Optical bandgap and electrical conductivity studies on near stoichiometric LiNbO3 crystals prepared by VTE process

Vapour transport equilibrium (VTE) technique was used to prepare near stoichiometric LiNbO₃ (NSLN) crystals. Simultaneous occurrence of reduction has been observed during the Li-enrichment that results in the weak absorption bands centred at 1.7, 2.6 and 3.7 eV in the absorption spectrum. Annealing in oxygen atmosphere resulted in decrease in the intensity of these bands. The indirect and direct band-gap energies for NSLN crystals evaluated from absorption studies are reported. The energy of the phonon involved in the indirect transition is ～85 meV (685 cm^?1). Near room temperature ac-conductivity measurements reveal lower conductivity for oxygen annealed NSLN crystal in comparison to as prepared NSLN and CLN specimens. The activation energies for ac-conductivity along the z-direction for NSLN and CLN crystals in the temperature range 500–1100 K are 1.03 eV and 0.96 eV, respectively.     

Characterization of luminescent chromophore obtained from silica spheres

Blue light emitting chromophores have been separated from silica spheres by soaking them into acetone for 120 days. The luminescent chromophores were not obtained from other solvents, including ether, methanol, ethanol, 2-propanol, chloroform and tetrahydrofuran. According to the Fourier transform infrared spectrum, the luminescent material is composed of C–OH, –CH₂, –CH₃, C=O, and Si–O–Si. UV–visible absorption peak of the chromophore is at 5.17 eV (240 nm). Field emission scanning electron microscope images show small cracks on the surface of aged spheres. The luminescence peak was at 2.81 eV (441 nm) for excitation energy between 3.88 and 3.35 eV and slightly shifted toward lower energy for excitation energy lower than 3.35 eV. The deconvoluted luminescent spectrum shows two emission bands at 3.08 and 2.74 eV, which are well-matched the oxygen deficient center model. Compared to the absorption peak (5.17 eV) and the emission peak (2.81 eV), large Stokes shift (2.36 eV) is observed.     

Near-infrared photoluminescence and thermally stimulated current in Cu3Ga5Se9 layered crystals: A comparative study

Near-infrared photoluminescence (PL) and thermally stimulated current (TSC) spectra of Cu₃Ga₅Se₉ layered crystals grown by Bridgman method have been studied in the photon energy region of 1.35–1.46 eV and the temperature range of 15–115 K (PL) and 10–170 K (TSC). An infrared PL band centered at 1.42 eV was revealed at T = 15 K. Radiative transitions from shallow donor level placed at 20 meV to moderately deep acceptor level at 310 meV were suggested to be the reason of the observed PL band. TSC curve of Cu₃Ga₅Se₉ crystal exhibited one broad peak at nearly 88 K. The thermal activation energy of traps was found to be 22 meV. An energy level diagram demonstrating the transitions in the crystal band gap was plotted taking account of results of PL and TSC experiments conducted below room temperature.     

Spectroscopic characterizations of individual single-crystalline GaN nanowires in visible/ultra-violet regime

Spectroscopic investigations of individual single-crystalline GaN nanowires with a lateral dimensions of ～30–90 nm were performed using the spatially resolved technique of electron energy-loss spectroscopy in conjunction with scanning transmission electron microscope showing a 2-Å electron probe. Positioning the electron probe upon transmission impact and at aloof setup with respect to the nanomaterials, we explored two types of surface modes intrinsic to GaN, surface exciton polaritons at ～8.3 eV (～150 nm) and surface guided modes at 3.88 eV (～320 nm), which are in visible/ultra-violet spectral regime above GaN bandgap of ～3.3 eV (～375 nm) and difficult to access by conventional optical spectroscopies. The explorations of these electromagnetic resonances might expand the current technical interests in GaN nanomaterials from the visible/UV range below ～3.5 eV to the spectral regime further beyond.     

Optical properties and structural characteristics of ZnO thin films grown on a-plane sapphire substrates by plasma-assisted molecular beam epitaxy

We investigated structural and optical properties of ZnO thin films grown on (112?0) a-plane sapphire substrates using plasma-assisted molecular beam epitaxy. Negligible biaxial stress in ZnO thin films is due to the use of (112?0) a-plane sapphire substrates and slow substrate cooling. The 14 K photoluminescence spectrum shows a blueshift of energy positions compared with ZnO single crystal. A donor with binding energy of 43 meV and an acceptor with binding energy of ～170 meV are identified by well-resolved photoluminescence spectra. A characteristic emission band at 3.320 eV (so-called A-line) is studied. Based on analysis from photoluminescence spectra, the origin of the A-line, it seems, is more likely an (e, A°) transition, in which defect behaves as an acceptor. The room-temperature photoluminescence is dominated by the FX at 3.307 eV, which is an indication of strongly reduced defect density in ZnO thin films.     

The near infrared cavity-enhanced absorption spectrum of methyl cyanide

The absorption spectrum of methyl cyanide (CH₃CN) has been measured in the near IR between 6000 and 8000 cm^?1 with a resolution of 0.12 cm^?1 using Fourier transform incoherent broadband cavity-enhanced absorption spectroscopy. The spectrum contains several weakly perturbed spectral regions; potential vibrational combination bands contributing to the spectrum are outlined. Line positions and cross-sections of CH₃CN between 6814 and 7067 cm^?1 have been measured at high-resolution of 0.001 cm^?1 using diode laser based off-axis cavity-enhanced absorption spectroscopy. A total of 4630 new absorption lines of CH₃CN are identified in this region. A value for the self-broadening coefficient has determined to be (3.3±0.2)×10^?3 cm^?1 mbar^?1 for one isolated line at 7034.171 cm^?1. Several line series have been identified in these regions and an autocorrelation analysis performed with a view to aiding future assignments of the rotational-vibrational transitions.     

Fine structure of far infrared spectrum of ethanol in the lowest OH-torsional vibrational trans-state (e0) of ethanol

In this report the spectroscopic results for far infrared Fourier transform spectrum corresponding to the b-type transitions within the lowest lying trans-substrate (e₀) have been presented. The calculated matrix elements connecting various K-levels suggest that ΔK = 1 transitions within the trans- subs-state should be quite strong but the transitions between the trans state to the gauche states would quite week (practically non-existent). This was also concluded by previous studies using microwave and millimeter wave regions (Pearson et al., 1982; Millar, 1995). The assignments were confirmed by direct observations at the spectrum and the agreement between the observed and calculated spectrum using precise energy levels reported by Pearson et al. (1982). All the strong ^RR and some ^RQ branch lines starting from K = 10 ← 9 through K = 24 ← 23 have been identified. State dependent expansion parameters for all the 15 sub-bands have been presented. These parameters can reproduce the experimental wave numbers within experimental uncertainty. An atlas for about 450 transition lines corresponding to transitions within the e₀ torsional–vibrational species has been prepared. To our knowledge this is the first time the high resolution far infra-red spectral region study for ethanol have been performed.     

Intrinsic excitons in 12CaO·7Al2O3

Unusual crystal structure of 12CaO·7Al₂O₃ is composed by a framework of positively charged nanocages, which enable accommodation of various negative ions (and even electrons) inside these cages. Different filling of cages leads to significant changes in electronic structure and as the result in luminescence properties, as well. Luminescence was studied using time-resolved spectroscopy in VUV in the temperature range from 6 to 300 K. Electron loaded samples exhibit UV luminescence band peaked at ～5 eV. The excitation spectrum of this emission has the onset at the energy gap value of 6.8 eV, and its decay is well described with the sum of two exponential functions with life-times of τ₁ = 3.7 ns and τ₂ = 29 ns, respectively. Its thermal quenching is well approximated by the sum of two Mott-Seitz type curves with the activation energies of 34 meV and 70 meV. Experimental results indicate that this luminescence is possibly due to radiative decay of two singlet self-trapped exciton states, which hole components are localized on two non-equivalent framework oxygens.     

Structural and photoluminescence investigation on the hot-wire assisted plasma enhanced chemical vapor deposition growth silicon nanowires

High density of silicon nanowires (SiNWs) were synthesized by a hot-wire assisted plasma enhanced chemical vapor deposition technique. The structural and optical properties of the as-grown SiNWs prepared at different rf power of 40 and 80 W were analyzed in this study. The SiNWs prepared at rf power of 40 W exhibited highly crystalline structure with a high crystal volume fraction, X_C of ～82% and are surrounded by a thin layer of SiO_x. The NWs show high absorption in the high energy region (E>1.8 eV) and strong photoluminescence at 1.73 to 2.05 eV (red–orange region) with a weak shoulder at 1.65 to 1.73 eV (near IR region). An increase in rf power to 80 W reduced the X_C to ～65% and led to the formation of nanocrystalline Si structures with a crystallite size of <4 nm within the SiNWs. These NWs are covered by a mixture of uncatalyzed amorphous Si layer. The SiNWs prepared at 80 W exhibited a high optical absorption ability above 99% in the broadband range between 220 and ～1500 nm and red emission between 1.65 and 1.95 eV. The interesting light absorption and photoluminescence properties from both SiNWs are discussed in the text.     

Improved measurements and analysis of the far-infrared spectrum of methanol-D1 (CH2DOH) arising from trans- (e0) to gauche- (e1 & o1) states

In this work the millimeter-wave (MMW) and far infrared (FIR) absorption spectrum for the asymmetrically deuterated Methanol (CH₂DOH) species measured recently at a temperature of −60 °C with better accuracy and signal/noise (S/N) ratio than known before has been assigned for transitions originating at the lowest lying trans- to gauche-states. The entire spectrum for 50–1200 cm⁻¹ has been re-recorded recently using the Synchrotron Radiation Source coupled with the Bruker Fourier Transform Infrared (FTIR) spectrometer with a resolution of about 0.001 cm⁻¹ or better. Complete spectrum has not been exploited a great deal but it helped to entangle overlapping lines in the present work. This also fills the gap remaining in the usual FTIR in the range 400–500 cm⁻¹. Hence it is expected to help the interacting partner for the Coriolis interaction encountered earlier. The assigned transitions mostly for the axial rotational angular momentum quantum number K + 1 ← K, both for R- and Q-sub bands for wide range of rotational angular momentum quantum number. The MMW spectrum has been recalibrated and assigned for a number of Q-branches. The assignments are confirmed rigorously using closed loop residual technique. The assigned ^rR and ^rQ lines have been analyzed in terms of polynomial expansion parameters. The new assignments are presented for about 750 transitions and a grand atlas of more than 1000 lines has been prepared which will be made available through the open source server at “research gate”. The present work should be useful in the area of astrophysical detection and further understanding of the energy relaxation pathways in the molecule.     

Electronic excitations and luminescence of SrAlF5 crystals doped with Ce3+ ions

This paper reports the results of a time-resolved photoluminescence and energy transfer processes study in Ce³⁺ doped SrAlF₅ single crystals. Several Ce³⁺ centers emitting near 4 eV due to 5d-4f transitions of Ce³⁺ ions substituting for Sr²⁺ in non-equivalent lattice sites were identified. The lifetime of these transitions is in the range of 25–35 ns under intra-center excitation in the energy region of 4–7 eV at T = 10 K. An effective energy transfer from lattice defects to dopant ions was revealed in the – 7–11 eV energy range. Both direct and indirect excitation channels are efficient at room temperature. Excitons bound to dopants are revealed at T = 10 K under excitation in the fundamental absorption region above 11 eV, as well as radiative decay of self-trapped excitons resulting in luminescence near 3 eV.     

Fourier Transform Infrared spectrum of the OCD bending mode in methanol-D1

The infrared (IR) spectra corresponding to OCD bending vibration of asymmetrically deuterated methanol species CH₂DOH have been recorded with a Fourier Transform Spectrometer. The spectrum shows a typical structure of a parallel a-type band. This is expected because the bending vibration mainly executed parallel to the symmetry axis The Q-branch lines are grouped closely around 896 cm⁻¹ and the P- and R-Branches show complex structure. Nonetheless it was possible to assign a-type P- and R-branch lines up to K value of 8 and J value up to about 20 in most cases. The Q-branch lines for higher K values can be followed to about J = 15, the presence of which confirmed the assignments. The observations suggest that in the OCD bend some energy levels are highly interacted by highly excited torsional state from the ground torsional state. A full catalogue is presented along with the effective molecular parameters. An intensity anomaly was also observed in the transitions. So far it has been possible to assign only transitions between e₀ ← e₀ states. Plausible explanations of intensity anomaly are presented. Lastly, a number of optically pumped far infrared (FIR) laser lines have been assigned either to exact or tentative quantum states. These assignments should prove valuable for production of new FIR laser lines.     

Evolution of interface properties of the Pentacene/Bi(0001) system

Using angle-resolved photoemission spectroscopy we measured the evolution of the electronic properties of the Pentacene (Pn)/Bi(0001) interface. From thickness dependent photoemission spectra of the substrate and Pn film we conclude that Pn growth is epitaxial. Pentacene highest occupied molecular orbital (HOMO) valence band features are identical for sub-monolayer (ML) as well as for thick films which suggests a thickness independent film morphology. The Pn/Bi interaction is weak and results in a lowering of the HOMO binding energy by 180 ± 5 meV and 80 ± 5 meV for the first and second MLs respectively. The interface dipole (ID) is fully developed over the first ～ 1.2 ML of Pn coverage and has a value of ID = 310 ± 10 meV. The hole injection barrier across the interface is Φ_h = 1.03 ± 0.01 eV.     

Optical properties of Cr/Fe(t)/MgO (0 0 1) thin films

In this work we report on the optical properties of single-crystalline iron thin films. For this, Cr-capped Fe films with thickness, t, in the range 30–300 Å were prepared on MgO (0 0 1) by DC magnetron sputtering, and then studied by optical absorption technique within the range from 1.0 to 3.6 eV. All measurements were carried out at room temperature using a fiber optics spectrophotometer. The intensity of the transmitted light decreases with increasing film thickness. The optical constants of the films are deduced from a model that considers the transmission of light by two absorbing films on an absorbing substrate. The absorption coefficient of the Fe films is also calculated from the transmission data. The absorption spectra show the following characteristics: (i) two large absorption peaks centered at about 1.20 and 2.65 eV; and (ii) a sharp step near 1.40 eV. These structures are associated with conventional interband transitions of the iron film.     

Photoluminescence study of polycrystalline CsSnI3 thin films: Determination of exciton binding energy

We report on the determination of exciton binding energy in perovskite semiconductor CsSnI₃ through a series of steady state and time-resolved photoluminescence measurements in a temperature range of 10–300 K. A large binding energy of 18 meV was deduced for this compound having a direct band gap of 1.32 eV at room temperature. We argue that the observed large binding energy is attributable to the exciton motion in the natural two-dimensional layers of SnI₄ tetragons in this material.     

Photocatalytic degradation of ciprofloxacin drug in water using ZnO nanoparticles

We report the synthesis of nanostructure ZnO semiconductor with ～2.1 nm diameter using a chemical precipitation method. The resulting nanoparticles were characterized by X-ray diffraction analysis (XRD), Fourier-transform infrared (FT-IR) spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The optical properties were investigated by UV–vis and fluorescence techniques. The absorption spectra exhibit a sharp absorption edge at ～334 nm corresponding to band gap of ～3.7 eV. The fluorescence spectra displayed a near-band-edge ultraviolet excitonic emission at ～410 nm and a green emission peak at ～525 nm, due to a transition of a photo-generated electron from the conduction band to a deeply trapped hole. The photocatalytic activity of the prepared ZnO nanoparticles has been investigated for the degradation of ciprofloxacin drug under UV light irradiation in aqueous solutions of different pH values. The results showed that the photocatalytic degradation process is effective at pH 7 and 10, but it is rather slow at pH 4. Higher degradation efficiency (～50%) of the drug was observed at pH 10 after 60 min. Photodegradation of the drug follows a pseudo-first-order kinetics.     

Growth-morphology-luminescence correlation in ZnO-containing nanostructures synthesized in different media

Zinc hydroxide particles were prepared by a two-step process employing zinc nitrate hexahydrate, urea, ethylene glycol, water and p-toluene-sulfonic acid monohydrate (p-TSA). We used different concentrations of the reactants as well as different volume ratios of the solvents. ZnO particles were obtained by thermal treatment of the reaction products at two different temperatures: 350 °C and 500 °C. The samples were characterized by scanning field emission electron microscopy (SEM), X-ray diffraction (XRD) spectroscopy, BET analysis, thermogravimetry (TG) analysis and photoluminescence (PL) spectroscopy. It was found that after the thermal treatment particles become smaller, with the p-TSA concentration strongly affecting the morphology of the particles. Luminescence properties of the samples probed by PL at 8 K and room temperature exhibited a remarkable correlation with specimens′ nanomorphology. Luminescent features at ～2.0–2.2 eV, ～2.4–2.5 eV, ～2.65 eV, ～2.9 eV, ～3.0–3.1 eV and ～3.3 eV were observed in most specimens, although their relative intensity and temperature dependence were specific to an individual group of samples vis-à-vis their growth history and morphology.     

Low temperature adsorption and site-conversion process of CO on the Ni(111) surface

Low-temperature (25 K) adsorption states and the site conversion of adsorbed CO between the ontop and the hollow sites on Ni(111) were studied by means of temperature programmed desorption and infrared reflection absorption spectroscopy. The activation energy and pre-exponential factor of desorption were estimated to be 1.2 eV and 2.6 × 10¹³ s^? 1, respectively, in the limit of zero coverage. At low coverage, CO molecules preferentially adsorbed at the hollow sites below 100 K. With increasing temperature, the ontop sites were also occupied. Using a van't Hoff plot, the enthalpy and the entropy differences between the hollow and ontop CO were estimated to be 36 meV and 0.043 meV K^? 1, respectively, and the vibrational entropy difference was estimated to be 0.085 meV K^? 1. The positive entropy difference was the result of the low-energy frustrated translational mode of the ontop CO, which was estimated to be 4.6 ± 0.3 meV. With the harmonic approximation, the upper limit of the activation energy of site hopping from ontop sites to hollow sites was estimated to be 61 meV. In addition, it was suggested that the activation energy of hollow-to-hollow site hopping via a bridge site was less than 37 meV.     

Vacuum Ultraviolet Absorption Spectrum of Difluoromethane Reinvestigated

The vacuum ultraviolet (VUV) absorption spectrum of difluoromethane (CH₂F₂) was studied using synchrotron radiation from the storage ring Indus-1, Indore, India. Spectra were recorded in the spectral region 1050–1500 Å (～8.3–11.8 eV) at a resolution of 1.5 Å. Three absorption band systems were observed in this region. Overall features observed are in good agreement with previously published work. Some discrepancies in assignments of the observed vibronic bands carried out by previous workers have been resolved. The observed bands have been classified in terms of Rydberg series.     

New measurements and analysis of the far-infrared spectrum of CH2DOH in the lowest torsional vibrational state (e0)

In this work the far infrared (FIR) absorption spectrum has been measured for the asymmetrically mono deuterated Methanol (CH₂DOH) species in the wavenumber range of 15–1200 cm⁻¹ better accuracy and signal/noise ratio than known before. Assignments have been made for b-type transitions in the lowest lying torsional vibrational state trans-(e₀) for a wide range of rotational angular momentum. The assignments have been rigorously confirmed by the residual loop defect methods. The ^rR–branch wavenumbers are analyzed by the usual state dependent expansion parameters and the Q-Branch origins. These origins have been used to calculate the torsional and torsional-rotation interaction contributions. These findings are in good agreement with predicted from the Hamiltonian model described in recent publications. A large number of assignments have also been made in the millimeter wave spectrum recorded earlier and thereby evaluated the asymmetry splitting parameters for 4 different axial rotational angular momentum quantum numbers. The analysis and interpretation of the spectra are reported. New assignments for about 260 transitions are included the text and a catalog of about 1500 transitions belonging to the e₀ species is prepared (Appendix 1) and is made available through the open server in “Research Gate” and will be freely available to others.