Self-assembled CaMoO4 and CaMoO4:Eu hierarchical superstructures: Facile sonochemical route synthesis and tunable luminescent properties

Tetragonal CaMoO₄ and CaMoO₄:Eu³⁺ with various novel three-dimensional (3D) hierarchical architectures were successfully synthesized via a facile, efficient sonochemistry process in the absence of any surfactant or template. XRD, EDS, FE-SEM, and photoluminescence (PL) were employed to characterize the as-obtained products. It was found that morphology modulation could be easily realized by changing pH value of the precursor. The pH value of the precursor not only affected the substructures of the hierarchical structures, but also determined the size distributions of the final products. The formation mechanism for different hierarchical architectures was proposed on the basis of time-dependent experiments. The luminescence spectra showed that CaMoO₄:Eu³⁺ phosphors can be effectively excited by the near ultraviolet (UV) (396 nm) and blue (466 nm) light, and exhibited strong red emission around 615 nm, which was attributed to the Eu³⁺⁵D₀→⁷F₂ transition. Compared with Y₂O₃:Eu³⁺ phosphor, CaMoO₄:Eu³⁺ is much more stable, efficient and suitable, therefore, this phosphors could be a promising red component for possible applications in the field of LEDs.     

Advanced electrochemical performance of LiMn1.4Cr0.2Ni0.4O4 as 5 V cathode material by citric-acid-assisted method

Spinel LiMn₂O₄ and LiMn_1.4Cr_0.2Ni_0.4O₄ cathode materials were successfully synthesized by the citric-acid-assisted sol-gel method with ultrasonic irradiation stirring. The structure and electrochemical performance of the as-prepared powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectrometer, cyclic voltamogram (CV) and the galvanostatic charge-discharge test in detail. XRD shows that all the samples have high phase purity, and the powders are well crystallized. SEM exhibits that LiMn_1.4Cr_0.2Ni_0.4O₄ has more uniform cubic-structure morphology than that of LiMn₂O₄. EDX reveals that a small amount of Mn³⁺ still exists in LiMn_1.4Cr_0.2Ni_0.4O₄. The galvanostatic charge-discharge test indicates that the initial discharge capacities for the LiMn_1.4Cr_0.2Ni_0.4O₄ and LiMn₂O₄ at 0.15 C discharge rates are 130.8 and 130.2 mAh g⁻¹, respectively. After 50 cycles, their capacity are 94.1% and 85.1%, respectively. The CV curve implies that Ni and Cr dual substitutions are beneficial to the reversible intercalation and deintercalation of Li⁺, and suppress Mn³⁺ generation at high temperatures and provide improved structural stability.     

Preparation, characterization and electrochemical property of Sn-Fe-Mo-Al2O3 multi-phase composites

A novel technique has been developed to synthesize Sn-Fe-Mo-Al₂O₃, while nanoscale dispersion of a highly active tin phase was finely distributed in a stable inert multi-phase. The precursor was prepared by co-precipitation method with SnCl₄, FeCl₃, AlCl₃ and (NH₄)₆Mo₇O₂₄ as the raw materials. Sn-Fe-Mo-Al₂O₃ mixture was produced by reducing the precursor with H₂. The product was characterized by X-ray diffraction (XRD), ICP and scanning electron microscopy (SEM). The performance of the electrode was investigated. The Sn-Fe-Mo-Al₂O₃ electrode was found to have an initial charge capacity of over 461 mAh/g, and a reversible volumetric capacity of 2090 mAh/cm³, which is two times larger than that of graphite electrode (800 mAh/cm³). The coulomb efficiency in the first cycle was over 55%, but its cyclability was not improved significantly. In order to enhance the cycle performance, we investigated the anode after heat treated at 270 °C for 12 h. Under the same condition, the first charge-discharge characteristics were almost equivalent to the as-coated anode, and the retention capacity ratio after 20 cycles was improved from 41.1% to 86.5%. The heat-treated Sn-Fe-Mo-Al₂O₃ electrode exhibited better cycle life. The electrochemical reaction of the Sn-Fe-Mo-Al₂O₃ electrode with Li may obey the alloying-dealloying mechanism of Li_xSn(x?4.4) formation in the other tin-based electrodes.     

Porous LiNi0.75Co0.25O2 microspheres prepared via a hydrothermal process as cathode material for lithium ion batteries

Porous LiNi_0.75Co_0.25O₂ microspheres are successfully prepared by a simple hydrothermal process by using H[Ni_0.75Co_0.25OOH]₃ and LiOH as starting materials in the presence of urea for the first time. The synthesized samples are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), specific surface area (S_BET), and electrochemical performance. The synthesized LiNi_0.75Co_0.25O₂ has a good electrochemical performance with an initial discharge capacity of 169.3 mA g⁻¹ and good capacity retention of 96.7% after 50 cycles at 0.2 C (25 mA g⁻¹). The electrochemical lithium ion insertion/extraction process is quite reversible even at 5 C. Furthermore, the structure in the charge-discharge process is stable and the impedance increased slowly during cycling.     

Syntheses and properties of the Fe-Co/Fe3O4 ferrites

The Fe alloy-ferrite composites Fe-Co/Fe₃O₄ are synthesized by using disproportion of Fe (II) and reduction of Co (II) by Fe⁰ in a concentrated and boiling KOH solution. The Fe alloy and ferrites are prepared in aqueous solution without any templet and surfactants at low temperature. Their structures and magnetic properties are investigated by X-ray diffractometer (XRD) and vibrating sample magnetometer (VSM). From the results of XRD, it is shown that the samples have b.c.c and f.c.c structure of Fe, and the spinel structures of the ferrite before calcinations; the samples have b.c.c and spinel structures after calcinations at 300 °C; and the samples have only f.c.c structure and the spinel structures calcined at 500 °C.     

Synthesis and electrochemical performances of Li4Ti4.95Al0.05O12/C as anode material for lithium-ion batteries

Spinel compounds Li₄Ti_5−xAl_xO₁₂/C (x=0, 0.05) were synthesized via solid state reaction in an Ar atmosphere, and the electrochemical properties were investigated by means of electronic conductivity, cyclic voltammetry, and charge-discharge tests at different discharge voltage ranges (0-2.5 V and 1-2.5 V). The results indicated that Al³⁺ doping of the compound did not affect the spinel structure but considerably improved the initial capacity and cycling performance, implying the spinel structure of Li₄Ti₅O₁₂ was more stable when Ti⁴⁺ was substituted by Al³⁺, and Al³⁺ doping was beneficial to the reversible intercalation and deintercalation of Li⁺. Al³⁺ doping improved the reversible capacity and cycling performance effectively especially when it was discharged to 0 V.     

Particle size distribution and electrochemical properties of LiFePO4 prepared by a freeze-drying method

The electrochemical performance of carbon-coated nanocrystalline LiFePO₄ prepared by a freeze-drying method is examined. This method is based on the thermal decomposition of homogeneous phosphate-formate precursors. Structural and morphological characterization of LiFePO₄ is carried out by powder XRD, BET measurements, SEM and XPS analyses. The electrochemical behaviour is tested in model lithium cells using galvanostatic mode. By changing the solution concentration, the freeze-drying method allows preparing LiFePO₄ with mean particle sizes between 60 and 100 nm and different particle size distributions. The content of carbon appearing mainly on the particle surface depends on both the solution concentration and the annealing temperature. The effect of particle size distribution on the voltage profile of LiFePO₄ is also demonstrated. The specific capacity is mainly determined by the amount of carbon deposited on the particle surfaces.     

Recent development and application of Li4Ti5O12 as anode material of lithium ion battery

Lithium-ion batteries with both high power and high energy density are one of the promising power sources for electric devices, especially for electric vehicles (EV) and other portable electric devices. One of the challenges is to improve the safety and electrochemical performance of lithium ion batteries anode materials. Li₄Ti₅O₁₂ has been accepted as a novel anode material of power lithium ion battery instead of carbon because it can release lithium ions repeatedly for recharging and quickly for high current. However, Li₄Ti₅O₁₂ has an insulating character due to the electronic structure characterized by empty Ti 3d-states, and this might result in the insufficient applications of LTO at high current discharge rate before any materials modifications. This review focuses first on the present status of Li₄Ti₅O₁₂ including the synthesized method, doping, surface modification, application and theoretical calculation, then on its near future development.     

Synthesis and crystallographic studies of garnet-type AgCa2Mn2V3O12 and NaPb2Mn2V3O12

High-purity powder specimens of AgCa₂Mn₂V₃O₁₂ and NaPb₂Mn₂V₃O₁₂ have been successfully synthesized by solid-state chemical reaction. The Rietveld refinements from X-ray powder diffraction data verified that these compounds have the garnet-type structure (space group , No. 230) with the lattice constant of a=12.596(2) Å for AgCa₂Mn₂V₃O₁₂ and a=12.876(2) Å for NaPb₂Mn₂V₃O₁₂. Calculation of the bond valence sum supported that Mn is divalent and V is pentavalent in these garnets. Estimation of the quadratic elongation and the bond angle variance showed that the distortions of the MnO₆ octahedra and the VO₄ tetrahedra are significantly suppressed. Our new results of AgCa₂Mn₂V₃O₁₂ and NaPb₂Mn₂V₃O₁₂ are compared to those of AgCa₂M₂V₃O₁₂ and NaPb₂M₂V₃O₁₂ (M=Mg, Co, Ni, Zn).     

Magnetic susceptibility of vanadium garnets NaPb2Co2V3O12 and NaPb2Ni2V3O12

Vanadium garnets NaPb₂Co₂V₃O₁₂ and NaPb₂Ni₂V₃O₁₂ have been successfully synthesized. The X-ray diffraction experiments indicate that these compounds have the garnet structure of cubic symmetry of space group with the lattice constant of 12.742 Å (NaPb₂Co₂V₃O₁₂) and 12.666 Å (NaPb₂Ni₂V₃O₁₂), respectively. The magnetic susceptibility of NaPb₂Ni₂V₃O₁₂ shows the Curie-Weiss paramagnetic behavior between 4.2 and 350 K. The effective magnetic moment μ_eff of NaPb₂Ni₂V₃O₁₂ is 3.14 μ_B due to Ni²⁺ ion at A-site and the Weiss constant is −3.67 K (antiferromagnetic sign). For NaPb₂Co₂V₃O₁₂, the simple Curie-Weiss law cannot be applicable. The ground state is the spin doublet and the first excited state is spin quartet , according to Tanabe-Sugano energy diagram on the basis of octahedral crystalline symmetry. This excited spin quartet state just a bit higher than ground state influences strongly the complex temperature dependence of magnetic susceptibility for NaPb₂Co₂V₃O₁₂.     

Solution-combusting preparation of mono-dispersed Mn3O4 nanoparticles for electrochemical applications

Manganese oxide (Mn₃O₄) nanoparticles with average diameter of 15 nm were prepared using alcohol solution of manganese chloride as starting material via a facile solution-combusting method. The flame core zone was chosen to prepare mono-dispersed and high crystalline products, which were employed to modify glassy carbon electrode and detect dopamine via cyclic voltammetry. The results exhibited excellent electrochemical sensitivity. A linear relationship between the concentration of dopamine and its oxidation peak current was obtained by differential pulse voltammetry, which will find wide application in the biological detection.     

Size-controlled hydrothermal synthesis and electrochemical behavior of orthorhombic LiMnO2 nanorods

Large amount of uniform orthorhombic LiMnO₂ (o-LiMnO₂) nanorods was fabricated by a hydrothermal route in 180 °C using γ-MnOOH nanorods as precursors through an isomorphous ion exchange process. The size of as-obtained o-LiMnO₂ nanorods was determined by that of γ-MnOOH precursors, which could be deliberately controlled. The electrochemical performance of o-LiMnO₂ nanorods was characterized via galvanostatic tests, which suggested that the size of as-obtained products played an important role in their electrochemical performances.     

Synthesis,photophysical properties,and photocatalytic applications of Bi doped NaTaO3 and Bi doped Na2Ta2O6 nanoparticles

Phase formation and photophysical properties of bismuth doped sodium tantalum oxide (perovskite, defect pyrochlore) nanoparticles prepared by a hydrothermal method were studied in detail. It was revealed that the synthesis conditions like NaOH concentration and bismuth precursor (NaBiO₃·2H₂O) markedly affect the crystal structure of sodium tantalum oxide. At low NaOH concentration and high bismuth precursor (NaBiO₃·2H₂O) content, Bi doped Na₂Ta₂O₆ (defect pyrochlore) phase was predominantly formed, while at higher NaOH concentration, Bi doped NaTaO₃ (perovskite) phase was formed. It was observed that the defect pyrochlore (Bi doped Na₂Ta₂O₆) phase was formed and stabilized by the presence of dopant precursor (NaBiO₃·2H₂O). The chemical analysis of the samples confirmed the doping of Bi³⁺ cations in both phases. Doping of bismuth enabled visible light absorption up to 500 nm in perovskite and defect pyrochlore type sodium tantalum oxide. Bi doped NaTaO₃ samples showed better performance for the photocatalytic degradation of rhodamine B than that of Bi doped Na₂Ta₂O₆, under visible light irritation (λ>420 nm). The present results shed light on phase formation of sodium tantalate and these results are useful in understanding properties of NaTaO₃ based compounds, synthesized by the hydrothermal method.     

Characteristics of spherical-shaped Li4Ti5O12 anode powders prepared by spray pyrolysis

Spherical-shaped Li₄Ti₅O₁₂ anode powders with a mean size of 1.5 μm were prepared by spray pyrolysis. The precursor powders obtained by spray pyrolysis had no peaks of crystal structure of Li₄Ti₅O₁₂. The powders post-treated at temperatures of 800 and 900 °C had the single phase of spinel Li₄Ti₅O₁₂. The powders post-treated at a temperature of 1000 °C had main peaks of the Li₄Ti₅O₁₂ phase and small impurity peaks of Li₂Ti₃O₇. The spherical shape of the precursor powders was maintained after post-treatment at temperatures below 800 °C. The Brunauer-Emmett-Teller (BET) surface areas of the Li₄Ti₅O₁₂ anode powders post-treated at temperatures of 700, 800 and 900 °C were 4.9, 1.6 and 1.5 m²/g, respectively. The initial discharge capacities of Li₄Ti₅O₁₂ powders were changed from 108 to 175 mAh/g when the post-treatment temperatures were changed from 700 to 1000 °C. The maximum initial discharge capacity of the Li₄Ti₅O₁₂ powders was obtained at a post-treatment temperature of 800 °C, which had good cycle properties below current densities of 0.7 C.     

Stable cycle-life properties of Ti-doped LiFePO4 compounds synthesized by co-precipitation and normal temperature reduction method

Submicron-sized LiFePO₄ and Ti-doped LiFePO₄ cathode materials were synthesized by a reformative co-precipitation and normal temperature reduction method, for which Ti ions were added in the process of preparing precursors to pursue a kind of sufficient and homogenous doping way. ICP and XRD analyses indicate that Ti ions were sufficiently doped in LiFePO₄ and did not alter its crystal structure. It is noted that higher Ti ions doping levels are conducive to electrochemical performance of LiFePO₄, especially on the aspect of stable cycle-life at higher C rates. The sample doped with 3 at% Ti shows the most impressive cycling performance, even after 100 cycles, discharge capacity of 133 mAh g⁻¹ was obtained (102.3% of its initial value) at 1C rate, and the discharge decreased little from 124 to 120 mAh g⁻¹ (96.8% of its initial value) at 2C rate.     

Synthesis and electrochemical properties of Li4Ti5O12/C composite by the PVB rheological phase method

Spinel Li₄Ti₅O₁₂/C powders were synthesized successfully by a simple rheological phase method using polyvinylbutyral (PVB) as both template and carbon source. The structure and morphology characteristics of the composite were investigated by X-ray diffraction (XRD), field emission scanning electron microscopy and transmission electron microscopy. The XRD results showed that the composite had a good crystallinity. Its average particle size was about 2.1 μm with a narrow size distribution as a result of homogeneous mixing of the precursors. The in situ carbon coating produced by decomposition of PVB played an important role in improving electrical conductivity, thereby enhancing the rate capacity of Li₄Ti₅O₁₂ as anode material in Li-ion batteries. The Li₄Ti₅O₁₂/C composite, synthesized at 800 °C for 15 h under argon, containing 0.98 wt% of carbon, exhibited better electrochemical properties in comparison with the pristine Li₄Ti₅O₁₂, which could be attributed to the enhanced electrical conductive network of the carbon coating on the particle surface.     

The effect of doping LiMn2O4 spinel on its use as a cathode in Li-ion batteries: neutron diffraction and electrochemical studies

A series of compounds Li_1+yMn_2−xM′_xO₄ (x≤0.1;y≤0.02), have been synthesised by doping the parent LiMn₂O₄ spinel with various metal ions of variable oxidation state. Powder neutron diffraction data has been collected on these samples alongside a series of electrochemical experiments in order to elucidate the relationship between structure on the performance of these systems as Li batteries. Doping the LiMn₂O₄ spinel with a small amount of metal ions has a remarkable effect on the electrochemical properties. Whereas the capacity of the spinels doped with trivalent ions is much greater, the cycling fading properties are much enhanced with using divalent ions as dopants. The underlying reasons for this are discussed, and it is suggested that the occupancy of the tetrahedral site with divalent ions to form a more compact structure offers an improved structural stability to support greater Li insertion/extraction, but which ultimately prevents the free movement of Li also sited on the tetrahedral site of the lattice.     

Electrochemical behaviour of nano-sized spinel LiMn2O4 and LiAlxMn2−xO4 (x=Al: 0.00-0.40) synthesized via fumaric acid-assisted sol-gel synthesis for use in lithium rechargeable batteries

Pristine spinel LiMn₂O₄ and LiAl_xMn_2−xO₄ (x=Al: 0.00-0.40) with sub-micron sized particles have been synthesized using fumaric acid as chelating agent by sol-gel method. The synthesized samples were subjected to thermogravimetric analysis (TGA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and cyclic voltammetry (CV) and galvanostatic cycling studies. The TGA curve of the gel shows several weight-loss regions stepwise amounting to 55% till 800 °C attributed to the decomposition of the precursors. Calcination to higher temperatures (800 °C) yields pure-phase spinel (LiAl_xMn_2−xO₄), as it is evident from the high-intensity XRD reflections matching to the standard pattern. SEM and TEM studies confirm that the synthesized grains are of uniform regular surface morphology. FT-IR studies show stretching and bending vibration bands of Li-O, Li-Al-Mn-O. LiAl_0.1Mn_1.90O₄ spinel was found to deliver discharge capacity of 139 mA h/g during the first cycle with columbic efficiency of 97%. LiAl_0.1Mn_1.90O₄ spinel exhibits the high cathodic peak current indicating better electrochemical performance. Low doping (x=0.1) of Al is found to be beneficial in stabilizing the spinel structure.