SrZn2(PO4)2:Sn2+,Mn2+荧光粉的发光性质及其能量传递机理

采用高温固相法制备了SrZn₂(PO₄)₂:Sn²⁺(SZ₂P:Sn²⁺), SrZn₂(PO₄)₂:Mn²⁺(SZ₂P:Mn²⁺), SrZn₂ (PO₄)₂:Sn²⁺, Mn²⁺(SZ₂P:Sn²⁺, Mn²⁺) 荧光粉. 通过X射线衍射、激发和发射光谱详细研究了荧光粉的物相和发光性质. 在SrZn₂(PO₄)₂ 基质中, Sn²⁺离子发射光谱是峰值位于461 nm宽带谱, 归属于Sn²⁺离子的³P₁→¹S₀能级跃迁, SZ₂P:Mn²⁺激发光谱由基质吸收带(200–300 nm)和位于352, 373, 419, 431和466 nm的一系列激发峰组成, 分别对应Mn²⁺离子的⁶A₁(⁶S)→⁴E(⁴D), ⁶A₁(⁶S)→⁴T₂(⁴D), ⁶A₁(⁶S)→[⁴A₁(⁴G), ⁴E(⁴G)], ⁶A₁(⁶S)→⁴T₂(⁴G)和⁶A₁(⁶S)→⁴T₁(⁴G)能级跃迁, 因此, SZ₂P:Sn²⁺ 的发射光谱与SZ₂P:Mn²⁺的激发光谱有较大范围的重叠. 结果表明Sn²⁺对Mn²⁺发光有明显的敏化作用. 基于Dexter电多极相互作用能量传递公式和Reisfeld近似原理分析, 荧光粉SZ₂P:Sn²⁺, Mn²⁺中Sn²⁺-Mn²⁺离子之间的能量传递机理属于电四极-电四极相互作用引起的共振能量传递, 并计算出Sn²⁺-Mn²⁺离子之间能量传递临界距离R_c ≈ 1.78 nm. 通过改变Sn²⁺, Mn²⁺离子掺杂浓度, 实现了荧光粉发光颜色的调节, 在254 nm短波紫外激发下荧光粉发出较强的蓝白光. 研究结果表明SZ₂P:Sn²⁺, Mn²⁺荧光粉有望应用于紧凑型节能灯照明领域, 随着半导体紫外芯片技术的发展, 有潜力应用于未来的白光发光二极管照明领域.     

Ba9Y2(SiO4)6: Ce3+,Mn2+荧光粉的发光特性及能量传递

利用高温固相法制备了Ba₉Y₂(SiO₄)₆:Ce³⁺,Mn²⁺(BYS:Ce³⁺,Mn²⁺)荧光粉,并通过X射线衍射(XRD)谱、激发和发射光谱及荧光寿命的测试对材料的结构、发光特性和能量传递进行了研究。在327 nm激发下,BYS:Ce³⁺,Mn²⁺发射光谱中包含2个发射峰,分别为位于407 nm的Ce³⁺的蓝紫光发射和位于597 nm的Mn²⁺的红光发射。在该体系中,发现了Ce³⁺向Mn²⁺的有效能量传递,使得Mn²⁺在597 nm处的红光发射显著提高,当x(Mn²⁺)=0.25时,BYS:Ce³⁺,xMn²⁺的能量传递效率可达39%。实验表明,该荧光粉可为紫外基白光LED提供良好的红光光源。     

Eu2+,Mn2+在BaZnP2O7中的发光及Eu2+→Mn2+能量传递

采用高温固相法合成了BaZnP₂O₇:Eu²⁺,Mn²⁺荧光粉,并对其发光性质及Eu²⁺对Mn²⁺的能量传递机理进行了研究.Eu²⁺和Mn²⁺在380 nm和670nm的发射峰分别由Eu²⁺的5d—4f跃迁和Mn²⁺的⁴T₁(^{4关键词： 磷酸盐 2+}')" href="#">Eu²⁺ 2+')" href="#">Mn²⁺ 能量传递     

Na4Ca3(AlO2)10∶Eu2+,Mn2+荧光粉的发光特性

采用高温固相法,制得一种新型荧光粉Na₄Ca₃(AlO₂)₁₀∶Eu²⁺,Mn²⁺。样品的结构和发光性质分别由X射线衍射谱和荧光光谱来表征。在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺的激发光谱中出现了Eu²⁺的f-d跃迁吸收带;在发射光谱中,出现蓝光发射,峰值位于441 nm。当在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺中掺杂Mn²⁺时,发生了Eu²⁺→Mn²⁺的能量传递,在542 nm处出现了Mn²⁺的发射峰。在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺,Mn²⁺中,随着Mn²⁺浓度的增加,Eu²⁺粒子的发射强度减弱,而Mn²⁺粒子的发射强度增强,且Eu²⁺离子发射的衰减时间缩短,同时色度由蓝光移向白光。     

CaWO4：Sm3+荧光粉的发光性质及其能量传递机理

采用沉淀法制备了不同Sm³⁺掺杂浓度的白钨矿结构CaWO₄荧光粉材料. 对CaWO₄:Sm³⁺ 材料的光致发光性质的研究结果表明, 在404 nm光照下样品可以实现色纯度较高的红光发射, 而短波紫外240 nm光照下除Sm³⁺的特征发射外还能观察到CaWO₄自激发发射, 能够获得较强的白光; 实验发现Sm³⁺掺杂浓度为2%时样品的发光强度最高; 通过对实验数据的分析确定了Sm³⁺之间的能量传递类型为电偶极-电偶极相互作用, 并计算了能量传递的临界距离大约为2.0 nm. 关键词： 光致发光 4：Sm³⁺')" href="#">CaWO₄：Sm³⁺ 荧光寿命 能量传递     

真空紫外光激发下Ce3+、Tb3+激活的BaCa2(BO3)2的发光性质

利用XRD、VUV及UV光谱等方法对Ce³⁺、Tb³⁺离子掺杂以及Ce³⁺、Tb³⁺离子共掺的3种BaCa₂(BO₃)₂荧光粉的相纯度、发光性质、浓度猝灭现象进行研究。结果表明:3种荧光粉在VUV波段有较好的吸收,基质吸收带位于140～190 nm范围。Ce³⁺在BaCa₂(BO₃)₂的最低4f5d跃迁带位置在360 nm附近,其5d→²F_J(J=5/2, 7/2)发射峰分别位于393,424 nm。Tb³⁺掺杂的样品在172 nm激发下的发射光谱由4个窄带组成,分别对应⁵D₄→⁷F_J(J=3,4,5,6)的跃迁,其中占主导位置的是⁵D₄→⁷F₅的跃迁,大约位于543 nm处,主要为绿光发射。在Ce³⁺,Tb³⁺离子共掺杂的BaCa₂(BO₃)₂光谱中,观察到Ce³⁺-Tb³⁺离子间有能量传递。     

红色长余辉材料Mg2SiO4：Dy3+,Mn2+的制备及发光特性

用高温固相法制备了长余辉发光材料Mg₂SiO₄:Dy³⁺,Mn²⁺,对这种材料的红色长余辉性质进行了研究.对以不同掺杂浓度单掺杂Mn²⁺、单掺杂Dy³⁺以及双掺杂Dy³⁺,Mn²⁺的Mg₂SiO₄体系,通过在紫外激发下的发射光谱及其激发光谱的研究,确认了在双掺杂体系中,峰值为660nm的发光带对应着Mn²⁺的⁴T₁(⁴G)→⁶A₁(⁶S)跃迁,Mn²⁺为主要发光中心.Mn²⁺的660nm发射的激发谱分布很宽,样品在近紫外和可见光区都有良好的吸收,长波边可达600nm,是这种材料的一个显著优点.还研究了双掺杂体系中Dy³⁺对Mn²⁺的660nm发光带的敏化作用.另外,通过对单掺杂、双掺杂体系热释光曲线的比较,揭示了双掺杂体系中Dy³⁺的陷阱作用.     

Ca10Li（PO4）7∶Dy3+,Ce3+材料的制备及发光性能

采用高温固相法制备了Ca10Li(PO4)7∶Dy3+发光材料,研究了Dy3+在Ca10Li(PO4)7基质中的发光特性。XRD测量结果表明,烧结温度为1 050℃时所制备的样品为纯相Ca10Li(PO4)7晶体。从激发谱可以看出样品主激发峰位于349 nm(6H15/2→6P7/2),363 nm(6H15/2→6P5/2),385 nm(6H15/2→6M21/2),样品可被UVLED管芯有效激发。发射谱由位于481 nm(蓝)和572 nm(黄)的两个峰组成,对应的能级跃迁为4F9/2→6H15/2、6H13/2。研究了不同Dy3+掺杂浓度对发光强度的影响,当Dy3+的摩尔分数为10%时发光最强。掺入Ce3+作为敏化剂,Ce3+→Dy3+发生共振能量传递,当掺杂量为10%Dy3+、14%Ce3+时,样品发光最强,其强度为单掺10%Dy3+时的13.4倍,发光颜色由黄白变为蓝白。     

Sr2SiO4:Ce3+,Li+蓝紫色荧光粉发光性能的研究

以MCM-41为硅源,采用共沉淀法制备Sr_2-xSiO₄:xCe³⁺(x=0.01~0.09,步长为0.01)和Sr_1.95-ySiO₄: 0.05Ce³⁺,yLi⁺(y= 0.01~0.07,步长为0.02)蓝紫色荧光粉。Sr_2-xSiO₄:xCe³⁺的发射光谱是一个不对称的宽带,最大峰值在410 nm左右。Ce³⁺的最佳掺杂量为5%。Ce³⁺离子倾向于占据九配位的Sr(Ⅱ)格位。共掺电荷补偿剂Li⁺可以有效地提高Sr_1.95SiO₄: 0.05Ce³⁺的发光强度,其中Li⁺离子对1 100 ℃煅烧样品的发光强度的提高程度比1 000 ℃的更高,Li⁺的最佳掺杂量为y=0.05。     

Ba10(PO4)4(SiO4)2∶Eu2+荧光体的光谱特性

采用高温固相法合成了荧光体Ba₁₀（PO₄）₄（SiO₄）₂：Ce³⁺和Ba₁₀（PO₄）₄（SiO₄）₂：Eu²⁺,研究了两种荧光体的光谱特性。结果表明,两者都呈现较强的宽带激发特征。根据同种基质中Eu²⁺和Ce³⁺两种离子光谱特征的相关性,通过测得的Ba₁₀（PO₄）₂（SiO₄）₂基质中Ce³⁺的光谱数据估算了Ba₁₀（PO₄）₂（SiO₄）₂：Eu²⁺中Eu²⁺的斯托克斯位移（ΔS）和激发能量,估算结果与Ba₁₀（PO₄）₂（SiO₄）₂：Eu²⁺样品的光谱分析结果十分吻合。Ba₁₀（PO₄）₂（SiO₄）₂：Eu²⁺可以同时被紫光和蓝光激发,发出偏白的绿光,可用作白光LED的荧光粉。     

Ce3+/Eu2+共掺Ca3Si2O4N2荧光粉的光学特性

采用高温固相法制备了一种新型的白光LED用Ca3Si2O4N2∶Eu2+,Ce3+,K+荧光粉。利用X射线衍射仪对样品的物相结构进行了分析,结果表明:Ce3+和K+离子的掺杂没有改变Ca3Si2O4N2∶Eu2+荧光粉的主晶相。利用荧光光谱仪对样品的发光性能进行了测试,发现样品在355 nm激发下得到的发射光谱为峰值位于505 nm的单峰,是Eu2+离子5d-4f电子跃迁引起的。Ca3Si2O4N2∶Eu2+荧光粉通过Ce3+和K+离子的掺杂,发光明显增强。当Ce3+的摩尔分数为1%时,荧光粉的发光强度达到最大值,是单掺Eu2+离子荧光粉发光强度的168%。通过光谱重叠的方法计算Ce3+→Eu2+能量传递临界的距离为2.535 nm。     

Photoluminescence and efficient energy transfer from Ce3+ to Tb3+ or Mn2+ in Ca9ZnLi(PO4)7 host

Structural and spectroscopic characterizations of the Ce³⁺/Tb³⁺(Mn²⁺) solely and Ce³⁺–Tb³⁺(Mn²⁺) doubly doped phosphate compound Ca₉ZnLi(PO₄)₇ with β-Ca₃(PO₄)₂ structure have been performed by powder X-ray diffraction and photoluminescence spectra measurements. The weak green emission from Tb³⁺ and red emission from Mn²⁺ are significantly enhanced by introduction of sensitizer Ce³⁺ ions due to an efficient resonant-type energy transfer from Ce³⁺ to activators Tb³⁺ or Mn²⁺. The energy transfer efficiency and the mechanism have been estimated based on spectroscopic data. Meanwhile, the critical distances for energy transfer between the Ce³⁺ and Tb³⁺ or Mn²⁺ ions are also calculated by the method of spectral overlapping.     

近紫外荧光粉SrAl_2Si_2O_8∶Ce~(3+)的光致发光特性

采用高温固相反应法制备了xCe~(3+)(x=0.01%,0.05%,0.10%和0.30%)激活的Sr_(1-x)Al_2Si_2O_8近紫外荧光粉,利用X射线衍射(XRD)和扫描电镜(SEM)检测出荧光粉的物相结构,通过光致发光谱(PL)和激发光谱(PLE)表征了荧光粉的发光性质。结果显示,在中波紫外光激发下,发射峰位于长波紫外区,归属于Ce~(3+)的5d→2 F5/2和5d→2 F7/2跃迁。激发波长308nm时,观察到近紫外SrAl_2Si_2O_8荧光粉的发光强度随Ce~(3+)掺杂量增加而先增大后减小,同时发射峰位置红移。280和325nm波长选择性激发条件下的差异性发射行为表明SrAl_2Si_2O_8∶Ce~(3+)具有两种性质不同的发光中心,该结论由监测320和390nm发射时获得的形状具有明显区别的激发光谱亦可得以验证。离子半径的匹配性支持Ce~(3+)优先取代Sr~(2+),同时Van Uitert的经验公式估算结果推断出低浓度的Ce~(3+)生成九配位的Ce(Ⅰ)发光中心,高浓度掺杂情况下部分相互近邻的Ce~(3+)有效配位数减小,形成八配位的Ce(Ⅱ)发光中心。紫外280nm激发下峰位348nm的发射谱带源于Ce(Ⅰ)和Ce(Ⅱ)发光中心共同贡献,紫外325nm激发下发射峰位于378nm的发射带则主要对应于Ce(Ⅱ)发光中心。紫外光激发下Ce~(3+)发射出较强的近紫外光,表明SrAl_2Si_2O_8∶Ce~(3+)是一种适用于研发紫外荧光光源的荧光粉体材料。     

Tb~(3+)和Ce~(3+)在Sr_7Zr(PO_4)_6基质中能量传递及发光特性研究

用高温固相法制备了Sr_7Zr(PO_4)_6∶Tb~(3+)、Sr_7Zr(PO_4)_6∶Ce~(3+)及Sr_7Zr(PO_4)_6∶Tb~(3+),Ce~(3+)一系列荧光粉,并通过X射线衍射仪及荧光光谱仪分析了其结构和发光性质。结果表明,Sr_7Zr(PO_4)_6∶Tb~(3+)呈现特征绿色发射,最强发射峰位于543 nm,属于Tb~(3+)的5D4→7F5跃迁,激发峰位于226 nm处,但激发带较窄。为拓宽其激发带的宽度,在Sr_7Zr(PO_4)_6∶Tb~(3+)中掺入了Ce~(3+),观察到掺入Ce~(3+)后激发带变宽,且在Ce~(3+)的激发波长处激发得到了Tb~(3+)的发射,表明存在Ce~(3+)到Tb~(3+)的能量传递。     

Eu~(3+)掺杂的Na_2YMg_2(VO_4)_3荧光粉制备和发光特性

采用溶胶-凝胶法制备了Na2Y1-xMg2(VO4)3∶x Eu~(3+)(x=0.15~0.75)系列自激活荧光粉。用XRD、SEM、光致发光光谱和荧光衰减曲线分别对其结构、形貌和发光性能进行表征。XRD结果显示样品为纯石榴石结构,其中Eu~(3+)取代Y~(3+);SEM照片显示样品为粒径大小在0.3~1μm范围内不规则的光滑球状颗粒;光谱分析表明,Na2YMg2(VO4)3作为自激活发光基质可以被200~400 nm紫外光有效激发,发出源于VO_4~(3-)电荷迁移跃迁的波长范围为400~700 nm的宽谱带绿光。掺杂Eu~(3+)后,在340 nm紫外光激发下同时出现了VO_4~(3-)的电荷迁移带和Eu~(3+)的特征光谱。不同浓度Eu~(3+)掺杂的光谱和荧光衰减曲线表明,存在VO_4~(3-)和Eu~(3+)之间的能量传递。     

Nd~(3+):SrY_2O_4粉体的制备、结构与光谱性能研究

为探索新型激光晶体,采用固相法合成了(3 at.%)Nd~(3+):SrY_2O_4多晶,对其结构和发光性质进行了研究.对样品的X射线衍射谱进行Rietveld精修得到了样品的晶胞参数、原子位置等.在353 nm激发下,Nd~(3+):SrY_2O_4在可见波段的最强荧光峰位于419 nm,对应Nd3+的2D15/2→4I9/2跃迁.在824 nm激发下,Nd3+的4F3/2→4I11/2跃迁的荧光谱带宽约为90 nm,最强峰为1083 nm,荧光寿命为281.7μs.宽发射光谱和长的能级寿命表明,Nd~(3+):SrY_2O_4是一种很有希望的新波长激光二极管抽运超短脉冲激光材料.     

稀土离子Ce,Tb掺杂硼磷酸锶荧光粉的发光性质

采用高温固相法合成了2SrO·0.25B₂O₃·0.75P₂O₅:RE³⁺(RE=Ce,Tb)荧光粉。研究了其中Ce³⁺,Tb³⁺的光谱性质,Ce³⁺和Tb³⁺共掺杂时的能量传递效率,以及Ce³⁺和Tb³⁺的动力学过程。发现在共掺杂的样品中,Tb³⁺的⁵D₄→⁷F₅绿色发射比Tb³⁺单掺杂样品中的绿色发射有显著的提高。当Tb³⁺的含量从1%增加到8%时,Ce³⁺→Tb³⁺的能量传递效率逐渐增加至70%。通过动力学研究,在Ce³⁺和Tb³⁺共掺杂的样品中,提高Tb³⁺的浓度,Ce³⁺的寿命减小。此外,Ce³⁺离子寿命的倒数与Tb³⁺的浓度之间很好地符合线性函数关系,经过拟合Ce³⁺离子的电子跃迁速率和Ce³⁺→Tb³⁺的能量传递速率分别为5.1×10^-2和1.34ns^-1·mol^-1。Tb³⁺的⁵D₄→⁷F₅跃迁的衰减曲线很好地遵守指数式衰减,并且随着Ce³⁺的掺杂浓度提高,Tb³⁺的⁵D₄→⁷F₅寿命增加。结果表明在共掺杂的2SrO·0.25B₂O₃·0.75P₂O₅材料中存在Ce³⁺到Tb³⁺的有效能量传递,这种材料在541nm处有着较强的绿光发射,所以将在发光以及显示领域有潜在的应用前景。     

Photoluminescence properties and energy transfer in Y_2O_3:Eu~(3+) nanophosphors

The photoluminescence(PL) properties of Y2O3:Eu3+nanophosphors were systematically investigated with the goal of improving the color quality and quantum efficiency of Y2O3:Eu3+nanophosphors for potential applications in nanoscale devices. The emission spectra, excitation spectra and fluorescence decay curves were employed to trace the energy transfer process from Eu3+at C3isite to Eu3+at C2site. The experimental results show that the energy transfer process becomes more and more efficient with the increase in the Eu3+concentration. The emission of Eu3+at C2site is favorable because it has high radiative efficiency and better color quality. The successful suppress of the emission Eu3+at C3iis especially important for its applications in general illumination or display technology. The quantum efficiency and color quality of Y2O3:Eu3+can be improved by controlling the energy transfer between the Eu3+at S6site and Eu3+at C2site.