Influence of Al-doped ZnO and Ga-doped ZnO substrates on third harmonic generation of gold nanoparticles

Principal role of substrate types on the nonlinear optical properties of Au NP was investigated. Third harmonic generation (THG) studies were carried out for Au NP deposited on the Al-doped ZnO (AuNP/AZO) and Ga-doped ZnO (AuNP/GZO) substrates at fundamental wavelength of 20 ns Er:glass laser (generating at 1540 nm wavelength) during photostimulation by the 532 nm 15 ns laser pulses. Sizes of Au NP were 5 nm, 10 nm, 20 nm, and 30 nm. The output signal was registered at 513 nm. The photoinduced power density was increased from 0 up to 800 MW/cm². So in our work we explore the role of the substrate on the optically stimulated non-linear optical properties during simultaneous photo stimulation near the inter-band transition. The results were studied depending on the type of substrate and the sizes of the deposited nanoparticles. The analysis was done within a framework of interaction between the photoinduced light and SPR wavelengths. Control of the photoinduced temperature was done.     

Fabrication and characteristics of photodiode based on ZnO nanowire arrays and spray-coated regioregular P3HT layers

A photodiode based on well-aligned ZnO nanowire arrays (ZNAs) and spray-coated regioregular poly(3-hexylthiophene-2,5-diyl) (P3HT) layers hybrid hetero junctions was fabricated, and its electrical characteristics in dark and under illumination with a solar simulator were investigated. Current–voltage (I–V) data of ITO/ZNAs/P3HT/Ag device in dark and under illumination showed typical diode characteristics. A rectification ratio (RR) of 22.7 at 1.7 V and a low turn-on voltage of 0.4 V in dark were obtained. Also, the photodiode with high photo-response in the order of 0.31 A/W at -2 V using 80 mW/cm² illumination power was observed. Upon increasing illumination power from 40 to 100 mW/cm², the RR value for the photodiode continuously was improved with a highest value of 12.5.     

Operating temperature and the responsivity of split-off band detectors

A GaAs/AlGaAs heterojunction is used as a spin-split-off band IR detector operating at or around room temperature. This detector structure followed a similar layer architecture to the quantum well IR photo detectors (QWIP) and Heterojunction Interfacial Work function Internal Photoemission (HEIWIP) detectors. Compared to QWIPs, the emitter layer thickness is increased to avoid confinement. Unlike either the QWIPs or HEIWIPs, these detectors will have two energy gaps (barriers) to obtain the wavelength threshold which could be used to design detectors either for optimum operating temperature or optimum responsivity. The free carrier energy gap is determined by the Al fraction and the spin-split-off transition energy provides another handle on controlling the effective threshold of the detector. Unlike QWIPs, these will also detect normal incidence radiation. A preliminary detector showed a peak responsivity of 0.29 mA/W at 2.5 μm at room temperature.     

Synthesis and surface modification of ZnO:Cu nanoparticles by silica and PMMA

ZnO nanoparticles doped with Cu were synthesized by solid state reaction using different precursor routes and varying growth environment. Average crystallite size varied from 40 to 100 nm depending upon synthesis temperature, lower temperature favouring smaller particle size. Scanning electron microscope (SEM) images showed that particles synthesized at 250 °C were in the shape of nanorods but those synthesized at 900 °C had spherical shape. Luminescence emission showed marked dependence on the growth conditions varying from ultraviolet (UV) emission to green emission. For making the luminescent nanoparticles bio-compatible, a bioinorganic interface on ZnO:Cu nanoparticles was created by coating them with inert silica. Surface modification of ZnO:Cu was also done with lipophilic polymethylmethacrylate (PMMA). ZnO:Cu nanoparticles showed hexagonal wurtzite structure and the coating of silica was confirmed with the presence of two extra peaks due to silica in the XRD spectra. Thermogravimetric analysis (TGA) and FTIR spectroscopy indicated that PMMA molecules were adsorbed on the surface of ZnO:Cu nanoparticles. SEM images revealed that PMMA adsorption improved the dispersibilty of ZnO:Cu nanoparticles.     

ZnS修饰对ZnO纳米棒：P3HT复合薄膜I-V性质的影响

本文通过化学浴沉积法获得了直径约为50 nm, 长度约为250 nm的ZnO纳米棒阵列, 引入纳米ZnS对ZnO纳米棒进行表面修饰, 分别制备得到了具有ITO (indium tin oxides)/ZnO/Poly-(3-hexylthiophene) (P3HT)/Au和ITO/ZnO@ZnS/P3HT/Au结构的多层器件. 通过I-V曲线对比讨论了两种结构器件的开启电压, 串联电阻, 反向漏电流及整流比等参数, 认为包含ZnS修饰层器件的开启电压、串联电阻、反向漏电流明显降低, 整流比显著增强, 展现出更优异的电子传输性能. 光致发光光谱分析结果证实由于ZnS使ZnO纳米 棒的表面缺陷产生的非辐射复合被明显抑制, 弱化了电场激发下的载流子陷获, 改善了器件的导电特性. 关键词： ZnO纳米棒阵列 表面修饰 电流-电压特性     

The influence of Au thickness on the structural,optical and electrical properties of ZnO/Au/ZnO multilayer films

Transparent and conductive ZnO/Au/ZnO (ZAZ) multilayer films were deposited on glass substrates by magnetron sputtering without intentional substrate heating. The thickness of Au interlayer was set at 1, 2 and 3 nm.The observed structural, optical and electrical properties were dependent on the thickness of the Au interlayer. For all of the ZAZ films, the diffraction peaks in the XRD pattern were identified as the (002) and (103) planes of a ZnO films and the (111) plane of an Au interlayer. The ZAZ films with a 2 nm thick Au interlayer showed a higher figure of merit than the other ZAZ films prepared in this study, and they also demonstrated the relatively high work function of 5.13 eV.From these results, we concluded that a ZAZ film with a 2 nm thick Au interlayer is an alternative candidate for use as a transparent electrode in OLEDs and various flat panel displays.     

Utilization of surface plasmon resonance of Au/Pt nanoparticles for highly photosensitive ZnO nanorods network based plasmon field effect transistor

Hydrothermally processed highly photosensitive ZnO nanorods based plasmon field effect transistors (PFETs) have been demonstrated utilizing the surface plasmon resonance coupling of Au and Pt nanoparticles at Au/Pt and ZnO interface. A significantly enhanced photocurrent was observed due to the plasmonic effect of the metal nanoparticles (NPs). The Pt coated PFETs showed I_on/I_off ratio more than 3 × 10⁴ under the dark condition, with field-effect mobility of 26 cm² V⁻¹ s⁻¹ and threshold voltage of −2.7 V. Moreover, under the illumination of UV light (λ = 350 nm) the PFET revealed photocurrent gain of 10⁵ under off-state (−5 V) of operation. Additionally, the electrical performance of PFETs was investigated in detail on the basis of charge transfer at metal/ZnO interface. The ZnO nanorods growth temperature was preserved at 110 °C which allowed a low temperature, economical and simple method to develop highly photosensitive ZnO nanorods network based PFETs for large scale production.     

Molecular Beam Epitaxy growth and characterization of silicon – Doped InAs dot in a well quantum dot infrared photo detector (DWELL-QDIP)

We report the growth by Molecular Beam Epitaxy (MBE), fabrication and characterization of silicon doped 20 layer InAs dot in a well quantum dot infrared photo detector (DWELL-QDIP) device structures. Two structures with InAs dots of vertical heights of 50 Å and 40 Å were compared. A 2–8 μm band normal incidence photo response of the detector with polarization and bias dependence was obtained at 77 K. The specific peak detectivity D1 be 0.8 × 10⁹ Jones for one of the detectors.     

Sonochemical fabrication of edible fragrant antimicrobial nano coating on textiles and polypropylene cups

We report on a simple and effective ultrasound-assisted deposition of vanillin nanoparticles (∼50 nm in size), raspberry ketone (RK) nanoparticles (∼40 nm in size) and camphor nanoparticles (width ∼30 nm, length ∼40 nm in size) on textiles and on polypropylene surfaces. The excellent antibacterial and antifungal activity of the fragrant coatings on cotton bandages, and polypropylene surface against Escherichia coli (E. coli), Salmonella paratyphi A (S. paratyphi A) and the yeast Candida albicans (C. albicans) cultures was demonstrated. It is worth pointing out that these fragrant materials are edible, making them very useful for packaging. The mechanism of the edible fragrant coating formation and adhesion to the textile was discussed, and finally an up-scaling of the sonochemical process for textile coating was carried out.     

Structural and electrical properties of ZnO-doped 8 mol% yttria-stabilized zirconia

8 mol% Yttria-stabilized zirconia (8YSZ) powder was prepared by coprecipitation. ZnO (0.5, 1.0, 2.0, 5.0, 10.0 wt.%) was added to the YSZ powder through a mechanical mixing method. The densification , microstructure and electrical properties of the YSZ ceramics sintered at 1300 °C for 2 h, were investigated. It was found that the small addition of ZnO was effective in reducing the sintering temperature and promoting the densification rate of the ceramics. The 5.0 wt.% ZnO-doped YSZ has ∼ 96% relative density, as compared to ∼ 89% relative density for the undoped sample. The total conductivity of 8YSZ was evidently increased by doping small amount of ZnO. For the 0.5 wt.% doped sample, the total conductivity of 2.89 × 10^− 2 Ω^− 1 cm^− 1 and an increase of 120% in conductivity were observed at 800 °C, as compared to that of the undoped one. We also found that the grain boundary (GB) conductivity could be improved by small addition of ZnO. At intermediate temperature (∼ 300 °C), the maximum enhancement of GB conductivity was observed with 5.0 wt% ZnO dopant. Finally, the volume percentage of GB in the ceramics was estimated by the brick layer model. The possible mechanism related to the improved GB conduction of the YSZ due to the ZnO additions was discussed.     

Enhanced power efficiency of ZnO based organic/inorganic solar cells by surface modification

We present series of strategies to enhance efficiency of ZnO nanorods based organic/inorganic solar cells with spin-coated P3HT:PCBM blend as active layer. The performance of the as-fabricated devices is improved by controlling the size of ZnO nanorods, annealing temperature and time of active layer, surface modification of ZnO with PSBTBT. Optimized device of ITO/ZnO nanorod/P3HT:PCBM/Ag device with PSBTBT surface modification and air exposure reaches an efficiency of 2.02% with a short-circuit current density, open-circuit voltage and fill factor of 13.23 mA cm⁻², 0.547 V and 28%, respectively, under AM 1.5 irradiation of 100 mW m⁻², the increase in efficiency is 7-fold of the PSBTBT surface modified ITO/ZnO nanorods/P3HT:PCBM/Ag device compared with the unmodified one, which is own to the increased interface contact, expanded light absorption, tailored band alignment attributed to PSBTBT. We found exposure to air and surface modification is crucial to improve the device performance, and we discussed the mechanisms that affect the performance of the devices in detail.     

Characteristics of ZnO MSM UV photodetector with Ni contact electrodes on poly propylene carbonate (PPC) plastic substrate

In this study, we report the fabrication of ZnO metal-semiconductor-metal UV photodetector (MSM UV PD) by deposition ZnO thin film on poly propylene carbonate (PPC) plastic substrate using direct current (DC) sputtering technique, and Nickel (Ni) contact as electrodes. The structural, optical and electrical properties of the ZnO thin film were investigated by using atomic force microscopy (AFM), X-Ray diffraction (XRD) measurement, and photoluminescence (PL). The electrical characteristics of the detector were investigated using the current–voltage (I–V) measurements, the dark- and photo-currents were found to be 1.04 and 93.80 μA, respectively. Using forward dark conditions at 5 volt; the barrier height Φ_B was calculated to be 0.675 eV. Under incident wavelength of 385 nm, it was found that the maximum responsivity (R) of the Ni/ZnO/Ni MSM PD was found to be 1.59 A/W.     

Spin coating-pyrolysis derived highly c-axis-oriented ZnO layers pre-fired at various temperatures

Transparent ZnO layers were prepared on silica glass substrates by the spin coating-pyrolysis process. As-deposited films were pre-fired at 250 °C for 60 min, at 350 °C for 30 min, and at 500 °C for 10 min, followed by heat treatment at 900 °C for 30 min in air. The ZnO films were analyzed by high resolution X-ray diffraction, field emission-scanning electron microscopy, scanning probe microscopy, and ultraviolet–visible–near infrared spectrophotometry. (0 0 2)-oriented ZnO films were obtained by pre-firing at 350 °C and at 500 °C. All the ZnO films exhibited a high transmittance, above 80%, in the visible region, and showed a sharp fundamental absorption edge at 0.38–0.40 μm. The most highly c-axis-oriented ZnO with a homogeneous surface was observed at a pyrolysis temperature of 350 °C.     

Single image rectification of thermal images for geometric studies in façade inspections

This work presents a photogrammetric technique that provides geometric and thermal information about building façades. It uses low cost and portable scale bars, specially designed for thermal imaging, and processing software based on single image rectification. Image rectification corrects the original photo displacement due to the projection and perspective, and radial distortions introduced by the lens of the camera.The technique is tested by comparing laser scanning and thermal data. Seven segments of different orientation and length are selected for the measurement. Accuracy tests show errors between 44 mm and 151 mm. Precision values range between 22 mm and 61 mm for a maximum length of 7259 mm. The accuracy and precision results obtained for the technique open the possibility of extending its use to building inspection tasks.     

Photoluminescence of chemical solution-derived amorphous ZnO layers prepared by low-temperature process

Growth characteristic and optical properties of the amorphous ZnO thin films prepared on soda-lime–silica glass substrates by chemical solution process at 100 and 200 °C were investigated by using X-ray diffraction analysis, scanning probe microscope, ultraviolet spectrophotometer, and photoluminescence. The films exhibited an amorphous pattern even when finally heat treated at 100–200 °C for 60 min. The photoluminescence spectrum of amorphous ZnO films shows a strong near-band-edge emission, while the visible emission is nearly quenched.     

PtCo/Au nanocomposite: Synthesis,characterization, and magnetic properties

Magnetic PtCo/Au nanocomposites with narrow size distribution were synthesized in a reverse micelle, followed by a post-synthesis handling of the stabilizer-exchange technique. The PtCo/Au nanocomposites were characterized by ultraviolet visible spectroscopy, X-ray diffraction and transmission electron microscopy, respectively. Superconducting quantum interference device studies revealed that the nanocomposites were superparamagnetic above the blocking temperature (T_B=69 K), while the samples were ferromagnetic with Hc (628 Oe) and Ms (2.97 emu/g) at 5 K.     

Ultrasound-assisted synthesis of poly(MMA–co–BA)/ZnO nanocomposites with enhanced physical properties

The present study reports synthesis and characterization of poly(MMA–co–BA)/ZnO nanocomposites using ultrasound-assisted in-situ emulsion polymerization. Methyl methacrylate (MMA) was copolymerized with butyl acrylate (BA), for enhanced ductility of copolymer matrix, in presence of nanoscale ZnO particles. Ultrasound generated strong micro-turbulence in reaction mixture, which resulted in higher encapsulation and uniform dispersion of ZnO (in native form – without surface modification) in polymer matrix, as compared to mechanical stirring. The nanocomposites were characterized for physical properties and structural morphology using standard techniques such as XRD, FTIR, particle size analysis, UV–Visible spectroscopy, electrical conductivity, TGA, DSC, FE-SEM and TEM. Copolymerization of MMA and BA (in presence of ZnO) followed second order kinetics. Thermal stability (T_10% = 324.9 °C) and glass transition temperature (T_g = 67.8 °C) of poly(MMA-co-BA)/ZnO nanocomposites showed significant enhancement (35.1 °C for 1 wt% ZnO and 15.7 °C for 4 wt% ZnO, respectively), as compared to pristine poly(MMA–co–BA). poly(MMA–co–BA)/ZnO (5 wt%) nanocomposites possessed the highest electrical conductivity of 0.192 μS/cm and peak UV absorptivity of 0.55 at 372 nm. Solution rheological study of nanocomposites revealed enhancement in viscosity with increasing ZnO loading. Maximum viscosity of 0.01 Pa-s was obtained for 5 wt% ZnO loading.     

High room-temperature pyroelectric response of MgO-modified Pb0.99(Zr0.95Ti0.05)0.98Nb0.02O3 ceramics

The dielectric and pyroelectric responses of MgO-modified Pb_0.99(Zr_0.95Ti_0.05)_0.98Nb_0.02O₃ ceramics were investigated near F_R(LT)–F_R(HT) phase transition. It was found that MgO additive reduced the F_R(LT)–F_R(HT) phase transition temperature from 41 °C to room temperature (24 °C). Superior room-temperature pyroelectric properties were obtained in the composition of 0.10 wt% MgO addition without DC bias. The largest pyroelectric coefficient, 65 × 10⁻⁸ C cm⁻² K⁻¹, was detected. Accordingly, the detectivity figures of merit F_d had maximum values of 20 × 10⁻⁵ Pa^−1/2, and especially the voltage responsivity F_v = 0.91 m²C⁻¹ is the highest value reported so far among all pyroelectric materials. It shows promising potential for application in uncooled pyroelectric infrared detector.     

Influence of ultrasonication times on the tunable colour emission of ZnO nanophosphors for lighting applications

This paper reports on the sonochemical synthesis of zinc oxide (ZnO) nanophosphors (NPr) at different ultrasonication times (5 min, 30 min, 1 h, 5 h, 10 h and 15 h) for near white light emission applications. X-ray photoelectron spectroscopy indicated that the O1s peak consists of two components. These were O1 (ZnO) and O2 (deficient oxygen; OH groups) centred at 529.7 ± 0.3 eV and 531.1 ± 0.3 eV, respectively. All samples showed UV and defect level emission (DLE). The DLE enhancement was due to the increase in oxygen related defects such as oxygen vacancies/interstitials. Due to the combination of near UV and DLE near white light emission in ZnO NPr was obtained. The emission could be tuned with different ultrasonic times. It was found that the ultrasonication time influenced the growth mechanism and luminescence properties of the ZnO NPr.     

Fragmentation of elongated-shaped ZnO nanostructures into spherical particles by swift ion impact

This work reports on the fragmentation of rod-shaped ZnO nanostructures into spherical nanoparticles under 120 MeV Ag⁹⁺ swift ion irradiation. The visual evidence of the irradiation induced morphological change has been witnessed through electron microscopic studies. Typically, rods of 50 nm length and 21 nm diameter have transformed into particles of smaller dimension. Conversely, X-ray diffraction studies have revealed the lowering of crystallite size from 21.5 nm to 9 nm and an increase in microstrain by 11 times. Further, spectroscopic results, such as, significant blue shift (∼24 cm⁻¹) in vibrational features of Zn–O bonding, increase in native defect concentration in the nanostructures etc. also favor the irradiation led modification of nanostructures. It was anticipated that, dislodging and recrystallization of the constituent atoms of the elongated systems, as a consequence of suppression of the cohesive energy (owing to enormous energy deposition) caused by energetic ion irradiation, is chiefly responsible for the evolution of spherical nanoparticles.