Microstructure and properties of sol-gel derived Pb(Zr<Subscript>0.3</Subscript>Ti<Subscript>0.7</Subscript>)O<Subscript>3</Subscript> thin films on GaN/sapphire for nanoelectromechanical systems

Highly (111) oriented, phase-pure perovskite Pb(Zr_0.3Ti_0.7)O₃ (or PZT 30/70) thin films were deposited on single-crystal, (0001) wurtzite GaN/sapphire substrates using the sol-gel process and rapid thermal annealing. The phase, crystallinity, and stoichiometry of annealed PZT films were evaluated by X-ray diffraction and Rutherford backscattering spectroscopy. The atomic force microscopy revealed a smooth PZT surface (rms roughness ∼1.5 nm) with striations and undulations possibly influenced by the nature of the underlying GaN surface. The cross-sectional field-emission scanning electron microscopic images indicated a sharper PZT/GaN interface compared to that of sol-gel derived PZT on (111) Pt/TiO₂/SiO₂/(100) Si substrates. The capacitance-voltage (C-V) characteristics for PZT in the Pt/PZT/GaN (metal-ferroelectric-semiconductor or MFS) configuration were evaluated as a function of annealing temperature and applied voltage. The observed C-V hysteresis stemmed from trapped charge at defect sites within PZT. Also, the lower capacitance density (C/A = 0.35 μF/cm², where A is the area of an electrode) and remnant polarization (P _r ∼ 4 μC/cm²) for PZT in the MFS configuration, compared to the values for PZT in the MFM configuration (Pt/PZT/Pt), were attributed to the high depolarization field within PZT.     

Low-temperature processing of sol-gel derived Pb(Zr,Ti)O<Subscript>3</Subscript> thick films using CO<Subscript>2</Subscript> laser annealing

Fabrication of ferroelectric Pb(Zr_0.52Ti_0.48)O₃ (PZT) thick films on a Pt/Ti/SiO₂/Si substrate using powder-mixing sol-gel spin coating and continuous wave CO₂ laser annealing technique to treat the specimens with at a relatively low temperature was investigated in the present work. PZT fine powders were prepared by drying and pyrolysis of sol-gel solutions and calcined at temperatures from 400 to 750°C. After fine powder-containing sol-gel solutions were spin-coated on a substrate and pyrolyzed, CO₂ laser annealing was carried out to heat treat the specimens. The results show that laser annealing provides an extremely efficient way to crystallize the materials, but an amorphous phase may also form in the case of overheating. Thicker films absorb laser energy more effectively and therefore melt at shorter periods, implying a significant volume effect. A film with thickness of 1 μm shows cracks and rough surface morphology and it was difficult to obtain acceptable electrical properties, indicating importance of controlling interfacial stress and choosing appropriate size of the mixing powders. On the other hand, a thick film of 5 μm annealed at 100 W/cm² for 15 s exhibits excellent properties (P _r = 36.1 μC/cm², E _c = 19.66 kV/cm). Films of 10 μm form a melting zone at the surface and a non-crystallized bottom layer easily at an energy density of 100 W/cm², showing poor electrical properties. Besides, porosity and electrical properties of thick films can be controlled using appropriate processing parameters, suggesting that CO₂ laser annealing of modified sol-gel films is suitable for fabricating films of low dielectric constants and high crystallinity.     

Preparation of nanocrystalline TiO<Subscript>2</Subscript> powders for photocatalytic oxidation of phenol

Nanocrystalline TiO₂ powders in the anatase, rutile, and mixed phases prepared by hydrolysis of TiCl₄ solution were of ultrafine size (<7.2 nm) with high specific surface areas in the range 167 to 388 m²/g. In the photocatalytic degradation of phenol as model reaction, the photocatalytic properties of TiO₂ nanoparticles were evaluated by use of UV–vis absorption spectroscopy and total organic carbon (TOC) content. The synthetic mixed-phase TiO₂ powder calcined at 400 °C had higher activity than pure anatase or rutile; it degraded more than 90% phenol to CO₂ (evaluated by TOC) after irradiation with near UV light for 90 min at a catalyst loading of 0.4 g/L. The TOC results indicated that rutile TiO₂ crystallites of particle size 7.2 nm resulted in much better photocatalytic performance than particles of larger size. This result suggested that some intermediates, not determined by UV–vis absorption spectroscopy, existed in the solution after the photocatalytic process over the rutile TiO₂ photocatalysts of larger crystallite size.     

Effect of nanoscale CeO<Subscript>2</Subscript> on PVDF-HFP-based nanocomposite porous polymer electrolytes for Li-ion batteries

New poly (vinylidenefluoride-co-hexafluoro propylene) (PVDF-HFP)/CeO₂-based microcomposite porous polymer membranes (MCPPM) and nanocomposite porous polymer membranes (NCPPM) were prepared by phase inversion technique using N-methyl 2-pyrrolidone (NMP) as a solvent and deionized water as a nonsolvent. Phase inversion occurred on the MCPPM/NCPPM when it is treated by deionized water (nonsolvent). Microcomposite porous polymer electrolytes (MCPPE) and nanocomposite porous polymer electrolytes (NCPPE) were obtained from their composite porous polymer membranes when immersed in 1.0 M LiClO₄ in a mixture of ethylene carbonate/dimethyl carbonate (EC/DMC) (v/v = 1:1) electrolyte solution. The structure and porous morphology of both composite porous polymer membranes was examined by scanning electron microscope (SEM) analysis. Thermal behavior of both MCPPM/NCPPM was investigated from DSC analysis. Optimized filler (8 wt% CeO₂) added to the NCPPM increases the porosity (72%) than MCPPM (59%). The results showed that the NCPPE has high electrolyte solution uptake (150%) and maximum ionic conductivity value of 2.47 × 10⁻³ S cm⁻¹ at room temperature. The NCPPE (8 wt% CeO₂) between the lithium metal electrodes were found to have low interfacial resistance (760 Ω cm²) and wide electrochemical stability up to 4.7 V (vs Li/Li⁺) investigated by impedance spectra and linear sweep voltammetry (LSV), respectively. A prototype battery, which consists of NCPPE between the graphite anode and LiCoO₂ cathode, proves good cycling performance at a discharge rate of C/2 for Li-ion polymer batteries.     

Mid-temperature solid oxide fuel cells with thin film ZrO<Subscript>2</Subscript>: Y<Subscript>2</Subscript>O<Subscript>3</Subscript> electrolyte

Data on the mid-temperature solid-oxide fuel cells (SOFC) with thin-film ZrO₂-Y₂O₃ (YSZ) electrolyte are shown. Such a fuel cell comprises a carrying Ni-YSZ anode, a YSZ electrolyte 3–5 μm thick formed by vacuum ion-plasma methods, and a LaSrMnO₃ cathode. It is shown that the use of a combined method of YSZ electrolyte deposition, which involves the magnetron deposition of a 0.5–1.5-μm thick sublayer and its pulse electron-beam processing allows a dense nanostructured electrolyte film to be formed and the SOFC working temperature to be lowered down as the result of a decrease in both the solid electrolyte Ohmic resistance and the Faradaic resistance to charge transfer. SOFC are studied by the methods of voltammentry and impedance spectroscopy. The maximum power density of the SOFC under study is 250 and 600 mW/cm⁻² at temperatures of 650 and 800°C, respectively.     

Effect of annealing temperatures and of high content of the iron ion (Fe<Superscript>3+</Superscript>)-doping on transition anatase–rutile phase of nanocrystalline TiO<Subscript>2</Subscript> thin films prepared by sol–gel spin coating

Titanium dioxide doped with iron (III) was prepared by sol–gel Spin Coating method. The phase structures, morphologies, particle size of the doped TiO₂ have been characterized by X-ray diffraction (XRD), Raman spectroscopy, atomic force microscopy (AFM) and ultraviolet–visible (UV–Vis) spectrophotometer. The XRD and Raman results show that the 10% Fe³⁺-doped TiO₂ thin films crystallize in anatase phase between 600 and 800 °C, and into the anatase–rutile phase at 1,000 °C, and further into the rutile phase when the content of Fe³⁺ increases (20%). The grain size calculated from XRD patterns shows that the crystallinity of the obtained anatase particles increased from 39.4 to 43.4 nm as the temperature of annealing increase, whereas the size of rutile crystallites increases, with increasing Fe³⁺ concentrations from 36.9 to 38.1 nm. The AFM surface morphology results confirmed that the particle size increases by increasing the annealing temperature and also with an increasing of Fe³⁺ content. The optical band gap (E _g) of the films was determined by the UV–Vis spectrophotometer. We have found that the optical band gap decreased with an increasing of annealing temperatures and also with an increasing of Fe³⁺ content.     

DSC investigation of nanocrystalline TiO<Subscript>2</Subscript> powder

The aim of the article is to investigate the influence of particle size on titanium dioxide phase transformations. Nanocrystalline titanium dioxide powder was obtained through a hydrothermal procedure in an aqueous media at high pressure (in the range 25–100 atm) and low temperature (≤200 °C). The as-prepared samples were characterized with respect to their composition by ICP (inductive coupled plasma), structure and morphology by XRD (X-ray diffraction), and TEM (transmission electron microscopy), thermal behavior by TG (thermogravimetry) coupled with DSC (differential scanning calorimetry). Thermal behavior of nanostructured TiO₂ was compared with three commercial TiO₂ samples. The sequence of brookite–anatase–rutile phase transformation in TiO₂ samples was investigated. The heat capacity of anatase and rutile in a large temperature range are reported.     

Effect of heat treatment on electrochromic properties of TiO<Subscript>2</Subscript> thin films

Electrochromic titanium oxide (TiO₂) films were deposited on ITO/glass substrates by chemical solution deposition (CSD). The stock solutions were spin-coated onto substrates and then heated at various temperatures (200–500 °C) in various oxygen concentrations (0–80%) for 10 min. The effects of the processing parameters on the electrochromic properties of TiO₂ films were investigated. X-ray diffraction measurements demonstrated that the amorphous TiO₂ films were crystallized to form anatase films above 400 °C. The electrochromic properties and transmittance of TiO₂ films were measured in 1 M LiClO₄–propylene carbonate (PC) non-aqueous electrolyte. An amorphous 350 nm-thick TiO₂ film that was heated at 300°C in 60% ambient oxygen exhibited the maximum transmittance variation (ΔT%), 14.2%, between the bleached state and the colored state, with a ΔOD of 0.087, Q of 10.9 mC/cm², η of 7.98 cm²/C and x in Li _x ClO₄ of 0.076 at a wavelength (λ) of 550 nm.     

Preparation of nanocrystalline Fe-doped TiO<Subscript>2</Subscript> powders as a visible-light-responsive photocatalyst

Nanocrystalline Fe-doped TiO₂ powders were prepared using TiOSO₄, urea, and Fe(NO₃)₃ · 9H₂O as precursors through a hydrothermal method. The as-synthesized yellowish-colored powders are composed of anatase TiO₂, identified by X-ray diffraction (XRD). The grain size ranged from 9.7 to 12.1 nm, calculated by Scherrer’s method. The specific surface area ranged from 141 to 170 m²/g, obtained by the Brunauer–Emmett–Teller (BET) method. The transmission electron microscopy (TEM) micrograph of the sample shows that the diameter of the grains is uniformly distributed at about 10 nm, which is consistent with that calculated by Scherrer’s method. Fe³⁺ and Fe²⁺ have been detected on the surface of TiO₂ powders by X-ray photoelectron spectroscopy (XPS). The UV–Vis diffuse reflection spectra indicate that the light absorption thresholds of the Fe-doped TiO₂ powders have been red-shifted into the visible light region. The photocatalytic activity of the Fe-doped TiO₂ was evaluated through the degradation of methylene blue (MB) under visible light irradiation. The Fe-doped TiO₂ powders have shown good visible-light photocatalytic activities and the maximum degradation ratio is achieved within 4.5 h.     

Multifunctional performances of nanocomposite SiO<Subscript>2</Subscript>/TiO<Subscript>2</Subscript> doped cationic EBODAC film coated on natural cellulose matrix

Reverse micellar microemulsions were utilised to synthesise stable lead titanate colloids from typical sol–gel type molecular precursors. The particles of a few nanometres in diameter that formed by hydrolysis in the micelle cores demonstrated a nanocrystalline texture without the need for thermal treatment. In a chemical solution deposition routine based on the nanoparticle dispersions, ferroelectric PbTiO₃ thin films showing excellent remanent polarisation of more than 50 μC cm⁻² were derived. The electrical characteristics of the layers were correlated to their microstructure which was controlled by the precursor composition and the annealing conditions. A columnar morphology that was realised by spinning on coatings of up to 100 nm in individual thickness proved most favourable with respect to the ferroelectric performance of the films.     

Influence of NH<Subscript>3</Subscript>-treating temperature on visible light photocatalytic activity of N-doped P<Subscript>25</Subscript>-TiO<Subscript>2</Subscript>

The influence of NH₃-treating temperature on the visible light photocatalytic activity of N-doped P₂₅-TiO₂ as well as the relationship between the surface composition structure of TiO₂ and its visible light photocatalytic activity were investigated. The results showed that N-doped P₂₅-TiO₂ treated at 600°C had the highest activity. The structure of P₂₅-TiO₂ was converted from anatase to rutile at 700°C. Moreover, no N-doping was detected at the surface of P₂₅-TiO₂. There was no simply linear relationship between the visible light photocatalytic activity and the concentration of doped nitrogen, and visible light absorption. The visible light photocatalytic activity of N-doped P₂₅-TiO₂ was mainly influenced by the synergistic action of the following factors: (i) the formation of the single-electron-trapped oxygen vacancies (denoted as V_o^·); (ii) the doped nitrogen on the surface of TiO₂; (iii) the anatase TiO₂ structure.     

Synthesis of ammonia from natural gas at atmospheric pressure with doped ceria–Ca<Subscript>3</Subscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript>–K<Subscript>3</Subscript>PO<Subscript>4</Subscript> composite electrolyte and its proton conductivity at intermediate temperature

A new type of oxide–salt composite electrolyte, yttrium doped ceria YDC–Ca₃(PO₄)₂–K₃PO₄, was developed and demonstrated for its promising use for ammonia synthesis. Using this composite electrolyte, ammonia was synthesized from nitrogen and natural gas at atmospheric pressure in the solid-state proton conducting cell reactor, and the optimal condition for ammonia production was determined . The evolved rate of ammonia is up to 6.95×10⁻⁹ mol s⁻¹ cm⁻².     

Temperatures and kinetics of anatase to rutile transformation in doped TiO<Subscript>2</Subscript> heated in microwave field

The influence of aliovalent ions such as Mn, Cr, Fe, Mo, and V on the temperature and kinetics of anatase to rutile phase transformation in TiO₂ heated in microwave field was studied in this work. The results indicated that heat treatment method and dopants considerably affected the anatase-to-rutile phase transition temperature and kinetics of transformation. The activation energy for anatase to rutile transformation of TiO₂ derived from the isothermal data was found to be 328.4 kJ mol^–1, which was considerably reduced by the addition of dopants in TiO₂ matrix. The activation energy for Mo, Mn and V doped samples was 252.0, 101.3 and 96.4 kJ mol^–1, respectively.     

Investigation on LiCoPO<Subscript>4</Subscript> powders as cathode materials annealed under different atmospheres

An uncomplicated Pechini-assisted sol–gel process in aqueous solutions is used for the synthesis of Li–Co phosphate powders as cathode materials. The powders are annealed under different conditions in flowing nitrogen and in flowing air. The structural, morphological, and electrochemical properties are strongly dependent upon the annealing conditions. After the treatment in air, the X-ray diffraction (XRD) patterns reveal the presence of LiCoPO₄ as a single phase. The morphology of the powders consists of a homogeneous and good interconnected blend of grains with different sizes; the cyclic voltammetry (CV) curves show a very good reversibility with very close values of the mean peak maxima in the cathodic region. The electrochemical measurements deliver a discharge specific capacity of 37 mAhg⁻¹ at a discharge rate of C/25 at room temperature. After annealing in nitrogen, the XRD analysis detects the formation of Li₄P₂O₇ and to Co₂P as secondary phases; the morphological investigation indicated that the LiCoPO₄ particles took shape of prisms with an average size of 2 μm. The CV curves are associated with a large polarization and poor irreversibility. The electrochemical measurements deliver a discharge specific capacity of 42 mAh g⁻¹ at a discharge rate of C/25 at room temperature and lower capacity fade (approx. 35%).     

Thermal and hydrothermal stability of flame hydrolytically synthesized SiO2/TiO2 mixed oxides

The phase stability of the two TiO₂ modifications (anatase and rutile) in fumed SiO₂/TiO₂ nano-composites (0–24.8 wt-% silica) under thermal and hydrothermal conditions was investigated by X-ray powder diffraction, transmission electron microscopy (TEM) and gas adsorption methods (BET). The results show that the phase transformation from anatase to rutile type of structure and the growth of anatase crystallites are significantly retarded by mixing small amounts of SiO₂ into TiO₂, while the specific surface area is maintained. The SiO₂/TiO₂-composites reveal a remarkable shift in the anatase to rutile transformation temperature from approx. 500 °C (pure TiO₂) to approx. 1000 °C (samples with SiO₂ contents of more than 10%). The rate of phase transformation from anatase to rutile is enhanced under hydrothermal conditions compared to conventional thermal treatment, e.g. pure titania (AEROXIDE^® TiO₂ P25) annealed under hydrothermal conditions (100 g/m³ absolute humidity, 4 h at 600 °C) had a rutile content of 85%, while the same specimens annealed in absence of humidity contained only 46% rutile. However, the difference in rate of phase transformation became less pronounced when the silica content in SiO₂/TiO₂-composites was further increased.TEM results showed that the surface of the anatase crystallites was covered with silica. This averts coalescence of anatase crystallites and keeps them under a critical size during the annealing process. When the crystal domains grew larger, a rapid conversion to rutile took place. The critical size of anatase crystallites for the phase transformation was estimated to be 15–20 nm.     

Electrochemical properties of perovskite and A<Subscript>2</Subscript>MO<Subscript>4</Subscript>-type oxides used as cathodes in protonic ceramic half cells

Three selected materials have been prepared and shaped as cathode of half cells using the proton-conducting electrolyte BaCe_0.9Y_0.1O_3 − δ (BCY10): two perovskite compounds, Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 − δ (BSCF) and La_0.6Sr_0.4Fe_0.8Co_0.2O_3 − δ (LSFC), and the praseodymium nickelate Pr₂NiO_4 + δ (PRN) having the K₂NiF₄-type structure. The electrochemical properties of these compounds have been studied under zero current conditions (two-electrode cell) and under polarization (three-electrode cell). Their measured area-specific resistances were about 1–2 Ω cm² at 600 °C. Under direct current polarization, it appears that the three compounds show almost similar values of current densities at 625 °C; however, at lower temperatures, BSCF appears to be the most efficient cathode material.     

TiO2 nanotube array film prepared by anodization as anode material for lithium ion batteries

TiO₂ array film fabricated by potentiostatic anodization of titanium is characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and charge–discharge measurements. The XRD results indicated that the TiO₂ array is amorphous, and after calcination at 500 °C, it has the anatase form. The pore size and wall thickness of TiO₂ nanotube arrays synthesized at different anodization voltages are highly dependent on the applied voltage. The electrochemical performance of the prepared TiO₂ nanotube array as an electrode material for lithium batteries was evaluated by galvanostatic charge–discharge measurement. The sample prepared at 20 V shows good cyclability but low discharge capacity of 180 mA h cm⁻³, while the sample prepared at 80 V has the highest discharge capacity of 340 mA h cm⁻³.     

Effect of calcination temperature on the microstructure of porous TiO<Subscript>2</Subscript> film

To obtain porous TiO₂ film, the precursor sol was prepared by hydrolysis of Ti isopropoxide and then complexed with trehalose dihydrate. The porous TiO₂ film was fabricated by the dip-coating technique on glass substrates using this solution. The TiO₂ film was calcined at 500 °C. The maximum thickness of the film from one-run dip-coating was ca. 740 nm. The film was composed of nanosized particle and pores. The porosity of the TiO₂ film was increased by addition of trehalose dihydrate to the sol. The porous TiO₂ films were calcined at different temperatures. The effects of calcination temperature on the microstructure of the porous TiO₂ film were investigated. The porous film prepared from sol containing trehalose still kept the porous structure after calcination at 950 °C. The phase transition temperature of the film from anatase to rutile was shifted from 650 to 700 °C by addition of trehalose to the sol.     

Preparation of Ca<Subscript>3</Subscript>Co<Subscript>4</Subscript>O<Subscript>9</Subscript> by polyacrylamide gel processing and its thermoelectric properties

Ca₃Co₄O₉ powder was prepared by a polyacrylamide gel route in this paper. The effect of the processing on microstructure and thermoelectric properties of Ca₃Co₄O₉ ceramics via spark plasma sintering were investigated. Electrical measurement shows that the Seebeck coefficient and conductivity are 170 μV/K and 128 S/cm, respectively, at 700 °C, yielding a power factor value of 3.70 × 10⁻⁴ W m⁻¹ K⁻² at 700 °C, which is larger than that of Ca₃Co₄O₉ ceramics via solid-state reaction processing. The polyacrylamide gel processing is a fast, cheap, reproducible and easily scaled up chemical route to improve the thermoelectric properties of Ca₃Co₄O₉ ceramics by preparing the homogeneous and pure Ca₃Co₄O₉ phase.     

Optimization on fabrication and performance of A-site-deficient La0.58Sr0.4Co0.2Fe0.8O3-δ cathode for SOFC

A-site-deficient perovskite cathode material La_0.58Sr_0.4Co_0.2Fe_0.8O_3 − δ (L58SCF) is coated on the yttria-stabilized zirconia electrolyte by screen-printing technique. Several key fabrication parameters including selection of additives (binder and pore former), effect of coating thickness, sintering temperature and time on the microstructure, and electrochemical performance of cathode are investigated by scanning electron microscopy and electrochemical impedance spectroscopy. We study the microstructure and the electrochemical property of the cathode with different kinds of additives. Results show that the cathode possesses fine microstructure, enough porosity, and ideal electrochemical property when polyvinyl butyral serves as both binder and pore former in the cathode. The cathode with three screen-printing coats (thickness 28 ± 7 μm, weight 6.07 ± 0.72 mg cm⁻²) sintering at 1,000 °C for 2 h shows lower polarization resistance of 0.183 Ω cm² at 800 °C. Based on the optimized parameters, the polarization resistances of the L58SCF–Ce_0.8Gd_0.2O_{1.9 – δ} composite cathode display the R _p values of 0.067 Ω cm² at 800 °C, 0.106 Ω cm² at 750 °C, 0.225 Ω cm² at 700 °C, and 0.550 Ω cm² at 650 °C.