Mechanosynthesis of nanopowders of the proton-conducting electrolyte material Ba(Zr, Y)O3−δ

The formation of perovskite nanopowders of the common proton-conducting, electrolyte material Ba(Zr_1−xY_x)O_3−δ is demonstrated by room temperature mechanosynthesis for the compositional range x=0, 0.058 and 0.148. This is achieved with a planetary ball mill at 650 rpm in zirconia vials, starting from BaO₂ with ZrO₂, (ZrO₂)_0.97(Y₂O₃)_0.03 or (ZrO₂)_0.92(Y₂O₃)_0.08 precursors, respectively. Powder X-ray diffraction (XRD) reveals the formation of the perovskite phase in the early stages of milling with phase purity being achieved after milling times of 240 min for composition x=0.058 whereas 420 min is necessary for composition x=0.148. In contrast, traces of ZrO₂ are apparent in composition x=0 even after milling times of 420 min. The use of BaCO₃ as precursor does not allow the formation of the perovskite phase for any composition. The perovskite crystallites are spherical in shape with an average size determined from XRD of ca. 30 nm in agreement with transmission electron microscopy observations. FTIR spectra demonstrate that contamination levels of BaCO₃ in the mechanosynthesized powders are very low. The spherical shape and nanoscale of the crystallites allow densification levels that are highly competitive when compared to BaZrO₃-based materials formed by alternative synthesis techniques documented in the literature.     

Cr3+在不同基质Y3Ga5O12或Ga2O3中的荧光特性

以Ga_2O_3、Y_2O_3、Cr(NO_3)_3·9H_2O为原料,柠檬酸为配位剂,通过溶胶-凝胶高温固相合成法制备出Ga_(2-2x)O_3∶2xCr~(3+)(Ga_2O_3∶xCr)与Y_3Ga_(5-5x)O_(12)∶5xCr~(3+)(YGG∶xCr)2种多晶粉体(x=0.01,0.03,0.05,0.07)。并采用X射线衍射(XRD)、红外光谱(IR)、扫描电镜(SEM)、荧光光谱(PL)对样品的结构、组成、形貌和荧光性能进行测试分析。XRD和IR分析结果显示在900℃煅烧后Ga_2O_3∶xCr和YGG∶xCr两种样品均成相。SEM照片显示Ga_2O_3∶xCr样品形貌为柱形多面体,YGG∶xCr为短棒状。PL结果显示Cr~(3+)在Ga_2O_3和YGG两种基质中的最强荧光发射峰分别位于742和740 nm,均属于Cr~(3+)的~2E-~4A_2跃迁,对比发现Cr~(3+)在YGG基质中的荧光发射强度更强,在远红光区的荧光性能更好,能满足温室照明中植物光合作用的需求。     

Y2SiO5:Ce3+荧光体的基质多面体替换及其对发光性能的调控研究

荧光材料基质的结构调制对于调控发光材料的发光性能,探索固体结构-性能关系具有重要的研究意义。本文以Y2SiO5基质为模型,分别利用Si/Al和Si/P取代,以[AlO4]和[PO4]四面体替换[SiO4]四面体,设计合成了一系列组成为Y1.95Si1-xAlxO5-xFx∶0.05Ce3+(x=0.05,x=0.1,x=0.2,x=0.4,x=1)和Y1.95-yCaySi1-yPyO5∶0.05Ce3+(y=0,y=0.02,y=0.04,y=0.06,y=0.08,y=0.2)的荧光材料。结合X射线衍射、荧光光谱、荧光寿命等测试手段对其进行了表征分析。结果表明,在x≤0.2,y≤0.04时得到的产物能够保持Y2SiO5的结构特征,在一定的基质组成替换范围内,设计合成的样品Y1.95Si1-xAlxO5-xFx∶0.05Ce3+、Y1.95-yCaySi1-yPyO5∶0.05Ce3+能提高发光强度,发射光谱呈现蓝移现象。荧光寿命测试表明这两个系列的化合物中Ce3+所处的基质环境变化较小,Ce3+发光也未产生较大的变化。     

The Crystal Structures, Microstructure and Ionic Conductivity of Ba2In2O5 and Ba(InxZr1−x)O3−x/2

This paper describes the results of electron microscopy, high-temperature powder neutron diffraction, and impedance spectroscopy studies of brownmillerite-structured Ba₂In₂O₅ and perovskite structured Ba(In_xZr_1−x)O_3−x/2. The ambient temperature structure of Ba₂In₂O₅ is found to adopt Icmm symmetry, with disorder of the tetrahedrally coordinated (In³⁺) ions of the type observed previously in Sr₂Fe₂O₅. Ba₂In₂O₅ undergoes a ∼6-fold increase in its ionic conductivity over the narrow temperature range from ∼1140 K to ∼1230 K, in broad agreement with previous studies. This transition corresponds to a change from the brownmillerite structure to a cubic perovskite arrangement with disordered anions. Electron microscopy investigations showed the presence of extended defects in all the crystals analyzed. Ba(In_xZr_1−x)O_3−x/2 samples with x=0.1 to 0.9 adopt the cubic perovskite structure, with the lattice parameter increasing with x.     

High performance protonic ceramic membrane fuel cells (PCMFCs) with Ba0.5Sr0.5Zn0.2Fe0.8O3−δ perovskite cathode

Protonic ceramic membrane fuel cells (PCMFCs) based on proton-conducting electrolytes have attracted much attention because of many advantages, such as low activation energy and high energy efficiency. BaZr_0.1Ce_0.7Y_0.2O_3−δ (BZCY7) electrolyte based PCMFCs with stable Ba_0.5Sr_0.5Zn_0.2Fe_0.8O_3−δ (BSZF) perovskite cathode were investigated. Using thin membrane BZCY7 electrolyte (about 15 μm in thickness) synthesized by a modified Pechini method on NiO-BZCY7 anode support, PCMFCs were assembled and tested by selecting stable BSZF perovskite cathode. An open-circuit potential of 1.015 V, a maximum power density of 486 mW cm⁻², and a low polarization resistance of the electrodes of 0.08 Ω cm² was achieved at 700 °C. The results have indicated that BZCY7 proton-conducting electrolyte with BSZF cathode is a promising material system for the next generation solid oxide fuel cells.     

Optical properties of (Y1−xTmx)3GaO6 and subsolidus phase relation of Y2O3-Ga2O3-Tm2O3

A serial of samples in Y₂O₃-Ga₂O₃-Tm₂O₃ pseudo-ternary system are prepared by solid-state chemical reaction method. The range of solid solution in (Y_1−xTm_x)₃GaO₆ is 0<x<0.384. Powder X-ray diffraction shows that the compounds crystallize in Gd₃GaO₆ (Cmc2₁)-type structure. The solid solubilities of Y_3+xGa_5−xO₁₂ (x=0-0.77) and Tm_3+xGa_5−xO₁₂ (x=0-0.62) are 37.5-47.11 at% Y₂O₃, and 37.5-45.26 at% Tm₂O₃, respectively. PL spectra of Tm-doped Y₃GaO₆ show that there is a sharp blue emission at ∼456 nm from the ¹D₂→³F₄ transition at room temperatures with two lifetimes (∼5 and ∼15 μs) and a narrow saturation range of PL intensity for the Tm³⁺ content from x=0.005 to 0.03. The sharp emission and long lifetime of (Y_1−xTm_x)₃GaO₆ indicate that Y₃GaO₆ is a potential phosphor and laser crystal host material.     

Evolution and characterization of fluorite-like nano-SrBi2Nb2O9 phase in the SrO-Bi2O3-Nb2O5-Li2B4O7 glass system

Transparent glasses of various compositions in the system (100−x)Li₂B₄O₇−x(SrO-Bi₂O₃-Nb₂O₅) (where x=10, 20, 30, 40, 50 and 60, in molar ratio) were fabricated via splat quenching technique. The glassy nature of the as-quenched samples was established by differential thermal analyses. X-ray powder diffraction (XRD) and transmission electron microscopic studies confirmed the amorphous nature of the as-quenched and crystallinity in the heat-treated samples. Fluorite phase formation prior to the perovskite SrBi₂Nb₂O₉ phase was analyzed by both the XRD and high-resolution transmission electron microscopy. Dielectric and the optical properties (transmission, optical band gap and Urbach energy) of these samples have been found to be compositional dependent. Refractive index was measured and compared with the values predicted by Wemple-Didomemenico and Gladstone-Dale relations. The glass nanocomposites comprising nanometer-sized crystallites of fluorite phase were found to be nonlinear optic active.     

合成方法对Rh/CeO2-ZrO2-La2O3催化剂的结构、表面性能及DeNOx活性的影响

用沉积沉淀法合成两种不同系列的CeO2-ZrO2-La2O3混合氧化物(ZrO2和La2O3沉积CeO2粒子(标记为A-x)以及CeO2和La2O3沉积ZrO2粒子(标记为B-x)),并用作Rh催化剂的载体。XRD、拉曼、TPR、XPS和O2脉冲等表征结果显示出不同的沉积顺序将导致不同的结构和氧化还原性能,且B-x具有更高的氧迁移性、储氧能力和表面Ce浓度。当其负载Rh后,Rh/B-x催化剂具有更高的NO和CO转化率及N2选择性,且Ce的最佳含量为50at%。这可能归因于Rh负载于富铈表面形成更多有利于NO分解的表面Ce3+活性位。     

Preparation and characterization of lithium ion-conducting glass-ceramics in the Li1 + xCrxGe2 − x(PO4)3 system

Li₂O–Cr₂O₃–GeO₂–P₂O₅ based glasses were synthesized by a conventional melt-quenching method and successfully converted into glass-ceramics through heat treatment. Experimental results of DTA, XRD, ac impedance techniques and FESEM indicated that Li_1.4Cr_0.4Ge_1.6(PO₄)₃ glass-ceramics treated at 900 °C for 12 h in the Li_1 + xCr_xGe_2 − x(PO₄)₃ (x = 0–0.8) system exhibited the best glass stability against crystallization and the highest ambient conductivity value of 6.81 × 10⁻⁴ S/cm with an activation energy as low as 26.9 kJ/mol. In addition, the Li_1.4Cr_0.4Ge_1.6(PO₄)₃ glass-ceramics displayed good chemical stability against lithium metal at room temperature. The good thermal and chemical stability, excellent conducting property, easy preparation and low cost make it promising to be used as solid-state electrolytes for all-solid-state lithium batteries.     

Crystal structure and electrical conductivity of cubic fluorite-based (YO1.5) x (WO3)0.15(BiO1.5)0.85- x (0?≤ ?x ≤?0.4) solid solutions

(WO₃)_0.15(BiO_1.5)_0.85 exhibits a tetragonal structure derived from the fluorite subcell. The electrical conductivity of (WO₃)_0.15(BiO_1.5)_0.85 is lower than that of Y₂O₃-doped Bi₂O₃. The structure and electrical conductivity of samples formulated as (YO_1.5) _x (WO₃)_0.15(BiO_1.5)_{0.85- x} (x = 0.1, 0.2, 0.3, and 0.4) were investigated. The as-sintered (YO_1.5)_0.1(WO₃)_0.15(BiO_1.5)_0.75 exhibited a single cubic structure that is isostructural with δ-Bi₂O₃. For x = 0.2, 0.3, and 0.4, the as-sintered samples consisted of a cubic fluorite structure and rhombohedral Y₆WO₁₂. After heat treatment at 600 °C for 200 h, the cubic structures are stable for x = 0.1, 0.3, and 0.4. A transformation from cubic to rhombohedral phase after heat treatment at 600 °C for 200 h was observed in the sample originally formulated as (YO_1.5)_0.2(WO₃)_0.15(BiO_1.5)_0.65.     

Properties of the perovskites, SrMn1−xFexO3−δ (x=1/3, 1/2, 2/3)

The SrMn_1−xFe_xO_3−δ (x=1/3, 1/2, 2/3) phases have been prepared and are shown by powder X-ray and neutron (for x=1/2) diffraction to adopt an ideal cubic perovskite structure with a disordered distribution of transition-metal cations over the six-coordinate B-site. Due to synthesis in air, the phases are oxygen deficient and formally contain both Fe³⁺ and Fe⁴⁺. Magnetic susceptibility data show an antiferromagnetic transition at 180 and 140 K for x=1/3 and 1/2, respectively and a spin-glass transition at 5, 25, 45 K for x=1/3, 1/2 and 2/3, respectively. The magnetic properties are explained in terms of super-exchange interactions between Mn⁴⁺, Fe^(4+δ)+ and Fe⁽³⁺⁾⁺. The XAS results for the Mn-sites in these compounds indicate small Mn-valence changes, however, the Mn-pre-edge spectra indicate increased localization of the Mn-e_g orbitals with Fe substitution. The Mössbauer results show the distinct two-site Fe⁽³⁺⁾+/Fe^(4+δ)+ disproportionation in the Mn- substituted materials with strong covalency effects at both sites. This disproportionation is a very concrete reflection of a localization of the Fe-d states due to the Mn-substitution.     

Synthesis of nano-sized crystalline oxide ion conducting fluorite-type Y2O3-doped CeO2 using perovskite-like BaCe0.9Y0.1O2.95 (BCY) and study of CO2 capture properties of BCY

Formation of nano-sized Y₂O₃-doped CeO₂ (YCO) was observed in the chemical reaction between proton conducting Y₂O₃-doped BaCeO₃ (BCY) and CO₂ in the temperature range 700-1000 °C, which is generally prepared by wet-chemical methods that include sol-gel, hydrothermal, polymerization, combustion, and precipitation reactions. BCY can capture CO₂ of 0.13 g per ceramic gram at 700 °C, which is comparable to that of the well-known Li₂ZrO₃ (0.15 g per ceramic gram at 600 °C). Powder X-ray diffraction (PXRD), energy dispersive X-ray analysis (EDX), laser particle size analysis (LPSA), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and ac impedance spectroscopy were employed to characterize the reaction product obtained from reaction between BCY and CO₂ and subsequent acid washing. PXRD study reveals presence of fluorite-like CeO₂ (a=5.410 (1) Å) structure and BaCO₃ in reaction products. TEM investigation of the acid washed product showed the formation of nano-sized material with particle sizes of about 50 nm. The electrical conductivity of acid washed product (YCO) in air was found to be about an order higher than the undoped CeO₂ reported in the literature.     

The Phase Relations in the System In2O3–TiO2–MgO at 1100 and 1350°C

The phase relations in the system In₂O₃–TiO₂–MgO at 1100 and 1350°C are determined by a classical quenching method. In this system, there are four pseudobinary compounds, In₂TiO₅, MgTi₂O₅ (pseudobrookite type), MgTiO₃ (ilmenite type), and Mg₂TiO₄ (spinel type) at 1100°C. At 1350°C, in addition to these compounds there exist a spinel-type solid solution Mg_2−xIn_2xTi_1−xO₄ (0≤x≤1) and a compound In₆Ti₆MgO₂₂ with lattice constants a=5.9236(7) Å, b=3.3862(4) Å, c=6.3609(7) Å, β=108.15(1)°, and q=0.369, which is isostructural with the monoclinic In₃Ti₂FeO₁₀ in the system In₂O₃–TiO₂–MgO. The relation between the lattice constants of the spinel phase and the composition nearly satisfies Vegard's law. In₆Ti₆MgO₂₂ extends a solid solution range to In₂₀Ti₁₇Mg₃O₆₇ with lattice constants of a=5.9230(5) Å, b=3.3823(3) Å, c=6.3698(6) Å, β=108.10(5)°, and q=0.360. The distributions of constituent cations in the solid solutions are discussed in terms of their ionic radius and site preference effect.     

Conductivity studies of dense yttrium-doped BaZrO3 sintered at 1325 °C

High-temperature proton conductors have wide applications in the areas of fuel cells, electrolysis and hydrogen separation. Barium zirconate-based materials are of interest due to their good stability and high protonic conductivity. The reported conductivity of these ceramic materials is generally less than 10⁻² S/cm, even at high temperatures. This is not high enough for an electrolyte-supported device to achieve an ASR of less than 0.2 Ω cm² therefore thin film electrolytes are required for successful application. As BaZrO₃-based materials have to be sintered at temperatures as high as 1700 °C, this makes it difficult to find a suitable supporting electrode which will not undergo significant chemical reaction with the BaZrO₃-based electrolyte during fabrication of the required electrode supported electrolyte. In this paper, proton-conducting BaZr_0.8Y_0.2O_2.9 was successfully sintered at 1325 °C with a relative density of 96% via addition of 1 wt% ZnO. Fabrication of electrochemical cells using proton-conducting BaZr_0.8Y_0.2O_2.9 as the electrolyte thus becomes possible. The formula of the 1 wt% ZnO added sample is Ba_0.97Zr_0.77Y_0.19Zn_0.04O_3−δ which exhibits a tetragonal structure with space group P4/mbm (127); a=5.9787(1) Å, c=4.2345(1) Å, V=151.36(1) Å³. It was found that a solid solution was formed for a limited range of Zn doping. Conductivity has been studied as a function of atmosphere (air, dry and wet 5% H₂/Ar) with the changes in bulk and grain boundary on changing atmosphere being monitored as a function of time. The total conductivity of Ba_0.97Zr_0.77Y_0.19Zn_0.04O_3–δ is 1.0×10⁻³ S/cm above 600 °C therefore it may be used as a proton-conducting thin film electrolyte for efficient electrochemical devices at such temperatures. The grain boundary resistance is insignificant at high temperature for the well-sintered sample.     

g-C3N4/双钙钛矿复合材料的制备及氧催化性能

通过溶胶-凝胶法制备出不同Ni掺杂比例的双钙钛矿Sr_2Ni_xCo_(2-x)O_6(x=0.2,0.4,0.6,0.8),通过热分解法制备出具有层状结构的纳米颗粒g-C_3N_4,并制备其复合物催化剂。将双钙钛矿和g-C_3N_4分别制备成双功能电极片,用于测试其对氧还原(ORR)和氧析出(OER)的催化活性,然后选取具有最佳氧催化活性的Ni掺杂比例x=0.4的双钙钛矿与一定重量比例的g-C_3N_4进行复合,测试复合催化剂的氧催化活性。结果表明,复合后的催化剂催化效果明显优于单一催化剂,当g-C_3N_4添加量占双钙钛矿的30%(w/w)时复合催化剂催化氧还原反应的最大电流密度为395.7 mA·cm~(-2)(-0.6 V vs Hg/HgO),氧析出反应的最大电流密度为372.0mA·cm~(-2)(1 V vs Hg/HgO),这表明g-C_3N_4与Sr_2Ni_(0.4)Co_(1.6)O_6复合后协同催化能够提高双钙钛矿的氧催化活性。     

Investigation of the quasi-ternary system LaMnO3-LaCoO3-“LaCuO3”—I: the series La(Mn0.5Co0.5)1−xCuxO3−δ

The La(Mn_0.5Co_0.5)_1−xCu_xO_3−δ series with x=0, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8 and 1 was synthesized by the Pechini method to obtain insight into the phase formation in the quasi-ternary LaMnO₃-LaCoO₃-“LaCuO₃” system caused by the instability of LaCuO₃ under ambient conditions. After sintering at 1100°C some remarkable results were obtained: LaMn_0.3Co_0.3Cu_0.4O_3−δ crystallized as a single phase in the orthorhombic perovskite structure typical of LaCuO₃. Among the synthesized compositions this compound showed the highest electrical conductivity in air at 800°C (155 S cm⁻¹) and also the highest thermal expansion coefficient (α_30−800°C=15.4×10⁻⁶ K⁻¹). The LaCuO_3−δ composition also crystallized as a single phase but in a monoclinic structure although previous investigations have shown that other phases are preferably formed after sintering at 1100°C. The electrical conductivity and thermal expansion coefficient were the lowest within the series of compositions, i.e. 9.4 S cm⁻¹ and 11.9×10⁻⁶ K⁻¹, respectively.     

Synthesis and characterization of Fe2O3/SiO2 nanocomposites

Fe₂O₃/SiO₂ nanocomposites based on fumed silica A-300 (S_BET = 337 m²/g) with iron oxide deposits at different content were synthesized using Fe(III) acetylacetonate (Fe(acac)₃) dissolved in isopropyl alcohol or carbon tetrachloride for impregnation of the nanosilica powder at different amounts of Fe(acac)₃ then oxidized in air at 400–900 °C. Samples with Fe(acac)₃ adsorbed onto nanosilica and samples with Fe₂O₃/SiO₂ including 6–17 wt% of Fe₂O₃ were investigated using XRD, XPS, TG/DTA, TPD MS, FTIR, AFM, nitrogen adsorption, Mössbauer spectroscopy, and quantum chemistry methods. The structural characteristics and phase composition of Fe₂O₃ deposits depend on reaction conditions, solvent type, content of grafted iron oxide, and post-reaction treatments. The iron oxide deposits on A-300 (impregnated by the Fe(acac)₃ solution in isopropanol) treated at 500–600 °C include several phases characterized by different nanoparticle size distributions; however, in the case of impregnation of A-300 by the Fe(acac)₃ solution in carbon tetrachloride only α-Fe₂O₃ phase is formed in addition to amorphous Fe₂O₃. The Fe₂O₃/SiO₂ materials remain loose (similar to the A-300 matrix) at the bulk density of 0.12–0.15 g/cm³ and S_BET = 265–310 m²/g.     

Matrix-Inducing Synthesis of SrxY10?x(SiO4)y(PO4)6?yO2: Eu3+ Micron Crystalline Coral Like Phosphors by Sol-Gel Composition of Hybrid Precursors

In the context, Sr_xY_10−x(SiO₄)_y(PO₄)_6−yO₂ doped with 1 mol%Eu³⁺ (x = 2, y = 6; x = 4, y = 4; x = 5, y = 3; x = 8, y = 0) were synthesized by using 3-aminopropyl-triethoxysilane (APES) as the sources of the silicate network. X-ray diagrams confirm that Sr_xY_10−x(SiO₄) _y(PO₄)_6−yO₂: Eu³⁺ solid solutions are formed as a pure apatitic phase. The SEM picture shows that there exist some novel unexpected coral like morphological structures. The luminescent intensity is the strongest for the host composition of Sr₄Y₆(SiO₄)₄(PO₄)₂O₂ although the effect of the composition on the luminescent intensity is little.     

Thermoelectric properties of Cu-doped n-type (Bi2Te3)0.9–(Bi2−xCuxSe3)0.1(x=0–0.2) alloys

n-Type (Bi₂Te₃)_0.9–(Bi_2−xCu_xSe₃)_0.1 (x=0–0.2) alloys with Cu substitution for Bi were prepared by spark plasma-sintering technique and their structural and thermoelectric properties were evaluated. Rietveld analysis reveals that approximate 9.0% of Bi atomic sites are occupied by Cu atoms and less than 4.0 wt% second phase Cu_2.86Te₂ precipitated in the Cu-doped parent alloys. Measurements show that an introduction of a small amount of Cu (x0.1) can reduce the lattice thermal conductivity (κ_L), and improve the electrical conductivity and Seebeck coefficient. An optimal dimensionless figure of merit (ZT) value of 0.98 is obtained for x=0.1 at 417 K, which is obviously higher than those of Cu-free Bi₂Se_0.3Te_2.7 (ZT=0.66) and Ag-doped alloys (ZT=0.86) prepared by the same technologies.     

Synthesis and CO2 capture evaluation of Li2−xKxZrO3 solid solutions and crystal structure of a new lithium-potassium zirconate phase

Solid solutions of lithium and potassium metazirconates Li_2−xK_xZrO₃ (where, 0?x?2) were prepared by coprecipitation. Samples were characterized by powder X-ray diffraction, scanning electron microscopy, and thermogravimetric analyses. Results showed that the solubility limits of potassium into Li₂ZrO₃ is x=0.2. Furthermore, at higher potassium concentrations, a new phase was synthesized, Li_2.27K_1.19Zr_2.16O_6.05. For structural studies of this new phase, XRD data were analyzed by Rietveld refinements. Additionally, at high potassium concentrations different phases of ZrO₂ were found, as potassium tends to sublimate. On the other hand, lithium-potassium metazirconate solid solutions, Li_2−xK_xZrO₃, were tested as CO₂ captors. Thermal analyses into a CO₂ flux showed that Li_2−xK_xZr₂O₃ solid solutions present a better CO₂ absorption than Li₂ZrO₃ pure. The differences observed in the CO₂ sorption processes were explained with thermodynamic data.