Electromagnetic and microwave absorption properties of carbonyl iron/La0.6Sr0.4MnO3 composites

In this work carbonyl iron/La_0.6Sr_0.4MnO₃ composites were prepared to develop super-thin microwave absorbing materials. The complex permittivity, permeability and microwave absorption properties are investigated in the frequency range of 8-12 GHz. An optimal reflection loss of −12.4 dB is reached at 10.5 GHz with a matching thickness of 0.8 mm. The thickness of carbonyl iron/La_0.6Sr_0.4MnO₃ absorber is thinner, compared with conventional carbonyl iron powders with the same absorption properties. The bandwidth with a reflection loss exceeding −7.4 dB is obtained in the whole measured frequency range with the thickness of 0.8 mm. The excellent microwave absorption properties are attributed to a better electromagnetic matching established by the combination of the enhanced dielectric loss and nearly invariable magnetic loss with the addition of La_0.6Sr_0.4MnO₃ nanoparticles in the composites. Our work indicates that carbonyl iron/La_0.6Sr_0.4MnO₃ composites may have an important application in wide-band and super-thin electromagnetic absorbers in the frequency range of 8−12 GHz.     

Microstructure characterization and magnetic behavior of NiAlxFe2−xO4 and Ni1−yMnyAl0.2Fe1.8O4 ferrites

NiAl_xFe_2−xO₄ and Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites were prepared by the conventional ceramic method and were characterized by X-ray diffraction, scanning electron microscopy, and magnetic measurements. The single spinel phase was confirmed for all prepared samples. A proper explanation of data is possible if the Al³⁺ ions are assumed to replace Fe³⁺ ions in the A and B sites simultaneously for NiAl_xFe_2−xO₄ ferrites, and if the Mn²⁺ ions are assumed to replace Ni²⁺ ions in the B sites for Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites. Microstructural factors play an important role in the magnetic behavior of Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites with large Mn²⁺ content.     

Magnetic and Microwave Absorbing Properties of Electrospun Ba(1−x)LaxFe12O19 Nanofibers

Ba_(1−x)La_xFe₁₂O₁₉ (0.00≤x≤0.10) nanofibers were fabricated via the electrospinning technique followed by heat treatment at different temperatures for 2 h. Various characterization methods including scanning electron microscopy (SEM), X-ray diffraction (XRD), vibrating sample magnetometer (VSM), and microwave vector network analyzer were employed to investigate the morphologies, crystalline phases, magnetic properties, and complex electromagnetic parameters of nanofibers. The SEM images indicate that samples with various values of x are of a continuous fiber-like morphology with an average diameter of 110±20 nm. The XRD patterns show that the main phase is M-type barium hexaferrite without other impurity phases when calcined at 1100 °C. The VSM results show that coercive force (H_c) decreases first and then increases, while saturation magnetization (M_s) reveals an increase at first and then decreases with La³⁺ ions content increase. Both the magnetic and dielectric losses are significantly enhanced by partial substitution of La³⁺ for Ba²⁺ in the M-type barium hexaferrites. The microwave absorption performance of Ba_0.95La_0.05Fe₁₂O₁₉ nanofibers gets significant improvement: The bandwidth below −10 dB expands from 0 GHz to 12.6 GHz, and the peak value of reflection loss decreases from −9.65 dB to −23.02 dB with the layer thickness of 2.0 mm.     

Effect of illumination on magnetization and microwave absorption of La1−xCaxMnO3 (x<0.2) films

Light-induced changes of the hysteresis loops of magnetization and microwave absorption are investigated in low-doped La_1−xCa_xMnO₃ (x<0.2) thin films. The width of the hysteresis loops decreases clearly under illumination with visible or near-infrared light at temperatures below 50 K. The microwave conductivity has a minimum value at magnetic fields corresponding to the magnetization reversal and is shifted towards weaker fields under illumination. These effects show complex nonexponential time evolution and dependence on strength of the magnetic field. The results can be explained by assuming that small ferromagnetic metallic regions exist within the insulating ferromagnetic phase of the sample, and that these regions are expanded by optically induced charge transfer between Jahn–Teller split e_g states of neighboring Mn³⁺ ions. Decrease of the Mn³⁺ XPS core level spectrum is observed in the samples under illumination with a HeNe laser.     

Enhancement of initial permeability due to Mn substitution in polycrystalline Ni0.50−xMnxZn0.50Fe2O4

The structural and magnetic properties of Mn substituted Ni_0.50−xMn_xZn_0.50Fe₂O₄ (where x=0.00, 0.10 and 0.20) sintered at various temperatures have been investigated thoroughly. The lattice parameter, average grain size and initial permeability increase with Mn substitution. Both bulk density and initial permeability increase with increasing sintering temperature from 1250 to 1300 °C and above 1300 °C they decrease. The Ni_0.30Mn_0.20Zn_0.50Fe₂O₄ sintered at 1300 °C shows the highest relative quality factor and highest initial permeability among the studied samples. The initial permeability strongly depends on average grain size and intragranular porosity. From the magnetization as a function of applied magnetic field, M(H), it is clear that at room temperature all samples are in ferrimagnetic state. The number of Bohr magneton, n(μ_B), and Neel temperature, T_N, decrease with increasing Mn substitution. It is found that Mn substitution in Ni_0.50−xMn_xZn_0.50Fe₂O₄ (where x=0.20) decreases the Neel temperature by 25% but increases the initial permeability by 76%. Possible explanation for the observed characteristics of microstructure, initial permeability, DC magnetization and Neel temperature of the studied samples are discussed.     

Yafet-Kittel-type magnetic ordering in Ni0.35Zn0.65Fe2O4 ferrite detected by magnetosensitive microwave absorption measurements

Magnetosensitive microwave absorption measurements of polycrystalline ferrite Ni_0.35Zn_0.65Fe₂O₄ was carried out at 9.4 GHz (X-band) as a function of temperature. Temperature dependence of the total linewidth (ΔH_pp) deduced from the resonance spectra showed the passage through the Curie point (T_c~430 K). Additionally, the plot ΔH_pp vs. T also indicated the existence of another magnetic phase transition at ~240 K, which can be associated with a Yafet-Kittel-type canting of the magnetic moments. Low-field microwave absorption (LFMA) and the magnetically modulated microwave absorption spectroscopy (MAMMAS) were used to give a further knowledge on this material. For low temperature, these techniques give evidence of a Yafet-Kittel-type canting of the magnetic moments.     

Hall effect in a GdBa2Cu3O7−δ/La0.75Sr0.25MnO3 perovskite bilayer

We present results on the Hall coefficient R_H in the normal state for a GdBa₂Cu₃O_7−δ/La_0.75Sr_0.25MnO₃ bilayer and a La_0.75Sr_0.25MnO₃ film grown by dc magnetron sputtering on (1 0 0) SrTiO₃. We find that the electric transport on the bilayer can be qualitatively described using a simple parallel layers model. The GdBa₂Cu₃O_7−δ layer presents a carrier density approximately equal to that reported for 7 − δ = 6.85 oxygen doping. Also we observe an unexpected presence of two Hall resistivity regimes, effects that may be associated with the internal magnetic field induced on the superconducting layer by the ferromagnetic layer.     

Magnetoresistive properties of Zn1−xCoxFe2O4 ferrites

The magnetic and magnetoresistive properties of spinel-type Zn_1−xCo_xFe₂O₄ (x=0, 0.2 and 0.4) ferrites are extensively investigated in this study. A large negative magnetoresistance (MR) effect is observed in Zn_1−xCo_xFe₂O₄ ferrites of spinel structure. These materials are either ferrimagnetic or paramagnetic at room temperature, and show a spin-(cluster) glass transition at low temperatures, depending on the chemical compositions. The MR curves as a function of magnetic fields, MR(H), are parabolic at all temperatures for paramagnetic polycrystalline ZnFe₂O₄. The MR for ZnFe₂O₄ at 110 K in the presence of 9 T applied magnetic field is 30%. On the other hand, MR(H) are linear for x=0.2 and 0.4 ferrimagnetic Zn_1−xCo_xFe₂O₄ samples up to 9 T. The MR effect is independent of the sintering temperatures, and can be explained with the help of the spin-dependent scattering and the Yafet–Kittel angle of Zn_1−xCo_xFe₂O₄ mixed ferrites.     

Magnetic and microwave absorbing properties of polyaniline/γ-Fe2O3 nanocomposite

The conducting protonated polyaniline (ES)/γ-Fe₂O₃ nanocomposite with the different γ-Fe₂O₃ content were synthesized by in-situ polymerization. Its morphology, microstructure, DC conductivity and magnetic properties of samples were characterized by transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), four-wire-technique, and vibrating sample magnetometer (VSM), respectively. The microwave absorbing properties of the nanocomposite powders dispersing in wax coating with the coating thickness of 2 mm were investigated using a vector network analyzers in the frequency range of 7–18 GHz. The pure ES has shown the absorption band with a maximum absorption at approximately 16 GHz and a width (defined as frequency difference between points where the absorption is more than 8 dB) of 3.24 GHz, when 10% γ-Fe₂O₃ by weight is incorporated , the width is broadened to 4.13 GHz and some other absorption bands appear in the range of 7–13 GHz. The parameter dielectric loss tan δ_e (=ε″/ε′) in the 7–18 GHz is found to decrease with increasing γ-Fe₂O₃ contents with 10%, 20%, 30%, respectively, but magnetic loss tan δ_m (=μ″/μ′) increases with increasing γ-Fe₂O₃ contents. The results show that moderate content of γ-Fe₂O₃ nanoparticles embedded in protonated polyaniline matrix may create advanced microwave absorption properties due to simultaneous adjusting of dielectric loss and magnetic loss.     

Microwave absorption properties of Sr2FeMoO6 nanoparticles

The microwave absorption properties of nanosized double perovskite Sr₂FeMoO₆ and epoxy resin composites were investigated in the frequency range of 2-18 GHz using the coaxial method. The Sr₂FeMoO₆ composites with an optimal 20 wt% epoxy resin showed a strong electromagnetic attenuation of −49.3 dB at 8.58 GHz with a matching thickness of 2.15 mm. Moreover the optimum absorption frequency at which the reflection loss is less than −20 dB, which corresponds to 99% reflection loss of the incident microwave, is from 5.7 to 13.2 GHz with the matching thickness ranging from 3.0 to 1.5 mm. The excellent microwave-absorption properties are a consequence of a proper electromagnetic match due to the existence of the insulating matrix of anti-site defects and anti-phase domains, which not only contribute to the dielectric loss but also to the reduced eddy current loss.     

Synthesis and investigation of magnetic properties of substituted ferrite nanoparticles of spinel system Mn1−xZnx[Fe2−yLy]O4

Superparamagnetic nanoparticles of the spinel ferrite four-element system Mn_1−xZn_x[Fe_2−yL_y]O₄ (where L:Gd³⁺, La³⁺, Ce³⁺, Eu³⁺, Dy³⁺, Er³⁺,Yb³⁺) were synthesized by the co-precipitation method. The magnetic moments of the 10 nm diameter nanoparticles were comparable to the ones of Fe₃O₄ nanoparticles. A comparatively low T_C (∼52–72 °C) was observed for some of the compositions. The heating mechanism of the superparamagnetic particles in the AC magnetic field at radiofrequency range is discussed and especially the absence of the hysteresis loop in the M–H curve at room temperature. One possible explanation—spontaneous particle agglomeration—was experimentally verified.     

Defect formation and transport in mixed-conducting La0.90Sr0.10Al0.85−xFexMg0.15O3−δ

The redox behavior of perovskite-type La_0.90Sr_0.10Al_0.85−xFe_xMg_0.15O_3−δ (x=0.20-0.40) mixed conductors was analyzed by the Mössbauer spectroscopy and measurements of the total conductivity and Seebeck coefficient in the oxygen partial pressure range from 10⁻²⁰ to 0.5 atm at 1023-1223 K. The results combined with oxygen-ion transference numbers determined by the faradaic efficiency technique in air, were used to calculate defect concentrations, mobilities, and partial ionic and p- and n-type electronic conductivities as a function of oxygen pressure. The redox and transport processes can be adequately described in terms of oxygen intercalation and iron disproportionation reactions, with the thermodynamic functions independent of defect concentrations. No essential delocalization of the electronic charge carriers was found. The oxygen non-stoichiometry values estimated from the conductivity vs. p(O₂) dependencies, coincide with those evaluated from the Mössbauer spectra.     

Effect of Fe substitution on magnetocaloric effect in La0.7Sr0.3Mn1−xFexO3 (0.05≤x≤0.20)

We have studied the effect of Fe substitution on magnetic and magnetocaloric properties in La_0.7Sr_0.3Mn_1−xFe_xO₃ (x=0.05, 0.07, 0.10, 0.15, and 0.20) over a wide temperature range (T=10-400 K). It is shown that substitution by Fe gradually decreases the ferromagnetic Curie temperature (T_C) and saturation magnetization up to x=0.15 but a dramatic change occurs for x=0.2. The x=0.2 sample can be considered as a phase separated compound in which both short-range ordered ferromagnetic and antiferromagnetic phases coexist. The magnetic entropy change (−ΔS_m) was estimated from isothermal magnetization curves and it decreases with increase of Fe content from 4.4 J kg⁻¹ K⁻¹ at 343 K (x=0.05) to 1.3 J kg⁻¹ K⁻¹ at 105 K (x=0.2), under ΔH=5 T. The La_0.7Sr_0.3Mn_0.93Fe_0.07O₃ sample shows negligible hysteresis loss, operating temperature range over 60 K around room temperature with refrigerant capacity of 225 J kg⁻¹, and magnetic entropy of 4 J kg⁻¹ K⁻¹ which will be an interesting compound for application in room temperature refrigeration.     

Phase boundary between uniaxial and planar ferromagnets in layered perovskite manganite La2−2xSr1+2xMn2O7 (0.313⩽x⩽0.350)

We have examined magnetizations as a function of temperature and magnetic field in layered perovskite manganites La_2−2xSr_1+2xMn₂O₇ single crystals (x=0.313, 0.315, 0.318, 0.320 and 0.350) in order to determine the phase boundary between two ferromagnets (one is an uniaxial ferromagnet whose easy axis is parallel to the c-axis and the other is a planar ferromagnet whose easy axis is within the ab-plane) and following results are obtained: (i) all the present manganites exhibit magnetic transitions from a ferromagnet to a paramagnet at 76, 107, 116, 120 and 125 K for x=0.313, 0.315, 0.318, 0.320 and 0.350, respectively; (ii) for x=0.318, 0.320 and 0.350, the magnetic structure is a planar ferromagnet below Curie temperature; (iii) for x=0.313 and 0.315, the magnetic structure changes from an uniaxial to a planar ferromagnet at 66 and 85 K, respectively. From the results described above we have constructed the magnetic phase diagram of layered perovskite manganite La_2−2xSr_1+2xMn₂O₇ (0.313?x?0.350).     

Magnetic properties of the Ce2Fe17−xMnx helical magnets up to high magnetic fields

Magnetic properties of the Ce₂Fe_17−xMn_x, x=0–2, alloys in magnetic fields up to 40 T are reported. The compounds with x=0.5–1 are helical antiferromagnets and those with 1<x?2 are helical ferromagnets or helical antiferromagnets at low and high T, respectively. Mn ions in the system carry average magnetic moment of 3.0±0.2 μ_B that couple antiparallelly to the Fe moments. Easy-plane magnetic anisotropy in the Ce₂Fe_17−xMn_x compounds weakens upon substitution of Mn for Fe. The absolute value of the first anisotropy constant in the Ce₂Fe_17−xMn_x helical ferromagnets decreases slower with increasing temperature than that calculated from the third power of the spontaneous magnetization. Noticeable magnetic hysteresis in the Ce₂Fe_17−xMn_x, x=0.5–2, helical magnets over the whole range of magnetic fields reflects mainly irreversible deformation of the helical magnetic structure during the magnetization of the compounds. A contribution from short-range order (SRO) magnetic clusters to the magnetic hysteresis of the helical magnets has been also estimated.     

Magnetoelectric characterization of xNi0.75Co0.25Fe2O4-(1−x)BiFeO3 nanocomposites

Magnetoelectric (ME) nanocomposites containing Ni_0.75Co_0.25Fe₂O₄-BiFeO₃ phases were prepared by citrate sol-gel process. X-ray diffraction (XRD) analysis showed phase formation of xNi_0.75Co_0.25Fe₂O₄-(1−x)BiFeO₃ (x=0.1, 0.2, 0.3 and 0.4) composites on heating at 700 °C. Transmission electron microscopy revealed the formation of powders of nano order size and the crystal size was found to vary from 30 to 85 nm. Dispersion in dielectric constant (ε) and dielectric loss (tan δ) in the low-frequency range have been observed. It is seen that nanocomposites exhibit strong magnetic properties and a large ME effect. On increasing Ni_0.75Co_0.25Fe₂O₄ contents in the nanocomposites, the saturation magnetization (M_S) and coercivity (H_C) increased after annealing at 700 °C. The large ME output in the nanocomposites exhibits strong dependence on magnetic bias and magnetic field frequency. The large value of ME output can be attributed to small grain size of ferrite phase of nanocomposite being prepared by citrate precursor process.     

Influence of frequency, temperature and composition on electrical properties of polycrystalline Co0.5CdxFe2.5−xO4 ferrites

Polycrystalline ferrites with general formula Co_0.5Cd_xFe_2.5−xO₄ (0.0?x?0.5) were prepared by sol-gel method. The dielectric properties ε′, ε″, loss tangent tan δ and ac conductivity σ_ac have been studied as a function of frequency, temperature and composition. The experimental results indicate that ε′, ε″, tan δ and σ_ac decrease as the frequency increases; whereas they increase as the temperature increases. These parameters are found to increase by increasing the concentration of Cd content up to x=0.2, after which they start to decrease with further increase in concentration of Cd ion. The dielectric properties and ac conductivity in studied samples have been explained on the basis of space charge polarization according to Maxwell and Wagner's two-layer model and the hoping between adjacent Fe²⁺ and Fe³⁺ as well as the hole hopping between Co³⁺and Co²⁺ ions at B-sites. The values of activation energies E_f for conduction process are determined from Arrhenius plots, and the variations in these activation energies as a function of Cd content are discussed. The complex impedance analysis is used to separate the grain and grain boundary of the system Co_0.5Cd_xFe_2.5−xO₄. The variations of both grain boundary and grain resistances with temperature and composition are evaluated in the frequency range 42 Hz-5 MHz.     

Electromagnetic and microwave absorption properties of Fe3O4 magnetic films plated on hollow glass spheres

Magnetic hollow spheres of low density were prepared by plating Fe₃O₄ magnetic films on hollow glass spheres using ferrite plating. The complex permeability and permittivity of spheres–wax composites were measured in the range of 2–18 GHz. The complex permeability and permittivity increased, and the dielectric and magnetic losses were improved as the volume fraction of the magnetic spheres in the composites increased from 60% to 80%, which also resulted in a great improvement of microwave absorption properties. For composites with volume fraction 80%, its magnetic resonance frequency was at about 13 GHz and it appeared three loss peaks in the calculated reflection loss curves; the bandwidth less than −10 dB was almost 4 GHz which was just in the Ku-band frequencies (12–18 GHz) and a minimum reflection loss of −20 dB was obtained when the thickness was 2.6 mm; the microwave absorbing properties were mainly due to the magnetic loss. The results showed that the magnetic spheres composites were good and light microwave absorbers in the Ku-band frequencies.     

Magnetic and microwave absorption properties of BaFe12−x (Mn0.5Cu0.5Zr)x/2O19 synthesized by sol–gel processing

BaFe_12−x (Mn_0.5Cu_0.5Zr)_x/2O₁₉ hexaferrites with x=1, 2 and 3 were prepared by sol–gel process. The ferrite powders possess hexagonal shape and are well separated from one another. The powders of these ferrites were mixed with polyvinylchloride (PVC) plasticizer to be converted into a microwave absorbing composite ferrite with a thickness of 1.8 mm. X-ray diffractometer (XRD), scanning electron microscope (SEM), ac susceptometer, vibrating sample magnetometer and vector network analyzer were used to analyze its structure, electromagnetic and microwave absorption properties. The results showed that magnetoplumbite structures for all samples were formed. The sample with higher magnetic susceptibility and coercivity exhibits a larger microwave absorbing ability. Also the present investigation demonstrates that a microwave absorber using BaFe_12−x(Mn_0.5Cu_0.5Zr)_x/2O₁₉ (x=2 and 3)/PVC with a matching thickness of 1.8 mm can be fabricated for applications over 15 GHz, with reflection loss more than −25 dB for specific frequencies, by controlling the molar ratio of the substituted ions.