Mössbauer spectroscopy and magnetic properties in thin films of FexNi100−x electroplated on silicon (1 0 0)

Fe_xNi_100−x thin films were produced by galvanostatic electrodeposition on Si (1 0 0), nominal thickness 2800 nm, and x ranging 7-20. The crystalline structure of the sample was determined by X-ray diffraction (XRD). The magnetic properties were investigated by vibration sample magnetometry (VSM) and room temperature ⁵⁷Fe Mössbauer spectroscopy. Conversion Electron Mössbauer spectroscopy (CEMS) in both film surfaces for the thick self-supported films showed that the magnetic moment direction is in the plane and conventional transmission (MS) that the directions are out of the plane films. The results were interpreted assuming a three-layer model where the external layer has in-plane magnetization and the internal one, out of plane magnetization.     

Magnetic study of nanostructured zinc ferrite irradiated with 100 MeV O-beam

Nanostructured zinc ferrite of particle size 10 nm was synthesized by using the nitrates of appropriate cations and citric acid. This system was irradiated by 100 MeV oxygen beam with the fluence of 5×10¹³ ions/cm². The particle size of the system remains almost same after the irradiation. We observe decrease in magnetization of the sample after irradiation at 300 and 10 K. The nature of the σ-H plot shows the presence of superparamgnetic domains at 300 K even after irradiation. The blocking temperature decreases from 276 to 63 K after irradiation. The Mössbauer spectroscopy supports the presence of superparamgnetic domains at 300 K in both the samples. The decrease in magnetization after irradiation is attributed to the decrease in cation inversion and increase in canting angle as observed from in-field Mössbauer spectroscopy.     

Magnetism of ferriprotoporphyrin IX monomers and dimers

The SQUID and the ⁵⁷Fe Mössbauer spectroscopy studies of the magnetic properties of monomeric and dimeric forms of iron porphyrin were performed between 2 and 305 K. The effective magnetic relaxation rate of the Fe atoms in iron porphyrin monomers exhibits complex temperature dependence, resulting from the competing spin-spin and spin-lattice relaxation processes. The dimerization of iron porphyrin dramatically speeds up the magnetic relaxation. The Fe-Fe antiferromagnetic exchange coupling constant in Fe-O-Fe dimer is J≈−110 cm⁻¹. The complementary application of SQUID and the Mössbauer spectroscopy is proposed as a new precise quantitative analytical methodology for monitoring of the aggregation process of iron porphyrin.     

Molecular material—{N(n-C4H9)4[Ni(II)0.5 Fe(II)0.5 Fe(III)(C2O4)3]}∞: Magnetic, Mössbauer and electrical conductivity studies

We have attempted to characterize the magnetic and electrical properties of a new mixed-metal molecular material {NBu₄[Ni(II)_0.5Fe(II)_0.5Fe(III)(ox)₃]}_N synthesized by the use of trioxalatoferrate as the building block. Mössbauer spectroscopy was utilized in order to understand local spin structures in this compound. The results indicate that the compound is a semiconducting ferrimagnet with T_N=30 K and room temperature conductivity of 6×10⁻¹⁵ Ω⁻¹ cm⁻¹ along with 1.8 eV activation energy under dark. The compound has no appreciable electrical response towards illumination.     

PLD of Fe3O4 thin films: Influence of background gas on surface morphology and magnetic properties

Ablation of Fe₃O₄ targets has been performed using a pulsed UV laser (KrF, λ = 248 nm, 30 ns pulse duration) onto Si(100) substrates, in reactive atmospheres of O₂ and/or Ar, with different oxygen partial pressures. The as-deposited films were characterised by atomic force microscopy (AFM), X-ray diffraction (XRD), conversion electron Mössbauer spectroscopy (CEMS) and extraction magnetometry, in order to optimise the deposition conditions in the low temperature range. The results show that a background mixture of oxygen and argon improves the Fe:O ratio in the films as long as the oxygen partial pressure is maintained in the 10⁻² Pa range. Thin films of almost stoichiometric single phase polycrystalline magnetite, Fe_2.99O₄, have been obtained at 483 K and working pressure of 7.8 × 10⁻² Pa, with a high-field magnetization of ∼490 emu/cm³ and Verwey transition temperature of 112 K, close to the values reported in the literature for bulk magnetite.     

The role of iron in the formation of the magnetic structure and related properties of La0.8Sr0.2Co1−xFexO3 (x=0.15, 0.2, 0.3)

La_0.8Sr_0.2Co_1−xFe_xO₃ (x=0.15, 0.2, 0.3) samples were studied by means of AC magnetic susceptibility, magnetization, magnetoresistance and ⁵⁷Fe Mössbauer spectrometry. Iron was found to take on a high spin 3d^5−α electronic state in each of the samples, where α refers to a partly delocalized 3d electron. The compounds were found to exhibit a spin-cluster glass transition with a common transition temperature of ∼53 K. The spin-cluster glass transition is visualized in the ⁵⁷Fe Mössbauer spectra as the slowing down of magnetic relaxation below ∼70 K, thereby showing that iron takes part in the formation of the glassy magnetic phase. The paramagnetic-like phase found at higher temperatures is identified below T_c≈195 K as being composed of weakly interacting, magnetically ordered nanosized clusters of magnetic ions in part with a magnetic moment oriented opposite to the net magnetic moment of the cluster. For each of the samples a considerable low-temperature negative magnetoresistance was found, whose magnitude in the studied range decreases with increasing iron concentration. The observed results obtained on the present compounds are qualitatively explained assuming that the absolute strengths of magnetic exchange interactions are subject to the relation ∣J_Co–Co∣<∣J_Fe–Co∣<∣J_Fe–Fe∣.     

Stress relaxation in Fe/Si neutron supermirrors by He irradiation

Magnetic supermirrors are widely used in polarized neutron applications. A key issue in producing these multilayer structures is to avoid residual stress in the layers, which may cause the layers to peel off. In this work He⁺ ion irradiation of 500 keV energy was applied at fluences of 1, 24, 50, 100×10¹⁴ ions/cm² with the aim of reducing residual stress. Structural, magnetic and neutron-optical properties were investigated by grazing incidence high-angle X-ray diffraction, magneto-optical Kerr effect, conversion electron Mössbauer spectroscopy and polarized neutron reflectometry. We find a monotonous decrease of the tensile stress upon irradiation from 1.76 to 0.37 GPa with a coupled decrease of neutron reflectivity at the critical angle and decrease of the maximum polarizing efficiency from 23% to 4% at the highest fluence compared to the as-prepared reference supermirror. The supermirrors exhibit a superposition of uniaxial and fourfold in-plane magnetic anisotropy.     

Mössbauer spectroscopy studies of spin reorientations in amorphous and crystalline (Co0.2Fe0.8)72.5Si12.5B15 glass coated micro-wires

Thermo-gravimetric, differential scanning calorimetry and comprehensive ⁵⁷Fe Mössbauer spectroscopy studies of amorphous and crystalline ferromagnetic glass coated (Co_0.2Fe_0.8)_72.5Si_12.5B₁₅ micro-wires have been recorded. The Curie temperature of the amorphous phase is T_C(amorp) ∼730 K. The analysis of the Mössbauer spectra reveals that below 623 K the easy axis of the magnetization is axial-along the wires, and that a tangential or/and radial orientation occurs at higher temperatures. At 770 K, in the first 4 hours the Mössbauer spectrum exhibits a pure paramagnetic doublet. Crystallization and decomposition to predominantly α-Fe(Si) and Fe₂B occurs either by raising the temperature above 835 K or isothermally in time at lower temperatures. Annealing for a day at 770 K, leads to crystallization. In the crystalline material the magnetic moments have a complete random orientation. After cooling back to ambient temperature, both α-Fe(Si) and Fe₂B in the glass coated wire show pure axial magnetic orientation like in the original amorphous state. The observed spin reorientations are associated with changes in the stress induced by the glass coating.     

Relationship between structural and magnetic properties in (Ti,Fe)O2 powders obtained by mechanical milling

Fe-doped TiO₂ samples with different Fe content were prepared by mechanical alloying starting from TiO₂ rutile and FeO. The samples were structurally and magnetically characterized by XRD, Mössbauer spectroscopy, X-ray absorption spectroscopy (XAS), AC-susceptibility and magnetization measurements. XAS results showed that Fe ions were incorporated into the rutile phase with oxygen coordination that was lower than that expected in this phase. The oxygen coordination number decreased with the increase of Fe²⁺ ions such as it was previously found in the milled samples of TiO₂ doped with hematite. The RT Mössbauer spectra were reproduced using two paramagnetic interactions, one corresponding to Fe²⁺ (δ∼0.87 mm/s) and the other to Fe³⁺ (δ∼0.31 mm/s). Magnetometry measurements showed the presence of paramagnetic and ferromagnetic-like interactions at room temperature. Although saturation and coercivity of the ferromagnetic phase increased with iron, the effective magnetic moment per iron atom decreased, probably due to the precipitation of Fe rich antiferromagnetic structures.     

Heat-induced charge transfer in cobalt iron cyanide

The heating of Co(2+) ferricyanide above 80 °C induces an inner charge transfer from Co(2+) towards Fe(III) to form the mixed valence system Co(2+)Co(III) ferri- ferro-cyanide. This charge transfer takes place preserving the material framework and forming a solid solution of the initial and final species. The cell edge of the cubic cell (Fm-3m) of this solid solution follows a regular variation with the material composition. This mixed valence system was characterized using X-ray diffraction, infrared, thermo-gravimetric, Mössbauer and magnetic measurements. Its formation is easily detected by the appearance of an intermediate ν(CN) absorption band in the infrared spectra at around 2120 cm⁻¹, 40 cm⁻¹ below and above the observed frequency for this vibration in Co(2+) ferri- and ferro-cyanide, respectively.     

Study of [Fe(pyim)3] complexes: dynamic spin equilibrium on encapsulation in zeolite Y

Tris complex of Fe^II2(2′-pyridyl)imidazole has been encapsulated in the supercages of zeolite Y and characterized by using powder XRD, FTIR, Mössbauer spectroscopy, variable temperature magnetization and MAS NMR techniques and results have been compared with those obtained for this complex with ClO₄⁻ and SO₄²⁻ as anions. At room temperature, the [Fe(pyim)₃](ClO₄)₂ complex exhibited low spin state, while [Fe^II(pyim)₃]SO₄ exhibited the existence of both low and high spin states. The encapsulated [Fe^II(pyim)₃]²⁺ complex exhibited a broad quadrupole doublet characterized by isomer shift, δ=+0.55 mm/s and quadrupole splitting ΔE_q=1.26 mm/s. The magnetization measurements carried out for the encapsulated [Fe^II(pyim)₃]²⁺ complex showed a systematic decrease in its values with decreasing temperature down to 75 K with no indication of thermal hysteresis effects. These results suggest the existence of a dynamic spin state equilibrium between the high and low spin states for the encapsulated [Fe^II(pyim)₃]²⁺ complex with time constant comparable to the characteristic Mössbauer time scale of ⁵⁷Fe nuclei.     

Large vertical loop shifts in mechanically synthesized (Mn,Fe)2O3−t nanograins

Magnetic properties of zero field cooled (ZFC) and field cooled (FC) sample of (Mn,Fe)₂O_3−t nanograins have been investigated by magnetometry (up to 70 kOe) and Mössbauer spectroscopy (up to 60 kOe) in the temperature interval 4.2–300 K. Large horizontal (up to 0.8 kOe) and vertical (up to 80%) shifts of the magnetization hysteresis loops are observed in the FC regime. The obtained results are discussed in terms of exchange interaction between an antiferromagnetic core and a spin-glass-like state of the nanograins boundaries. It is shown that hysteresis loop shifts (horizontal and vertical) depend on the field cooling magnitude, an effect that can be understood by the change of the boundary magnetic structure induced by the external magnetic field. The vertical magnetization shift is described by a phenomenological model, which takes into account the magnetic interaction between the spin-glass like boundary spins and the applied field.     

Influence of doping concentration on room-temperature ferromagnetism for Fe-doped BaTiO3 ceramics

Ba(Ti_1−xFe_x)O₃ ceramics (x=7, 30 and 70 at%) were prepared by solid-state reaction. All samples are single-phase with 6H-BaTiO₃-type hexagonal perovskite structure. Mössbauer spectra show all Fe atoms to be present as Fe³⁺ in BaTiO₃ lattice, occupying M1 octahedral and pentahedral sites. Room-temperature ferromagnetism is exhibited and saturation magnetization gradually decreases with increasing Fe content. The observed ferromagnetism is considered to be an intrinsic property of Ba(Ti_1−xFe_x)O₃, originating from super-exchange interactions between Fe³⁺ in different occupational sites associated with oxygen vacancies. The variation in magnetization with Fe content is related to the ratio of pentahedral to octahedral sites and oxygen vacancies.     

Synthesis and characterization of the xZnO-(1−x)α-Fe2O3 nanoparticles system

The xZnO-(1−x)α-Fe₂O₃ nanoparticles system has been obtained by mechanochemical activation for x=0.1, 0.3 and 0.5 and for ball milling times ranging from 2 to 24 h. Structural and morphological characteristics of the zinc-doped hematite system were investigated by X-ray diffraction (XRD) and Mössbauer spectroscopy. The Rietveld structure of the XRD spectra yielded the dependence of the particle size and lattice constant on the amount x of Zn substitutions and as function of the ball milling time. The x=0.1 XRD spectra are consistent with line broadening as Zn substitutes Fe in the hematite structure and the appearance of the zinc ferrite phase at milling times longer than 4 h. Similar results were obtained for x=0.3, while for x=0.5 the zinc ferrite phase occurred at 2 h and entirely dominated the spectrum at 24 h milling time. The Mössbauer spectra corresponding to x=0.1 exhibit line broadening as the ball milling time increases, in agreement with the model of local atomic environment. Because of this reason, the Mössbauer spectrum for 12 h of milling had to be fitted with two sextets. For x=0.3 and 12 milling hours, the Mössbauer spectrum reveals the occurrence of a quadrupole-split doublet, with the hyperfine parameters characteristic to zinc ferrite, ZnFe₂O₄. This doublet clearly dominates the Mössbauer spectrum for x=0.5 and 24 h of milling, demonstrating that the entire system of nanoparticles consists finally of zinc ferrite. As ZnO is not soluble in hematite in the bulk form, the present study clearly demonstrates that the solubility limits of an immiscible system can be extended beyond the limits in the solid state by mechanochemical activation. Moreover, this synthesis route allowed us to reach nanometric particle dimensions, which would make the materials very important for gas sensing applications.     

Structure and magnetic properties of (Nd,Dy)16(Fe,Co)76−xTixB8 powders prepared by mechanical alloying

Nanocrystalline (Nd,Dy)₁₆(Fe,Co)_76−xTi_xB₈ magnets were prepared by mechanical alloying and respective heat treatment at 973–1073 K/30–60 min. An addition of 0.5 at % of Ti results in an increase of coercivity from 796 to 1115 kA m⁻¹. Partial substitution of Nd by Dy results in an additional increase of coercivity up to 1234 kA m⁻¹. Mössbauer investigations shows that for x?1 the (Nd,Dy)₁₆(Fe,Co)_76−xTi_xB₈ powders are single phase. For higher Ti contents (x>1) the mechanically alloyed powders heat treated at 973 K are no more single phase, and the coercivity decreases due to the presence of an amorphous phase. A heat treatment at a higher temperature (1073 K) for longer time (1 h) results in the full recrystallisation of powders. The mean hyperfine field of the Nd₂Fe₁₄B phase decreases for titanium contents of 0?x?1, and remains constant for x>1. This indicates that the Ti content in the Nd₂Fe₁₄B phase reaches its maximum value.     

Correlation between site preference and magnetic properties of substituted strontium ferrite thin films

SrFe_12−x(Sn_0.5Zn_0.5)_xO₁₉ thin films with x=0−5 were synthesized by a sol-gel method on thermally oxidized silicon wafer (Si/SiO₂). The site preference and magnetic properties of Zn-Sn substituted strontium ferrite thin films were studied using ⁵⁷Fe Mössbauer spectroscopy and magnetic measurements. Mössbauer spectra displayed that the Zn-Sn ions preferentially occupy the 2b and 4f₂ sites. The preference for these sites is responsible for the anomalous increase in the magnetization at high Zn-Sn substitutions. X-ray diffraction (XRD) patterns and field emission scanning electron microscope (FE-SEM) micrographs demonstrated that single phase c-axis hexagonal ferrite films with rather narrow grain size distribution were obtained. Vibrating sample magnetometer (VSM) was employed to probe magnetic properties of samples. The maximum saturation of magnetization and coercivity at perpendicular direction were 265 emu/g and 6.3 kOe, respectively. It was found that the complex susceptibility has linear variation with static magnetic field.     

Anti-Invar properties and magnetic order in fcc Fe-Ni-C alloy

Anti-Invar effect was revealed in the fcc Fe-25.3%Ni-0.73%C (wt%) alloy, which demonstrates high values of thermal expansion coefficient (TEC) (15-21)×10⁻⁶ K⁻¹ accompanied by almost temperature-insensitive behavior in temperature range of 122-525 K. Alloying with carbon considerably expanded the low temperature range of anti-Invar behavior in fcc Fe-Ni-based alloy. The Curie temperature of the alloy T_C=195 K was determined on measurements of temperature dependences of magnetic susceptibility and saturation magnetization. The Mössbauer and small-angle neutron scattering (SANS) experiments on the fcc Fe-25.3%Ni-(0.73-0.78)%C alloys with the varying temperatures below and above the Curie point and in external magnetic field of 1.5-5 T were conducted. Low value of the Debye temperature Θ_D=180 K was estimated using the temperature dependence of the integral intensity of Mössbauer spectra for specified temperature range. The inequality B_eff=(0.7-0.9)B_ext was obtained in external field Mössbauer measurement that points to antiferromagnetically coupled Fe atoms, which have a tendency to align their spins perpendicular to B_ext. Nano length scale magnetic inhomogeneities nearby and far above T_C were revealed, which assumed that it is caused by mixed antiferromagnetically and ferromagnetically coupled Fe atom spins. The anti-Invar behavior of Fe-Ni-C alloy is explained in terms of evolution of magnetic order with changing temperature resulting from thermally varied interspin interaction and decreasing stiffness of interatomic bond.     

The interaction of Fe on MgO(1 0 0) surfaces

The atomic interaction and magnetic properties of ultrathin Fe films grown on cleaved and polished MgO(1 0 0) surfaces were studied by conversion electron Mössbauer spectroscopy (CEMS). ⁵⁷Fe layers were deposited as probe atoms in different layer positions in 10 ML thick Fe films. Fe layers of different thicknesses were formed on polished and cleaved substrate surfaces at RT deposition. The analysis of the spectra showed no Fe-O^2- interaction in MgO/Fe interface. FeO phase formation was excluded. The Mössbauer spectrum of 5 ML ⁵⁷Fe sample showed enhanced internal magnetic field at 80 K. No interdiffusion of ⁵⁷Fe and ⁵⁶Fe atoms was observed between the layers at room temperature.     

Mössbauer spectroscopic study of the thermal spin crossover in [Fe(II)(isoxazole)6](ClO4)2

The ⁵⁷Fe Mössbauer spectroscopy of mononuclear [Fe(II)(isoxazole)₆](ClO₄)₂ has been studied to reveal the thermal spin crossover of Fe(II) between low-spin (S=0) and high-spin (S=2) states. Temperature-dependent spin transition curves have been constructed with the least-square fitted data obtained from the Mössbauer spectra measured at various temperatures between 84 and 270 K during a cooling and heating cycle. This compound exhibits an unusual temperature-dependent spin transition behaviour with T_C(↓)=223 and T_C(↑)=213 K occurring in the reverse order in comparison to those observed in SQUID observation and many other spin transition compounds. The compound has three high-spin Fe(II) sites at the highest temperature of study of which two undergo spin transitions. The compound seems to undergo a structural phase transition around the spin transition temperature, which plays a significant role in the spin crossover behaviour as well as the magnetic properties of the compound at temperatures below T_C. The present study reveals an increase in high-spin fraction upon heating in the temperature range below T_C, and an explanation is provided.     

Ferromagnetic-to-antiferromagnetic transition in (Hf1−xTix)Fe2 intermetallic compounds induced by geometrical frustration of the Fe(2a) sites

The ferromagnetic-to-antiferromagnetic transition in the hexagonal (Hf_1−xTi_x)Fe₂ (0?x?1) intermetallic compounds has been investigated by ⁵⁷Fe Mössbauer spectroscopy. At 10 K, the transition occurs within rather narrow concentration limits, around x=0.55–0.65. We found that the key factor governing the unexpected quick change of the magnetic structure is the magnetic frustration of the Fe(2a) sites. The magnetic frustration is caused by the noncollinearity of the Fe(6h) magnetic sublattice. The noncollinearity arises from the rotation of the magnetic moments due to the competition between the ferromagnetic exchange interactions and the antiferromagnetic Fe(6h)–Ti–Fe(6h) interaction. In the compounds with x=0.4–0.6, the temperature transitions to the antiferromagnetic state are observed. As an example, the Hf_0.4Ti_0.6Fe₂ compound is completely antiferromagnetic above 200 K.