The near normal incidence thermoreflectance spectra of Cd₃As₂ have been investigated at room temperature and liquid nitrogen temperature in the spectral range 2.5–6.2 eV.     

Photo-synthesis of As3S2 crystal from AsAs2S2 mixture

Existence of As₃S₂ compound which is stable in a certain temperature range higher than room temperature has been confirmed in AsAs₂S₂ system. Photo-synthesis effect of As₃S₂ crystal from As and As₂S₂ mixture, namely light induced conversion from a crystalline state to another crystalline state, has also been investigated.     

Multiferroic studies on (BiFeO3)m(BaTiO3)n superlattice structures

BiFeO₃ has been studied extensively due to its room temperature multiferroic features and has been proven as a promising candidate for device applications. But BiFeO₃ possesses some drawbacks like high leakage current and complicated magnetic ordering, giving rise to a canted antiferromagnetic behavior. Hence, a superlattice approach of BiFeO₃ and BaTiO₃ with a good lattice matching was fabricated and the room temperature ferroelectric and ferromagnetic properties were studied. The macroscopic and local probe studies reveal a ferroelectric nature at room temperature, and most importantly a weak ferromagnetic like behavior was observed. The ferromagnetic behavior is expected to arise due to the variation introduced in the spin modulation of single BiFeO₃ layer due to the superstructure formation.     

Ferroelectric relaxor behaviour in Pb(Fe0.5Ta0.5)O3

The relaxor ferroelectric lead iron tantalate, Pb(Fe_0.5Ta_0.5)O₃ (PFT) is synthesized by Coulombite precursor method. The X-ray diffraction pattern of the sample at room temperature shows a cubic phase. The field dependence of dielectric response is measured in a frequency range 0.1 kHz — 1 MHz and in a temperature range from 173–373 K. The temperature dependence of permittivity (ɛ′) shows broad maxima at various frequencies. The frequency dependence of the permittivity maximum temperature (T _m ) has been modelled using Vogel-Fulcher relation.      

Structural phase transition in superconducting BaPb0.75Bi0.25O3

The room temperature crystallographic properties of distorted perovskite-type system BaPb_1-xBi_xO₃ were examined by using X-ray diffraction analysis. In addition, structural temperature changes were investigated for superconducting BaPb_0.75Bi_0.25O₃ crystals with T_c=11.4K. It was found that the room temperature structure of BaPb_1-xBi_xO₃ has an orthorhombic symmetry in the range of O≤×?0.9 and a monoclinic one in 0.9?×≤1, and that superconducting BaPb_0.75Bi_0.25O₃ shows a structural transition from an orthorhombic to a monoclinic phase at about 160K.     

稀土掺杂La-Sr-Mn-O的室温磁致伸缩效应

采用两种不同的方法制备了不同稀土含量的(La_1-xR_x)_2/3Sr_1/3MnO₃(R=Sm,Tb)大块多晶样品,并研究了它们的晶体结构及室温下的磁致伸缩效应.分析表明,随Sm,Tb对La的替代,样品的晶体结构从菱面体相转变为正交相.在结构相转变点附近,样品在室温下的磁致伸缩效应出现极大值.样品在室温下的磁致伸缩主要来源于材料中的交换磁致伸缩. 关键词：     

The multiferroic properties of Bi(Fe0.95Co0.05)O3 films

Bi(Fe_0.95Co_0.05)O₃ films were prepared on conductive indium tin oxide (ITO)/glass substrates by chemical solution deposition. Well saturated polarization hysteresis loop has been observed with a remnant polarization value of about 22 μC/cm² at room temperature. Weak ferromagnetism with saturation magnetization of about 3 emu/cm³ was observed at room temperature. The clear observation of both room temperature ferroelectric and ferromagnetic properties suggests the potential multiferroic applications of Bi(Fe_0.95Co_0.05)O₃.     

KZnF3:Cr3+ — A tunable solid state NIR-laser

Pulsed laser operation at room temperature and cw laser output below 260 K has been demonstrated with the laser material KZnF₃:Cr³⁺ in the spectral range between 775—826 nm. The system can be tuned by dispersive elements in the resonator or by temperature variation.     

Phase diagram of the relaxor (1−x)Pb(Zn1/3Nb2/3)O3-xPbTiO3 investigated by dielectric and Raman spectroscopies

Lead zinc niobate-lead titanate[(1−x)Pb(Zn_1/3Nb_2/3)O₃-xPbTiO₃] (PZN-PT) crystals with x=4.5% and x=12% have been investigated using dielectric and Raman measurements over a range of temperatures. Above room temperature, dielectric measurements show that both compositions exhibit structural phase transitions according to the phase diagram proposed by Kuwata et al. [Ferroelectrics 387 (1981) 579]. Below room temperature, an anomaly at around 180 K for the x=12% sample is observed, suggesting another phase transition. Raman measurements are used to study all phase transitions.     

Electron concentration and mobility in In2O3

The electron concentration and mobility in polycrystalline In₂O₃ have been measured as a function of temperature and partial oxygen pressure, in the temperature range from 25 to 700°C. These experimental data are critically compared with literature data. A conduction model is proposed. Theoretical values of the electron concentration as a function of the partial oxygen pressure are reported for temperatures from 700 to 1400°C. An estimate is given for the minimum room temperature “intrinsic” electron concentration in In₂O₃ after a high temperature annealing experiment. It is also shown that interpretations of conductivity values for porous material in terms of carrier concentration only, can be very misguiding.     

Large room temperature magnetoresistance in YSZ doped La0.67Ba0.33MnO3 composite

The temperature dependence of the resistivity for composite samples of (1−x)La_0.67Ba_0.33MnO₃+xYSZ(LBMO/YSZ) with different YSZ doping level of x has been investigated in a magnetic field range of 0-7000 Oe, where the YSZ represents yttria-stabilized zirconia (8 mol% Y₂O₃+92 mol% ZrO₂). With increasing YSZ doping level, the range of 0-10%, the metal-insulator transition temperature (T_P) decreases. However, the resistivity, specially the low temperature resistivity, increases. Results also show that the YSZ doping level has an important effect on a low field magnetoresistance (LFMR). In the magnetic field of 7000 Oe, a room temperature magnetoresistance value of 20% was observed for the composite with a YSZ doping level of 2%, which is encouraging for potential application of CMR materials at room temperature and low field.     

Li4SiO4-Li3VO4赝二元系和Li4GeO4-Li4SiO4-Li3VO4赝三元系中新的锂离子导体

本文在室温到300℃的温度范围内研究了Li₄SiO₄-Li₃VO₄和Li₄GeO₄-Li₄SiO₄-Li₃VO₄体系中的离子导电性,发现γ_II相固溶体Li_3+xV_1-xSi_xO₄是好的锂离子导体。所研究的成分中Li_3.3V_0.7Si_0.3O₄的离子电导率最高,室温下为1×10^-5Ω^-1·cm^-1,在42—192℃的电导激活能为0.36eV,电子电导率可以忽略,因而这是迄今所发现的最好的锂离子导体之一。粗略确定了Li₄GeO₄-Li₄SiO₄-Li₃VO₄三元系中电导率高的范围,发现在Li_3.5V_0.5Ge_0.5O₄中Si部分取代Ge可以使电导率进一步提高,Li_3.5V_0.5Ge_0.4Si_0.1O₄的室温电导率可达1.3×10^-5Ω^-1·cm^-1,电导激活能为0.40eV。 关键词：     

The role of As2O3 on the stability and some physical properties of PbO-Sb2O3 glasses

PbO-Sb₂O₃ glasses added with different concentrations of As₂O₃ (10-55 mol%) were prepared to understand their IR spectra, elastic properties (Young's modulus E, Shear modulus G, microhardness H), optical absorption and dielectric properties (constant ε, loss tan δ, ac conductivity σ_ac over a moderately wide range of frequency and temperature and breakdown strength in air medium at room temperature). Results have indicated that the structure of the PbO-Sb₂O₃-As₂O₃ glass is more rigid when the concentration of As₂O₃ is around 40 mol%.     

Structural and impedance properties of Ca3Nb2O8 ceramics

Polycrystalline sample of Ca₃Nb₂O₈ was prepared by a high-temperature solid-state reaction technique. X-ray diffraction (XRD) analysis confirms the formation of single-phase compound of hexagonal (rhombohedral) crystal structure at room temperature. Scanning electron micrograph of the material showed uniform grain distribution on the surface of the sample. Detailed studies of dielectric properties of the compound, studied in a wide frequency range (10²-10⁶ Hz) at different temperatures (25-500 °C), exhibit a dielectric anomaly suggesting phase transition of ferroelectric-paraelectric and structural type at 300 °C. Electrical properties of the material were analyzed using a complex impedance technique. The Nyquists plot showed the presence of bulk effect in the material in the studied temperature range. Studies of electrical conductivity over a wide temperature range suggest that the compound has negative temperature coefficient of resistance behavior.     

Optical properties of surface-modified Bi2O3 nanoparticles

Stearic acid coated Bi₂O₃ nanoparticles in the size range of 5-13 nm were synthesized by the microemulsion method. HRTEM showed that the morphology of Bi₂O₃ nanoparticles was ellipsoidal. The absorption edge of Bi₂O₃ nanoparticles showed a blue shift of ∼0.45 eV, comparing with that of the bulk Bi₂O₃. At room temperature, Bi₂O₃ nanoparticles also showed a strong luminescence at 397 and 420 nm, depending on the excitation wavelength.     

Electro- and thermoreflectance of Bi2Te3 and Bi2Se3

Electroreflectance measurements in Bi₂Te₃ and Bi₂Se₃ with the electric field vector of the incident light both inclined and perpendicular to the C-axis have been made at room temperature. The structures found by other workers in the reflection measurements are observed in the present experiment, together with new structures at 0.91 eV, 1.18 eV, 1.78 eV, and 2.61 eV in Bi₂Se₃ which are not related to formerly observed transitions. From these measurements, the selection rules for direct optical transitions in Bi₂Te₃ and Bi₂Se₃ are studied. Thermoreflectance measurements are also made at both room and liquid-nitrogen temperatures. The positions of the peaks obtained in the present work are compared with the electroreflectance and reflection data.     

Metamagnetic behavior of an organometallic polymer: [{Fe(C13H17N3)2}SO4·6H2O]n

The organic polymer of (C₁₃H₁₇N₃)_n has been demonstrated to show metamagnetic behavior when the polymer is combined with iron (II) sulfate. The resulting iron-bonded polymer exhibits the field-induced phase transition from an antiferro- to a ferromagnetic phase at relatively weak magnetic field strength (< 600 Oe) in the temperature range of 1.9–300 K. This iron-bonded polymer [{Fe(C₁₃H₁₇N₃)₂}SO₄·6H₂O]_n is the first example of magnetic polymer which has a backbone frame of organic polymer and shows magnetically ordered state even at room temperature.     

Electrical transport measurements in TiS3

Results of measurements of conductivity and Hall coefficient in the temperature range 15–300K and of thermal emf in the temperature range 80–400K, carried out on TiS₃ samples, are reported. The results indicate that these crystals are semiconducting with extrinsic n-type conductivity. The mobility of the carriers is about 30 cm²/V sec at room temperature, increases up to about 100 cm²/V sec at 100K and drops at lower temperatures. The Seebeck coefficient is in qualitative agreement with these findings but its detailed temperature dependence is not yet understood.     

BaSn1-xSbxO3-δ和Ba1-yLaySnO3-δ的导电机制

测量了ＢａＳｎ_1-xＳｂ_xＯ_3-δ和Ｂａ_1-yＬａ_yＳｎＯ_3-δ样品的低温电阻率和磁化率．实验结果表明，在较低温度区域，两类样品的导电机制均是传导电子的范围可变跳跃。而在较高温度区域，ＢａＳｎ_1-xＳｂ_xＯ_3-δ样品的电导主要是电子从定域态到扩展态的跃迁所贡献，Ｂａ_1-yＬａ_yＳｎＯ_3-δ样品的电导则可能来源于电子的最近邻跳跃。 关键词：