An efficient solid‐state polycondensation method for synthesizing stereocomplexed poly(lactic acid)s with high molecular weight

Simultaneous solid‐state polycondensation (SSP) of the powdery prepolymers of poly(L ‐lactic acid) (PLLA) and poly(D ‐lactic acid) (PDLA) can produce entire stereocomplexed poly(lactic acid)s (sc‐PLA) with high molecular weight and can be an alternative synthetic route to sc‐PLA. Ordinary melt polycondensations of L ‐ and D ‐lactic acids gave the PLLA and PDLA prepolymers having medium molecular weight which were pulverized for blending in 1:1 ratio. The resultant powder blends were then subjected to SSP at 130–160 °C for 30 h under a reduced pressure of 0.5 Torr. Some of the products thus obtained attained a molecular weight (M_w) as high as 200 kDa, consisting of stereoblock copolymer of PLLA and PDLA. A small amount of the stereocomplex should be formed in the boundaries of the partially melted PLLA and PDLA where the hetero‐chain connection is induced to generate the blocky components. The resultant SSP products showed predominant stereocomplexation after their melt‐processing in the presence of the stereoblock components in spite of containing a small amount of racemic sequences in the homo‐chiral PLLA and PDLA chains. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3714–3722, 2008     

Immiscibility–miscibility phase transformation in blends of poly(ethylene succinate) with poly(L‐lactic acid)s of different molecular weights

Using differential scanning calorimetry (DSC), polarizing optical microscopy (POM), and Fourier transformed infrared spectroscopy (FTIR), upper critical solution temperature (UCST) phase behavior with immiscibility–miscibility transformation in blends of poly(ethylene succinate) (PESu) with poly(lactic acid)s (PLAs), such as poly(D ,L ‐lactic acid) (PDLLA), poly(L ‐lactic acid) (PLLA), poly(D ‐lactic acid) (PDLA), differing in D/L configurations and molecular weights were investigated. All three binary blends of PDLLA/PESu, PLLA/PESu, and PESu/PDLA exhibit UCST behavior, which means they are immiscible at ambient temperature but can become miscible upon heating to higher temperatures at 240–268 °C depending on molecular weights. The PLLAs/PESu blends at UCST could be reverted back to the original phase‐separated morphology, as proven by solvent redissolution. The blends upon quenching from above UCST could be frozen into a quasi‐miscible state, where the Flory‐Huggins interaction parameter (χ₁₂) was determined to be a negative value (by melting point depression technique). The interaction between PDLLA and PESu in blend resulted in significant reduction in spherulite growth rate of PESu. Furthermore, blends of PESu with lower molecular weight PLLA or PDLA (M_w of PLLA and PDLA are 152,000 and 124,000 g/mol, respectively), instead of the higher M_w of PDLLA (M_w of PDLLA = 157,000 g/mol), are immiscible with UCST phase behavior, which are affected by molecular weights rather than the ratio of L/D monomer in the chemical structure of PLAs. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1135–1147, 2010     

Linear and four‐armed poly(l‐lactide)‐block‐poly(d‐lactide) copolymers and their stereocomplexation with poly(lactide)s

Linear and four‐armed poly(l ‐lactide)‐block‐poly(d ‐lactide) (PLLA‐b‐PDLA) block copolymers are synthesized by ring‐opening polymerization of d ‐lactide on the end hydroxyl of linear and four‐armed PLLA prepolymers. DSC results indicate that the melting temperature and melting enthalpies of poly (lactide) stereocomplex in the copolymers are obviously lower than corresponding linear and four‐armed PLLA/PDLA blends. Compared with the four‐armed PLLA‐b‐PDLA copolymer, the similar linear PLLA‐b‐PDLA shows higher melting temperature (212.3 °C) and larger melting enthalpy (70.6 J g^?1). After these copolymers blend with additional neat PLAs, DSC, and WAXD results show that the stereocomplex formation between free PLA molecular chain and enantiomeric PLA block is the major stereocomplex formation. In the linear copolymer/linear PLA blends, the stereocomplex crystallites (sc) as well as homochiral crystallites (hc) form in the copolymer/PLA cast films. However, in the four‐armed copolymer/linear PLA blends, both sc and hc develop in the four‐armed PLLA‐b‐PDLA/PDLA specimen, which means that the stereocomplexation mainly forms between free PDLA molecule and the inside PLLA block, and the outside PDLA block could form some microcrystallites. Although the melting enthalpies of stereocomplexes in the blends are smaller than that of neat copolymers, only two‐thirds of the molecular chains participate in the stereocomplex formation, and the crystallization efficiency strengthens. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 1560–1567     

Water‐disintegrative and biodegradable blends containing poly(L‐lactic acid) and poly(butylene adipate‐co‐terephthalate)

In this study, novel biodegradable materials were successfully generated, which have excellent mechanical properties in air during usage and storage, but whose structure easily disintegrates when immersed in water. The materials were prepared by melt blending poly(L ‐lactic acid) (PLLA) and poly(butylene adipate‐co‐terephthalate) (PBAT) with a small amount of oligomeric poly(aspartic acid‐co‐lactide) (PAL) as a degradation accelerator. The degradation behavior of the blends was investigated by immersing the blend films in phosphate‐buffered saline (pH = 7.3) at 40 °C. It was shown that the PAL content and composition significantly affected morphology, mechanical properties, and hydrolysis rate of the blends. It was observed that the blends containing PAL with higher molar ratios of L ‐lactyl [LA]/[Asp] had smaller PBAT domain size, showing better mechanical properties when compared with those containing PAL with lower molar ratios of [LA]/[Asp]. The degradation rates of both PLLA and PBAT components in the ternary blends simultaneously became higher for the blends containing PAL with higher molar ratios of [LA]/[Asp]. It was confirmed that the PLLA component and its decomposed materials efficiently catalyze the hydrolytic degradation of the PBAT component, but by contrast that the PBAT component and its decomposed materials do not catalyze the hydrolytic degradation of the PLLA component in the blends. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Characteristics of the biodegradability and physical properties of stereocomplexes between poly(L‐lactide) and poly(D‐lactide) copolymers

Random and block copolymerizations of L ‐ or D ‐lactide with ε‐caprolactone (CL) were performed with a novel anionic initiator, (C₅Me₅)₂SmMe(THF), and they resulted in partial epimerization, generating D ,L ‐ or meso‐lactide polymers with enhanced biodegradability. A blend of PLLA‐r‐PCL [82/18; PLLA = poly(L ‐LA) and PCL = poly(ε‐caprolactone)] and PDLA‐r‐PCL [79/21; PDLA = poly(D ‐LA)] prepared by the solution‐casting method generated a stereocomplex, the melting temperature of which was about 40 °C higher than that of the nonblended copolymers. A blend of PLLA‐b‐PCL (85/15) and PDLA‐b‐PCL (82/18) showed a lower elongation at break and a remarkably higher tensile modulus than stereocomplexes of PLLA‐r‐PCL/PDLA‐r‐PCL and PLLA/PDLA. The biodegradability of a blend of PLLA‐r‐PCL (65/35) and PDLA‐r‐PCL (66/34) with proteinase K was higher than that of PLLA‐b‐PCL (47/53) and PDLA‐b‐PCL (45/55), the degradability of which was higher than that of a PLLA/PDLA blend. A blend film of PLLA‐r‐PDLLA (69/31)/PDLA‐r‐PDLLA (68/32) exhibited higher degradability than a film of PLLA/PDLLA [PDLLA = poly(D ,L ‐LA)]. A stereocomplex of PLLA‐r‐PCL‐r‐PDMO [80/18/2; PDMO = poly(L ‐3,D ,L ‐6‐dimethyl‐2,5‐morpholinedion)] with PDLA‐r‐PCL‐r‐PDMO (81/17/2) showed higher degradability than PLLA‐r‐PDMO (98/2)/PDLA‐r‐PDMO (98/2) and PLLA‐r‐PCL (82/18)/PDLA‐r‐PCL (79/21) blends. The tensile modulus of a blend of PLLA‐r‐PCL‐r‐PDMO and PDLA‐r‐PCL‐r‐PDMO was much higher than that of a blend of PLLA‐r‐PDMO and PDLA‐r‐PDMO. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 438–454, 2005     

Crystal modifications and multiple melting behavior of poly(L‐lactic acid‐co‐D‐lactic acid)

The crystal modifications and multiple melting behavior of poly(L ‐lactic acid‐co‐D ‐lactic acid) (98/2) as a function of crystallization temperature were studied by wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry (DSC). It was found that the disorder (α′) and order (α) phases of poly(L ‐lactic acid) (PLLA) were formed in cold‐crystallized poly(L ‐lactic acid‐co‐D ‐lactic acid) samples at low (<110 °C) and high (≥110 °C) temperatures, respectively. A disorder‐to‐order (α′‐to‐α) phase transition occurred during the annealing process of the α′‐crystal at elevated temperatures, which proceeded quite slowly even at the peak temperature of the exotherm P_exo but much more rapidly at higher temperature close to the melting region. The presence or absence of an additional endothermic peak before the exotherm in the DSC thermograph of the α′‐crystal was strongly dependent on the heating rate, indicating that a melting process involved during the α′‐to‐α phase transition. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2011     

Synthesis of star‐shaped poly(D,L‐lactic acid‐alt‐glycolic acid)‐b‐poly(L‐lactic acid) with the poly(D,L‐lactic acid‐alt‐glycolic acid) macroinitiator and stannous octoate catalyst

Two types of three‐arm and four‐arm, star‐shaped poly(D,L ‐lactic acid‐alt‐glycolic acid)‐b‐poly(L ‐lactic acid) (D,L ‐PLGA50‐b‐PLLA) were successfully synthesized via the sequential ring‐opening polymerization of D,L ‐3‐methylglycolide (MG) and L ‐lactide (L ‐LA) with a multifunctional initiator, such as trimethylolpropane and pentaerythritol, and stannous octoate (SnOct₂) as a catalyst. Star‐shaped, hydroxy‐terminated poly(D,L ‐lactic acid‐alt‐glycolic acid) (D,L ‐PLGA50) obtained from the polymerization of MG was used as a macroinitiator to initiate the block polymerization of L ‐LA with the SnOct₂ catalyst in bulk at 130 °C. For the polymerization of L ‐LA with the three‐arm, star‐shaped D,L ‐PLGA50 macroinitiator (number‐average molecular weight = 6800) and the SnOct₂ catalyst, the molecular weight of the resulting D,L ‐PLGA50‐b‐PLLA polymer linearly increased from 12,600 to 27,400 with the increasing molar ratio (1:1 to 3:1) of L ‐LA to MG, and the molecular weight distribution was rather narrow (weight‐average molecular weight/number‐average molecular weight = 1.09–1.15). The ¹H NMR spectrum of the D,L ‐PLGA50‐b‐PLLA block copolymer showed that the molecular weight and unit composition of the block copolymer were controlled by the molar ratio of L ‐LA to the macroinitiator. The ¹³C NMR spectrum of the block copolymer clearly showed its diblock structures, that is, D,L ‐PLGA50 as the first block and poly(L ‐lactic acid) as the second block. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 409–415, 2002     

Novel poly(l‐lactide)/poly(d‐lactide)/poly(tetrahydrofuran) multiblock copolymers with a controlled architecture: Synthesis and characterization

Novel poly(l ‐lactide) (PLLA)/poly(d ‐lactide) (PDLA)/poly(tetrahydrofuran) (PTHF) multiblock copolymers with designed molecular structure were synthesized by a two‐stage procedure. Well‐defined PDLA‐PLLA‐PTHF‐PLLA‐PDLA pentablock copolymers were prepared by sequential ring opening polymerization of l ‐ and d ‐lactides starting from PTHF glycol, with the length of the (equimolar) PLLA and PDLA blocks being varied. Then, these dihydroxyl‐terminated pentamers were transformed into multiblock copolymers by melt chain‐extension with hexamethylene diisocyanate–being the first time that the coupling of pentablock units is reported. The successful formation of macromolecular chains with a multiblock and well‐defined architecture was demonstrated by ¹H NMR spectroscopy. The thermal properties and structuring of the resulting materials were investigated by means of DSC and WAXD measurements and DMA analysis. Stereocomplexation was found to be promoted during solution and melt crystallization. This approach affords materials combining the high rigidity and strength (other than improved thermal resistance) of the hard stereocomplex crystallites with the flexibility imparted by the soft block, whereby their properties can be finely tailored through the composition of the basic pentablock units without limitations on the final molecular weight. The adopted reaction conditions make this process highly appealing in view of the possibility to perform it in extruder. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 3269–3282     

Enhancing crystallization behavior for optimized performances of poly(TMC‐b‐(LLA‐ran‐GA)) by PDLA/PLLA stereocomplex crystallization

The blends of poly(1,3‐trimethylene carbonate‐b‐(l ‐lactide‐ran‐glycolide)) (PTLG) with poly(d ‐lactide) (PDLA) were prepared via solution‐casting method using CH₂Cl₂ as solvent. The poly(l ‐lactide) (PLLA) segments of PTLG with PDLA chain constructed as stereocomplex structures and growth stereocomplex crystals of PLA (sc‐PLA). The effects of sc‐PLA crystals on thermal behavior, mechanical properties, thermal decomposition of the PTLG/PDLA blends were investigated, respectively. The differential scanning calorimetry (DSC) and wide‐angle X‐ray diffraction (WAXD) results showed that the total crystallinity of the PTLG/PDLA blends was increased with the PDLA content increasing. Heterogeneous nucleation of sc‐PLA crystals induced crystallization of the PLLA segments in PTLG. The crystallization temperature of samples shifted to 107.5°C for the PTLG/PDLA‐20 blends compared with that of the PTLG matrix, and decreased the half‐time of crystallization. The mechanical measurement results indicated that the tensile strength of the PTLG/PDLA blends was improved from 21.1 MPa of the PTLG matrix to 39.5 MPa of PTLG/PDLA‐20 blends. The results of kinetics of thermal decomposition of the PTLG/PDLA blends by TGA showed that the apparent activation energy of the PTLG/PDLA blends was increased from 59.1 to 72.1 kJ/mol with the increasing of the PDLA content from 3 wt% to 20 wt%, which indicated the enhancement of thermal stability of the PTLG/PDLA blends by addition of PDLA. Furthermore, the biocompatibility of the PTLG/PDLA blends cultured with human adipose‐derived stem cells was evaluated by CCK‐8 and live/dead staining. The experiment results proved the PTLG/PDLA blends were a kind of biomaterial with excellent physical performances with very low cytotoxicity.     

Polyethylene‐poly(L‐lactide) diblock copolymers: Synthesis and compatibilization of poly(L‐lactide)/polyethylene blends

A model polyethylene‐poly(L ‐lactide) diblock copolymer (PE‐b‐PLLA) was synthesized using hydroxyl‐terminated PE (PE‐OH) as a macroinitiator for the ring‐opening polymerization of L ‐lactide. Binary blends, which contained poly(L ‐lactide) (PLLA) and very low‐density polyethylene (LDPE), and ternary blends, which contained PLLA, LDPE, and PE‐b‐PLLA, were prepared by solution blending followed by precipitation and compression molding. Particle size analysis and scanning electron microscopy results showed that the particle size and distribution of the LDPE dispersed in the PLLA matrix was sharply decreased upon the addition of PE‐b‐PLLA. The tensile and Izod impact testing results on the ternary blends showed significantly improved toughness as compared to the PLLA homopolymer or the corresponding PLLA/LDPE binary blends. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2755–2766, 2001     

Synthesis and properties of multiblock copolymers consisting of poly(L‐lactic acid) and poly(oxypropylene‐ co‐oxyethylene) prepared by direct polycondensation

A multiblock copoly(ester–ether) consisting of poly(l ‐lactic acid) (PLLA) and poly(oxypropylene‐co‐oxyethylene) (PN) was prepared and characterized. Preparation was done via the solution polycondensation of a thermal oligocondensate of l ‐lactic acid, a commercially available telechelic polyether (PN: Pluronic‐F68), and dodecanedioic acid as a carboxyl/hydroxyl adjusting agent. When stannous oxide was used as the catalyst, the molecular weight of the resultant PLLA/PN block copolymers became very high (even with a high PN content) under optimized reaction conditions. The refluxing of diphenyl ether (solvent) at reduced pressure allowed the efficient removal of the condensed water from the reaction system and the feed‐back of the intermediately formed l ‐lactide at the same time in order to successfully bring about a high degree of condensation. The copolymer films obtained by solution casting became more flexible with the increasing PN content as soft segments. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1513–1521, 1999     

Vibrational dynamics and heat capacity in poly(L‐lactic acid)

Poly(L ‐lactic acid) (PLLA) (? CH(CH₃) ? COO? )_n is a biodegradable polymer, which exhibits many applications in the biomedical field and where thermoplastics are employed. A comprehensive study of the normal modes and their dispersion in PLLA using Wilson′s GF matrix method as modified by Higgs is being reported. Assignments of calculated normal modes have been made and characteristic features of dispersion curves are discussed. Heat capacity has been calculated via density‐of‐states using Debye relation in the temperature range 10–250 K, which is in fairly good agreement with the experimental data. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 175–182, 2010     

Oriented crystallization of poly(L‐lactic acid) in uniaxially oriented blends with poly(vinylidene fluoride)

This article describes the oriented crystallization of poly(L ‐lactic acid) (PLLA) in uniaxially oriented blends with poly(vinylidene fluoride) (PVDF). Uniaxially drawn films of PLLA/PVDF blend with fixed ends were heat‐treated in two ways to crystallize PLLA in oriented blend films. The crystal orientation of PLLA depended upon the heat‐treatment process. The crystal c‐axis of the α form crystal of PLLA was highly oriented in the drawing direction in a sample cold‐crystallized at T_c = 120 °C, whereas the tilt‐orientation of the [200]/ [110] axes of PLLA was induced in the sample crystallized at T_c = 120 °C after preheating at T_p = 164.5–168.5 °C. Detailed analysis of the wide‐angle X‐ray diffraction (WAXD) indicated that the [020]/ [310] crystal axes were oriented parallel to the drawing direction, which causes the tilt‐orientation of the [200]/ [110] axes and other crystal axes. Scanning electron microscopy (SEM) suggested that oriented crystallization occurs in the stretched domains of PLLA with diameters of 0.5–2.0 μm in the uniaxially drawn films of PVDF/PLLA = 90/10 blend. Although the mechanism for the oriented crystallization of PLLA was not clear, a possibility was heteroepitaxy of the [200]/[110] axes of the α form crystal of PLLA along the [201]/[111] axes of the β form crystal of PVDF that is induced by lattice matching of d₁₀₀(PLLA) ≈ 5d₂₀₁(PVDF). © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 1376–1389, 2008     

Melt polycondensation of L‐lactic acid with Sn(II) catalysts activated by various proton acids: A direct manufacturing route to high molecular weight Poly(L‐lactic acid)

Poly(L ‐lactic acid) (PLLA) was produced by the melt polycondensation of L ‐lactic acid. For the optimization of the reaction conditions, various catalyst systems were examined at different temperature and reaction times. It was discovered that Sn(II) catalysts activated by various proton acids can produce high molecular weight PLLA [weight‐average molecular weight (M_w ) ≥ 100,000] in a relatively short reaction time (≤15 h) compared with simple Sn(II)‐based catalysts (SnO, SnCl₂ · 2H₂O), which produce PLLA with an M_w of less than 30,000 after 20 h. The new catalyst system is also superior to the conventional systems in regard to racemization and discoloration of the resultant polymer. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1673–1679, 2000     

Synthesis and characterization of multiblock copolymers based on L‐lactic acid,citric acid,and poly(ethylene glycol)

Because poly(L ‐lactic acid) (PLLA) is a biodegradable polyester with low immunogenicity and good biocompatibility, it is used as a biomaterial. However, hydrophobic PLLA does not have any reactive groups. Thus, its application is limited. To increase the hydrophilicity of PLLA and accelerate its degradation rate, functionalized pendant groups and blocks were introduced through copolymerization with citric acid and poly(ethylene glycol) (PEG), respectively. This article describes the synthesis and characterization of poly(L ‐lactic‐co‐citric acid) (PLCA)‐PLLA and PLCA‐PEG multiblock copolymers. The results indicated that the hydrolysis rate was enhanced, and the hydrophilicity was improved because of the incorporation of carboxyl groups in PLCA‐PLLA. The joining of the PEG block led to improved hydrophilicity of PLCA, and the degradation rate of PLCA‐PEG accelerated as compared with that of PLCA‐PLLA. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2073–2081, 2003     

Stereoselective Interaction between Isotactic and Optically Active Poly(lactic acid) and Phenyl‐Substituted Poly(lactic acid)

Isotactic and optically active poly(D ‐lactic acid) (PDLA) and phenyl‐substituted poly(lactic acid)s (Ph‐PLAs), i.e., poly(D ‐phenyllactic acid) (Ph‐PDLA) and poly(L ‐phenyllactic acid) (Ph‐PLLA), were synthesized and stereospecific interactions between the synthesized polymers were investigated by their thermal properties and crystallization behavior using differential scanning calorimetry (DSC). The DSC measurements indicated that PDLA is miscible with Ph‐PLAs and that the attractive interaction between PDLA and L ‐configured Ph‐PLA is higher than that between PDLA and D ‐configured Ph‐PDLA. In other words, the latter result means that poly(lactic acid) (PLA) has a higher stereoselective attractive interaction with Ph‐PLA with the reverse configuration than with Ph‐PLA of the same configuration. These results strongly suggest that PLA‐based materials with a wide variety of physical properties and biodegradability can be fabricated by blending them with substituted PLAs with the reverse and same configurations.

     

Temperature‐modulated differential scanning calorimetry studies on the origin of double melting peaks in isothermally melt‐crystallized poly(L‐lactic acid)

In this work, the melting behaviors of nonisothermally and isothermally melt‐crystallized poly(L ‐lactic acid) (PLLA) from the melt were investigated with differential scanning calorimetry (DSC) and temperature‐modulated differential scanning calorimetry (TMDSC). The isothermal melt crystallizations of PLLA at a temperature in the range of 100–110 °C for 120 min or at 110 °C for a time in the range of 10–180 min appeared to exhibit double melting peaks in the DSC heating curves of 10 °C/min. TMDSC analysis revealed that the melting–recrystallization mechanism dominated the formation of the double melting peaks in PLLA samples following melt crystallizations at 110 °C for a shorter time (≤30 min) or at a lower temperature (100, 103, or 105 °C) for 120 min, whereas the double lamellar thickness model dominated the formation of the double melting peaks in those PLLA samples crystallized at a higher temperature (108 or 110 °C) for 120 min or at 110 °C for a longer time (≥45 min). © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 466–474, 2007     

Mechanical properties and structure of the zone‐drawn poly(L‐lactic acid) fibers

The zone‐drawing (ZD) method was applied three times to the melt‐spun poly(L ‐lactic acid) (PLLA) fibers of low molecular weight (M_v = 13,100) at different temperatures under various tensions. The mechanical properties and superstructure of the ZD fibers were investigated. The resulting ZD‐3 fiber had a draw ratio of 10.5, birefringence of 37.31 × 10⁻³, and crystallinity of 37%, while an orientation factor of crystallites remarkably increased to 0.985 by the ZD‐1. The Young's modulus and tensile strength of the ZD‐3 fiber respectively attained 9.1 GPa and 275 MPa, and the dynamic storage modulus was 10.4 GPa at room temperature. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 991–996, 1999     

Effects of chain configuration on UCST behavior in blends of poly(L‐lactic acid) with tactic poly(methyl methacrylate)s

Chain configuration influences phase behavior of blends of poly(methyl methacrylate) (PMMA) of different tactic configurations (syndiotacticity, isotacticity, or atacticity) with poly(L ‐lactic acid) (PLLA). Blends system of sPMMA/PLLA is immiscible with an asymmetry‐shaped UCST at ～250 °C. The phase behavior of the sPMMA/PLLA blend is similar to the aPMMA/PLLA blend that has been already proven in the previous work to exhibit similar UCST temperatures (230–250 °C) and asymmetry shapes in the UCST diagrams. On the other hand, the iPMMA/PLLA blend remains immiscible up to thermal degradation without showing any transition to UCST upon heating. The blend system with UCST, that is, sPMMA/PLLA, can be frozen in a state of miscibility by quenching to rapidly solidify from the homogeneous liquid at UCST, where the T_g‐composition relationship for the sPMMA/PLLA blend fits well with the Gordon‐Taylor T_g model with k = 0.15 and the blend's T leads to χ₁₂ = ?0.26 for the UCST‐quenched sPMMA/PLLA blend. Both parameters (k and χ) as characterized for the frozen miscible blend suggest a relatively weak interaction between the two constituents (sPMMA and PLLA) in the blends. The interaction strength is likely not strong enough to maintain a thermodynamic miscibility when the blend is at ambient temperature or any lower temperatures below UCST. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2355–2369, 2008     

The effects of melt annealing and counterpart's molecular weight on the thermal properties and phase morphology of poly(L‐lactide)‐based blends

The thermal properties and phase morphology of poly(L ‐lactide) (PLLA)‐based blends have been studied. Two poly(ethylene glycol)s (PEGs) with molecular weight (MW) of about 1,500 (1.5k) g/mol and 2,000,000 (2M) g/mol, respectively, were used as counterparts. The blends were annealed at a preselected temperature of 200 °C for either 2 min or 30 min before the characterizations. Both PEGs were determined to enhance the crystallizability of PLLA. After a 2‐min process of annealing, the PEG(1.5k)'s crystallization efficiency on PLLA has been noted to increase with the increase of its content. Conversely, PEG(2M)'s crystallization efficiency declined with the increase of its content. Extending the annealing time has evidently changed the PEGs' crystallization effect on PLLA. Moreover, the PEG(1.5k) has, to a greater extent, brought about the depression of PLLA's melting temperature by increasing its content, and this depression increased with the annealing time. The blends exhibited lower thermal stability than those of the parent components, particularly for the PEG(1.5k)‐included system with a higher PEG content. Regardless of the annealing time, the PEG(1.5k)‐included blends have shown homogeneous melt morphology under light microscope, whereas the PEG(2M)‐included blends have displayed phase‐separated melt morphology. In addition to the composition, PEG's MW and annealing time influence the crystalline morphology of the blends. The ringed PLLA spherulites have appeared mostly in the 2‐min annealed PEG(1.5k)‐included blends. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1497–1510, 2009