Crystal structure of BaMg2Si2O7 and Eu luminescence

Crystal structure of BaMg₂Si₂O₇ was determined and refined by a combined powder X-ray and neutron Rietveld method (monoclinic, C2/c, no. 15, Z=8, a=7.24553(8) Å, b=12.71376(14) Å, c=13.74813(15) Å, β=90.2107(8)°, V=1266.44(2) Å³; R_p/R_wp=3.38%/4.77%). The structure contains a single crystallographic type of Ba atom coordinated to eight O atoms with C₁ (1) site symmetry. Under 325-nm excitation Ba_0.98Eu_0.02Mg₂Si₂O₇ exhibits an asymmetric emission band around 402 nm. The asymmetric shape of the emission band is likely associated with a small electron-phonon coupling in BaMg₂Si₂O₇. The integrated intensity of the emission band was observed to remain constant over the temperature range 4.2-300 K.     

Rietveld refinement and photoluminescent properties of a new blue-emitting material: Eu activated SrZnP2O7

A new efficient blue phosphor, Eu²⁺ activated SrZnP₂O₇, has been synthesized at 1000 °C under reduced atmosphere and the crystal structure and photoluminescence properties have been investigated. The crystal structure of SrZnP₂O₇ was obtained via Rietveld refinement of powder X-ray diffraction (XRD) pattern. It was found that SrZnP₂O₇ crystallizes in space group of P2₁/n (no. 14), Z=4, and the unit cell dimensions are: a=5.30906(2) Å, b=8.21392(3) Å, c=12.73595(5) Å, β=90.1573(3)°, and V=555.390(3) Å³. Under ultraviolet excitation (200-400 nm), efficient Eu²⁺ emission peaked at 420 nm was observed, of which the luminescent efficiency at the optimal concentration of Eu²⁺ (4 mol%) was estimated to be 96% as that of BaMgAl₁₀O₁₇:Eu²⁺. Hence, the SrZnP₂O₇:Eu²⁺ exhibit great potential as a phosphor in different applications, such as ultraviolet light emitting diode and photo-therapy lamps.     

Crystallographic and magnetic characterisation of the brownmillerite Sr2Co2O5

Sr₂Co₂O₅ with the perovskite-related brownmillerite structure has been synthesised via quenching, with the orthorhombic unit cell parameters a=5.4639(3) Å, b=15.6486(8) Å and c=5.5667(3) Å based on refinement of neutron powder diffraction data collected at 4 K. Electron microscopy revealed L-R-L-R-intralayer ordering of chain orientations, which require a doubling of the unit cell along the c-parameter, consistent with the assignment of the space group Pcmb. However, on the length scale pertinent to NPD, no long-range order is observed and the disordered space group Imma appears more appropriate. The magnetic structure corresponds to G-type order with a moment of 3.00(4) μ_B directed along [1 0 0].     

The non-centrosymmetric borate oxides, MBi2B2O7 (M=Ca, Sr)

Two novel noncentrosymmetric borates oxides, MBi₂B₂O₇ or MBi₂O(BO₃)₂ (MCa, Sr), have been synthesized by solid-state reactions in air at temperatures in the 600-700 °C range. Their crystal structures have been determined ab initio and refined using powder neutron diffraction data. CaBi₂B₂O₇ crystallizes in the orthorhombic Pna2₁ space group with a=8.9371(5) Å, b=5.4771(3) Å, c=12.5912(7) Å, Z=4, R_wp=0.118, χ²=2.30. SrBi₂B₂O₇ crystallizes in the hexagonal P6₃ space group with a=9.1404(4) Å, c=13.0808(6) Å, Z=6, R_wp=0.115, χ²=4.15. Large displacement parameters suggest the presence of disorder in SrBi₂B₂O₇ as also revealed by diffuse 2×a superstructure reflections in electron diffraction patterns. Both structures are built of identical (001) neutral layers of corner-sharing BO₃ triangles and MO₆ trigonal prisms forming six-membered rings in which Bi₂O groups are located. Adjacent layers are stacked in a staggered configuration and connected through weak Bi-O bonds. A moderate efficiency for second harmonic generation (SHG) has been measured for a powder sample of CaBi₂B₂O₇ (d_eff=2d_eff(KDP)).     

Crystal and magnetic structures of the brownmillerite compound Ca2Fe1.039(8)Mn0.962(8)O5

The crystal and magnetic structures of the brownmillerite material, Ca₂Fe_1.039(8)Mn_0.962(8)O₅ were investigated using powder X-ray and neutron diffraction methods, the latter from 3.8 to 700 K. The compound crystallizes in Pnma space group with unit cell parameters of a=5.3055(5) Å, b=15.322(2) Å, c=5.4587(6) Å at 300 K. The neutron diffraction study revealed the occupancies of Fe³⁺ and Mn³⁺ ions in both octahedral and tetrahedral sites and showed some intersite mixing and a small, ∼4%, Fe excess. While bulk magnetization data were inconclusive, variable temperature neutron diffraction measurements showed the magnetic transition temperature to be 407(2) K below which a long range antiferromagnetic ordering of spins occurs with ordering wave vector k=(000). The spins of each ion are coupled antiferromagnetically with the nearest neighbors within the same layer and coupled antiparallel to the closest ions from the neighboring layer. This combination of intra- and inter-layer antiparallel arrangement of spins forms a G-type magnetic structure. The ordered moments on the octahedral and tetrahedral sites at 3.8 K are 3.64(16) and 4.23(16) μ_B, respectively.     

Superstructure of a phosphor material Ba3MgSi2O8 determined by neutron diffraction data

Ba₃MgSi₂O₈, a phosphor host examined for use in white-light devices and plant-growth lamps, was synthesized at 1225 °C in air. Its crystal structure has been determined and refined by a combined powder X-ray and neutron Rietveld method (, Z=3, a=9.72411(3) Å, c=7.27647(3) Å, V=595.870(5) Å³; R_p/R_wp=3.79%/5.03%, χ²=4.20). Superstructure reflections, observed only in the neutron diffraction data, provided the means to establish the true unit cell and a chemically reasonable structure. The structure contains three crystallographically distinct Ba atoms—Ba1 resides in a distorted octahedral site with S₆ () symmetry, Ba2 in a nine-coordinate site with C₃ (3) symmetry, and Ba3 in a ten-coordinate site with C₁ (1) symmetry. The Mg atoms occupy distorted octahedral sites, and the Si atom occupies a distorted tetrahedral site.     

Crystal chemistry and crystallography of the SrR2CuO5 (R=lanthanides) phases

The crystal chemistry and crystallography of the compounds SrR₂CuO₅ (Sr-121, R=lanthanides) were investigated using the powder X-ray Rietveld refinement technique. Among the 11 compositions studied, only R=Dy and Ho formed the stable SrR₂CuO₅ phase. SrR₂CuO₅ was found to be isostructural with the “green phase”, BaR₂CuO₅. The basic structure is orthorhombic with space group Pnma. The lattice parameters for SrDyCuO₅ are a=12.08080(6) Å, b=5.60421(2) Å, c=7.12971(3) Å, V=482.705(4) Å³, and Z=8; and for the Ho analog are a=12.03727(12) Å, b=5.58947(7) Å, c=7.10169(7) Å, V=477.816(9) Å³, and Z=8. In the SrR₂CuO₅ structure, each R is surrounded by seven oxygen atoms, forming a monocapped trigonal prism (RO₇). The isolated CuO₅ group forms a distorted square pyramid. Consecutive layers of prisms are stacked in the b-direction. Bond valence calculations imply that residual strain is largely responsible for the narrow stability of the SrR₂CuO₅ phases with R=Dy and Ho only. X-ray powder reference diffraction patterns for SrDy₂CuO₅ and SrHo₂CuO₅ were determined.     

Synthesis and structural investigation of the compounds containing HF2 anions: Ca(HF2)2, Ba4F4(HF2)(PF6)3 and Pb2F2(HF2)(PF6)

Three new compounds Ca(HF₂)₂, Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) were obtained in the system metal(II) fluoride and anhydrous HF (aHF) acidified with excessive PF₅. The obtained polymeric solids are slightly soluble in aHF and they crystallize out of their aHF solutions. Ca(HF₂)₂ was prepared by simply dissolving CaF₂ in a neutral aHF. It represents the second known compound with homoleptic HF environment of the central atom besides Ba(H₃F₄)₂. The compounds Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) represent two additional examples of the formation of a polymeric zigzag ladder or ribbon composed of metal cation and fluoride anion (MF⁺)_n besides PbF(AsF₆), the first isolated compound with such zigzag ladder. The obtained new compounds were characterized by X-ray single crystal diffraction method and partly by Raman spectroscopy. Ba₄F₄(HF₂)(PF₆)₃ crystallizes in a triclinic space group P1¯ with a=4.5870(2) Å, b=8.8327(3) Å, c=11.2489(3) Å, α=67.758(9)°, β=84.722(12), γ=78.283(12)°, V=413.00(3) Å³ at 200 K, Z=1 and R=0.0588. Pb₂F₂(HF₂)(PF₆) at 200 K: space group P1¯, a=4.5722(19) Å, b=4.763(2) Å, c=8.818(4) Å, α=86.967(10)°, β=76.774(10)°, γ=83.230(12)°, V=185.55(14) ų, Z=1 and R=0.0937. Pb₂F₂(HF₂)(PF₆) at 293 K: space group P1¯, a=4.586(2) Å, b=4.781(3) Å, c=8.831(5) Å, α=87.106(13)°, β=76.830(13)°, γ=83.531(11)°, V=187.27(18) Å³, Z=1 and R=0.072. Ca(HF₂)₂ crystallizes in an orthorhombic Fddd space group with a=5.5709(6) Å, b=10.1111(9) Å, c=10.5945(10) Å, V=596.77(10) Å³ at 200 K, Z=8 and R=0.028.     

Crystal structure and luminescence of Sr0.99Eu0.01AlSiN3

Strontium europium aluminum silicon nitride, Sr_0.99Eu_0.01AlSiN₃, was synthesized by heating a mixture of binary nitrides at 2173 K and a N₂ gas pressure of 190 MPa. Single crystals of Sr_0.99Eu_0.01AlSiN₃ approximately 30 μm were obtained. The structure was confirmed to be an isotypic structure of CaAlSiN₃ in the orthorhombic space group Cmc2₁, analyzed by single-crystal X-ray diffraction. The lattice parameters are a=9.843(3), b=5.7603(16), c=5.177(2) Å, cell volume=293.53(17) Å³. It shows an orange-red photoluminescence by 5d→4f transition of Eu²⁺ at around 610 nm under excitation ranging from ultraviolet to 525 nm. The photoluminescence intensity, temperature characteristics, and oxidative stability were comparable or superior to those of CaAlSiN₃:Eu²⁺ phosphor.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Structural study of the NaCdVO4-Cd3V2O8 and CdO-V2O5 sections of the ternary system Na2O-CdO-V2O5

The NaCdVO₄-Cd₃V₂O₈ and CdO-V₂O₅ sections of the ternary system Na₂O-CdO-V₂O₅ have been studied and the crystal structures of Cd₃V₂O₈ and Cd₁₈V₈O₃₈ compounds were determined from single-crystal X-ray diffraction data. Cd₃V₂O₈ crystallizes with the maricite-type structure in space group Pnma, a=9.8133(10) Å, b=6.9882(10) Å, c=5.3251(10) Å and Z=4, whereas Cd₁₈V₈O₃₈ crystallizes in space group P1 with a new-type structure, a=8.5761(14), b=8.607(3), c=12.896(2) Å, α=95.64(1), β=102.45(1), γ=108.42(1)° and Z=1. The Cd₃V₂O₈ structure is made up of Cd1O₄ infinite chains of edge-sharing Cd1O₆ octahedra which are parallel to the b direction. The Cd1O₄ chains are linked together by VO₄ tetrahedra and strongly distorted Cd2O₄ tetrahedra. The structure of Cd₁₈V₈O₃₈ is based on an ordered three-dimensional framework of cadmium and vanadium polyhedra that share corners. The distorted CdO₆ octahedra, CdO₅ trigonal bipyramids and CdO₅ square pyramids share corners, edges or faces.     

Ab initio structure determination of new compound Li4CaB2O6

A new compound, Li₄CaB₂O₆, has been synthesized by solid-state reaction and its structure has been determined from powder X-ray diffraction data by direct methods. The refinement was carried out using the Rietveld methods and the final refinement converged with R_p=10.4%, R_wp=14.2%, R_exp=4.97%. This compound belongs to the orthorhombic space group Pnnm, with lattice parameters a=9.24036(9) Å, b=8.09482(7) Å, and c=3.48162(4) Å. Fundamental building units are isolated [BO₃]³⁻ anionic groups, which are all parallel to the a-b plane stacked along the c-axis. The Ca atoms are six-coordinated by the O atoms to form octahedral coordination polyhedra, which are joined together through edges along the c-axis, forming infinitely long three-dimensional chains. The Li atoms have a four-fold and a five-fold coordination with O atoms that lead to complex Li-O-Li chains that also extend along the c-axis. The infrared spectrum of Li₄CaB₂O₆ was also studied, which is consistent with the crystallographic study.     

Synthesis, characterization, and structure determination of the orthorhombic U2(PO4)(P3O10)

β-UP₂O₇ has been synthesized under hydrothermal conditions (θ=500°C, P=200 MPa), using UO₂ and H₃PO₄. β-UP₂O₇ crystallizes in the orthorhombic space group Pn2₁a, with a=11.526 (2) Å, b=7.048 (2) Å, c=12.807 (2) Å and Z=4. Its structure has been determined through direct methods and difference Fourier synthesis and has been refined to R=0.0396. The structure is built on UO₈ polyhedral chains along the b-axis. PO₄³⁻ and P₃O₁₀⁵⁻ groups coexist in the structure and the latter groups form non-linear chains. Cohesion of the structure is made through the linkage of UO₈ chains by PO₄ and P₃O₁₀ groups leading to the formula U₂(PO₄)(P₃O₁₀) instead of β-UP₂O₇. Vibrational and optical spectra confirm the results obtained by X-ray diffraction. DTA-TGA measurements show that the transformation of U₂(PO₄)(P₃O₁₀) to the cubic α-UP₂O₇ occurs at θ=870°C.     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

Preparation, structural and magnetic characterization of DyCrMnO5

The title compound has been first synthesized by a citrate technique followed by thermal treatments under moderate oxygen pressure conditions, and characterized by X-ray and neutron powder diffraction (NPD) and magnetization measurements. The crystal structure of DyCrMnO₅ has been refined from NPD data in the space group Pbam; a=7.2617(6) Å, b=8.5161(6) Å, and c=5.7126(5) Å at 295 K. This oxide is isostructural with RMn₂O₅ oxides (R=rare earths) and it contains infinite chains of (Cr, Mn)⁴⁺O₆ octahedra-sharing edges, linked together by (Mn, Cr)³⁺O₅ pyramids and DyO₈ units. The high degree of antisite disordering exhibited by DyCrMnO₅ is noteworthy. The octahedral positions are occupied by roughly 50% of Mn and Cr cations, and the pyramidal groups contain two thirds of Mn and one third of Cr cations. We assume that Mn and Cr cations at the octahedral positions exhibit a tetravalent oxidation state, whereas the metals at the pyramidal positions are trivalent, in order to preserve the electroneutrality of this oxide. The susceptibility vs temperature curve of DyCrMnO₅ does not suggest the establishment of a long-range magnetic structure even at low temperatures; the NPD technique does not provide any signal of magnetic ordering, since the reflections do not show any magnetic contribution.     

Structural studies on a high-pressure polymorph of NaYSi2O6

High-pressure synthesis experiments in the system Na₂O-Y₂O₃-SiO₂ revealed the existence of a previously unknown polymorph of NaYSi₂O₆ or Na₃Y₃[Si₃O₉]₂ which was quenched from 3.0 GPa and 1000 °C. Structural investigations on this modification have been performed using single-crystal X-ray diffraction data collected at ambient conditions. Furthermore, unpolarized micro-Raman spectra have been obtained from single-crystal material. The high-P modification of NaYSi₂O₆ crystallizes in the centrosymmetric space group C2/c with 12 formula units per cell (a=8.2131(9) Å, b=10.3983(14) Å, c=17.6542(21) Å, β=100.804(9)°, V=1481.0(3) Å³, R(|F|)=0.033 for 1142 independent observed reflections) and belongs to the group of cyclo-silicates. Basic building units are isolated three-membered [Si₃O₉] rings located in layers parallel to (010). Within a single layer the rings are concentrated in strings parallel to [100]. The sequence of directedness of up (U) or down (D) pointing tetrahedra of a single ring is UUU or DDD, respectively. Stacking of the layers parallel to b results in the formation of a three-dimensional structure in which yttrium and sodium cations are incorporated for charge compensation. In more detail, four non-tetrahedral cation positions can be differentiated which are coordinated by 6 and 8 oxygen ligands. Refinements of the site occupancies did not reveal any indication for mixed Na-Y populations on these positions. Finally, several geometrical parameters of rings occurring in cyclo-trisilicate structures have been compiled and are discussed.     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

Synthesis, structure and magnetic properties of the S=1/2, one-dimensional antiferromagnet, Y5Re2O12

Single crystals of Y₅Re₂O₁₂ have been grown, and the crystal structure has been determined by X-ray diffraction. This compound crystallizes in space group C2/m with cell dimensions of a=12.4081(10) Å b=5.6604(5)Å, c=7.4951(6) Å, β=107.837(3)°, Z=2. The final refinement led to R1=0.0238, WR2=0.0459 for 1053 observed reflections with F>4σ(F₀). Edge-sharing ReO₆ octahedra form infinite linear [ReO₂O_4/2]_n chains along the b direction with alternating short and long Re-Re distances. Three crystallographically independent yttrium atoms surround O2 to form OY₄ tetrahedra, which share edges and corners in the ab plane to form a two-dimensional Y₅O₄ network which separates the [ReO₂O_4/2]_n magnetic chains. This compound is therefore isostructural with the series Ln₅Re₂O₁₂Ln=Gd-Lu, which have been known since 1969. The average Re oxidation state is +4.5 in the chains and a reasonable, if qualitative MO scheme results in one unpaired electron per Re dimer. Consistent with this, magnetic susceptibility data can be fitted to the one-dimensional antiferromagnetic Heisenberg model with S=1/2 and parameters J^intra/k=−89(1)K, g=2.15(4) and χ(TIP)=5(1)×10⁻⁴ emu/mol. There is no sign of long-range magnetic order down to 2 K. These results are contrasted with those for the isostructural Y₅Mo₂O₁₂.     

Single-crystal synthesis and structure refinement of the LiCoO2-LiAlO2 solid-solution compounds: LiAl0.32Co0.68O2 and LiAl0.71Co0.29O2

Single crystals of the LiCoO₂-LiAlO₂ solid solution compounds LiAl_0.32Co_0.68O₂ and LiAl_0.71Co_0.29O₂ were synthesized by a flux method using alumina crucibles. A single-crystal X-ray diffraction study confirmed the trigonal space group and the lattice parameters a=2.8056(11) Å, c=14.1079(15) Å, and c/a=5.028 for LiAl_0.32Co_0.68O₂, and a=2.8023(7) Å, c=14.184(4) Å, and c/a=5.061 for LiAl_0.71Co_0.29O₂. The crystal structures have been refined to the conventional values R=3.2% and wR=2.4% for LiAl_0.32Co_0.68O₂, and R=3.6% and wR=3.5% for LiAl_0.71Co_0.29O₂. The evidence of the location of Al atoms in the pseudotetragonal coordination (6c site), reported previously in LiAl_0.2Co_0.8O₂, could not be observed in the present electron density distribution maps in both LiAl_0.32Co_0.68O₂ and LiAl_0.71Co_0.29O₂. The octahedral distortion analysis indicated that the Al-substitution strongly affected the distortion of the LiO₆ octahedron in this solid-solution compound system, but hardly affected that of the (Al.Co)O₆ octahedron.     

High-pressure synthesis and structural characterization of three new polyphosphides, α-SrP3, BaP8, and LaP5

Three novel metal polyphosphides, α-SrP₃, BaP₈, and LaP₅, were prepared in BN crucibles by the reaction of the respective stoichiometric mixtures under a high pressure of 3 GPa at 950-1000°C. Their crystal structures were determined from single-crystal X-ray data (α-SrP₃: space group C2/m, a=9.199(6) Å, b=7.288(3) Å, c=5.690(3) Å, β=113.45(4)°, Z=4, R₁/wR₂=0.0684/0.1180 for 471 observed reflections and 22 variables; BaP₈: space group P−1, a=6.762(2) Å, b=7.233(2) Å, c=8.567(2) Å, α=86.32(2)°, β=84.31(2)°, γ=70.40(2)°, Z=2, R₁/wR₂=0.0476/0.1255 for 2702 observed reflections and 82 variables; LaP₅: space group P2₁/m, a=4.885(1) Å, b=9.673(3) Å, c=5.577(2) Å, β=105.32(2)°, Z=2, R₁/wR₂=0.0391/0.1034 for 1272 observed reflections and 31 variables). α-SrP₃ is isostructural with SrAs₃ and the crystal structure consists of two-dimensional puckered polyanionic layers _∞²[P₃]²⁻ that stack along the c-axis yielding channels occupied by Sr²⁺ counterions. BaP₈ crystallizes in a new structure type which contains a three-dimensional infinite polyanionic framework _∞³[P₃]²⁻, with large channels hosting the barium cations. LaP₅ is a layered compound containing _∞²[P₅]³⁻ polyanionic layers separated by La³⁺ ions. All three compounds exhibit expected diamagnetic behaviors.