Exploration of layered-type pseudo four-component Li-Ni-Co-Ti oxides

A series of layered-type pseudo four-component Li-Ni-Co-Ti oxides were prepared to explore optimal cathode materials for a lithium-ion secondary battery. The new layered-type compounds were prepared using a combinatorial material-preparation system based on electrostatic spray deposition (the “M-ist Combi” system), and combinatorial powder X-ray diffraction. The composition region of the new compounds (Li_α(Ni_xCo_yTi_z)O₂ (α∼1, 0 ≤ x ≤ 1, 0 ≤ y ≤ 1, z∼0.2, x + y + z = 1.0)) was found to be wider than the composition region previously reported (LiNi_0.8−yCo_0.2Ti_yO₂ (0 ≤ y ≤ 0.1)).     

Raman scattering and room temperature ferromagnetism in Co-doped SrTiO3 particles

Raman scattering has been used to study the influence of cobalt, an effective dopant to obtain SrTiO₃ magnetic oxide, on the lattice dynamics of SrTiO₃. It is found that Co doping increases the lattice defects and induces a Raman vibration mode of 690 cm⁻¹. On the other hand, the ferromagnetism dependence on the x and annealing temperature was clearly and coherently observed in SrTi_1−xCo_xO₃ (x = 0, 0.01, 0.03 and 0.05) nanoparticles. It is found that the ferromagnetism of SrTi_1−xCo_xO₃ nanoparticles is weakly related to crystal deformation and oxygen vacancies in SrTiO₃. So, F-center model can explain the origin of the ferromagnetism in the prepared Co-doped SrTiO₃ samples. At the same time, the finding of large room-temperature ferromagnetism (1.6 emu/g) in this system would stimulate further interest in the area of more complicated ternary oxides.     

Effect of allied and alien ions on the EPR spectrum of Mn-containing lithium-manganese spinel oxides

Electron paramagnetic resonance spectroscopy was used for studying the effect of allied and alien ions on the EPR spectrum of Mn⁴⁺-containing lithium-manganese spinel oxides. Manganese spinel oxides with paramagnetic Mn⁴⁺ and diamagnetic substituents in the 16d spinel sites were studied: Li[Mg_0.5Mn_1.5]O₄, Li[Mg_0.5−xCo_2xMn_1.5−x]O₄, 0<x≤0.5, and Li[Li_1/3Mn_5/3]O₄. Ni²⁺-ions with integer-spin-ground state (S=1) were selected as alien ions: Li[Mg_0.5−xNi_xMn_1.5]O₄ (0≤x≤0.5), Li[Li_(1−2x)/3Ni_xMn_(5−x)/3]O₄ (0≤x≤0.5), and Li[Ni_0.5Mn_1.5−yTi_y]O₄ (0≤y≤1.0). It was shown that in Ni-substituted oxides the low temperature EPR response comes from magnetically correlated Ni-Mn spins, while at high registration temperature Mn⁴⁺ ions give rise to the EPR profile. Analysis of the EPR line width allows differentiating between the contributions of the density of paramagnetic species and the strength of the exchange interactions in magnetically concentrated systems. The density of allied and alien paramagnetic species has no effect on the EPR line width in cases when the strengths of antiferro- and ferromagnetic interactions on an atomic site are close. On the contrary, when antiferro- or ferromagnetic interactions on an atomic site are dominant, the EPR line width increases with the density of paramagnetic species.     

(Mo + N) codoped TiO2 for enhanced visible-light photoactivity

A series of Ti_1−xMo_xO_2−yN_y samples were prepared by using sol-gel method and characterized by X-ray diffraction, transmission electron microscopy and UV-vis absorption spectroscopy. All Ti_1−xMo_xO_2−yN_y samples are anatase phase. It is found that Mo, N mono-doping can increase visible light absorption, while (Mo + N) co-doping can greatly enhance absorption in whole visible region. Results of our first-principles band structure calculations reveal that (Mo + N)-doping, especially passivated co-doping can increase the up-limit of dopant concentration and create more impurity bands in the band gap of TiO₂, which leads to a greatly increase of its visible-light absorption without a decrease of its redox potential. It reveals that (Mo + N) co-doped TiO₂ is promising for a photocatalyst with high photocalystic activity under visible light.     

氧压对SrTiO3和SrNb0.2Ti0.8O3薄膜晶格参数的影响及激光感生热电电压效应

采用脉冲激光沉积技术制备了SrTiO₃和SrNb_0.2Ti_0.8O₃薄膜.X射线衍射分析表明在LaAlO₃(100)单晶平衬底上生长的SrTiO₃及SrNb_0.2Ti_0.8O₃薄膜是沿［001］取向的近外延生长.随着氧压在一定范围内逐渐增大,SrTiO₃薄膜的晶格参数减小,而SrNb_0.2Ti_0.8O₃薄膜的晶格参数先减小后增大.同时摸索出制备具有二维电子气超晶格(SrTiO₃/SrNb_0.2Ti_0.8O₃)_L的最佳氧压为1.0×10^-2Pa.另外在LaAlO₃(100)倾斜衬底上制备的SrNb_0.2Ti_0.8O₃薄膜中观察到激光感生热电电压效应. 关键词： 0.2Ti_0.8O₃薄膜')" href="#">SrNb_0.2Ti_0.8O₃薄膜 晶格参数 激光感生热电电压 脉冲激光沉积     

Enhanced luminescence of Ca3B2O6:Dy phosphors by Na-codoping for LED applications

The Ca_2.95−yDy_0.05B₂O₆:yNa⁺ (0≤y≤0.20) phosphors were synthesized at 1100 °C in air by the solid-state reaction route. The as-synthesized phosphors were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE), photoluminescence (PL) spectra and thermoluminescence (TL) spectra. The PLE spectra show the excitation peaks from 300 to 400 nm due to the 4f-4f transitions of Dy³⁺. This mercury-free excitation is useful for solid-state lighting and light-emitting diodes (LEDs). The emission of Dy³⁺ ions on 350 nm excitation was observed at 480 nm (blue) due to the ⁴F_9/2→⁶H_15/2 transitions, 575 nm (yellow) due to ⁴F_9/2→⁶H_13/2 transitions and 660 nm (red) due to weak ⁴F_9/2→⁶H_11/2 emissions. The PL results from the investigated Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors show that Dy³⁺ emissions increase with the increase of the Na⁺ codoping ions. The integral intensity of yellow to blue (Y/B) can be tuned by controlling Na⁺ content. By the simulation of white light, the optimal CIE value (0.328, 0.334) can be achieved when the content of Na⁺-codoping ions is y=0.2. The results imply that the Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors could be potentially used as white LEDs.     

La substitution in four-layers Aurivillius phase SrBi4Ti4O15

Ceramics with the nominal composition of SrBi_4−xLa_xTi₄O₁₅ have been prepared within the range of 0≤x≤1.8, and the dielectric properties are investigated. Single phase SrBi_4−xLa_xTi₄O₁₅ solid solution exists until the secondary phase of La_2/3TiO₃ appears at x=1.6. The Curie temperature is 520 °C for pure SrBi₄Ti₄O₁₅, and it shifts to low temperature with increasing x, which is due to the smaller structural distortion caused by La³⁺ substitution. In addition, the dielectric constant anomaly is suppressed with the substitution. No dielectric relaxation behavior is observed. When x≥1.2, the paraelectric state is attained in the present ceramics. La³⁺ substitution effects on the SrBi₄Ti₄O₁₅ ceramics are also compared with the previous work on Bi_4−xLa_xTi₃O₁₂.     

Dielectric characteristics of cation deficient TbMnO3

Cation deficient polycrystalline Tb_1−xMnO₃ (x= 0.05, 0.10) and TbMn_1−yO₃ (y =0.05, 0.10) samples were fabricated by conventional solid-state reaction. The complex dielectric properties of the cation deficient TbMnO₃ were investigated as the function of temperature (77 K≤T≤350 K) and frequency (100 Hz≤ f≤ 200 kHz) separately. Compared to the parent TbMnO₃, the cation deficient TbMnO₃ samples exhibit not only high dielectric constant but also low dissipation factor. Nyquist plots of complex impedance show that the dielectric properties originate from two main relaxation sources, i.e. bulk contributions and grain boundary effects.     

Luminescent properties of HTP AgGd1−xW2O8:Eux and AgGd1−x(W1−yMoy)2O8:Eux phosphor for white LED

Intense red phosphors, AgGd_1−xEu_x(W_1−yMo_y)₂O₈ (x=0.0-1.0, y=0.0-1.0), have been synthesized through traditional solid-state reaction and characterized by X-ray diffraction (XRD) and photoluminescence (PL). XRD results reveal that AgGd_1−xEu_xW₂O₈ synthesized at 1000 °C has a tetragonal crystal structure, which is named as high temperature phase (HTP) AgGdW₂O₈. All phosphors compositions with Eu³⁺ show red and green emission on excitation either in the charge-transfer or Eu³⁺ levels. Analysis of the emission spectra with different Eu³⁺ concentrations reveal that the optimum dopant concentration for Eu³⁺ is x=0.6 in the HTP AgGd_1−xEu_xW₂O₈ (x=0.0-1.0). Studies on the AgGd_0.4Eu_0.6(W_1−yMo_y)₂O₈ (y=0.0-1.0) and AgGd_1−xEu_x(W_0.7Mo_0.3)₂O₈ (x=0.0-1.0) show that the emission intensity is maximum for compositions with y=0.3 and x=0.5, respectively, and a decrease in emission intensity is observed for higher y or x values. The Mo⁶⁺ and Eu³⁺ co-doped AgGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped AgGd(WO₄)₂ in UV region. The intense emission of the tungstate/molybdate phosphors under 394 and 465 nm excitations, respectively, suggests that these materials are promising candidates as red-emitting phosphors for near-UV/blue GaN-based white LED for white light generation.     

Control of luminescence and conductivity of delafossite-type CuYO2 by substitution of rare earth cation (Eu, Tb) and/or Ca cation for Y cation

Delafossite-type oxides of CuTb_yY_1−yO₂, CuEu_yY_1−yO₂, CuCa_xTb_yY_1−x−yO₂ and CuCa_xEu_yY_1−x−yO₂ have been prepared by solid state reactions. The lattice-parameter dependence on the composition implies substitution of the Tb³⁺, Eu³⁺ and Ca²⁺ cations for the Y³⁺ site. Noticeable sharp emission lines due to the f-f transitions (⁵D₄→⁷F_J, J=3-6) of Tb³⁺ or due to the f-f transitions (⁵D₀→⁷F_J, J=0-4) of Eu³⁺ are observed at room temperature. Electrical conductivities of CuCa_xTb_yY_1−x−yO₂ and CuCa_xEu_yY_1−x−yO₂ are larger than those of CuTb_yY_1−yO₂ and CuEu_yY_1−yO₂, indicating the increase of the hole concentration caused by the substitution of Ca²⁺ for the Y³⁺ site. These results indicate the controllability of the luminescence and conductivity in CuCa_xTb_yY_1−x−yO₂ and CuCa_xEu_yY_1−x−yO₂ delafossite-type oxides by simultaneous substitution of the rare earth Tb³⁺ or Eu³⁺ cation and the Ca²⁺ cation for the Y³⁺ site.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

Fabrication of FeSe1−x superconducting films with bulk properties

We have fabricated high-quality FeSe_1−x superconducting films with a bulk T_c of 11–12 K on different substrates, Al₂O₃(0 0 0 1), SrTiO₃(1 0 0), MgO(1 0 0), and LaAlO₃(1 0 0), by using a pulsed laser deposition technique. All the films were grown at a high substrate temperature of 610 °C, and were preferentially oriented along the (1 0 1) direction, the latter being to be a key to fabricating of FeSe_1−x superconducting thin films with high T_c. According to the energy dispersive spectroscopy data, the Fe:Se composition ratio was 1:0.90 ± 0.02. The FeSe_1−x film grown on a SrTiO₃ substrate showed the best quality with a high upper critical magnetic field [H_c2(0)] of 56 T.     

A novel UV-emitting phosphor: Li6CaB3O8.5:Pb

Pure Li₆CaB₃O_8.5 and Li₆Ca_1−xPb_xB₃O_8.5 (0.005≤x≤0.04) materials were prepared by a solution combustion synthesis method. The phase of synthesized materials was determined using the powder XRD and FTIR. The synthesized materials were investigated using spectrofluorometer at room temperature. The emission and excitation bands of the synthesized phosphors were observed at 307 and 268 nm, respectively. The dependence of the emission intensity on the Pb²⁺ concentration for the Li₆Ca_1−xPb_xB₃O_8.5 (0.005≤x≤0.04) was studied and observed that the optimum concentration of Pb²⁺ in phosphor is 0.01 mol. The Stokes shift of the synthesized phosphor was calculated to be 4740 cm^-1.     

Hf1−xSixOy dielectric films deposited by UV-photo-induced chemical vapour deposition (UV-CVD)

Hf_1−xSi_xO_y is an attractive candidate material for high-k dielectrics. We report in this work the deposition of ultra-thin Hf_1−xSi_xO_y films (0.1 ≤ x ≥ 0.6) on silicon substrate at 450 °C by UV-photo-induced chemical vapour deposition (UV-CVD) using 222 nm excimer lamps. Silicon(IV) and hafnium(IV) organic compounds were used as the precursors. Films from around 5 to 40 nm in thickness with refractive indices from 1.782 to 1.870 were grown. The deposition rate was found to be of 6 nm/min at a temperature of 450 °C. The physical, interfacial and electrical properties of hafnium silicate (Hf_1−xSi_xO_y) thin films were investigated by using X-ray photoelectron spectroscopy, ellipsometry, FT-IR, C-V and I-V measurements. XRD showed that they were basically amorphous, while Fourier transform infrared spectroscopy (FT-IR), clearly revealed Hf-O-Si absorption in the photo-CVD deposited Hf_1−xSi_xO_y films. Surface and interfacial properties were analysed by TEM and XPS. It is found that carbon content in the films deposited by UV-CVD is very low and it also decreases with increasing Si/(Si + Hf) ratio, as low as about 1 at.% at the Si/(Si + Hf) ratio of 60 at.%.     

Combinatorial synthesis and optical characterization of alloy and superlattice films based on SrTiO3 and LaAlO3

We have grown alloy and superlattice films consisting of SrTiO₃ (STO) and LaAlO₃ (LAO) by pulsed laser deposition using composition-spread technique. All the (STO)_x(LAO)_1−x (0 ≤ x ≤ 1) alloy and superlattice films exhibited a single-phase perovskite structure. The optical properties of these films were characterized by absorption spectroscopy at room temperature. The spectra show a broad absorption due to O 2p-Ti 3d(t_2g) transition in an ultraviolet region. We found that absorption edges of both alloy and superlattice films systematically shifted to higher energy with increasing LAO composition. Clear difference was observed in the composition dependence of the indirect and a direct band edges.     

Photoluminescence properties of Eu in Y(PO3)3 under VUV excitation

The photoluminescence properties of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) are investigated. The excitation spectrum of Y_0.85(PO₃)₃:0.15Eu₃⁺ shows that both the (PO₃)₃³⁻ groups and the CT bands of O²⁻-Y³⁺ can efficiently absorb the excitation energy in the region of 120-250 nm. Under 147 nm excitation, the optimal emissive intensity of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) is about 36% of the commercial phosphor (Y,Gd)BO₃:Eu³⁺, which hints that the absorbed energy by the host matrix could be efficiently transferred to Eu³⁺. We try to study the concentration quenching mechanism of Y_1−x(PO₃)₃:xEu³⁺ (0<x≤0.2) under 147 and 172 nm excitation.     

Promotion of surface SOx on the selective catalytic reduction of NO by hydrocarbons over Ag/Al2O3

The promotion of sulfur oxides on the selective catalytic reduction (SCR) of NO by hydrocarbons in the presence of a low concentration of sulfur oxides over Ag/Al₂O₃ has been investigated by a flow reaction test and in situ infrared spectroscopy. When the C₃H₆ (or C₁₀H₂₂) + NO + O₂ feed-flow reaction was tested, maximum NO reduction was below 30% over fresh Ag/Al₂O₃. After the addition of SO₂ to the feed flow, conversion increased slightly. Conversion increased further after SO₂ was cut-off from the feed flow. This demonstrated that the increase in NO reduction activity of the catalyst was related to SO_x adsorbed on the catalyst. SO_x adsorbed on the catalytic surface (1375 cm⁻¹) was detected by IR spectroscopy and was stable within the temperature range. NCO species, as an intermediate in NO reduction, on SO_x-adsorbed Ag/Al₂O₃ in a C₃H₆ + NO + O₂ feed flow was observed in in situ IR spectra during the elevation of the reaction temperature from 473 to 673 K, while it was only observed at 673 K on fresh Ag/Al₂O₃ under the same experimental conditions. We suggest that SO_x in low concentrations depressed the combustion of reductants by contaminating hydrocarbon combustion active sites on the catalyst, resulting in an increase in NO reduction efficiency of the reductants.     

Dielectric properties and temperature stability of BaTiO3 co-doped La2O3 and Tm2O3

The influence of La₂O₃ and Tm₂O₃ co-doping on the dielectric properties and the temperature stability of BaTiO₃ was investigated. BaTiO₃ ceramics were prepared with the compositional formula of (Ba_1−xLa_x)(Ti_1-x/4−yTm_y)O₃. La₂O₃ and Tm₂O₃ co-doping in BaTiO₃ mainly had effects on an increase in the dielectric constant and the temperature stability, respectively. The increase of La₂O₃ concentration and the decrease of Tm₂O₃ concentration in BaTiO₃ resulted in a decrease of lattice parameter and tetragonality because La³⁺ ion substituting for Ba site is smaller than Ba²⁺ ion and Tm³⁺ ion substituting for Ti site is larger than Ti⁴⁺ ion. With the increase of La₂O₃ and the decrease of Tm₂O₃, the dielectric constant of BaTiO₃ was enhanced in spite of the reduction of tetragonality. P-E hysteresis measurements revealed that this phenomenon was based on the improvement of remanent polarization with the increase of La₂O₃ concentration. The introduction of excess Tm₂O₃ in BaTiO₃ suppressed the grain growth and BaTiO₃ ceramics showed higher temperature stability due to the stable tetragonal structure and the small grain size with the increase of Tm₂O₃ concentration.     

Electrical conductivity and complex electric modulus of titanium doped nickel-zinc ferrites

The samples Ni_1+x−yZn_yTi_x Fe_2−2xO₄; y=0.1, 0.0≤x≤0.5 were prepared in a single-phase spinel structure as indicated from X-ray analysis. Electrical conductivity and dielectric measurements at different temperatures from 300 K to 600 K in the frequency range from 42 Hz to 5 MHz have been analyzed. The relation of conductivity with temperature revealed a semiconductor to semimetallic behavior as Ti⁴⁺ concentration increases. The conduction mechanism depends mainly on the valence exchange between the different metal ions in the same site or in different sites. The dielectric constant as a function of temperature and frequency showed that there is a strong dependence on the compositional parameter x. The electrical modulus has been employed to study the relaxation dynamics of charge carriers. The result indicates the presence of correlation between motions of mobile ion charges. The activation energies extracted from M′(ω) and M″(ω) peaks are found to follow the Arrhenius law. The electrical conductance of the samples found to be dependent on the temperature and frequency.     

Effect of microstructure on the conductivity of a NASICON-type lithium ion conductor

Sintering temperature is used to control the microstructure of Li_{1 + x + y}Al_xTi_2 − xSi_yP_3 − yO₁₂ (x = 0.3, y = 0.2), a NASICON-type glass-ceramic. Scanning Electron Microscope imaging, X-Ray Diffraction, and Electrochemical Impedance Spectroscopy are employed to show that increase in sintering temperature increases conductivity while generating secondary crystalline phases. Total conductivity is as high as 3.81 × 10⁻⁴ S cm⁻¹ for sintering temperatures above 1000 °C. Crystallization of dielectric phases places the optimal sintering temperature in the 900 °C to 1000 °C range. Thermal analysis of the glass precursor reveals the glass transition, and crystallization temperatures.