Preparation of a new pyrochlore-type compound Na0.32Bi1.68Ti2O6.46(OH)0.44 by hydrothermal reaction

A new pyrochlore-type Na_0.32Bi_1.68Ti₂O_6.46(OH)_0.44 with the cubic cell of a=10.339(5) Å was prepared by hydrothermal reaction using TiO₂ (anatase) and Bi₂O₃ in NaOH solution. This compound was obtained when the molar ratio of NaOH/TiO₂ was above 2 and the reaction temperature was above 240 °C. The TG-curve of as-prepared sample showed a mass loss of 0.8 mass% which was caused by release of OH group. This compound decomposed to a pyrochlore-type compound and a layered-type Na_0.5Bi_4.5Ti₄O₁₅ above 800 °C. The optical band gap of Na_0.32Bi_1.68Ti₂O_6.46(OH)_0.44 was estimated to be 2.5 eV.     

Preparation and visible light photocatalytic activity of Bi2O3/Bi2WO6 heterojunction photocatalysts

The Bi₂O₃/Bi₂WO₆ heterojunction photocatalysts were prepared by a two-step solvothermal process using Bi(NO₃)₃-ethylene glycol solution as Bi source. The catalysts were characterized by X-ray diffraction, scanning and transmission electron microscopy, X-ray photoelectron spectroscopy, and UV-vis diffuse reflection spectroscopy. The heterostructure catalysts are composed of Bi₂O₃ nanoparticles as modifier and 3D Bi₂WO₆ microspheres as substrate. Bi₂O₃ nanoparticles with diameters of about 10-15 nm are tightly grown on the lateral surface of the Bi₂WO₆ microspheres. The hierarchical Bi₂O₃/Bi₂WO₆ microspheres exhibit higher photocatalytic activity than the single phase Bi₂WO₆ or Bi₂O₃ for the degradation of rhodamine B under visible light illumination (λ>420 nm). The enhancement of the photocatalytic activity of the Bi₂O₃/Bi₂WO₆ heterojunction catalysts can be ascribed to their improved light absorption property and the reduced recombination of the photoexcited electrons and holes during the photocatalytic reaction. The effect of loading amount of Bi₂O₃ on the catalytic performance of the heterojunction catalysts was also investigated and the optimal content of Bi₂O₃ is 3 wt%. The Bi₂O₃/Bi₂WO₆ heterojunction photocatalysts are essentially stable during the photocatalytic process.     

CTAB-Mn3O4 nanocomposites: Synthesis,NMR and low temperature EPR studies

We are reporting on the synthesis of Mn₃O₄ nanoparticles and CTAB-Mn₃O₄ nanocomposites via a sonochemical route using MnCl₂, ethanol, NaOH and CTAB. The crystalline phase was identified as Mn₃O₄. The crystallite size of the CTAB-Mn₃O₄ nanocomposite was identified as 13 ± 5 nm from X-ray line profile fitting and the particle size from TEM was 107.5 ± 1.4 nm. The interaction between CTAB and the Mn₃O₄ nanoparticles was investigated by FTIR and ¹H NMR spectroscopies. Two different magnetic phase transitions were observed for both samples below the Curie temperature (43 °C) by using a low temperature Electron Paramagnetic Resonance (EPR) technique. Also we determined the effect of the capping with CTAB on the reduction in absorbed power.     

Phase formation, crystal chemistry, and properties in the system Bi2O3-Fe2O3-Nb2O5

Subsolidus phase relations have been determined for the Bi₂O₃-Fe₂O₃-Nb₂O₅ system in air (900-1075 °C). Three new ternary phases were observed—Bi₃Fe_0.5Nb_1.5O₉ with an Aurivillius-type structure, and two phases with approximate stoichiometries Bi₁₇Fe₂Nb₃₁O₁₀₆ and Bi₁₇Fe₃Nb₃₀O₁₀₅ that appear to be structurally related to Bi₈Nb₁₈O₅₇. The fourth ternary phase found in this system is pyrochlore (A₂B₂O₆O′), which forms an extensive solid solution region at Bi-deficient stoichiometries (relative to Bi₂FeNbO₇) suggesting that ≈4-15% of the A-sites are occupied by Fe³⁺. X-ray powder diffraction data confirmed that all Bi-Fe-Nb-O pyrochlores form with positional displacements, as found for analogous pyrochlores with Zn, Mn, or Co instead of Fe. A structural refinement of the pyrochlore 0.4400:0.2700:0.2900 Bi₂O₃:Fe₂O₃:Nb₂O₅ using neutron powder diffraction data is reported with the A cations displaced (0.43 Å) to 96g sites and O′ displaced (0.29 Å) to 32e sites (Bi_1.721Fe_0.190(Fe_0.866Nb_1.134)O₇, Fd3¯m (#227), ). This displacive model is somewhat different from that reported for Bi_1.5Zn_0.92Nb_1.5O_6.92, which exhibits twice the concentration of small B-type cations on the A-sites as the Fe system. Bi-Fe-Nb-O pyrochlores exhibited overall paramagnetic behavior with large negative Curie-Weiss temperature intercepts, slight superparamagnetic effects, and depressed observed moments compared to high-spin, spin-only values. The single-phase pyrochlore with composition Bi_1.657Fe_1.092Nb_1.150O₇ exhibited low-temperature dielectric relaxation similar to that observed for Bi_1.5Zn_0.92Nb_1.5O_6.92; at 1 MHz and 200 K the relative permittivity was 125, and above 350 K conductive effects were observed.     

The study of Bi3B5O12: synthesis, crystal structure and thermal expansion of oxoborate Bi3B5O12

The paper presents a new data on the crystal structure, thermal expansion and IR spectra of Bi₃B₅O₁₂. The Bi₃B₅O₁₂ single crystals were grown from the melt of the same stoichiometry by Czochralski technique. The crystal structure of Bi₃B₅O₁₂ was refined in anisotropic approximation using single-crystal X-ray diffraction data. It is orthorhombic, Pnma, a=6.530(4), b=7.726(5), c=18.578(5) Å, V=937.2(5) Å³, Z=4, R=3.45%. Bi³⁺ atoms have irregular coordination polyhedra, Bi(1)O₆ (d(B-O)=2.09-2.75 Å) and Bi(2)O₇ (d(B-O)=2.108-2.804 Å). Taking into account the shortest bonds only, these polyhedra are considered here as trigonal Bi(1)O₃ (2.09-2.20 Å) and tetragonal Bi(2)O₄ (2.108-2.331 Å) irregular pyramids with Bi atoms in the tops of both pyramids. The BiO₄ polyhedra form zigzag chains along b-axis. These chains alternate with isolated anions [B₂^IVB₃^IIIO₁₁]⁷⁻ through the common oxygen atoms to form thick layers extended in ab plane. A perfect cleavage of the compound corresponds to these layers and an imperfect one is parallel to the Bi-O chains. The Bi₃B₅O₁₂ thermal expansion is sharply anisotropic (α₁₁≈α₂₂=12, α₃₃=3×10⁻⁶ °C⁻¹) likely due to a straightening of the flexible zigzag chains along b-axis and decreasing of their zigzag along c-axis. Thus the properties like cleavage and thermal expansion correlate to these chains.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

A novel nonenzymatic sensor based on LaNi0.6Co0.4O3 modified electrode for hydrogen peroxide and glucose

In this paper, LaNi_0.6Co_0.4O₃ (LNC) nanoparticles were synthesized by the sol–gel method, and the structure and morphology of LNC nanoparticles were characterized by X-ray diffraction spectrum, scanning electron microscopy and transmitting electron microscopy. And then, LNC was used to modify carbon paste electrode (CPE) without any adhesive to fabricate hydrogen peroxide and glucose sensor, and the results demonstrated that LNC exhibited strong electrocatalytical activity by cyclic voltammetry and amperometry. In H₂O₂ determination, linear response was obtained in the concentration range of 10 nM–100 μM with a detection limit of 1.0 nM. In glucose determination, there was the linear region of 0.05–200 μM with a detection limit of 8.0 nM. Compared with other reports, the proposed sensor also displayed high sensitivity toward H₂O₂ (1812.84 μA mM⁻¹ cm⁻²) and glucose (643.0 μA mM⁻¹ cm⁻²). Moreover, this prepared sensor was applied to detect glucose in blood serum and hydrogen peroxide in toothpaste samples with satisfied results, indicating its possibility in practical application.     

Low-temperature synthesis of K2NbO3F powders by an alternative approach of solid-state reaction

K₂NbO₃F powders were directly synthesized by an alternative solid-state method at low temperature. Stoichiometric ammonium niobium oxalate, K₂C₂O₄ and KF were mixed with small amounts of water and then dried at room temperature. X-ray diffraction results show that layered perovskite K₂NbO₃F powders can be obtained by calcining the mixture in temperature range from 550 to 700 °C for 3 h. The elemental composition, powder morphology and particle size of calcination products were analyzed by scanning electron microscope-energy dispersive spectroscopy (SEM/EDS). The SEM images suggest that the particles of the powders obtained at 550 °C are irregular platelets with a diameter of 0.5-1 μm and a thickness of 100-200 nm. The platelets are 3-5 μm in diameter and 1-2 μm in thickness when the calcination temperature reaches 700 °C. K₂NbO₃F decomposes to K₅(NbO₃)₄F and KF when the temperature reaches 800 °C.     

The structural investigation of Ba4Bi3F17

The anion-excess ordered fluorite-related phase Ba₄Bi₃F₁₇ has been synthesized by a solid state reaction of BaF₂ and BiF₃ at 873 K. The crystal structure of Ba₄Bi₃F₁₇ has been studied using electron diffraction and X-ray powder diffraction (a=11.2300(2) Å, c=20.7766(5) Å, S.G. , R_I=0.020, R_P=0.036). Interstitial fluorine atoms in the Ba₄Bi₃F₁₇ structure are considered to form isolated cuboctahedral 8 : 12 : 1 clusters. The structural relationship between Ba₄Bi₃F₁₇ and similar rare-earth-based phases is discussed.     

Synthesis of Fe3O4\SiO2\Ag nanoparticles and its application in surface-enhanced Raman scattering

To obtain a recyclable surface-enhanced Raman scattering (SERS) material, we developed a composite of Fe₃O₄\SiO₂\Ag with core\shell\particles structure. The designed particles were synthesized via an ultrasonic route. The Raman scattering signal of Fe₃O₄ could be shielded by increasing the thickness of the SiO₂ layer to 60 nm. Dye rhodamine B (RB) was chosen as probe molecule to test the SERS effect of the synthesized Fe₃O₄\SiO₂\Ag particles. On the synthesized Fe₃O₄\SiO₂\Ag particles, the characteristic Raman bands of RB could be observed when the RB solution was diluted to 5 ppm (1×10⁻⁵ M). Furthermore, the synthesized particles could keep their efficiency till four cycles.     

Crystal chemistry and crystallography of the Aurivillius phase Bi5AgNb4O18

Bi₅AgNb₄O₁₈ is a new phase, which was discovered during the phase equilibrium study of the Bi₂O₃-Ag₂O-Nb₂O₅ system. Bi₅AgNb₄O₁₈ was prepared at 750°C and is stable in air up to its melting temperature of 1160.1±5.0°C (standard error of estimate). Results of a Rietveld refinement using neutron powder diffraction confirmed that Bi₅AgNb₄O₁₈ is isostructural with Bi₃TiNbO₉, Bi₅NaNb₄O₁₈, and Bi₅KNb₄O₁₈. The structure was refined in the orthorhombic space group A2₁am, Z=2, and the lattice parameters are a=5.4915(2) Å, b=5.4752(2) Å, c=24.9282(8) Å, and V=749.52(4) Å³. The structure can be described as the m=2 member of the Aurivillius family, (Bi₂O₂)²⁺ (A_m−1B_mO_3m+1)²⁻ (where A=Bi and B=Ag, Nb), which is characterized by perovskite-like (A_m−1B_mO_3m+1)²⁻ slabs regularly interleaved with (Bi₂O₂)²⁺ layers. The octahedral [NbO₆] units are distorted with Nb-O distances ranging from 1.856(4) to 2.161(2) Å and the O-Nb-O angles ranging from 82.6(3)° to 98.5(3)°. These octahedra are tilted about the a- and c-axis by about 10.3° and 12.4°, respectively. Ag was found to substitute exclusively into the Bi-site that is located in the layer between the two distorted [NbO₆] units. Although the Ag substitutes into the Bi-site with the Bi:Ag ratio of 1:1, the existence of a superlattice was not detected using electron diffraction. A comparison of (Bi₂O₂)²⁺(A_m−1Nb_mO_3m+1)²⁻ structures (where A=Ag, Na, and K) revealed a relation between the pervoskite tolerance factor, t, and structural distortion. The reference pattern for Bi₅AgNb₄O₁₈ has been submitted to the International Centre for Diffraction Data (ICDD) for inclusion in the Powder Diffraction File.     

Preparation and performances of nanosized Ta2O5 powder photocatalyst

Nanosized-Ta₂O₅ powder photocatalyst was successfully synthesized by using sol-gel method via TaCl₅ butanol solution as a precursor. Ta₂O₅ species can be formed under 500 °C via the decomposition of the precursor. The crystalline phase of Ta₂O₅ powder photocatalyst can be obtained after being calcined above 600 °C for 4 h. The crystal size and particle size of Ta₂O₅ powder photocatalyst was about 50 nm. A good photocatalytic performance for the degradation of gaseous formaldehyde was obtained for the nanosized-Ta₂O₅ powder. The Ta₂O₅ powder formed at 700 °C for 4 h and at 650 °C for 12 h showed the best performance. The calcination temperature and time play an important role in the crystallization and photocatalytical performance of nanosized-Ta₂O₅ powder.     

Preparation and photoluminescence properties of RE:Na3La9O3(BO3)8 (RE=Er, Yb) crystals

Using Na₂CO₃-H₃BO₃-NaF as fluxes, transparent RE:Na₃La₉O₃(BO₃)₈ (abbr. RE:NLBO, RE=Er, Yb) crystals have been grown by the top seed solution growth (TSSG) method. The X-ray powder diffraction analysis shows that the RE:NLBO crystals have the same structure with NLBO. The element contents were determined by molar to be 0.64% Er³⁺ in Er:NLBO, 2.70% Yb³⁺ in Yb:NLBO, respectively. The polarized absorption spectra of RE:NLBO have been measured at room temperature and show that both Er:NLBO and Yb:NLBO have a strong absorption bands near 980 nm with wide FWHM (Full Wave at Half Maximum) (21 nm for Er:NLBO and 25 nm for Yb:NLBO). Fluorescence spectra have been recorded. Yb:NLBO has the emission peaks at 985 nm, 1028 nm and 1079 nm and the emission peak of Er:NLBO is at 1536 nm. Spectral parameters have been calculated by the Judd-Ofelt theory for Er:NLBO and the reciprocity method for Yb:NLBO, respectively. The calculated values show that Er:NLBO is a candidate of 1.55 μm laser crystals and Yb:NLBO is a candidate for self-frequency doubling crystal.     

Effect of capping and particle size on Raman laser-induced degradation of γ-Fe2O3 nanoparticles

Diol capped γ-Fe₂O₃ nanoparticles are prepared from ferric nitrate by refluxing in 1,4-butanediol (9.5 nm) and 1,5-pentanediol (15 nm) and uncapped particles are prepared by refluxing in 1,2-propanediol followed by sintering the alkoxide formed. X-ray diffraction (XRD) shows that all the samples have the spinel phase. Raman spectroscopy shows that the samples prepared in 1,4-butanediol and 1,5-pentanediol and 1,2-propanediol (sintered at 573 and 673 K) are γ-Fe₂O₃ and the 773 K-sintered sample is Fe₃O₄. Raman laser studies carried out at various laser powers show that all the samples undergo laser-induced degradation to α-Fe₂O₃ at higher laser power. The capped samples are however, found more stable to degradation than the uncapped samples. The stability of γ-Fe₂O₃ sample with large particle size (15.4 nm) is more than the sample with small particle size (10.2 nm). Fe₃O₄ having a particle size of 48 nm is however less stable than the smaller γ-Fe₂O₃ nanoparticles.     

Crystal structure, stoichiometry, and dielectric relaxation in Bi3.32Nb7.09O22.7 and structurally related ternary phases

The crystal structure of the phase previously reported to occur at 4:9 Bi₂O₃:Nb₂O₅ has been determined using single-crystal X-ray and powder neutron diffraction (P6₃/mmc; a=7.4363(1) Å, c=19.7587(5) Å; Z=2). The structural study combined with phase equilibrium analyses indicate that the actual composition is Bi_3.32Nb_7.09O_22.7. This binary compound is the end-member of a family of four phases which form along a line between it and the pyrochlore phase field in the Bi₂O₃:Fe₂O₃:Nb₂O₅ system. The structures are derived from the parent pyrochlore end-member by chemical twinning, and can also be described as unit-cell intergrowths of the pyrochlore and hexagonal tungsten bronze (HTB) structures. The dielectric properties of the three chemically twinned pyrochlore phases, Bi_3.32Nb_7.09O_22.7, Bi_9.3Fe_1.1Nb_16.9O_57.8 and Bi_5.67FeNb₁₀O₃₅, were characterized. All exhibit low-temperature, broad dielectric relaxation similar to that of the Bi-Fe-Nb-O pyrochlore. At 1 MHz and ≈175 K the observed relative permittivites were 345, 240, and 205, respectively, compared to 125 for the Bi-Fe-Nb-O pyrochlore. The higher relative permittivities observed for the chemically twinned pyrochlore derivatives are ascribed to the presence of HTB blocks in their structures: The Bi atoms located in the HTB blocks feature highly asymmetric coordination environments compared to pyrochlore, and the magnitude of the relative permittivity increases with the proportion of Bi located within the HTB portions of the structures.     

The non-centrosymmetric borate oxides, MBi2B2O7 (M=Ca, Sr)

Two novel noncentrosymmetric borates oxides, MBi₂B₂O₇ or MBi₂O(BO₃)₂ (MCa, Sr), have been synthesized by solid-state reactions in air at temperatures in the 600-700 °C range. Their crystal structures have been determined ab initio and refined using powder neutron diffraction data. CaBi₂B₂O₇ crystallizes in the orthorhombic Pna2₁ space group with a=8.9371(5) Å, b=5.4771(3) Å, c=12.5912(7) Å, Z=4, R_wp=0.118, χ²=2.30. SrBi₂B₂O₇ crystallizes in the hexagonal P6₃ space group with a=9.1404(4) Å, c=13.0808(6) Å, Z=6, R_wp=0.115, χ²=4.15. Large displacement parameters suggest the presence of disorder in SrBi₂B₂O₇ as also revealed by diffuse 2×a superstructure reflections in electron diffraction patterns. Both structures are built of identical (001) neutral layers of corner-sharing BO₃ triangles and MO₆ trigonal prisms forming six-membered rings in which Bi₂O groups are located. Adjacent layers are stacked in a staggered configuration and connected through weak Bi-O bonds. A moderate efficiency for second harmonic generation (SHG) has been measured for a powder sample of CaBi₂B₂O₇ (d_eff=2d_eff(KDP)).     

Structure and magnetic order in the series BixRE1−xFe0.5Mn0.5O3 (RE=La,Nd)

The influence of Bi³⁺ on the structural and magnetic properties of the rare-earth-containing perovskites REFe_0.5Mn_0.5O₃ (RE=La,Nd) was studied, and the limit of bismuth substitution was determined to be x≤0.5 in Bi_xRE_1−xFe_0.5Mn_0.5O_3+δ (RE=La,Nd) at ambient pressure. Crystal structures in both La and Nd series were determined to be GdFeO₃-type Pnma with the exception of the Bi_0.3La_0.7Fe_0.5Mn_0.5O₃ sample, which is monoclinic I2/a in the a⁻b⁻b⁻ tilt scheme. The samples undergo a transition to G-type antiferromagnetic order along with a weak ferromagnetic component, mixed with cluster-glass type behavior. The substitution of bismuth into the lattice results in a drop in T_N relative to the lanthanide end-members. Long range ordering temperatures T_N in the range 240-255 K were observed, with a significantly lower ordered magnetic moment in the case of lanthanum (M∼1.7-1.9 μ_B) than in the case of neodymium (M∼2.1 μ_B).     

Long Fe3O4 nanowires decorated by CdTe quantum dots: Synthesis and magnetic-optical properties

This work describes the synthesis and magnetic-optical properties of Fe₃O₄ nanowires decorated by CdTe quantum dots. The composite nanowires with a length of 1 μm and an average diameter of 23±3 nm were prepared in a high yield through the preferential growth of Fe₃O₄ on CdTe quantum dots using ethylenediamine as template. Their growth mechanism was discussed based on the results of control experiments. Studies on the optical and magnetic properties of the composite nanowires reveal that they assume not only yellow-green emission feature but also room temperature ferromagnetism.     

The crystal chemistry of Bi6TP2O15+x, T=Fe, Ni, Zn: Isomorphism and polymorphism, structural relationship to Bi6TiP2O16

The crystal structures of compounds with nominal compositions Bi₆FeP₂O_15+x (I), Bi₆NiP₂O_15+x (II) and Bi₆ZnP₂O_15+x (III) were determined from single-crystal X-ray diffraction data. They are monoclinic, space group I2, Z=2. The lattice parameters for (I) are a=11.2644(7), b=5.4380(3), c=11.1440(5) Å, β=96.154(4)°; for (II) a=11.259(7), b=5.461(4), c=11.109(7) Å, β=96.65(1)°; for (III) a=19.7271(5), b=5.4376(2), c=16.9730(6) Å, β=131.932(1)°. Least squares refinements on F² converged for (I) to R1=0.0554, wR₂=0.1408; for (II) R₁=0.0647, wR₂=0.1697; for (III) R₁=0.0385, wR₂=0.1023. The crystals are complexly twinned by 2-fold rotation about , by inversion and by mirror reflection. The structures consist of edge-sharing articulations of OBi₄ tetrahedra forming layers in the a-c plane that then continue by edge-sharing parallel to the b-axis. The three-dimensional networks are bridged by Fe and Ni octahedra in (I) and (II) and by Zn trigonal bipyramids in (III) as well as by oxygen atoms of the PO₄ moieties. Bi also randomly occupies the octahedral sites. Oxygen vacancies exist in the structures of the three compounds due to required charge balances and they occur in the octahedral coordination polyhedron of the transition metal. In compound (III), no positional disorder in atomic sites is present. The Bi-O coordination polyhedra are trigonal prisms with one, two or three faces capped. Magnetic susceptibility data for compound (I) were obtained between 4.2 and 350 K. Between 4.2 and 250 K it is paramagnetic, μ_eff=6.1 μ_B; a magnetic transition occurs above 250 K.     

A Facile synthesis of flower-like Co3O4 porous spheres for the lithium-ion battery electrode

The porous hierarchical spherical Co₃O₄ assembled by nanosheets have been successfully fabricated. The porosity and the particle size of the product can be controlled by simply altering calcination temperature. SEM, TEM and SAED were performed to confirm that mesoporous Co₃O₄ nanostructures are built-up by numerous nanoparticles with random attachment. The BET specific surface area and pore size of the product calcined at 280 °C are 72.5 m² g⁻¹ and 4.6 nm, respectively. Our experiments further demonstrated that electrochemical performances of the synthesized products working as an anode material of lithium-ion battery are strongly dependent on the porosity.