Eu~(3 )、Si~(4 )共掺杂TiO_2光催化剂的协同效应

采用溶胶-凝胶-浸渍法制备了Eu/Ti/Si纳米光催化剂,并通过XRD、FT-IR、EPR等进行了表征.结果表明,掺入Eu3 和Si4 ,阻止了TiO2从锐钛矿晶型向金红石晶型的转变,使TiO2的粒径减小,且Eu3 能够促进Si4 进入TiO2的晶格中.以甲基橙为光催化反应模型化合物,考察了光催化剂的活性.测定了甲基橙在不同光催化剂上的吸附常数,探讨了催化剂对甲基橙的吸附机理.Eu3 和Si4 的最佳掺入量分别为wEu=0.03%、wSiO2=39.06%,且Eu3 和Si4 同时掺入TiO2光催化剂产生协同效应.讨论了光催化活性与催化剂性质的关系.     

La2O3掺杂TiO2光催化剂的制备和性能

采用溶胶-凝胶法制备了La2O3掺杂TiO2纳米光催化剂，并通过XRD、TEM、BET和XPS等手段进行了表征．掺入La2O3后，阻止了TiO2从锐钛矿晶型向金红石晶型的转变，使TiO2的粒径减小，比表面积增大．以甲基橙为光催化降解反应模型化合物，考察了光催化剂的活性．测定了甲基橙在纯TiO2和La2O3掺杂TiO2光催化剂上的吸附常数．考察了pH、H2O2对降解性能的影响．讨论了光催化活性与催化剂性质的关系．     

低量La3+掺杂S-TiO2光催化剂的制备、表征及其光催化活性

采用溶胶-凝胶-浸渍法制备了La³⁺/S-TiO₂纳米光催化剂,通过XRD、BET、XPS、UV-Vis等手段进行了表征.以甲基橙溶液为光催化降解反应的模型化合物,考察了光催化剂的活性,探讨了低量La³⁺掺杂对TiO₂纳米粒子光催化活性的影响机制.实验结果表明:S改性TiO₂后明显提高了TiO₂纳米粒子的光催化活性,而La³⁺掺杂S-TiO₂后,进一步提高了TiO₂纳米粒子的光催化活性,La³⁺的最佳掺杂量(相对于TiO₂的质量分数)为0.369%;La³⁺/S-TiO₂(ω(La³⁺)=0.369%)为纳米光催化剂时,甲基橙的脱色率达到92.4%(光照120min);XRD和BET分析表明,低量La³⁺掺杂抑制了TiO₂由锐钛矿向金红石的转变,阻碍了TiO₂晶粒的生长,提高了TiO₂的比表面积;XPS分析表明,S、La³⁺掺杂可以导致粉体的表面羟基含量增加,掺杂S以S⁶⁺形式置换TiO₂晶格中的Ti⁴⁺;UV-Vis分析表明,光催化剂La³⁺/S-TiO₂比纯TiO₂具有较强的紫外光吸收性能.与纯TiO₂相比,La³⁺掺杂TiO₂纳米粒子光催化氧化活性的提高应归因于La³⁺掺杂增加了表面羟基含量,增大了比表面积,增强了样品表面的紫外光吸收能力.     

具有可见光响应的C、N共掺杂TiO2纳米管光催化剂的制备

为了提高二氧化钛对可见光的利用效率,采用等离子体电解方法对二氧化钛实现了C、N共掺杂.掺杂通过等离子体电解HCONH2、NaNO2、(NH2)2CO产生活性N、C实现.XPS结果表明,C、N掺杂进入了氧化钛晶格.紫外漫反射光谱分析表明,氧化钛对可见光(＞400 nm)的响应增强,其光催化降解能力也大大增强.C、N共掺杂TiO2是一种利用太阳能的理想的光催化剂.     

Fe3+,Si4+掺杂TiO2纳米材料相变和热稳定性研究

Guth等人在1977年首次报道了铁(Ⅲ)掺杂二氧化钛催化剂对氮气光催化还原为氨具有独特的光催化效果,开辟了一条太阳能转化为化学能的新途径,引起了人们对铁(Ⅲ)掺杂二氧化钛的研究热潮。大量的研究结果表明,纯的二氧化钛或三氧     

具有可见光响应的C、N共掺杂TiO2纳米管光催化剂的制备

为了提高二氧化钛对可见光的利用效率, 采用等离子体电解方法对二氧化钛实现了C、N共掺杂. 掺杂通过等离子体电解HCONH2、NaNO2、(NH2)2CO产生活性N、C实现. XPS结果表明, C、N掺杂进入了氧化钛晶格. 紫外漫反射光谱分析表明, 氧化钛对可见光(>400 nm)的响应增强, 其光催化降解能力也大大增强. C、N共掺杂TiO2是一种利用太阳能的理想的光催化剂.     

具有可见光响应的C、N共掺杂TiO2纳米管光催化剂的制备（英文）

为了提高二氧化钛对可见光的利用效率,采用等离子体电解方法对二氧化钛实现了C、N共掺杂.掺杂通过等离子体电解HCONH2、NaNO2、（NH2）2CO产生活性N、C实现.XPS结果表明,C、N掺杂进入了氧化钛晶格.紫外漫反射光谱分析表明,氧化钛对可见光（〉400nm）的响应增强,其光催化降解能力也大大增强.C、N共掺杂TiO2是一种利用太阳能的理想的光催化剂.     

硼铈共掺杂纳米TiO2光催化降解三氯杀螨醇和菊酯类农药

采用溶胶-凝胶法在钛酸丁酯水解过程引入硼酸、硝酸铈,制备具有光催化活性的硼铈共掺杂纳米二氧化钛（TiO2）,经XRD、TEM、FT-IR、UV-Vis-DRS表征晶体结构,在日光灯照射下,光催化降解三氯杀螨醇、高氟氯氰菊酯、氟戊菊酯农药。结果表明：硼铈共掺杂的TiO2只有锐钛矿型,而纯的或掺铈的TiO2有含有锐钛矿型、金红石相和少量板钛矿型,UV-Vis-DRS测定结果表明硼铈共掺杂的TiO2禁带宽度变小,硼铈共掺杂的TiO2在可见光区吸光度高于掺杂铈和不掺杂的TiO2,在420nm~850nm有强的吸收;在同样光照下对三氯杀螨醇、高氟氯氰菊酯、氟戊菊酯的降解试验证明硼铈共掺杂纳米TiO2的光催化活性高于不掺杂或只掺杂铈的TiO2。     

硼硫共掺杂TiO2的光催化性能及掺杂机理

采用水热法制备了硼硫共掺杂的TiO2光催化剂(TiO2-B-S),并用其光催化降解甲基橙.结果表明,在240℃下水热反应12h时制得的TiO2-B-S具有较高的催化活性,紫外光照射50min和太阳光照射230min时对甲基橙的降解率分别达99.8%和81%.X射线粉末衍射、紫外-可见漫反射光谱和X射线光电子能谱等研究表明,TiO2-B-S为锐钛矿晶型,硫硼掺杂能抑制TiO2粒径的生长;TiO2-B-S同时具有较高的紫外光和可见光活性的原因可能是掺杂的硼以B3 进入晶格中,导致TiO2晶格畸变,带隙变窄.掺杂的硼和硫还提高了TiO2的表面酸度和对可见光的吸收.     

铁、氮共掺杂二氧化钛粉末的制备及光催化活性

Using TiCl₄ as the titanium source, nanoparticles of TiO₂ doped with nitrogen(N-TiO₂) were synthesized by triethylamine. TiO₂ powder codoped with iron and nitrogen(Fe/N-TiO₂) were prepared by adsorption-deposition of Fe³⁺ on N-TiO₂ and calcining at 400 ℃ for 2 h. From the XPS results for N1s binding energy at 399.6 eV and 396.6 eV, it is proposed that the partial N atoms as substitution atoms replace for O atoms in TiO₂ lattice. The onset of the absorption spectrum of Fe/N-TiO₂ has a 45 nm red-shift compared with that of TiO₂. The results of photocatalytic degradation of methylene blue solution indicate that Fe/N-TiO₂(0.45% Fe³⁺) has a higher activity. Its photocatalytic activity is about 2 times as high as that of pure TiO₂ under UV-light, and 3 times under sunlight. Doping of nitrogen in TiO₂ enhances photoresponse in visible light region and doping of Fe³⁺ reduces the recombination of electrons and holes. Both of the above effects are beneficial for improving the performances of Fe/N-TiO₂ photocatalyst.     

包覆型磁性二氧化钛的制备及其光催化性能的研究

采用表面改性的方法分别制备了两种核-壳和核-壳-壳式结构的TiO2/γ-Fe2O3,TiO2/S iO2/γ-Fe2O3包覆型磁性二氧化钛.用XRD、TG-DTA、TEM、BET、和IR等手段对样品进行了结构表征,并研究了它们在紫外光照射下对甲基橙的降解性能.结果表明,在紫外光的照射下,包覆型磁性二氧化钛可有效地降解甲基橙;TiO2/S iO2/γ-Fe2O3的光催化活性优于TiO2/γ-Fe2O3,前者在循环使用三次后降解率仍不低于95%.     

Preparation,Characterization and Photocatalytic Activity of Fe,La Co-doped Nanometer Titanium Dioxide Photocatalysts

A series of photocatalysts of un-doped, single-doped and co-doped nanometer titanium diox-ide (TiO₂) have been successfully prepared by template method using Fe(NO₃)₃·9H₂O, La(NO₃)₃·6H₂O, and tetrabutyl titanate as precursors and glucan as template. Scanning electron microscopy, X-ray diffraction, and N₂ adsorption-desorption measurement were em-ployed to characterize the morphology, crystal structure and surface structure of the samples. The photo-absorbance of the obtained catalysts was measured by UV-Vis absorption spec-troscopy, and the photocatalytic activities of the prepared samples under UV and visible light were estimated by measuring the degradation rate of methyl orange in an aqueous solu-tion. The characterizations indicated that the prepared photocatalysts consisted of anatase phase and possessed high surface area of ca. 163-176 m²/g. It was shown that the Fe and La co-doped nano-TiO₂ could be activated by visible light and could thus be used as an effective catalyst in photo-oxidation reactions. The synergistic effect of Fe and La co-doping played an important role in improving the photocatalytic activity. In addition, the possibil-ity of cyclic usage of co-doped nano-TiO₂ was also confirmed, the photocatalytic activity of codoped nano-TiO₂ remained above 89.6% of the fresh sample after being used four times.     

二氧化钛涂覆多壁碳纳米管的制备及可见光催化活性

以多壁碳纳米管(MWCNTs)为反应性模板, 金属钛粉为钛源, 采用熔盐法制备碳化钛涂覆的MWCNTs中间体, 然后通过控制氧化制备二氧化钛涂覆的MWCNTs复合光催化剂. 考察了熔盐反应温度、MWCNTs和钛粉的摩尔比及氧化温度等对产物的结构和形貌的影响. 采用X射线衍射(XRD)、场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)和X射线光电子能谱(XPS)等技术对其进行了系统的表征; 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了催化剂的可见光(λ>420 nm)催化活性. 结果表明: 所制备的催化剂基本保持了原始MWCNTs的纤维状形貌, 二氧化钛涂层在MWCNTs表面分布均匀, 并与MWCNTs之间结合紧密, 形成了Ti－O－C键. MWCNTs增强了污染物亚甲基蓝在催化剂表面的吸附, Ti－O－C键的形成使得在二氧化钛价带附近形成了杂质能级, 提高了对可见光的吸收和利用, 因此所制备的TiO₂/MWCNTs复合光催化剂表现出较高的可见光催化活性.     

稀土镧掺杂二氧化钛的光催化特性

二氧化钛有合适的禁带宽度,在光催化体系中有较好的稳定性,是一种较为理想的半导体光催化剂.近来,在太阳能转换和储存,二氧化碳还原,有害复杂有机物降解等方面都引起了广泛的研究兴趣.已有文献报导了不同的掺杂催化体系对其光催化性能的影响.Ｋａｋｕｔａ[1,2]等研究了二氧化钛复合氧化物体系的光催化性能.Ｃｈｏｉ[3]等系统地研究了过渡金属氧化物掺杂的二氧化钛的光催化性能和空穴电子复合之间的联系.也有研究者从掺杂体系的晶体结构和表面物化性质,如晶相(锐钛矿,金红石,无定形),比表面积,晶粒尺寸和表面羟基的角度讨论与光催化活性的关…     

磁性二氧化钛纳米粒子的制备及其光催化性能

以硫酸钛和Fe3O4为原料, 采用共沉淀法制备了掺杂不同量Fe3O4的磁性纳米TiO2 (Fey-TiO2+x) , 通过X-射线衍射(XRD)、热重-差示扫描量热(TG-DSC)、紫外-可见吸收光谱(UV-Vis) 和荧光光谱等分析手段对样品的晶体类型、光谱吸收特征和磁响应性等进行了表征;以太阳光为光源, 考察其对甲基橙的光催化降解活性. 结果表明, Fey-TiO2+x纳米粒子主要以锐钛矿相存在, 粒子的粒径约为12 nm;在8 mT外加磁场作用下, 粒子悬浮液的吸光度在12 min内减少70%, 而无外加磁场时仅减少25%, 说明Fey-TiO2+x纳米粒子具有良好的磁响应性. Fe2+和Fe3 +离子掺入TiO2 后, 使TiO2晶格形成缺陷, 使吸收带边由380 nm 红移到460 nm, 从而提高了TiO2对可见光的吸收效率. Fe的最佳掺杂量为Ti的0.05%(摩尔比), 该催化剂在240 min内对甲基橙的降解率接近100%;加入少量H2O2能显著提高Fe0.05-TiO2的光催化性能, 在20 min内对甲基橙的降解率即接近100%.     

铁和铈共掺杂二氧化钛中的协同效应

The co-doping of iron and cerium into TiO2 was studied by means of X-ray diffraction, Raman spectroscopy, UV-Vis diffuse reflectance spectroscopy and X-ray photoelectron spectroscopy. when separately doping via the sol-gel method, iron was introduced in the framework of anatase TiO2 whereas cerium was not; interestingly, both iron and cerium were introduced in the framework when co-doping by the sol-gel method. The co-doped TiO2 behaves much more intense surface hydroxyl concentration than the separately-doped and pure TiO2. This observation demonstrates for the first time a cooperative effect in the co-doping of transitional metals in the framework of TiO2.     

用高温热水解法制备高活性TiO2纳米微晶光催化剂

采用钛酸四西酯在有机溶剂中高温热水解与结晶同时进行的方法，制备了二氧化钛纳米微晶光催化剂．以XRD、BET、TEM、TG和DTA等方法对获得的微晶进行了表征．所制得的TiO2纳米微晶平均值径约为12nm，比表面积在100m2·g-1以上，并能在报宽的煅烧温度范围内保持锐钛矿型晶体结构．将它应用于光分解甲基橙，具有高的光催化活性．     

空心锌铬铁氧体/二氧化钛复合物的制备及去污性能

以葡萄糖溶液为原料,通过水热法制备了分散性良好的碳微球;以碳微球为模板,应用化学沉淀法和热处理技术除去碳核获得空心铬锌铁氧体;用钛酸四丁酯作为钛源,在空心铁氧体表面包覆二氧化钛制备了锌铬铁氧体/二氧化钛二元复合物.采用现代分析技术表征了制备样品的微观结构、形貌和电磁性能,并对其吸附和降解染料废水的性能进行了研究.结果表明,Zn Cr_(0.25)Fe_(1.75)O_4对染料废水具有较好的去污效果,对甲基橙和罗丹明B的去污效率分别为87%和83%;TiO_2对铁氧体的包覆能提高复合物对染料废水的光催化降解性能,其中m_(T/ZCF)=0.3的ZnCr_(0.25)Fe_(1.75)O_4/TiO_2复合物的去污效果最佳,几乎与纯二氧化钛相仿.     

CaMoO4∶Eu3+发光材料的制备和发光性质的研究

用共沉淀法与高温焙烧法制备了样品CaMoO4:Eu3+.TG-DTA谱图表明:800℃时,样品吸收的能量最大,即形成稳定的CaMoO4:Eu3+结构.用XRD谱图进一步分析表明:800℃时,样品CaMoO4:Eu3+已形成CaMoO4的白钨矿结构.由于2个Eu3+取代3个Ca2+,导致了晶体产生微小的晶体缺陷,从而形成具有p-n结的半导体.经过激发和发射谱图的测试发现:这种缺陷结构不但可以使Eu3+禁戒的4f电子发生跃迁,而且可以使MoO42-的能量高效地传递给Eu3+.尤其使与MoO42-的发射特征峰(488 nm)部分重叠的Eu3+(465 nm)的7F0→5D2电子跃迁得到了极大的加强,进而在λex=465 nm的发射谱图中,自激活荧光体MoO42-的发射强度被大大减弱甚至猝灭,而Eu3+的5D0→7F2(612 nm)跃迁的红光发光强度被大大增强,使该材料成为有潜在应用价值的发光材料.