碳纳米管/四针状纳米氧化锌复合涂层的电磁波吸收特性

以碳纳米管(CNT)和四针状纳米氧化锌(NT-ZnO)混合物作为吸收剂、环氧树脂(EP)为黏结剂制备吸波涂层,研究不同CNT和NT-ZnO含量对吸波性能的影响.采用三次刷涂后,发现当CNT含量达到12%,NT-ZnO的含量为8%、涂层厚度为1·5mm时,吸波涂层的最小反射率为-23·07dB,小于-10dB的吸波带宽为5GHz,涂层的面密度2kg/m2·复合涂层的吸波性能比纯CNT和纯NT-ZnO涂层有显著的提高,并对其吸波机理进行了分析.     

四针状氧化锌/炭黑复合吸波材料吸波性能的研究

利用四针状氧化锌和炭黑为吸收剂,硅橡胶为基体,制备了一种复合吸波材料,并探究了不同含量的炭黑、四针状氧化锌以及复合材料的厚度对其吸波性能的影响。同时使用了扫描电子显微镜、矢量网络分析仪等仪器对不同质量分数的复合吸波材料样品进行微观形貌和电磁性能的表征。结果表明,在一定范围内,样品的厚度、炭黑的含量和四针状氧化锌的含量增加,会提高样品的吸波性能,当样品的厚度为2 mm,碳粉和四针状氧化锌的质量分数含量分别为8%和10%时,复合吸波材料的最小反射损耗值可以达到-14.68 dB,符合当下吸波材料轻薄宽频的发展趋势。该复合材料具有吸收剂含量低、轻薄、弹性大等优点,在电磁屏蔽领域具有潜在的应用前景。     

微弧等离子喷涂碳纳米管/纳米Al2O3-TiO2复合涂层的吸波性能研究

将碳纳米管与纳米Al₂O₃-TiO₂陶瓷粉末超声共混制备了碳纳米管/纳米Al₂O₃-TiO₂复合粉末,测试了复合粉末在2—18GHz波段的电磁参数.研究表明：随着碳纳米管质量分数的增加,碳纳米管/纳米Al₂O₃-TiO₂复合粉末的复介电常数和损耗角不断增大.当碳纳米管质量分数和厚度增加时,复合粉末对电磁波的反射率峰值先增加后减小,而谐振频率不断向低频移动.采用微弧等离子喷涂制备了7wt%碳纳米管/纳米Al₂O₃-TiO₂复合吸波涂层,当厚度为1.5mm时,涂层最小反射率为-24.0dB,当厚度为2.0mm时,涂层小于-10dB的频带宽为3.60GHz,当温度为500℃高温时,1.0mm厚的涂层最小高温反射率为-12.2dB,小于-10dB频带宽为2.0GHz.复合涂层的实际厚度D与理论厚度d呈线关系：d=0.898D+0.515. 关键词： 等离子喷涂 碳纳米管 2O₃-TiO₂')" href="#">纳米Al₂O₃-TiO₂ 吸波性能     

基于磁/电介质混合型基体的宽带超材料吸波体的设计与制备

本文设计了一种基于磁/电介质混合型基体的宽带超材料吸波体, 吸波体基本单元由电阻膜、磁/电介质混合型基体以及金属背板组成. 采用时域有限差分法对超材料吸波体吸波性能进行了仿真, 使用遗传算法优化了反射率小于-10 dB的带宽. 仿真结果表明, 当超材料吸波体厚度为2.5 mm时, 在7.8–18 GHz频率范围内的反射率小于-10 dB, 具有厚度薄、宽带、极化不敏感等优点. 通过等效电路模型对其工作机理进行了分析与讨论. 最后制备样品进行测试, 测试结果与仿真结果一致.     

宽频带碳团簇型吸波涂层的制备与性能

为满足对吸波涂层薄、轻、宽的要求,通过吸波涂层的优化设计,制备了密度较低的宽频带碳团簇型吸波涂层.该涂层为三层结构,总厚度为2.10 mm,在8～12.4GHz频率范围内,对微波的最小反射率为-42dB,其中反射率小于-10dB的工作频带达90%以上,且性能稳定,有较好的实用前景.     

碳纳米管复合吸波涂层微波吸收性能的模拟计算

如何利用碳纳米管复合吸波涂层的参数进行吸波性能优化是电磁屏蔽研究的热点之一.涂层参数对吸波性能影响的研究主要停留在实验探索阶段,而碳纳米管的结构参数对吸波性能影响的研究鲜有报道.因此,从微观结构层次研究涂层参数对吸波性能的影响有重要意义.基于多壁碳纳米管的等效电路,利用碳纳米管结构参数与等效电路各元件参数的关系,研究了碳纳米管损耗微波的机理,建立了碳纳米管结构参数与微波反射率的关系式.根据此关系式,利用Matlab软件模拟计算了碳纳米管管长、管径、涂层中碳纳米管的含量以及涂层厚度对微波反射率的影响.模拟计算结果表明:涂层的微波反射率随碳纳米管含量变化的模拟曲线与实验结果符合;碳纳米管含量和厚度是影响吸收峰位置和吸收强度的重要参量,而碳纳米管直径和长度是主要影响吸收峰强度的参量.     

圆环单元FSS对改善吸波体雷达吸波特性的影响

设计了圆环单元的频率选择表面（FSS）结构,并将该结构置于吸波材料中构成了复合吸波结构。利用谱域法对该结构进行数值模拟,计算出频率为2～16GHz微波波段的反射系数,并研究了圆环单元尺寸和排布周期对其吸波特性的影响。结果表明：当圆环单元FSS的单元间距为10mm,单元尺寸为3．3mm时,其共振频率的反射率由-8．15dB降低为-14．54dB,-5dB吸波带宽由1．2GHz拓展为3．05GHz;且随圆环单元尺寸增大,共振反射率增加;随单元排列周期增加,吸波材料带宽增大。结果表明,利用FSS可以明显改善吸波材料涂层的吸波性能,通过凋整相关参数可以获得所需的复合吸波结构,拓展FSS在吸波材料中的应用范围。     

含螺旋单元频率选择表面的宽频带强吸收复合吸波体

设计和制备了含螺旋单元频率选择表面吸波片的三层复合吸波体,上层和下层均为磁性吸波片,中间层为带缺口的螺旋单元频率选择表面.复合吸波体在总厚度分别为1.4,1.7和2.0 mm时,其反射率在-10d B以下的频带宽度分别达到了9.29,6.69和7.11 GHz,与不含有频率选择表面的吸波体相比较(其他参数相同),-10d B以下反射率带宽分别提高了159.5%,69.3%和129.4%,复合吸波体在总厚度低于吸波体时,也取得了更好的反射效果.带缺口圆螺旋单元的频率选择表面嵌入吸波体中,引入了额外的吸收频带,拓宽了吸波体的反射率频带宽度.仿真分析表明嵌入频率选择表面能够改善吸波体的阻抗匹配性,进而影响其反射率.     

一种基于3D打印技术的结构型宽频吸波超材料

设计了一种三层宽频吸波超材料,其表层和中间层为单元尺寸不同的周期阵列结构,底层为吸波平板结构,优化后的总厚度仅为4.7 mm,并采用三维(3D)打印技术成功制备了该吸波超材料.吸波体反射率测试结果表明,在电磁波垂直入射条件下,宽频吸收峰分别出现在5.3和14.1 GHz,两峰叠加使得其在4-18 GHz频率范围内反射损耗均小于-10 dB.采用S参数反演法计算了每一层的等效电磁参数,并利用多层结构反射率公式推导得出该模型的理论反射率,理论计算结果与实测结果基本一致.通过研究能量损耗、电场分布和磁场分布揭示了吸波机理,分析表明该吸波体的宽频吸收效果源于三层结构产生的吸收带宽叠加.本文提出的吸波超材料具有良好的宽频吸收效果,尤其在低频范围吸波性能较佳,结合3D打印快速成型技术,可获得结构精细的三层吸波超材料,具有重要的实际应用价值和广阔的应用前景.     

吸波材料研究现状及碳团簇型吸波材料设计

简要介绍了铁氧体吸波材料,手性材料,金属微粉吸波材料,导电高聚物材料,多晶铁纤维材料,纳米材料和智能隐身材料的研究和应用现状.并根据吸波材料工作原理,进行碳团簇型吸波材料实验研究,结果显示,所制样品有很好的吸波性能,在总厚度为2.11 mm的情况下,在8.2～12.4 GHz频带内,最大反射衰减可达-29dB,有效频宽占总带宽的100%,基本达到实用水平.     

Microwave absorption properties of a wave-absorbing coating employing carbonyl-iron powder and carbon black

To prevent serious electromagnetic interference, a single-layer wave-absorbing coating employing complex absorbents composed of carbonyl-iron powder (CIP) and carbon black (CB) with epoxy resin as matrix was prepared. The morphologies of CIP and CB were characterized by scanning electron microscope (SEM) and transmission electron microscope (TEM), respectively. The electromagnetic parameters of CIP and CB were measured in the frequency range of 2-18 GHz by transmission/reflection technology, and the electromagnetic loss mechanisms of the two particles were discussed, respectively. The microwave absorption properties of the coatings were investigated by measuring reflection loss (RL) using arch method. The effects of CIP ratio, CB content and thickness on the microwave absorption properties were discussed, respectively. The results showed that the higher thickness, CIP or CB content could make the absorption band shift towards the lower frequency range. Significantly, the wave-absorbing coating could be applied in different frequency ranges according to actual demand by controlling the content of CIP or CB in composites.     

Electromagnetic and microwave absorption properties of carbonyl iron and carbon fiber filled epoxy/silicone resin coatings

The microwave electromagnetic properties of carbonyl-iron particles as magnetic absorber and carbon fiber as conductive absorber filled insulating epoxy/silicone resin coatings were investigated. The complex permittivity of the coatings increased while the complex permeability remained almost constant in the frequency range of 2–18 GHz, when the carbon fiber content was increased and the carbonyl-iron content kept constant. The minimum reflection loss of the coatings shifted to the lower frequency region by increasing the carbon fiber content or coating thickness. When the content of carbonyl iron was 65 wt% and carbon fiber was 2 wt%, the reflection loss below −10 dB can obtain in the frequency range of 8–18 GHz with coating thickness being 1 mm.     

Preparation and microwave absorption properties of electroless Co-P-coated nickel hollow spheres

Co-P-coated nickel hollow spheres (NHSs) were prepared by electroless plating technology. The morphology and component content of Co-P coating varies with the change of sodium citrate concentration in elctroless plating solution. And as phosphorus content increases in coatings, resulting in smaller grain, coercivity of microspheres decreases. The microwave absorption properties of spheres-wax composite were investigated in the range of 2-18 GHz. Both permittivity and permeability increase with an increase of cobalt content in coatings. For composite layer, a minimal reflection loss (RL, −36.9 dB) of was predicted at 8.1 GHz with a thickness of 3 mm.     

锁相热像方法实验测量Nb2O5薄膜吸收率

利用锁相热像方法定量测量了光学镀膜的吸收率。待测薄膜吸收周期调制的激光能量,在表面形成热波,将红外相机记录的热分布信号进行锁相相关处理,获得信噪比提高的热图像。采用标准吸收样品对系统进行定标,可获得光热信号幅度与样品吸收率之间的定量联系,进而在相同实验条件下测量待测样品,可通过光热信号直接计算获得其绝对吸收率。在1 060 nm波长处开展了实验研究,测量获得了不同厚度Nb₂O₅镀膜的吸收率数值,实测的吸收可达80 ppm。     

多腔耦合微波表面波PECVD法沉积 DLC薄膜研究

报道了利用多腔耦合微波表面波等离子体增强化学气相沉积(PECVD)的方法制备类金刚石(DLC)薄膜。通过发射光谱(OES)测量,对Ar等离子体中的各种放电参数以及全部四个腔室内放电的均匀性作出评估。采用表面轮廓仪测量了薄膜的厚度;薄膜的表面形貌、组成结构通过原子力显微镜(AFM)、激光拉曼光谱和X射线衍射光谱(XPS)进行了表征。在12.5μm厚度的有机薄膜聚酯(PET)表面沉积一定厚度DLC后,通过测量水蒸气透过率(WVTR)对DLC薄膜的阻隔性能进行了研究。结果表明,这种多腔耦合微波表面波等离子体装置,不仅能够实现四个腔室同时相对均匀的放电,也能够实现单个腔室的轴向均匀放电。制备的DLC薄膜结构致密、成分均匀,可以使PET薄膜阻隔性能提高约20倍。     

Process and performance of hot dip zinc coatings containing ZnO and Ni-P under layers as barrier protection

A new coating system of under layer for hot dip zinc coating was explored as an effective coating for steel especially for application in relatively high aggressive environments. The influence of different barrier layers formed prior to hot dip galvanization was investigated to optimize high performance protective galvanic coatings. The deposition of ZnO and Ni-P inner layers and characteristics of hotdip zinc coatings were explored in this study. The coating morphology was characterized by scanning electron microscope (SEM) analysis. The hot dip zinc coatings containing under layer showed substantial improvement in their properties such as good adhesion, and high hardness. In addition, a decrease in the thickness of the coating layer and an enhancement of the corrosion resistance were found. Open circuit potential (OCP) of different galvanized layers in different corrosive media viz. 5% NaCl and 0.5 M H₂SO₄ solutions at 25 ± 1 °C was measured as a function of time. A nobler OCP was exhibited for samples treated with ZnO and Ni than sample of pure Zn; this indicates a dissolution process followed by passivation due to the surface oxide formation. The high negative OCP can be attributed to the better alloying reaction between Zn and Fe and to the sacrificial nature of the top pure zinc layer.     

Enhanced microwave absorption in ZnO/carbonyl iron nano-composites by coating dielectric material

The microwave absorption properties of zinc oxide/carbonyl iron composite nanoparticles fabricated by high energy ball milling were studied at 0-20 GHz. Experiments showed that ZnO as a kind of dielectric material coating carbonyl iron particles made the bandwidth of reflection loss (RL)<−5 dB expanding to the low frequency, and enhanced absorption effect obviously. For a 3 mm thickness absorber of ZnO/carbonyl iron after 30 h milling, the values of RL<−5 dB and RL<−8 dB were obtained in the frequency range from 7.0 GHz to 17.8 GHz and from 9.8 dB to 14.9 dB, respectively, and its strongest RL peak was −29.34 dB at 13.59 GHz. The magnetic loss of carbonyl iron particles and the dielectric loss of ZnO particles were the main mechanisms of microwave absorption for the composites.     

M型钡铁氧体陶瓷微珠核壳腔结构吸波材料

利用自反应淬熄法制备了一种M型钡铁氧体空心陶瓷微珠材料,在此基础上,对其表面进行超声波化学镀Ni-Co复合层,从而形成了具有核/壳/腔结构的材料;通过扫描电子显微镜、能谱仪和X射线衍射仪分析表明,该材料具有中空结构,主要物相BaFe12O19为M型钡铁氧体,经过化学镀后,在其表面形成了一层Ni-Co复合层;经过吸波性能测试,化学镀Ni-Co复合层后,在2~18GHz范围内,当厚度为2.10mm时,最低反射率达到了-28.62dB,反射率小于-10dB的带宽为3.33GHz。