Effects of Zr-substitution on microstructure and properties of YCaVIG ferrites

Y_2.6−xCa_0.4+xZr_xV_0.2Fe_4.8−xO₁₂ (Zr_x:YCaVIG) ferrite materials have been prepared by an oxide process. The phase formation and microstructure were analyzed by X-ray diffraction and scanning electron microscopy, respectively. The effects of Zr⁴⁺ substitution on phase compositions, sintering properties, microstructures and electromagnetic properties were investigated. The results indicate that all the sintered specimens with different Zr⁴⁺ contents show a single garnet structure. The addition of ZrO₂ can gradually increase the lattice constant, and lower the sintering temperature and the theoretical density. With the increase of Zr⁴⁺ content, the dielectric loss (tan δ_ε) and coercivity (H_c) decrease and then slightly increase, which is due to the variation of the microstructure. But the saturation magnetization (4πM_s) shows the opposite variation compared to the former two properties. However, the dielectric constant (ε_r) remains stable and remanence (B_r) monotonically declines. Finally, the specimen of Y_2.3Ca_0.7Zr_0.3V_0.2Fe_4.5O₁₂ sintered at 1350° possesses the optimum electromagnetic properties: ε_r=14.8, tan δ_ε=1.35×10⁻³, 4πM_s=1638 Gs, B_r=596 Gs, H_c=0.75 Oe and ΔH (ferromagnetic resonance linewidth)=66 Oe.     

Magnetoelectric characterization of xNi0.75Co0.25Fe2O4-(1−x)BiFeO3 nanocomposites

Magnetoelectric (ME) nanocomposites containing Ni_0.75Co_0.25Fe₂O₄-BiFeO₃ phases were prepared by citrate sol-gel process. X-ray diffraction (XRD) analysis showed phase formation of xNi_0.75Co_0.25Fe₂O₄-(1−x)BiFeO₃ (x=0.1, 0.2, 0.3 and 0.4) composites on heating at 700 °C. Transmission electron microscopy revealed the formation of powders of nano order size and the crystal size was found to vary from 30 to 85 nm. Dispersion in dielectric constant (ε) and dielectric loss (tan δ) in the low-frequency range have been observed. It is seen that nanocomposites exhibit strong magnetic properties and a large ME effect. On increasing Ni_0.75Co_0.25Fe₂O₄ contents in the nanocomposites, the saturation magnetization (M_S) and coercivity (H_C) increased after annealing at 700 °C. The large ME output in the nanocomposites exhibits strong dependence on magnetic bias and magnetic field frequency. The large value of ME output can be attributed to small grain size of ferrite phase of nanocomposite being prepared by citrate precursor process.     

Effect of Bi2O3 on EPR, optical transmission and DC conductivity of vanadyl doped alkali bismuth borate glasses

Glasses with composition xBi₂O₃·(30−x)M₂O·70B₂O₃ (M=Li, Na) containing 2 mol% V₂O₅ have been prepared over the range 0≤x≤15 (x is in mol%). The electron paramagnetic resonance spectra of VO²⁺ of these glasses have been recorded in the X-band (≈9.3 GHz) at room temperature (RT≈300 K). Spin Hamiltonian parameters, g_∥, g_⊥, A_∥, A_⊥, dipolar hyperfine coupling parameter, P, and Fermi contact interaction parameter, K, have been calculated. The molecular orbital coefficients, α² and γ², have been calculated by recording the optical transmission spectra. In xBi₂O₃·(30−x)Li₂O·70B₂O₃ glasses there is decrease in the tetragonality of the V⁴⁺O₆ complex for x up to 6 mol% whereas for x≥6 mol%, tetragonality increases. In xBi₂O₃·(30−x)Na₂O·70B₂O₃ glasses there is increase in the tetragonality of the V⁴⁺O₆ complex with increasing x. The 3d_xy orbit expands with increase in Bi₂O₃:M₂O ratio. Values of the theoretical optical basicity, Λ_th, have also been reported. The DC conductivity increases with increase in temperature. The order of conductivity is 10⁻⁵ ohm⁻¹ m⁻¹ at low temperature and 10⁻³ ohm⁻¹ m⁻¹ at high temperature. The DC conductivity decreases and the activation energy increases with increase in Bi₂O₃:M₂O ratio.     

Structural, electrical and magnetic characterizations of Ni-Cu-Zn ferrite synthesized by citrate precursor method

Fine powders of NiCuZn ferrite with composition Ni_(0.7−x)Cu_xZn_0.3Fe₂O₄ (where x=0, 0.2, 0.4 and 0.6) were prepared by the citrate precursor method. X-ray diffraction measurements confirm the formation of single-phase cubic spinel structure. The grain size was estimated by SEM micrograph which increases with Cu content. Dielectric constant (?) and loss tangent (tan δ) were measured as a function of frequency. The ? and tan δ show a decreasing trend with increase of frequency for all the samples. The DC resistivity was measured as a function of temperature. The temperature-dependent DC resistivity measurements show that the room-temperature DC resistivity of NiCuZn ferrite with x=0.2 is of the order of 10⁹ Ω cm. The AC conductivity (σ_AC) was studied as a function of frequency. The hysteresis data indicate that the maximum saturation magnetization of 38.66 emu/g is obtained for the composition with x=0.2.     

Low-temperature sintering and microwave dielectric properties of Ca2Zn4Ti15O36 ceramics

The sintering behavior, microstructures, and microwave dielectric properties of Ca₂Zn₄Ti₁₅O₃₆ ceramics with B₂O₃ addition were investigated. The crystalline phases and microstructures of Ca₂Zn₄Ti₁₅O₃₆ ceramics with 0-10 wt% B₂O₃ addition were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS). The sintering temperature of Ca₂Zn₄Ti₁₅O₃₆ ceramic was lowered from 1170 to 930 °C by 10 wt% B₂O₃ addition. Ca₂Zn₄Ti₁₅O₃₆ ceramics with 8 wt% B₂O₃ addition sintered at 990 °C for 2 h exhibited good microwave dielectric properties, i.e., a quality factor (Qf) 11,400 GHz, a relative dielectric constant (ε_r) 41.5, and a temperature coefficient of resonant frequency (τ_f) 94.4 ppm/°C.     

A novel high-k ‘Y5V’ barium titanate ceramics co-doped with lanthanum and cerium

Structural, dielectric, and ferroelectric properties of a novel high-k ‘Y5V’ (Ba_1−xLa_x)(Ti_1−x/4−yCe_y)O₃ ceramics (where x=0.03 and y=0.05, denoted by BL3TC5) with the highest ‘Y5V’ dielectric response (ε′>10 000) among rare-earth-doped BaTiO₃ ceramics to date are investigated in detail using SEM, TEM, XRD, DSC, EPR, Raman spectroscopy (RS), temperature and frequency, electric field dependences of dielectric permittivity (ε′), and temperature and electric field dependences of ferroelectric hysteresis loops. The BL3TC5 diffusion of ferroelectric phase transition occurs around dielectric peak temperatures (T_m) near a room temperature characteristic of dielectric thermal relaxation. Powder XRD data and defect complex model were given. “Relaxor” behavior associated with an order/disorder model and formation of a solid solution were discussed. The EPR results provided the evidence of Ti vacancies as compensating for lattice defects. High-k relaxor nature of BL3TC5 is characterized by an average cubic structure with long-range lattice disordering and local polar ordering; a slow change of the ε′ (T) and P_r(T) curves around T_m; no phase transition observed by DSC; and a broad, red-shifted A₁ (TO₂) Raman phonon mode at 251 cm⁻¹ accompanying the disappearance of the “silent” mode at 305 cm⁻¹ and a clear anti-resonance effect at 126 cm⁻¹ at room temperature.     

Synthesis, magnetic and dielectric properties of Er-Ni doped Sr-hexaferrite nanomaterials for applications in High density recording media and microwave devices

A sol-gel combustion method has been successfully employed for the synthesis of Sr-hexaferrite nanomaterials doped with Er³⁺ and Ni²⁺ at strontium and iron sites, respectively. The X-ray diffraction analysis confirmed the single magnetoplumbite phase and the crystallite size was found to be in the range of 14-16 nm, suitable for obtaining signal-to-noise ratio in the high density recording media. The magnetic properties such as saturation magnetization (M_s), remanence (M_r) and coercivity (H_c) were calculated from hysteresis loops. M_s, M_r and H_c are observed to increase with the Er-Ni content. The dielectric constant (ε´) and dielectric loss (tan δ) is found to decrease with the increase in frequency and is explained on the basis of Maxwell-Wagner and Koops theory. The decrease in dielectric constant and dielectric loss but increase in saturation magnetization and remanence with Er-Ni content suggests that the materials are suitable for applications in microwave devices and high density recording media .     

Comparison of piezoelectricity in Ta and La substituted lead calcium titanate ceramics

This paper reports the experimental investigations on the effect of La³⁺ and Ta⁵⁺ substitution on the structural characteristics and dielectric and piezoelectric properties of lead calcium titanate (PCT) ceramic. The PCT samples with A-site and B-site substitution having the composition formula Pb_0.76−x/2La_xCa_0.24(Ti_0.98Mn_0.02)_1−x/2O₃ and Pb_0.76Ca_0.24Mn_0.02Ti _0.98−5x/4Ta_xO₃, x=0 and 0.02, respectively_, were prepared using conventional solid-state reaction method. Phase formation and structural analysis were studied using X-ray diffraction and scanning electron microscopy, respectively. Dielectric constant (ε′) and loss tangent (tan δ) as a function of frequency were measured at room temperature as well as elevated temperature. Both ε′ and tan δ decreased with increase in frequency at room temperature. Curie temperature decreased with La and Ta doping in PCT ceramics due to a decrease in the tetragonality of PCT ceramics. Piezoelectric charge coefficients (d₃₃, d₃₁) increased with La³⁺ substitution due to reorientation of the grains and decreased with Ta⁵⁺ substitution because of the increase in porosity. Figure of merit d_hg_h increased and decreased with La and Ta substitution, respectively. A good ferroelectric behaviour is obtained for La substitution, while no hysteresis is obtained for Ta substitution.     

Electrical conduction and dielectric properties of vanadium phosphate glasses doped with lithium

AC conductivity and dielectric studies on vanadium phosphate glasses doped with lithium have been carried out in the frequency range 0.2-100 kHz and temperature range 290-493 K. The frequency dependence of the conductivity at higher frequencies in glasses obeys a power relationship, σ_ac=Aω^s. The obtained values of the power s lie in the range 0.5≤s≤1 for both undoped and doped with low lithium content which confirms the electron hopping between V⁴⁺ and V⁵⁺ ions. For doped glasses with high lithium content, the values of s≤0.5 which confirm the domination of ionic conductivity. The study of frequency dependence of both dielectric constant and dielectric loss showed a decrease with increasing frequency while they increase with increasing temperature. The results have been explained on the basis of frequency assistance of electron hopping besides the ionic polarization of the glasses. The bulk conductivity increases with increasing temperature whereas decreases with increasing lithium content which means a reduction of the V⁵⁺.     

Post-sintering annealing effect on the diffuse phase transition in (Pb1−xBax)(Yb0.5Ta0.5)O3 ceramics

The effect of post sintering annealing on the dielectric response of (Pb_1−xBa_x)(Yb_0.5Ta_0.5)O₃ ceramics in the diffuse phase transition range (x=0.2) has been investigated. The samples are prepared by conventional solid-state reaction method. The samples are sintered at 1300 °C for 2 h and annealed at different temperatures (800, 900 and 1000 °C) for 8 h and at 800 °C for different time durations (8, 12 and 24 h). A significant change in the dielectric response has been observed in all the samples. The dielectric constant increases remarkably and the dielectric loss tangent decreases. The dielectric peaks of the annealed samples are observed to be more diffused with noticeable frequency dispersion compared to the as sintered sample.     

Electron paramagnetic resonance, optical and electrical properties of vanadyl doped alkali germanoborate glasses

Glasses with composition xGeO₂.(0.30−x)M₂O.0.70B₂O₃ (M=Li, K) containing 2.0 mol% of V₂O₅ have been prepared in the range 0.00≤x≤0.15 by normal melt quenching method. Electron paramagnetic resonance (EPR), optical transmission and absorption spectra and dc conductivity of these glasses have been studied. Spin Hamiltonian parameters (SHPs) of VO²⁺ ions, dipolar hyperfine coupling parameter, P, Fermi contact interaction parameter, K and molecular orbital coefficients (α² and γ²) have been calculated. In GeO₂·Li₂O·B₂O₃ glasses there is no change in the tetragonality of the V⁴⁺O₆ complex and the size of 3d_xy orbit also remains unchanged with increase in GeO₂ content. In GeO₂·K₂O·B₂O₃ glasses, there is an increase in the tetragonality of the V⁴⁺O₆ complex and the 3d_xy orbit expands with increase in GeO₂ content. Values of the theoretical optical basicity, Λ_th, have also been reported. Optical band gap decreases with increase in GeO₂ content. The dc conductivity of these glasses decreases and the activation energy increases with increase in GeO₂:M₂O ratio.     

A new, lead free, family of perovskites with a diffuse phase transition: NaNbO3-based solid solutions

(1−x)NaNbO₃-(x)ABO₃ perovskite solid solutions belonging to group II according to the Krainik classification [Izv. Akad. Nauk SSSR, Ser. Phys. 28 (1964) 643] exhibit a dramatic diffusion of the dielectric permittivity ε′ maximum and relaxor-type behavior when the second component concentration exceeds a threshold value x₀. The concentration phase transition to this relaxor-like phase is abrupt (of the first order kind) that is seen from the step in the dependence of the ε′(T) maximum temperature, T_m, on x. Some relaxor-like properties appear even at x<x₀ in the course of cooling while disappear during the course of heating. Due to this fact and because of coupling of the antiferroelectric (AFE) and ferroelectric (FE) order parameters a giant (up to 100 K) temperature hysteresis of ε′(T) arises at AFE-AFE first order phase transition. The T_m values of all the known NaNbO₃-ABO₃ relaxor-type compositions are well below the room temperature and the dielectric permittivity maximal values, ε′_m, are much lower than in the case of Pb-containing relaxors. However both T_m and ε′_m values can be increased substantially by Li or K-doping leading to the formation of NaNbO₃-ABO₃-LiNbO₃ (KNbO₃) solid solutions.     

Dielectric dispersion in PbO-Sb2O3-As2O3:V2O5 glasses

Dielectric properties, viz. dielectric constant ε′, loss tan δ and a.c conductivity σ_ac (over a wide range of frequency and temperature) and dielectric breakdown strength of PbO-Sb₂O₃-As₂O₃ glasses doped with V₂O₅ (ranging from 0 to 0.5 mol%) are studied. Analysis of these results, based on optical absorption and ESR spectra, indicates that the insulating strength of the glasses is comparatively high when the concentration of V₂O₅ is about 0.3 mol% in the glass matrix.     

Densification, microstructural evolution, and dielectric properties of CaTiO3-LaGaO3 microwave ceramics

The relations among the densification, microstructural evolution, and microwave dielectric properties of the (1−x)CaTiO₃-xLaGaO₃ ceramics with x=0.34 and 0.36 were investigated in this study. The results indicated that (1−x)CaTiO₃−xLaGaO₃ ceramics can be densified at 1300 °C with at least 97% of the theoretical value. The ceramics reported an orthorhombic perovskite structure, and no other detectable phases were found. Both ε_r and Q×f values can be improved by slowing the cooling rate during sintering. The ε_r and Q×f values of the 0.64CaTiO₃-0.36LaGaO₃ ceramics at cooling rates of >10 °C/min and 0.1 °C/min are 48.1 and 27,500 and 48.7 and 38,000, respectively. The higher densification obtained at a slower cooling rate plays an important role in improving the microwave dielectric properties.     

Phase transformation behavior and dielectric characteristics of BaTi1−x(Al1/2Nb1/2)xO3 (0.01≤x≤0.40) ceramics

Microstructure, phase transformation behavior and dielectric properties of BaTi_1−x(Al_1/2Nb_1/2)_xO₃ (0.01≤x≤0.40) ceramics were investigated. A high level of (Al_1/2Nb_1/2)⁴⁺ substitution for Ti⁴⁺ ions was not conducive to the stability of the perovskite structure and resulted in the formation of BaAl₂O₄. As x was increased, lattice constants and unit cell volume decreased, reached a minimum at x=0.10 and then increased. The BaTi_1−x(Al_1/2Nb_1/2)_xO₃ ceramics at room temperature experienced a transformation from ferroelectric to paraelectric phase with increasing (Al_1/2Nb_1/2)⁴⁺ concentration. Meanwhile, permittivity of the BaTi_1−x(Al_1/2Nb_1/2)_xO₃ ceramics was markedly reduced, while Q value was slightly increased. Frequency dispersion of dielectric peak was obviously increased as x was increased from 0.01 to 0.10. It is of great interest that a dielectric abnormity represented by a broad dielectric peak at 200-400 K was observed for the composition with x=0.40.     

Study of (Bi2O3)(BaxMo1−xO3) polycrystalline ceramic as relaxor ferroelectric

Solid solutions of bismuth layered (Bi₂O₃)(Ba_xMo_1−xO₃) (0.2≤x≤0.8, x is in step of 0.2) ceramics were prepared by conventional solid-state reaction of the constitutive oxides at optimized temperatures with a view to study its electrical properties. Powder X-ray diffraction has been employed for physical characterization and an average grain size of ∼16 to 22 nm was obtained. XRD study reveals the single phase structure of the samples. Dielectric properties such as dielectric constant (ε′), dielectric loss (tanδ) and ac electrical conductivity (σ_ac) of the prepared ceramics sintered at various temperatures in the frequency range 10¹–10⁷ Hz have been studied. A strong dispersion observed in the dielectric properties shows the relaxor type behavior of the ceramic. The presence of maxima in the dielectric permittivity spectra indicates the ferroelectric behavior of the samples. Impedance plots (Cole–Cole plots) at different frequencies and temperatures were used to analyze the electric behavior. The value of grain resistance increases with the increase in Ba ion concentration. The conductivity mechanism shows a frequency dependence, which can be ascribed to the space charge mainly due to the oxygen vacancies. The relaxation observed for the M″ (ω) or Z″ (ω) curves is correlated to both localized and long range conduction. A single ‘master curve’ for the normalized plots of all the modulus isotherms observed for a given composition indicates that the conductivity relaxation is temperature independent.     

Electrical conduction and magnetoelectric effect of (x) BaTiO3 + (1−x) Ni0.92Co0.03Cu0.05Fe2O4 composites in ferroelectric rich region

Particulate composites with composition (x)BaTiO₃+(1−x)Ni_0.92Co_0.03Cu_0.05Fe₂O₄ in which x varies as 1, 0.85, 0.70, 0.55 and 0 (in mol%) were prepared by the conventional double sintering ceramic technique. The presence of two phases viz. ferromagnetic (Ni_0.92Co_0.03Cu_0.05Fe₂O₄) and ferroelectric (BaTiO₃) was confirmed by X-ray diffraction analysis. The dc resistivity and thermo-emf measurements were carried out with variation of temperature. The ac conductivity (σ_ac) measurements investigated in the frequency range 100 Hz to 1 MHz conclude that the conduction in these composites is due to small polarons. The variation of dielectric constant and loss tangent with frequency (20 Hz to 1 MHz) was studied. The static magnetoelectric conversion factor, i.e. dc (dE/dH)_H was measured as a function of intensity of applied magnetic field. The changes were observed in electrical properties as well as in magnetoelectric voltage coefficient as the molar ratio of the constituent phases was varied. A maximum value of magnetoelectric conversion factor of 536.06 μV/cm Oe was observed for the composite with 70% BaTiO₃+30% Ni_0.92Co_0.03Cu_0.05Fe₂O₄ at a dc magnetic field of 2.3 K Oe. The maximum magnetoelectric conversion output has been explained in terms of ferrite-ferroelectric content, applied static magnetic field and resistivity.     

The influence of microscopic parameters on the ionic conductivity of SrBi2(Nb1−xVx)2O9−δ(0≤x≤0.3) ceramics

Layered SrBi₂(Nb_1−xV_x)₂O_9−δ (SBVN) ceramics with x lying in the range 0-0.3 (30 mol%) were fabricated by the conventional sintering technique. The microstructural studies confirmed the truncating effect of V₂O₅ on the abnormal platy growth of SBN grains. The electrical conductivity studies were centred in the 573-823 K as the Curie temperature lies in this range. The concentration of mobile charge carriers (n), the diffusion constant (D₀) and the mean free path (a) were calculated by using Rice and Roth formalism. The conductivity parameters such as ion-hopping rate (ω_p) and the charge carrier concentration (K′) term have been calculated using Almond and West formalism. The aforementioned microscopic parameters were found to be V₂O₅ content dependent on SrBi₂(Nb_1−xV_x)₂O_9−δ ceramics.     

Percolation phenomenon in barium samarium titanate-silver composite

Ba₄Sm_9.33Ti₁₈O₅₄-Ag (BST-Ag) composites were prepared by a solid-state ceramic route and its dielectric properties were investigated in the vicinity of percolation threshold. The structure and microstructure of the composites were analyzed by X-ray diffraction along with optical and scanning electron microscopy observations. The effects of silver content and frequency on the dielectric properties of BST-Ag composites were studied using a LCR meter. The relative permittivity (ε_r) of the composite increases with silver content below the percolation limit and is in agreement with power law. A 0.14 volume fraction of silver loading increases the relative permittivity of the composite from 50 to 450 at 10 kHz. Addition of 0.15 volume fraction of silver increases the relative permittivity of the composite in the order of 10⁵. It is found that the giant relative permittivity is almost constant for frequencies from 1 kHz to 1 MHz. This high ε_r composite offers the perspectives for application in electromechanical devices.