Tunneling magnetoresistance in exchange-biased CoFeB/AlOx/Co/IrMn junctions

A series of exchange-biased magnetic tunneling junctions (MTJs) were made in an in-plane deposition field (h) = 500 Oe. The deposition sequence was Si(1 0 0)/Ta(30 Å)/CoFeB(75 Å)/AlO_x(d Å)/Co(75 Å)/IrMn(90 Å)/Ta(100 Å), where d was varied from 12 Å to 30 Å. The MTJ was formed by the cross-strip method with a junction area of 0.0225 mm². The tunneling magnetoresistance (ΔR/R) of each MTJ was measured. The high-resolution cross-sectional transmission electron microscopic (HR X-TEM) image shows the very smooth interface and clear microstructure. X-ray diffraction (XRD) demonstrates that the IrMn layer of the MTJ exhibits a (1 1 1) texture. From the results (ΔR/R) increases from 17% to 50%, as d increases from 12 Å to 30 Å. The tunneling resistance (R_o) of these junctions ranges from 150 Ω to 250 Ω. The exchange-biasing field (H_ex) of the MTJ is 50-95 Oe. Finally, the saturation resistance (R_s) was measured as a function of the angle (α) of rotation, where α is the angle between h and the in-plane saturation field (H_s) = 1.1 kOe. The following figure presents the dependence of R_s on α, instead of originally expected independence, the curve actually varies with a period of π.     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

Microstructure and magnetic properties of nanocomposite FePt/MgO and FePt/Ag films

An in-plane magnetic anisotropy of FePt film is obtained in the MgO 5 nm/FePt t nm/MgO 5 nm films (where t=5, 10 and 20 nm). Both the in-plane coercivity (H_c∥) and the perpendicular magnetic anisotropy of FePt films are increased when introducing an Ag-capped layer instead of MgO-capped layer. An in-plane coercivity is 3154 Oe for the MgO 5 nm/FePt 10 nm/MgO 5 nm film, and it can be increased to 4846 Oe as a 5 nm Ag-capped layer instead of MgO-capped layer. The transmission electron microscopy (TEM)-energy disperse spectrum (EDS) analysis shows that the Ag mainly distributed at the grain boundary of FePt, that leads the increase of the grain boundary energy, which will enhance coercivity and perpendicular magnetic anisotropy of FePt film.     

Controlled fabrication of nano-scale double barrier magnetic tunnel junctions using focused ion beam milling method

The controlled fabrication method for nano-scale double barrier magnetic tunnel junctions (DBMTJs) with the layer structure of Ta(5)/Cu(10)/Ni₇₉Fe₂₁(5)/Ir₂₂Mn₇₈(12)/Co₆₀Fe₂₀B₂₀(4)/Al(1)–oxide/Co₆₀Fe₂₀B₂₀(6)/Al(1)–oxide/Co₆₀Fe₂₀B₂₀(4)/Ir₂₂Mn₇₈(12)/Ni₇₉Fe₂₁(5)/Ta(5) (thickness unit: nm) was used. This method involved depositing thin multi-layer stacks by sputtering system, and depositing a Pt nano-pillar using a focused ion beam which acted both as a top contact and as an etching mask. The advantages of this process over the traditional process using e-beam and optical lithography in that it involve only few processing steps, e.g. it does not involve any lift-off steps. In order to evaluate the nanofabrication techniques, the DBMTJs with the dimensions of 200 nm×400 nm, 200 nm×200 nm nano-scale were prepared and their R–H, I–V characteristics were measured.     

Seedlayer interface enhanced magnetic anisotropy in CoPt (0 0 0 2)-textured films

The effects of interface roughness of Ta seedlayer on the structural and magnetic properties of Co₇₂Pt₂₈(20 nm)/Ru(30 nm)/Pt(2 nm)/Ta(5 nm)/glass were investigated. Uniaxial perpendicular magnetic anisotropy (8.6×10⁶ ergs/cc), coercivity (5.5 kOe) and nucleation field (−2.8 kOe) in the Co₇₂Pt₂₈ thin film sputter-deposited on relatively smooth surface of Ta seedlayer were achieved. The results showed that relatively smoother interface roughness of Ta seedlayer improved the CoPt/Ru (0 0 0 2) texture and magnetic properties.     

Magnetic and structural properties of CaO–SiO2–P2O5–Na2O–Fe2O3 glass ceramics

Magnetic properties of glass ceramics derived from glasses with composition 41CaO·(52−x)SiO₂·4P₂O₅·xFe₂O₃·3Na₂O (2?x?10 mol% iron oxide (Fe₂O₃)) are reported. Structural investigation revealed the presence of nanocrystalline magnetite phase in the heat-treated samples containing x?2 mol% Fe₂O₃. Magnetic hysteresis cycles of the glass-ceramic samples were obtained with a maximum applied field of ±20 kOe as well as a low field of ±500 Oe, in order to evaluate the potential of these glass ceramics for hyperthermia treatment of cancer. Samples with x>2 mol% of iron oxide exhibited magnetic behavior similar to soft magnetic materials with low coercivity. The evolution of magnetic properties in these samples as a function of iron oxide molar concentration is correlated with the amount and crystallite size of magnetite phase present in them.     

Monolayer deposition of L10 FePt nanoparticles via electrospray route

The deposition monolayers of L1₀ FePt nanoparticles via an electrospraying method and the magnetic properties of the deposited film were studied. FePt nanoparticles in a size of around 2.5 nm in diameter, prepared by a liquid process, were used as a precursor. The size of the deposited particles can be controlled up to 35 nm by controlling the sprayed droplet size that is formed by adjusting the precursor concentration and the precursor flow rate. The droplets were heated in a tubular furnace at a temperature of up to 900 °C to remove all organic compounds and to transform the FePt particles from disordered face centered cubic to an ordered FCT phase. Finally, the particles were deposited in the form of a monolayer film on a silicon substrate by electrostatic force and characterized by scanning electron microscopy. The monolayer of particles was obtained by the high charge on particles obtained during the electrospraying process. The magnetic properties of the monolayer were investigated by magneto-optic Kerr effect measurements. Coercivity up to 650 Oe for a film consisting of 35 nm L1₀ FePt nanoparticles was observed after heat treatment at a temperature of 800 °C.     

Evolution of magnetic and microstructural properties of thick sputtered NdFeB films with processing temperature

Ta (100 nm)/NdFeB (5 μm)/Ta (100 nm) films have been deposited onto Si substrates using triode sputtering (deposition rate ∼18 μm/h). A 2-step procedure was used: deposition at temperatures up to 400 °C followed by ex-situ annealing at higher temperatures. Post-deposition annealing temperatures above 650 °C are needed to develop high values of coercivity. The duration of the annealing time is more critical in anisotropic samples deposited onto heated substrates than in isotropic samples deposited at lower temperatures. For a given set of annealing conditions (750 °C/10′), high heating rates (?2000 °C/h) favour high coercivity in both isotropic and anisotropic films. The shape and size of Nd₂Fe₁₄B grains depend strongly on the heating rate.     

Magnetic and structural properties of laminated Co65Fe35 films

We report on coercivity mechanisms in Co₆₅Fe₃₅ films. Using a unique High Target Utilisation Sputtering System (HiTUS) sputtering system we have produced a range of samples with controlled grain size in the range 6-30 nm. This has enabled an evaluation of the effects of different seed layers (Ru, Cu, Ta and Mg) and the effects of lamination of the films. We found that in 100 Å single-layer films the coercivity rises abruptly from 29 to 90 Oe with grain size. We found that samples with Cu or Ru seed layers show the largest reduction in coercivity. The effects of lamination are more complex since it leads to a reduction in grain size whereas coercivity increases. We believe this is due to RKKY coupling through the metallic interlayers.     

Magnetic and bioactivity evaluation of ferrimagnetic ZnFe2O4 containing glass ceramics for the hyperthermia treatment of cancer

Glass ceramics of the composition xZnO·25Fe₂O₃·(40−x)SiO₂·25CaO·7P₂O₅·3Na₂O were prepared by the melt-quench method using oxy-acetylene flame. Glass-powder compacts were sintered at 1100 °C for 3 h and then rapidly cooled at −10 °C. X-ray diffraction (XRD) revealed 3 prominent crystalline phases: ZnFe₂O₄, CaSiO₃ and Ca₁₀(PO₄)₆(OH)₂. Vibrating sample magnetometer (VSM) data at 10 KOe and 500 Oe showed that saturation magnetization, coercivity and hence hysteresis area increased with the increase in ZnO content. Nano-sized ZnFe₂O₄ crystallites were of pseudo-single domain structure and thus coercivity increased with the increase in crystallite size. ZnFe₂O₄ exhibited ferrimagnetism due to the random distribution of Zn²⁺ and Fe³⁺ cations at tetrahedral A sites and octahedral B sites. This inversion/random distribution of cations was probably due to the surface effects of nano-ZnFe₂O₄ and rapid cooling of the material from 1100 °C (thus preserving the high temperature state of the random distribution of cations). Calorimetric measurements were carried out using magnetic induction furnace at 500 Oe magnetic field and 400 KHz frequency. The data showed that maximum specific power loss and temperature increase after 2 min were 26 W/g and 37 °C, respectively for the sample containing 10% ZnO. The samples were immersed in simulated body fluid (SBF) for 3 weeks. Scanning electron microscope (SEM), energy dispersive spectroscopy (EDX) and XRD results confirmed the growth of precipitated hydroxyapatite phase after immersion in SBF, suggesting that the ferrimagnetic glass ceramics were bioactive and could bond to the living tissues in physiological environment.     

Effect of Co underlayer on soft magnetic properties and microstructure of FeCo thin films

High saturation magnetization soft magnetic FeCo (=Fe₆₅Co₃₅) films were prepared using a thin Co underlayer. The FeCo/Co films exhibited a well-defined in-plane uniaxial anisotropy with easy axis coercivity (H_ce) of 10 Oe and hard axis coercivity (H_ch) of 3 Oe, and a half reduction of H_c with H_ce=4.8 Oe and H_ch=1.0 Oe was obtained when the composition was adjusted to 25 at% Co. The effective permeability of the films remains flat around 250 to 800 MHz. The saturation magnetostriction was 5.2×10⁻⁵ and the intrinsic stress was 0.8 GPa in FeCo single layer, both were slightly reduced by Co underlayer. The Co underlayer changed the preferred orientation of the FeCo films from (2 0 0) to (1 1 0) but more significantly, reduced the average grain size from ∼74 to ∼8.2 nm. It also reduced the surface roughness from 2.351 to 0.751 nm. The initial stage and interface diffusion properties were examined by TEM and XPS.     

The structure and magnetic properties of Zn1−xNixFe2O4 ferrite nanoparticles prepared by sol–gel auto-combustion

Zn_1−xNi_xFe₂O₄ ferrite nanoparticles were prepared by sol–gel auto-combustion and then annealed at 700 °C for 4 h. The results of differential thermal analysis indicate that the thermal decomposition temperature is about 210 °C and Ni–Zn ferrite nanoparticles could be synthesized in the self-propagating combustion process. The microstructure and magnetic properties were investigated by means of X-ray diffraction, scanning electron microscope, and Vibrating sample magnetometer. It is observed that all the spherical nanoparticles with an average grain size of about 35 nm are of pure spinel cubic structure. The crystal lattice constant declines gradually with increasing x from 0.8435 nm (x=0.20) to 0.8352 nm (x=1.00). Different from the composition of Zn_0.5Ni_0.5Fe₂O₄ for the bulk, the maximum M_s is found in the composition of Zn_0.3Ni_0.7Fe₂O₄ for nanoparticles. The H_c of samples is much larger than the bulk ferrites and increases with the enlarging x. The results of Zn_0.3Ni_0.7Fe₂O₄ annealed at different temperatures indicate that the maximum M_s (83.2 emu/g) appears in the sample annealed at 900 °C. The H_c of Zn_0.3Ni_0.7Fe₂O₄ firstly increases slightly as the grain size increases, and presents a maximum value of 115 Oe when the grains grow up to about 30 nm, and then declines rapidly with the grains further growing. The critical diameter (under the critical diameter, the grain is of single domain) of Zn_0.3Ni_0.7Fe₂O₄ nanoparticles is found to be about 30 nm.     

TaN underlayers for spin valves deposited directly on top of Si substrates

TaN underlayers for spin valves were studied, which were deposited directly on top of Si substrates. The experimental results obtained with the TaN underlayer were compared with those obtained with other (Ta, Mo, and MoN) underlayers. The spin valve structure was Si/Underlayer(tÅ)/NiFe(21 Å)/CoFe(28 Å)/Cu(22 Å)/CoFe(18 Å)/IrMn(65 Å)/Ta(25 Å). The TaN underlayer for a spin valve element exhibited good adhesion to the Si substrate. The XRD patterns of the annealed TaN on bare Si substrate at 900 °C showed no Ta silicide phases, which suggests that the TaN layer may also be used as a diffusion barrier between Si substrate and the ensuing spin valve active layers, as well as an underlayer. A spin valve element having TaN underlayer deposited directly on top of a Si substrate showed a high MR ratio of about 8.3% after annealing at 200 °C. It is concluded that it is advantageous to use a TaN underlayer if one wants to fabricate spin valve elements directly on top of Si substrates.     

High-frequency characteristics of CoFeVAlONb thin films

High-frequency characteristics of CoFeVAlONb thin films were studied. A thin film of Co_43.47Fe_35.30V_1.54Al_5.55O_9.93Nb_4.21 is observed to exhibit excellent magnetic properties; magnetic coercivity of 1.24 Oe, uniaxial in-plane anisotropy field of 66.99 Oe, and saturation magnetization of 19.8 kG. The effective permeability of the film is as high as 1089 and is stable up to 1.8 GHz, and with ferromagnetic resonance over 3 GHz. This film also has very high electrical resistivity of about 628 μΩ cm. These superior properties make it ideal for high-frequency magnetic applications.     

Magnetic properties of field-annealed FeCo thin films

Fe₅₀Co₅₀ thin films with thickness of 30 and 4 nm have been produced by rf sputtering on glass substrates, and their surface has been observed with atomic force microscopy (AFM) and magnetic force microscopy (MFM); MFM images reveal a non-null component of the magnetization perpendicular to the film plane. Selected samples have been annealed in vacuum at temperatures of 300 and 350 °C for times between 20 and 120 min, under a static magnetic field of 100 Oe. DC hysteresis loops have been measured with an alternating gradient force magnetometer (AGFM) along the direction of the field applied during annealing and orthogonally to it. Samples with a thickness of 4 nm display lower coercive fields with respect to the 30 nm thick ones. Longer annealing times affect the development of a harder magnetic phase more oriented off the film plane. The field applied during annealing induces a moderate magnetic anisotropy only on 30 nm thick films.     

Soft magnetic properties of FeCo films with Co underlayer

Bilayered Fe₆₅Co₃₅ (=FeCo)/Co films were prepared by facing targets sputtering with 4πM_s∼24 kg. The soft magnetic properties of FeCo films were induced by a Co underlayer. H_c decreased rapidly when the Co underlayer was 2 nm or more. The films showed well-defined in-plane uniaxial anisotropy with the typical values of H_ce=10 Oe and H_ch=3 Oe, respectively. High frequency characteristics of the films show the films can work at 0.8 GHz with real permeability as high as 250.     

Multiple antiferromagnet/ferromagnet interfaces as a probe of grain-size-dependent exchange bias in polycrystalline Co/Fe50Mn50

We have used ferromagnet/antiferromagnet/ferromagnet trilayers and ferromagnet/antiferromagnet multilayers to probe the grain size dependence of exchange bias in polycrystalline Co/Fe₅₀Mn₅₀. X-ray diffraction and transmission electron microscopy show that the Fe₅₀Mn₅₀ (FeMn) grain size increases with increasing FeMn thickness in the Co (30 Å)/FeMn system. Hence, in Co(30 Å)/FeMn(t_AF Å)/Co(30 Å) trilayers the two Co layers sample different FeMn grain sizes at the two antiferromagnet/ferromagnet interfaces. For FeMn thicknesses above 100 Å, where simple bilayers have a thickness-independent exchange bias, we are therefore able to deduce the influence of FeMn grain size on the exchange bias and coercivity (and their temperature dependence) simply by measuring trilayer and multilayer samples with varying FeMn thicknesses. This can be done while maintaining the (1 1 1) orientation, and with little variation in interface roughness. Increasing the average grain size from 90 to 135 Å results in a fourfold decrease in exchange bias, following an inverse grain size dependence. We interpret the results as being due to a decrease in uncompensated spin density with increasing antiferromagnet grain size, further evidence for the importance of defect-generated uncompensated spins.     

Electron scattering characteristics of polycrystalline metal transition films by in-situ electrical resistance measurements

In-situ electrical resistance measurements were performed to obtain the scattering characteristics of very thin polycrystalline metal transition magnetic alloys grown by ion beam deposition (IBD) on specific underlayers. The experimental curves show size effects at small film thicknesses and important differences between Co₈₅Fe₁₅ and Ni₈₁Fe₁₉ thin layers grown on identical underlayers of Ta70 Å/Ru13 Å. The largest difference was observed in Ni₈₁Fe₁₉ films grown on underlayers of amorphous Ta70 Å. The experimental curves of electrical resistivity/conductivity variation with layer thickness were well fit within the Mayadas and Shatzkes (M-S) model, assuming specific formulations for grain growth with layer thickness.     

Exchange bias and negative magnetoresistance in [Co/Bi/Co]/IrMn thin films]

The artificial control of grain-boundary resistance and its contribution to magnetic and magneto-transport properties in [Co(3 nm)/Bi(2.5 nm)/Co(3 nm)]Ir₂₀Mn₈₀(12 nm) thin films that exhibit exchange bias is studied. Transverse magnetoresistance (MR) loops exhibit a negative MR in thin films grown by magnetron sputtering on Si/SiN_x(100 nm) substrates. This negative MR effect is of the giant-MR (GMR) type, although its magnitude is less than 1%. A considerable exchange bias (EB) effect is observed only at lower temperatures, where both, GMR and isothermal magnetization loops exhibit a shift of −600 Oe at 5 K.     

Magnetic layer thickness dependence of magnetization reversal in electrodeposited CoNi/Cu multilayer nanowires

The magnetization reversal of electrodeposited CoNi/Cu multilayer nanowires patterned in an array using a hole template has been investigated. The reversal mode is found to depend on the CoNi layer thickness t(CoNi); with increasing t(CoNi) a transition occurs from coherent rotation to a combination of coherent and incoherent rotation at around t(CoNi)=51 nm. The reversal mode has been identified using the magnetic hysteresis loops measured at room temperature for CoNi/Cu nanowires placed at various angles between the directions of the nanowire axis and external fields using a vibrating sample magnetometer. The nanowire samples have a diameter of ∼250 nm and constant Cu layer thickness of 4.2 nm with various t(CoNi) ranging from 6.8 nm to 7.5 μm. With increasing t(CoNi), the magnetic easy axis moves from the direction perpendicular to nanowires to that parallel to the nanowires at around t(CoNi)=51 nm, indicating a change in the magnetization reversal mode. The reversal mode for the nanowires with thin disk-shaped CoNi layers (t(CoNi)=6.8, 12 and 17 nm) is of a coherent rotation type, while that for long rod-shaped CoNi layers (t(CoNi)=150 nm, 1.0, 2.5 and 7.5 μm) can be consistently explained by a combination of coherent rotation and a curling mode. The effects of dipole–dipole interactions between nanowires and between adjacent magnetic layers in each nanowire on the reversal process have been discussed.