Au/PZT/BIT/p-Si异质结的制备与性能研究

采用脉冲激光沉积(PLD)工艺,制备了以Bi₄Ti₃O₁₂(BIT)为过渡阻挡层的Au/PZT/BIT/p-Si异质结.研究了BIT铁电层对Pb(Zr_0.52Ti_0.48)O₃(PZT)薄膜晶相结构、铁电及介电性能的影响,对Au/PZT/BIT/p-Si异质结的导电机制进行了讨论.氧气氛530℃淀积的PZT为多晶铁电薄膜,与直接淀积在Si基片上相比,加入BIT铁电层后PZT铁 关键词： 铁电薄膜 异质结构 脉冲激光沉积(PLD)     

温度对ZnO/Al2O3(0001)界面的吸附、扩散及生长初期模式的影响

构建了一个ZnO沉积在α-Al₂O₃(0001)表面生长初期的模型，采用基于密度泛函理论的平面波超软赝势法进行了动力学模拟.发现在400，600和800℃的条件下界面原子有不同的扩散能力，因此温度对ZnO/α-Al₂O₃(0001)表面界面结构以及ZnO薄膜生长初期模式有决定性的影响.在整个ZnO吸附生长过程中，O原子的扩散系数大于Zn原子的扩散系数，O原子的层间扩散对薄膜的均匀生长起着重要作用.进一步从理论计算上证实了ZnO在蓝宝石(0001)上两种生长模式的存在，400℃左右生长模式主要是Zn螺旋扭曲生长，具有Zn六角平面对称特征，且有利于Zn原子位于最外表面.600℃左右呈现为比较规则的层状生长，且有利于O原子位于最外表面.模拟观察到在ZnO薄膜临近Al₂O₃基片表面处，Zn的空位缺陷明显多于O的空位缺陷. 关键词： 扩散 薄膜生长 2O₃(0001)')" href="#">α-Al₂O₃(0001) ZnO     

前驱液成分对TFA-MOD法制备YBa2Cu3O7-x薄膜超导性能的影响

采用三氟乙酸盐-金属有机沉积法(TFA-MOD)在铝酸镧单晶基体上制备了YBa₂Cu₃O_7-x (YBCO)超导薄膜.通过改变前驱液的成分,研究了金属元素的不同化学计量比对YBCO薄膜的结构和性能的影响.结果表明,按照钇盐Y(CH₃COO)₃与钡盐Ba(CH₃COO)₂的比例为Y ∶Ba=1 ∶1.5时所制备的YBCO薄膜的临界电流密度比严 关键词： 三氟乙酸盐-金属有机沉积 钇钡铜氧薄膜 前驱液成分 磁通钉扎     

Al2O3绝缘栅AlGaN/GaN MOS-HEMT器件温度特性研究

采用原子层淀积(ALD)实现了10nm Al₂O₃为栅介质的高性能AlGaN/GaN金属氧化物半导体高电子迁移率晶体管(MOS-HEMT). 通过对MOS-HEMT器件和传统MES-HEMT器件室温特性的对比,验证了新型MOS-HEMT器件饱和电流和泄漏电流的优势. 通过分析MOS-HEMT器件在30—180℃之间特性的变化规律,与国内报道的传统MES-HEMT器件随温度退化程度对比,得出了器件饱和电流和跨导的退化主要是由于输运特性退化造成的,证明栅介质减小了引 关键词： 原子层淀积 AlGaN/GaN MOS-HEMT器件 温度特性     

ZnSb掺杂的Ge2Sb2Te5薄膜的相变性能研究

本文采用双靶(ZnSb靶和Ge₂Sb₂Te₅靶)共溅射制备了系列ZnSb掺杂的Ge₂Sb₂Te₅(GST)薄膜. 利用X射线衍射、透射电子显微镜、原位等温/变温电阻测量、X射线光电子能谱等测试研究了薄膜样品的非晶形态、电学及原子成键特性. 利用等温原位电阻测试表明ZnSb掺杂的Ge₂Sb₂Te₅薄膜具有更高的结晶温度. 采用Arrhenius 公式计算发现ZnSb掺杂的Ge₂Sb₂Te₅薄膜的十年数据保持温度均高于传统的Ge₂Sb₂Te₅薄膜的88.9℃. 薄膜在200, 250, 300和350℃ 下退火后的X射线衍射图谱表明ZnSb的掺杂抑制了Ge₂Sb₂Te₅薄膜从fcc态到hex态的转变. 通过对薄膜的光电子能谱和透射电镜分析可知Zn, Sb, Te原子之间键进行重组, 形成Zn–Sb 和Zn–Te 键, 且构成非晶物质存在于晶体周围. 采用相变静态检测仪测试样品的相变行为发现ZnSb掺杂的Ge₂Sb₂Te₅薄膜具有更快的结晶速度. 特别是(ZnSb)_24.3(Ge₂Sb₂Te₅)_75.7薄膜, 其结晶温度达到250℃, 十年数据保持温度达到130.1℃, 并且在70 mW激光脉冲功率下晶化时间仅～64 ns, 远快于传统Ge₂Sb₂Te₅薄膜的晶化时间～280 ns. 以上结果表明(ZnSb)_24.3(Ge₂Sb₂Te₅)_75.7薄膜是一种热稳定性好且结晶速度快的相变存储材料.     

Al2O3绝缘层的AlGaN/GaN MOSHEMT器件研究

在研制AlGaN/GaN HEMT器件的基础上,采用ALD法制备了Al₂O₃ AlGaN/GaN MOSHEMT器件.通过X射线光电子能谱测试表明在AlGaN/GaN异质结材料上成功淀积了Al₂O₃薄膜.根据对HEMT和MOSHEMT器件肖特基电容、器件输出以及转移特性的测试进行分析发现：所制备的Al₂O₃薄膜与AlGaN外延层间界面态密度较小,因而MOSHEMT器件呈现出较 关键词： 2O₃')" href="#">Al₂O₃ ALD GaN MOSHEMT     

低电场下LiNbO3薄膜在非晶衬底上的取向生长

报道了外加低电场和衬底温度对脉冲激光淀积法制备的LiNbO₃薄膜取向的影响.在衬底温度为600℃和外加电场为7V/cm的条件下，在石英玻璃等非晶态衬底上获得了完全(001)取向的LiNbO₃薄膜.在对具有自发极化的LiNbO₃在电场作用下成核生长机制和温度对LiNbO₃自发极化强度的影响进行分析的基础上，给出了低电场诱导铁电薄膜取向生长的物理依据. 关键词：     

低温制备SnO2电子传输层用于钙钛矿太阳能电池

SnO₂具有光稳定性优异、可低温溶液制备等优点被视为电子传输层的优异材料之一,广泛应用于高效稳定的平面异质结钙钛矿太阳能电池.本文在低温(150℃)下采用旋涂工艺制备SnO₂电子传输层,探究了SnO₂前驱体溶液不同浓度(SnO₂质量分数为2.5%—10.0%)下制备的SnO₂电子传输层对钙钛矿太阳能电池性能的影响.通过对SnO₂薄膜进行扫描电子显微镜(SEM)、紫外-可见光(UV-Vis)吸收光谱和透射光谱分析,发现基底的覆盖率、透光率和SnO₂薄膜的带隙随SnO₂前驱液浓度的增加而增大;通过对SnO₂/钙钛矿(MAPbI₃)薄膜进行SEM、UV-Vis、X-射线衍射(XRD)、稳态光致发光(PL)光谱分析,发现SnO₂胶体分散液浓度为7.5%制备的SnO₂层上沉积的MAPbI₃的粒径最大,结晶度最好,具...     

La0.5Sr0.5CoO3薄膜的外延生长及其机理研究

利用脉冲激光制膜法,在多种衬底和温度条件下,系统研究了La_0.5Sr_0.5CoO₃(LSCO)薄膜的结构和外延生长特性,在LaAlO₃,SrTiO₃和MgO衬底上实现了LSCO薄膜的外延生长.外延生长的薄膜具有低的电阻率和金属性导电特征.研究表明,外延生长的最佳温度范围为700—800℃,最佳衬底为LaAlO₃.并着重探讨了衬底材料和淀积温度等多种因素对LSCO薄膜的生长与性 关键词：     

TiO2和SiO2薄膜应力的产生机理及实验探索

对最常用的TiO₂和SiO₂薄膜应力, 包括应力模型、应力测试方法和不同实验条件下的应力测试结果作了研究.基于曲率法模型，对TiO₂和SiO₂单层膜和多层膜进行了实验测试，得到了一些有价值的结果，特别是离子辅助淀积和基板温度等工艺参数对薄膜应力的影响.提出了薄膜聚集密度是应力的重要因素，低聚集密度产生张应力，而高聚集密度产生压应力.在多层膜中通过调节工艺参数，适当地控制张应力或压应力，可使累积应力趋向于零. 关键词： 薄膜应力 离子辅助淀积 聚集密度     

退火对Mn和N共掺杂的Zn0.88Mn0.12O:N薄膜特性的影响

以NH₃为掺N源,采用电子束反应蒸发技术生长了Mn和N共掺杂的Zn_1-xMn_xO:N薄膜,生长温度为300℃,然后在O₂气氛中400℃退火0.5 h.X射线衍射测量表明,Zn_0.88Mn_0.12O(Mn掺杂)薄膜或Zn_0.88Mn_0.12O:N(Mn和N共掺杂)薄膜仍具有单一晶相纤锌矿结构,未检测到杂质相 关键词： ZnO薄膜 Mn和N共掺杂 电学特性 磁特性     

两种不同(Ba,Sr)TiO3薄膜介电-温度特性的研究

研究并比较了两种不同(Ba_0.5,Sr_0.5)TiO₃(BSTO)薄膜介电-温度特性.采用脉冲激光沉积技术在Pt/Ti/SiO₂/Si(100)衬底上制备BSTO薄膜，发现制备条件的不同，可以得到介电性质完全不同的BSTO薄膜.在550℃和氮气氛下制备的BSTO薄膜在常温下具有很高的介电常数，在10kHz下，超过2500，并在200K温度以上介电常数基本不变.它的一些电学性质不同于在正常条件(650℃和氧气氛下)制得的BSTO薄膜，而类似于目前广泛报道的巨介电常数材料如CaCu_３Ti_４O₁₂.两种薄膜介电性质测试结果表明: 氧气氛下制备的BSTO薄膜呈现铁电-顺电相变，符合居里-外斯定律；低温氮气氛下制备的BSTO薄膜，介电弛豫时间和温度的关系符合德拜模型，是热激发弛豫.文中给出了产生这种介电特性的初步解释. 关键词： 薄膜 脉冲激光沉积 介电弛豫     

Effects of O2/Ar ratio and annealing temperature on electrical properties of Ta2O5 film prepared by magnetron sputtering

The effects of the oxygen-argon ratio on electric properties of Ta2O5 film prepared by radio-frequency magnetron sputtering were investigated.The Ta2O5 partially transforms from the amorphous phase into the crystal phase when annealing temperatures are 800℃ or higher.The lattice constant of Ta2O5 decreases with the increase of the O2/Ar ratio,which indicates that oxygen gas in the working gas mixture contributes to reducing the density of oxygen vacancies during the deposition process.For the films deposited in working gas mixtures with different O2/Ar ratios and subsequently annealed at 700℃,the effective dielectric constant is increased from 14.7 to 18.4 with the increase of the O2/Ar ratio from 0 to 1.Considering the presence of an SiO2 layer between the film and the silicon substrate,the optimal dielectric constant of Ta2O5 film was estimated to be 31.Oxygen gas in the working gas mixture contributes to reducing the density of oxygen vacancies,and the oxygen vacancy density and leakage current of Ta2O5 film both decrease with the increase of the O2/Ar ratio.The leakage current decreases after annealing treatment and it is minimized at 700℃.However,when the annealing temperature is 800℃ or higher,it increases slightly,which results from the partially crystallized Ta2O5 layer containing defects such as grain boundaries and vacancies.     

超高温度系数V0.97W0.03 O2多晶薄膜的制备研究

将V₂O₅粉体与WO₃粉体均匀混合并压制成靶，用离子束增强沉积加后退火技术在SiO₂衬底上制备掺钨VO₂多晶薄膜.X射线衍射表明，薄膜取向单一，为VO₂结构的［002］相,晶格参数d比VO₂粉晶增大约0.34%；薄膜从半导体相向金属相转变的相变温度约28；室温(300 K)时的电阻-温度系数(TCR)可大于10%/K，是目前红外热成像薄膜TCR的四倍.W离子的半径大于V离子的半径，W的掺入在薄膜中引入了张应力,使薄膜相变温度降低到室温附近，是IBED V_0.97W_0.03O₂薄膜的室温电阻温度系数提高的原因. 关键词： 二氧化钒薄膜 薄膜掺杂 离子束增强沉积     

Infrared Faraday rotation on thin film In2O3+SnO2 semiconductors

Two sets of thin film sputtered In₂O₃+SnO₂ samples, one prepared in argon atmosphere with oxigen, and the other without, at various temperatures between 100°C and 250°C, have been studied by measuring their Farday rotation from optical to infrared frequencies, as well as their optical transmission spectra. The effect of the different treatments on the carrier densities and mobilities, show values that grow with deposition temperature. This can be attributed to an increase in the number of oxygen vacancies. On the other hand, the presence of O₂ in the atmosphere during deposition, leads to smaller values at the same temperatures, compared to those obtained in samples prepared in atmosphere without oxygen, seemingly as a result of the filling of the vacancies.     

The structure and optical characters of the ZnO film grown on GaAs/Al2O3 substrate

In this paper ZnO films are grown on GaAs/Al₂O₃ substrates at different temperature by metal-organic chemical vapor deposition (MOCVD). The GaAs/Al₂O₃ substrates are formed by depositing GaAs layer (∼35 nm) on the Al₂O₃ substrate. The results of X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) demonstrate that most of the Ga and As atoms form Ga-As bond and the GaAs layer does not present any orientation. The characters of the ZnO films grown on GaAs/Al₂O₃ substrates are investigated by XRD, photoluminescence (PL), atomic force microscopy (AFM) and Raman scattering. Compared with ZnO film grown on Al₂O₃ substrate, ZnO film prepared by our fabrication scheme has good crystal and optical quality. Meanwhile its grain size becomes bigger according to the AFM image. Raman analysis indicates that the intrinsic defects and the in-plane tensile stress are obviously reduced in ZnO/GaAs/Al₂O₃ samples.     

Enhancing the thermal conductivity of polymer-assisted deposited Al2O3 film by nitrogen doping

<正>Polymer-assisted deposition technique has been used to deposit Al₂O₃ and N-doped Al₂O₃（AlON） thin films on Si（100） substrates.The chemical compositions,crystallinity,and thermal conductivity of the as-grown films have been characterized by X-ray photoelectron spectroscopy（XPS）,X-ray diffraction（XRD）,and 3-omega method,respectively. Amorphous and polycrystalline Al₂O₃ and AlON thin films have been formed at 700℃and 1000℃.The thermal conductivity results indicated that the effect of nitrogen doping on the thermal conductivity is determined by the competition of the increase of Al-N bonding and the suppression of crystallinity.A 67%enhancement in thermal conductivity has been achieved for the samples grown at 700℃,demonstrating that the nitrogen doping is an effective way to improve the thermal performance of polymer-assisted-deposited Al₂O₃ thin films at a relatively low growth temperature.     

High temperature thermoelectric properties of highly c-axis oriented Bi2Sr2Co2Oy thin films fabricated by pulsed laser deposition

High-temperature thermoelectric transport property measurements have been performed on the highly c-axis oriented Bi2Sr2Co20v thin films prepared by pulsed laser deposition on LaA1Oa （001）. Both the electric resistivity p and the seebeck coefficient S of the film exhibit an increasing trend with the temperature from 300 K-1000 K and reach up to 4.8 m. cm and 202 V/K at 980 K, resulting in a power factor of 0.85 mW/mK which are comparable to those of the single crystalline samples. A small polaron hopping conduction can be responsible for the conduction mechanism of the film at high temperature. The results demonstrate that the Bi2Sr2Co2Oy thin film has potential application has high temperature thin film thermoelectric devices,     

Growth of SiO2 on InP substrate by liquid phase deposition

We have grown silicon dioxide (SiO₂) on indium phosphorous (InP) substrate by liquid phase deposition (LPD) method. With inserting InP wafer in the treatment solution composed of SiO₂ saturated hydrofluorosilicic acid (H₂SiF₆), 0.1 M boric acid (H₃BO₃) and 1.74 M diluted hydrochloric acid (HCl), the maximum deposition rate and refractive index for the as-grown LPD-SiO₂ film were about 187.5 Å/h and 1.495 under the constant growth temperature of 40 °C. The secondary ion mass spectroscope (SIMS) and energy dispersive X-ray (EDX) confirmed that the elements of silicon, oxygen, and chloride were found in the as-grown LPD-SiO₂ film. On the other hand, the effects of treatment solution incorporated with the hydrogen peroxide (H₂O₂) that can regulate the concentration of OH⁻ ion were also shown in this article. The experimental results represented that the deposition rate decreases with increasing the concentration of hydrogen peroxide due to the reduced concentration of SiO₂ saturated H₂SiF₆ in treatment solution.     

Growth and characterization of Y2O3 thin films

Y₂O₃ thin films were grown on silicon (1 0 0) substrates by pulsed-laser deposition at different substrate temperatures and O₂ pressures. The structure and composition of films are studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The Y₂O₃ thin films deposited in vacuum strongly oriented their [1 1 1] axis of the cubic structure and the film quality depended on the substrate temperature. The magnitude of O₂ pressure obviously influences the film structure and quality. Due to the silicon diffusion and interface reaction during the deposition, yttrium silicate and SiO₂ were formed. The strong relationship between composition and growth condition was discussed.