Low-temperature synthesis and growth of superparamagnetic Zn0.5Ni0.5Fe2O4 nanosized particles

Mono-disperse spinel Ni_0.5Zn_0.5Fe₂O₄ nanosized particles have been synthesized via a hydrothermal method at low temperature. X-ray diffraction (XRD), transmission electron microscope (TEM) and high-resolution transmission electron microscope (HRTEM) analysis indicated that the synthesized nanocrystals were of pure cubic spinel structure with the size about 6-20 nm. The activation energy of grain growth is 35.06 kJ/mol experimented by the Arrhenius equation. A primary experimental model was put forward to shed light on the growth mechanism of crystallined spinel Ni-Zn ferrite nanosized particles under hydrothermal conditions. The magnetic measurements shows that the prepared Ni_0.5Zn_0.5Fe₂O₄ nanoparticle possess good superparamagnetic behavior.     

Estimating the cation distributions in the spinel ferrites Cu0.5−xNi0.5ZnxFe2O4 (0.0≤x≤0.5)

Ferrite samples of the composition Cu_0.5−xNi_0.5Zn_xFe₂O₄ (0.0≤x≤0.5) were synthesized by chemical co-precipitation. The samples exhibited a single phase cubic spinel structure, and the saturation magnetization of the samples was found to increase with increasing Zn content. Using a quantum mechanical method proposed by our group, the cation distributions in the samples were estimated. Estimated cation distributions obtained by fitting the magnetic moments of the samples were then used to perform Rietveld fitting for X-ray diffraction patterns. The acceptable error parameters in the Rietveld fitting indicate that the estimated cation distributions in the samples are reasonable.     

Effect of calcination temperature on the structure and hydroxylation activity of Ni0.5Cu0.5Fe2O4 nanoparticles

Nanocrystalline Ni_0.5Cu_0.5Fe₂O₄ was synthesized by sol-gel method with varying calcination temperature over the range of 500-1000. The powders obtained were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). In addition, thermal analysis (TG-DTG-DTA) of the precursor was carried out. The study reveals the simultaneous decomposition and ferritization process at rather low temperature (280-350). For the crystalline structure investigated, single cubic spinel is gained when the precursor was decomposed at 800-1000, whereas separated crystal CuO formed when calcination temperature is below 800. The increase of calcination temperature favors the appearance of Fe_B³⁺, Cu_A²⁺ and O on the spinel surface. The hydroxylation activity is relative to the amount of Cu_B²⁺ species on the spinel surface. The lattice oxygen species on the spinel surface are favorable for the deep oxidation of phenol.     

Research on charge-ordering state in La0.5Sr0.5MnO2.88 and La0.5Sr0.5Mn0.5Ti0.5O3 systems

The structural, magnetic and transport properties of La_0.5Sr_0.5MnO_2.88 and La_0.5Sr_0.5Mn_0.5Ti_0.5O₃ samples have been investigated systematically. Indeed, this series has been considered to understand the influence of physical parameters such as oxygen deficiency and titanium doping effect in undoped La_0.5Sr_0.5MnO₃ sample. Ceramic material based on La_0.5Sr_0.5MnO_2.88 exhibits interesting behaviours of charge-ordering (CO), ferromagnetic (FM) states and a good conductivity down to the lowest temperatures. The substitution of Ti for Mn destroyed drastically the CO, damaged the motion of itinerant e_g electrons and changed the local parameters of perovskite cell. A change of the structure from tetragonal to rhombohedral symmetry is observed causing a weakening of double-exchange interaction. The experiment results show that the suppression of the CO is sensitive to the variety of Mn³⁺/Mn⁴⁺ ratio. In a field of 8 T at 10 K, FM and CO phase can be evaluated to be ∼20:80 according to the μ_exp/μ_cal ratio for La_0.5Sr_0.5MnO_2.88, whereas the CO state is suppressed for La_0.5Sr_0.5Mn_0.5Ti_0.5O₃ sample, FM and anti-ferromagnetic (AFM) phase are coexisted and evaluated to be ∼54:46, respectively.     

Magnetic and structural studies of the alloy system REIn0.5Ag0.5

The structural and magnetic properties of the alloy system REIn_0.5Ag_0.5 [RE = Gd, Tb, Dy, Ho, Er, Tm and Yb] are reported. All these alloys (except that of Yb) crystallize in a cubic CsCl type structure at room temperature. Low temperature X-ray diffraction data does not reveal any structural phase transformation down to 8 K. On the basis of magnetic susceptibility data at a different temperature (3–300 K) and applied magnetic field (2 × 10⁵ to 8 × 10⁶ A m^-1, it has been concluded that GdIn_0.5Ag_0.5 is ferromagnetic (T_c = 118 K), TbIn_0.5Ag_0.5 and DyIn_0.5Ag_0.5 are meta magnetic (T_N = 66 and 30 K, respectively) and alloys involving Ho, Er, Tm and Yb are ferrimagnetic with Néel temperatures (T_N) equal to 24, 22, 21 and 20 K, respectively. The evaluated effective magneton number (p) is found to be slightly larger compared to theoretical values for tripositive ions of Gd, Tb and Dy and a bit smaller for Ho, Er, Tm and Yb. The results have been qualitatively explained using appropriate theories.     

Reentrant spin glass behavior and large initial permeability of Co0.5−xMnxZn0.5Fe2O4

A series of polycrystalline ferrites having nominal chemical composition Co_0.50−xMn_xZn_0.5Fe₂O₄ (0<x<0.4) have been synthesized by the solid-state reaction technique. The XRD analysis confirms single phase cubic spinel structure for all compositions. Lattice constant increases from 0.84195 to 0.84429 nm with the increasing Mn content and obeys Vegard's law. The average grain size increases by increasing both Mn content and sintering temperatures. Room temperature saturation magnetization increases for x=0.1 and decreases for increasing Mn content. The coercivity decreases with increasing Mn content due to the decrease of anisotropy constant. A reentrant spin glass behavior of these samples is observed from the zero field cooled magnetization measurements. The real part of the initial permeability increases by increasing both Mn content and sintering temperatures. This is due to the homogeneous grain growth and densification of the ferrites. The highest initial permeability 137 is observed for x=0.4 sintered at 1573 K on the other hand, the highest relative quality factor (2522) is obtained for the sample Co_0.2Mn_0.3Zn_0.5Fe₂O₄ sintered at 1523 K. The Mn substituted Co_0.50−xMn_xZn_0.5Fe₂O₄ ferrites showed improved magnetic properties.     

Neutron diffraction study of magnetic ordering in Tm0.5Eu0.5Se

A single crystal of the magnetic semiconductor Tm_0.5Eu_0.5Se was studied by means of neutron diffraction in the temperature range from 1.8 to 293 K. Long-range magnetic order is detected at temperatures below T_c = (18.5±1) K. The measured ferromagnetic moment component of (2.12±0.05) μ_B per rare-earth ion at saturation in zero external magnetic field indicates approximately antiparallel alignment of Tm moment and Eu spin (mutual angle 134°). The experimentally determined neutron magnetic form factor confirms the divalent state of both Tm and Eu in Tm_0.5Eu_0.5Se.     

Glassy-ferromagnetic behavior in Eu0.5Sr0.5CoO3

Polycrystalline perovskite cobalt oxide Eu_0.5Sr_0.5CoO₃ was prepared by the conventional solid-state reaction method. X-ray powder patterns indicated the prepared samples are pure, cubic perovskite structure (Pm3?m), and with no evidence of any secondary phases. The dc magnetization and ac susceptibility measurements were carried out to investigate the magnetic properties of the sample, and which indicated that cluster-glasses properties are suppressed with the increasing of the coercive field. We denied the possibility of spin-glasses and the existence of the Hopkinson effect in Eu_0.5Sr_0.5CoO₃ through the temperature-dependent ac susceptibility measurements, and explained the magnetic behavior of Eu_0.5Sr_0.5CoO₃ with the competition between magnetic anisotropy and the external magnetic field.     

A comparative study of Fd-3m and P4332 “LiNi0.5Mn1.5O4”

“LiNi_0.5Mn_1.5O₄” is generally reported to crystallize in the spinel structure within two different space groups (Fd-3m and P4₃32) depending on the oxygen stoichiometry/ordering of the Ni/Mn cations. This paper presents a contribution to the study of these two phases in order to have a better insight on how the preparation method influence their electrochemical properties. The phases were synthesized by a ceramic route and thoroughly characterized using X-ray diffraction (XRD), FTIR and Raman spectroscopy. This latter technique, together with the obtaining of the electrochemical signature, allows discriminating between the types of spinel phases. Based on thermal in situ XRD measurements, we further propose a peritectoid transformation as an explanation for the appearance of a nickel based rock salt phase during the preparation. Finally, we discuss on the electrochemical deinsertion mechanism.     

Mössbauer study of the re-entrant spin-glass behaviour in the mixed spinel ferrites Mg(0.9+x)Fe2(1−x)Ni0.1TixO4 (x=0.5 and 0.6)

Samples of the mixed spinel ferrite series Mg_(0.9+x)Fe_2(1−x)Ni_0.1Ti_xO₄ with x=0.5 and 0.6, prepared by solid state reaction of the appropriate oxides, have been investigated with ⁵⁷Fe Mössbauer spectroscopy. The as-prepared samples are found to be mainly superparamagnetic due to magnetic cluster formation. Samples after at least three times reheated exhibit spectra, which can be rather interpreted by a transversal relaxation of the spin above and spin-glass behaviour below the respective freezing temperatures T_f. External-field spectra reveal the canting to occur only on the octahedral sites. From the derived transition temperatures and thresholds together with data from earlier investigated sample with x=0.7 a compositional magnetic phase diagram for this spinel series is obtained.     

Fabrication and magnetic properties of Ni0.50.5Zn0.5Fe2O4 nanofibres by electrospinning

NiZn ferrite/polyvinylpyrrolidone composite fibres were prepared by sol–gel assisted electrospinning.Ni0.5Zn0.5Fe2O4 nanofibres with a pure cubic spinel structure were obtained subsequently by calcination of the composite fibres at high temperatures.This paper investigates the thermal decomposition process,structures and morphologies of the electrospun composite fibres and the calcined Ni0.5Zn0.5Fe2O4 nanofibres at different temperatures by thermogravimetric and differential thermal analysis,x-ray diffraction,Fourier transform infrared spectroscopy and field emission scanning electron microscopy.The magnetic behaviour of the resultant nanofibres was studied by a vibrating sample magnetometer.It is found that the grain sizes of the nanofibres increase significantly and the nanofibre morphology gradually transforms from a porous structure to a necklace-like nanostructure with the increase of calcination temperature.The Ni0.5Zn0.5Fe2O4 nanofibres obtained at 1000 C for 2 h are characterized by a necklace-like morphology and diameters of 100–200 nm.The saturation magnetization of the random Ni0.5Zn0.5Fe2O4 nanofibres increases from 46.5 to 90.2 emu/g when the calcination temperature increases from 450 to 1000 C.The coercivity reaches a maximum value of 11.0 kA/m at a calcination temperature of 600 C.Due to the shape anisotropy,the aligned Ni0.5Zn0.5Fe2O4 nanofibres exhibit an obvious magnetic anisotropy and the ease magnetizing direction is parallel to the nanofibre axis.     

Sound velocity in La0.5Ca0.5MnO3

In this Letter the microscopic theory of the relative change in velocity of sound with temperature of La_0.5Ca_0.5MnO₃ is reported. The phonon Green function is calculated using the Green function technique of Zubarev in the limit of zero wave vector and low temperature. The lattice model electronic Hamiltonian in the presence of the phonon interaction with hybridization between the conduction electrons and the l-electrons is used. The relative change in velocity of sound at various temperatures is studied for different model parameters namely the position of the l-level, the effective phonon coupling strength and hybridization strength. The phonon anomalies observed experimentally at different temperatures are explained theoretically. An abrupt change in velocity at Neel temperature (TN) is observed clearly. It is observed that different parameters influence the velocity of sound.     

Dielectric and piezoelectric properties of lead-free (Na0.5K0.5)NbO3-SrTiO3 ceramics

In this article, we report successful preparation of dense [(Na_0.5K_0.5)_1−xSr_x](Nb_1−xTi_x)O₃ (x=0.005-0.100) ceramics by ordinary sintering in air. The dependence of phase structure on doping content of SrO and TiO₂ has been determined by the X-ray diffraction technique. It was found that the crystal structure changed from orthorhombic to tetragonal at x≈0.040. Dielectric study revealed that the dielectric relaxor behavior was induced by doping of SrO and TiO₂ into (Na_0.5K_0.5)NbO₃. The samples in the composition range from x=0.005 to 0.020 exhibited excellent electrical properties, piezoelectric constant of electromechanical planar and thickness coupling coefficients of k_p=26.6-32.5% and k_t=39.8-43.8%. The results show that the [(Na_0.5K_0.5)_1−xSr_x](Nb_1−xTi_x)O₃ ceramics are one of the promising lead-free materials for electromechanical transducer applications.     

Elastic stiffness constants and acoustic symmetry of LiY0.5Tb0.5F4

Measurements of ultrasound wave velocities between 4.2 and 293 K have been used to determine the temperature dependences of the seven adiabatic elastic stiffness tensor components of the laser host scheelite structure fluoride LiY_0.5Tb_0.5F₄. The sign of C₁₆ is negative, as found previously for other oxide and fluoride scheelites; therefore for LiY_0.5Tb_0.5F₄ the positions of the acoustic symmetry axes in the XY plane have the same sense as those of the other scheelites. The k and γ axes of acoustic symmetry lie at +31° and + 76° from the + X axis. Transformation of the elastic stiffness constants to a basis comprised of two acoustic symmetry axes together with the +Z axis enables a detailed comparison of the elastic behaviour of LiY_0.5Tb_0.5F₄ with those of other scheelite crystals.     

Observation by mössbauer spectroscopy of electron hoppings in the spinel series Zn1-xGexFe2O4

The Mössbauer spectra of the spinel series Zn_1-xGe_xFe₂O₄ with x = 0.25, 0.5 and 0.75 are observed between 77 and 623 K. In the detection limit of the Mössbauer spectrometry, the ferrous and ferric ions are all found on the B sites and the broadening of the spectra between the Curie point and 623 K is correlated with an electron hopping process via a conduction band. This process favors a “double exchange” which can explain the magnetic order in the compounds with x = 0.25 and x = 0.5 below 200 and 250 K.     

Na0.5K0.5NbO3-BiFeO3 lead-free piezoelectric ceramics

Lead-free (Na_0.5K_0.5)NbO₃-based piezoelectric ceramics were successfully fabricated by substituting with a small amount of BiFeO₃ (BF). Difficulty in sintering of pure NKN ceramics can be eased by adding a few molar percent of BF, and the crystalline structure is also changed, leading to a morphotropic phase boundary (MPB) between ferroelectric orthorhombic and rhombohedral phases. The MPB exists near the 1-2 mol% BF-substituted NKN compositions, exhibiting enhanced ferroelectric, piezoelectric, and electromechanical properties of P_r=23.3 μC/cm², d₃₃=185 pC/N, and k_p=46%, compared to an ordinarily sintered pure NKN ceramics. The MPB composition has a Curie temperature of ∼370 °C, comparable to that of some commercial PZT materials.     

Ferroelectric-relaxor behavior of (Na0.5K0.5)NbO3-based ceramics

We report that ferroelectric-relaxor behavior is induced by doping of SrO and TiO₂, or BaO and TiO₂ into classic ferroelectric (Na_0.5K_0.5)NbO₃. It is found that [(Na_0.5K_0.5)_0.9Sr_0.1](Nb_0.9Ti_0.1)O₃ ceramics exhibit a pronounced ferroelectric-relaxor behavior, comparable to that of [(Na_0.5K_0.5)_0.9Ba_0.1](Nb_0.9Ti_0.1)O₃ ceramics. Our results indicate that the relaxor behavior is closely related to the appearance of micropolar regions in these systems. The relaxor behavior should arise from the dynamic response of micropolar clusters. Raman spectra of [(Na_0.5K_0.5)_1−xSr_x](Nb_1−xTi_x)O₃ ceramics measured in the wavenumber range from 100 to 1200 cm⁻¹ confirm that the first order scattering is dominant in phonon bands should result from both short-range ordered region (micropolar regions) and disordered matrix. The frequency dependence of dielectric permittivity measurements show that the relaxor behavior of SrO and TiO₂, or BaO and TiO₂ doped (Na_0.5K_0.5)NbO₃ ceramics is not a Debye type in the radio frequency range.     

Structure and magnetization studies of Nd0.5−xPrxSr0.5MnO3 system

The structural and magnetic properties of Nd_0.5−xPr_xSr_0.5MnO₃ (x=0, 0.1, 0.2, 0.3, 0.4 and 0.5) system have been investigated. With the substitution of Pr in Nd_0.5Sr_0.5MnO₃, it shows a gradual structure transformation from the Imma orthorhombic symmetry to the tetragonal I4/mcm phase, and the crystallographic transition remains incomplete, even in Pr_0.5Sr_0.5MnO₃. A large bifurcation between zero-field-cooled (ZFC) and field-cooled (FC) susceptibility has been observed below Curie temperature (T_C), which is characteristic of coexistence of ferromagnetism (FM) and antiferromagnetism (AFM) at low temperature region. The magnetization of Pr_0.5Sr_0.5MnO₃ is larger than that of Nd_0.5Sr_0.5MnO₃, while Nd_0.5Sr_0.5MnO₃ with more CE-type AFM shows larger magnetization than Nd_0.3Pr_0.2Sr_0.5MnO_3, which mixed with CE-type (majority) and A-type (minority) AFM at low temperature, indicating that the magnetization of Nd_0.5−xPr_xSr_0.5MnO₃ system is affected by A-site disorder combined with orbital ordering of A-type AFM and CE-type AFM.     

Site preference and magnetism of Fe3−xCrxAl0.5Si0.5

In order to gain better insight into the origin of the observed differences between Fe_3−xCr_xAl and Fe_3−xCr_xSi, alloys of Fe_3−xCr_xAl_0.5Si_0.5 (x=0, 0.125, 0.250, 0.375 and 0.5) were prepared and studied by means of X-ray and neutron diffraction as well as by magnetization measurements. Electronic structure calculations of these alloys have been performed by means of TB-LMTO-ASA method. It was expected, and experimentally verified, that the presence of silicon and aluminum atoms in 1:1 proportion will result in the independence of the lattice parameter on the iron/chromium concentration. All samples have been proved to be a single phase of the DO₃-type of structure. Theoretical and experimental results indicate that chromium atoms locate preferentially in B sublattice. Cr magnetic moments are oriented antiparallel to Fe magnetic moments. Neutron measurements show a linear dependence of the magnetic moments of Fe(A,C), Fe(B) and Cr(B) as a function of Cr concentration. However the calculated total magnetic moment decreases faster with chromium content than indicated by the experiment.     

Analysis of low temperature specific heat in Nd0.5Sr0.5MnO3 and R0.5Ca0.5MnO3 (R=Nd,Sm, Dy and Ho) compounds

We report on the specific heat C(T) of doped manganites Nd_0.5Sr_0.5MnO₃, Nd_0.5Ca_0.5MnO₃, Sm_0.5Ca_0.5MnO₃, Dy_0.5Ca_0.5MnO₃ and Ho_0.5Ca_0.5MnO₃ in the temperature range 2?T?300 K using modified rigid ion model (MRIM). The present specific heat results are in general satisfactory agreement with experimental data except at very low temperatures (i.e. T?12 K). Also a sharp peak observed in the experimental results for these compounds around 5 K could not be revealed by our computed results as they arise due to Schottky-like anomaly. Besides, we have reported the cohesive and the thermal properties of these compounds. The results obtained by us are discussed in detail.