Luminescence kinetics of LiNbO3:Yb3+-Er3+, LiNbO3:Er3+, and LiNbO3:Yb3+ crystals under selective excitations in the impurity subsystem

The results of investigations of luminescent radiations’ kinetic characteristics for LiNbO₃:Yb³⁺-Er³⁺, LiNbO₃:Er³⁺, and LiNbO₃:Yb³⁺ crystals under optical excitations at 532 nm and 1064 nm wavelengths are presented. The shapes and times of rise and damping of luminescent signals at 550 nm, 980 nm and 1555 nm wavelengths under selective excitations in the impurity subsystem of the investigated materials are determined. Comparison of the temporal characteristics of luminescent responses of LiNbO₃ crystals doped separately with Yb³⁺ and Er³⁺ ions with those of the LiNbO₃:Yb³⁺-Er³⁺ crystal allows identifying the contributions from different energy transfer processes of optical excitation taking place in the impurity subsystem of the material.     

Luminescence spectroscopy of Er-doped and Er, Yb-codoped LaPO4 single crystals

LaPO₄ single crystals lightly doped with Er³⁺, and codoped with Er³⁺ and Yb³⁺ have been grown by spontaneous nucleation in a lead phosphate flux. Absorption and luminescence spectra have been measured in the visible and near-IR regions and the excited state dynamics has been studied upon pulsed laser excitation. The obtained results have allowed the evaluation of the effective emission cross-sections around 1.5 μm, that have been found to be similar to important oxide laser crystals doped with Er³⁺. Efficient visible upconversion has been observed upon excitation at 980 nm in the codoped crystals. This behaviour is attributed to Yb³⁺-Er³⁺ energy transfer processes.     

Preparation and characterization of upconversion luminescent LaF3:Yb,Er/LaF3 core/shell nanocrystals

LaF₃:Yb³⁺,Er³⁺/LaF₃ core/shell nanocrystals were successfully synthesized using solvothermal method. The crystal structure, morphology and photoluminescence properties of as-prepared nanocrystals were investigated in detail. XRD patterns show that the obtained LaF₃:Yb³⁺,Er³⁺ core and LaF₃:Yb³⁺,Er³⁺/LaF₃ core/shell nanocrystals exhibit hexagonal structure. The average particle size is about 9.3 nm and 11.4 nm for core and core/shell nanocrystals, respectively. Compared with LaF₃:Yb³⁺,Er³⁺ nanocrystals, both the upconversion emission intensity and the lifetime increase in LaF₃:Yb³⁺,Er³⁺/LaF₃ core/shell nanocrystals. The enhancement can be attributed to the LaF₃ shell which can eliminate the nonradiative centers on the surface of LaF₃:Yb³⁺,Er³⁺ nanocrystals.     

Group delay dispersion measurement of Yb:YAl3(BO3)4 crystal with white-light interferometry

We report the group delay dispersion of Yb³⁺:YAl₃(BO₃)₄ (Yb:YAB) crystal measured by a white-light interferometer, and compare with that calculated from the Sellmeier formulae provided by the crystal supplier, over the wavelength range from 1000 nm to 1080 nm. The data should be useful for the dispersion compensation for femtosecond pulse generation in Yb:YAB lasers.     

Enhancement of upconversion luminescence in Tm/Er/Yb-codoped glass ceramic containing LiYF4 nanocrystals

A transparent Er³⁺–Tm³⁺–Yb³⁺ tri-doped oxyfluoride glass ceramics containing LiYF₄ nanocrystals were prepared. Under 980 nm laser diode (LD) pumping, intensive red, green and blue upconversion (UC) was obtained. The blue, green, and red UC radiations correspond to the transitions ¹G₄→³H₆ of Tm³⁺, ²H_11/2/⁴S_3/2→⁴I_15/2, and ⁴F_9/2→⁴I_15/2 of Er³⁺ ions, respectively. This is similar to that in Tm³⁺–Yb³⁺ and/or Er³⁺–Yb³⁺ co-doped glass ceramics. However, the blue UC radiations of the Er³⁺–Yb³⁺ co-doped glass ceramics is two-photon process due to cooperative energy transfer. The UC mechanisms were proposed based on spectral, kinetic, and pump power dependence analyses.     

Optical and EPR study of BaY2F8 single crystals doped with Yb

Optical and electron paramagnetic resonance study have been carried out on BaY₂F₈ single crystals doped with Yb ions at 0.5 and 10 mol%. The crystals have been obtained using the Czochralski method modified for fluoride crystal growth. Optical transmission measurements in the range of 190-3200 nm and photoluminescence measurements were carried out at room temperature. Absorption spectra of BaY₂F₈ single crystals doped with Yb due to the ²F_7/2→²F_5/2 transitions have been observed in the 930-980 nm range. To analyze the possible presence of Yb²⁺ ions in the investigated crystals, irradiation with γ-quanta with a dose of 10⁵ Gy have been performed. The observed photoluminescence bands show usual emission in IR and other one in VIS, being an effect of cooperative emission of Yb³⁺ ions and energy up-conversion transitions of photons from IR to UV-vis(visible) due to hoping process between energy levels of paired Yb³⁺ and Er³⁺, where Er³⁺ ions are unintentional dopants. The EPR spectra of BaY₂F₈:Yb 10 mol% consist of many overlapping lines. They have been analyzed in terms of spin monomers, pairs, and clusters. The angular dependence of the resonance lines positions have been studied also to find the location of coupled ytterbium ions in the crystal structure.     

The up-conversion properties of Yb and Er doped Y4Al2O9 phosphors

Er³⁺ doped and Yb³⁺/Er³⁺ co-doped Y₄Al₂O₉ phosphors are prepared by the sol-gel method. The effect of dopant concentration on the structure and up-conversion properties is investigated by X-ray diffraction (XRD) and photoluminescence, respectively. XRD pattern indicates that the sample structure belongs to monoclinic. Under 980 nm excitation, the green and red up-conversion emissions are observed and the emission intensities depended on the Yb³⁺ ion concentration. The green up-conversion emissions decrease with the increase of Yb³⁺ concentration, while red emission increases as Yb³⁺ concentration increases from 0 to 8 at% and then decreases at high Yb³⁺ concentration. The mechanisms of the up-conversion emissions are discussed and results shows that in Er³⁺ and Yb³⁺/Er³⁺ co-doped system, cross-relaxation (CR) and energy transfer (ET) processes play an important role for the green and red up-conversion emissions.     

Optical spectroscopy of Yb/Er codoped NaY(WO4)2 crystal

Erbium and ytterbium codoped double tungstates NaY(WO₄)₂ crystals were prepared by using Czochralski (CZ) pulling method. The absorption spectra in the region 290-2000 nm have been recorded at room temperature. The Judd-Ofelt theory was applied to the measured values of absorption line strengths to evaluate the spontaneous emission probabilities and stimulated emission cross sections of Er³⁺ ions in NaY(WO₄)₂ crystals. Intensive green and red lights were measured when the sample were pumped by a 974 nm laser diode (LD), especially, the intensities of green upconversion luminescence are very strong. The mechanism of energy transfer from Yb³⁺ to Er³⁺ ions was analyzed. Energy transfer and nonradiative relaxation played an important role in the upconversion process. Photoexcited luminescence experiments are also fulfilled to help analyzing the transit processes of the energy levels.     

Er3+及Er3+/Yb3+掺杂ZrO2-Al2O3的制备及发光性质

采用共沉淀法制备了纳米晶ZrO₂-Al₂O₃∶Er³⁺发光粉体.所制备的粉体室温下具有Er3+离子特征荧光发射,主发射在绿光,其中位于547 nm、560 nm的绿光最强,并得出稀土离子与基质之间有能量传递.对不同煅烧温度下的样品研究表明:因不同温度下所制得的样品晶相不同.研究了纳米晶ZrO2-Al2O3∶Er3+及ZrO₂-Al₂O₃∶Er³⁺/Yb³⁺的上转换发光,并分析了上转换的跃迁机制.发现ZrO₂-Al₂O₃∶Er³⁺的绿光为双光子过程,而ZrO₂-Al₂O₃∶Er³⁺、Yb³⁺的上转换光谱中,红光和绿光也为双光子过程,而极弱的蓝光为三光子过程.讨论了Er³⁺的浓度猝灭现象.最适宜掺杂浓度的原子分数为2%（Er³⁺/Zr⁴⁺）.     

The fluorescence properties of Yb3+ and Er3+ Co-doped YAl3(BO3)4 powders prepared by sol-gel method

Yb³⁺ and Er³⁺ co-doped YAB powders were prepared by sol-gel method. The structure and fluorescence properties were investigated. XRD pattern indicated that the single phase was obtained at 1150°C and the structure belonged to rhombohedral. Under 379 nm excitation, two emissions around 983 nm and 1531 nm were observed and the effect of Yb³⁺ ion concentration on the emission intensity was discussed. The energy transfer was observed under 930 nm excitation and the energy transfer efficiencies for all samples were calculated. The lifetimes of ² F _5/2 level of Yb³⁺ ion and ⁴ I _13/2 level of Er³⁺ ion were measured and the effect of Yb³⁺ ion concentration on the lifetime was also discussed. The results indicated that there was an additional mechanism for the decay of ⁴ I _13/2 level in powder samples. The Yb³⁺ and Er³⁺ co-doped YAB powders should be a potential candidate for ceramic laser materials.     

Er3+，Er3+/Yb3+掺杂氟化镧超微材料的光谱特性与上转换发光

采用共沉淀法制备了Er³⁺掺杂和Er³⁺/Yb³⁺共掺杂LaF₃超微材料,所制备的样品的颗粒呈球形,尺寸为250nm左右.计算得到Er³⁺单掺杂样品中对应着⁴S_3/2和⁴F_9/2能级的发光量子效率分别为67.0%和71.9%.研究发现,随着Yb³⁺离子浓度的增加 关键词： 3+')" href="#">Er³⁺ 3+')" href="#">Yb³⁺ 发光 能量传递     

Preparation and upconversion properties of Ba2ErF7 and Ba2ErF7:Yb powders

Novel Ba₂ErF₇ and Yb³⁺-doped Ba₂ErF₇ powders were synthesized by a coprecipitation method. In Ba₂ErF₇ sample, abundant upconverted emission bands from violet to infrared region are observed under 980 nm excitation, whereas only green and red emissions are observed under 812 nm excitation. Under the two excitations, the luminescence decay curves of the green and red emissions are measured and the quenching behaviors of Yb³⁺ doping are also explored. It is found that a suitable Yb³⁺ concentration can efficiently enhance the intensity ratio of the blue and violet emissions to the green and red ones, which may be due to the competition between the energy transfer process from Er³⁺ to Yb³⁺ and the sensitizing process from Yb³⁺ to Er³⁺ in Ba₂ErF₇:Yb³⁺. This indicates that the Yb³⁺-doped Ba₂ErF₇ might be a good candidate for blue and violet upconversion phosphor.     

Influence of Yb doping concentration on upconversion luminescence of Er in Lu2O3 phosphor

Cubic phase Lu₂O₃:Er³⁺/Yb³⁺ nanocrystal phosphors were prepared by sol–gel method. Fourier transform infrared (FT-IR) spectra were measured to evaluate the vibrational feature of the samples. Green and red radiations were observed upon 980 nm diode laser excitation. Laser power and Er³⁺ or Yb³⁺ doping concentration dependence of upconversion luminescence were studied to understand upconversion mechanisms. Excited state absorption, cross relaxation and energy transfer processes are the possible mechanisms for the visible emissions.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Investigation of infrared to visible conversion in Cs2Na(Er0.2Yb0.4Y0.4)Cl6 crystal

A conversion of infrared radiation into green fluorescence of Er⁺³ in centrosymmetric Cs₂Na(Er_0.2Yb_0.4Y_0.4)Cl₆ crystals is examined and interpreted on the basis of stepwise energy transfer mechanism. Some aspects of the conversion process are discussed.     

Ce3+对Er3+/Yb3+共掺氟磷酸盐玻璃光谱性质的影响

研究了能量接受离子Ce³⁺对Er³⁺上转换发光强度以及Er³⁺在1.5μm附近波段发光性能参数的影响，并从能量匹配及能级结构角度出发对Er³⁺/Ce³⁺间的能量转移机制进行了分析.分析认为，⁴I_11/2能级的Er³⁺通过无辐射能量转移把能量传递给²F_5/2能级的Ce³⁺关键词： 氟磷酸盐玻璃 光谱性质 光纤放大器 3+和Ce³⁺')" href="#">Er³⁺和Ce³⁺     

Visible upconversion emission and non-radiative direct Yb to Er energy transfer processes in nanocrystalline ZrO2:Yb,Er

Wide band gap Yb³⁺ and Er³⁺ codoped ZrO₂ nanocrystals have been synthesized by a modified sol-gel method. Under 967 nm excitation strong green and red upconversion emission is observed for several Er³⁺ to Yb³⁺ ions concentration ratios. A simple microscopic rate equation model is used to study the effects of non-radiative direct Yb³⁺ to Er³⁺ energy transfer processes on the visible and near infrared fluorescence decay trends of both Er³⁺ and Yb³⁺ ions. The microscopic rate equation model takes into account the crystalline phase as well as the size of nanocrystals. Nanocrystals phase and size were estimated from XRD patterns. The rate equation model succeeds to fit simultaneously all visible and near infrared fluorescence decay profiles. The dipole-dipole interaction parameters that drive the non-radiative energy transfer processes depend on doping concentration due to crystallite phase changes. In addition the non-radiative relaxation rate (⁴I_11/2→⁴I_13/2) is found to be greater than that estimated by the Judd-Ofelt parameters due to the action of surface impurities. Results suggest that non-radiative direct Yb³⁺ to Er³⁺ energy transfer processes in ZrO₂:Yb,Er are extremely efficient.     

Crystal growth and spectroscopic characterization of Yb:LiTaO3

Spectroscopic properties are presented for Yb³⁺ incorporated into single crystals of LiTaO₃ grown by the top-seeded solution growth method. From an analysis of the absorption and fluorescence spectra, we are able to determine the Stark-level components of the ²F_7/2 (the ground-state multiplet manifold) and the ²F_5/2 (the excited-state multiplet manifold of Yb³⁺ (4f¹³)). The room-temperature fluorescence lifetime of ²F_5/2 is 678 μs as measured on a thin sample to reduce possibilities for reabsorption. Spectral comparisons of Yb³⁺-doped LiTaO₃ and LiNbO₃ are drawn. The crystal-field splitting of Yb³⁺(4f¹³) in both crystal hosts is modeled using a set of crystal-field splitting parameters, B_nm, determined from a recent spectroscopic analysis of Er³⁺(4f¹¹) in LiNbO₃. Without adjustment of the B_nm parameters, the model predicts the Stark-level energy and the symmetry label for each level in reasonable agreement with the experimental values. Less photorefractive than its niobate cousin, LiTaO₃ has potential for use in numerous integrated electro-optical circuits and devices.     

Spectroscopic properties of Yb ions in La2(WO4)3 crystal

Yb³⁺-doped La₂(WO₄)₃ single crystals were grown by the Czochralski technique. Absorption and fluorescence spectra of the crystal were recorded at the room temperature. The stimulated emission cross-sections of Yb³⁺ ions were calculated using the reciprocity method and Fuchtbauer-Ladenburg formula, respectively. The fluorescence decay curves of ²F_5/2 manifold of Yb³⁺ ions were recorded at room temperature for both crystal and powder samples. The effect of radiation trapping on the spectroscopic properties is discussed. Comparison with other Yb³⁺-doped laser crystals is made. The results show that Yb³⁺:La₂(WO₄)₃ crystal is a promising laser material.     

Optical parameters of Nd3＋：Er3＋：yb3＋ co-doped borosilicate glasses and their energy transfers at high temperature

This paper reports that a series of Nd³⁺:Er³⁺:Yb³⁺ co-doped borosilicate glasses have been prepared and their absorption spectra measured. The J--O intensity parameters Ω_k (k=2, 4, 6), spontaneous radiative lifetime τ_rad, spontaneous transition probability A, fluorescence branching ratio β and oscillator strength f_ed of the Nd³⁺ ions at room temperature are calculated based on Judd--Ofelt (J--O) theory. The temperature dependence of the up-conversion photoluminescence characteristics in a Nd³⁺:Er³⁺:Yb³⁺ co-doped sample is studied under a 978 nm semiconductor laser excitation, and the energy transfer mechanisms among Yb³⁺, Er³⁺ and Nd³⁺ ions are analysed. The results show that the J--O intensity parameters Ω₂ increase when the Nd³⁺ concentration of the Nd³⁺:Er³⁺:Yb³⁺ co-doped borosilicate glasses increases. The possibility of spontaneous transition is small and lifetimes are long at levels of ⁴F_5/2 and ⁴F_3/2. The intensity of Nd³⁺ emissions at 595, 691, 753, 813 and 887 nm are markedly enhanced when the sample temperature exceeds 400 K. The reasons being the cooperation of the secondary sensitization from Er³⁺ to Nd³⁺ and the contribution of a multi-phonon.