研究制备新型炭材料是提高电化学电容器性能的有效途径。本文以二氧化硅干凝胶为模板,以合成间苯二酚-甲醛(RF)干凝胶为炭前驱体,采用同步合成模板法制得了比表面积达1100m²·g^-1,孔径分布集中,平均孔径为4.5nm的炭材料。循环伏安研究表明,与比表面积为1720m²·g^-1的活性炭相比,本研究制得的炭材料具有更优异的电化学电容性能,2mV·s^-1时比容量达195F·g^-1。     

简易模板法制备有序介孔碳

通过一种简易的模板法制备了有序介孔碳,即硅/P123三嵌段共聚物复合物经硫酸处理后,再加入蔗糖碳源经碳化和除硅处理合成出有序介孔碳。该方法与传统硬模板相比,其合成工序简单,成本更低;与其他简化合成方法相比,避免了由碳源不足而造成的介孔碳有序性低的缺点。通过小角XRD、N2吸脱附和HRTEM对样品及其中间过程进行了表征。结果表明,自晶化过程后,样品在合成的各个时期均保持着有序的介孔结构,当蔗糖添加量为1.5g时合成出的介孔碳材料有序性最高,比表面积和孔容也最高,分别为1261m2·g-1,1.03cm3·g-1。     

半晶化双螺旋介孔MnO2的合成和电化学性质

Mesoporous silica KIT-6 has novel three-dimensional gyroidal channel structure, space group of 1a-3d, and ordered tunable pores up to 10 nm. In this paper, such mesostructured silica was employed as hard template to prepare semicrystalline gyroidal mesoporous MnO2. The structure was investigated by XRD, TEM and HRTEM, and found to be of high quality 1a-3d symmetry, in good accordance with the template structure. The material has a BET surface of 118 m2·g^-1 and pore volume of 0.35 cm3·g^- 1 after eliminating template. Mesoporous MnO2 has shown good electrochemical property as supercapacitor material in 1 mol·L^-1 Na2SO4 and 1 mol·L^-1 LiClO4 solutions, but interesting pseudocapacitance behavior was observed in the case of 6 mol·L^-1 KOH. It was found that mesoporous MnO2 performed stable reversible electrochemical behavior with capacitance of 220 F·g^-1 in a potential range of -0.1-0.55 V vs. Hg/HgO in alkaline solution, demonstrating that it is a promising novel electrode material for the fabrication of electrochemical capacitors.     

Design of hierarchical porous aluminas by using one-pot synthesis and different calcination temperatures

Hierarchical aluminas with pore sizes ranging from a few nanometers to micrometers were obtained using an one-pot sol?Cgel synthesis. The aluminas were synthesized under acid conditions from aluminum isopropoxide in presence of poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) triblock copolymer template and decahydronaphthalene as emulsifier agent. High-resolution transmission electron microscopy, small-angle X-ray scattering, nitrogen physisorption isotherms and mercury intrusion porosimetry provided evidences of porous structure at different hierarchical levels. The produced aluminas possess hierarchical structure composed of different family of pores that coexist in form of cylinders, pyramids and stacking of platelets. The morphology observed by electron microscopy suggests that the cylindrical pores result from the stacking platelets and that the cylinders and pyramidal pores form the walls of macropores of circular section. These aluminas with hierarchical porous architecture present large surface areas (ca. 435?m² g^?1) and pore volumes (ca. 2.1?cm³ g^?1), tunable pore-size distributions and good thermal stability.     

Templated Synthesis of Tailored Clays (Based on Sol-Gel Techniques) to Yield Increased Pore Volumes for Sorption and Exchange

Synthesis and modification of Laponite-related materials by surfactants and globular cations, leading to increased pore volume and enhanced specific surface area, is reported. Materials produced using cationic and neutral surfactants, as well as those with varying tail length and head size are compared. The characteristics of these tailored materials have been determined via nitrogen sorption porosimetry and X-ray powder diffraction. The appropriate choice of surfactant leads to markedly enhanced total pore volumes and modified textures. Most significantly, an increase in total pore volume from 0.27 cm³ g^?1 (Laponite RD without templating) to 0.94 cm³ g^?1 (using a non-ionic surfactant as template/modifier) is reported.     

大碳层间距的沥青基多级孔碳材料的制备及其在超级电容器中的应用

基于KOH活化法,以纳米级片层多孔MgO为模板剂,制备大碳层间距的沥青基超级电容器用多级孔碳材料。考察了模板剂添加量对多孔碳材料孔分布、碳层间距等理化性能及电化学性能的影响。结果表明模板剂添加量为沥青质量的25%时,多孔碳材料比表面积、孔体积分别为2 634 m~2·g~(-1)、1.12 cm~3·g~(-1),碳层间距高达0.374 nm,用于超级电容器电极材料时,1和20A·g~(-1)电流密度下的比电容分别为338和277 F·g~(-1),经过10 000次循环恒电流充放电,1 A·g~(-1)下容量保持率为93.5%,展现了优异的电化学性能。     

Thermal evolution of mesoporous titania prepared by CO2 supercritical extraction

Porous anatase is attractive because of its notable photo-electronic properties. Titania wet gel prepared by hydrolysis of Ti-alkoxide was immersed in the flow of supercritical CO₂ at 60°C and the solvent was extracted (aerogel). Mesoporous TiO₂ consisting of anatase nano-particles, about 5 nm in diameter, have been obtained. Thermal evolution of the microstructure of the aerogel was evaluated by TGA-DTA, N₂ adsorption, TEM and XRD, and discussed in comparison with that of the corresponding xerogel. The diffraction peaks of anatase were found for the as-extracted gel while the xerogel dried at 90°C was amorphous. After calcination at 600°C, the average pore size of the aerogel, about 20 nm in diameter, was 4 times larger than that of the xerogel, and the pore volume, about 0.35 cm³ g⁻¹, and the specific surface area, about 60 m² g⁻¹, were 2 times larger than those of the xerogel. XRD peaks of rutile have been found after calcination at 600°C. The particle sizes of anatase and rutile are about 13 and 25 nm in diameter, respectively. The surface morphology of TiO₂ nano-particles has been discussed in terms of their surface fractal dimensions estimated from the N₂ gas adsorption isotherms.     

Mesoporous carbon/sulfur composite with N-doping and tunable pore size for high-performance Li-S batteries

Mesoporous carbons (MCs) were used as the matrixes to load sulfur for lithium sulfur (Li-S) batteries, and pore sizes were tuned by heat treatment at different high temperatures. The cathode material shows the highest discharge capacity of 1158.2 mAh g^?1 at the pore size of 4.1 nm among as-prepared nitrogen-free materials with different sizes. Meanwhile, the nitrogen doping of mesoporous carbon helps to inhibit the diffusion of polysulfide species via an enhanced surface adsorption. The carbon/sulfur containing N (4.56%) shows a high initial discharge capacity of 1315.8 mAh g^?1 and retains about 939 mAh g^?1 after 100 cycles at 0.2 C. The improved electrochemical performance is ascribed to the proper pore size, surface chemical property, and conductivity of the N-doped carbon material.     

壳聚糖基多孔碳材料的制备及其超级电容性能

以胶态SiO₂纳米粒子为模板,壳聚糖为碳源,ZnCl₂为活化剂,制备了具有不同比表面积和孔体积的氮掺杂介孔碳。采用多种表征手段对碳材料的微观形貌、比表面积和孔道结构进行了表征,探究了壳聚糖与SiO₂纳米粒子的比例以及ZnCl₂活化剂对碳材料孔体积和比表面积的影响。结果表明,在未使用活化剂时碳材料(CSi-1.75)的孔体积高达4.53 cm³·g^-1,但其比表面积最小(729 m²·g^-1);使用ZnCl₂作为活化剂制备的碳材料(CSi-1.75-Zn)比表面积为1 032 m²·g^-1,但其孔体积下降到1.99 cm³·g^-1,且具有最多的吡啶氮和吡咯氮。在以6.0 mol·L^-1KOH为电解液的三电极体系中,当电流密度为0.5 A·g^-1时,CSi-1.75...     

Synthesis of Ordered Mesoporous Carbon Materials by Dry Etching

A novel synthesis method for ordered mesoporous carbons is presented. The inverse replication of a silica template was achieved using the carbonization of sucrose within mesoporous KIT‐6. Instead of liquid acid etching, as in classical nanocasting, a novel dry chlorine etching procedure for template removal is presented for the first time. The resultant ordered mesostructured carbon material outperforms carbons obtained by conventional hard templating with respect to high specific micro‐ and mesopore volumes (0.6 and 1.6 cm³ g^?1, respectively), due to the presence of a hierarchical pore system. A high specific surface area of 1671 m² g^?1 was achieved, rendering this synthesis route a highly convenient method to produce ordered mesoporous carbons.     

壳聚糖基多孔碳材料的制备及其超级电容性能

以胶态SiO₂纳米粒子为模板,壳聚糖为碳源,ZnCl2为活化剂,制备了具有不同比表面积和孔体积的氮掺杂介孔碳。采用多种表征手段对碳材料的微观形貌、比表面积和孔道结构进行了表征,探究了壳聚糖与SiO₂纳米粒子的比例以及ZnCl2活化剂对碳材料孔体积和比表面积的影响。结果表明,在未使用活化剂时碳材料(CSi-1.75)的孔体积高达4.53 cm³·g^-1,但其比表面积最小(729 m²·g^-1);使用ZnCl₂作为活化剂制备的碳材料(CSi-1.75-Zn)比表面积为1032 m²·g^-1,但其孔体积下降到1.99 cm³·g^-1,且具有最多的吡啶氮和吡咯氮。在以6.0 mol·L^-1 KOH为电解液的三电极体系中,当电流密度为0.5 A·g^-1时,CSi-1.75-Zn的比电容为344 F·g^-1,而CSi-1.75的比电容仅为255 F·g^-1。这表明碳材料的比表面积对超级电容性能影响最大,而孔体积影响较小。电容贡献分析结果表明,相对于CSi-1.75,CSi-1.75-Zn的双电层电容和赝电容都得到了提高,这表明更大的比表面积和更多的吡啶氮和吡咯氮有利于提高碳材料的超级电容性能。     

Manganese Oxide/Graphene Aerogel Composites as an Outstanding Supercapacitor Electrode Material

Graphene aerogels (GA), prepared with an organic sol–gel process, possessing a high specific surface area of 793 m² g^?1, a high pore volume of 3 cm³ g^?1, and a large average pore size of 17 nm, were applied as a support for manganese oxide for supercapacitor applications. The manganese oxide was electrochemically deposited into the highly porous GA to form MnO₂/GA composites. The composites, at a high manganese oxide loading of 61 wt. %, exhibited a high specific capacitance of 410 F g^?1 at 2 mV s^?1. More importantly, the high rate specific capacitances measured at 1000 mV s^?1 for these composites were two‐fold higher than those obtained with samples prepared in the absence of the GA support. The specific capacitance retention ratio, based on the specific capacitance obtained at 25 mV s^?1, was maintained high, at 85 %, even at the high scan rate of 1000 mV s^?1, in contrast with the significantly lower value of 67 % for the plain manganese oxide sample. For the cycling stability, the specific capacitance of the composite electrode decayed by only 5 % after 50,000 cycles at 1000 mV s^?1. The success of this MnO₂/GA composite may be attributed to the structural advantages of high specific surface areas, high pore volumes, large pore sizes, and three‐dimensionally well‐connected network of the GA support. These structural advantages made possible the high mass loading of the active material, manganese oxide, large amounts of electroactive surfaces for the superficial redox events, fast mass‐transfer within the porous structure, and well‐connected conductive paths for the involved charge transport.     

Porous carbon synthesized by direct carbonization of potassium biphthalate for high-performance supercapacitors

Porous carbons have been synthesized by a direct carbonization of potassium biphthalate without an activation process. The experimental results demonstrate that the carbonization temperature plays a crucial role in determining the surface area and pore structure as well as the correlative capacitive performance. The carbon-700/800/900 samples display surface areas of 672, 1,023, and 1,380 m² g^?1 and total pore volumes of 0.38, 0.56, and 0.78 cm³ g^?1, respectively. The specific capacitances of the carbon-700/800/900 samples are 300.4, 272.3, and 243.4 F g^?1, respectively, at a current density of 0.5 A g^?1. More importantly, the carbon-900 sample possesses the highest capacitance retention (~98.4 %) even undergoing charge–discharge 10,000 times. The potassium biphthalate used as a carbon source is inexpensive and commercially available, making it promising for the large-scale production of porous carbons as an excellent electrode material for supercapacitors.     

Dual template method to prepare hierarchical porous carbon nanofibers for high-power supercapacitors

Hierarchical porous carbon nanofibers serving as electrode materials are prepared through carbonization and hydrofluoric acid treatment of polyacrylonitrile-based electrospinning involving dual templates. The hierarchical porous structures are synergistically tailored by varying template contents in the spinning solution. The carbon nanofibers prepared from the electrospinning of polyacrylonitrile containing 15/15 wt.% polymethylmethacrylate/tetraethyl orthosilicate exhibit the largest specific surface area (699 m² g^?1) and microporous volume (0.196 cm³ g^?1). In 6 M KOH electrolyte, a symmetrical supercapacitor equipped with the hierarchical porous carbon nanofibers demonstrates its high-end specific capacitance of 170 F g^?1, superior rate capability, and high-power density output up to 14.7 kW kg^?1. Cycling evolution indicates capacitance fading is only 5.8 % of initial capacitance at a current density of 1 A g^?1 even after 8,000 cycles. The excellent electrochemical performances of the carbon nanofiber are mainly ascribed to the optimized pore size distributions of both micropores and mesopores and the unique hierarchical pore structures possessed by abundant micropores.     

Hierarchical mesoporous carbon materials: preparation by direct tri-constituent co-assembly and the electrochemical performance

Hierarchical mesoporous carbon materials with large microporosity were prepared by direct tri-constituent co-assembly with the use of resols as the carbon precursor, tetraethyl orthosilicate as the inorganic precursor, and triblock copolymer F127 as the soft template. Bimodal pore size distributions in the range of 1.5–4 and 7.5–12 nm were obtained in the synthesized hierarchical mesoporous carbon materials after etching of silica by HF acid, showing a high surface area of 1,675 m²?g^?1 with a large pore volume of 2.06 cm³?g^?1. The electrochemical performance of the hierarchical mesoporous carbons was evaluated as an electrode material for electrochemical supercapacitor, showing a specific capacitance as high as 152 F?g^?1 at a scan rate of 5 mV?s^?1 in 6 M KOH aqueous solution and a good cycling stability with capacitance retention of 99 % over 500 cycles.     

Ammonia-treatment assisted fully encapsulation of Fe2O3 nanoparticles in mesoporous carbons as stable anodes for lithium ion batteries

To improve the initial coulombic efficiency and bulk density of ordered mesoporous carbons, active Fe₂O₃ nanoparticles were introduced into tubular mesopore channels of CMK-5 carbon, which possesses high specific surface area (>1700 m²·g^?1) and large pore volume (>1.8 cm³·g^?1). Fine Fe₂O₃ nanoparticles with sizes in the range of 5–7 nm were highly and homogenously encapsulated into CMK-5 matrix through ammonia-treatment and subsequent pyrolysis method. The Fe₂O₃ loading was carefully tailored and designed to warrant a high Fe₂O₃ content and adequate buffer space for improving the electrochemical performance. In particular, such Fe₂O₃ and mesoporous carbon composite with 47 wt% loading exhibits a considerably stable cycle performance (683 mAh·g^?1 after 100 cycles, 99% capacity retention against that of the second cycle) as well as good rate capability. The fabrication strategy can effectively solve the drawback of single material, and achieve a high-performance lithium electrode material.     

Nitrogen-containing nanoporous carbons by a rational template carbonization method evinced in the cases of 1, 10-phenanthroline and benzimidazole

We demonstrate a rational template carbonization method to produce nitrogen-containing nanoporous carbons at 800 °C, using 1, 10-phenanthroline (or benzimidazole) as carbon/nitrogen source and magnesium citrate as template. The mass ratio of 1, 10-phenanthroline (or benzimidazole) and magnesium citrate has exerted the vital role in the determination of pore structures and the resulting electrochemical performances. It reveals that the carbon-P:Mg-1:1 (obtained by heating 1, 10-phenanthroline and magnesium citrate at 800 °C with the mass ratio of 1:1) and carbon-B:Mg-1:1 (obtained by heating benzimidazole and magnesium citrate at 800 °C with the mass ratio of 1:1) samples both are amorphous, nitrogen-containing, and highly nanoporous in nature. The carbon-P:Mg-1:1 sample has a large BET surface area of 1,657.4 m² g^?1 and high pore volume of 1.83 cm³ g^?1, and those of carbon-B:Mg-1:1 sample are of 1,105.4 m² g^?1 and 1.67 cm³ g^?1, respectively. Based on a three-electrode system using a 6-mol L^?1 KOH aqueous solution as electrolyte, the carbon-P:Mg-1:1 and carbon-B:Mg-1:1 samples can deliver large specific capacitances of 289.0 and 255.6 F g^?1 at a current density of 0.5 A g^?1. They can also exhibit high energy densities of 40.1 and 35.5 Wh kg^?1 when designated the power density as 0.25 kW kg^?1 as well as highly long-term cycling durabilities.     

有序介孔碳的简易模板法制备与电化学电容性能研究

0引言电化学电容器(Electrochemical Capacitors),又称为超级电容器(supercapacitors)是介于传统电容器和二次电池之间的一种新型储能装置,它具有循环寿命长、比容量高、能快速充放电等优点[1,2]。近年来随着电子、电气设备的日趋小型化以及电动汽车工业的不断发展,作为后备电源和记忆候补装置的超级电容器日益引起了人们的广泛关注。碳材料由于具有成本低、比表面积大、导电性优良、制备电极工艺简单等特点,一直是超级电容器电极材料的首选。其中,活性炭是最早采用的多孔电极材料,其比表面积可高达2500￣3000m·2g-1[3]。然而,活性炭材料…     

Gels dried under supercritical and ambient conditions: a comparative study and their subsequent conversion to silica–carbon composite aerogels

In present work, we have prepared gels with various compositions of methyltrimethoxysilane—3-(2,3-epoxypropoxy) propyltrimethoxysilane (MTMS-GPTMS) using a two-step acid base sol–gel process. To make a comparative study between the two common drying routes, we prepared gels under supercritical and also under ambient conditions. The density of the supercritically dried hybrid aerogels lies between 0.18 and 0.31 gcm^?3, while the density of the ambient dried ones ranges between 0.35 and 0.42 gcm^?3. The surface area of MTMS-0.25 GPTMS aerogel dried under supercritical conditions, has been found to be 464 m² g^?1 with a pore volume and average pore diameter of 1.24 cm³ g^?1 and 11 nm respectively. The same composition dried under ambient conditions is found to have similar properties i.e. a BET surface area of 439 m² g^?1, pore volume of 1.22 cm³ g^?1 and average pore diameter of 11 nm. The aerogels were later pyrolyzed yielding silica/carbon composite aerogels. The pyrolized aerogels possessed a surface area as high as 207 m² g^?1 with a total pore volume of 0.98 cm³ g^?1. The pyrolysed aerogels were also calcined to yield carbon free materials.     

酸法纳米纤维素模板剂合成介孔TiO2及光催化活性

以生物可再生资源的酸法纳米纤维素为模板剂,四氯化钛为钛源,采用液相水解-沉淀法制备了具有介孔结构的TiO2光催化剂。采用低温N2物理吸附-脱附、透射电镜(TEM)、X射线衍射(XRD)、热重-量热扫描(TG/DSC)、傅里叶变换红外(FTIR)、X射线光电子能谱(XPS)等对介孔TiO2进行了表征,并以甲基橙为模型物,考察了介孔TiO2光催化活性。结果表明,以酸法纳米纤维素为模板剂合成的TiO2光催化活性显著提高,且具有良好的孔隙结构,平均孔径5.03 nm、总孔容积0.35 cm3.g-1、比表面积192m2.g-1;纤维素模板剂合成的TiO2表面羟基数量降低;纤维素长链分子结构之间的羟基与TiO2表面羟基的键合,可有效限制TiO2前驱体的生长和团聚,并抑制锐钛矿相TiO2向金红石相转变。