Synthesis of nanosized TiO2/SiO2 catalysts by the ultrasonic microemulsion method and their photocatalytic activity

Nanosized TiO₂/SiO₂ catalysts prepared by hydrolysis of titanium n-butoxide in microemulsion showed enhanced photocatalytic activity. In the presence of catalyst ME-2 and after 90 min irradiation by UV light, methylene blue was completely converted evidenced by the absence of its absorption band in the UV-Vis spectra. This catalyst demonstrated much better degradation ability than P-25 and naked TiO₂.     

TiO2/Cu2O/Pt复合空心微球的制备及其光催化性能

以锐钛矿相TiO₂溶胶为基底,采用沉淀法和液相沉积法制备了TiO₂/Cu₂O/Pt复合空心微球,通过改变n₍Ti⁴⁺)∶n_Cu2+和H₂Pt Cl₆·6H₂O溶液的加入量对TiO₂的形貌和结构进行调控,采用不同的方法对不同样品的物相及结构、微观形貌和光学性能进行了对比分析。分析结果表明,复合材料中Pt与Cu₂O的引入产生协同效应,不仅在一定程度上阻止了电子-空穴的复合,还降低了禁带宽度,在可见光区域光吸收明显增强。与TiO₂、Cu₂O和TiO₂/Cu₂O光催化剂相比较,TiO₂/Cu₂O/Pt降解有机污染物的能力显著增强,首次光照120 min可降解93%的甲基橙(MO)溶液,4次循环后降解率为71%,具有良好的光催化...     

ZnFe2O4/Ag/TiO2复合材料的制备及其光催化性能

以硝酸银、钛酸四丁酯、无水氯化锌、六水氯化铁为原料,采用溶胶-凝胶法与溶剂热相结合的方法制备了ZnFe₂O₄/Ag/TiO₂复合材料,通过扫描电子显微镜、能谱分析仪、X射线粉末衍射仪、X射线光电子能谱仪、振动样品磁强计、紫外可见分光光度计对样品进行表征及测试。结果表明：ZnFe₂O₄/Ag/TiO₂-10具有最佳的光催化效果,在紫外和可见光下对染料的降解率都能达到90%以上,具有优异的紫外可见光光催化活性。ZnFe₂O₄/Ag/TiO₂具有独特的磁性,能在外部磁场作用下进行回收利用,这使其在实际应用中成为可能。通过磁分离技术重复回收利用5次后仍然保持优良的光催化性能,说明ZnFe₂O₄/Ag/TiO₂-10具有优异的磁性及较高的光催化循环稳定性。     

ZnFe2O4/Ag/TiO2复合材料的制备及其光催化性能

以硝酸银、钛酸四丁酯、无水氯化锌、六水氯化铁为原料,采用溶胶-凝胶法与溶剂热相结合的方法制备了ZnFe₂O₄/Ag/TiO₂复合材料,通过扫描电子显微镜、能谱分析仪、X射线粉末衍射仪、X射线光电子能谱仪、振动样品磁强计、紫外可见分光光度计对样品进行表征及测试。结果表明： ZnFe₂O₄/Ag/TiO₂-10具有最佳的光催化效果,在紫外和可见光下对染料的降解率都能达到90%以上,具有优异的紫外可见光光催化活性。ZnFe₂O₄/Ag/TiO₂具有独特的磁性,能在外部磁场作用下进行回收利用,这使其在实际应用中成为可能。通过磁分离技术重复回收利用5次后仍然保持优良的光催化性能,说明ZnFe₂O₄/Ag/TiO₂-10具有优异的磁性及较高的光催化循环稳定性。     

TiO2/Cu2O/Pt复合空心微球的制备及其光催化性能

以锐钛矿相TiO₂溶胶为基底,采用沉淀法和液相沉积法制备了TiO₂/Cu₂O/Pt复合空心微球,通过改变n_Ti⁴⁺∶ n_Cu²⁺和H₂PtCl₆·6 H₂O溶液的加入量对TiO₂的形貌和结构进行调控,采用不同的方法对不同样品的物相及结构、微观形貌和光学性能进行了对比分析。分析结果表明,复合材料中Pt与Cu₂O的引入产生协同效应,不仅在一定程度上阻止了电子-空穴的复合,还降低了禁带宽度,在可见光区域光吸收明显增强。与TiO₂、Cu₂O和TiO₂/Cu₂O光催化剂相比较,TiO₂/Cu₂O/Pt降解有机污染物的能力显著增强,首次光照120 min可降解93%的甲基橙(MO)溶液,4次循环后降解率为71%,具有良好的光催化稳定性能。     

TiO2/CuS异质结的制备及光催化降解染料废水的研究

以原位沉淀法和水热法混合的合成手段,制备了TiO_2/CuS异质结光催化剂。这种异质结改善了单一TiO_2半导体光催化剂的缺陷,明显提高了太阳光下光催化降解甲基橙的效率。TiO_2与CuS之间形成的异质结结构和合适的能带结构能够扩展材料对太阳光谱的响应范围并且很好地收集和传输光诱导载流子,从而提高了载流子的分离效率,最终使半导体的光催化活性明显增强。结果表明,太阳光照射25min后,相比于TiO_2/MnS、TiO_2/CdS和TiO_2/ZnS异质结,TiO_2/CuS异质结(TiO_2和CuS的摩尔比为3∶1)对甲基橙的降解效果最佳,降解效率能达到97.3%。为提高半导体的光催化活性提供了一条可行的路径。     

冷等离子体强化制备TiO2光催化材料及其机理

等离子体技术在材料制备和改性方面的优势得到众多研究者的认可。Ti O2具有化学稳定性高、氧化活性强、生产成本低等优势,被广泛应用于太阳能电池和光催化领域。本文综述了近年来介质阻挡放电等离子体在强化制备Ti O2光催化材料方面的研究成果,包括等离子体辅助制备Ti O2光催化薄膜和Ti O2的等离子体法掺杂两个方面,并分析了其作用机理。从目前的研究成果来看,等离子体技术制得的Ti O2光催化材料具有更好的均匀性和催化活性,这主要得益于等离子体中的高能电子,一方面,Ti O2粒子吸附电子,彼此之间产生静电场的斥力作用,可以抑制颗粒的团聚,另一方面,电子的强还原能力,能够打断Ti-O键,形成氧空位,从而提高其催化性能。     

易分离回收的BiOBr/TiO2/PAN催化剂的制备及光催化降解盐酸四环素研究

为了用BiOBr提高TiO₂的光催化活性,人们做了大量的研究。然而,大多数工作合成的都是粉体结构,难以回收且易造成二次污染。本文通过静电纺丝技术结合溶剂热法制备了柔性的BiOBr/TiO₂/PAN 纳米纤维膜,因其独特的自支撑膜结构,使问题得到解决。通过 SEM、TEM、XPS 、XRD和BET等对其结构和形貌进行表征,使用 UV-Vis DRS、EIS和i-t对其光电性能进行分析。结果表明,与单独的TiO₂/PAN相比,在可见光照射下,BiOBr/TiO₂/PAN 纳米纤维膜对盐酸四环素(TCH)降解的光催化活性增强,在140min内降解效率达到72.97%;5次循环实验中,催化剂的催化性能趋于稳定,循环后的XRD和SEM表明催化剂形貌和晶体结构没有发生改变,表现出优异的耐久性。     

Fe_2O_3/TiO_2纳米管阵列的制备及其光催化性能

在钛基体上采用阳极氧化法制备了TiO2纳米管阵列,采用化学浴方法在TiO2纳米管阵列上修饰了Fe2O3纳米颗粒。利用扫描电镜、X射线衍射和紫外可见漫反射光谱等手段对材料进行了表征,同时测试了材料的光电化学性能及其光催化降解亚甲基蓝染料废水的性能。结果表明,Fe2O3纳米颗粒的修饰将TiO2纳米管阵列的光响应拓宽至可见光区域,提高了光电流,Fe2O3/TiO2纳米管阵列的光电流是未修饰的TiO2纳米管阵列的9倍。而在光催化反应中,亚甲基蓝最高降解率可达80%,比未修饰的TiO2纳米管阵列高出30%。     

Solid-phase photocatalytic degradation of polystyrene plastic with TiO2 as photocatalyst

Solid-phase photocatalytic degradation of polystyrene (PS) plastic with TiO₂ as photocatalyst was investigated in the ambient air under ultraviolet light irradiation. Higher weight loss rate, lower average molecular weight, increased carbonyl peak intensity, less volatile organics and more CO₂ emitted with irradiation in PS-TiO₂ composite sample compared to pure PS sample were observed. These facts indicated the higher photodegradation rate of PS-TiO₂ sample than that of PS sample, and emphasized the potential of the composite sample in bring about complete photodegradation of polystyrene plastic. It is implied that the degradation initially occurred over TiO₂ particles, followed by the diffusion reaction with the aid of reactive oxygen species generated on TiO₂ particle surface.     

Fe2O3/TiO2纳米管阵列的制备及其光催化性能

在钛基体上采用阳极氧化法制备了TiO₂纳米管阵列,采用化学浴方法在TiO₂纳米管阵列上修饰了Fe₂O₃纳米颗粒.利用扫描电镜、X射线衍射和紫外可见漫反射光谱等手段对材料进行了表征,同时测试了材料的光电化学性能及其光催化降解亚甲基蓝染料废水的性能.结果表明,Fe₂O₃纳米颗粒的修饰将TiO₂纳米管阵列的光响应拓宽至可见光区域,提高了光电流,Fe₂O₃/TiO₂纳米管阵列的光电流是未修饰的TiO₂纳米管阵列的9倍.而在光催化反应中,亚甲基蓝最高降解率可达80%,比未修饰的TiO₂纳米管阵列高出30%.     

TiO2/BiNbO4复合光催化剂的制备及降解气相苯性能

采用固相反应法制备出BiNbO4,将其与TiO2耦合,得到TiO2/BiNbO4复合光催化剂。考察了催化剂在紫外光照射下催化降解气相苯的活性。结果表明,TiO2与BiNbO4耦合后催化活性明显提高,其中36%TiO2/BiNbO4紫外光照5 h对苯的降解率是P-25的3.7倍。紫外-可见漫反射谱(UV-Vis DRS)、XRD、XPS和低温氮吸附-脱附等表征结果表明TiO2与BiNbO4的能级匹配,二者之间存在能带协同效应。耦合后的TiO2/BiNbO4的光生电子和空穴能有效分离,从而提高了催化剂催化活性。     

Synthesis of nanosized TiO2/SiO2 particles using microwave processes and their photocatalytic activity on the decomposition of orange II

The nanosized titania and TiO₂/SiO₂ particles were prepared by the microwave-hydrothermal method. The effect of physical properties TTIP/TEOS ratio and calcination temperature has been investigated. The major phase of the pure TiO₂ particle is of the anatase structure, and a rutile peak was observed above 800°C. In TiO₂/SiO₂ particles, however, no significant rutile phase was observed, although the calcination temperature was 900°C. No peaks for the silica crystal phase were observed at either silica/titania ratio. The crystallite size of TiO₂/SiO₂ particles decreases as compared to pure TiO₂ at high calcination temperatures. The TiO₂/SiO₂ particles show higher activity on the photocatalytic decomposition of orange II as compared to pure TiO₂ particles.     

High photocatalytic degradation activity of polyethylene containing polyacrylamide grafted TiO2

A novel photocatalytic polyacrylamide grafted TiO₂ (PAM-g-TiO₂) nanocomposite was prepared and embedded into a low density polyethylene (LDPE) plastic. Photocatalytic degradation of the LDPE/PAM-g-TiO₂ composite film was carried out under ambient conditions under ultraviolet light irradiation. The properties of composite film were compared with those of the pure LDPE film by measuring the changes in weight loss, carbonyl index, molecular weight, tensile strength and elongation at break. PAM-g-TiO₂ embedded LDPE showed highly enhanced photocatalytic degradation. Irradiating the LDPE/PAM-g-TiO₂ composite film for 520 h under UV light reduced its weight by 39.85% and average molecular weight (M_w) by 94.60%, while that of pure LDPE film was only 1.03% and 69.59%, respectively. The addition of PAM-g-TiO₂ brought about the good dispersion of TiO₂ in LDPE matrix and improved the hydrophilicity of composite film, which were able to facilitate the degradation of LDPE. The photocatalytic degradation mechanism of the films is briefly discussed.     

大尺寸TiO2/SiO2大孔材料的制备及光降解性能

先以三维骨架聚合物为整体型模板,利用硅酸酯原位溶胶-凝胶过程并结合高温烧结的方法制备出大尺寸大孔径的SiO2载体,然后通过钛酸丁酯溶液浸渍、原位水解、煅烧制备出大尺寸的TiO2/SiO2大孔材料并用SEM、TEM、FTIR、XRD和XPS对其表征,结果表明SiO2载体具有三维连续的超薄层,TiO2以纳米薄层方式均匀地沉积在SiO2的三维超薄层上,形成TiO2/SiO2/TiO2三层夹心结构,层与层界面存在Si-O-Ti键,同时复合结构提高了TiO2由锐钛矿相向金红石相的转变温度.以甲基橙为目标降解物考察不同条件下制备的复合材料的光催化活性,采用复合材料吸入甲基橙溶液的方式,并借助甲醇萃取手段研究光降解动力学过程.结果表明,该复合材料具有较好的光降解催化活性,当焙烧温度为600℃和TiO2的负载量为54.5wt%时,其活性最大且降解速率常数达到1.78 h-1.     

钛铁矿制备二氧化钛-四氧化三铁复合材料及其光催化应用

TiO_2因具有多种优异的特性被广泛应用在半导体光催化领域,但是纳米结构的TiO_2颗粒细微,在进行光催化反应之后,难以回收再利用。本文以廉价钛铁矿为原料制备光催化剂TiO_2,同时利用副产物铁合成Fe_3O_4,并采用简单温和的浸渍法制备Fe_3O_4/TiO_2磁性复合材料。通过XRD、FT-IR、SEM、EDS等手段对材料形态结构进行表征分析,并以光降解有机污染物若丹明B为探针反应,考察其光催化性能。结果表明,质量比为1∶10的Fe_3O_4/TiO_2复合材料结构稳定、分散均匀,具有最优的光催化活性(波长356nm下反应3h,若丹明B降解率达到64.0%),并表现出良好的重复性。同时,动力学结果显示降解符合一级反应动力学。     

Ag/质子化g-C3N4纳米棒材料的制备及其光催化降解性能

制备了 Ag 负载于质子化 g-C₃N₄(pCN)的纳米棒材料(Ag/pCN),对比了 g-C₃N₄(CN)、表面负载 Ag 的 CN(Ag/CN)、pCN 和 Ag/pCN在可见光条件下光催化降解亚甲蓝(MB)溶液的效果。结果表明,Ag/pCN光催化效率最高(92.63%),并且具有良好的稳定性;通过光电流-时间(I-t)曲线、Nyquist曲线、Mott-Schokkty曲线和捕获实验探究了Ag/pCN光催化降解MB的机理：虽然pCN的π共轭体系较CN发生变化,但由于形成了纳米棒,其比表面积的增加以及Ag负载的协同效应致使Ag/pCN具有优异的光催化性能。光催化过程中羟基自由基(·OH)是起主要作用的活性物质,其由光生电子(e^-)与表面吸附的 O₂反应产生以及光生空穴(h⁺)与H₂O或OH^-反应产生。     

Structural characterization and photocatalytic activity of hollow binary ZrO2/TiO2 oxide fibers

The formation of hollow binary ZrO₂/TiO₂ oxide fibers using mixed precursor solutions was achieved by activated carbon fibers templating technique combined with solvothermal process. The samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), N₂ adsorption, X-ray photoelectron spectroscopy (XPS), UV-vis, and infrared (IR) spectroscopy. The binary oxide system shows the anatase-type TiO₂ and tetragonal phase of ZrO₂, and the introduction of ZrO₂ notably inhibits the growth of TiO₂ nanocrystallites. Although calcined at 575 °C, all hollow ZrO₂/TiO₂ fibers exhibit higher surface areas (>113 m²/g) than pure TiO₂ hollow fibers. The Pyridine adsorption on ZrO₂/TiO₂ sample indicates the presence of stronger surface acid sites. Such properties bring about that the binary oxide system possesses higher efficiency and durable activity stability for photodegradation of gaseous ethylene and trichloromethane than P25 TiO₂. In addition, the macroscopic felt form for the resulting materials is more beneficial for practical applications than traditional catalysts forms.     

双介孔结构的纳米TiO2/I2复合材料的制备及其可见光催化性能

以钛酸丁酯为前驱体, 碘溶胶为碘源, 在室温下采用水解沉淀法制备了单质碘和纳米TiO₂复合的双介孔结构光催化剂(M-I₂-TiO₂). 采用X射线衍射(XRD)、透射电子显微镜(TEM)、比表面分析(BET)、紫外-可见(UV-Vis)漫反射光谱和傅里叶变换-红外光谱(FT-IR)对M-I₂-TiO₂进行了表征. 以次甲基蓝(MB)溶液为模拟废水, 对M-I₂-TiO₂的光催化性能进行了评价, 研究了不同热处理温度对光催化活性的影响. 结果表明, M-I₂-TiO₂在可见光区有显著的吸收, 300 ℃热处理得到的样品比表面积高达227.6 m²/g, 600 ℃热处理所得样品的比表面积仍高达111.8 m²/g, 而400 ℃热处理所得样品具有最好的光催化降解性能. 双介孔结构纳米TiO₂/I₂复合材料的光催化降解性能显著高于相同方法制备的纯TiO₂和Degussa P-25商业产品. 催化剂经6次重复使用其光催化活性基本保持不变.     

Bi2Ti2O7/TiO2/Bi4Ti3O12多异质结的构筑及其增强的可见光催化性能

以静电纺丝技术制备的TiO₂纳米纤维为基质,硝酸铋为铋源,KOH为矿化剂,成功制备了多异质结Bi₂Ti₂O₇/TiO₂/Bi₄Ti₃O₁₂复合纳米纤维光催化剂。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、紫外可见漫反射光谱(UV-Vis DRS)等一系列表征,对其物相组成、微观形貌和光学性质等进行分析。结果表明：TiO₂纳米纤维的介入,将Ⅰ型异质结Bi₂Ti₂O₇/Bi₄Ti₃O₁₂分离为2个Ⅱ型异质结Bi₂Ti₂O₇/TiO₂和Bi₄Ti₃O₁₂/TiO₂。Bi₂