Optimisation of the effect of colemanite as a new synergistic agent in an intumescent system

An intumescent system including ammonium polyphosphate (APP) as an acid source and blowing agent, pentaerythritol (PER) as a carbonific agent and colemanite as a synergistic agent is used to enhance flame retardancy of polypropylene (FR-PP). In order to investigate the synergism between colemanite and the flame retardant materials (APP and PER), D-optimal mixture design was employed. The limiting oxygen index (LOI) and amount of residue (AoR) were accepted as response 1 and response 2, respectively. Applying D-optimal strategy, 18 experiments were performed. Filler content was fixed at 30 wt% of total amounts of flame retardant PP composites. Constraints were determined according to the ratio of APP/PER ranging between 1 and 3. Statistical analysis of the cubic model revealed that lack of fit (LoF) was not significant for the cubic and linear model for both responses. The model suggested an optimum composite formulation with concentration levels 65% of APP, 28% of PER and 7% of colemanite that gives an LOI of 40.3. The experimental LOI and AoR of optimum formulation were achieved as 39.3 and 21.4 with 2.5% and 2.2% errors, respectively.     

Effect of a novel charring-foaming agent on flame retardancy and thermal degradation of intumescent flame retardant polypropylene

A new triazine polymer was synthesized by using cyanuric chloride, ethanolamine and ethylenediamine as raw materials. It is used both as a charring agent and as a foaming agent in intumescent flame retardants, designated as charring-foaming agent (CFA). Effect of CFA on flame retardancy, thermal degradation and mechanical properties of intumescent flame retardant polypropylene (PP) system (IFR-PP system) has been investigated. The results demonstrated that the intumescent flame retardant (IFR) consisting of CFA, APP and Zeolite 4A is very effective in flame retardancy of PP. It was found that when the weight ratio of CFA to APP is 1:2, that is, the components of the IFR are 64 wt% APP, 32 wt% CFA and 4 wt% Zeolite 4A, the IFR presents the most effective flame retardancy in PP systems. LOI value of IFR-PP reaches 37.0, when the IFR loading is 25 wt% in PP. It was also found that when the IFR loading is only 18 wt% in PP, the flame retardancy of IFR-PP can still pass V-0 rating, and its LOI value reaches 30.2. TGA data obtained in pure nitrogen demonstrated that CFA has a good ability of char formation itself, and CFA shows a high initial temperature of the thermal degradation. The char residue of CFA can reach 35.7 wt% at 700 °C. APP could effectively promote the char formation of the APP-CFA system. The char residue reaches 39.7 wt% at 700 °C, while it is 19.5% based on calculation. The IFR can change the thermal degradation behaviour of PP, enhance T_max of the decomposition peak of PP, and promote PP to form char, based upon the results of the calculation and the experiment. This is attributed to the fact that endothermic reactions took place in IFR charring process and the char layer formed by IFR prevented heat from transferring into inside of IFR-PP system. TGA results further explained the effective flame retardancy of the IFR containing CFA.     

Synergistic effects of cerium phosphate and intumescent flame retardant on EPDM/PP composites

An intumescent flame retardant system composed of ammonium polyphosphate (APP) and pentaerythritol (PER) was used for flame retarding ethylene–propylene–diene‐modified elastomer (EPDM)/polypropylene (PP) blends. Cerium phosphate (CeP) was synthesized and the effect on flame retardancy and thermal stability of EPDM/PP composites based on intumescent flame retardant (IFR) were studied by limiting oxygen index (LOI), UL‐94, and thermogravimetic analysis (TGA), respectively. Scanning electron microscopy (SEM) and Fourier transform infrared spectrometry (FTIR) were used to analyze the morphological structure and the component of the residue chars formed from the EPDM/PP composites, and the mechanical properties of the materials were also studied. The addition of CeP to the EPDM/PP/APP/PER composites gives better flame retardancy than that of EPDM/PP/APP/PER composites. TGA and RT‐FTIR studies indicated that an interaction occurs among APP, PER, and EPDM/PP. The incorporation of CeP improved the mechanical properties of the materials. Copyright © 2010 John Wiley & Sons, Ltd.     

Synergistic effect of boron containing substances on flame retardancy and thermal stability of clay containing intumescent polypropylene nanoclay composites

The functions of nanoclay and three different boron containing substances, zinc borate (ZnB), borophosphate (BPO₄), and boron silicon containing preceramic oligomer (BSi), were studied to improve the flame retardancy of polypropylene (PP)‐nanoclay‐intumescent system composed of ammonium polyphosphate (APP) and pentaerythritol (PER). The flame retardancy of PP composites was investigated using limiting oxygen index (LOI), UL‐94 standard, thermogravimetric analysis (TGA), and cone calorimeter. According to the results obtained, the addition of 20 wt% intumescent flame retardant (IFR) improved the flame retardancy by increasing the char formation. Addition of clay slightly increases the LOI value and reduces the maximum heat release rate (HRR). Addition of clay also increases the barrier effect due to intumescent char, especially in thin samples. Boron compounds show their highest synergistic effect at about 3 wt% loading. According to UL‐94 test and LOI test, 3 wt% ZnB containing composite shows the highest rating (V0) and BPO₄ containing sample shows the highest LOI value (26.5). Copyright © 2010 John Wiley & Sons, Ltd.     

Synergistic improvement of fire retardancy and mechanical properties of ferrocene‐based polymer in intumescent polypropylene composite

The ferrocene‐based polymer (PDPFDE) accompanied with traditional intumescent flame retardant (IFR) system (ammonium polyphosphate (APP)/pentaerythritol (PER) = 3/1, mass ratio) has been used as additive flame retardant in polypropylene (PP), aiming to lower the total loading amount. The thermal stability and fire retardant properties were investigated by thermogravimetric analysis (TGA), limiting oxygen index (LOI), vertical combustion (UL‐94), and cone calorimetry (CONE). The fire retardant mechanism was studied by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and Raman spectroscopy. The results showed that the PP1 with 25 wt% IFR only passed the UL‐94 V‐1 rating, but the PP6 loaded by 0.5 wt% PDPFDE and 22.5 wt% IFR possessed an LOI value of 28.5% and passed the UL‐94 V‐0 rating; the peak heat release rate (pHRR) and total heat release (THR) are decreased by 63% and 43%, respectively, compared with pure PP. In addition, the char residue of PP6 manifested a very compact and smooth surface, indicating a more effective barrier layer. Meanwhile, it was interesting that the addition of PDPFDE evidently improved the impact strength and elongation at break of PP/IFR composites.     

The influence of KH-550 on properties of ammonium polyphosphate and polypropylene flame retardant composites

Ammonium polyphosphate (APP)/polypropylene (PP) composites were prepared by melt blending and extrusion in a twin-screw extruder. APP was first modified by a silane coupling agent KH-550 then added to polypropylene. The surface modification of APP by the coupling agent decreased its water solubility and its interface compatibility with the PP matrix. Limiting oxygen index (LOI) and thermogravimetric analysis (TGA) were used to characterize the flame retardant property and the thermal stability of the composites. The addition of APP improved the flame retardancy of PP remarkably. The crystal structures of APP/PP composites were characterized by X-ray diffraction (XRD). The results indicated that β-crystal phase PP may be formed. The structures and morphologies of APP, KH-550/APP and APP/PP composites were characterized by field-emission scanning electron microscope (FESEM). The mechanical property tests showed good mechanical properties of composite materials. Compared with unmodified one, the impact strength, tensile strength and elongation of modified APP/PP were all improved.     

Microencapsulation of ammonium polyphosphate with hydroxyl silicone oil and its flame retardance in thermoplastic polyurethane

Microencapsulated ammonium polyphosphate (MAPP) is prepared using hydroxyl silicone oil by in situ polymerization and characterized by XPS. Microencapsulation gives MAPP better water resistance and flame retardance compared with APP in thermoplastic polyurethane (TPU). Thermal stability and fire resistance behavior have been analyzed and compared. The LOI value of the TPU/MAPP composite is higher than that of the TPU/APP composite. The UL 94 rating of the TPU/MAPP composite is V-0 at the 20 wt% additive level, whereas TPU/APP gives V-2 rating at the same loading level. The water resistant properties of the TPU composites are studied. Results of the cone calorimeter and microscale combustion calorimeter experiment show that MAPP is an effective flame retardant in TPU compared with APP.     

Synergistic effect of boron containing substances on flame retardancy and thermal stability of intumescent polypropylene composites

The synergistic effect of four different boron containing substances, zinc borate (ZnB), borophosphate (BPO₄), boron silicon containing preceramic oligomer (BSi) and lanthanum borate (LaB), were studied to improve the flame retardancy of a polypropylene (PP) intumescent system composed of ammonium polyphosphate (APP) and pentaerythritol (PER). The flame retardancy of PP composites was investigated by limiting oxygen index (LOI), UL-94 standard, thermogravimetric analysis (TGA) and cone calorimeter tests. The addition of 20 wt% intumescent flame retardant (IFR) improves the flame retardancy by increasing the char formation. According to LOI and UL-94 test, boron compounds show their highest synergistic effect at 1 wt% loading. BPO₄ containing composite shows the highest LOI (30), lowest maximum heat release rate (HRR) and lowest total heat release rate (THR) value. Although the char yield increases as the amount of boron compounds increases, the flame retarding effect decreases. Cone calorimeter and TGA data indicate that the boron compounds are likely to show their synergistic effect by reinforcing the integrity of char which improves its barrier effect rather than increasing the char yield.     

Simultaneous improvement in the flame retardancy and water resistance of PP/APP through coating UV-curable pentaerythritol triacrylate onto APP

To improve the flame-retardant efficiency and water resistance of ammonium polyphosphate(APP), the UV-curable pentaerythritol triacrylate(PETA) was used to microencapsulate APP via the UV curing polymerization method. The prepared PETA-microencapsulated APP(PETA-APP) was characterized by Fourier transform infrared spectroscopy(FTIR), scanning electron microscopy(SEM), and thermogravimetric(TG) analysis. PETA-APP was used as intumescent flame retardant(IFR) alone to flame retard polypropylene(PP). The water resistance of PP/PETA-APP composites was investigated, and the effect of PETA on the combustion behaviors of PP/APP composites was studied through limiting oxygen index(LOI), vertical burning test(UL-94) and cone calorimeter(CC) test, respectively. With 40 wt% of PETA-APP, the PP/PETA-APP system could achieve a LOI value of 30.0% and UL-94 V-0 rating after treatment in hot water for 168 h, while the LOI value of the system containing 40 wt% uncoated APP was only 19.2%, and it failed to pass the UL-94 rating. CC test results showed that the heat release rate(HRR), mass loss rate(MLR) and smoke production rate(SPR) of PP/PETAAPP system decreased significantly compared with PP/APP system, especially the peak of HRR was decreased by 51.4%. The mechanism for the improvement of flame reatardancy for PP/PETA-APP composites was discussed based on FTIR and X-ray photoelectron spectroscopy(XPS) tests. All these results illustrated that simultaneous improvement of flame retardancy and water resistance for PP/APP was achieved through coating UV-curable PETA onto APP.     

The investigation of intumescent flame-retarded polypropylene using poly(hexamethylene terephthalamide) as carbonization agent

A novel intumescent flame retardant, containing ammonium polyphosphate (APP), and poly(hexamethylene terephthalamide) (PA6T), was prepared for flame retarding polypropylene (PP). The flame retardation of the PP composites was characterized by limiting oxygen index (LOI). The thermal degradation of the composites was investigated by means of thermogravimetric analysis (TG) and TG coupled with Fourier transform infrared spectroscopy (TG-FTIR). The morphology of the char obtained after combustion of the composites was studied by scanning electron microscopy. It has been found the intumescent flame retardant showed good flame retardancy, with the LOI value of the PA6T/APP/PP (5/25/70) system increasing from 17.5 to 32. Meanwhile, the TG and TG-FTIR work indicated that PA6T could be effective as a carbonization agent and there was a synergistic reaction between PA6T and APP, which effectively promoted the char formation of the PP composites. Moreover, it was revealed that uniform and compact intumescent char layer was formed after combustion of the intumescent flame retarded PP composites.     

Synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate on the thermal and flame retardant properties of polypropylene

The synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate (MAPP) on the thermal and flame retardancy of polypropylene (PP) are investigated by limiting oxygen index (LOI), UL‐94 test, cone calorimetry, thermogravimetric analysis (TGA), scanning electron micrograph (SEM), and water resistance test. The results of cone calorimetry show that heat release rate peak (PHRR), total heat release (THR), and the mass loss of PP with 30 wt% intumescent flame retardant (IFR, CFA/MAPP = 1:2) decreases remarkably compared with that of pure PP. The HRR, THR, and mass loss decrease, respectively from 1140 to 100 kW/m², from 96 to 16.8 MJ/m², and from 100 to 40%. The PP composite with CFA/MAPP = 1:2 has the best water resistance, and it can still obtain a UL‐94 V‐0 rating after 168 hr soaking in water. Copyright © 2008 John Wiley & Sons, Ltd.     

Synthesis of a novel ionic liquid containing phosphorus and its application in intumescent flame retardant polypropylene system

A novel ionic liquid containing phosphorus ([PCMIM]Cl) was synthesized and characterized by FTIR, ¹H NMR, ¹³C NMR and ³¹P NMR. Moreover, a new intumescent flame retardant (IFR) system, which was composed of [PCMIM]Cl and ammonium polyphosphate (APP), was used to impart flame retardancy and dripping resistance to polypropylene (PP). The flammability and thermal behaviors of intumescent flame‐retarded PP (PP/IFR) composites were evaluated by limiting oxygen index (LOI), UL‐94 test, thermogravimetric analysis (TGA) and cone calorimeter test. It was found that there was an obvious synergistic effect between [PCMIM]Cl and APP. When the weight ratio of [PCMIM]Cl and APP was 1:5 and the total amount of IFR was kept at 30 wt%, LOI value of PP/IFR composite reached 31.8, and V‐0 rating was obtained. Moreover, both the peak heat release rate and the peak mass loss rate of PP/IFR composites decreased significantly relative to PP and PP/APP composite from cone calorimeter analysis. The TGA curves suggested that [PCMIM]Cl had good ability of char formation, and when combined with APP, it could greatly promote the char formation of PP/IFR composites, hence improved the flame retardancy. Additionally, the rheological behaviors and mechanical properties of PP/IFR composites were also investigated, and it was found that [PCMIM]Cl could also serve as an efficient lubricant and compatibilizer between APP and PP, endowing the materials with satisfying processability and mechanical properties. Copyright © 2013 John Wiley & Sons, Ltd.     

Preparation and Characterization of Core/Shell-like Intumescent Flame Retardant and its Application in Polypropylene

With a shell of starch-melamine-formaldehyde (SMF) resin, core/shell-like ammonium polyphosphate (SMFAPP) is prepared by in situ polymerization, and is characterized by SEM, FTIR and XPS. The shell leads SMFAPP a high water resistance and flame retardance compared with APP in polypropylene (PP). The flame retardant action of SMFAPP and APP in PP are studied using LOI, UL 94 test and cone calorimeter, and their thermal stability is evaluated by TG. The flame retardancy and water resistance of the PP/SMFAPP composite at the same loading is better than that of the PP/APP composite. UL 94 ratings of PP/SMFAPP can reach V-0 at 30 wt% loading. The flame retardant mechanism of SMFAPP was studied by dynamic FTIR, TG and cone calorimeter, etc.     

The synergistic flame‐retardant effect of O‐MMT on the intumescent flame‐retardant PP/CA/APP systems

The flame retardancy of a novel intumescent flame‐retardant polypropylene (IFR‐PP) system, which was composed of a charring agent (CA), ammonium polyphosphate (APP), and polypropylene (PP), could be enhanced significantly by adding a small amount (1.0 wt%) of an organic montmorillonite (O‐MMT). The synergistic flame‐retardant effect was studied systematically. The thermal stability and combustion behavior of the flame‐retarded PP were also investigated by thermogravimetric analysis (TGA), limiting oxygen index (LOI), vertical burning test (UL‐94), scanning electronic microscopy (SEM), and cone calorimeter test (CCT). TGA results demonstrated that the onset decomposition temperatures of IFR‐PP samples, with or without O‐MMT, were higher than that of neat PP. Compared with IFR‐PP, the LOI value of IFR‐PP containing 1.0 wt% O‐MMT was increased from 30.8 to 33.0, and the UL‐94 rating was also enhanced to V‐0 from V‐1 when the total loading of flame retardant was the same. The cone calorimeter results showed that the IFR‐PP with 1.0 wt% of O‐MMT had the lowest heat release rate (HRR), total heat release (THR), total smoke production (TSP), CO production (COP), CO₂ production (CO₂P), and mass loss (ML) of all the studied IFR‐PP samples, with or without O‐MMT. All these results indicated that O‐MMT had a significantly synergistic effect on the flame‐retardancy of IFR‐PP at a low content of O‐MMT. Copyright © 2009 John Wiley & Sons, Ltd.     

Effect of Organo‐Modified Nanosepiolite on Fire Behaviors and Mechanical Performance of Polypropylene Composites

The objective of the study was to investigate the effect of the organo‐modified nanosepiolite (ONSep) on improving the fire safety of polypropylene (PP). The composites based on PP, flame retardant master batch (MB‐FR, 25 wt% PP+50 wt% decabromodiphenyl ether (DBDPE)+25% antimony trioxide (ATO)) and ONSep were prepared via melt blending. The results of the limiting oxygen index (LOI) and vertical burning rating (UL‐94) test indicated that PP/40 wt% MB composites had no rating with seriously dripping phenomenon, while the LOI value was only 22.5. However, as 4 wt% ONSep was added in PP/40 wt% MB composites, the composites achieved UL94 V‐0 rating and the LOI value was 24.3. In comparison, PP/50 wt% MB composites could not reach the V‐0 rating either. The TGA results revealed that the addition of ONSep enhanced the thermal stability of the PP/MB‐FR composites. The cone calorimeter results indicated that the heat release rate, average mass loss rate, smoke production rate and smoke temperature of the PP/40 wt% MB‐FR/4 wt% ONSep composites decreased in comparison with those of PP/40 wt% MB‐FR composites. Simultaneously, the Young modulus and impact strength were also much better improved with the increase of ONSep loading. Therefore, the synergistic flame retardancy of ONSep in PP/MB‐FR matrix significantly containing a halogen based flame retardant (DBDPE) significantly improved the fire safety and mechanical properties of the composites, and allowed to decrease the total amount of brominated fire retardants.     

Great enhancement of efficiency of intumescent flame retardants by titanate coupling agent and polysiloxane

Modified intumescent flame retardants (MIFRs) and polysiloxane (APID) have been used in combination to enhance the flame retardancy of polypropylene (PP). The IFR system was composed of melamine (MEL), ammonium polyphosphate (APP) and pentaerythritol (PER). Aimed to improve the thermal stability of the IFR and its dispersivity in PP, titanate coupling agent NDZ‐201 was used to modify the IFRs via ball milling. MIFRs and APID have a cooperative effect on the flame retardant properties of PP. With 25 wt.% of MIFR and APID, the flame retardant sample (PPMA) was rated V0 for UL‐94, the LOI value was 34.3%, and the peak heat release rate (PHRR) was reduced by 80% in cone calorimeter test. In addition, APID could improve the compatibility of MIFR with the PP matrix, thereby increasing the mechanical properties of PP blends. The flame retardant effect of APID and MIFR in PP was presented in the condensed phase resulting in a rigid, thermally stable and expanded carbon layer due to different char structures.     

Synthesis and application in polypropylene of a novel of phosphorus-containing intumescent flame retardant

A novel phosphorus-containing triazine oligomer poly(2-morpholinyl-4-penta-erythritol phosphate-1,3,5-triazine) (PMPT) was synthesized as a kind of tri-component intumescent flame retardant (IFR). The chemical structure of PMPT was characterized by FTIR, 1H-NMR and 31P-NMR, and the mechanical and flammability properties of FR-PP were measured. The FTIR results showed that the expected chemical reactions had happened at each step. The 1H-NMR and 31P-NMR spectra also agreed with the chemical structure of PMPT. The slight effect of PMPT on the mechanical properties of FR-PP suggested that PMPT and PP are compatible. The high limited oxygen index (LOI) values of FR-PP revealed that PMPT was an efficient IFR and there was the synergistic effect between PMPT and ammonium polyphosphate/ pentaerythritol (APP/PER).     

Thermal and Mechanical Properties of Zeolite Filled Ethylene Vinyl Acetate Composites

Ethylene vinyl acetate (EVA) composites filled with zeolite (25 vol.%) were prepared using an internal mixer followed by compression molding machine. In order to enhance the thermal properties and fire retardancy of the composites, an intumescent flame retardant consisting of ammonium polyphosphate (APP)/pentaerythritol (PER) was incorporated into the composites. Two kinds of flame retardants were used which are untreated APP (APP1) and silane treated APP (APP2), where their effectiveness was evaluated by means of differential scanning calorimetry (DSC) and also thermogravimetric analysis (TGA). The results showed that both types of flame retardants have the ability to enhance the thermal stability of EVA/zeolite composites by producing charred layer which protects the underlying composites from the action of flame. Moreover, the incorporation of APP1 and APP2 has a significant effect on the composites degree of crystallinity. Meanwhile the results of tensile testing showed that the composites with APP2/PER exhibit better tensile properties compared to that with APP1/PER. This is expected since the application of silane-treated APP (APP2) could improve the dispersion of APP particles within EVA matrix.     

Effect of anion of polyoxometalate based organic–inorganic hybrid material on intumescent flame retardant polypropylene

In this work, 12‐tungestocobaltic acid based organic–inorganic hybrid material, [Bmim]₆CoW₁₂O₄₀ (CoW) was synthesized and applied as a synergist in polypropylene (PP)/intumescent flame retardant (IFR) composites. The flame retardant properties were investigated by the limiting oxygen index (LOI), UL‐94 vertical burning test, thermal gravimetric analyzer (TGA), cone calorimeter and scanning electron microscopy (SEM) etc. The results showed that the PP composites with 16 wt% IFR and 1 wt% CoW achieves the UL‐94 V‐0 rating and gets a LOI value 28.0. However, only add no less than 25 wt% single IFR, can the PP composites obtain the UL‐94 V‐0 rating, which suggests that CoW has good synergistic effects on flame retardancy of PP/IFR composites. In addition, the SEM and cone calorimeter tests indicated the CoW improves the quality of char layer. The rate of char formation has been enhanced also because of the existence of CoW. It is the combination of a better char quality and a high rate of char formation promoted by CoW that results in the excellent flame retardancy of PP/IFR composites. Copyright © 2016 John Wiley & Sons, Ltd.     

Synergistic effects of aluminum hypophosphite on intumescent flame retardant polypropylene system

The effects of aluminum hypophosphite(AHP) as a synergistic agent on the flame retardancy and thermal degradation behavior of intumescent flame retardant polypropylene composites(PP/IFR) containing ammonium polyphosphate(APP) and triazine charring-foaming agent(CFA) were investigated by limiting oxygen index(LOI), UL-94 measurement, thermogravimetric analysis(TGA), cone calorimeter test(CONE), scanning electron microscopy(SEM) and X-ray photoelectron spectroscopy(XPS). It was found that the combination of IFR with AHP exhibited an evident synergistic effect and enhanced the flame retardant efficiency for PP matrix. The specimens with the thickness of 0.8 mm can pass UL-94 V-0 rating and the LOI value reaches 33.5% based on the total loading of flame retardant of 24 wt%, and the optimum mass fraction of AHP/IFR is 1:6. The TGA data revealed that AHP could change the degradation behavior of IFR and PP/IFR system, enhance the thermal stability of the IFR and PP/IFR systems at high temperatures and promote the char residue formation. The CONE results revealed that IFR/AHP blends can efficiently reduce the combustion parameters of PP, such as heat release rate(HRR), total heat release(THR), smoke production rate(SPR) and so on. The morphological structures of char residue demonstrated that AHP is of benefit to the formation of a more compact and homogeneous char layer on the materials surface during burning. The analysis of XPS indicates that AHP may promote the formation of sufficient char on the materials surface and improve the flame retardant properties.