金银纳米粒子的复合组装及表面增强拉曼光谱研究

采用自组装技术在硅基底上进行金银纳米粒子的混合组装, 通过控制组装溶液中金银溶胶的体积比而控制基底上金银纳米粒子的密度. SEM结果显示金银呈亚单层均匀分布, 以吡啶为探针分子, 在不同波长的激发光下研究了纯金、银以及混合组装时的SERS效应. 利用金银在不同激发线下增强效应的不同以及探针分子吸附在金银纳米粒子表面主要谱峰相对强度差别的特点, 通过一系列校正以及差谱方法研究了金银共存时SERS效应的变化, 并分离出混合体系中金的增强行为, 结果表明在金银同时组装时吡啶的SERS谱峰特征主要表现为银纳米粒子的行为, 分离出的金SERS光谱特征接近银的行为, 说明金银纳米粒子之间产生了一定的耦合作用.     

Surface-enhanced Raman scattering of TSPP,Ag(II)TSPP,and Pb(II)TSPP adsorbed on AgI and AGCl colloids

Surface-enhanced Raman scattering (SERS) was measured for meso-tetrakis(4-sulfonatophenyl)porphine (TSPP) and its metal derivatives Ag(II)TSPP and Pb(II)TSPP adsorbed on AgI colloids, and for TSPP adsorbed on AgCl colloids. The experiments show that TSPP molecules adsorbed on AgI colloids undergo a silver incorporation, while TSPP adsorbed on AgCl colloids are converted into the porphyrin diacid H₄TSPP²⁺ and the metalloporphyrin Ag(II)TSPP. The concentration dependences of SERS spectra for TSPP adsorbed on the two substrates are quite different.     

A rapid and simple chemical method for the preparation of Ag colloids for surface-enhanced Raman spectroscopy using the Ag mirror reaction

Colloidal silver (Ag) nanoparticles (AgNP) have been widely used for surface-enhanced Raman spectroscopy (SERS) applications. We report a simple, rapid and effective method to prepare AgNP colloids for SERS using the classic organic chemistry Ag mirror reaction with Tollens’ reagent. The AgNP colloid prepared with this process was characterized using SEM, and the reaction conditions further optimized using SERS measurements. It was found that Ag mirror reaction conditions that included 20 mM AgNO₃, 5 min reaction time, and 0.5 M glucose produced AgNP colloids with an average size of 319.1 nm (s.d ± 128.1). These AgNP colloids exhibited a significant SERS response when adenine was used as the reporter molecule. The usefulness of these new AgNP colloids was demonstrated by detecting the nucleotides adenosine 5′-mono-phosphate (AMP), guanosine 5′-monophosphate (GMP), cytidine 5′-monophosphate (CMP), and uridine 5′-monophosphate (UMP). A detection limit of 500 nM for AMP was achieved with the as-prepared AgNP colloid. The bacterium Mycoplasma pneumoniae was also easily detected in laboratory culture with these SERS substrates. These findings attest to the applicability of this AgNP colloid for the sensitive and specific detection of both small biomolecules and microorganisms.     

Surface-enhanced Raman scattering and surface-enhanced resonance Raman scattering excitation profiles of Ag-2,2'-bipyridine surface complexes and of [Ru(bpy)3]2+ on Ag colloidal surfaces: manifestations of the charge-transfer resonance contributions to the overall surface enhancement of Raman scattering

Excitation profiles of SERS (surface-enhanced Raman scattering) and/or SERRS (surface-enhanced resonance Raman scattering) spectral bands of two forms of a Ag-bpy (bpy = 2,2'-bipyridine) surface complex and of [Ru(bpy)3]2+ on Ag nanoparticle (hydrosol) surfaces were determined from the spectra excited in the 458-600 nm region and are reported together with the FT-SERS spectra of the Ag-bpy surface complex and FT Raman spectra of [Ru(bpy)3] Cl2. Seven of the observed 11 fundamentals as well as their first overtones and combination bands are selectively enhanced in SERS of the Ag-bpy surface complex formed in the Ag colloid/HCl/bpy system. The profiles of these bands show a common maximum at approximately 540 nm. The selectively enhanced bands of the Ag-bpy surface complex have nearly the same wavenumbers as those enhanced in the SERRS and resonance Raman spectra of [Ru(bpy)3]2+ upon excitation close to the 453 nm maximum of its MLCT absorption band. Moreover, the intensity patterns of the bpy vibrations of the two species match both in resonance (541 nm excitation for Ag-bpy, 458 nm for [Ru(bpy)3]2+) and in off-resonance (458 and 1064 nm for Ag-bpy, 1064 nm for [Ru(bpy)3]2+). The distinct band shapes of the excitation profiles of the selectively enhanced vibrational modes of the Ag-bpy surface complex, as well as the observation of overtones and combination bands in the SERS spectra upon excitation into this "band", are interpreted in terms of a charge-transfer resonance contribution to the overall SERS enhancement. In view of the near-coincidence of the vibrational modes coupled to the resonant electronic transition of Ag-bpy with those coupled to the MLCT transition of [Ru(bpy)3]2+, the resonant electronic transition is tentatively assigned to a Ag metal to bpy (pi*) CT transition.     

碘化银胶体上四苯基卟啉金属配合物的表面增强拉曼光谱研究

研究了四苯基卟啉金属配合物（MTPP,M=Ag,Mg,Cu,Pd）在AgI胶体上的表面增强拉曼光谱（SERS）。结果显示MgTPP与基底发生金属交换生成AgTPP,而在PdTPP和CuTPP上则未发现金属交换。除卟啉环的振动外,一些苯环振动带也被显著增强。在1400～1600cm-1范围,PdTPP和CuTPP的SERS与AgTPP有很大差别,可能反映了吸附分子在次甲基桥碳原子Cm附近立体构型的差异。     

Surface enhanced Raman scattering investigation of the halide anion effect on the adsorption of 1,2,3-triazole on silver and gold colloidal nanoparticles

The halide anion effect on the adsorption of 1,2,3-triazole on Ag and Au colloidal nanoparticles has been investigated by means of surface enhanced Raman scattering (SERS), UV-visible absorption spectroscopy, and scanning electron microscopy. To interpret the SERS spectra, the vibrational spectra of 1,2,3-triazole were assigned with the help of density functional theoretical (DFT) calculations of the two tautomers of 1,2,3-triazole, both free and bound to Ag and Au adatoms. Upon addition of halide anions, both tautomers interact with the Ag surface through one nitrogen atom. Analogous behavior is observed in the case of basified Au colloids, whereas at the usual pH of these hydrosols (approximately 6) the adsorption of 1,2,3-triazole is the same of that observed in halide-free colloids.     

Synthesis, characterization and SERS activity of Au-Ag nanorods

The formation mechanism and morphology of Au-Ag bimetallic colloidal nanoparticles depend on the composition. Ag coated Au colloidal nanoparticles have been prepared by deposition of Ag through chemical reduction on performed Au colloid. The composition of the Au(100-x)-Ag(x) particles was varied from x=0 to 50. The obtained colloids were characterized by UV-vis spectroscopy and transmission electron microscopy (TEM). The Au(80)-Ag(20) colloid consists of alloy nanorods with dimension of 25nmx100nm. The activity of these nanorods in surface enhanced Raman spectroscopy (SERS) was checked by using sodium salicylate as an adsorbate probe. Intense SERS bands are observed indicating its usefulness as a SERS substrate in near infrared (NIR) laser excitation.     

Identification of biotic and abiotic particles by using a combination of optical tweezers and in situ Raman spectroscopy.

A highly versatile setup, which introduces an optical gradient trap into a Raman spectrometer, is presented. The particular configuration, which consists of two lasers, makes trapping independent from the Raman excitation laser and allows a separate adjustment of the trapping and excitation wavelengths. Thus, the excitation wavelength can be chosen according to the needs of the application. We describe the successful application of an optical gradient trap on transparent as well as on reflective, metal-coated microparticles. Raman spectra were recorded from optically trapped polystyrene beads and from single biological cells (e.g., erythrocytes, yeast cells). Also, metal-coated microparticles were trapped and used as surface enhanced Raman spectroscopy (SERS) substrates for tests on yeast cells. Furthermore, the optical gradient trap was combined with a SERS fiber probe. Raman spectra were recorded from trapped red blood cells using the SERS fiber probe for excitation.     

Surface-enhanced Raman spectroscopy based on conical holed enhancing substrates

In this contribution, surface-enhanced Raman spectroscopy (SERS) based on conical holed glass substrates deposited with silver colloids was reported for the first time. It combines the advantages of both dry SERS assays based on plane films deposited with silver colloids and wet SERS assays utilizing cuvettes or capillary tubes. Compared with plane glass substrates deposited with silver colloids, the conical holed glass substrates deposited with silver colloids exhibited five-to ten-folds of increase in the rate of signal enhancement, due to the internal multiple reflections of both the excitation laser beam and the Raman scattering photons within conical holes. The application of conical holed glass substrates could also yield significantly stronger and more reproducible SERS signals than SERS assays utilizing capillary tubes to sample the mixture of silver colloids and the solution of the analyte of interest. The conical holed glass substrates in combination with the multiplicative effects model for surface-enhanced Raman spectroscopy (MEM_SERS) achieved quite sensitive and precise quantification of 6-mercaptopurine in complex plasma samples with an average relative prediction error of about 4% and a limit of detection of about 0.02 μM using a portable i-Raman 785H spectrometer. It is reasonable to expect that SERS technique based on conical holed enhancing substrates in combination with MEM_SERS model can be developed and extended to other application areas such as drug detection, environmental monitoring, and clinic analysis, etc.     

Silica-coated gold nanostars for combined surface-enhanced Raman scattering (SERS) detection and singlet-oxygen generation: a potential nanoplatform for theranostics

This paper reports the synthesis and characterization of surface-enhanced Raman scattering (SERS) label-tagged gold nanostars, coated with a silica shell containing methylene blue photosensitizing drug for singlet-oxygen generation. To our knowledge, this is the first report of nanocomposites possessing a combined capability for SERS detection and singlet-oxygen generation for photodynamic therapy. The gold nanostars were tuned for maximal absorption in the near-infrared (NIR) spectral region and tagged with a NIR dye for surface-enhanced resonance Raman scattering (SERRS). Silica coating was used to encapsulate the photosensitizer methylene blue in a shell around the nanoparticles. Upon 785 nm excitation, SERS from the Raman dye is observed, while excitation at 633 nm shows fluorescence from methylene blue. Methylene-blue-encapsulated nanoparticles show a significant increase in singlet-oxygen generation as compared to nanoparticles synthesized without methylene blue. This increased singlet-oxygen generation shows a cytotoxic effect on BT549 breast cancer cells upon laser irradiation. The combination of SERS detection (diagnostic) and singlet-oxygen generation (therapeutic) into a single platform provides a potential theranostic agent.     

Reaction of metallotetraphenylporphyrins on hydroxyl-modified silver colloid and Ag2O colloid by surface-enhanced Raman scattering.

This paper reports a novel reaction of metallotetraphenylporphyrins on hydroxyl-modified silver colloid and Ag2O colloid. Surface-enhanced Raman spectra of Ag(II) and Cu(II) complexes of tetraphenylporphyrin (TPP) adsorbed on the hydroxyl-modified Ag colloid and Ag2O colloid have been studied. The time-dependent SERS spectra of MTPP (M = Ag, Cu) on hydroxyl-modified Ag colloid were recorded and dramatic change on SERS spectra was observed. The final spectra were found to be strikingly different from the corresponding normal Raman spectra (NRS), with the appearance of new Raman bands at 1614. 1417, 947, 674 and 292 cm(-1). The UV-visible absorption spectrum of MTPP on hydroxyl-modified Ag colloid exhibits a broad shoulder near 460 nm. Similar spectral phenomena were also observed for AgTPP and CuTPP adsorbed on Ag2O colloid. The observed spectral alterations were ascribed to new species formation due to the irreducible oxidation of MTPP on the colloids.     

Surface-Enhanced Raman Scattering of Rhodamine 123 in Silver Hydrosols and in Langmuir-Blodgett Films on Silver Islands

Surface-enhanced Raman scattering(SERS) of the Rhodamine 123 (Rh 123) molecule on ion-induced silver colloids has been studied. A time-dependent study of the SER spectra at a particular pH confirms charge transfer interaction between the probe molecule and the metal. The SER spectra of Rh 123 in Ag sol is compared with that of the molecules organized in a monolayer on silver island films by the Langmuir-Blodgett (LB) technique. The origin of high SERS activity of Rh 123 molecules in a monolayer on a silver island film is shown to be due to physisorption whereas in the ion-induced colloidal SERS both physisorption and chemisorption machanisms are involved. From these results, the contribution of charge transfer interaction to SERS in Ag sol has been estimated. In monolayer SERS, all the in-plane and out-of-plane (of xanthene ring) modes are more or less equally enhanced. This indicates that the xanthene plane of Rh 123 molecule organized in a LB film is oriented neither flat nor perpendicular to the silver island surface but is tilted. Copyright 2001 Academic Press.     

Raman and SERS recognition of β-carotene and haemoglobin fingerprints in human whole blood

The present work reports on Raman and Surface Enhanced Raman Scattering (SERS) vibrational fingerprints of β-carotene and haemoglobin in fresh whole blood (i.e. right after blood test) with different laser excitations, i.e. visible (514 nm) and near-infrared (NIR, 785 nm). The use of colloidal silver nanoparticles significantly increases the Raman signal, thus providing a clear SERS spectrum of blood. The collected spectra have been examined and marker bands of β-carotene and of the haem prosthetic group of haemoglobin have been found. In particular, the fundamental features of β-carotene (514 nm excitation), blood proteins and haem molecules (785 nm excitation) were recognized and assigned. Moreover haemoglobin SERS signals can be identified and related with its oxygenation state (oxy-haemoglobin). The data reported show the prospects of Raman and SERS techniques to detect important bio-molecules in a whole blood sample with no pre-treatment.     

Excitation spectra of surface enhanced Raman scattering on sols.

A phenomenological approach is described for practical computations of the excitation spectra in surface enhanced Raman scattering (SERS) obtained with aggregated metal colloids.     

Synthesis of AgcoreAushell bimetallic nanoparticles for immunoassay based on surface-enhanced Raman spectroscopy

Layered core-shell bimetallic silver-gold nanoparticles were prepared by coating Au layers over Ag seeds by a seed-growth method. The composition of Ag100-xAux particles can vary from x=0 to 30. TEM and SEM images clearly show that the bimetallic nanoparticles are of core-shell structure with some pinholes on the surface. Strong surface-enhanced Raman (SER) signals of thiophenol and p-aminothiophenol have been obtained with these colloids. It was found that the SERS activity of aggregated colloids critically depends on the molar ratio of Ag to Au. With the increase of the Au molar fraction, the SERS activity enhances first and then weakens, with the maximal intensity being 10 times stronger than that of Ag colloids. The AgcoreAushell nanoparticles were then labeled with monoclonal antibodies and SERS probes and used for immunoassay analysis. In the proposed system, antibodies immobilized on a solid substrate can interact with the corresponding antigens to form a composite substrate, which can capture reporter-labeled AgcoreAushell nanoparticles modified with the same antibodies. The immunoreaction between the antibodies and antigens was demonstrated by the detection of characteristic Raman bands of the probe molecules. AgcoreAushell bimetallic nanoparticles, as a new SERS active and biocompatible substrate, will be expected to improve the detection sensitivity of immunoassay.     

Enhancement origin of SERS from pyridine adsorbed on AgCl colloids

SERS of pyridine molecules adsorbed on AgCl colloids are recorded. The enhancement origins are discussed by studying the effects of illumination, thiosulfate, hydrogen peroxide and ferricyanide on SERS of pyridine on AgCl colloids. In addition to an important contribution of local field enhancement on photolytic Ag particles in AgCl colloid, the surface Ag⁺ complexes on AgCl colloids as the SERS-active sites also make an important contribution to SERS of pyridine on AgCl colloid.     

Characterization and surface-enhanced Raman spectral probing of silver hydrosols prepared by two-wavelength laser ablation and fragmentation

A four step Ag foil laser ablation-Ag nanoparticle fragmentation procedure in ultrapure water was carried out both under argon and in air. Pulses of a high power Nd/YAG laser were used for laser ablation (1064 nm) and for the three step Ag hydrosol treatment in the absence of Ag foil in the sequence 1064-532-1064 nm. Transmission electron microscopy (TEM) and surface plasmon (SP) extinction spectra provide evidence of Ag nanoparticle fragmentation in the second and third step of the procedure carried out under argon. While polydispersity of Ag hydrosol increases in the second step, both the polydispersity and the mean size of the nanoparticles are reduced in the third step. Qualitative and quantitative surface-enhanced Raman scattering (SERS)/surface-enhanced resonance Raman scattering (SERRS) spectral probing of systems with Ag hydrosols and the selected adsorbates at 514.5 nm excitation shows that Ag hydrosols obtained in the second step of the preparation procedure carried out in air are the most suitable substrates for SERS/SERRS experiments performed at this excitation wavelength.     

Surface-enhanced Raman scattering measurements on silver nanoparticles covered with differently formed platinum films

Gold and silver electromagnetic nanoresonators covered by a thin layer of platinum are often used to study adsorption of various molecules on “model platinum surfaces” with surface-enhanced Raman scattering (SERS) spectroscopy. In this contribution spectra of pyridine adsorbed on films formed from core–shell Ag@Pt and Ag@Ag–Pt nanoparticles and pure Pt or Ag nanoparticles were measured using a confocal Raman microscope. The SERS spectra of pyridine adsorbed on alloy Ag@Ag–Pt nanoparticles could not be obtained as a linear combination of spectra measured on pure Ag and Pt surfaces. In other words, for silver electromagnetic nanoresonators covered by platinum there is no simple correlation between the “quality” of the deposited Pt layer and the relative intensity of SERS bands characteristic for adsorbate interacting with silver. The SERS spectra accumulated from various places of a film formed from Ag@Pt or Ag@Ag–Pt nanoclusters may differ significantly. Using Ag@Pt nanoparticles with practically negligible amount of Ag on the surface (as per the stripping measurement), it is possible to record SERS spectrum in which the contribution characteristic for pyridine adsorbed on the Ag surface is well visible. It means that, even for macroscopic samples of core–shell Ag–Pt nanoparticles, averaging of many spectra measured at various locations of the sample should be carried out to characterize reliably their properties.     

Surface-enhanced Raman scattering of EDOT and PEDOT on silver and gold nanoparticles

Surface-enhanced Raman scattering (SERS) spectra of the conducting polymer poly(3,4-ethylenedioxythiophene) (PEDOT) and its monomer 3,4-ethylenedioxythiophene (EDOT) on Ag and Au nanoparticles presenting different morphologies and stabilizing agents have been obtained using the excitation radiation at 633 nm. The SERS spectra of the monomer and polymer are strongly dependent both on the metal and capping agent of the substrate. SERS spectra of EDOT on Au nanospheres indicates that adsorption occurs with the thiophene ring perpendicular to the metal surface. In contrast, polymerization takes place on the silver surface of Ag nanospheres. EDOT adsorption on Ag nanoprisms with polyvinylpyrrolidone (PVP) as capping agent occurs similarly to that observed on gold. Surface-enhanced resonance Raman scattering (SERRS) spectra of PEDOT on gold nanostars that present a thick layer of PVP show no chemical interaction of PEDOT with the metal surface; however, when PEDOT is adsorbed on citrate stabilized gold nanospheres, the SERRS spectra suggest that thiophene rings are perpendicular to the surface. Oxidation of PEDOT also is observed on Ag nanospheres. The investigation of the interface between PEDOT and metal surface is crucial for the development in polymer-based optoelectronic devices since this interface plays a crucial role in their stability and performance.     

Surface-enhanced Raman scattering study of the anthraquinone red pigment carminic acid

FT-Raman and surface-enhanced Raman scattering (SERS) spectroscopy were applied in the vibrational characterization and study of the adsorption and acidity behaviour of the highly fluorescent anthraquinone red pigment carminic acid (CA) on Ag nanoparticles prepared by chemical reduction with citrate and hydroxylamine. The SERS spectra were obtained at several pHs and excitation wavelengths and on Ag nanoparticles prepared by two different methods: chemical reduction with citrate and hydroxylamine in order to find the best experimental conditions for the vibrational study and detection of CA. Three CA forms can be identified on the metal surface, corresponding to the mono-, di- and tri-anionic CA species, whose relative intensity in the SERS spectra can markedly vary depending on the chemical properties of the offered surface and the excitation wavelength. This study could be very helpful for researchers trying to apply surface-enhanced techniques in the detection of small amounts of anthraquinone molecules, both under a cultural heritage and under a biological point of view.