制备方法对CuO/CeO_2-MnO_x催化剂富氢条件下催化氧化CO性能的影响

分别以一次沉淀法、沉积沉淀浸渍法及直接混合焙烧法制备了Cu O/Ce O2-Mn Ox催化剂,并运用XRD(X射线衍射)、N2吸附脱附、XPS(X射线光电子能谱)、H2-TPR(程序升温还原)等手段对催化剂进行了表征,讨论了Cu O/Ce O2-Mn Ox催化剂的制备方法对富氢条件下CO催化氧化性能的影响。分析结果表明:沉积沉淀浸渍法制备的Cu O/Ce O2-Mn Ox催化剂并不具有最大的比表面积及最小的晶粒尺寸,但表现出最优的催化活性;沉积沉淀浸渍法使Cu O/Ce O2-Mn Ox催化剂表面分布较多的活性铜物种及丰富的Mn Ox,使得催化剂表面晶格氧含量增多,同时表面羟基、碳酸盐等易导致催化剂失活的物种减少,这些是其具有高催化活性的关键因素。     

B,N-SnO2/TiO2光催化剂的制备及其光催化性能研究

为了提高TiO₂在可见光下的光催化活性, 采用聚合物前驱体法制备了B,N共掺杂的SnO₂/TiO₂(B,N-SnO₂/TiO₂)粉体型光催化剂. 进一步为了提高光催化剂的实用性, 通过浸渍-裂解法制备了氧化铝纤维毡负载的B,N-SnO₂/TiO₂光催化剂. 利用X射线衍射仪、场发射扫描电子显微镜、场发射透射电子显微镜、X射线光电子能谱、比表面积分析仪、紫外-可见分光光度计等对其进行了表征. 以氧氟沙星水溶液为模拟污染物, 考察了B,N-SnO₂/TiO₂粉体型光催化剂和负载型光催化剂的可见光催化活性及稳定性. 结果表明, 该粉体型光催化剂在可见光下光照15 min, 对氧氟沙星的降解率可达98.3%. 负载型光催化剂也表现出了良好的光催化性能及可重复性和稳定性, 在21次重复使用后光催化性能几乎不发生变化.     

可磁分离的氮掺杂二氧化钛光催化剂的制备及光催化性能

将氮掺杂二氧化钛和通过液相催化相转化制备的磁性载体混合、煅烧制备了一种可磁分离的光催化剂TiO2-xNx/SiO2/NiFe2O4(TSN), 这种光催化剂显示出了典型的铁磁性和可见光活性(λ>400 nm). 对该光催化剂的XRD谱图和透射电镜照片进行分析. 结果表明, SiO2/NiFe2O4(SN)纳米粒子黏附在TiO2-xNx聚集体的表面形成了TSN复合光催化剂. 利用光催化降解甲基橙的效果来评价这种光催化剂的活性. 结果表明, 在NiFe2O4和TiO2-xNx之间包覆一层无定形的SiO2, 可以显著地提高催化剂的脱色效果.     

负载于二氧化硅上的小尺寸氧化亚铜物种促进丙烯选择性氧化生成丙烯醛

氧化物负载的含铜材料是丙烯选择性氧化制备丙烯醛的理想催化剂,一直以来都受到人们的广泛关注.然而,对于该催化体系的结构与性能之间的关系仍不是很清楚.因此,我们以碳酸钠为沉淀剂,通过沉积沉淀法将铜负载于高比表面的二氧化硅载体上,从而得到了均匀分散且小尺寸的Cu/SiO2催化剂.另外,采用浸渍法制得了相同负载量的分散不均匀、大尺寸的Cu/SiO2催化剂.丙烯选择性氧化反应活性测试发现,沉积沉淀法制备的催化剂比浸渍法制备的更有利于丙烯醛的生成,表现出了优异的催化性能:在300℃反应时,丙烯的转化率达到25.5%,丙烯醛的选择性达到66.8%,对应的丙烯醛的生成速率高达10.5 mmol·h^-1·gcat.^-1或111.2 mmol·h^-1·gCu^-1,远远超出了浸渍法制备的催化剂性能(1.7 mmol·h^-1·gcat.^-1或17.2mmol·h^-1·gCu^-1)和文献中报道的结果.结合高角度环形暗场扫描透射电子显微镜(HAADF-STEM)和X射线吸收精细结构(XAFS)技术,对沉积沉淀法制备的催化剂进行表征,发现在反应后铜物种的结构发生了明显的变化,由小尺寸的氧化铜(CuO)团簇转变为氧化亚铜(Cu2O)团簇,并且铜物种的尺寸没有明显的增大.为了进一步探索铜物种在预处理(氢气还原)以及催化反应时(丙烯+氧气)的结构变化,对不同方法合成的两种催化剂进行了原位X射线粉末衍射测试,发现不同尺寸的铜物种在还原和反应时都经历了从氧化铜(CuO)变为金属Cu再到Cu2O的结构变化,并且Cu2O在320 min的反应过程中可以稳定存在,说明它是该催化反应的活性物种.另外,通过原位双光束傅里叶变换红外光谱追踪反应时气体分子在催化剂表面的吸脱附状态,发现丙烯可以有效地吸附在小尺寸Cu/SiO2催化剂表面,随着Cu2O的形成,检测到了烯丙基中间体(CH2=CHCH2*)的产生,该物种可以与邻近Cu2O上的一个氧发生反应,从而生成丙烯醛,因此结合N2O滴定实验,我们可认为,高度分散的小尺寸的Cu2O物种是丙烯进行高效选择性氧化反应生成丙烯醛的活性物种.     

Ag_2O-TiO_2/海泡石复合光催化剂制备及其可见光光催化性能（英文）

传统的Ti O2半导体光催化剂存在光谱响应范围窄、量子效率低及不易回收等不足,使其在实际应用中受到限制.通过离子掺杂、贵金属沉积和半导体复合等方法对Ti O2进行改性可以拓展其光响应范围,其中半导体复合方法最为常用.复合半导体的特殊能带结构能够有效促进光生载流子的界面迁移,实现光生电荷的有效分离,提高光催化性能,且通过固定化或负载可改善Ti O2的可回收利用性能.鉴于此,本文针对半导体Ti O2的复合和负载制备及其光催化降解有机污染物的性能和反应机理进行了研究.采用条件温和、稳定的溶胶-凝胶法于低温制备出Ti O2/海泡石复合物,通过浸渍和焙烧将Ag2O负载于其上,修饰和拓展了Ti O2的可见光响应范围,最终获得了可见光响应、高效、稳定的Ag2O-Ti O2/海泡石复合光催化剂.利用X射线衍射(XRD)、X射线光电子能谱(XPS)、扫描电镜(SEM)、透射电镜(TEM)、N2吸附-脱附和紫外-可见光光谱(UV-vis)等手段对其物理化学特性进行了表征.XRD结果表明,复合样品中Ti O2呈锐钛矿相和金红石相的混合晶相.TEM结果表明,复合样品中存在Ag2O和Ti O2两种组分,晶格条纹相互交叠形成了异质结结构.UV-vis谱表明,与Ti O2/海泡石相比,Ag2O-Ti O2/海泡石复合光催化剂的吸收带边明显红移,展现了较强的可见光吸收能力.N2吸附-脱附结果表明,Ag2O-Ti O2/海泡石复合光催化剂具有较大的比表面积和介孔结构,这有助于增强催化剂对污染物的吸附能力并提供更多的复合位点.以酸性红G为模拟污染废水,研究了焙烧温度和Ag2O负载量等制备条件对所制催化剂可见光催化性能的影响.结果表明,在可见光照射下,焙烧温度为200°C,Ag2O负载量为10%条件下制备的复合光催化剂对酸性红G的降解率为98%,与Ag2O-Ti O2、Ag2O/海泡石和Ti O2/海泡石等复合物相比,Ag2O-Ti O2/海泡石复合光催化剂展现了优异的可见光催化性能.此外,Ag2O-Ti O2/海泡石复合光催化剂同样能够在可见光条件下有效降解常见室内空气污染物甲醛,进一步证实了催化剂优异的光催化性能.化学荧光法和活性物种捕获实验表明,复合光催化剂降解有机污染物的活性基团主要是光生空穴和超氧自由基.催化剂能带结构分析表明,Ag2O和Ti O2具有相匹配的能带结构,两者复合有利于光生载流子分离和迁移,增强催化剂光催化活性.海泡石作为光催化剂载体能够有效固载光催化成分,增加光催化剂有效表面积和活性位,有利于提高复合光催化剂的吸附性能和回收利用率.     

Cu/SiO2催化剂制备方法对其草酸二甲酯催化氢解性能的影响

以化学吸附水解法、蒸氨法和浸渍法制备了Cu/SiO2催化剂, 并用于草酸二甲酯氢解制备乙二醇的反应. 发现用化学吸附水解法制备的催化剂具有最高的催化活性和乙二醇选择性, 乙二醇得率可达92.6%. 对还原前后不同方法制备的催化剂进行表征发现, 浸渍法制备的催化剂中Cu物种不能很好地得到分散, 因此活性较差. 蒸氨法和化学吸附水解法能较好地分散Cu物种. 由于化学吸附水解法制备的催化剂的Cu0表面积较蒸氨法的大, 且Cu＋表面积相当, 故活性高于蒸氨法制备的催化剂.     

高分子模板作用下的正八面体微/纳米Cu2O晶体制备

探讨了羟乙基纤维素、壳聚糖、聚乙烯醇、聚丙烯酰胺、不同分子晕的聚乙二醇等高分子模板,存水合肼还原法制备微/纳米Cu2O晶体中的应用特性.通过X射线衍射、扫描电镜等埘Cu2O晶体进行了表征.本工作制得了粒径在300～500 nm的正八体微/纳米Cu2O晶体.结果显示,化学沉积法制备微/纳米Cu2O时,宜选用易形成单个均一胶团、不易形成空间网络结构、具有良好空间位阻效应且分子量适中的高分子化合物作为模板.本工作获得的水合肼还原法制备Cu2O的最佳条件为:反应温度55℃,nOH-:nCu2+=2∶1.     

CoB/C催化硼氢化钠水解制氢的性能

使用浸渍负载-还原法及化学镀法制备了活性炭负载的CoB催化剂,研究了这些催化剂催化硼氢化钠水解制氢反应的性能。在温度为20℃,反应液为1%NaBH4+5%NaOH的条件下,浸渍负载-还原法制备的CoB/C催化剂的产氢活性为2 022mL.min-1.g-1(Co),而化学镀法制备的CoB/C催化剂的产氢活性可达2 503 mL.min-1.g-1(Co),相同条件下非负载的CoB催化剂的产氢活性仅为1 351 mL.min-1.g-1(Co)。化学镀法制备的CoB/C催化剂重复使用5次后其活性仍能保持初始活性的70%,而浸渍负载的CoB/C催化剂及非负载的CoB催化剂的活性分别降至初始活性的30%和10%,化学镀法制备的CoB/C催化剂显示出更好的催化性能。此外该催化剂在空气中放置30 d后催化活性没有明显下降,这为其存储和使用带来了便利。进一步的物理化学表征表明,非负载的CoB极易团聚,形成的二次粒子粒径在400~800 nm,而活性炭负载的CoB催化剂团聚现象则大大减弱,CoB的分散性明显好于非负载催化剂。载体的存在可进一步阻止CoB活性组分在催化反应过程中发生团聚而避免活性下降。化学镀法制备的催化剂中,载体与CoB之间有更强的相互作用而使得后者结合紧密,分散良好,不易流失,催化剂整体上具有更好的稳定性。     

Cu负载Fe柱撑钠化海泡石: 结构特点及其丙烯选择性催化还原NO性质研究

采用羟基铁离子柱撑钠化海泡石改性后, 以浸渍法制备了铜负载铁柱撑钠化海泡石Cu/Fe-NaPILCS催化剂, 作为比较以浸渍法制备了铁负载钠化海泡石(Fe-NaSep), 铜负载钠化海泡石(Cu-NaSep)和铜铁负载钠化海泡石(Cu/Fe-NaSep)催化剂. 并将它们应用于C₃H₆选择性催化还原NO的反应(C₃H₆-SCR). 通过X射线衍射仪(XRD)、TGA-DTG分析、N₂-等温吸附/脱附、H₂-程序升温还原(TPR)和X射线光电子能谱仪(XPS)等技术对样品进行表征. N₂-等温吸附/脱附和TGA-DTG分析结果表明, Fe-NaPILCS的比表面积和孔体积较海泡石原矿具有较大的增加, 热稳定性也明显提高|XRD和XPS结果表明, 在Cu/Fe-NaPILCS催化剂上同时存在Fe^3＋/Fe^2＋和Cu^2＋/Cu^＋不同氧化态的氧化物种, 在Cu和Fe之间存在电子迁移. H₂-TPR结果表明, Cu/Fe-NaPILCS催化剂上存在大量的孤立铜离子物种(isolated Cu^2＋-ions, (Cu^2＋)_i). Fe柱撑钠化海泡石负载的Cu/Fe-NaPILCS催化剂的催化活性明显优于未柱撑海泡石负载的Cu/Fe-NaSep催化剂, 这可能与Cu/Fe-NaPILCS具有较大的比表面积、孔体积和更优的氧化还原性能, 及其具有更多有利于C₃H₆-SCR反应的(Cu^2＋)_i物种有关.     

Ag@AgBr光催化剂的制备及其可见光催化降解亚甲基蓝反应性能

采用沉积-沉淀及光还原法制备了Ag@AgBr等离子体光催化剂,利用X射线衍射、扫描电镜和紫外-可见漫反射光谱对其进行了表征,并考察了该等离子体光催化剂在可见光(λ420nm)下的催化性能,探讨了催化剂用量、pH值、亚甲基蓝初始浓度、H2O2添加量、循环使用及捕获剂对Ag@AgBr催化性能的影响.结果表明,当亚甲基蓝的初始浓度为10mg/L,催化剂用量为1g/L,pH=9.8时,光照12min后,亚甲基蓝的降解率高达96%,且样品经5次循环使用后活性基本保持不变;而少量H2O2的添加对光催化活性影响不大,过量的H2O2会降低光催化活性;乙二胺四乙酸捕获空穴后比异丙醇捕获·OH后的光催化活性降得更低.同时,对Ag@AgBr等离子体光催化剂可见光降解亚甲基蓝的催化机理进行了分析.     

S掺杂S-TiO_2/SiO_2可见光响应光催化剂的制备及性能

以四氯化钛为钛源,硫脲为硫源,采用液相水解-沉淀法制备了S掺杂的TiO2/SiO2(S-TiO2/SiO2)催化剂,并以苯酚为模型物,考察了催化剂在可见光区、紫外光区和太阳光下的光催化活性,以及催化剂的使用寿命和分离性能.采用X射线光电子能谱、傅里叶变换红外光谱、紫外-可见漫反射光谱、X射线衍射、透射电镜及N2吸附-脱附等技术对催化剂进行了表征.结果表明,S以+6价形式进入TiO2体相并置换晶格中的Ti4+,适量S掺杂的S-TiO2/SiO2在紫外光区、可见光区和太阳光下均表现出较高的光催化活性.SiO2与TiO2界面间有Ti-O-Si键形成,结合牢固.S掺杂在TiO2表面生成Ti-O-S键,形成新的能级结构,使光催化剂在450～550nm产生吸收,诱发TiO2可见光催化活性;同时提高了TiO2表面羟基数量.SiO2的加入可减小TiO2颗粒的平均尺寸,增大催化剂的比表面积,改善催化剂的分离性能,提高催化剂的使用寿命.     

铝板为基础的S掺杂TiO_2催化分解有毒有机气体(英文)

S-doped TiO2(S-TiO2) films were immobilized on flexible low-cost aluminum sheets(S-TiO2-AS) using a sol-gel dipping process and low post-processing temperatures. The photocatalytic degradation of toxic organic vapors using the prepared films was evaluated using a continuous-flow glass tube under visible light exposure. The surface properties of the S-TiO2-AS and TiO2-AS films were examined by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, and ultraviolet-visible spectroscopy. The photolysis of benzene, toluene, ethyl benzene, and xylene(BTEX) did not occur on the bare AS. In contrast, the photocatalytic degradation efficiencies of the target pollutants using S-TiO2-AS were higher than those obtained using reference TiO2-AS photocatalyst. In particular, the average photocatalytic degradation efficiencies of BTEX using S-TiO2-0.8-AS(S/Ti ratio = 0.8) over a 3-h process were 34%, 78%, 91%, and 94%, respectively, whereas those of TiO2-AS were 2%, 11%, 21%, and 36%, respectively. The photocatalytic decompo-sition efficiencies of BTEX under visible irradiation using S-TiO2-AS increased with increasing S/Ti ratios from 0.2 to 0.8, but decreased when the ratio further increased to 1.6. Thus, S-TiO2-AS can be prepared using optimal S/Ti ratios. The degradation of BTEX over S-TiO2-AS depended on the air flow rates and initial concentrations of the target chemical. Overall, under optimal conditions, S-TiO2-AS can be effectively applied for the purification of toxic organic vapors.     

Spectroscopic study for photocatalytic decomposition of organic compounds on titanium dioxide containing sulfur under visible light irradiation

Yellowish S-containing TiO2 (S-TiO2) powders were prepared by calcination of a mixture of titanium(III) chloride and ammonium thiocyanate solutions. Three kinds of S-TiO2 were prepared by varying the concentration of ammonium thiocyanate (0.5, 1 or 13 M). X-ray photoelectron spectroscopy spectra of the S-TiO2 showed that sulfur atoms existed on the surface of TiO2 powders. But the peaks assigned to S disappeared after Ar+ etching, which means that these atoms were not doped in the bulk of the TiO2 powders. While UV-visible absorption spectra of S-TiO2 showed that the absorption edges of these photocatalysts were seen to shift to a longer wavelength (lower band gap energy) than those of undoped rutile TiO2 prepared and commercial anatase type TiO2 (ST-01). The S-TiO2 (1 M) exhibited higher photocatalytic activity than ST-01 for degradation of methylene blue in aqueous solution under visible light irradiation (lambda > 400 nm). It was also confirmed by IR spectroscopy that acetaldehyde in oxygen under visible light irradiation (lambda > 400 nm) was decomposed to acetic acid by the S-TiO2 and ST-01 at the first decomposition step.     

甲醇热还原法制备高分散Cu2O微米立方体及其光催化性能

通过简单的甲醇热还原法制备高分散Cu2O微米立方体,制备过程中无需添加表面活性剂。利用X射线衍射(XRD)、场发射扫描电镜(FESEM)、高分辨透射电镜(HRTEM)、X射线光电子能谱(XPS)等分析测试手段对样品的物相及形貌进行表征;通过紫外可见漫反射(UV-Vis)及光致发光光谱(PL)对样品的光化学性能进行表征;样品的光催化性能通过可见光(λ>400 nm)催化降解罗丹明B染料(RhB)脱色活性进行测试表征。同时,对样品光催化性能与物理化学性能之间的内在联系进行了研究。结果表明:制备温度对样品的形态及光催化性能有着重要影响,当制备温度为140℃时,可制备得到高分散Cu2O微立方体并且其显示出最优的光催化活性;当制备温度进一步提高时,得到的样品为超细铜粉,样品的光催化性能迅速降低。     

Synthesis and characterization of sulfur-titanium dioxide nanocomposites for photocatalytic oxidation of cyanide using visible light irradiation

A sol-gel method was used to prepare TiO2and sulfur-TiO2(S-TiO2)nanocomposites, which were characterized by N2 adsorption-desorption, X-ray diffraction, X-ray photoelectron spectroscopy, photoluminescene, ultraviolet visible and transmission electron microscopy measurements. The photocatalytic performance of TiO2 and S-TiO2nanocomposites, with respect to the photocatalytic oxidation of cyanide under visible light irradiation, was determined. The results reveal that S is well dispersed on the surface of TiO2 nanoparticles. Additionally, the surface area of the S-TiO2nano-composites was observed to be smaller than that of the TiO2nanoparticles because of blocked pores caused by doping with S. The S-TiO2nanocomposite (0.3 wt% S) exhibited the lowest band gap and the highest photocatalytic activity in the oxidation of cyanide. The photocatalytic performance of S-TiO2(0.3 wt% S) nanocomposites was stable, even after the fifth reuse of the nanoparticles for the oxidation of cyanide.     

新型可见光响应的 InVO4-Cu2O-TiO2三元纳米异质结：制备及其光催化性能

由于日益严重的环境和能源危机,可见光催化剂的开发已成为当今最具挑战和紧迫的任务之一.将 TiO2和其它窄禁带半导体复合,已被证明是一种有效的可提高其可见光光催化性能的策略. Cu2O是一种禁带宽度为2.0 eV的 p型窄禁带半导体, InVO4则是一种禁带宽度为2.0 eV的 n型半导体,因它们可用于可见光光解水产氢和有机污染物的可见光降解而在过去的数年中引起了人们广泛的关注.但是纯的 Cu2O和 InVO4由于光生电子空穴对在其内部快速地复合,光催化活性通常都比较低.基于能带工程的策略本文设计了一种新型的可见光响应的 InVO4-Cu2O-TiO2三元纳米异质结,并通过普通的湿化学法进行制备：先通过水热法制备 InVO4,再通过溶胶-凝胶法制备 InVO4-TiO2二元复合物,最后通过沉淀和还原过程制备得到 InVO4-Cu2O-TiO2三元纳米异质结.
　　在10%InVO4-40%Cu2O-50%TiO2三元纳米异质结的 X-射线衍射谱中没有观察到明显的杂质峰;通过透射电子显微技术和高分辨透射电子显微技术观察到了它们之间异质结的形成,纳米颗粒的尺寸范围在5?20 nm;经紫外可见漫反射光谱估算得到10%InVO4-40%Cu2O-50%TiO2的禁带宽度为2.78 eV,在可见光区域具有较强的吸收.以普通的9 W节能灯作为可见光光源光照甲基橙5 h后,纯的 InVO4, TiO2和 Cu2O几乎没有光催化活性;10%InVO4-90%TiO2的光催化活性也很低,甲基橙降解率为8%;70%Cu2O-30%TiO2对甲基橙降解率达84%,但初始活性较低;10%InVO4-40%Cu2O-50%TiO2对甲基橙降解率接近90%,并且循环使用6次后,其光催化活性的保持率还维持在90%以上,而50%Cu2O-50%TiO2光催化活性的保持率只有74%.
　　经对使用过的10%InVO4-40%Cu2O-50%TiO2进行 X射线光电子能谱表征发现,存在一弱小的 Cu(II)震动卫星峰,表明在 InVO4-Cu2O-TiO2的光催化过程中 Cu2O的光蚀并不严重.从能带工程的角度分析, InVO4-Cu2O-TiO2三元纳米异质结具有优异的可见光催化性能的主要原因为： InVO4的导带电极电位约为?0.5 eV(vs. SHE,下同),价带电位约为+1.5 eV, Cu2O的分别约为?1.6和+0.4 eV,与 TiO2(导带和价带电极电位分别约为?0.23和+2.97 eV)相比,它们的导带位置更负,将它们组装成三元复合结构,可见光激发的导带电子就可能从 InVO4和 Cu2O的导带迁移到 TiO2的导带上去.同时, n型的 TiO2和 InVO4都与 p型的 Cu2O形成 p-n异质结, n型的 TiO2和 InVO4之间形成 n-n异质结,由于 p-n异质结中内电场的存在以及不同能级相互耦合,可进一步促进可见光激发的导带电子从 InVO4和 Cu2O的导带迁移到 TiO2的导带上去,以及可见光激发的价带空穴从 InVO4的价带迁移到 Cu2O的价带上去,从而实现光生载流子空间上的有效分离.本文有望为新型可见光响应的半导体复合催化剂的设计和制备提供新的思路.     

Visible-light-responsive photocatalytic reaction on tetrahedrally-coordinated chromium oxide moieties loaded on ZSM-5 zeolites and HMS mesoporous silica: partial oxidation of propane

Chromium oxide (Cr-oxide) moieties loaded on ZSM-5 zeolites and HMS mesoporous silica molecular sieves were prepared by an impregnation method and characterized by various spectroscopic methods (XRD, XAFS, UV-Vis, photoluminescence) and their photocatalytic reactivities for partial oxidation of propane under visible light irradiation were investigated. The local structure of Cr-oxide species depended to a large extent on the zeolite types and Si/A1 ratios of zeolites. Tetrahedrally-coordinated isolated Cr-oxide moieties can be loaded on HMS and ZSM-5 having the higher Si/A1 ratios. On these catalysts, in the presence of propane and O₂, a partial oxidation proceeded under visible light irradiation to produce acetone with high selectivity. The charge-transfer excited state of the tetrahedral Cr-oxide moieties plays a significant role in the selective photocatalytic reactions under visible light irradiation.     

水热法制备铂掺杂二氧化钛及其可见光催化性能

以纳米管钛酸为前驱体,采用水热法制备了Pt掺杂TiO2样品.水热反应过程中,纳米管钛酸表面羟基与氯铂酸发生酸碱中和反应,导致反应后pH值升高;在130°C开始纳米管钛酸晶体结构由正交晶系转变为锐钛矿相TiO2.表面化学组成分析表明,掺杂的Pt主要以+2价形式存在.以丙烯为模型污染物,评价样品的可见光(λ≥420nm)光催化活性.结果表明,Pt-TiO2具有明显的可见光光催化降解丙烯的活性,其中160°C水热处理制得的Pt-TiO2活性最高.最后讨论了低温水热法Pt掺杂的形成机理及Pt-TiO2具有可见光响应的原因.     

花状Cu2O/Cu的水热合成及其光催化性能

以硝酸铜为前驱体, 不采用任何模板, 通过逐步水热法合成了花状Cu2O/Cu复合纳米材料. 用扫描电镜(SEM)、X射线衍射(XRD)和紫外-可见漫反射光谱(DRS)对样品进行表征. 结果表明, 花状纳米Cu2O/Cu材料是由长为300-500 nm, 宽为30-70 nm的带状花瓣构成, 在可见光区域有很强的吸收. 复合材料中Cu的含量可以通过反应时间进行调控. 对染料Procion Red MX-5B(PR)的可见光催化降解, Cu能明显提高Cu2O的光催化性能. 当Cu质量分数为27%-71%时, 复合材料Cu2O/Cu的催化活性明显高于单相Cu2O. 与立方体形貌的Cu2O/Cu复合材料相比, 花状纳米Cu2O/Cu复合材料对染料PR有更高的催化降解性能. 且该复合材料有较高的循环回收利用率.