铈对16Mn钢中夹杂物和组织的影响

在高温钼丝炉内向16Mn钢中加入不同含量的铈进行脱氧,分析了钢中夹杂物和组织的变化,并探讨了含铈夹杂物诱发晶内铁素体形核的机制.结果表明:随钢中铈含量的增加,夹杂物依次转变为CeAlO3,Ce2O2S和Ce2S3.经铈处理后,钢液在1873 K时保温300 s,夹杂物最为细小弥散.钢中晶内铁素体随铈含量的增加而增加,但最佳的铈含量约为0.032%(质量分数).钢中Ce2O2S和Ce2S3夹杂与α-Fe相之间的错配度分别只有1.2%和0.5%,均可作为IGF非常有效的形核核心,促进其形成.     

稀土碳锰纯净钢中夹杂物形成与转化的热力学计算及观察分析

用多相、多组元平衡的热力学计算方法, 对稀土碳锰纯净钢中夹杂物的析出和转化进行了计算. 结果表明, 稀土元素能有效地变质Al2O3夹杂, 在本实验所用材料的成分条件下, Al2O3完全消失的稀土含量为: 1600 ℃时, La>0.009%, Ce>0.01%; 1518 ℃时, La>0.012%, Ce>0.013%, 稀土变质Al2O3的产物主要为RE2O2S. 当La含量大于0.028%, Ce含量大于0.027%后, 体系中将会有RES产生, 但夹杂物仍然以RE2O2S为主. 对试样的扫描电镜观察和分析证实了热力学计算的结果.     

钇对H13钢中夹杂物的影响EI北大核心CSCD

研究了不同Y含量对H13模具钢中夹杂物的种类、形态、尺寸和成分等的影响机制。实验室采用电渣重熔冶炼添加Y获得了Y含量分别0.0008%,0.006%和0.012%(质量分数)的H13电渣锭。利用OM,SEM,ASPEX和热力学计算等方法研究Y对钢中夹杂物的影响。结果表明,不添加稀土的H13钢中夹杂物以MgO·Al_(2)O_(3)外包覆(Cr,V,Mo)C的复合夹杂为主;Y添加量为0.0008%的H13钢材中夹杂物以YAlO_(3)外包覆(Cr,V,Mo)C的复合夹杂物为主;Y添加量为0.006%的H13钢中夹杂物以YAlO_(3)和YAlO_(3)外包覆(Cr,V,Mo)C的复合夹杂物为主;Y添加量为0.012%的H13钢中夹杂物以单独存在的Y_(2)O_(3),YS·Y_(2)O_(3),YS外包覆(Cr,V,Mo)C的复合夹杂物为主。当H13钢中的Y达到0.012%时,钢中尺寸小于5μm的夹杂物占96%以上。     

稀土氧化物对中高碳钢堆焊金属中夹杂物变质作用的热力学分析

采用热力学方法,研究了稀土氧化物对中高碳钢堆焊金属中夹杂物的变质作用。夹杂物生成的热力学分析表明,在堆焊熔池中,稀土氧化物可以被碳还原成稀土元素,稀土元素可以与氧、硫生成稀土氧化物、稀土硫化物和稀土硫氧化物,从而达到脱氧、脱硫、净化堆焊熔池的作用;稀土氧化物还可以直接与硫作用,生成稀土硫氧化物,起到脱硫的效果。     

稀土在镁合金溶液中作用的热力学分析

本文对多种稀土元素在镁合金溶液中的作用进行了热力学分析，并讨论了稀土在溶液中的去氧和除氢机制，计算结果表明，稀土与镁溶液中的氧化物夹杂发生交互作用，产生稀土氧化物而除去氧化物夹杂，通过与溶液中的氢发生交互作用，产生稀土氢化物而达到了溶液除氢；但与主要成分为ＭｇＣｌ２的熔剂发生交互作用则降低了溶液中的稀土含量。     

钢中氧化物夹杂分析的误差来源及结果的可靠性

本文综述了采用化学-电化学方法分析钢中氧化物夹杂的误差来源。基体元素的水解、钝化、共存相的干扰和包裹相等引起正偏差;化学溶损、沉淀处理等引入的负偏差;以及随机误差。相应地提出了提高分析精度的具体措施。对这种既无标样又无标准可循的分析其结果的可靠性不仅需根据钢中氧含量而定,还需根据夹杂物的总量与分量的吻合程度来判定,此外要结合钢的化学成份,冶炼工艺,脱氧制度来综合判断。     

钢液凝固过程中稀土夹杂物的显微形貌及形成机制的研究

用透射电镜和扫描电镜研究了钢液凝固过程中形成的稀土夹杂物的结构类型及类型及形貌，并运用热力学理论分析其形成过程。研究结果表明，在钢液凝固过程中，随着硫氧比的提高，稀土与氧硫反应产物依次是ＲＥ２０３、Ｒ３２Ｏ３与ＲＥ２９２Ｓ的复合物，ＲＥ２Ｏ２Ｓ以及ＲＥ２Ｓ３，此外还少量ＲＥＯ３。ＲＥ２ＯＥ呈典型胞状，ＲＥ２９Ｏ２Ｓ则为表面光滑的团球状。     

稀土元素在钢中的热力学参数及应用

综合报道了通过采用几种不同的高温金属溶液实验方法，研究所得到的稀土元素在金属溶液冶炼温度范围内分别与硫、氧、氧 硫、碳、氮、低熔点铜、磷、钛、铌、钒等重要元素相互作用规律及有关的一系列热力学参数和温度函数式，并简要地讨论了这些热力学参数在含稀土钢中的应用。     

大气环境中铈氧物组成研究

采用X射线衍射仪(XRD)、扫描电镜(SEM)和X射线光电子能谱(EDS)研究了大气环境中铈氧化物的组成变化. 实验结果表明, 大气环境中铈的氧化物主要由Ce2O3, Ce7O12和CeO2构成, 氧化初期主要是Ce2O3, 随着氧化时间增加, 大部分Ce2O3逐渐转变为Ce7O12, 而在局部微裂纹集中处直接生成CeO2, 随着氧化过程的进行, Ce7O12逐渐转变为CeO2, 240 h后 Ce7O12几乎完全转变为CeO2;扫描电镜结合能谱分析表明Ce7O12主要以连续致密氧化膜存在, 而CeO2则出现大量微裂纹, 这种变化与两者密度上的差异有关.     

铈对重轨钢中珠光体相变及组织的影响

研究了不同铈量对轨钢珠光体相变及形态的影响。随钢中固溶铈含量增加，等温珠光体相变的孕育期延长，珠光体片间距减小，形态从片状向粒状发展，对珠光体相变速率影响不大。固溶铈还能细化奥氏体晶粒，铈减小缺陷处（晶界、位错等）的能量，是产生上述结果的主要原因。     

镧和铈钝化镀锌钢板的研究

采用镧盐和铈盐钝化镀锌钢板,通过醋酸铅点滴,失重,中性盐雾和电化学交流阻抗实验检测试样耐腐蚀性能.实验结果显示镧盐和铈盐钝化试样的耐黑变时间分别为70和44 s;腐蚀速率为1.9979×10-3g·m-3·h-1和3.6523×10-3g·m-2·h-1;抗白锈时间为54和46 h;阻抗值大幅提高;实验结果表明镧盐和铈盐钝化处理能大幅度提高试样耐腐蚀性,镧盐转化膜相对于铈盐转化膜更耐腐蚀.清漆划格实验表明清漆在稀土钝化后的试样表面附着力良好;原子力扫描结果显示稀土转化膜由大量不定型的固体颗粒不均匀沉积而成;EDS检测结果表明镧盐转化膜由O,Fe,Zn和La组成,铈盐转化膜由O,Fe,Zn和Ce组成.     

钢中夹杂物的电解萃取

介绍了一种有机溶液电解萃取和检测钢中非金属夹杂物的方法,能将含氧化物、硅酸钙、硅铝酸钙夹杂物从钢试样中完整无损地提取出来,并直接观察其三维立体形貌。并将夹杂物进行了统计分析,得到夹杂物的形貌、类型、尺寸、元素组成及数量分布,对炼钢生产过程的控制和优化有一定的指导作用。     

Thermodynamic Study on Vesicle Formation and Adsorption of Decyltrimethylammonium Decyl Sulfate

The surface tension of an aqueous solution of decyltrimethylammonium decyl sulfate (DeTADeS) was measured as a function of temperature T at various molalities &mcirc; under atmospheric pressure. DeTADeS has been found to form equilibrium multilamellar vesicles (MLV) spontaneously. The surface density, the entropies of adsorption, and the entropy of vesicle formation are evaluated. The mechanism of formation of equilibrium vesicles is investigated from the standpoint of thermodynamics and from the comparison of the results with those of the micelle-forming systems. From the relatively small change of the surface density Gamma;(H) on T at a given &mcirc;, the adsorbed film is implied to be tightly packed due to the strong electrostatic attraction between the polar headgroups. The energy change associated with adsorption from the vesicular state per mole of surfactant Delta(V)(H)u is positive in the entire temperature range; thus, the curved bilayer in MLV is energetically more favorable than the planar adsorbed film. From the negative values of the entropy of vesicle formation Delta(W)(V)s, it is concluded that vesicle formation is driven by enthalpy whereas micelle formation is mostly entropy driven. Copyright 2001 Academic Press.     

铈在低硫铌钛钢中的微合金化作用

在实验室条件下采用50 kg真空感应炉冶炼和两段控制轧制工艺, 采用THERMECMASTOR-Z热模拟机对过冷奥氏体连续冷却转变曲线进行了测定, 试验结果表明, 低硫铌钛钢中稀土铈能提高钢的临界点tAr3和tAr1, 并且使(tAr3-tAr1)温度区间增大; 并使钢的CCT曲线右移和上移, 降低了钢的淬透性; 铈会使贝氏体转变点升高, 同时加大了贝氏体转变间隔; 当冷却速度较高时, 稀土使马氏体由粗条状变为细条状, 降低了Ms点, 并且增强了马氏体结构的板条化趋势, 抑制了片状晶生成.     

含Ce的水热体系中结构稳定性及变价现象

利用ＸＲＤ、ＩＲ及ＸＰＳ谱研究了含Ｃｅ的水热体系中产物及其经过各种后处理的样品结构稳定性及Ｃｅ离子的价态变化。结果表明，不同的原料导致Ｃｅ离子稳定于不同的价态，如直接形成包括纳米晶在内的ＣｅＯ２及一新相ＣｅＯＨＣＯ３，样品ＣｅＯＨＣＯ３经２ＧＰａ的冷压处理未发生结构转变，经高温焙烧处理得到具有高结晶度的棕红色的ＣｅＯ２，当初始原料为Ｃｅ２（ＳＯ４）３和Ｃｅ（ＮＯ３）３时，产物为ＣｅＯ２；而当初始原     

镁合金铈转化膜的形成及表征

采用X射线光电子能谱（XPS）、原子力显微镜（AFM）、电化学方法等对AZ31镁合金铈转化膜的组成、形貌结构及耐蚀性能进行了表征,并结合成膜动力学研究探讨了膜的形成机制。结果表明,镁合金铈转化膜的主要成分为铈的氧化物/氢氧化物,铈在膜中以三价和四价两种价态存在。膜可以分为两层,内、外层膜由不同的微结构组成,这种微结构的差异使内、外层膜之间结合力较弱,成为限制膜耐蚀性能提高的根本原因之一。成膜过程中,成膜溶液pH值升高,使Ce3＋发生水解反应沉积析出铈的氢氧化物/氧化物。铈转化膜的生长动力学遵循抛物线规律。     

纳米La203合成过程热力学及试验研究

本文对溶胶-凝胶法合成La2O3合成过程进行研究,计算了La(NO3)3和La(OH)3的热力学数据.在此基础上,对氧化镧的合成过程进行热力学进行了分析,确定了合成工艺条件,并采用溶胶-凝胶法制备出了纳米氧化镧粉末.     

Microstructural and Mechanical Properties of Al-20%Si Containing Cerium

In this paper the effect of cerium addition in hypereutectic Al-Si alloys was studied. Casting method was used to produce Al-20Si with variation of Ce contents. The sample characterization studied was investigated by Optical Microscope, X-ray fluorescence and X-ray Diffraction. Vickers microhardness and wear test was carried out to study the influence of Ce towards the Al-20Si alloys. The addition of Ce in the Al-20Si alloys refined the Si primary phase as the Ce content increases. The results showed that the addition of 0.46 to 2.24 wt.% of cerium in Al-20Si alloys led to the formation of fine cells dispersed in the Al-matrix. These fine cells consist of a mixture of eutectic Si particles and intermetallic Al3Ce and CeAl1.2Si0.8 phase in Al matrix. The amount of rod- like intermetallic Al3Ce and CeAl1.2Si0.8 phase increases with increasing Ce content. The microhardness of Al-20Si alloys increases with the increase in Ce content. Addition of Ce up to 1.61 wt.% Ce improve the wear properties of Al-20Si alloy.     

碳锰洁净钢中镧和铈在晶界的行为

应用高分辨TEM，SEM和XRD研究碳锰洁净钢中镧和铈的存在形式、分布以及在晶界的行为。研究结果表明，镧和铈在洁净钢中存在固溶态、稀土夹杂物和稀土第二相。固溶稀土偏析在晶界，洁净钢中稀土仍有净化钢液和变质夹杂的作用。适量稀土能减少S和P在晶界的偏析，净化晶界提高钢的冲击韧性。过量稀土在晶界产生有害的稀土第二相，导致性能显著降低。