Mg2+掺杂Zn2SiO4:Mn2+的溶胶-凝胶法合成及真空紫外发光特性研究

采用溶胶-凝胶法（sol-gel method）于不同气氛条件下成功合成了Zn_1.92-xMg_xSiO₄:0.08Mn²⁺（0≤x≤0.12）系列粉末样品.利用X射线衍射(XRD)、光致发光(PL)谱等分析手段对Zn_1.92-xMg_xSiO₄:0.08Mn²⁺系列     

Ho3+/Yb3+→α-NaYF4单晶的上转换荧光光谱特性

以KF作为助熔剂,采用固液界面温度梯度(70～90 oC/cm),通过改进的助熔剂-坩埚下降法从NaF-YF₃熔体系统中生长出了Ho³⁺/Yb³⁺离子双掺杂的α-NaYF₄单晶体. 在980 nm激光泵浦下可以观察到544 nm的上转换绿光和657和751 nm的上转换红光. 上转换的绿光强度明显强于上转换红光. 通过测量泵浦功率和上转换光的强度之间的关系研究了上转换发光的机理. 当Ho³⁺的掺杂浓度保持为1.0 mol%的情况下,Yb³⁺的浓度为8.08 mol%时上转换强度最强.     

Mn4+掺杂对BiFeO3陶瓷微观结构和电学性能的影响研究

利用传统的固相反应法制备了BiFe_1-xMn_xO₃ (x= 0-0.20)陶瓷样品, 研究了不同Mn⁴⁺掺杂量对BiFeO₃陶瓷密度、物相结构、显微形貌、 介电性能和铁电性能的影响.实验结果表明:所制备的BiFe_1-xMn_xO₃ 陶瓷样品的钙钛矿主相均已形成,具有良好的晶体结构, 且在掺杂量x=0.05附近开始出现结构相变.随着Mn⁴⁺添加量的增加, 体系的相结构有从菱方钙钛矿向斜方转变的趋势,且样品电容率大幅度增大, 而介电损耗也略有增加;在测试频率为10⁴ Hz条件下, BiFe_0.85Mn_0.15O₃ (ε_r=1065)的 ε_r是纯BiFeO₃ (ε_r=50.6)的22倍; 掺杂后样品的铁电极化性能均有不同程度的提高,可能是由于Mn⁴⁺稳定性优于 Fe³⁺,高价位Mn⁴⁺进行B位替代改性BiFeO₃陶瓷, 能减少Bi³⁺挥发,抑制Fe³⁺价态波动,从而降低氧空位浓度,减小样品的电导和漏电流.     

LD抽运Er3+，Yb3+共掺磷酸盐玻璃被动调Q激光器的理论分析和数值计算

研究了以Co²⁺:MgAl₂O₄晶体为饱和吸收体的LD抽运Er³⁺,Yb³⁺共掺磷酸盐玻璃激光器.针对双掺离子之间的能量传递和Er³⁺的多种跃迁过程，结合Co²⁺:MgAl₂O₄晶体中Co²⁺离子的饱和吸收特性，给出了详尽的速率方程，在其基础上进行了数值分析，分析了输出镜透过率、激光介质长度、谐振腔长度、腔内往返损耗、饱和吸收体长度对激光阈值、峰值功率、单脉冲能量以及脉冲宽度的影响.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

Al掺杂的尖晶石型LiMn2O4的结构和电子性质

采用基于密度泛函理论的第一性原理方法, 在广义梯度近似(GGA)和GGA+U方法下对尖晶石型LiMn₂O₄及其Al掺杂 的尖晶石型LiAl_0.125Mn_1.875O₄晶体的结构和电子性质进行了计算. 结果表明: 采用GGA方法得到尖晶石型LiMn₂O₄是立方晶系结构, 其中的Mn离子为+3.5价, 无法解释它的Jahn-Teller 畸变. 给出的LiMn₂O₄能带结构特征也与实验结果不符. 而采用GGA+U方法得到在低温下的LiMn₂O₄和其掺杂 体系LiAl_0.125Mn_1.875O₄的晶体都是正交结构, 与实验一致. 也能明确地确定Mn的两种价态Mn³⁺/Mn⁴⁺的分布并且能够说明Mn³⁺O₆的z方向有明显的Jahn-Teller 畸变, 而Mn⁴⁺O₆则没有畸变. LiMn₂O₄的能带结构与实验比较也能够符合. 采用GGA+U方法对Al掺杂体系的LiAl_0.125Mn_1.875O₄的研究表明, 用Al替换一个Mn不会明显地改变晶体的电子性质, 但可以有效地消除Al³⁺O₆ 八面体的Jahn-Teller畸变, 从而改善正极材料LiMn₂O₄的性能, 这与电化学实验的观察结果相一致.     

纳米YPO4:Eu3+的合成及发光性质研究

采用水热法合成了纳米Y_1-xPO₄:xEu³⁺（005≤x≤030）系列荧光粉,并对样品进行了热处理.通过X射线衍射（XRD）、扫描电镜（SEM）等手段分析了合成样品的结构及形貌,结果表明合成的样品均为四方磷钇矿结构,在酸性和碱性条件下分别为球状和细棒状,且均在纳米尺度.研究其在真空紫外（VUV）激发下的发光性质发现,样品的激发峰最大值位于142 nm左右;与固相法的样品相比,PO^3-     

Sr2CeO4电荷迁移发光的光谱结构规律研究

利用高温固相反应法分别合成了不同物相形成机理的Sr₂CeO₄，Sr ₂CeO₄∶Ca ²⁺和Sr₂CeO₄∶Ba²⁺样品，并对其光谱特性进行 了研究.结果发现，对于由SrO和CeO₂直接反应生成的Sr₂CeO₄(Ⅰ)，激发主峰位于256nm 左右；而对于SrCeO₃和SrO反应生成的Sr₂CeO₄(Ⅱ)，激发主峰位于279nm左右.在Sr₂CeO₄(Ⅰ)中掺入Ca²⁺，其激发光谱随着Ca²⁺离子浓度的增加逐渐接近于Sr₂CeO_{4(Ⅱ)的激发光谱.激发主峰带应属于CeO6八面体终端Ce⁴⁺—O^2-键的电荷迁移 带.对于激发光谱中340nm左右的弱激发峰，其峰值波长不受形成机理及Ca²⁺掺杂的影响，只是其强度 随着 激发主峰的红移而增加，它可能属于CeO6八面体平面上Ce⁴⁺—O2-键的电荷 迁移带.形成机理及Ca²⁺掺杂对发射光谱没有影响.Ca²⁺在Sr 2CeO 4(Ⅱ)与Ba²⁺在Sr2CeO4(Ⅰ)和(Ⅱ)中均难 于替代Sr²⁺的位置.}     

Er3+：GdVO4中Er3+离子的光谱参数计算和晶场中能级分裂的讨论

对Er³⁺：GdVO₄样品的光谱参数以及Er³⁺在晶场中能级的分裂情况进行了研究. 首先对样品进行了吸收光谱的测量，接着用Judd-Ofelt理论拟合出了Er³⁺在GdVO₄晶体中的强度参量Ω_t，并由此计算了跃迁的振子强度、自发辐射跃迁速率、荧光分支比和积分发射截面. 通过计算结果可以发现有较多能级之间的跃迁都有大于10^-6的振子强度和大于10^-18cm的积分发射截面，并且具有较高的荧光分支比，特别是²H_11/2→⁴I_15/2，⁴S_3/2→⁴I_15/2，⁴F_9/2→⁴I_15/2和⁴I_13/2→⁴I_15/2等几个强发光能级除了具有较大的振子强度和积分发射截面外还有很好的应用前景，因此也更加值得关注. 最后还利用群论讨论了Er³⁺离子在GdVO₄晶场中各能级的分裂情况并对各Stark子能级的J_z混杂情况进行了分析.     

La2Zr2O7:Eu3+纳米棒的合成、表征及其荧光性能

采用传统固相法和水热法成功地制备出棒状La₂Zr₂O₇:Eu³⁺荧光粉. 利用X射线粉末衍射仪、透射电镜和荧光光谱仪等分析了产物的结构、形貌和发光特性. 结果表明红色荧光粉La₂Zr₂O₇:Eu³⁺有良好的晶相,属于立方结构,空间点群为Fd3m; 其形貌主要为纳米棒, 平均直径约47 nm, 长度为50～700 nm. 并对纳米棒的生长机理进行了探讨. 在466 nm蓝光激发下,La₂Zr₂O₇:Eu³⁺荧光粉能发射出Eu³⁺的特征红色荧光,发射主峰位于616 nm处,归属于Eu³⁺的⁵DO_→⁷F2_{超灵敏电偶极跃迁.此外,在产物的发射光谱中能够观察到⁵D}1_→⁷FJ _{(J=0, 1, 2)跃迁和⁵D}1_→⁷FJ _{(J=1, 2, 4)跃迁的劈裂峰,这说明Eu³⁺处在低对称性的晶体场格位中.}     

Theoretical studies of the spin-Hamiltonian parameters for the orthorhombic Pr4+ centers in Sr2CeO4 crystals

Theoretical studies of spin-Hamiltonian (SH) parameters associated with Pr⁴⁺ in Sr₂CeO₄ single crystals have been made by using the complete diagonalizing energy matrix method (CDM) for the 4f ¹ electronic configuration. The calculated results are in excellent agreement with the experimental data. The negative signs of the anisotropic g _i -factors and hyperfine structure constants A _i (where i = ∥ or ⊥) for the orthorhombic Pr⁴⁺ ion in Sr₂CeO₄ are suggested from the calculations. By comparing the results obtained by the CDM with the experimental data, one finds it is valid to interpret the SH parameters for 4f ¹ ions in crystals. The results are discussed.      

Crystal fields of Pr in LiYF4 under pressure

Fluorescence spectra of LiYF₄:Pr³⁺ have been measured between 12,000 and 22,000 cm⁻¹ under pressures up to 10 GPa. In total, 25 crystal field energy levels were obtained and used for the determination of free-ion and crystal field parameters under pressure. According to the nephelauxetic effect, the free-ion parameters decrease with increasing pressure. The relative decrease is larger for the Slater than for the spin-orbit coupling parameter. This behavior is consistent with former studies on Pr³⁺ in different crystals and can be explained by a special covalency model. According to an effective D_2d symmetry, five crystal field parameters B₀²(f,f), B₀⁴(f,f), B₄⁴(f,f), B₀⁶(f,f), and B₄⁶(f,f) are non-zero. The pressure-induced changes of these parameters have been determined up to the maximum pressure of 10 GPa. In order to improve the calculation of the crystal field levels, the configuration interactions with the 4f¹6p¹ configuration have been taken into account. The effect of these interactions are also analyzed under pressure and distinct improvements of the energy level calculations have been obtained.     

Absorption coefficients of an undoped YVO4 crystal

In this paper, the absorption coefficients α_o (for ordinary ray) and α_e (for extraordinary ray) of an undoped YVO₄ crystal were calculated by measuring the transmissivities and refractive indices. The mean values 0.00549 cm⁻¹ of α_o measured by unpolarized light, and 0.00432 cm⁻¹ of α_o and 0.00420 cm⁻¹ of α_e measured by linear polarized light were reported, respectively. The corresponding absorption curves were given. The discussions about the errors were made. This work is available to evaluate quantificationally the quality of undoped YVO₄ crystal and provides the significant data of absorption coefficient for its applications.     

Atomic 6p-Tl0 centers in ferroelectric Rb2ZnCl4 crystals

Abstract

Several Tl⁰ (6s²6p ¹)-type paramagnetic centers, produced by low temperature X-ray irradiation, were observed and studied by electron spin resonance (ESR) in the orthorhombic ferroelectric phase of thallium doped Rb₂ZnCl₄ crystals. The centers were formed by electron trapping at Tl⁺ ions localized substitutionally at Rb⁺ sites. The number and properties of the observed centers account for the tripling of the unit cell in the ferroelectric phase.     

Blue luminescence in Tm-doped KGd(WO4)2 single crystals

Up-conversion blue emissions of trivalent thulium ions in monoclinic KGd(WO₄)₂ single crystals at 454 and 479 nm are reported for a single pump laser source at 688 nm. We grew thulium-doped KGd(WO₄)₂ single crystals at several concentrations from 0.1% to 10%. We recorded a polarized optical absorption spectrum for the ³F₂+³F₃ energy levels of thulium at room temperature and low temperature (6 K). From the low temperature emission spectra we determined the splitting of the ³H₆ ground state. The blue emissions are characterized as a function of the dopant concentration and temperature from 10 K to room temperature. To our knowledge, this is the first time that sequential two-photon excitation process (STEP) generated blue emissions in thulium-doped single crystals with a single excitation wavelength.     

Synthesis and characterization of Ca2Sn1-xCexO4 with blue luminescence originating from Ce^4＋ charge transfer transition

Ce^4＋-doped Ca2SnO4 with a one-dimensional structure, which emits bright blue light, is prepared by using a solid-state reaction method. The x-ray diffraction results show that the Ce^4＋ ions doped in Ca2SnO4 occupy the Sn^4＋ sites. The excitation and emission spectra of Ca2Sn1-xCexO4 appear to have broad bands with peaks at - 268nm and -442nm, respectively. A long excited-state lifetime （-83μs） for the emission from Ca2Sn1-xCexO4 suggests that the luminescence originates from a ligand-to-metal Ce^4＋ charge transfer （CT）. The luminescent properties of Ca2Snl_xCexO4 have been compared with those of Sr2CeO4, which is the only material reported so far to show Ce^4＋ CT luminescence. More interestingly, it is observed that the emission intensity of Ca2Sn1-xCexO4 with a small doping concentration （x - 0.03） is comparable to that of Sr2CeO4 in which the concentration of active centre is 100%.     

Normal Coordinates Analysis for The M(NH3)2+ 4 Complex Ions in D4h and Td Symmetries. Simplified Molecular Models

A normal coordinates analysis for the M(NH₃)²⁺ ₄ complex ions in T_d symmetry (M = Zn, Cd, Co) and in D_4h symmetry (M = Cu, Pd, Pt) has been undertaken on the basis of a General Valence Force Field (GVFF), using simplified molecular models. Throughout the course of the present work, we have relaxed the point mass approximation for the NH₃-ligands in order to investigate, on a quantitative basis, some relevant ligand - framework coupling vibrations. The simplest molecular model able to accomplish this purpose is to treat the ammino group, in a linear ligator approximation. We show that these model calculations provide a satisfactory set of vibrational frequencies as well as consistent sets of force constants.     

Synthesis and photoluminescence properties of Sm-doped CaWO4 nanoparticles

The Sm³⁺-doped CaWO₄ nanoparticles were synthesized by hydrothermal method. The room temperature photoluminescence (PL) spectra of Sm³⁺-doped CaWO₄ nanoparticles doped with different Sm³⁺ concentrations under 405 nm excitation have been investigated. The PL spectra showed four strong emission peaks at 460, 571, 609, and 653 nm. The first emission peak at 460 nm could be due to a structural defect of the lattice, an oxygen-deficient WO₃ complex. The other three emissions at 571, 609, and 653 nm were due to the f-f forbidden transitions of the 4f electrons of Sm³⁺, corresponding to ⁴G_5/2→⁶H_5/2 (571 nm), ⁶H_7/2 (609 nm), and ⁶H_9/2 (653 nm), respectively. In addition, the optimum Sm³⁺ concentration in CaWO₄ nanoparticles for optical emission was determined to be 1.0%. The Sm³⁺⁴G_5/2→⁶H_7/2 (609 nm) emission intensity of Sm³⁺-doped CaWO₄ nanoparticles significantly increased with the increase of Sm³⁺ concentration, and showed a maximum when Sm³⁺ doping content was 1.0%. If Sm³⁺ concentration continued to increase, namely more than 1.0%, the Sm³⁺⁴G_5/2→⁶H_7/2 emission intensity would decrease. The present materials might be a promising phosphor for white-light LED applications.     

The up-conversion properties of Yb and Er doped Y4Al2O9 phosphors

Er³⁺ doped and Yb³⁺/Er³⁺ co-doped Y₄Al₂O₉ phosphors are prepared by the sol-gel method. The effect of dopant concentration on the structure and up-conversion properties is investigated by X-ray diffraction (XRD) and photoluminescence, respectively. XRD pattern indicates that the sample structure belongs to monoclinic. Under 980 nm excitation, the green and red up-conversion emissions are observed and the emission intensities depended on the Yb³⁺ ion concentration. The green up-conversion emissions decrease with the increase of Yb³⁺ concentration, while red emission increases as Yb³⁺ concentration increases from 0 to 8 at% and then decreases at high Yb³⁺ concentration. The mechanisms of the up-conversion emissions are discussed and results shows that in Er³⁺ and Yb³⁺/Er³⁺ co-doped system, cross-relaxation (CR) and energy transfer (ET) processes play an important role for the green and red up-conversion emissions.