<Subscript>2</Subscript> evolution over TiO<Subscript>2</Subscript> nano-sheet films by surface loading NiS nanoparticles

NiS/TiO₂ nano-sheet films (NiS/TiO₂ NSFs) photocatalysts were prepared by loading NiS nanoparticles as noble metal-free cocatalysts on the surface of TiO₂ films through a solvothermal method. The prepared samples were characterized by XRD, SEM, EDS, UV–Vis absorption spectra and XPS analysis. The photocatalytic H₂ evolution and photoluminescence spectroscopy (PL) experiments indicated that the NiS cocatalysts could efficiently promote the separation of photogenerated charge carriers in TiO₂ and consequently enhance the H₂ evolution activity. The hydrogen yield obtained from the optimal sample reached 4.31 μmol cm^–2 at 3.0 h and the corresponding energy efficiency was about 0.26%, which was 21 times higher than that of pure TiO₂ NSF. A possible photocatalytic mechanism of NiS cocatalyst on the improvement of the photocatalytic performance of TiO₂ NSF was also proposed.     

Enhancement of visible-light photocatalytic activity of Cu-doped TiO<Subscript>2</Subscript> nanoparticles

Bare TiO₂ and Cu-doped TiO₂ nanoparticles with different nominal doping amounts of Cu ranging from of 0.5 to 5.0 mol% were synthesized using the modified sol–gel method. The samples were physically characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectroscopy, Brunauer–Emmett–Teller-specific surface area, UV–Vis diffuse reflectance spectroscopy, zeta potential, X-ray photoelectron spectroscopy, inductively coupled plasma, and photoluminescence techniques. The Cu-doped TiO₂ exhibited good photocatalytic activity in mineralization of oxalic acid and formic acid under visible light irradiation. Photomineralization of oxalic and formic acids under visible light irradiation revealed greatly enhanced photoactivity exhibited by the 2.0 mol% Cu-doped TiO₂ photocatalyst compared to bare TiO₂ . The enhanced photocatalytic performance arises from copper ion doping in the TiO₂ structure, leading to an extended photoresponsive range, enhanced photogenerated charge separation, and transportation efficiency.     

Synthesis and photocatalytic activity of TiO<Subscript>2</Subscript> nanoparticles fluorine-modified with TiF<Subscript>4</Subscript>

Fluorine-modified TiO₂ nan oparticles were synthesized by introducing TiF₄ as a fluorine source either before or after the sufficient hydrolysis and condensation of Ti(OEt)₄. The photocatalytic activity of the fluorine-modified catalysts was found to be greatly affected by the fluorine position in TiO₂ nanoparticles. When TiF₄ and Ti(OEt)₄ hydrolyzed with synchronization, the fluorine tended to be doped in the lattice. The formation of Ti³⁺ defects could result in charge recombination in bulk and bring down the photocatalytic activity. In contrast, if TiF₄ was introduced after the sufficient hydrolysis and condensation of Ti(OEt)₄. Ti−F bonds could exist mainly on the TiO₂ particles surface, which not only prevented the growth of anatase crystals but also facilitated the transfer of organic compounds from solution to catalyst surface by reducing the hydrophilic properties.