Production of micron-sized monodispersed core/shell composite polymer particles by seeded dispersion polymerization

 The effect of the weight ratio of seed polymer/monomer on the morphology of the poly(methyl methacrylate) (PMMA)/polystyrene (PS) monodispersed composite particles produced by batch seeded dispersion polymerization of styrene with 1.64-μm-sized monodispersed PMMA seed particles in a methanol/water medium (4/1 w/w) was examined. In the PMMA/PS weight ratios of 3/1 and 2/1, the composite particles had a clear morphology consisting of a PMMA core and a PS shell. In the ratio of 1/1, a lot of small PS domains were observed in the PMMA core though the PS shell was still formed. By stepwise addition of styrene monomer, the formation of the small PS domain was depressed and complete core/shell morphology was formed. Absorption/release treatments of toluene into/from the PMMA/PS (1/1 w/w) composite particles resulted in a drastic morphological change from the core/shell structure to a multi- layered one. Received: 2 February 1999 Accepted in revised form: 7 April     

Production of micron-sized, monodispersed, multilayered composite polymer particles by multistep seeded dispersion polymerization

 Micron-sized, monodispersed, poly(methyl methacrylate) (PMMA)/polystyrene (PS)/PMMA/PS multilayered composite particles were successfully produced by three-step seeded dispersion polymerizations in methanol/water media. The first seeded dispersion polymerization was carried out with 2-μm-sized, monodispersed PMMA particles.     

Production of electrically conductive, core/shell polystyrene/polyaniline composite particles by chemical oxidative seeded dispersion polymerization

Micron-sized, monodispersed, electrically conductive polystyrene (PS)/polyaniline (PAn) composite particles were produced by chemical oxidative seeded dispersion polymerization of aniline at 0 °C with 1.37-μm-sized, monodispersed PS seed particles in HCl aqueous solution, where the pH value was kept at 2.5 with a pH stat. The composite particles consisted of a PS core and a PAn shell. A pellet of the composite particles had a conductivity of 3.4 × 10⁻³ S/cm. Received: 5 April 2000 Accepted: 10 August 2000     

Production of micron-sized monodispersed composite polymer particles by seeded polymerization utilizing the dynamic swelling method

 In order to develop the seeded polymerization technique utilizing the dynamic swelling method (DSM) proposed by authors for the production of micron-sized mono-dispersed “composite” polymer particles consisting of two kinds of polymers, the seeded polymerization for the dispersion of ethyl methacry-late (EMA)-swollen PS particles prepared utilizing DSM was carried out. Monodispersed PS/poly(ethyl methacrylate) (PEMA) composite particles having 7 μm in diameter were produced by the addition of NaCl to lower the solubility of EMA in medium and by the addition of CuCl₂ as a water-soluble inhibitor to depress the by-production of submicron-sized PEMA particles. Received: 16 July 1996 Accepted: 10 October 1996     

Production of micron-sized, monodisperse composite polymer particles having epoxy groups by seeded dispersion polymerization

 Micron-sized, monodisperse polystyrene (PS)/glycidyl methacrylate–divinylbenzene copolymer core/shell composite particles having epoxy groups in the shells were produced by seeded dispersion copolymerization of glycidyl methacrylate and divinylbenzene in an ethanol/water medium with 1.65-μm-sized, monodisperse PS seed particles. By chemical modifications of epoxy groups with sodium hydrogensulfite and dimethylamine, composite polymer particles having sulfonate and dimethylamino groups, respectively, in the shells were prepared. Received: 13 September 2000 Accepted: 31 January 2001     

Production of core/shell polystyrene/poly(3,5-xylidine) composite particles by chemical oxidative seeded dispersion polymerization

Micron-sized monodispersed polystyrene (PS)/poly(3,5-xylidine) (PXy) composite particles were produced by chemical oxidative seeded dispersion polymerization of 3,5-xylidine at 20 °C with 1.6-μm-sized monodispersed PS seed particles in HCl aqueous solution, the pH of which was always kept at 2.5 with a pH stat. The composite particles produced consisted of a PS core and a PXy shell. Received: 16 December 1998 Accepted in revised form: 25 March 1999     

Influences of the locations of monomer and initiator in the seeded polymerization systems on the morphologies of micron-sized monodispersed composite polymer particles

Three kinds of micron-sized monodispersed polystyrene (PS)/poly(n-butyl methacrylate) (PBMA) composite particles (PS/BMA=2/1, wt. ratio) were produced by two kinds of seeded polymerizations ofn-butyl methacrylate (BMA) in the presence of about 2 m-sized monodispersed PS particles, and their morphologies were examined. One was produced by a seeded dispersion polymerization where almost monomers and initiators exist in an ethanol/water (1/1, w/w) medium. The others two were produced by seeded polymerizations utilizing the dynamic swelling method, where almost monomers exist in the PS seed particles, with 2,2-azobisisobutyronitrile initiator in the monomer-swollen particles and with 2,2-azobis [2-(2-imidazolin-2-yl)propane] initiator in an ethanol/water (1/5, w/w) medium. In the former polymerization, the produced composite particles had a core-shell structure consisting of a PS-core and a PBMA-shell, whereas in the latter two polymerizations, they had a POO (Polymeric Oil-in-Oil) structure consisting of a PS-matrix and many PBMA-domains, regardless of the location of initiator in the systems. From these results, it is concluded that the location of BMA monomer in the seeded polymerization systems with micron-sized monodispersed PS seed particles greatly affects the morphologies of produced PS/PBMA composite particles.Part CLI of the series Studies on Suspension and Emulsion     

Morphology of anomalous polystyrene/ polybutyl acrylate composite particles produced by seeded emulsion polymerization

 Recently, we found that “golf ball”-like polystyrene (PS)/polybutyl acrylate (PBA) composite particles could be produced by seeded emulsion polymerization of butyl acrylate (BA) with PS seed particles. In this article, the effects of the polymerization temperature, BA monomer concentration, and the presence of 1-octanol, which is a good solvent for PBA and a poor solvent for PS in the polymerization, on the morphology was studied. Received: 25 February 1997 Accepted: 4 October 1997     

Morphology of micron-sized monodispersed poly(butyl methacrylate)/polystyrene composite particles produced by seeded dispersion polymerization

In order to develop the seeded dispersion polymerization technique for the production of micron-sized monodispersed core/shell composite polymer particles the effect of polymerization temperature on the core/shell morphology was examined. Micron-sized monodispersed composite particles were produced by seeded dispersion polymerizations of styrene with about 1.4-μm-sized monodispersed poly(n-butyl methacrylate) (Pn-BMA) and poly(i-butyl methacrylate) (Pi-BMA) particles in a methanol/water (4/1, w/w) medium in the temperature range from 20 to 90 °C. The composite particles, PBMA/polystyrene (PS) (2/1, w/w), consisting of a PBMA core and a PS shell were produced with 2,2′-azobis(4-methoxy-2,4-dimethyl valeronitrile) initiator at 30 °C for Pn-BMA seed and with 2,2′-azobis(isobutyronitrile) initiator at 60 °C for Pi-BMA seed. The polymerization temperatures were a little above the glass-transition temperatures (T _g) of both Pn-BMA (20 °C) and Pi-BMA (40 °C). On the other hand, when the seeded dispersion polymerizations were carried out at much higher temperatures than the T _g of the seed polymers, composite particles having a polymeric oil-in-oil structure were produced. Received: 14 October 1998 Accepted in revised form: 2 June 1999     

Morphology of micron-sized monodispersed composite polymer particles produced by seeded polymerization for the dispersion of highly monomer-swollen polymer particles

 Monodispersed polystyrene (PS)/poly(n-butyl methacrylate) (PBMA) composite particles having 9.4 μm in diameter were produced by seeded polymerization for the dispersion of highly n-butyl methacrylate (BMA)-swollen PS particles, and their morphologies were examined. The highly BMA-swollen PS particles (about 150 times the weight of the PS seed particles) were prepared by mixing monodispersed 1.8 μm-sized PS seed particles and 0.7 μm sized BMA droplets prepared with an ultrasonic homogenizer in ethanol/water (1/2, w/w) medium at room temperature. After NaNO₂ aqueous solution as inhibitor was added in the dispersion, the seeded polymerization was carried out at 70 °C. In an optical microscopic observation, one or two spherical high contrast regions which consisted mainly of PS were observed inside PS/PBMA composite particles. In the PS domain, there were many fine spherical PBMA domains. Such morphologies were based on the phase separation of PS and PBMA within the homogeneous swollen particles during the seeded polymerization. Received: 04 June 1997 Accepted: 27 August 1997     

Preparation of polystyrene/poly (4-butyltriphenylamine) composite particles by chemical oxidative seeded dispersion polymerization

Polystyrene (PSt)/poly (4-butyltriphenylamine; PBTPA) composite particles was prepared by a chemical oxidative seeded dispersion polymerization of (4-butyltriphenylamine) with PSt seed particles that were prepared by nonaqueous dispersion polymerization of styrene. Monodisperse composite particles were obtained when the ratio of monomer to seed, the rate of monomer feed, and poly(N-vinyl pyrrolidone; PVP) concentration was appropriately selected. The introduction of PBTPA was confirmed by the presence of the characteristic absorption band attributed to PBTPA from a Fourier transform infrared spectra. The solvent extraction with ethyl acetate revealed that composite particles consisted of PSt core and PBTPA shell. Then two-dimensional arrays of composite particles were also fabricated.     

Production of micron-sized monodispersed polymer particles by seeded polymerization for the dispersion of highly monomer-swollen particles prepared with submicron-sized polymer seed particles utilizing the dynamic swelling method

For the purpose of extending the size range of polymer seed particles used in “dynamic swelling method” (DSM), first it was verified theoretically that the submicron-sized polymer particles produced by emulsion polymerization can also absorb a large amount of monomer by DSM in both equilibrium and kinetic control states. Next, on the basis of the theoretical results, experimentally about 2.6 μm-sized styrene-swollen polystyrene (PS) particles were prepared utilizing DSM in the presence of 0.64 μm-sized monodispersed PS seed particles produced by emulsifier-free emulsion polymerization. Moreover, 2.5 μm-sized monodispersed PS particles were produced by the addition of cupric chloride as a water-soluble inhibitor to depress the by-production of submicron-sized PS particles in the seeded polymerization at 30°C with 2,2′-azobis(4-methoxy-2,4-dimethylvaleronitrile) initiator. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. A Polym. Chem. 36: 2513–2519, 1998     

Production of micron-sized, monodispersed, multihollow polystyrene/poly(3,5-xylidine) composite particles by chemical oxidative seeded polymerization

 Micron-sized, monodispersed polystyrene/poly(3,5-xylidine) composite polymer particles were produced by chemical oxidative seeded polymerization of 3,5-xylidine with 1.37-μm-sized, monodispersed polystyrene seed particles. The chemical oxidative seeded polymerization was conducted in an aqueous medium at 25 °C in the presence of poly(vinyl alcohol) as a stabilizer using ammonium persulfate as an oxidant. The composite particles had a multihollow structure. Received: 30 June 1999/Accepted in revised form: 21 October 1999     

Influence of particle diameter on the morphology of micron-sized, monodispersed composite polymer particles produced by seeded polymerization for the dispersion of highly monomer-swollen polymer particles

 Micron-sized, monodispersed polystyrene (PS)/poly (n-butyl methacrylate) (PBMA) composite particles, in which the PS domain(s) were dispersed in a PBMA continuous phase, were produced by seeded polymerization for dispersions of n-butyl methacrylate (BMA) swollen PS particles in a wide range of PS/BMA ratios in the presence of NaNO₂ as a water-soluble inhibitor. Moreover, in order to change the diameter of the composite particles at same PS/BMA ratio, PS/PBMA (1/150 w/w) composite particles were produced using five kinds of PS particles in a range of diameters from 0.64 to 3.27 μm as seeds. The percentages of the PS/PBMA composite particles having double and triple and over PS domains, which were thermodynamically unstable morphologies, increased with the increase in the diameter of BMA swollen PS particles. There was a clear influence of the size of the swollen particles on the morphology of the PS/PBMA composite particles produced. Received: 30 September 1999/Accepted: 18 April 2000     

Influence of the swelling state of seed polymer particles with monomer on the morphology of micron-sized monodispersed composite polymer particles produced by seeded polymerization utilizing the dynamic swelling method

 Micron-sized mono-dispersed polystyrene (PS)/poly(n-butyl methacrylate) (PBMA) composite particles (PS/PBMA=2/1 by weight) having a heterogeneous structure in which many fine PBMA domains dispersed in a PS matrix near the particle surface were produced by seeded polymerization of n-butyl methacrylate (BMA) of which almost all had been absorbed by 1.8 μm-sized monodispersed PS seed particles utilizing the dynamic swelling method. The morphology was varied by changing the PS/BMA ratio and polymerization temperature. It was concluded that the swelling state of 2 μm-sized BMA-swollen PS particles in the seeded polymerization process is one of the important factors to control the morphology of the composite particles. Received: 27 November 1996 Accepted: 21 March 1997     

Preparation of micron-size monodisperse poly(2-hydroxyethyl methacrylate) particles by dispersion polymerization

Dispersion polymerization of 2-hydroxyethyl methacrylate using four categories of polymeric stabilizers in a mixture of good and poor solvents was performed to produce polymeric particles. The stabilizers employed were methyl methacrylate and styrene homopolymers, methacryloyl-terminated poly(methyl methacrylate) and polystyrene macromonomers, an amphiphilic poly(methyl methacrylate-co-methacrylic acid-graft-styrene), and polybutadiene derivatives containing reactive vinyl groups. Dispersion copolymerization with a small amount of the macromonomer gave micron-size particles with relatively narrow size distribution. The amphiphilic graft copolymer and the polybutadiene derivatives also afforded monodisperse particles. The mixed ratio between good and poor solvents greatly affected the particle size and size distribution. © 1996 John Wiley & Sons, Inc.     

Preparation and characterization of micron-sized polystyrene/polysiloxane core/shell particles

A procedure has been developed to coat micron-sized polystyrene (PS) spheres with a smooth layer of polysiloxane by a sol–gel process of methyl trimethoxylsilane (MTMS) without using silane coupling agents. The thickness of the shells can be easily varied with different polystyrene seeds and methyl trimethoxysilane feed ratio. When we used PS particles with diameters of 2.09 μm prepared by conventional dispersion polymerization as seeds, the thickness of the polysiloxane shells can be varied from 0.11 to 0.21 μm. The particle size, size distribution, thermal decomposition, and solvent resistance were investigated by scanning electron microscope (SEM), transmission electron microscope (TEM), size analyzer, and TG, respectively.     

Morphological investigations of crosslinked polystyrene microspheres by seeded polymerization

 Crosslinked polystyrene microspheres with novel surface and inner morphologies were synthesized by seeded polymerization following a seed-swelling method, using uncrosslinked polystyrene microspheres as seeds and a mixture of toluene, styrene (St), and divinylbenzene (DVB) as the swelling agent. With the increasing toluene/ (St+DVB) ratio, the crosslinked particles changed from smooth-surfaced spheres to deformed spheres with dimples or heavy dents at the surface. A single hole inside the spherical particles was produced at low St/DVB ratio, while higher St/DVB ratios gave irregular dented or dimpled particles. Ultrathin cross-section observation by TEM revealed a non-uniformly crosslinked inner structure. Received: 20 January 1998 Accepted: 14 April 1998     

Micron-sized monodispersed polymer particles produced by seeded polymerization for the dispersion of high swelling of polymer particles with a large amount of monomer

 Micron-sized monodispersed polystyrene (PS)/poly(n-butyl methacrylate) composite particles were produced as follows. First, 1.77 μm-sized monodispersed PS seed particles produced by dispersion polymerization were dispersed in ethanol/water (1/2, w/w) medium dissolving poly(vinyl alcohol) as a stabilizer. n-Butyl methacrylate (BMA) monomer dissolving benzoyl peroxide initiator was emulsified in ethanol/water (1/2, w/w) solution of sodium dodecyl sulfate as emulsifier with ultrasonic homogenizer, and the BMA monomer emulsion was mixed with the PS seed emulsion. The PS seed particles absorbed with a large amount of BMA (about 150 times weight of the seed particles) for 2 h to about 10 μm in diameter while keeping good monodispersity and BMA droplets disappeared finally. The seeded polymerization was carried out at 70 °C after a certain amount of water was added to depress the redissolving of BMA from the swollen particles into the medium by raising from room temperature to the polymerzation temperature. Received: 21 February 1996 Accepted: 4 September 1996     

Preparation of monodispersed polystyrene microspheres uniformly coated by magnetite via heterogeneous polymerization

Composite microspheres of core-shell type were prepared by a seeded polymerization using monodispersed polystyrene seed latex (Ps) combined with an in situ dispersion of magnetite (Fe₃O₄) fine particles. The heterogeneous polymerization was carried out in aqueous dispersions of the Fe₃O₄ particles modified with sodium oleate. All the synthetic processes were carried out in a wet state to avoid serious agglomeration. The morphology of the composite particle and the size distribution were examined to discuss the effects on the polymerization parameters, such as monomer concentration, type and concentration of an initiator, magnetite particle concentration and the method of surface modification of Fe₃O₄.