Low temperature synthesis of nanosized ZnNb<Subscript>2</Subscript>O<Subscript>6</Subscript> photocatalysts by a citrate complex method

Nanosized ZnNb₂O₆ photocatalysts (band gaps ~4.0 eV) were successfully synthesized via a citrate complex method. Their particle sizes ranged from 50 to 150 nm. The result of Mott–Schottky measurement revealed that the flat-band potential of ZnNb₂O₆ was ca. −1.3 V versus Ag/AgCl at pH 6.6. The photocatalytic activities of the samples for the degradation of methyl orange were evaluated under UV-light (λ = 254 nm). It was found that the sample obtained at 850 °C showed the highest photocatalytic activity due to its opportune crystallinity and surface area. Furthermore, ·OH radicals were detected as the major oxidation agents responsible for the decomposition of methyl orange.     

Effect of the nature of anions of aluminum salts used to synthesize a precursor of the Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-ZrO<Subscript>2</Subscript> ceramics on the stabilization of the tetragonal modification of zirconium dioxide

Samples of a precursor for an aluminum oxide ceramics reinforced with zirconium oxide were synthesized by hydrolysis of various aluminum salts in the presence of a ZrO₂ sol under conditions of urea decomposition at 90°C and pH < 4 maintained, with hydrolysis products deposited onto the surface of ZrO₂ sol particles. It was found that the nature of a salt anion affects the interaction of hydrolysis products of the aluminum cation with the surface of ZrO₂ sol particles. The structure of products formed in thermal treatment of samples of a precursor for Al₂O₃-ZrO₂ (T = 1250°C) was characterized by X-ray phase analysis and scanning electron microscopy. The phase transition temperatures of the oxides Al₂O₃ and ZrO₂ contained in the precursor were estimated using the results of thermal analysis of the samples in the temperature range 20–1300°C.     

Synthesis and colour properties of pigments based on terbium-dopped Mg<Subscript>2</Subscript>SnO<Subscript>4</Subscript>

The main aim of this work was to synthesize the magnesium orthostannate doped by terbium cations and tested whether these materials can be used for colouring of the different materials, e.g. organic binder and ceramic glazes. Initial composition of pigments was counted according the general formula 2MgO(1 − x)SnO₂–xTbO₂, where values of x varied from 0.1 to 0.5 in 0.1 steps. The simultaneous TG/DTA measurements of mixture containing tin oxide, magnesium carbonate hydroxide and terbium oxide showed that the formation of a new compound started at temperature 1,029 °C, but single-phase system was not prepared. Granulometric compositions of samples that were prepared by calcining at temperatures 1,300–1,400 °C are characterized by values of median (d ₅₀) in range 4–8 μm. The calcining temperature 1,500 °C caused the increase of the particle sizes at around 12 μm. The composition of sample 2MgO–1.5SnO₂–0.5TbO₂ and heating temperature 1,500 °C are the most suitable conditions for preparation of colourfully interesting pigment that can be recommended also for colouring of ceramic glazes. Especially, for colouring of decorative lead containing glaze G 07091 containing 5 wt% of PbO and 8 wt% of Al₂O₃.     

Preparation of novel visible-light-driven In<Subscript>2</Subscript>O<Subscript>3</Subscript>–CaIn<Subscript>2</Subscript>O<Subscript>4</Subscript> composite photocatalyst by sol–gel method

Novel visible-light-activated In₂O₃–CaIn₂O₄ photocatalysts were developed in this paper through a sol–gel method. The photocatalytic activities of In₂O₃–CaIn₂O₄ composite photocatalysts were investigated based on the decomposition of methyl orange under visible light irradiation (λ > 400 nm). The obtained samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrum (EDS), X-ray photoelectron spectroscopy (XPS) and UV–vis diffused reflectance spectroscopy (DRS). The results revealed that the In₂O₃–CaIn₂O₄ composite samples with different In₂O₃ and CaIn₂O₄ content can be obtained by controlling the synthesis temperature, and the composite photocatalysts extended the light absorption spectrum toward the visible region. The photocatalytic tests indicated that the composite samples demonstrated high visible-light activity for decomposition of methyl orange. The significant enhancement in the In₂O₃–CaIn₂O₄ photo-activity under visible light irradiation can be ascribed to the efficient separation of photo-generated carriers in the In₂O₃ and CaIn₂O₄ coupling semiconductors.     

Thermoanalytical study of precursors for In<Subscript>2</Subscript>S<Subscript>3</Subscript> thin films deposited by spray pyrolysis

Thermal decomposition of precursors for In₂S₃ thin films obtained by drying aqueous solutions of InCl₃ and SC(NH₂)₂ at the In:S molar ratios of 1:3 (1) and 1:6 (2) was monitored by simultaneous TG/DTA/EGA-FTIR measurements in the dynamic 80%Ar + 20%O₂ atmosphere. XRD and FTIR were used to identify the dried precursors and products of the thermal decomposition. The precursors 1 and 2 are complex compounds, while in 2 free SC(NH₂)₂ is also present. The thermal degradation of 1 and 2 in the temperature range of 30–900 °C consists of four mass loss steps, the total mass loss being 89.1 and 78.5%, respectively. According to XRD, In₂S₃ is formed below 300 °C, crystalline In_2.24(NCN)₃ is detected only in 1 above 520 °C and In₂O₃ is the final decomposition product at 900 °C. The gaseous species evolved include CS₂, NH₃, H₂NCN, HNCS, which upon oxidation yield also COS, SO₂, HCN and CO₂.     

Structural evolution and magnetic properties of SrFe<Subscript>12</Subscript>O<Subscript>19</Subscript> nanofibers by electrospinning

The SrFe₁₂O₁₉/poly (vinyl pyrrolidone) (PVP) composite fiber precursors were prepared by the sol-gel assisted electrospinning with ferric nitrate, strontium nitrate and PVP as starting reagents. Subsequently, the M-type strontium ferrite (SrFe₁₂O₁₉) nanofibers were derived from calcination of these precursors at 750–1,000 °C.The composite precursors and strontium ferrite nanofibers were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer. The structural evolution process of strontium ferrite consists of the thermal decomposition and M-type strontium ferrite formation. After calcined at 750 °C for 2 h the single M-type strontium ferrite phase is formed by reactions of iron oxide and strontium oxide produced during the precursor decomposition process. The nanofiber morphology, diameter, crystallite size and grain morphology are mainly influenced by the calcination temperature and holding time. The SrFe₁₂O₁₉ nanofibers characterized with diameters of around 100 nm and a necklace-like structure obtained at 900 °C for 2 h, which is fabricated by nanosized particles about 60 nm with the plate-like morphology elongated in the preferred direction perpendicular to the c-axis, show the optimized magnetic property with saturation magnetization 59 A m² kg⁻¹ and coercivity 521 kA m⁻¹. It is found that the single domain critical size for these M-type strontium ferrite nanofibers is around 60 nm.     

Synthesis and characterization of submicron size particles of LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> by microemulsion route

Among the various positive electrode materials investigated for Li-ion batteries, spinel LiMn₂O₄ is one of the most important materials. Small particles of the active materials facilitate high-rate capability due to large surface to mass ratio and small diffusion path length. The present work involves the synthesis of submicron size particles of LiMn₂O₄ in a quaternary microemulsion medium. The precursor obtained from the reaction is heated at different temperatures in the range from 400 to 900 °C. The samples heated at 800 and 900 °C are found to possess pure spinel phase with particle size <200 nm, as evidenced from XRD, SEM, and TEM studies. The electrochemical characterization studies provide discharge capacity values of about 100 mAh g⁻¹ at C/5 rate, and there is a moderate decrease in capacity by increasing the rate of charge–discharge cycling. Studies also include charge–discharge cycling and ac impedance studies in temperature range from −10 to 40 °C. Impedance data are analyzed with the help of an equivalent circuit and a nonlinear least squares fitting program. From temperature dependence of charge-transfer resistance, a value of 0.62 eV is obtained for the activation energy of Mn³⁺/Mn⁴⁺ redox process, which accompanies the intercalation/deintercalation of the Li⁺ ion in LiMn₂O₄.     

XAFS investigation of [Pd(NH<Subscript>3</Subscript>)<Subscript>4</Subscript>][AuCl<Subscript>4</Subscript>]<Subscript>2</Subscript> and its thermolysis products

Thermolysis of double complex salt [Pd(NH₃)₄][AuCl₄]₂ has been studied in helium atmosphere from ambient to 350 °C. The XAFS of Pd K and Au L₃ edges and thermogravimetry measurements have been carried out to characterize the intermediates and the final product. In the temperature range 115–160 °C the complex is decomposed to form Pd(NH₃)₂Cl₂ and AuCl_4−x N _x species with x ranging from 2 to 3. Subsequent heating of the intermediate up to 300 °C leads to the total loss of NH₃. The Au–Cl and Au–Au bonds form the local environment of Au at the stage of decomposition while only four chlorine atoms are around Pd. At the temperature of 330 °C the Au and Pd nanoparticles as well as residues of palladium chloride are detected. The final product consists of separated Au and Pd nanoparticles.     

Non-isothermal decomposition kinetics of NiFe<Subscript>2</Subscript>O<Subscript>4</Subscript> nanoparticles synthesized using egg white solution route

The thermal decomposition kinetics of nickel ferrite (NiFe₂O₄) precursor prepared using egg white solution route in dynamical air atmosphere was studied by means of TG with different heating rates. The activation energy (E _α) values of one reaction process were estimated using the methods of Flynn–Wall–Ozawa (FWO) and Kissinger–Akahira–Sunose (KAS), which were found to be consistent. The dependent activation energies on extent of conversions of the decomposition reaction indicate “multi-step” processes. XRD, SEM and FTIR showed that the synthesized NiFe₂O₄ precursor after calcination at 773 K has a pure spinel phase, having particle sizes of ~54 ± 29 nm.     

Non-isothermal kinetics of the thermal decomposition of sodium oxalate Na<Subscript>2</Subscript>C<Subscript>2</Subscript>O<Subscript>4</Subscript>

The thermal transformation of Na₂C₂O₄ was studied in N₂ atmosphere using thermo gravimetric (TG) analysis and differential thermal analysis (DTA). Na₂C₂O₄ and its decomposed product were characterized using a scanning electron microscope (SEM) and the X-ray diffraction technique (XRD). The non-isothermal kinetic of the decomposition was studied by the mean of Ozawa and Kissinger–Akahira–Sunose (KAS) methods. The activation energies (E _α) of Na₂C₂O₄ decomposition were found to be consistent. Decreasing E _α at increased decomposition temperature indicated the multi-step nature of the process. The possible conversion function estimated through the Liqing–Donghua method was ‘cylindrical symmetry (R₂ or F_1/2)’ of the phase boundary mechanism. Thermodynamic functions (ΔH*, ΔG* and ΔS*), calculated by the Activated complex theory and kinetic parameters, indicated that the decomposition step is a high energy pathway and revealed a very hard mechanism.     

Thermal analysis of CsH<Subscript>2</Subscript>PO<Subscript>4</Subscript> nanoparticles using surfactants CTAB and F-68

A study concerned to thermogravimetric analysis is performed in cesium dihydrogen phosphate (CsH₂PO₄) that was synthesized, using cetyltrimethylammonium-bromide (CTAB), polyoxyethylene-polyoxypropylene (F-68) and mixture of (F-68:CTAB) with two mole ratio 0.06 and 0.12 as surfactant. The dehydration behavior of particles was studied using thermal gravimetric analysis and differential scanning calorimetric. Subsequently, the experimental results indicated that the first dehydration temperature in the range of 237–239 °C upon heating, the second peaks occur at temperature range 290–295 °C and overlapping in the thermogravimetric events is observed. The mass loss values are obtained in the range of 6.62–6.97 wt% that is less than reported theoretical value 7.8 wt%. These values show well compatibility of reaction CsH₂PO₄ to Cs₂H₂P₂O₇ with 3.92 wt% whereas mass loss value of CsH₂PO₄ to CsPO₃ is less than theoretical value 7.8 wt%. The activation energy of two steps dehydration are calculated using Kissinger equation for the samples synthesized via CTAB and (F-68) with minimum value mass loss 6.62% and maximum value mass loss 6.97%, respectively. The calculation results reveal that the reaction rate in the first step (CsH₂PO₄ → Cs₂H₂P₂O₇) is faster than the second step (CsH₂PO₄ → CsPO₃). The weight loss values of the samples demonstrate that existence of CTAB can be considered as effective factor which prevents more weight loss during the dehydration process.     

CCl<Subscript>4</Subscript> Decomposition in RF Thermal Plasma in Inert and Oxidative Environments

The decomposition of carbon tetrachloride was investigated in an RF inductively coupled thermal plasma reactor in inert CCl₄–Ar and in oxidative CCl₄–O₂–Ar systems, respectively. The exhaust gases were analyzed by gas chromatography-mass spectrometry. The kinetics of CCl₄ decomposition at the experimental conditions was modeled in the temperature range of 300–7,000 K. The simulations predicted 67.0 and 97.9% net conversions of CCl₄ for CCl₄–Ar and for CCl₄–O₂–Ar, respectively. These values are close to the experimentally determined values of 60.6 and 92.5%. We concluded that in RF thermal plasma much less CCl₄ reconstructed in oxidative environment than in an oxygen-free mixture.     

Oxidation of Dimethyl Sulfide in Air Using Electron-Beam Irradiation,and Enhancement of its Oxidation Via an MnO<Subscript>2</Subscript> Catalyst

The decomposition of dimethyl sulfide (DMS) at initial concentrations of 4.5–18.0 ppmv in air was studied under electron-beam (EB) irradiation. Doses to decompose 90% of input DMS were 2.5 kGy for 4.5 ppmv, 3.4 kGy for 10.6 ppmv, and 3.9 kGy for 18.0 ppmv. HCOOH, (CH₃)₂SO, and trace CH₃OH and (CH₃)₂SO₂ were produced as irradiation products in addition to CO₂ and CO. Application of an O₃ decomposition catalyst to an irradiated sample gas led to an enhancement in the oxidation of DMS and its products into CO₂ and the decomposition of O₃. For 10.6 ppmv DMS/air, the mineralization ratio increased from 41% via only EB irradiation to 100% via the combination treatment at 6.3 kGy. The yield of CO₂ to CO_x increased from 5.3 to 87.6% by combination with catalytic oxidation. This combination treatment enables the irradiation energy used to deodorize gas streams containing DMS to be reduced.     

Synthesis of electrospun BaSrTiO<Subscript>3</Subscript>/PVP nanofibers

Ba_1−x Sr _x TiO₃(x = 0–0.5, BST) nanofibers with diameters of 150–210 nm were prepared by using electrospun BST/polyvinylpyrrolidone (PVP) composite fibers by calcination for 2 h at temperatures in the range of 650–800 °C in air. The morphology and crystal structure of calcined BST/PVP nanofibers were characterized as functions of calcination temperature and Sr content with an aid of XRD, FT-IR, and TEM. Although several unknown XRD peaks were detected when the fibers were calcined at temperatures less than 750 °C, they disappeared with increasing the temperature (above 750 °C) due to its thermal decomposition and complete reaction in the formation of BST. In addition, the FT-IR studies of BST/PVP fibers revealed that the intensities of the O–H stretching vibration bands (at 3430 and 1425 cm⁻¹) became weaker with increasing the calcination temperature and a broad band at 540 cm⁻¹, Ti–O vibration, appeared sharper and narrower after calcination above 750 °C due to the formation of metal oxide bonds. However, no effect of Sr content on the crystal structure of the composites was detected.     

Sol–gel synthesis,characterization and photocatalytic activity of mesoporous TiO<Subscript>2</Subscript>/γ-Al<Subscript>2</Subscript>O<Subscript>3 </Subscript>granules

Mesoporous TiO₂/γ-Al₂O₃ composite granules were prepared by combining sol–gel/oil-drop method, using various titania solution. The product granules can be used as a photocatalyst or adsorbent in moving, fluidized bed reactors. The phase composition and pore structure of the granules can be controlled by calcination temperature and using different titania solution. In the photocatalysis of NH₃ decomposition, TiO₂/γ-Al₂O₃ granules using Degussa P25 powder treated thermally at 450 °C showed the highest catalytic ability. However, TiO₂/γ-Al₂O₃ granules using titania made by hydrothermal method had comparable performance in NH₃ decomposition.     

Gold catalysts supported on ZnO/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> for low-temperature CO oxidation

Gold catalysts with loadings ranging from 0.5 to 7.0 wt% on a ZnO/Al₂O₃ support were prepared by the deposition–precipitation method (Au/ZnO/Al₂O₃) with ammonium bicarbonate as the precipitation agent and were evaluated for performance in CO oxidation. These catalysts were characterized by inductively coupled plasma-atom emission spectrometry, temperature programmed reduction, and scanning transmission electron microscopy. The catalytic activity for CO oxidation was measured using a flow reactor under atmospheric pressure. Catalytic activity was found to be strongly dependent on the reduction property of oxygen adsorbed on the gold surface, which related to gold particle size. Higher catalytic activity was found when the gold particles had an average diameter of 3–5 nm; in this range, gold catalysts were more active than the Pt/ZnO/Al₂O₃ catalyst in CO oxidation. Au/ZnO/Al₂O₃ catalyst with small amount of ZnO is more active than Au/Al₂O₃ catalyst due to higher dispersion of gold particles.     

Thermal oxide synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanorods and Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanowires

Fe₃O₄ nanorods and Fe₂O₃ nanowires have been synthesized through a simple thermal oxide reaction of Fe with C₂H₂O₄ solution at 200–600°C for 1 h in the air. The morphology and structure of Fe₃O₄ nanorods and Fe₂O₃ nanowires were detected with powder X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The influence of temperature on the morphology development was experimentally investigated. The results show that the polycrystals Fe₃O₄ nanorods with cubic structure and the average diameter of 0.5–0.8 μm grow after reaction at 200–500°C for 1 h in the air. When the temperature was 600°C, the samples completely became Fe₂O₃ nanowires with hexagonal structure. It was found that C₂H₂O₄ molecules had a significant effect on the formation of Fe₃O₄ nanorods. A possible mechanism was also proposed to account for the growth of these Fe₃O₄ nanorods. Supported by the Fund of Weinan Teacher’s University (Grant No. 08YKZ008), the National Natural Science Foundation of China (Grant No. 20573072) and the Doctoral Fund of Ministry of Education of China (Grant No. 20060718010)     

Application of a dioxo-molybdenum(VI) complex anchored on TiO<Subscript>2</Subscript> for the photochemical oxidative decomposition of 1-chloro-4-ethylbenzene under O<Subscript>2</Subscript>

The catalytic activity of dioxo-molybdenum(VI)-dichloro[4,4′-dicarboxylato-2,2′-bipyridine] covalently anchored through the carboxylate function to the surface of TiO₂ has been tested for the oxidative degradation of 1-chloro-4-ethylbenzene in MeCN solution under argon and UV irradiation (λ = 254 nm). After 4–5 h of photochemical reaction, the Mo complex was reoxidized in the presence of O₂ in the dark, and then the reaction was continued under argon. The reaction proceeds by the intermediate formation of 4′-chloroacetophenone that undergoes further decomposition to chlorobenzene, plus small amounts of oxygen-containing organochlorine compounds, CO₂ and H₂O. Similar results were obtained for the decomposition of 4′-chloroacetophenone under the same conditions, which also gave chlorobenzene as one of the main products. The ratio of [final product]/[Mo complex] increases during the decomposition of 1-chloro-4-ethylbenzene (up to 350–400% for 30–35 h of reaction), which provides evidence of a catalytic process. The probable photochemical reactions are discussed.     

Chemical composition optimization and characterization of the NiO/B<Subscript>2</Subscript>O<Subscript>3</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> system as a catalyst for ethylene oligomerization

The samples of the NiO/B₂O₃-Al₂O₃ system with NiO contents from 0.48 to 38.30 wt % were synthesized by the impregnation of borate-containing alumina (20 wt % B₂O₃). It was found that nickel oxide occurred in an X-ray amorphous state in the samples containing to 23.20 wt % NiO. At a NiO content of 4.86 wt % or higher, the support was blocked by the modifier to cause a decrease in the specific surface area from 234 to 176 m²/g and in the amount of acid sites from 409–424 to 333 μmol/g. An extremal character of the dependence of catalyst activity in ethylene oligomerization on NiO content was found with a maximum in the range of 4.86–9.31 wt %. Based on spectroscopic data, it was found that ethylene activation on the NiO/B₂O₃-Al₂O₃ catalyst can be associated with the presence of Ni²⁺ cations, which chemically interact with the support. The catalyst containing 4.86 wt % NiO at 200°C, a pressure of 4 MPa, and an ethylene supply rate of 1.1 h⁻¹ provided almost complete ethylene conversion at the yield of liquid oligomerization products to 90.0 wt %; the total concentration of C⁸⁺ alkenes in these products was 89.0 wt %.     

Effect of metal substitution for cobalt on the oxygen adsorption properties of YBaCo<Subscript>4</Subscript>O<Subscript>7</Subscript>

YBaCo₄O₇ compound is capable to intake and release a large amount of oxygen in the temperature range of 200–400°C. In the present study, the effect of Zn, Ga and Fe substitution for Co on the oxygen adsorption/desorption properties of YBaCo₄O₇ were investigated by thermogravimetry (TG) method. Due to fixed oxidation state of Zn2+ ions, the substitution of Zn²⁺ for Co²⁺ suppresses the oxygen adsorption of YBaCo_4−xZn_xO₇. The substitution of Ga³⁺ for Co³⁺ also decreases the oxygen absorption capacity of YBaCo_4−xGa_xO₇. This can be explained by the strong affinity of Ga³⁺ ions towards the GaO₄ tetrahedron. Compared with Zn- and Ga-substituted samples, the drop of oxygen adsorption capacity is smallest for Fe-substituted samples because of the similar changeability of oxidation states of Co and Fe ions.