Crystal growth, characterization and spectroscopic study of europium-doped NaY(PO3)4

Europium-doped NaY(PO₃)₄ single crystals have been synthesized by the flux method with sizes around 1 mm³. The unit cell parameters at room temperature refined by X-ray powder diffraction are a=7.1510(4) Å; b=13.0070(8) Å; c=9.6973(2) Å; β=90.606(3)°, Z=4 with the space group P2₁/n in monoclinic system. The present single crystals have a needle shape, they are elongated along the a crystallographic direction, and their size is in the 500 μm–1 mm range. The linear thermal expansion tensor parameters were determined, being the maximum value along the b direction, 16.1×10⁻⁶ K⁻¹ and the minimum along the a direction being 11.7×10⁻⁶ K⁻¹. The IR vibration modes attributed to the group P–O are consistent with the crystallographic data concerning the chain aspect of the phosphate anion. This material melts incongruently at 1141 K. Intense visible emissions attributed to Eu^{3+ 5}D₀→⁷F₁, ⁵D₀→⁷F₂ and ⁵D₀→⁷F₄, electronic transitions have been observed after pumping at 355 nm at room temperature.     

Population dynamics of the F4 and H4 levels in highly-doped Tm:ZB(L)AN glasses

Population dynamics of the ³F₄ and ³H₄ levels in Tm³⁺ doped ZB(L)AN glasses was studied for Tm³⁺ concentrations from 0.5 to 12 mol%. Fluorescence waveforms from these levels were measured at 1.8 μm (³F₄) and 800 nm (³H₄) with both direct and indirect pumping. Decay from the ³F₄ level was found to be exponential with non-radiative decay rates proportional to the square of the Tm concentration. This indicated a process of energy migration by diffusion within the excited Tm³⁺ ions followed by quenching at sites to which the ions could migrate. The decay of the directly pumped ³H₄ level exhibited both exponential and non-exponential behavior depending on the concentration. For the lowest concentration (0.5 mol%) the decay was exponential, but at concentrations of 1, 2, 4 and 6 mol% the decay waveforms were distinctly non-exponential. The non-exponential waveforms could be fitted by the Yokota-Tanimoto model for diffusion of excited donors and dipole-dipole interactions with acceptors. This model produced values for C_DD and C_DA, the donor-donor and donor-acceptor energy transfer parameters, respectively. At the higher concentrations (8, 10, 12 mol%) the waveforms were exponential with decay rates from which the cross-relaxation parameter for the process ³H₄, ³H₆ → ³F₄, ³F₄ was obtained. When the ³F₄ level is pumped at 1660 nm, the decay of the ³H₄ level confirmed the influence of the up-conversion energy transfer process ³F₄, ³F₄ → ³H₄, ³H₆.     

Growth and shape control of orthorhombic Fe5(PO4)4(OH)3·2H2O single crystalline dendrites

Orthorhombic Fe₅(PO₄)₄(OH)₃·2H₂O single crystalline dendritic nanostructures have been synthesized by a facile and reproducible hydrothermal method without the aid of any surfactants. The influences of synthetic parameters, such as reaction time, temperature, the amount of H₂O₂ solution, pH values, and types of iron precursors, on the crystal structures and morphologies of the resulting products have been investigated. The formation process of Fe₅(PO₄)₄(OH)₃·2H₂O dendritic nanostructures is time dependent: amorphous FePO₄·nH₂O nanoparticles are formed firstly, and then Fe₅(PO₄)₄(OH)₃·2H₂O dendrites are assembled via a crystallization-orientation attachment process, accompanying a color change from yellow to green. The shapes and sizes of Fe₅(PO₄)₄(OH)₃·2H₂O products can be controlled by adjusting the amount of H₂O₂ solution, pH values, and types of iron precursors in the reaction system.     

Growth, thermal and spectral properties of Nd-doped NaGd(MoO4)2 crystal

Nd³⁺-doped NaGd(MoO₄)₂ crystal with dimensions were grown by Czochralski method. Nd³⁺:NaGd(MoO₄)₂ crystal melts at 1182 °C. The hardness of Nd³⁺:NaGd(MoO₄)₂ crystal is 334 VDH. The specific heat is 72.6 cal/mol K. The thermal expansion coefficients are for c-axis and for a-axis, respectively. The absorption cross-sections of Nd³⁺:NaGd(MoO₄)₂ crystal are with a FWHM of 9 nm at the 804 nm for π-polarization and with a FWHM of 17 nm at 807 nm for σ-polarization, respectively. The emission cross-section σ_em are at 1063 nm for π-polarization and 1.94×10^-20 at 1070 nm cm² for σ-polarization, respectively. The fluorescence lifetime τ_f is 93.9 μs at room temperature.     

Energy transfer between Tm and Er ions in a TeO2-based glass pumped at diode laser wavelength

In this paper we investigate the energy transfer processes in Tm³⁺/Er³⁺ doped telluride glass pumped at the commercial diode laser pump wavelength ∼800 nm. Tailoring the rare-earths content in the glass matrix, seven main energy transfer channels within the doping range considered were identified. A 6-fold enhancement of the Er³⁺ visible frequency upconversion fluorescence at ∼660 nm is observed due to the inclusion of Tm³⁺ ions. This is evidence of the relevant contribution of the route Er₁(⁴I_11/2) + Er₂(⁴I_13/2) → Er₁(⁴I_15/2) + Er₂(⁴F_9/2) to the process. Energy migration among pumped ⁴I_9/2 level reducing the efficiency of the upconversion emission rate (³H_11/2, ⁴S_3/2, and ⁴F_9/2) is observed for Er³⁺ above 1.5 wt%. The rate equations regarding the observed energy transfer routes are determined and a qualitative analysis of the observed processes is reported.     

Growth and optical properties of self-frequency-doubling laser crystal Yb:LuAl3(BO3)4

Single crystal of Yb:LuAl₃(BO₃)₄(Yb:LuAB) was grown by the flux method for the first time. The cell parameters of the grown crystal were estimated by X-ray diffraction analysis. The result indicates the symmetry of trigonal space group R32, with lattice parameters a=b=9.26372 Å, c=7.21405 Å, V=536.14 Å³, and Z=4. The absorption and emission spectra of Yb:LuAB crystal at room temperature has also been studied. The fluorescence lifetime for Yb:LuAB crystal is about 1.48 ms. The heat capacity was measured from 25 to 500 °C. Its second harmonic generation efficiency in LuAl₃(BO₃)₄ crystal is 3–4 times that of KDP crystal. These results show that Yb:LuAB crystal would be a potential self-frequency-doubling laser crystal.     

Crystal growth and spectroscopic properties of erbium doped Lu2SiO5

A high optical quality erbium doped Lu₂SiO₅ single crystal has been grown by the Czochralski method. The distribution coefficient of Er³⁺ was measured to be ∼0.926. The absorption and emission spectra as well as the fluorescence decay curve of the excited state ⁴I_13/2 were measured at room temperature. The spectroscopic parameters were calculated using the Judd–Ofelt theory, and the J–O parameters Ω₂, Ω₄ and Ω₆ were found to be 4.451×10^-20, 1.614×10^-20 and 1.158×10^-20 cm², respectively. The room-temperature fluorescence lifetime of the Er³⁺⁴I_13/2→⁴I_15/2 transition was measured to be 7.74 ms. The absorption and emission cross-section as well as the gain cross-section in the eye-safe regime of 1400–1700 nm were also determined and discussed.     

Crystal growth and luminescent properties of Pr-doped K(Y,Lu)3F10 single crystal for scintillator application

Pr1%:K(Y_1−xLu_x)₃F₁₀ (x=0, 0.2, 0.4) single crystals were grown by the μ-PD method. All the grown crystals were greenish and perfectly transparent without any inclusions or cracks. Radioluminescence spectra and decay kinetics of the Pr1%:K(Y,Lu)₃F₁₀ crystals were measured. Emission from the Pr³⁺ 5d–4f transition, peaking around 260 nm and of the decay time of around 22 ns were observed. The 5d–4f emission intensities of the Pr1%:K(Y,Lu)₃F₁₀ crystals were higher than that of the standard BGO scintillator.     

Improvement of the Tm:H4 level lifetime in silica optical fibers by lowering the local phonon energy

The role of some glass network modifiers on the quantum efficiency of the near-infrared fluorescence from the ³H₄ level of Tm³⁺ ion in silica-based doped fibers is studied. Modifications of the core composition affect the spectroscopic properties of Tm³⁺ ion. Adding 17.4 mol% of AlO_3/2 to the core glass caused an increase of the ³H₄ level lifetime up to 50 μs, 3.6 times higher than in pure silica glass. The quantum efficiency was increased from 2% to approximately 8%. On the opposite, 8 mol% of PO_5/2 in the core glass made the lifetime decrease down to 9 μs. These changes of Tm³⁺ optical properties are assigned to the change of the local phonon energy to which they are submitted by modifiers located in the vicinity of the doping sites. Some qualitative predictions of the maximum achievable quantum efficiency are possible using a simple microscopic model to calculate the non-radiative de-excitation rates.     

Energy transfer up-conversion in Tm-doped silica fiber

A study of the mechanisms responsible for the infra-red to near infra-red up-conversion in Tm³⁺-doped silica fibers is presented. Up-conversion luminescence was observed from the ³H₄ level of Tm³⁺ under 1586 nm pumping into the ³F₄ level. The quadratic dependence of the up-conversion luminescence at 800 nm on the 1800 nm luminescence from the ³F₄ level confirms that the ³H₄ level is populated by a two photon process. Two possible processes are proposed as mechanisms responsible for the up-conversion: excited state absorption and energy transfer up-conversion. The decay characteristics of the luminescence from the ³H₄ level were studied under direct and indirect pumping at 786 and 1586 nm, respectively. By comparing the decay waveforms to the solution of a simple set of rate equations, the energy transfer up-conversion process (³F₄, ³F₄ → ³H₄, ³H₆) was established at Tm₂O₃ concentrations greater than 200 ppm.     

Crystal growth and spectroscopic properties of Yb:CaYAlO4 single crystal

A Yb³⁺-doped CaYAlO₄ laser crystal has been grown by the Czochralski technique. The segregation coefficient was measured by Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES). The cell parameters were analyzed with X-ray diffraction experiments. Color defects in Yb:CaYAlO₄ have been evidenced to be similar to those in undoped CaYAlO₄. The polarized absorption spectra and the fluorescence spectrum of the Yb:CaYAlO₄ crystal were measured at room temperature. The fluorescence decay time of the Yb³⁺ ion was investigated. The results show that Yb:CaYAlO₄ has potential as a laser gain medium for an ultrashort laser system.     

Cs2LiGdCl6 (Ce): New scintillation material

We investigated the scintillation properties of Cs₂LiGdCl₆:Ce³⁺ as a function of the Ce concentration. X-ray excited luminescence spectra of the scintillation material showed broad emission bands between 360 and 460 nm, with two overlapping peaks, due to the d→f transitions on Ce³⁺ ions. The samples provide good scintillation results. The energy resolution was found to be 5.0% (FWHM) at 662 keV for 10% Ce sample. Under γ-ray excitation, Cs₂LiGdCl₆:Ce³⁺ showed three exponential decay time components of about 130–200 ns decay time constant. The light output of the investigated samples was 20,000 photons/MeV for a 10% Ce concentration. The light output deviation from the linear response is within 7% between the energy range of 31 and 1333 keV. Overall, the scintillation properties confirm that Cs₂LiGdCl₆:Ce³⁺ single crystal is a promising candidate for medical imaging and radiation detection.     

Investigation of infrared emission and lifetime in Tm-doped 75TeO2:20ZnO:5Na2O (mol%) glasses: Effect of Ho and Yb co-doping

In this paper we describe fabrication and characterization of rare-earth-doped active tellurite glasses to be used as active laser media for fiber lasers emitting in the 2 μm region. The base composition is (mol%): 75TeO₂-20ZnO-5Na₂O with different concentrations of Tm³⁺, Yb³⁺ and Ho³⁺ as dopants or co-dopants. Optical properties of doped glasses were studied and pumping at 800 nm and at 980 nm were tested in order to compare the efficiency of two pumping mechanisms. Optical characterization carried out on glasses containing only Tm³⁺ ions indicated the optimum concentration of Tm₂O₃ in terms of emission efficiency as 1 wt%. The addition of 5 wt% of Yb₂O₃ to Tm³⁺-doped glasses led to the best results in terms of intensity of fluorescence emission and of lifetime values. Yb and Ho co-doped Tm-tellurite glass was measured in emission.     

Blue emission of ZrO2:Tm nanocrystals with different crystal structure under UV excitation

In this paper, thulium doped ZrO₂ nanocrystals with different phases were prepared by Pechini sol-gel complex method. The effects of host structure, phases and concentration on luminescence properties of Tm³⁺ ions were investigated. With the increase of the concentration of Tm³⁺ ions, the phosphors phase transformed from monoclinic to tetragonal structure and all the phosphors emitted blue light. However, because the environment symmetry around Tm³⁺ in m-ZrO₂ (C_2h) is worse than that of t-ZrO₂ (D_4h), there were still obvious differences in the emission and excitation. The reason was investigated with the help of energy level diagram. In addition, the quenching concentration of Tm³⁺ in ZrO₂ host is 1 m/m%.     

Float zone growth of Dy:GdVO4 single crystals for potential use in solid-state yellow lasers

Single crystals of dysprosium-doped gadolinium orthovanadate (Dy:GdVO₄) were successfully grown by the floating zone method and their fluorescence properties were investigated. The as-grown crystals did not contain any macroscopic defects such as cracks and inclusions for any Dy-concentration of up to 4 at%. Every crystal showed optical homogeneity under observation with a polarizing microscope; that is, no low-angle grain boundaries and growth striations were detected. In the visible region, two distinct fluorescence bands were observed around 480 and 575 nm, corresponding to ⁴F_9/2→⁶H_15/2 and ⁴F_9/2→⁶H_13/2 transitions, respectively. The excitation spectrum for the emission of 573 nm indicates the possibility to use a commercially available laser diode of 450 nm as a pumping source for solid-state yellow laser.     

Growth and microstructural features of laser ablated LiCoO2 thin films

Thin films of LiCoO₂ were prepared by pulsed laser deposition technique and the properties were studied in relation to the deposition parameters. The films deposited from a sintered composite target (LiCoO₂+Li₂O) in an oxygen partial pressure of 100 mTorr and at a substrate temperature of 300 °C exhibited preferred c-axis (0 0 3) orientation perpendicular to the substrate surface. The AFM data demonstrated that the films are composed of uniform distribution of fine grains with an average grain size of 80 nm. The grain size increased with an increase in substrate temperature. The (0 0 3) orientation decreased with increase in (1 0 4) orientation for the films deposited at higher substrate temperatures (>500 °C) indicating that the films’ growth is parallel to the substrate surface. The composition of the experimental films was analyzed using X-ray photoelectron spectroscopy (XPS). The binding energy peaks of Co(2p_3/2) and Co(2p_1/2) are, respectively, observed at 779.3 and 794.4 eV, which can be attributed to the Co³⁺ bonding state of LiCoO₂. The electrochemical measurements were carried out on Li//LiCoO₂ cells with a lithium metal foil as anode and LiCoO₂ film as cathode of 1.5 cm² active area using a Teflon home-made cell hardware. The Li//LiCoO₂ cells were tested in the potential range 2.6-4.2 V. Specific capacity as high as 205 mC/cm² μm was measured for the film grown at 700 °C. The growth of LiCoO₂ films were studied in relation to the deposition parameters for their effective utilization as cathode materials in solid-state microbattery application.     

1.48 μm emission properties and the cross-relaxation mechanism in chalcohalide glass doped with Tm

1.48 μm emission properties and the cross-relaxation mechanism of Tm³⁺ ions in 0.7(Ge_0.25As_0.10S_0.65) + 0.15GaS_3/2 + 0.15CsBr glass were investigated. Both the relative intensity ratio of the 1.48 μm emission to 1.82 μm and the measured lifetime of the ³H₄ level decreased with increasing Tm³⁺ concentration. When temperature decreased from room temperature to 20 K, lifetimes of the ³H₄ level increased from 670 to 970 μs. At the same time, the critical distance for cross-relaxation decreased from 1.11 to 0.93 nm. These results indicate that cross-relaxation (³H₄, ³H₆ → ³F₄, ³F₄) became less effective as temperature decreased. Analysis of the temperature dependence of cross-relaxation rates showed that cross-relaxation in Tm³⁺ is a phonon-assisted energy transfer process. The major phonon contributing to the process is from the Ga-Br vibration in [GaS_3/2Br]⁻ units.     

Influence of some foreign metal ions on crystal growth kinetics of brushite (CaHPO4·2H2O)

Brushite, CaHPO₄·2H₂O, has been precipitated at 25 °C in the presence of Mg²⁺, Ba²⁺ or Cu²⁺ at concentrations up to 0.5 mM. When initial pH is sufficiently low to exclude nanocrystalline apatite as the initial solid phase, overall crystal growth rate may be determined from simple mass crystallization by recording pH as function of time. A combination of surface nucleation (birth-and-spread) and spiral (BCF) growth was found. Edge free energy was determined from the former contribution and was found to be a linear function of chemical potential of the additive, indicating constant adsorption over a wide range of additive concentrations. Average distances between adsorbed additive ions as calculated from slopes of plots are compatible with lattice parameters of brushite: 0.54 nm for Mg²⁺, 0.43 nm for Ba²⁺ and 0.86 nm for Cu²⁺. With the latter a sharp decrease in growth rate occurred early in the crystallization process, followed by an equally sharp increase to the previous level. When interpreted in terms of the Cabrera–Vermilyea theory of crystal growth inhibition, the results are consistent with an average distance between Cu ions of 0.88 nm, in perfect agreement with the above value.     

Optical properties of and concentration quenching in Bi2O3-B2O3-Ga2O3 glasses

Er₂O₃-doped Bi₂O₃-B₂O₃-Ga₂O₃ glasses were prepared by the conventional melt-quenching method, and the Er³⁺:⁴I_13/2 → ⁴I_15/2 fluorescence properties are studied for different Er³⁺ concentrations. when the Er₂O₃ concentration increases from 0.03 to 3.0 mol%, the measured lifetime of Er³⁺:⁴I_13/2 level decrease from 2.24 to 0.9 m s, and from 0.25 to 0.20 m s for the Er³⁺:⁴I_11/2 level. The fast energy migration among Er³⁺ ions cause the reduction of lifetime of the ⁴I_13/2 level, whereas the change in the ⁴I_11/2 level is mainly due to a cooperative upconversion process (⁴I_11/2, ⁴I_11/2) → (⁴F_7/2, ⁴I_15/2). Based on the dipole-dipole interaction theory, the interaction parameter, C_Er,Er, for the migration rate of Er³⁺:⁴I_13/2 ↔ ⁴I_13/2 was calculated to be 32 × 10⁻⁴⁰ cm⁶ s⁻¹.     

Growth and scintillation properties of the Na2W2O7 crystal

The growth and scintillation properties of the Na₂W₂O₇ crystal are reported. The solid reaction between Na₂CO₃ and WO₃ is used to synthesise the Na₂W₂O₇ material. The Na₂W₂O₇ single crystal has been grown by the Bridgman method. And the Na₂W₂O₇ single crystal with sizes 14×7×6 mm³ has been achieved. The transmission spectra, the Ultraviolet fluorescence spectra and the X-ray excited luminescence spectra of the Na₂W₂O₇ crystal are measured. The measurement results show that the Na₂W₂O₇ crystal is a promising intrinsic scintillator.