Correlation between hydrogen‐bonding interaction and mechanical properties of polyimide fibers

Novel co‐polymerization polyimide (PI) fibers based on 4,4′‐oxydianiline (ODA)‐pyromellitic dianhydride (PMDA) were prepared. 2‐(4‐Aminophenyl)‐5‐aminobenzimidazole (PABZ) containing the N? H group was introduced into the structure of the fibers as the proton donor. The results of Fourier transform infrared (FTIR) and dynamic mechanical analysis (DMA) showed that hydrogen bonding occured between the N? H group and chains, which strongly enhanced interchain interaction. This hydrogen bonding interaction increased the tensile strength and initial modulus of the PI fibers up to 2.5 times and 26 times, respectively, compared to those of homo‐PI PMDA‐ODA fibers with no hydrogen‐bonding interaction because of the absence of proton donors after the imidization process. In the mean time, glass transition temperature (T_g) of the modified PI fibers was found to be 410–440°C, which was higher than that of the homo‐PI PMDA‐ODA fibers. From the result, a novel access to molecular design and manufacture of high performance PI fibers with good properties could be provided. Copyright © 2009 John Wiley & Sons, Ltd.     

Mechanical properties of BPDA-ODA polyimide fibers

An aromatic polyimide was synthesized via a one-step polycondensation reaction between biphenyltetracarboxylic dianhydride (BPDA) and 4,4′-oxydianiline (ODA) in p-chlorophenol. The polyimide (BPDA-ODA) solution dopes were spun into fibers by means of dry-jet wet spinning. The as-spun fibers were drawn and treated in heating tubes for improving the mechanical properties. The thermal treatment on the fibers resulted in a relatively high tensile strength and modulus. Thermal mechanical analysis (TMA) was employed to study the linear coefficient of thermal expansion (CTE). Thermal gravimetry analysis (TGA) spectra showed that the BPDA-ODA fibers possessed an excellent property of thermo-oxidative degradation resistance. The sonic modulus E_s of the polyimide fibers was measured.     

Enhancement of properties of polyimide/silica hybrid nanocomposites by benzimidazole formed hydrogen bond

Polyimide/silica hybrid nanocomposites were prepared by sol–gel method without coupling agent. A novel diamine with a benzimidazole group, 2‐(4‐aminophenyl)‐5‐aminobenzimidazole (PABZ), was introduced to copolymerize with 4,4'‐oxydianiline (ODA) and pyromellitic dianhydride (PMDA) to synthesize polyimide (PI) matrix. The compatibility between PI and silica was improved by hydrogen bonds formed between silica phase and the –NH– group on benzimidazole of the new diamine. Highly transparent hybrid films were obtained when silica content reached as high as 30 wt%. SEM results show that silica particles with sizes much smaller than that in PMDA‐ODA/silica system disperse homogeneously in the PI matrix. Differing from most hybrid systems without coupling agent, the tensile strength of PABZ system increases from 152 MPa to 165 MPa with silica content increasing from 0 to 20 wt%, while, it decreases linearly in PMDA‐ODA system. DMA analysis shows that the introduction of PABZ largely increases the glass transition temperature (Tg) for all silica contents, which is suggested to be due to the more rigid structures and stronger interaction between the two phases. Meanwhile, the decomposition temperature and char yields at 800 °C are both higher than that of pure PIs. The structures of the hybrid films were identified by FTIR spectra, which indicate that different silica morphologies are developed, resulted from the hydrogen bonds between benzimidazole and silica phase. Copyright © 2011 John Wiley & Sons, Ltd.     

Synthesis and Crystal Structure of a New Adamantane Amide Derivative

A novel adamantane acyl amide derivative containing two phthalimido pendant groups(C31H31N3O5) has been synthesized,and its structure was characterized by elemental analysis,IR,1 H NMR spectra,and single-crystal X-ray diffraction.The crystal belongs to triclinic,space group P1 with a=7.3158(10),b=13.2405(18),c=14.378(2),α=72.419(2),β=84.496(2),γ=81.799(2)o,V=1312.0(3)3,Z=2,Dc=1.330 g/cm 3,μ=0.09 mm-1,Mr=525.59,F(000)=556,S=1.001,R=0.0523 and wR=0.0707 for 5901 unique reflections with 2363 observed ones(I>2σ(I)).π-π stacking interactions(offset face-to-face) exist between the two rings of phthalimides from the neighboring molecules in the title crystal structure.The intermolecular dihedral angle between the two rings of neighboring phthalic amides is 6.26° and the distance is 4.008.     

Preparation and dielectric properties of polyimide foams containing crosslinked structures

In order to obtain cellular materials with low dielectric properties, crosslinked polyimide foams were prepared using 3,3′,4,4′‐benzophenonetetracarboxylic dianhydride (BTDA), 4,4′‐oxydianiline (ODA) and 2,4,6‐triaminopyrimidine (TAP) as monomer via a poly(ester‐amine salt) precursor process. The structures of the precursors and the polyimide foams were characterized by thermogravimetric analysis (TGA) and FT‐IR, while the morphologies of the polyimide foams were viewed from scanning electron microscopy (SEM) measurements. The results revealed that the poly(ester‐amine salt) precursor containing TAP could successfully be converted to a crosslinked polyimide foam with relatively uniform cell structure. Also, the crosslinking of TAP improved the mechanical properties of foams in comparison with the non‐crosslinking systems. With increasing content of TAP, the dielectric constants of the polyimide foams decreased gradually. For the foam with TAP molar ratio at 15%, the dielectric constant was as low as 1.77 at the frequency of 10 kHz. Though the thermal resistance decreased slightly for crosslinked foams, the decomposition temperatures were still maintained above 520°C. Copyright © 2006 John Wiley & Sons, Ltd.     

Synthesis and properties of polyimide ionomers containing sulfoalkoxy and fluorenyl groups

A series of sulfopropylated and sulfobutylated polyimide copolymers containing fluorenyl groups, SPI‐4, were synthesized to investigate the effect of alkyl side chains on the properties (stability, mechanical strength, water uptake, and proton conductivity) of the polymimide electrolyte membranes. SPI‐4 showed much better hydrolytic stability (in 10% MeOH aq at 100 °C) than the main chain sulfonated polyimide, SPI‐1. Tough, flexible, and ductile membranes were obtained from these copolymers. At high relative humidity all the SPI‐4 membranes showed high mechanical properties (>34 MPa of the maximum stress) and proton conductivity (>0.1 Scm^?1). These properties are comparable to or even better than those of the perfluorosulfonic acid ionomer (Nafion 112). The new polyimide ionomers have proved to be a possible candidate as polymer electrolyte membrane for PEFCs and DMFCs. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4439–4445, 2005     

Synthesis and Crystal Structure of 4-Oxo-1,2,4-triazino[4,5-a]benzimidazole

The title compound 4-oxo-1,2,4-triazino[4,5-a]benzimidazole(C9H6N4O,Mr = 186.18) has been synthesized and structurally characterized by IR,NMR and single-crystal X-ray diffraction. The crystal belongs to monoclinic,space group P21/c,with a = 9.1530(18) ,b = 7.2260(14),c = 12.604(3) ,β = 106.92(3) ,V = 797.5(3) 3,Z = 4,Dc = 1.551 g/cm3,λ(MoKa) = 0.71073,F(000) = 384,μ(MoKa) = 0.109 mm-1,the final R = 0.0632 and wR = 0.1095. A total of 1444 unique reflections were collected,of which 767 with I > 2σ(I) were observed. The structure of the title compound is planar. In packing,the molecules are intersected to each other to form chains along three dimensions,together by intermolecular N-H…O and C-H…N hydrogen bonds. The whole structure is further stabilized by π…π interaction between two adjacent tricyclic ring systems,with the centroid-to-centroid distance of 3.369(4) .     

Preparation and properties of covalently cross-linked sulfonated copolyimide membranes containing benzimidazole groups

A series of sulfonated copolyimides containing benzimidazole groups (SPIs) were synthesized by random copolymerization of 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA), 2-(4-aminophenyl)-5-aminobenzimidazole (APABI), 4,4′-diaminodiphenyl ether-2,2′-disulfonic acid (ODADS) and 9,9-bis(4-aminophenyl)fluorene (BAPF) in m-cresol in the presence of benzoic acid and triethylamine at 180 °C for 20 h. Membranes with good mechanical properties were prepared by solution cast method. Proton exchange treatment resulted in ionic cross-linking and the membranes were further covalently cross-linked by treating them in polyphosphoric acid (PPA) at 180 °C for 6 h. The covalently cross-linked membranes displayed slightly lower ion exchange capacities (IECs) and proton conductivities than the corresponding covalently uncross-linked ones because small part of the sulfonic acid groups had been consumed during the cross-linking process. Fenton’s test (3% H₂O₂ + 3 ppm FeSO₄, 80 °C) revealed that benzimidazole groups played an important role in the radical oxidative stability of the membranes, while the cooperative effect of benzimidazole groups and covalent cross-linking led to much more significant enhancements in the radical oxidative stability of the membranes than each alone. The membrane 4 (ODADS/APABI/BAPF = 2/1/1, by mol), for example, after covalent cross-linking could maintain membrane form within 8 h measurement, which was much longer than that (3 h) before covalent cross-linking under the same conditions. The membrane 5 (ODADS/BAPF = 3/1, by mol) without benzimidazole groups, however, after covalent cross-linking started to break into pieces after 85 min measurement, which was only slightly longer than that (60 min) before cross-linking under the same conditions.     

Structure and properties of polyimide films during a far‐infrared‐induced imidization process

The conversion of poly(amic acid) into polyimide (PI) was achieved with far‐infrared radiation (FIR) and conventional thermal treatments. The structure and properties of PI films during different stages of imidization were studied with Fourier transform infrared spectroscopy, weight‐loss analysis during imidization, tensile property measurements, and dynamic mechanical thermal analysis. The effects of the imidization degree, postimidization, and solvent on the thermal and mechanical properties of PI films were quantitatively investigated. The corresponding structural changes were also examined. The experimental results showed that the imidization process proceeded more quickly and more completely in an FIR oven than in a conventional oven. A prolonged FIR treatment at a lower temperature (25–100 °C) accelerated the imidization process. The tensile stress–strain curves had a fanlike distribution with the development of the FIR imidization process and a fishtail distribution with conventional thermal imidization. During FIR imidization, the best tensile properties were obtained at 340 °C, and thermooxidative degradation occurred at about 420 °C. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2490–2501, 2004     

Structure of a poly(2,5‐benzimidazole)/phosphoric acid complex

As‐cast films of poly(2,5‐benzimidazole) exhibit uniplanar orientation in which the planes of the aromatic rings lie parallel to the film surface. Upon doping with phosphoric acid, the original crystalline order is lost, but the doped film can be stretched to produce films with uniaxial orientation. After thermal annealing at 540 °C, nine Bragg reflections are resolved in the fiber diagram, and these are indexed by an orthorhombic unit cell with the dimensions a = 18.1 Å, b = 3.5 Å, and c = 11.4 Å, containing four monomer units of two chains. The absence of odd‐order 00l reflections points to a 2₁ chain conformation, which is probably planar so that the aromatic units can be stacked along the b axis. The water and phosphoric acid contents of the crystalline structure cannot be determined exactly because of the presence of extensive amorphous regions that probably have different solvation. The best agreement between the observed and calculated intensities is for an idealized structure containing two phosphoric acids and two water molecules per unit cell. However, the phosphoric acid is probably present mainly in the form of pyrophosphoric acid and its higher oligomers. In addition, the X‐ray data are consistent with a more disordered structure containing chains with random (up and down) polarity and a lack of c‐axis registry. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2576–2585, 2004     

含苯并咪唑三足配体的金属配位化合物的合成及对碘的吸附性能

通过溶剂热法合成了2种新型金属配位化合物[Co₃(L1)₂Cl₆]_n(1)和{[Cu (L1)(SO₄)]·2CH₃OH}_n(2),其中L1=2,2′,2″-三(1-苯并咪唑基)乙基胺,是一种中性苯并咪唑三足有机配体。单晶X射线衍射分析表明化合物1是一维链状结构、化合物2是三维结构;红外光谱和粉末X射线衍射表征证实化合物1和2的纯度较高。热重分析表明化合物1和2是耐热性的材料。碘吸附实验表明,2个化合物对环己烷溶液中的碘和气态碘都有很高的捕获性能且具有良好的循环利用性。同时,它们的吸附动力学最符合准二级模型,吸附过程以化学吸附为主。吸附机理研究进一步表明化合物的结构中含有苯、氮杂环等活性基团,间接增加了与碘的吸附位点,提高了与碘的化学反应性和碘的去除率。     

含苯并咪唑三足配体的金属配位化合物的合成及对碘的吸附性能

通过溶剂热法合成了2种新型金属配位化合物[Co₃(L1)₂Cl₆]_n (1)和{[Cu(L1)(SO₄)]·2CH₃OH}_n (2),其中L1=2,2'',2″-三(1-苯并咪唑基)乙基胺,是一种中性苯并咪唑三足有机配体。单晶X射线衍射分析表明化合物1是一维链状结构、化合物2是三维结构;红外光谱和粉末X射线衍射表征证实化合物1和2的纯度较高。热重分析表明化合物1和2是耐热性的材料。碘吸附实验表明,2个化合物对环己烷溶液中的碘和气态碘都有很高的捕获性能且具有良好的循环利用性。同时,它们的吸附动力学最符合准二级模型,吸附过程以化学吸附为主。吸附机理研究进一步表明化合物的结构中含有苯、氮杂环等活性基团,间接增加了与碘的吸附位点,提高了与碘的化学反应性和碘的去除率。     

Synthesis,Crystal Structure of the Receptor Derived from Diethoxycarbonyl Glycoluril for Aromatic Amide Guest

The receptor derived from the diethoxycarbonyl glycoluril was synthesized and characterized by IR, ¹H NMR, MS techniques and X‐ray single crystal analysis. Single crystal X‐ray diffraction reveals that the receptor remains monomeric because of its bulky t‐Bu groups on the side walls. Its unique binding properties for aromatic amides were studied through ¹H NMR and IR techniques.     

Synthesis and properties of ultralow dielectric porous polyimide films containing adamantane

A series of novel ultralow dielectric porous polyimide (PI) films containing adamantane groups was prepared via the thermolysis of polyethylene glycol (PEG) oligomers mixed into PI matrix. Scanning electron microscopy results indicated that the porous PI films showed closed pores with an average diameter of 120 ± 10 nm. Good thermal properties with 5% weight loss temperature of 499 °C in air atmosphere and glass transition temperature in excess of 310 °C were shown for porous PI films. Notably, the ultralow dielectric constant of porous PI films with 1.85 at 1 MHz was obtained and revealed via broadband dielectric spectroscopy. The effects of the chemical structure of the PI matrix and PEG content on the decomposition behavior of PEG and the performance of porous films were investigated. Wide‐angle X‐ray diffraction results indicated that the PI matrix with large d‐spacing generated weaker interactions between the PEG and PI backbone than those of PI matrix with small d‐spacing. As a result, the PEG for the PI matrix with large d‐spacing was completely decomposed. As indicated by the broadband dielectric spectroscopy results, lower dielectric porous PI films were prepared when the PEG contents in the PI matrix increased from 0 to 20 wt %. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018 , 56, 549–559     

Mechanical properties of polyimide/multi-walled carbon nanotube composite fibers

A series of polyimide (PI)/multi-walled carbon nanotube (MWCNT) composite fibers were prepared by copolymerizing a mixture of monomers and carboxylic-functionalized MWCNTs, followed by dry-jet wet spinning, thermal imidization, and hot-drawing process. The content of the carboxylic groups of MWCNTs significantly increased when treated with mixed acid, whereas their length decreased with treatment time. Both the carboxylic content and length of MWCNTs influenced the mechanical properties of the composite fibers. Fiber added with 0.1 wt% MWCNTs treated for 4 h exhibited the best mechanical properties, i.e., 1.4 GPa tensile strength and 14.30% elongation at break, which were 51% and 32% higher than those of pure PI fibers, respectively. These results indicated that a suitable MWCNT content strengthened and toughened the resultant PI composite fibers, simultaneously. Moreover, raising draw ratio resulted in the increase of tensile strength and tensile modulus of the composite fibers.     

液晶性芳香酰胺化合物的合成

合成了一系列炖粹以酰胺基为中心桥键的刚性芳香酰胺小分子化合物，并对其作了表征，发现其中有些化合物具有液晶性。酰胺键之间能形成很强的分子间氢键，使芳香酰胺小分子化合物的熔点很高，难于形成液成液晶态。研究发现，如果在这类化合物的中心苯环上引入合适的取代基以减弱分子间氢键，同时引入合适的末端基时，则可使芳香酰胺化合物生成液晶相的能力增强。     

Development of novel cardo‐containing phenylethynyl‐terminated polyimide with high thermal properties

A phenylethynyl‐terminated reactive diluent [Card‐4‐phenylethynylphthalic anhydride (PEPA)], which contained fluorenyl cardo structures, was successfully synthesized and used as a modifier for flexible phenylethynyl‐terminated imide oligomer (PEI‐PEPA). The chemical structure, crosslink characterization, molecular weights, and thermal properties of the products were characterized. The imide systems with addition of 10, 20, 30, and 40 wt% Card‐PEPA to PEI‐PEPA (PEI‐PEPA‐Card) and their cured resin systems were prepared. The thermal curing behaviors of imide systems at different heating rates were analyzed by using differential scanning calorimetry. Thermal properties such as glass transition temperature (T_g) and char yield at 800°C of the resultant resin systems were studied by differential scanning calorimetry, dynamic mechanical analysis, and thermogravimetric analysis. The rheological properties were also investigated using a dynamic rheometry. These properties were found to be outstanding compared with pure PEI‐PEPA. The uncured imide systems exhibited lower T_g and lower isothermal viscosity with addition of Card‐PEPA. Furthermore, the T_g and char yield of the cured resin systems increased with addition of Card‐PEPA. The cured resin systems containing 40 wt% Card‐PEPA exhibited the highest T_g of 359°C and char yield at 800°C of 66.5%. Copyright © 2016 John Wiley & Sons, Ltd.     

Synthesis of diallyl‐containing polyimide and the effect of allyl groups on properties

A diallyl‐containing bisphenol, 1,1‐bis(3‐allyl‐4‐hydroxyphenyl)‐1‐(6‐oxido‐6H ‐dibenzo [c,e][1,2] oxaphosphorin‐6‐yl) ethane ( 1 ), was prepared by a two‐step procedure. Then, a diallyl‐containing diamine, 1,1‐bis(3‐allyl‐4‐(4‐aminophenoxy)‐phenyl)‐1‐(6‐oxido‐6H‐dibenzo [c,e][1,2] oxaphosphorin‐6‐yl)ethane ( 3 ), was prepared from the nucleophilic substitution of ( 1 ) with 4‐fluoronitrobenzene, followed by the reduction by Fe/HCl. A flexible polyimide ( 4 ) with curable diallyl linkages was prepared from the condensation of ( 3 ) and 4,4′‐oxydiphthalic anhydride in m‐cresol in the presence of isoquinoline. Curing polyimide ( 4 ) at 300 °C leads to thermosetting polyimide ( 5 ). We discussed the amounts of allyl group on T_g, coefficient of thermal expansion, and thermal stability of thermosetting polyimides, and found that thermal properties and dimensional stability of thermosetting polyimides increase with the amounts of cured allyl moieties. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 513–520     

AO-resistant properties of polyimide fibers containing phosphorous groups in main chains

A series of polyimide fibers containing phosphorus element derived from (3-aminophenyl) methyl phosphine oxide (DAMPO) diamine was exposed to an artificial atomic oxygen environment which simulated the space environment in low earth orbit (LEO). The mass loss, surface morphology, chemical composition, and mechanical properties of the fibers before and after atomic oxygen (AO) exposure were compared in detail with a blank sample. Results showed that the phosphor-containing fibers demonstrated lower mass change and less tensile strength reduction. SEM results showed that the fibers with phosphorous element had relatively dense surface after AO exposure. Meanwhile, XPS results indicated that a passivated phosphate layer, which could protect the following under-layer from attacking by AO, was formed on the surface of the fibers. These results indicated that the incorporation of diamine (DAMPO) into the main chains could protect the fibers for avoiding further erosion from AO exposure. Hence, the phosphor-containing PI fibers exhibits potential application in space fields.