HA在PVA/CMC共混膜上的交互沉积及其表征

用溶液浇铸法制备聚乙烯醇/羧甲纤维素钠(PVA/CMC)共混膜,在对其进行交联改性的基础上,通过交互沉积法在膜表面沉积羟基磷灰石(HA),以制备PVA/CMC/HA复合材料。通过SEM、FT-IR、XRD等对其进行表征,探索PVA与CMC共混比例及交互周期对HA矿化速率的影响。结果表明,经过交联后的薄膜,在醇水混合溶液中能够稳定存在,其表面生成的HA含量随着交互周期和CMC含量的增加有明显增加,这种共混薄膜材料有望成为软骨修复材料的有效基体。     

纳米羟基磷灰石/聚乙烯醇/明胶复合材料的结构和力学性能

采用机械共混法、原位化学合成法、原位水热法制备了一系列纳米羟基磷灰石/聚乙烯醇/明胶(n-HA/PVA/GEL)复合材料;利用X射线衍射仪、透射电镜及傅立叶变换红外光谱仪等分析了复合材料的结构;利用材料试验机测定了复合材料的力学性能.结果表明,利用原位水热法可使n-HA有效地在PVA高分子中均匀分散,并提高n-HA颗粒...     

β成核剂修饰多壁碳纳米管增强聚丙烯纳米复合材料的分散及结晶行为

利用非共价键改性方法,用芳香二羧酸酰胺类的β成核剂(β-NA)改性多壁碳纳米管(MWCNTs),采用溶液法制备了聚丙烯(PP)/β-NA-MWCNTs复合材料.通过广角X射线衍射(WAXD)分析了复合材料的结晶形态,结果表明β-NA-MWCNTs诱导聚丙烯生成大量β晶,同时提高了复合材料的结晶度.含5.0 wt％β-N...     

相分离对聚偏氟乙烯/聚甲基丙烯酸甲酯共混物的力学与耐紫外老化性能的影响

采用熔融共混法制备聚偏氟乙烯/聚甲基丙烯酸甲酯( PVDF/PMMA)共混物,考察其力学性能、耐紫外老化性能、熔体动态流变、结晶与热分解行为.PMMA含量(wPMMA)为10 wt％时,共混物形成均相结构,力学与耐老化性能最好.wPMMA≥20 wt％时,PMMA形成球状聚集体,共混物力学性能与耐候性显著降低.PMMA的存在可提高PVDF的结晶度,降低熔融温度,但不改变PVDF晶体结构.     

聚偏氟乙烯-磺化聚醚砜相容性及其成膜性能

研究了聚偏氟乙烯(PVDF)-磺化聚醚砜(SPES)的相容性及其成膜性能.首先通过溶解度参数、粘度法和目测法研究共混溶液的相容性,接着采用浊度法测定了共混溶液的热力学性质,最后采用浸没沉淀法制备了共混膜并探讨了成膜性能.结果显示,PVDF和SPES为部分相容体系,随着SPES含量的增加,共混溶液相容性逐渐减小,当SPES含量增加到50wt%时,体系发生分相.共混溶液的成膜性能良好,SPES含量增加有利于体系发生液液分相,生成高孔隙率膜,并且极大的提高了PVDF膜的亲水性和水通量.     

聚丙烯/石墨导电纳米复合材料的制备与性能

用溶液插层及其与熔体混合相结合的母料熔体混合 (MMM)方法制备了聚丙烯 (PP) 马来酸酐接枝聚丙烯 (gPP) 膨胀石墨 (EG) (gPP EG =3 2wt)导电纳米复合材料 ,其室温逾渗阀值 (c)分别为 6wt%和 8wt % ,明显低于直接熔体混合制得复合材料和PP EG对照材料的c=11wt%和 12wt% .增加gPP含量 (Cg)能提高复合材料的电导率 (σ) ,例如对于MMM法制备的复合材料 ,固定PP gPP =1 1wt时 ,c 降为 7wt% ;保持EG含量 =9wt%时 ,σ在Cg>30wt %后跃升 7个数量级以上 .通过TEM、SEM和OM观察 ,从制备方法、EG和gPP含量影响复合材料形态和微结构的角度 ,分析说明了出现上述差异和现象的原因 .     

聚甲基乙撑碳酸酯/氧化石墨烯纳米复合材料的制备及性能研究

本文采用改进Hummers法制备氧化石墨烯(GO),通过原子力显微镜对GO片层形貌进行表征;以聚甲基乙撑碳酸酯(PPC)、聚乙烯醇(PVA)和氧化石墨烯(GO)为原料,采用溶液和熔融共混法相结合,制备PPC/PVA/GO纳米复合材料,研究其力学性能、热学性能和动态流变行为。结果表明,当GO含量为0.5 wt%时,拉伸强度达到了22.03 MPa,与纯PPC相比提高了25.8%;当GO含量增大到1.0 wt%时,拉伸强度开始降低;断裂伸长率随GO的加入呈现降低的趋势。GO含量为1.0%时复合材料的热学性能最好,与纯PPC相比,复合材料的完全热分解温度从350℃提高到了400℃以上,并且热分解速率下降了12%/min;复合材料的复数黏度、储能模量和损耗模量随PVA及GO的引入也有一定程度的提高。     

二氧化碳/环氧丙烷/马来酸酐三元共聚物对PPC/PHB共混物力学性能的影响

采用稀土三元催化剂制备了二氧化碳-环氧丙烷-马来酸酐三元共聚物(PPCMA).用红外和核磁谱图确定了PPCMA的结构及马来酸酐单元的含量,3 wt％马来酸酐投料量的PPCMA(共聚物中马来酸酐单元含量4.1％)的玻璃化转变温度(Tg)和起始热分解温度(Td-5％)分别为13.4℃和217℃,拉伸强度为2.88 MPa,断裂伸长率为1669％,与二氧化碳-环氧丙烷共聚物(PPC)相比,引入少量马来酸酐的PPCMA有望成为一种韧性材料,并可对PPC和聚3-羟基丁酸酯(PHB)共混体系进行改性.当在PPC/PHB共混体系中添加10 wt％的PPCMA时,所得共混材料的拉伸强度为18.2 MPa,断裂伸长率则提高到85％,较没有添加PPCMA的样品提高了4.25倍,因此PPCMA的加入能有效提高PPC/PHB共混体系的韧性,改善PPC/PHB共混体系的力学性能.偏光显微镜的研究表明PPC/PHB共混体系加入PPCMA后,很快形成大量尺寸小的PHB球晶,且结晶速度大幅度提高,因此PPCMA在一定意义上可视为一种特殊的“成核剂”.     

原位制备PEI/SiO2复合材料及其改性环氧树脂的研究

在N,N-二甲基乙酰胺/四氢呋喃(DMAc/THF)混合溶剂中,在正硅酸乙酯(TEOS)存在条件下,通过溶胶-凝胶法原位制备了聚醚酰亚胺(PEI)/SiO2复合材料.在该复合材料中,当SiO2含量低于20 wt％时,透射电镜(TEM)和扫描电镜(SEM)的观察表明,SiO2纳米粒子可以均匀分散,粒径可在80～300 n...     

聚氨酯(PU)/聚乙烯醇(PVA)共混体系的有关性能及其模型研究

本文研究了聚氨酯(PU)-聚乙烯醇(PVA)共混体系的动态力学性质、相逆转现象和透气性能.发现当PVA重量含量为30-50％时,共混体系发生了连续相与分散相的逆转.进一步,通过力学模型描述了该共混体系的模量-组成关系、动态力学温度谱以及透气系数与PVA含量的关系曲线.所有实验数据都落在理论预测的范围内,并分别与改进的Kerner模型和组合Kerner模型相符合.     

Ab-initio study of electronic,optical, thermal,and transport properties of Cr4AlB6

Theoretical investigation of different physical parameters of Cr₄AlB₆ have been done within the framework of density functional theory. Cr₄AlB₆ is a no band gap material. Its Cr-3d states contributes the most at the Fermi level. Thermal properties are investigated using quasi-harmonic Debye model as implemented in Gibbs code for different values of pressure and temperature. Study of transport property suggests that its electrical conductivity increases nonlinearly with increase in temperature but the relative change in its value is very low whereas its thermal conductivity increases linearly with the increase in temperature and relative increase in thermal conductivity is very high. The behavior of Cr₄AlB₆ is anisotropic and property is ceramic. It has potential applications in making ceramic capacitors. Its reflectivity is high in low energy region. It suggests that material can be used as coating material for far-infrared radiation. Study of the transport property suggests that because of very high value of thermal conductivity, it can be used for heat sink applications.     

Thermal,structural and electrical properties

The chloro compound of 3-hydroxy-2-quinoxalinecarboxylic acid with nickel(II) has been prepared in ethanolic solution from which a solid compound was isolated. Spectral and magnetic measurements show that the nickel ions are in an octahedral environment. Thermogravimetry, differential thermal analysis and electrical conductivity data are reported for 3-hydroxy-2-quinoxalinecarboxylic acid and its nickel complex. The conductivity measurements indicate that electron/hole traps are emptied during heating of the complex but repopulation occurs in about 24 h at room temperature.     

Reliability of flexible electrically conductive adhesives

Based on our previous work about electrically conductive adhesives (ECAs), a flexibilizer named 1,3‐propanediol bis (4‐aminobenzoate) was used to fabricate flexible ECAs (FECAs). ECAs, FECAs, and electronic devices connected by them were carried out the hot and humid aging test under constant humidity level of 85% relative humidity at 85 °C for 600 h. After aging, the bulk resistance change of ECAs was about 26%, that of FECAs was a little higher, about 29%. The contact resistance change of devices connected by ECAs and FECAs was very great, about 450% and 410%, respectively. The bonding area at connection interface between colloids and devices had delamination, even cracks. The delamination of ECAs was calculated about 60%, the average shear strength of ECAs was reduced about 45%, and those of FECAs were about 50% and 30%, respectively, so FECAs had a higher bonding stability in hot and humid environment. Copyright © 2012 John Wiley & Sons, Ltd.     

Assimilation of manganese metal ion doped hydroxyapatite by Co-Precipitation technique

Calcium phosphate mineral [HAp] is a vital ingredient in orthopaedics, dental and hard tissue applications in mammals. Since it can absorb a large number of impurities, the doped HAp has the potential for biomedical applications using its physical and structural properties. In this research, the Mn-doped HAp in which x calcium atoms are replaced by Mn (Ca_10-x Mn_x (PO₄)₆(OH)₂ where x = 0.2, 0.4, 0.6, 0.8 mol) is obtained by the co-precipitation method. The physical properties of Mn-doped HAp, such as average crystallite size and degree of crystalline, are determined through XRD studies. The peaks corresponding to the functional groups PO4^3?, CO, and OH of the samples are identified by FTIR studies. The impedance spectroscopy method helps in the investigation of electrical conductivity, and dielectric loss in the impedance spectra for various doping concentrations. The average molar ratio of HApMn is determined with the help of EDX. It was found that there is a decrease in the degrees of crystallization with the doping element concentration (Mn) in all the samples. The diffraction (hkl) indices are confirmed from the selected area electron diffraction (SAED) rings, and the morphological study of the samples using TEM confirms the shape as a rod-like structure. To conclude, the variation in the characteristics of HAp relies on the doping concentration of Mn.     

Typical superparamagnetism with improved electrical properties of nano modified bismuth ferrite multiferroic composites

Multiferroic composites with the chemical formula, (0.5) BiFeO₃ + (0.5) Ni_0.5Zn_0.5Fe₂O₄, in bulk and nano forms were synthesized by preparing bismuth ferrite (BiFeO₃ or BFO) in bulk (B) and nano (N) forms and nickel zinc ferrite (Ni_0.5Zn_0.5Fe₂O₄or NZFO) in nano form. Single phase BFO was synthesized using conventional solid-state reaction as well as sol-gel autocombustion methods and NZFO powders were prepared by using sol-gel autocombustion method, respectively. X-ray diffraction (XRD) studies reveal the existence of rhombohedrally distorted perovskite structure for BFO and cubic spinel phase for NZFO in single phase as well as composite samples. Microstructural studies and energy dispersive spectroscopy (EDS) data reveal the formation of grains, intergranular porosities and chemical purity of the synthesized samples. Dielectric and AC conductivity measurements confirm the existence of space charge polarization along with the small polaron model in these composites. Ferroelectric and magnetic studies show that there was a considerable enhancement in the ferroelectric and magnetic orders for the nano form of the BFO (N) + NZFO composite. The observed remnant polarization values 2.80388 & 7.75901 μC/cm², saturation magnetization values 37.96072 & 40.47491emu/gm for bulk BFO (B) + NZFO and nano BFO (N) + NZFO composites, respectively. Interestingly, both the samples exhibit superparamagnetic behaviour at room temperature with coercivities close to zero. This typical behaviour is attributed to the corresponding anisotropic contributions originated from the individual constituents. The observed variations in BFO (N) + NZFO sample attributed to the corresponding structural modifications brought about by the variations due to its size effect in the present work.     

Tetrametallic macrocyclic frameworks constructed from ferrocenedicarboxylato and 2,2-bipyridine: synthesis, molecular structures and characteristics

Four novel tetranuclear macrocyclic compounds [Cd₂(η²-O₂CFcCO₂)₂(2,2^′-bpy)₂(H₂O)₂] · 2H₂O (1), [Zn₂(η²-O₂CFcCO₂)₂(2,2^′-bpy)₂(H₂O)₂] · CH₃OH · H₂O (2), [Co₂(O₂CFcCO₂)₂(2,2^′-bpy)₂(μ₂-OH₂)₂] · CH₃OH · 2H₂O (3), and [Ni₂(O₂CFcCO₂)₂(2,2^′-bpy)₂(μ₂-OH₂)₂] · CH₃OH · 2H₂O (Fc=(η⁵-C₅H₄)Fe(η⁵-C₅H₄) (4) have been synthesized and structurally characterized by single crystal diffraction. The magnetic behaviors for compounds (3) and (4) are studied in the temperature range of 5.0-300 K. The results show that the antiferromagnetic coupling of Co^II-Co^II pairs occurs in (3), and unusual global ferromagnetic coupling between nickel (II) ions exists in (4). The solution-state differential pulse voltammetries of compounds (1)-(4) all show two peaks with large separations (ΔE) that indicate strong interactions between two ferrocene moieties. Their fluorescent and thermal properties were also investigated.