Permeation of electrolyte water-methanol solutions through a Nafion membrane

The volume flux through a cation-exchange membrane (Nafion 117) separating two equal electrolyte water-methanol solutions as a function of the pressure difference was determined under different experimental conditions. The results show that permeation rates through the membrane are strongly dependent on the methanol content of the solutions, thus the value of the flux increases when the methanol percentage increases. The effect of the electrolyte concentration of the solution on the membrane permeability is less important, although its influence becomes significant at low electrolyte concentration and high methanol content on solvent. This behavior is explained in terms of the amount of solvent sorbed by the membrane. Typical flux behaviors observed with pressure difference are linear at low pressures, exhibiting a positive deviation at higher pressure difference values.     

A Pd-impregnated nanocomposite Nafion membrane for use in high-concentration methanol fuel in DMFC

Pd nanophases in a Nafion polymer membrane electrolyte were used to enhance DMFC performance by preventing or reducing methanol crossover through the electrolyte. Interestingly, the Pd-impregnated nanocomposite membrane showed a lower permeability for methanol and maintained a proton conductivity comparable to that of a pure Nafion membrane. Because of the modification of the membrane by the Pd nanophases, a high molar concentration of methanol could be applied for use in practical DMFC without any power loss.     

含杂萘联苯结构聚合物膜的直接甲醇燃料电池性能

质子交换膜是直接甲醇燃料电池(DMFC)的关键组成部分. 通过磺化制备了磺化杂萘联苯聚醚酮(SPPEK)、磺化杂萘联苯聚醚砜(SPPES)和磺化杂萘联苯聚醚砜酮(SPPESK)三种含杂萘联苯结构的新质子交换膜, 测试了其热稳定性、质子导电性和甲醇透过性能. SPPESK的热分解温度比相近离子交换容量(IEC)的SPPEK和SPPES约低100 ℃, 三种膜均具有良好的导电和阻醇性能; 分别以三种膜为电解质组装DMFC考察了其性能, DMFC的开路电压随膜的阻醇性的提高而增大, 三种膜的开路电压均高于Nafion115膜, 但在较高电流密度的区域三种新膜的性能均比Nafion115膜差.     

聚偏氟乙烯-Nafion共混膜的制备及阻醇质子导电性能研究

直接甲醇燃料电池 (Ｄｉｒｅｃｔｍｅｔｈａｎｏｌｆｕｅｌｃｅｌｌ,ＭＤＦＣ)以高效、清洁和燃料储运方便等优点成为一类极具发展潜力的新型动力源 .但目前ＤＭＦＣ中普通使用的全氟磺酸膜 (如ＮａｆｉｏｎＴＭ 系列膜 )阻醇性能太差 ,导致大量甲醇从阳极穿过膜直接透到阴极 ,造成燃料的浪费和电池整体性能的下降 .据文献报道 ,即使甲醇浓度低到 1ｍｏｌ Ｌ ,也有近40 %的醇透过膜 .缺乏高性能的阻醇质子导电聚合物电解质膜是制约ＤＭＦＣ发展的瓶颈之一 .已有一些研究人员致力于新型膜材料的开发 ,如有人研制了聚苯并咪唑膜[1] 及各种掺杂…     

Streaming potential across cation-exchange membranes in methanol-water electrolyte solutions

Streaming potential measurements across charged membranes separating two equal solutions have been carried out. Two cation-exchange membranes with different cross-linked and swelling properties (Ionics and Nafion membranes) and methanol-water electrolyte solutions of KCl have been used in the experiments. The obtained results show that the streaming potential is higher for the Ionics membrane and that the values depend on the methanol content of the solutions. A different behavior is found in the dependence of the streaming potential on the methanol percentage for each membrane. The study of the relaxation times in the decay of electrokinetic steady states of streaming potential has been carried out from the time dependence of the streaming potential when the pressure difference through the membrane is suppressed. The results show the existence of two different parts or partial relaxations, mechanical and electric. A different behavior of the mechanical relaxation time with the methanol percentage has been found for the two membranes, but any significant difference between their electric relaxation times. These differences have been explained in terms of the different degree of swelling of the membranes used.     

Diffusion and sorption of methanol and water in Nafion using time-resolved Fourier transform infrared-attenuated total reflectance spectroscopy

Direct methanol fuel cells (DMFCs) are promising portable power sources. However, their performance diminishes significantly because of high methanol crossover (flux) in the polymer electrolyte membrane (e.g., Nafion 117) at the desired stoichiometric methanol feed concentration. In this study, the diffusion and sorption of methanol and water in Nafion 117 were measured using time-resolved Fourier transform infrared-attenuated total reflectance (FTIR-ATR) spectroscopy. This technique is unique because of its ability to measure multicomponent diffusion and sorption within a polymer on a molecular level in real time as function of concentration. Both the effective mutual diffusion coefficients and concentrations of methanol and water in Nafion 117 were determined with time-resolved FTIR-ATR spectroscopy as a function of methanol solution concentration. The methanol flux, calculated from FTIR-ATR, matched that determined from a conventional technique (permeation cell) and increased by almost 3 orders of magnitude over the methanol solution concentration range studied (0.1-16 M). Furthermore, the data obtained in this study reveal that the main contribution to the increase in methanol flux is due to methanol sorption in the membrane.     

Sorption and diffusion of methanol and water in PVDF‐g‐PSSA and Nafion® 117 polymer electrolyte membranes

Sorption and diffusion properties of poly(vinylidene fluoride)‐graft‐poly(styrene sulfonic acid) (PVDF‐g‐PSSA) and Nafion® 117 polymer electrolyte membranes were studied in water/methanol mixtures. The two types of membranes were found to have different sorption properties. The Nafion 117 membrane was found to have a maximum in‐solvent uptake around 0.4 to 0.6 mole fraction of methanol, while the PVDF‐g‐PSSA membranes took up less solvent with increasing methanol concentration. The proton NMR spectra were recorded for membranes immersed in deuterated water/methanol mixtures. The spectra showed that the hydroxyl protons inside the membrane exhibit resonance lines different from the resonance lines of hydroxyl protons in the external solvent. The spectral features of the lines of these internal hydroxyl groups in the membranes were different in the Nafion membrane compared with the PVDF‐g‐PSSA membranes. Diffusion measurements with the pulsed field gradient NMR (PFG‐NMR) method showed that the diffusion coefficient of the internal hydroxyl groups in the solvent immersed Nafion membrane mirrors the changes in the diffusion coefficients of hydroxyl and methyl protons in the external solvent. For the PVDF‐g‐PSSA membranes, a decrease in the diffusion coefficient of the internal hydroxyl protons was seen with increasing methanol concentration. These results indicate that the morphology and chemical structure of the membranes have an effect on their solvent sorption and diffusion characteristics. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 3277–3284, 2000     

燃料电池聚合物电解质膜的研究进展

本文根据聚合物电解质膜燃料电池操作温度、使用的电解质和燃料的不同,将其分为高温质子交换膜燃料电池、低温质子换膜燃料电池、直接甲醇燃料电池和阴离子交换膜燃料电池,综述了它们所用电解质膜的最新进展.第一部分简要介绍了这4种燃料电池的优点和不足.第二部分首先介绍了Nafion膜的结构模型,并对平行柱状纳米水通道模型在介观尺度上进行了修正;接着分别对应用于不同燃料电池的改性膜的改性思路作了分析;最后讨论了用于不同燃料电池的新型质子交换膜的研究,同时列举了性能突出的改性膜和新型质子交换膜.第三部分介绍了阴离子交换膜的研究现状.第四部分对未来聚合物电解质膜的研究作了展望.     

An NMR study of methanol diffusion in polymer electrolyte fuel cell membranes

Methanol diffusion in two polymer electrolyte membranes, Nafion 117 and BPSH 40 (a 40% disulfonated wholly aromatic polyarylene ether sulfone), was measured using a modified pulsed field gradient NMR method. This method allowed for the diffusion coefficient of methanol within the membrane to be determined while immersed in a methanol solution of known concentration. A second set of gradient pulses suppressed the signal from the solvent in solution, thus allowing the methanol within the membrane to be monitored unambiguously. Over a methanol concentration range of 0.5–8 M, methanol diffusion coefficients in Nafion 117 were found to increase from 2.9 × 10⁻⁶ to 4.0 × 10⁻⁶ cm² s⁻¹. For BPSH 40, the diffusion coefficient dropped significantly over the same concentration range, from 7.7 × 10⁻⁶ to 2.5 × 10⁻⁶cm² s⁻¹. The difference in diffusion behavior is largely related to the amount of solvent sorbed by the membranes. Increasing the methanol concentration results in an increase in solvent uptake for Nafion 117, while BPSH 40 actually excludes the solvent at higher concentrations. In contrast, diffusion of methanol measured via permeability measurements (assuming a partition coefficient of 1) was lower (1.3 × 10⁻⁶ and 6.4 × 10⁻⁷ cm² s⁻¹ for Nafion 117 and BPSH 40 respectively) and showed no concentration dependence. The differences observed between the two techniques are related to the length scale over which diffusion is monitored and the partition coefficient, or solubility, of methanol in the membranes as a function of concentration. For the permeability measurements, this length is equal to the thickness of the membrane (178 and 132 μm for Nafion 117 and BPSH 40 respectively) whereas the NMR method observes diffusion over a length of approximately 4–8 μm. Regardless of the measurement technique, BPSH 40 is a greater barrier to methanol permeability at high methanol concentrations.     

直接甲醇燃料电池新型聚合物膜的研究

通过溶液共混方法 ,制备了聚偏氟乙烯与聚苯乙烯磺酸 (PVDF_PSSA)、聚偏氟乙烯与Nafion(PVDF_Nafion)两种共混膜 .研究了膜组成对膜电导率和甲醇透过率的影响 .与Nafion 1 1 7膜相比 ,PVDF_Nafion共混膜在Nafion含量为 2 5wt%时 ,电导率σ下降 2个数量级 ,而甲醇透过率P却降低 3个数量级 .若以 (σ/P)为综合指标 ,则PVDF_Nafion共混膜和PVDF_PSSA共混膜的综合性能分别比Nafion 1 1 7膜高约 4 0倍、1 6倍     

Surface observation of solvent-impregnated Nafion membrane with atomic force microscopy

Surface morphology modification of the Nafion 117 membrane has been investigated by atomic force microscopy. The effects of water and methanol on the topography and structure of the surface were studied using the contact and tapping atomic force microscopy modes. Nafion topography considerably changes when samples absorb water. However, samples stored in methanol are characterized by flat surfaces. Surface modification was linked to an expansion phenomenon during the swelling of Nafion by solvents. Tapping-mode phase images showed that ionic and cluster domains are distinguishable from the surface of samples impregnated either in water or methanol.     

磺化聚醚酰亚胺/聚醚砜共混型质子交换膜的制备及其性能

以磺化聚醚酰亚胺(SPEI)和聚醚砜(PES)为原料, 采用溶液共混法成功制备出了SPEI/PES共混型质子交换膜,并经热重分析、AFM、SEM等对膜的结构和性能进行了表征. 结果表明, 共混膜较纯SPEI膜具有更高的热稳定性和较低的溶胀性; 在室温环境下, 共混膜在干态和湿态时均具有优异的机械性能; 与纯SPEI膜相比, 共混膜的形态结构更为致密, 这将有利于降低甲醇的渗透性. 采用交流阻抗法和隔膜扩散法分别考察了膜的质子传导性和阻醇性能, 对于共混质量比为50/50的膜来说, 其质子传导率达到了5.5 mS·cm-1的水平, 能满足质子交换膜的需求, 但其甲醇渗透系数明显降低, 仅为市用Nafion 112膜的5%, 这表明该共混膜有望作为一种新型的直接甲醇燃料电池用质子交换膜.     

Nafion膜在直接甲醇燃料电池中的应用及改进

Nafion质子交换膜性能优越,广泛应用于固体聚合物燃料电池中,但因存在甲醇渗透问题,使其在直接甲醇燃料电池中的应用受限制。本文讨论了Nafion质子交换膜的物质传输机理,侧重介绍甲醇分子的渗透机理,综述了基于降低甲醇渗透率而对Nafion膜所做的改进性研究和几种具有应用前景的替代膜。     

采用Nafion粘结剂的PEMFC氧电极研究

研究了聚合物电解质燃料电池（PEMFC）中以Nation溶液取代PTFE乳液作粘结剂的效果．并对催化剂层内Nafion含量进行了优化，同时探讨了气体工作压力和离子交换膜的影响，实验发现：1．使用Nafion溶液后显著提高电池性能，Nafion含量为2mg·cm－2时性能技好；2．气体压力增大改善了电池位能；3．使用Nafion115膜的电池性能优于使用Nafion117膜的电池．要进一步提高电池性能，减小欧姆控制区的斜率是必要的．     

低甲醇透过直接甲醇燃料电池

复合膜;甲醇透过率;低甲醇透过直接甲醇燃料电池     

Electrolithographic investigations of the hydrophilic channels in Nafion membranes

Nafion membranes are used as semisolid electrolytes in methanol and hydrogen fuel cells. The ion conduction takes place through those hydrophilic channels in the Nafion that can provide continuous pathways through the membrane. There is as yet limited information about the density, the size, and the shape of these channels. We have developed two electrochemical methods of visualizing the pore structure which involve the creation of metal lithographs using the membrane pores as templates. In the experiments, the membrane is supported on a flat solid surface on one side, and is in contact with an electrolyte on the other side. Using hydrogen-terminated n-doped Si(111), we deposited gold from an electrolyte containing a gold salt. The Au ions traverse the membrane through the pores, reach the silicon surface, and are spontaneously reduced. A metallic Au deposit is formed on the silicon surface, at the base of the hydrophilic channel. The Au deposits are imaged after the membrane is dissolved. Another method involves supporting the membrane on a Pt surface and depositing silver wires through the hydrophilic channels of the membrane. The scanning electron microscope pictures of these wires provide an image of the size and the shape of the hydrophilic channels.     

磷钨酸/磺化聚醚醚酮质子导电复合膜

直接甲醇燃料电池(Direct methanol fuelcell,DMFC)作为各种用途的可移动动力源具有高效、清洁和燃料储运方便等优点,成为20世纪90年代以来研究与开发的热点。目前,这种电池的研究难点主要集中在催化剂不稳定和质子交换膜透醇上,DMFC膜不但要可传递质子和绝缘电子,还应具有     

Sulfonated poly(ether ether ketone)/poly(vinylpyrrolidone) acid–base polymer blends for direct methanol fuel cell application

Acid–base polymer blends for polymer electrolyte membranes have been prepared by blending sulfonated poly(ether ether ketone) (SPEEK) with poly(vinylpyrrolidone) (PVP) to reduce methanol uptake and to decrease methanol permeability while maintaining high proton conductivity. The acid‐base interaction occurring on the sulfonic acid group and on the tertiary amide group was characterized by FTIR and DMA. As the composition of PVP lowered than 20 wt % in the blends, the acid–base interaction causes great reduction on methanol uptake and the methanol permeability; however, the proton conductivity is still high. In this work, membrane–electrode assemblies (MEAs) have been prepared for direct methanol fuel cell (DMFC) from both blend membrane and Nafion 117. DMFC single cell performance was also evaluated. Results confirmed that SPEEK (with the degree of sulfonation (DS) = 69%) blended with PVP (M_n = 1,300,000) with a ratio of 80/20 (w/w) exhibits higher open‐circuit voltages (OCV) and lower polarization loss than those of Nafion 117. These acid–base blends will be suitable for DMFC application. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 565–572, 2006     

磺化聚芳醚砜/磺化聚酰亚胺复合质子交换膜的制备与性能研究

利用溶液浇铸法制备了一系列双磺化型磺化聚芳醚砜/磺化聚酰亚胺(SPAES/SPI)复合质子交换膜.扫描电子显微镜(SEM)结果显示复合膜不存在明显的相分离,表明二者具有很好的相容性.由于SPI的引入,复合膜在甲醇中稳定性较纯SPAES具有大幅的提高,比Nafion112低得多的甲醇吸收率表明了这些复合膜具有比后者更低的甲醇透过率.复合膜显示了与单组分膜相类似的高温分解稳定性,磺酸基团的分解温度达到了290℃以上.复合膜显示出远高于纯SPAES膜的尺寸稳定性能,在130℃高温中200h处理后,所有的复合膜均保持了高的机械性能,而此时纯SPAES膜已经溶解于水中.而且由于两种磺化聚合物间的复合,复合膜维持了较高的IEC水平,显示了较高的质子导电率,在80%相对湿度时的质子导电率与Nafion112相近,而在水中的质子导电率均高于Nafion112.     

Self-assembled polyelectrolyte multilayered films on Nafion with lowered methanol cross-over for DMFC applications

The paper is concerned with the deposition of self-assembled polyelectrolyte multilayer on Nafion membrane by layer-by-layer (LbL) technique with lowered methanol cross-over for direct methanol fuel cell (DMFC) applications. The formation of self-assembled multilayered film on Nafion was characterized by UV–vis spectroscopy and it was found that the polyelectrolyte layers growth on the Nafion surface regularly. Furthermore, the proton conductivity and methanol cross-over measurements were carried out for characterization of the LbL self-assembled composite membranes. The results showed that the concentration and pH of the polyelectrolytes significantly affect the proton conductivity and methanol barrier properties of the composite membranes. 10⁻¹ monomol polyelectrolyte concentration and pH 1.8 was found to be optimum deposition conditions considering proton conductivity and methanol permeation properties of the LbL self-assembled composite membranes. The methanol permeability of the 10 bi-layers of PAH1.8/PSS1.8 deposited LbL self-assembly composite membrane was significantly suppressed and found to be 4.41 × 10⁻⁷ cm²/s while the proton conductivity value is in acceptable range for fuel cell applications.