Synthesis and electrocatalytic activities of Co<Subscript>3</Subscript>O<Subscript>4</Subscript> nanocubes

In this article, a hydrothermal method was developed to synthesize Co₃O₄ nanocubes using hydrogen peroxide (H₂O₂) as oxidant, Co(NO₃)₂·6H₂O as a cobalt source. The products are characterized in detail by multiform techniques including X-ray diffraction (XRD), energy dispersive X-ray analysis (EDS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that the obtained products are Co₃O₄ nanocubes with size ranging between 20 and 40 nm. The effects of the hydrogen peroxide concentration on the size of the products have been studied. The electrocatalytic activities of H₂O₂ reduction on Co₃O₄ nanocubes in phosphate buffer were also evaluated.     

Controlled-synthesis,characterization, and magnetic properties of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanostructures

Fe₃O₄ nanostructures with different morphologies, including uniform nanoparticles, nanorods and nanowire bundles, have been successfully synthesized via a facile hydrothermal route. Based on the observation of TEM images, the growth mechanism of one-dimensional Fe₃O₄ nanostructures is in accordance with Ostwald ripening process. From the hysteresis loops of as-prepared Fe₃O₄ products, we found that the morphology has great influence on the magnetic properties. The uniform Fe₃O₄ nanoparticles have higher saturation magnetization and lower coercivity than that of Fe₃O₄ nanorods and nanowires bundles. These phenomena attribute to the high shape anisotropy of nanorods and nanowire bundles, which prevent them from magnetizing in directions other than along their easy magnetic axes. PACS 81.07.-b; 75.50.Bb; 75.30.Gw; 81.10.Dn; 81.16.Be     

Structural and magnetic properties of layered Ca<Subscript>3</Subscript>Co<Subscript>4</Subscript>O<Subscript>9</Subscript> thin films

Layered cobalt oxides Ca₃Co₄O₉ thin films have been grown directly on c-cut sapphire substrates using pulsed laser deposition. X-ray diffraction and transmission electron microscopy characterizations show that the deposited films present the expected monoclinic structure and a texture along the direction perpendicular to the Al₂O₃(001) plane. The Ca₃Co₄O₉ structure presents six variants in the film plane. Rutherford backscattering spectroscopy shows that the films are stoichiometric and that the film thickness agrees with the nominal value. The susceptibility χ of the films, recorded along the c-axis of the substrate, after field cooling and zero field cooling in an applied field of 1 kOe shows two magnetic transitions at 19 and 370 K which agree well with previous findings on single crystal samples. In turn, at low temperature (5 K), the magnetization curve along the c-axis exhibits coercive field and remanent magnetization much smaller than those reported for bulk samples, which can be related to the influence of structural variants and structural defects.     

Formation of three-dimensional arrays of magnetic clusters NiO,Co<Subscript>3</Subscript>O<Subscript>4</Subscript>, and NiCo<Subscript>2</Subscript>O<Subscript>4</Subscript> by the matrix method

A method has been proposed for the formation of three-dimensional arrays of isolated magnetic clusters NiO, Co₃O₄, and NiCo₂O₄ in the sublattice of pores in the matrix of bulk synthetic opals through a single impregnation of the pores with melts of nickel and cobalt nitrate crystal hydrates and their thermal degradation. The method makes it possible to controllably vary the degree of filling of pores in the matrix with oxides within 10–70 vol %. The composition and structure of the synthesized materials, as well as the dependences of their static magnetic susceptibility on the magnetic field strength, have been investigated.     

Synthesis and magnetic properties of FeNi<Subscript>3</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> core-shell nanocomposites

In this study, FeNi₃/Al₂O₃ core-shell nanocomposites, where individual FeNi₃ nanoparticles were coated with a thin layer of alumina, were fabricated by a modified sol-gel method. Several physical characterizations were performed on the samples of FeNi₃/Al₂O₃ nanocomposites with different thickness of Al₂O₃ shell. The encapsulation of FeNi₃ nanoparticles with alumina stops FeNi₃ agglomeration during heat treatment, and prevents interaction among the closely spaced magnetic FeNi₃ nanoparticles. The Al₂O₃ insulating shell improves the soft magnetic properties of FeNi₃. The study of the complex permeability of the samples shows that the real part μ’ of the permeability of the sample with Al molar content of 20% (Al/(Fe+Ni)) is as high as 12, and independent of frequency up to at least 1 GHz. The tunneling magnetoresistance arising from the presence of the Al₂O₃ shell have also been studied.     

Magnetic properties of aerugite Co<Subscript>10</Subscript>Ge<Subscript>3</Subscript>O<Subscript>16</Subscript>

This paper reports on the first study of the temperature and field dependences of the magnetization, heat capacity, and electrical properties of synthesized polycrystalline samples of aerugite Co₁₀Ge₃O₁₆, as well as on x-ray diffraction analysis of this compound. It is shown that the cobalt ions in this compound occupy three nonequivalent positions. The results of the experimental and theoretical studies suggest that aerugite is a ferrimagnet with two uncompensated magnetic moments of the cobalt atom per formula unit.     

Dandelion-like mesoporous Co<Subscript>3</Subscript>O<Subscript>4</Subscript> as anode materials for lithium ion batteries

A dandelion-like mesoporous Co₃O₄ was fabricated and employed as anode materials of lithium ion batteries (LIBs). The architecture and electrochemical performance of dandelion-like mesoporous Co₃O₄ were investigated through structure characterization and galvanostatic charge/discharge test. The as-prepared dandelion-like mesoporous Co₃O₄ consisted of well-distributed nanoneedles (about 40 nm in width and about 5 μm in length) with rich micropores. Electrochemical experiments illustrated that the as-prepared dandelion-like mesoporous Co₃O₄ as anode materials of LIBs exhibited high reversible specific capacity of 1430.0 mA h g^?1 and 1013.4 mA h g^?1 at the current density of 0.2 A g^?1 for the first and 100th cycle, respectively. The outstanding lithium storage properties of the as-prepared dandelion-like mesoporous Co₃O₄ might be attributed to its dandelion-like mesoporous nanostructure together with an open space between adjacent nanoneedle networks promoting the intercalation/deintercalation of lithium ions and the charge transfer on the electrode. The enhanced capacity as well as its high-rate capability made the as-prepared dandelion-like mesoporous Co₃O₄ to be a good candidate as a high-performance anode material for LIBs.     

Synthesis and studies of trisubstituted biphthalonitrile/Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> magnetic hybrid microspheres

New trisubstituted biphthalonitrile/magnetite (TSB/Fe₃O₄) magnetic hybrid microspheres were synthesized from TSB and FeCl₃ · 6H₂O using the method of one-stage thermal temperature crystallization of solvents. The morphology and structure of magnetic hybrid microspheres were inspected using a scanning electron microscope, IR Fourier spectroscopy, and X-ray diffraction. It was found that the grown TSB/Fe₃O₄ magnetic hybrid microspheres represent spherical particles with an average size of ~137 nm and a small size spread. The size and size distribution of magnetic hybrid microspheres can be controlled by a small change in the ratio of TSB and Fe³⁺ ion contents in the microsphere. TSB/Fe₃O₄ hybrid microspheres exhibit a rather high saturation magnetization (58.16 emu g^–1) and new microwave electromagnetic properties, i.e., lower (in comparison with published) dielectric losses at low frequencies; magnetic losses are increased obviously due to an increase in the TSB content. Furthermore, it is detected that magnetic hybrid microspheres absorb microwaves, and strong reflection losses in a wide frequency range are established. The effective reflection loss of–31 dB is obtained in the microwave range from 2 to 16 GHz due to TSB content variations. Wide absorption properties of microwaves along with regular spherical shape and excellent magnetic properties offer wide opportunities for various applications of TSB/Fe₃O₄ magnetic hybrid microspheres as functional materials.     

Magnetic properties of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> surface

The magnetic properties of the magnetite Fe₃O₄(110) surface have been studied by spin resolved Auger electron spectroscopy (SRAES). Experimental spin resolved Auger spectra are presented. The results of calculation of Auger lines polarization carried out on the basis of electronic state density are presented. Problems related to magnetic moments of bivalent (Fe²⁺) and trivalent (Fe³⁺) ions on the Fe₃O₄(110) surface are discussed. It is established that the deposition of a thin bismuth film on the surface results in significant growth of polarization of iron Auger peaks, which is due to additional spin-orbit scattering of electrons by bismuth atoms.     

Elastic,magnetic, and magnetoelectric properties of the CaBaCo<Subscript>4</Subscript>O<Subscript>7</Subscript> multiferroic

The structural, elastic, magnetic, and magnetoelectric properties of the CaBaCo₄O₇ multiferroic are experimentally studied and compared with the properties of the related YBaCo₄O₇ cobaltite, where Y³⁺ ions substitute for Ca²⁺ ions. Unlike the frustrated YBaCo₄O₇ magnet, the softening of Young’s modulus and the hysteresis in the ΔE(T)/E ₀ curve of ferrimagnetic CaBaCo₄O₇ in the paramagnetic region are weak, and the anomaly during the magnetic transition increases by almost an order of magnitude. This difference can point to different characters of the development of a long-range magnetic order in these two cobaltites. The distortion of the crystal structure that removes the frustrations of exchange interactions is found to correlate with the magnetic behavior of the cobaltites under study. The magnetization curves of the Ca cobaltite have two steps below 15 K, which can point to the presence of a metastable state in a high magnetic field. The study of the longitudinal and transverse magnetoelectric effects in a pulsed magnetic field demonstrates that their magnitudes are maximal near T _C and change their character from linear to quadratic during passage through this temperature.     

Synthesis,characterization, and cell performance of Li<Subscript>0.5</Subscript>FeV<Subscript>1.5</Subscript>O<Subscript>4</Subscript>

A Li_0.5FeV_1.5O₄ sample was synthesized using sol-gel route. The X-ray diffraction study indicates formation of spinel phase (with Fd3m space group) for this sample. LiO₄, LiO₆, and V-O bonds were identified from the Raman spectrum, while LiO₄ and Fe-O bonds were identified from the FTIR spectrum of this sample phase. The FESEM study indicates formation of inhomogeneous grains. The surface area of 74.39 m²/g was estimated from the Brunauer-Emmett-Teller (BET) surface area analysis technique. The cyclic voltammetry study of Li_0.5FeV_1.5O₄ indicates an anodic peak at 2.1 V while a cathodic peak at 1.98 V. The charge-discharge study exhibits two voltage plateaus respectively at 2.1 and at 4 V. Stable electrochemical capacity of 40 mAh/g for Li_0.5FeV_1.5O₄ was found for 30 cycles. The electrochemical impedance spectroscopy study indicates smaller bulk resistance and higher ionic diffusion, i.e., less Warburg impedance for this phase. An energy density of 89 Wh/kg, a power density of 33 W/kg, and a 90% Coulombic efficiency was achieved with relatively good cyclic stability from Li_0.5FeV_1.5O₄.     

Conductivity of nanostructured India oxide films containing Co<Subscript>3</Subscript>O<Subscript>4</Subscript> or ZrO<Subscript>2</Subscript>

The effect of additives of cobalt and zirconium oxides on the conductivity of nanostructured composites based on indium oxide is studied. It is shown that addition of up to 20 wt % ZrO₂ to In₂O₃ leads to a sharp decrease in the conductivity of the composite. For the Co₃O₄?In₂O₃ system, the conductivity decreases up to a Co₃O₄ content of 60 wt %, after which it increases. At a Co₃O₄ content in the Co₃O₄?In₂O₃ system of up to 60 wt %, n-type conduction takes place, changing to p-type at 80 to 100 wt % Co₃O₄. Zirconium oxide exhibits practically no n-type conduction, so electric current in the ZrO₂?In₂O₃ system flows through In₂O₃ nanocrystals, i.e., n-type conduction takes place. Possible causes of the observed effects are considered.     

Enhanced electrochemical properties and thermal stability of LiNi<Subscript>1/3</Subscript>Co<Subscript>1/3</Subscript>Mn<Subscript>1/3</Subscript>O<Subscript>2</Subscript> by surface modification with Eu<Subscript>2</Subscript>O<Subscript>3</Subscript>

Layered LiNi_1/3Co_1/3Mn_1/3O₂ cathode material is synthesized via a sol-gel method and subsequently surface-modified with Eu₂O₃ layer by a wet chemical process. The effect of Eu₂O₃ coating on the electrochemical performances and thermal stability of LiNi_1/3Co_1/3Mn_1/3O₂@Eu₂O₃ cells is investigated systematically by the charge/discharge testing, cyclic voltammograms, AC impedance spectroscopy, and DSC measurements, respectively. In comparison, the Eu₂O₃-coated sample demonstrates better electrochemical performances and thermal stability than that of the pristine one. After 100 cycles at 1C, the Eu₂O₃-coated LiNi_1/3Co_1/3Mn_1/3O₂ cathode demonstrates stable cyclability with capacity retention of 92.9 %, which is higher than that (75.5 %) of the pristine one in voltage range 3.0–4.6 V. Analysis from the electrochemical measurements reveals that the remarkably improved performances of the surface-modified composites are mainly ascribed to the presence of Eu₂O₃-coating layer, which could efficiently suppress the undesirable side reaction and increasing impedance, and enhance the structural stability of active material.     

Electric and magnetic properties of CoFe<Subscript>2</Subscript>O<Subscript>4</Subscript>/Pb(Zr<Subscript>0.52</Subscript>Ti<Subscript>0.48</Subscript>)O<Subscript>3</Subscript> bilayer thin films prepared by pulsed-laser deposition

CoFe₂O₄ (CFO) thin film with highly (111)-preferential orientation was first deposited on the silicon substrate by a pulsed-laser deposition, and then Pb(Zr_0.52Ti_0.48)O₃ (PZT) layers were deposited with different oxygen pressures to form the bilayer CFO/PZT nanocomposite thin films. X-ray diffraction showed that the PZT preferential orientation was strongly dependant on the oxygen pressure. The smooth film surface was obtained after depositing the CFO and PZT layers. The bilayer thin films exhibit good ferromagnetic and ferroelectric properties, and a low leakage current density of 0.004 μA/cm² at 50 kV/cm. The leakage current density curves show loops for the electric polarized field when the electric field reverses. PACS 77.84.Lf; 75.80+q; 81.05.Zx; 81.15.Fg     

Plasmachemical synthesis and basic properties of CoFe<Subscript>2</Subscript>O<Subscript>4</Subscript> magnetic nanoparticles

Cobalt-ferrite (CoFe₂O₄) nanoparticles (CFNPs) are obtained using direct plasmachemical synthesis in the plasma of a low-pressure arc discharge. The formation of the CFNPs with an average size of 9 nm and a narrow granulometric composition is established employing the methods of X-ray structure analysis and transmission microscopy. The CFNP behavior upon high-temperature annealing is analyzed. The CFNP functional groups are determined using the infrared Fourier spectrum. The results of the X-ray energy dispersion confirm the correspondence of the ratio of the number of atoms of each material to the nominal stoichiometry. The basic magnetic properties of the obtained and annealed samples are investigated at room temperature using the vibrating spectrum magnetometry (VSM).     

Synthesis and characterization of hollow nanoparticles of crystalline Gd<Subscript>2</Subscript>O<Subscript>3</Subscript>

Although Gd₂O₃ (gadolinia) nanoparticle is the subject of intense research interest due to its magnetic property as well as controllable emission wavelengths by doping of various lanthanide ions, it is known to be difficult to prepare monodisperse crystalline gadolinia nanoparticles because it requires high temperature thermal annealing process to enhance the crystallinity. In this article, we demonstrate the synthesis of hollow nanoparticles of crystalline Gd₂O₃ by employing poly(N-vinylpyrrolidone) (PVP) to stabilize the surface of Gd(OH)CO₃·H₂O nanoparticles and to successively form SiO₂ shell as a protecting layer to prevent aggregation during calcinations processes. Silica shells could be selectively removed after calcinations by a treatment with basic solution to give hollow nanoparticles of crystalline Gd₂O₃. The formation mechanism of hollow nanoparticles could be suggested based on several characterization results of the size and shape, and crystallinity of Gd₂O₃ nanoparticles by TEM, SEM, and XRD.     

Enhancement of electrochemical properties of Ca<Subscript>3</Subscript>Co<Subscript>4</Subscript>O<Subscript>9</Subscript> as anode materials for lithium-ion batteries by transition metal doping

Misfit-layered calcium cobaltites (Ca₃Co₄O₉, Ca₃Co_3.9Fe_0.1O₉, and Ca₃Co_3.9Mn_0.1O₉), as anode materials for lithium-ion batteries, were synthesized by a simple hydro-decomposition method. All synthesized samples do not show any impurity phase. They exhibited plate-like particle with the particle size of 1–2 μm. The specific capacities of doped samples showed higher electrochemical performance compared to the undoped sample. After charge/discharge of 50 cycles, the specific capacities of Ca₃Co₄O₉, Ca₃Co_3.9Fe_0.1O₉, and Ca₃Co_3.9Mn_0.1O₉ were 343, 562, and 581 mAh g^?1, respectively. The doped samples showed an increase of over 60% compared to the undoped sample. The cyclic voltammetry profile of the doped samples showed the enhanced reactivity corresponding to their improved electrochemical performance. The capacity improvement of doped samples resulted from the metal oxide/Li conversion reactions, volume change, and high reactivity.     

Synthesis and structural,magnetic, and resonance properties of the LiCuFe<Subscript>2</Subscript>(VO<Subscript>4</Subscript>)<Subscript>3</Subscript> compound

Complex studies have been performed for the structural, static magnetic, and resonance properties of a new magnet LiCuFe₂(VO₄)₃ prepared by solid-phase synthesis. The temperature dependence of the susceptibility has an anomaly at temperature T_max = 9.6 K. At high temperatures, the LiCuFe₂(VO₄)₃ sample is in the paramagnetic state described by the Curie–Weiss law at T > 50 K and mainly determined by iron ions with effective magnetic moment μ_eff(exp) = 8.6μ_B per formula unit. At low temperatures, a long-range magnetic order is observed in the magnetic subsystem of the sample; the order is predominantly characterized by the antiferromagnetic exchange interaction and high frustration level. The exchange interaction parameters are estimated in a six-sublattice representation of the LiCuFe₂(VO₄)₃ magnet. It is shown that the LiCuFe₂(VO₄)₃ compound is an antiferromagnet with strong intrachain and frustrating interchain exchange interactions.     

Synthesis of ZnAl<Subscript>2</Subscript>O<Subscript>4</Subscript>/α-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> complex substrates and growth of GaN films

With the solid phase reaction between pulsed-laser-deposited (PLD) ZnO film and α-Al₂O₃ substrate, ZnAl₂O₄/α-Al₂O₃ complex substrates were synthesized. X-ray diffraction (XRD) spectra show that as the reaction proceeds, ZnAl₂O₄ changes from the initial (111)-oriented single crystal to poly-crystal, and then to inadequate (111) orientation. Corresponding scanning electron microscope (SEM) images indicate that the surface morphology of ZnAl₂O₄ transforms from uniform islands to stick structures, and then to bulgy-line structures. In addition, XRD spectra present that ZnAl₂O₄ prepared at low temperature is unstable at the environment of higher temperature. On the as-obtained ZnAl₂O₄/α-Al₂O₃ substrates, GaN films were grown without any nitride buffer using light-radiation heating low-pressure MOCVD (LRH-LP-MOCVD). XRD spectra indicate that GaN film on this kind of complex substrate changes fromc-axis single crystal to poly-crystal as ZnAl₂O₄ layer is thickened. For the single crystal GaN, its full width at half maximum (FWHM) of X-ray rocking curve is 0.4°. Results indicate that islands on thin ZnAl₂O₄ layer can promote nucleation at initial stage of GaN growth, which leads to the (0001)-oriented GaN film.     

Structural and magnetic properties of size-controlled Mn<Subscript>0.5</Subscript>Zn<Subscript>0.5</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript> nanoparticles and magnetic fluids

Mn_0.5Zn_0.5Fe₂O₄ ferrite nanoparticles with tunable Curie temperature and saturation magnetization are synthesized using hydrothermal co-precipitation method. Particle size is controlled in the range of 54 to 135 Å by pH and incubation time of the reaction. All the particles exhibit super-paramagnetic behaviour at room temperature. Langevin’s theory incorporating the interparticle interaction was used to fit the virgin curve of particle magnetization. The low-temperature magnetization follows Bloch spin wave theory. Curie temperature derived from magnetic thermogravimetric analysis shows that Curie temperature increases with increasing particle size. Using these particles magnetic fluid is synthesized and magnetic characterization is reported. The monolayer coating of surfactant on particle surface is confirmed using thermogravimetric measurement. The same technique can be extended to study the magnetic phase transition. The Curie temperature derived using this measurement complies with the low-temperature magnetic measurement. The room-temperature and high-temperature magnetization measurements are also studied for magnetic fluid systems. The magnetic parameters derived for fluid are in good agreement with those obtained for the particle system.