Novel sulfonated poly (ether ether ketone)/silica coated carbon nanotubes high‐performance composite membranes for direct methanol fuel cell

The major risk of using carbon nanotubes (CNTs) to modify proton exchange membranes (PEMs) in fuel cells is possible short‐circuiting due to the excellent electrical conductivity of CNTs. In this article, silica‐coated CNTs (SiO₂@CNTs) were successfully prepared by a simple sol–gel process and then used as a new additive in the preparation of sulfonated poly (ether ether ketone) (SPEEK)‐based composite membranes. The insulated and hydrophilic silica coated on the surface of CNTs not only eliminated the risk of short‐circuiting, but also enhanced the interfacial interaction between CNTs and SPEEK, and hence promoted the homogeneous dispersion of CNTs in the SPEEK matrix. Moreover, compared to the methanol permeability of the pure SPEEK membrane (3.42 × 10^?7 cm² s^?1), the SPEEK/SiO₂@CNT composite membrane with a SiO₂@CNT loading of 5 wt% exhibits almost one order of magnitude decrease of methanol crossover, while the proton conductivity still remained above 10^?2 S cm^?1 at room temperature. The obtained results expose the possibility of SPEEK/SiO₂@CNT membranes to be served as high‐performance PEMs in direct methanol fuel cells. Copyright © 2015 John Wiley & Sons, Ltd.     

直接甲醇燃料电池中的膜性能比较

制备了磺化聚醚醚酮(SPEEK)和磺化酚酞型聚醚砜(SPES-C)两种质子交换膜,考察了其质子导电和阻醇性能.实验发现,两种新型质子交换膜具有一定的化学稳定性和质子电导率,尤其在高温下两种新膜的质子电导率与Nafion膜接近.两种新膜的甲醇透过系数要比Nafion膜的低1～2个数量级.分别以两种新型膜和Nafion115膜为电解质制备了直接甲醇燃料电池膜电极,讨论了膜材料的性能对直接甲醇燃料电池性能的影响.结果表明,膜材料的阻醇性越好,电池的开路电压越高;膜的电导率越高,在较高电流密度区域内电池的性能越好.     

Preliminary evaluation of sulfonated poly(ether ether ketone)/monoethanolamine/adipic acid composite membranes for direct methanol fuel cell applications

A series of sulfonated poly(ether ether ketone)/monoethanolamine/adipic acid (SPEEK/MEA/AA) composite membranes are prepared and investigated to assess their possibility as proton exchange membranes in direct methanol fuel cells (DMFCs). A preliminary evaluation shows that introducing MEA and AA into SPEEK matrix decreases the thermal stability of membrane. However, the degradation temperatures are still above 260 °C, satisfying the requirement for fuel cell operation. Compared with the pure SPEEK membrane, the composite membranes exhibit not only lower water uptake and swelling ratios but also better mechanical property and oxidative stability. Noticeably, the methanol diffusion coefficient of the composite membranes decrease significantly from 3.15 × 10^?6 to 0.76 × 10^?6 cm²/s with increasing MEA and AA content, accompanied by only a small sacrifice in proton conductivity. Although both the methanol diffusion coefficient and the proton conductivity of composite membranes are lower than those of pure SPEEK and Nafion® 117 membranes, their selectivity (conductivity/methanol diffusion coefficient) are higher. In addition, the composite membranes show excellent stability in aqueous methanol solution. The good thermal and chemical stability, low swelling ratio, excellent mechanical property, low methanol diffusion coefficient, and high selectivity make the use of these composite membranes in DMFCs quite attractive. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2871–2879, 2007     

SPEEK/PES-C、SPEEK/SPES-C共混质子交换膜研究

通过在磺化聚醚醚酮(SPEEK,DS=61.68%)中分别混入酚酞型聚醚砜(PES-C)、磺化酚酞型聚醚砜(SPES-C,DS=53.7%)制备出SPEEK/PES-C、SPEEK/SPES-C共混质子交换膜.结果表明,共混的两种聚合物之间均具有较好的相容性.PES-C、SPES-C的混入能有效降低膜的溶胀及甲醇透过,且随着共混量的增加,这种作用越趋明显.纯SPEEK膜在75℃左右溶解,而SPEEK/PES-C(30wt%)、SPEEK/SPES-C(30wt%)共混膜在80℃时溶胀度仅为22.5%、26.32%.在室温至80℃范围内,纯SPEEK及共混膜的甲醇透过系数都在10-7cm2.s-1数量级上,远小于Nafion115膜.在饱和湿度下,温度大于90℃时,SPEEK/PES-C(20wt%)共混膜电导率超过Nafion115膜;温度大于110℃时,SPEEK/SPES-C(30wt%)共混膜电导率与Nafion115膜相当,达到0.11S.cm-1.高电导率,低透醇系数以及明显提高了的可使用温度表明该类共混膜有望在DMFC中使用.     

含氨基磺化聚芳醚酮砜质子交换膜的制备与性能

通过四元缩聚的方法合成了带有氨基的磺化度可控的磺化聚芳醚酮砜共聚物(Am-SPAEKS). 采用红外光谱和核磁共振谱表征了Am-SPAEKS共聚物的结构. 该共聚物膜具有较好的热性能、尺寸稳定性、较高的质子传导率和阻醇能力. 在80℃时Am-SPAEKS-1膜的质子传导率达到0.0894 S/cm, 而其甲醇渗透系数在25℃时为0.24×10^-6 cm²/s, 低于相同温度下SPAEKS膜(0.87×10^-6 cm²/s)和Nafion膜(2×10^-6 cm²/s). 结果表明, Am-SPAEKS膜能够满足质子交换膜燃料电池(PEMFC)的使用要求.     

Sulfonated Poly(ether ether ketone) and Poly(ethylene glycol) Diacrylate Based Semi-Interpenetrating Network Membranes for Fuel Cells

Polymer electrolyte membranes are prepared from novel semi-interpenetrating polymer network material where the sulfonated poly (ether ether ketone) (SPEEK) is the linear polymer and the poly (ethylene glycol) diacrylate (PEGDA) is the cross-linking constituent. The semi-IPN is prepared by in situ polymerization of PEGDA in the presence of sulfonated poly (ether ether ketone). SPEEK is prepared by direct sulfonation of commercial PEEK (Gatone? 1100) by reported procedures. SPEEK with degree of sulfonation 63% (calculated from FT-NMR) is selected as the base membrane and different semi-IPN membranes were prepared by varying the PEGDA and SPEEK ratio. The degree of sulfonation of SPEEK and the formation of semi-IPN were confirmed by spectroscopy studies. The various semi-IPN membranes were characterized for ion-exchange capacity, water uptake, hydrolytic stability, proton conductivity and thermal stability for evaluating the suitability of these membranes for fuel cells. The proton conductivity of the membranes decreased with increasing PEGDA content. The Semi-IPN membranes exhibited conductivities (30°C) from 0.018 S/cm to 0.006 S/cm. These interpenetrating network membranes showed higher hydrolytic stability than the pure SPEEK membrane. This study shows that semi-IPN membranes based on PEGDA and SPEEK can be viable candidates for electrolyte membranes.     

Sulfonated poly(ether ether ketone) composite membranes based on amino-modified halloysite nanotubes that effectively immobilize phosphotungstic acid

In this work, we prepared amino-modified halloysite nanotubes (PEI-DHNTs) via the co-deposition of self-polymerized dopamine and polyethylenimine (PEI) on the surface of nanotubes, which was confirmed by X-ray photoelectron spectroscopy (XPS) and Thermogravimetric analysis (TGA). A series of composite proton exchange membranes (PEMs) were prepared by incorporating PEI-DHNTs and phosphotungstic acid (HPW) into sulfonated poly(ether ether ketone) (SPEEK). It was found that both PEI-DHNTs and HPW were well dispersed in the polymer matrix, exhibiting excellent filler-matrix compatibility. The composite membranes demonstrated enhanced proton conductivity, reaching as high as 0.078 S cm⁻¹ with 33.3 wt.% HPW loading, which was ~90% higher than that of SPEEK control membrane. Such improvement was mainly attributed to the strong acid–base pairs formed by PEI-DHNT with both SPEEK and HPW, which shortened proton hopping distance and created more continuous proton conduction pathways. Furthermore, the membrane conductivity remained almost constant after 1 year's immersion in liquid water, indicating the successful immobilization of HPW in the composite membranes.     

Sulfonated montmorillonite/sulfonated poly(ether ether ketone) (SMMT/SPEEK) nanocomposite membrane for direct methanol fuel cells (DMFCs)

A nanocomposite membrane of sulfonated montmorillonite/sulfonated poly(ether ether ketone) (SMMT/SPEEK) is proposed for direct methanol fuel cells (DMFCs). The SMMT is clay modified with silane of which the structure consists of a sulfonic acid group for proton conductivity improvement. The micro- and nano-scaled morphologies of the membranes perform the increase in inorganic aggregation with SMMT loading content as confirmed by SEM and AFM. The membrane stability, i.e., the liquid uptake in water and in methanol aqueous solution, as well as the mechanical stability increases with the SMMT loading content whereas thermal stability does not improve significantly. The methanol permeability reduction is obtained when the SMMT loading content increases for various methanol concentrations (1.5–4.5 M). A comparative study of the SPEEK nanocomposite membranes with SMMT and with pristine MMT shows fourfold proton conductivity enhancement after sulfonation. The DMFC single cell tests inform us that all nanocomposite membranes give the significant performance revealed by the plot of current density–voltage and power density.     

DMFC用PES/SPEEK共混阻醇质子交换膜

将磺化聚醚醚酮(SPEEK, 磺化度DS为68.3%)和聚醚砜(PES)两种聚合物共混制得PES/SPEEK共混膜. DSC研究表明两种聚合物之间具有较好的相容性, 因而共混膜均匀致密, 未发生大尺度相分离. PES的混入能有效降低膜的溶胀度及甲醇透过系数. 纯SPEEK 膜40 ℃时在1 mol•L−1甲醇水溶液中溶胀度达到160%, 45 ℃时就完全溶解, 而含30%(w)PES的共混膜在80 ℃时的溶胀度仅有15%. 室温下含20%−30%(w)PES的共混膜的甲醇透过系数为1×10−7 cm2•s−1左右, 比Nafion 115膜的透过系数小一个数量级. 尽管80 ℃下30%(w)PES/SPEEK共混膜的电导率与Nafion 115膜相当, 但由于共混膜的厚度比Nafion 115膜小1/3左右, 膜电阻较小, 因而其电池性能比Nafion 115膜的好.     

Polyaniline decorated graphene oxide on sulfonated poly(ether ether ketone) membrane for direct methanol fuel cells application

In direct methanol fuel cells (DMFC), methanol crossover is a major issue which has reduced the performance of polymer electrolyte membrane (PEM) for energy generation. In this study, graphene oxide (GO) and conductive polyaniline decorated GO (PANI-GO) were used as additives in fabrication of sulfonated poly(ether ether ketone) (SPEEK) nanocomposite PEM membrane to reduce methanol crossover. PANI-GO was synthesized by in situ polymerization method and the formation of PANI coated GO nanostructures was confirmed by surface morphology and crystallinity analysis. The membrane morphology and topography analysis confirmed that GO and PANI-GO were well dispersed on the surface of SPEEK membrane. 0.1 wt% PANI-GO modified SPEEK nanocomposite membrane exhibited the highest water uptake and ion exchange capacity of 40% and 1.74 meq g^?1, respectively. The oxidative stability of the nanocomposite membranes also improved. Lower methanol permeability of 4.33 × 10^?7 cm^?2S^?1 was noticed for 0.1 wt% PANI-GO modified SPEEK membrane. PANI-GO modified SPEEK membrane enhanced the proton conductivity, which was due to the existence of acidic and hydrophilic group present in PANI and GO. PANI-GO modified SPEEK membrane held higher selectivity of 1.94 × 10⁴ S cm^?3 s^?1. Overall, these studies revealed that PANI-GO modified SPEEK membrane is a potential material for DMFC applications.     

DMFCs用磺化聚醚醚酮/功能化二氧化硅复合质子交换膜

在磺化度(DS)为55.1%的磺化聚醚醚酮(SPEEK)中掺杂功能化二氧化硅(吸湿性SiO2溶胶及带有磺酸基团的二氧化硅(SiOx-S)粒子)制备SPEEK/SiO2和SPEEK/SiOx-S复合质子交换膜.SiO2和SiOx-S的掺杂能有效提高复合膜的抗溶胀、阻醇性能及高温低湿情况下的电导率.纯SPEEK膜在80℃溶胀为52.6%,而SiO2和SiOx-S掺杂量为15%的复合膜在此温度下分别仅有26.2%和27.3%的溶胀.在室温至80℃范围内,SPEEK/SiO2(20 wt%)和SPEEK/SiOx-S(20 wt%)复合膜的甲醇透过系数比Nafion115膜小近2个数量级.在120℃、相对湿度(RH)为40%情况下,SPEEK纯膜的电导率仅为2.6×10-4S.cm-1,SPEEK/SiO2(20 wt%)复合膜约为2.0×10-3S.cm-1,而SPEEK/SiOx-S(20 wt%)复合膜高达1.0×10-2S.cm-1,与Nafion115相当.SPEEK/SiO2(20 wt%)和SPEEK/SiOx-S(20 wt%)2种复合膜的尺寸稳定性较高,膜电极无催化剂与膜分离现象,其DMFCs单电池性能好于SPEEK膜.     

Crosslinking of sulphonated poly (ether ether ketone) using aromatic bis(hydroxymethyl) compound

2,6-Bis(hydroxymethyl)-4-methyl phenol and 1,4-bis(hydroxymethyl) benzene have been used as crosslinkers in sulphonated poly (ether ether ketone) (SPEEK DS 65%, IEC 1.84 mequiv./g) for the preparation of proton exchange membranes (PEMs). Crosslinking of SPEEK has been achieved by thermally activated bridging of the polymer chain with the hydroxymethyl group of crosslinker through condensation reaction with sulphonic acid group. The physico-chemical properties of uncrosslinked and crosslinked membrane were evaluated in terms of ion exchange capacity (IEC), water uptake, ionic conductivity and mechanical properties. The crosslinked membrane showed controlled swelling, ionic conductivity of 25–50 mS/cm at 80 °C and good mechanical properties. The chemical stability of the crosslinked membranes was studied by Fenton's test. The % loss in weight and changes in physico-chemical properties of the treated membranes were determined.     

Hybird Membrane with High Proton Conductivity and Selectivity Based on SPEEK for Direct Methanol Fuel Cells

Composite membranes based on sulfonated silica/sulfonated poly(ether ether ketone)(SPEEK) were prepared by means of sol-gel method so as to gain a high conductivity and reasonable methanol permeability.The sulfonated silica is generated in situ via the hydrolysis of sulfonated 3-anminopropyl triethoxysilane(KH550) synthesized newly from 3-aminopropyl triethoxysilane and 1,4-butane sultone.The membrane with a silica mass fraction of 5% exhibits a conductivity of 0.187 S/cm at 80 °C and a methanol coefficient with 9.72×10-7 cm2/s.The composite membranes show improved condutive ability and better selectivity that can be promisingly used in direct methanol fuel cell.     

全钒液流电池用磺化聚醚醚酮/锂皂石质子膜的结构及性能

通过溶液流延法制备了磺化聚醚醚酮/锂皂石(SPEEK/Lap)复合膜, 对其物理化学性质、 机械性能、 化学稳定性及单电池性能进行了测试. 在SPEEK基质中引入的Lap有效改善了复合膜的质子传导率、 溶胀率和机械性能. 当Lap添加量(质量分数)从0.2%增到1.5%时, 复合膜的质子传导率随之增加(19.9~23.6 mS/cm). SPEEK/Lap-0.2复合膜的自放电时间为57.2 h, 是Nafion 117膜的2.4倍和纯SPEEK膜的1.5倍. 在80 mA/cm ²电流密度下, SPEEK/Lap-0.2复合膜的电压效率(VE, 86.5%)和能量效率(EE, 84.0%)明显高于Nafion 117膜(VE: 83.8%, EE: 80.7%)和纯SPEEK膜(VE: 81.4%, EE: 78.9%). 同时, SPEEK/Lap-0.2复合膜经100次充放电循环测试后具有良好的循环稳定性和结构稳定性.     

Characterization and performance of proton exchange membranes for direct methanol fuel cell: Blending of sulfonated poly(ether ether ketone) with charged surface modifying macromolecule

Modification of sulfonated poly(ether ether ketone) (SPEEK) membrane was attempted by blending charged surface modifying macromolecule (cSMM). The modified membrane was tested for direct methanol fuel cell (DMFC) application; i.e. a SPEEK/cSMM blend membrane was compared to a SPEEK membrane and a Nafion 112 membrane for the thermal and mechanical stability, methanol permeability, and proton conductivity. Thermal and mechanical stability of the blended membrane were slightly reduced from the SPEEK membrane but still higher than the Nafion 112 membrane. The blend membrane was found to be promising for DMFC applications because of its lower methanol diffusivity (2.75 × 10⁻⁷ cm² s⁻¹) and higher proton conductivity (6.4 × 10⁻³ S cm⁻¹), than the SPEEK membrane. A plausible explanation was given for the favorable effect of cSMM blending.     

含杂萘联苯结构聚合物膜的直接甲醇燃料电池性能

质子交换膜是直接甲醇燃料电池(DMFC)的关键组成部分. 通过磺化制备了磺化杂萘联苯聚醚酮(SPPEK)、磺化杂萘联苯聚醚砜(SPPES)和磺化杂萘联苯聚醚砜酮(SPPESK)三种含杂萘联苯结构的新质子交换膜, 测试了其热稳定性、质子导电性和甲醇透过性能. SPPESK的热分解温度比相近离子交换容量(IEC)的SPPEK和SPPES约低100 ℃, 三种膜均具有良好的导电和阻醇性能; 分别以三种膜为电解质组装DMFC考察了其性能, DMFC的开路电压随膜的阻醇性的提高而增大, 三种膜的开路电压均高于Nafion115膜, 但在较高电流密度的区域三种新膜的性能均比Nafion115膜差.     

自交联型磺化聚醚醚酮质子交换膜的合成

以含3,3'-二烯丙基双酚 A 结构单元的聚醚醚酮为基膜材料, 通过自由基加成反应在取代基上引入磺酸基团, 合成侧链型磺化聚醚醚酮(SPEEK)质子交换膜. 用傅里叶变换红外(FTIR)光谱、 核磁共振氢谱(¹H NMR)、 热重分析(TG)和扫描电子显微镜(SEM)等方法对 SPEEK 的结构进行表征. 实验结果表明, 巯基丙磺酸被接枝在聚醚醚酮侧基上, SPEEK 膜具有明显的亲水疏水微相分离形貌, 磺酸基团相互聚集形成离子通道. SPEEK 膜离子交换容量为 2.12 mmol/g, 钒离子渗透率为 1.54×10^-6 cm²/min, 低于Nafion117 膜的钒离子渗透率, 阻钒能力优于 Nafion117 膜. 以 SPEEK-4 膜组装电池的自放电时间约为130 h, 长于 Nafion117 膜的 66 h. 电池充放电循环 50 次, SPEEK-4 膜的库仑效率、 电压效率和能量效率没有明显降低, 显示出良好的稳定性.     

Sulfonated poly(ether ether ketone)/polyaniline composite proton-exchange membrane

Sulfonated poly(ether ether ketone) (PEEK) was prepared by sulfonation of commercial Victrex^@ PEEK and degree of sulfonation was found to be about 44.5% by ¹H NMR. Sulfonated PEEK/polyaniline composite membranes, in order to prevent methanol crossover, were prepared by chemical polymerization of a thin layer of polyaniline (PANI) in the presence of a high oxidant concentration on a single face modification. FTIR and PANI coating density studies confirmed the loading of PANI in sulfonated PEEK membrane matrix. PANI composite membranes with different polymerization time were prepared and subjected to thermogravimetric analysis as well as electrochemical and methanol permeability study to compare with sulfonated PEEK and Nafion 117 membrane. Ion-exchange capacity, water uptake, proton transport numbers and proton conductivities for different PANI composite sulfonated PEEK (SPEEK) membranes were found to be dependent on the coating density of the PANI in the membrane matrix and were slightly lower than that of Nafion 117 membrane. Methanol permeability of these membranes (especially SPEEK/PANI-1.5) was about four times lower than Nafion 117 membrane. Among the all SPEEK membranes synthesized in this study, SPEEK-1.5 appears to be more suitable for direct methanol fuel cell (DMFC) application considering optimum physicochemical and electrochemical properties, thermal stability as well as very low methanol permeability. Above all, the cost-effective and simple fabrication technique involved in the synthesis of such composite membranes makes their applicability quite attractive.     

不同磺化度下的磺化聚醚醚酮对全钒储能液流电池性质影响的研究

本文报道了采用浓硫酸作为磺化剂,成功合成了不同磺化度下的聚醚醚酮(PEEK)膜,并深入研究了磺化条件包括磺化时间和磺化剂的用量对所获薄膜性能的影响,获得了在不同磺化度（DS）下SPPEK膜的离子交换容,含水率,机械性能,质子电导率等参数,特别测定了在全钒液流电池工作条件下钒离子(Ⅳ)渗透率,首次为该类液流储能电池使用价廉质优的质子交换膜提供了基础实验数据。室温条件下的实验结果如下：1）磺化12小时后,膜的磺化度46%,含水量为28%,钒离子(Ⅳ)选择性最佳（钒离子渗透率为1.2×10-7 cm2/min-1,是Nafion117 (2.9×10-6 cm2/min-1)的1/24）,其质子电导率只有0.02 S/cm;2）磺化96小时其磺化度达79%的膜,质子电导率达0.16 S/cm,是Nafion117 (0.10S/cm) 的1.6倍, 但其机械性能最差;3）与Nafion117膜相比,磺化在36到48小时的SPPEK膜其机械力学性能好,薄膜的钒离子渗透率、离子交换容IEC、质子导电率和含水率高,且对钒离子的选择性佳,尤其价格仅为Nafion膜的1/13,是理想的Nafion膜的代替物,可望直接应用于全钒氧化还原液流（VRB）电池中。本文还讨论了磺化时间和不同磺化剂量对膜的性质的影响。     

Modification of sulfonated poly(ether ether ketone) with phenolic resin

Soluble phenol formaldehyde resin containing hydroxymethyl groups has been used to modify sulfonated poly(ether ether ketone) (SPEEK). Modification has been carried out with films containing both the polymers and using dimethyl formamide (DMF) as casting solvent at various temperatures under reduced pressure. Associated solvent and the hydrogen‐bonded by‐product dimethyl amine (DMA) were removed through mild alkali–acid–water treatment. Cured and treated films show good and consistent mechanical properties, water uptake (22–25%), ion‐exchange capacity (1.1–1.5 meq/g) and proton conductivity (125–150 mS/cm) at 30°C and hold promise for application in fuel cells, as indicated by a polarization study in a fuel cell test station. Copyright © 2007 John Wiley & Sons, Ltd.