The Infrared and Raman Spectra of β-and α-Tricalcium Phosphate (Ca3(Po4)2)

Factor group analysis was applied to interpret the vibrational spectra of β-and α-tricalcium phosphate (Ca₃(PO₄)₂). The analysis predicts the number of bands formed due to the splitting of the fundamental vibrational modes of the PO₄ ^3-ion. The number of the infrared and Raman bands predicted by this analysis for the two phases are drastically different and can be ascribed to the difference in atomic arrangements in the two phases resulting in greater shielding of the PO₄ ^3-ions in the β-phase than in the α-phase. Discrepancies in the number of predicted and experimentally-observed bands can be attributed to the weak intensities of some vibrational modes or the convolution of vibrations and limited spectral resolution.     

Infrared spectra of BeSO4.4H2O and its deuterated analogue in 4000–1200 cm−1 region

IR spectra of BeSO₄.4H₂O and its deuterated analogue at ∼300 K and ∼110 K are reported in the region 4000–1200 cm⁻¹ using thin film and nujol mull techniques. The observed bands have been assigned as the internal modes of the water and the overtones and combinations of various modes using the recently revised assignments of SO₄ ²⁻ and Be(aq)₄ fundamentals in the region 1200–250 cm⁻¹ (Srivastavaet al 1976). The splitting of the internal modes of water has been discussed in the light of the effects of deuteration and cooling and it is shown that all the water molecules in a unit cell are asymmetric but crystallographically equivalent.     

Vibrational spectra of (NH4)3ZnCl5

IR and Raman spectra of (NH₄)₃ZnCl₅ have been recorded. The observed spectra have been analysed on the basis of the vibrations of ZnCl ₄ ²⁻ and NH ₄ ⁺ ions. The appearance of multiple Raman bands indicates the presence of two different types of ammonium ions. The effect of anisotropic crystalline field over the ZnCl₄ and NH₄ tetrahedra is also discussed. The assignment of internal modes has been verified by the potential energy distribution calculations.     

Infrared spectra of BeSO4.4H2O and its deuterated analogue at 110K in 1200–250 cm−1 region

IR absorption spectra of BeSO₄.4H₂O and its deuterated analogue are reported in the region 1200–250 cm⁻¹ at 110 K. The half-widths and relative integrated intensities of the bands are also reported. The study largely confirms the assignments for thev ₃ andv ₄ modes of SO ₄ ²⁻ ion and thev ₃ mode of Be(aq) ₄ ²⁺ , complex as made by Diemet al. The assignments of the other modes of SO ₄ ²⁻ and Be(aq) ₄ ²⁺ , and the librational modes of water are given a more solid footing as result of the present investigation.     

The infrared and laser Raman spectra of K2Zn(SO4)2 · 6H2O

The Raman spectra of the single crystal of K₂Zn(SO₄)₂·6H₂O belonging toC _2h ⁵ space group in the 40–1200 cm⁻¹ region in different scattering geometries and their spectra ofthe microcrystalline salt in the 1500-50 cm⁻¹ region have been reported. The dynamics of the crystal has been described in terms of 186 phonon modes under the unit cell approximation. The weak bands in the region 400–900 cm⁻¹ have been assigned to the libratory modes of H₂O molecules in contradiction to the assignments reported by Ananthanarayanan. The ambiguities existing in the literature about the assignments ofν ₂ ^c andν ₅ ^c modes of [Zn(H₂O)₆]²⁺ have also been removed. The translatory and libratory modes of different units of the crystal have been identified and assignments are made using farir and Raman data on various isomorphous tutton salts. It has been inferred that both SO ₄ ²⁻ tetrahedron and [Zn(H₂O)₆]²⁺ octahedron undergo linear as well as angular distortions from their free state symmetries in the crystal.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Influence of ligand coordination of cobalt ions on structural properties of ZnO-ZnF2-B2O3 glass system by means of spectroscopic studies

The glasses of the composition 10ZnO-30ZnF₂-60B₂O₃ doped with different concentrations of CoO were prepared. Differential scanning calorimetric (DSC) studies, optical absorption, photoluminescence and infrared spectra of these glasses have been carried out. DSC studies have indicated that the resistance of the glass against devitrification increases with the increase in the concentration of CoO. Optical absorption spectra have exhibited one octahedral band due to ⁴T_1g(F)→²T_1g(H) and two tetrahedral bands due to ⁴A₂(⁴F)→⁴T₁(⁴P) ⁴A₂(⁴F)→⁴T₁(⁴F) transitions of Co²⁺ ions at about 525, 570 and 1400 nm, respectively. As the concentration of CoO is increased the tetrahedral bands are observed to grow at the expense of octahedral band. The luminescence spectra have exhibited two emission bands in the spectral regions of 600-700 nm and 800-900 nm due to ⁴T₁(⁴P)→⁴A₂(⁴F) and ⁴T₁(⁴P)→⁴T₂(⁴F) tetrahedral transitions of Co²⁺ ions, respectively. With the increasing content of cobalt ions in the glass matrix, the half width and intensity of these bands are observed to increase. The analysis of the results of these two spectra coupled with IR spectra has indicated that as the concentration of CoO is increased in the glass matrix, the tetrahedral occupancy of cobalt ions dominates over the octahedral occupancy and increase the rigidity of the glass network.     

The enhancement of luminescence in Co-doped cubic Eu2O3 using Li and Al ions

The co-doping of Li⁺ and Al³⁺ ions drastically enhances the luminescence of cubic Eu₂O₃. The integrated emission intensity of ⁵D₀→⁷F_J bands (J=1-4) at 580-710 nm increases by a factor of about 6.7 in the co-doped Eu₂O₃ compared to the un-doped Eu₂O₃. In order to confirm that the co-doped ions were actually incorporated into the host lattice, the structural characteristics were studied using Raman spectroscopy, XPS, XRD, photoluminescence lifetime, and an SEM. These analyses consistently indicate a certain structural evolution in their results with an increase in the co-doping concentration. Variations in the crystal structure, the crystal morphology, and the intensity variation of the Raman modes at 465 and 483 cm⁻¹ are presented as the evidences showing the incorporation of the co-doped ions into the host. The luminescence enhancement is discussed in terms of concentration quenching, reduction of defect sites, and the modification of the local symmetry of the Eu³⁺ ions, especially in the inversion symmetry sites.     

Luminescence of La3F3[Si3O9]:Ce

The luminescence properties of Ce³⁺ in La₃F₃[Si₃O₉] are reported. Excitation and emission bands corresponding to 4f¹→5d¹ transitions of Ce³⁺ were identified. The center of gravity of the 5d states lies at remarkable high energy (43.2×10³ cm⁻¹) for Ce³⁺ in a silicate compound. This high value is attributed to the combined oxygen/fluoride coordination of the Ce³⁺ ion. Emission from the lowest 4f5d level to the ²F_5/2 and ²F_7/2 levels was found at 32.4×10³ and 30.4×10³ cm⁻¹. These results are compared with literature data on silicates and fluorides. From the values found for Ce³⁺, predictions are made for the positions of the 4f5d bands of Pr³⁺ and Er³⁺ in La₃F₃[Si₃O₉]. For both ions, it is concluded that in this host lattice emission is expected from high lying 4fⁿ energy levels.     

Luminescence of ZnWO4 and CdWO4 thin films prepared by spray pyrolysis

Thin films of ZnWO₄ and CdWO₄ were prepared by spray pyrolysis and the structural, optical, and luminescence properties were investigated. Both ZnWO₄ and CdWO₄ thin films showed a broad blue-green emission band. The broad band of ZnWO₄ films was centered at 495 nm (2.51 eV) consisted of three bands at 444 nm (2.80 eV), 495 nm (2.51 eV) and 540 nm (2.30 eV). The broad band of CdWO₄ films at 495 nm (2.51 eV) could be decomposed to three bands at 444 nm (2.80 eV), 495 nm (2.51 eV) and 545 nm (2.28 eV). These results are consistent with emission from the WO₆⁶⁻ molecular complex. The luminance and efficiency for ZnWO₄ film at 5 kV and 57 μA/cm² were 48 cd/m² and 0.22 lm/w, respectively, and for CdWO₄ film the values were 420 cd/m² and 1.9 lm/w.     

Abnormally enhanced Eu emission in Y2O2SO4:Eu inherited from their precursory dodecylsulfate-templated concentric-layered nanostructure

A new nanostructure-mediated approach was demonstrated to synthesize Eu³⁺-doped yttrium oxysulfates Y₂O₂SO₄:Eu³⁺ giving rise to abnormally enhanced Eu³⁺ emission. Yttrium and europium salts, sodium dodecylsulfate (SDS), and urea at various Eu³⁺ concentrations were reacted in aqueous solution at 80, 85, and 87 °C to yield Eu³⁺-doped dodecylsulfate-templated yttrium oxide mesophases with straight-layered (S-type), concentric-layered (C-type) and layer-to-hexagonal transient-layered (T-type) structures, respectively. On calcination at 1000 °C, all of these mesophases were converted into Y₂O₂SO₄:Eu³⁺ to exhibit luminescence bands including the ⁵D₀-⁷F₂ transition with a tendency in intensity to saturate or reach a maximum at 10-12 mol% Eu doping. The Eu³⁺ emissions for Y₂O₂SO₄:Eu³⁺ mediated by the T- and C-type mesophases were enhanced in intensity by a factor of about two and three times, respectively, stronger than those for not only compositionally the same sulfate Y₂O₂SO₄:Eu³⁺ obtained from yttrium-based sulfates but also Y₂O₃:Eu³⁺ obtained in the SDS-free system. In contrast, the emission intensities for the S-type-mesophase-mediated Y₂O₂SO₄:Eu³⁺ were close to those for the latter sulfates. The abnormally enhanced emission is likely based on specific deformation of sulfate groups induced through the conversion of concentric dodecylsulfate-layers to straight sulfate-layers in the oxysulfate framework upon calcination.     

The AB2-XA1 electronic transition of NO2: A rovibronic survey covering 14 300-18 000 cm

More than 250 rotationally resolved vibrational bands of the A²B₂-X²A₁ electronic transition of ¹⁵NO₂ have been observed in the 14 300-18 000 cm⁻¹ range. The bands have been recorded in a recently constructed setup designed for high resolution spectroscopy of jet cooled molecules by combining time gated fluorescence spectroscopy and molecular beam techniques. The majority of the observed bands has been rotationally assigned and can be identified as transitions starting from the vibrational ground state or from vibrationally excited (hot band) states. An exceptionally strong band is located at 14 851 cm⁻¹ and studied in more detail as a typical benchmark transition to monitor ¹⁵NO₂ in atmospheric remote sensing experiments. Standard rotational fit routines provide band origins, rotational and spin rotation constants. A subset of 177 vibronic levels of ²B₂ vibronic symmetry has been analyzed in the energy range between 14 300 and 17 250 cm⁻¹, in terms of integrated density and using Next Neighbor Distribution. It is found that the overall statistical properties and polyad structure of ¹⁵NO₂ are comparable to those of ¹⁴NO₂ but that the internal structures of the polyads are completely different. This is a direct consequence of the X²A₁-A²B₂ vibronic mixing.     

SrAl_2B_2O_7:Dy~(3+)材料的制备及其发光性能

采用高温固相法制备了SrAl2B2O7:Dy3+发光材料.在350nm紫外光激发下,测得SrAl2B2O7:Dy3+材料的发射光谱为一个多峰宽谱,主峰分别为480,573和678nm;分别和Dy3+的4F9/2→6H15/2,4F9/2→6H13/2,4F9/2→6H11/2的跃迁发射相对应;监测573nm的发射峰,得到材料的激发光谱为一个多峰宽谱,主峰分别为295,325,350,365,400nm.研究了Dy3+掺杂浓度对SrAl2B2O7:Dy3+材料发射光谱的影响,随着Dy3+掺杂浓度的增大,SrAl2B2O7:Dy3+材料的Iy/Ib逐渐增大,根据Judd-Ofelt理论解释了其原因.随着Dy3+掺杂浓度的增大,Dy3+的4F9/2→6H13/2跃迁产生的573nm发射峰强度先增大,在4%时达到最大值,之后减小,其自身的浓度猝灭机理为电偶极-电偶极相互作用.不同的电荷补偿剂Li+,Na+,K+的引入均使发光强度得到提高,尤其以Li+最佳,发光强度提高了大约33%.     

Photoluminescence spectra of thenardite Na2SO4 activated with rare-earth ions, Ce, Sm, Tb, Dy and Tm

Five Na₂SO₄:RE³⁺ phosphors activated with rare-earth (RE) ions (RE³⁺=Ce³⁺, Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) were synthesized by heating natural thenardite Na₂SO₄ from Ai-Ding Salt Lake, Xinjiang, China with small amounts of rare-earth fluorides, CeF₃, SmF₃, TbF₃, DyF₃ and TmF₃, at 920 °C in air. The photoluminescence (PL) and optical excitation spectra of the obtained phosphors were measured at 300 and 10 K. In the PL spectrum of Na₂SO₄:Ce³⁺ at 300 K, two overlapping bands with peaks at 335 and 356 nm due to Ce³⁺ were first observed. Narrow bands observed in PL and excitation spectra of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors were well identified with the electronic transitions within the 4fⁿ (n=5, 8, 9 and 12) configurations of RE³⁺. The existence of excitation bands with high luminescence efficiency at wavelengths shorter than 230 nm is characteristic of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors. The obtained results suggest that these phosphors are unfavorable as the phosphor for usual fluorescence tubes, i.e., mercury discharge tubes, but may be favorable as the phosphor for UV-LED fluorescent tubes and as cathodoluminescence, X-ray luminescence and thermoluminescence phosphors.     

Optical properties of Mn-activated Na2SnF6 and Cs2SnF6 red phosphors

Alkaline hexafluorostantanate red phosphors Na₂SnF₆:Mn⁴⁺ and Cs₂SnF₆:Mn⁴⁺ are synthesized by chemical reaction in HF/NaMnO₄ (CsMnO₄)/H₂O₂/H₂O mixed solutions immersed with tin metal. X-ray diffraction patterns suggest that the synthesized phosphors have a tetragonal symmetry with the space group D_4h¹⁴ (Na₂SnF₆:Mn⁴⁺) and a trigonal symmetry with the space group D_3d³ (Cs₂SnF₆:Mn⁴⁺). Photoluminescence (PL) analysis, PL excitation (PLE) spectroscopy, and the Raman scattering techniques are used to investigate the optical properties of the phosphors. The Franck-Condon analysis of the PLE data yields the Mn⁴⁺-related optical transitions to occur at ∼2.39 and ∼2.38 eV (⁴A_2g→⁴T_2g) and at ∼2.83 and ∼2.76 eV (⁴A_2g→⁴T_1g) for Na₂SnF₆:Mn⁴⁺ and Cs₂SnF₆:Mn⁴⁺, respectively. The crystal field parameters (Dq) of the Mn⁴⁺ ions in the Na₂SnF₆ and Cs₂SnF₆ hosts are determined to be ∼1930 and ∼1920 cm⁻¹, respectively. Temperature-dependent PL measurements are performed from 20 to 440 K in steps of 10 K, and the obtained results are interpreted by taking into account the Bose-Einstein occupation factor. Comprehensive discussion is given on the phosphorescent properties of a family of Mn⁴⁺-activated alkaline hexafluoride salts.     

Cr3+掺杂的Cd3Al2Ge3O12光谱特性及晶场参数计算

采用高温固相法合成了Cd₃Al₂Ge₃O₁₂：Cr³⁺多晶材料,利用X射线衍射对其结构进行了分析,通过Cr³⁺的室温吸收光谱、室温和77K发射光谱分别对其光谱特性和晶场参数进行了分析和计算.结果表明：在450 nm的蓝光激发下,Cd₃Al₂Ge₃O₁₂：Cr³⁺室温发 关键词： 3Al₂Ge₃O₁₂：Cr³⁺')" href="#">Cd₃Al₂Ge₃O₁₂：Cr³⁺ 荧光光谱 晶场参数 可调谐激光     

Infrared active phonon modes and ionicity of single crystal MgAl2O4

Near-normal incident infrared reflectivity spectra of （100） MgAl2O4 spinel single crystal have been measured at different temperatures in the frequency region between 50 and 6000 cm^-1. Eight infrared-active phonon modes are identified, which are fitted with the factorized form of the dielectric function. The dielectric property and optical conductivity of the MgAl2O4 crystal are analysed. From TO/LO splitting, the effective Szigeti charges and Born effective charges at different temperatures are calculated for studying the ionicity and the effect of polarization. Based on the relationship between the （LO-TO）1 splitting, which represents the transverse and longitudinal frequencies splitting of the highest energy phonon band in the reflectivity spectrum, and the ionic-covalent parameter, the four main phonon modes are assigned. MgA1204 can be considered as a pure ionic crystal and its optical characters do not change with decreasing temperature, so it may be used as a suitable substrate for high-Tc superconducting thin films.     

Studies of the local compressibility of Cr 3+-centered octahedron in LiSc (WO 4)2 crystal from the pressure dependence of the optical spectra

The pressure-induced shifts of optical spectral bands ⁴T₂ and ²E for the preferential Cr³⁺-centered octahedron for Cr³⁺ at the Sc³⁺ site of the LiSc (WO ₄)₂ crystal have been calculated from crystal-field theory. From the calculation, the local linear compressibility d ln R/d p≈?3.3×10^?4 kbar^?1 for the Cr³⁺ center in a LiSc (WO ₄)₂ crystal is obtained. The result is discussed.     

Theoretical explanation of optical absorption spectra and covalent effect of Ni2+ ions in octahedral sites of Ca3Sc2Ge3O12 crystal

The optical absorption spectra (d-d transition bands) and covalent effect of Ni²⁺ ions in octahedral sites of Ca₃Sc₂Ge₃O₁₂ crystal have been investigated by the full energy matrix based on the two spin–orbit coupling parameters model. The bond length of octahedral site is R_i?=?2.19 Å, which can be determined by the cubic crystal-field parameter and optical spectral data. The lattice distortion of the Ni²⁺ center in Ca₃Sc₂Ge₃O₁₂ crystal is also obtained from the calculations. In addition, the result has shown that the covalent effect of Ni²⁺ ion in the octahedral site of Ga₃Sc₂Ge₃O₁₂ is obvious and cannot be ignored. The calculated d-d transition bands agree well with that of the experimental findings, suggesting that the present methods can explain reasonably the optical spectral data and covalent effect of 3d⁸ ions in octahedral lattices.     

Photoluminescence characterization of Ce and Dy doped Li2CaGeO4 phosphors

Ce³⁺ and Dy³⁺ activated Li₂CaGeO₄ phosphors were prepared by a solid-state reaction method, and characterized by XRD (X-ray diffraction) and photoluminescence techniques. The characteristic emission bands of Dy³⁺ due to ⁴F_9/2→⁶H_15/2 (blue) and ⁴F_9/2→⁶H_13/2 (yellow) transitions were detected in the emission spectra of Li₂CaGeO₄:Dy³⁺. Ce³⁺ broad band emission was observed in Li₂CaGeO₄:Ce³⁺ phosphors at 372 and 400 nm due to 5d→4f transition when excited at 353 nm. Co-doping of Ce³⁺ enhanced the luminescence of Dy³⁺ significantly and concentration quenching occurs when Dy³⁺ is beyond 0.04 mol%. White-light with different hues can be realized by tuning Dy³⁺ concentration in the phosphors.