Cu-In-O composite thin films deposited by reactive DC magnetron sputtering

Cu-In-O composite thin films were deposited by reactive DC magnetron sputtering at room temperature. The samples were characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), UV/vis spectrophotometer, four-probe measurement and Seebeck effect measurement, etc. The samples contain Cu, In and O. The ratios of Cu to In and O to In increase with increase in O₂ flow rates. The ratio of Cu to In is over 1 and this suggests that Cu is in excess. The obtained Cu-In-O thin films are very possibly made of rhombohedral In₂O₃ and monoclinic CuO. Transmittance of the films decreases with increase in O₂ flow rate. The decrease in transmittance results from increase in Cu content in the films. The optical band gap of all the samples is estimated to be 4.1-4.4 eV, which is larger than those of In₂O₃ and CuO. The sheet resistance of the films decreases with increase in O₂ flow rate. Conductivity of the films is a little low, due to the addition of Cu and the poor crystalline quality of the film. The conduction behavior of the films is similar to that of In₂O₃ and the conduction mechanism of Cu-In-O thin films is through O vacancy.     

Influence of sputter-etching of substrate on the microstructural and optical properties of ZnO films deposited by RF magnetron sputtering

ZnO films were prepared using radio frequency magnetron sputtering on Si(1 1 1) substrates that were sputter-etched for different times ranging from 10 to 30 min. As the sputter-etching time of the substrate increases, both the size of ZnO grains and the root-mean-square (RMS) roughness decrease while the thickness of the ZnO films shows no obvious change. Meanwhile, the crystallinity and c-axis orientation are improved by increasing the sputter-etching time of the substrate. The major peaks at 99 and 438 cm⁻¹ are observed in Raman spectra of all prepared films and are identified as E₂(low) and E₂(high) modes, respectively. The Raman peak at 583 cm⁻¹ appears only in the films whose substrates were sputter-etched for 20 min and is assigned to E₁(LO) mode. Typical ZnO infrared vibration peak located at 410 cm⁻¹ is found in all FTIR spectra and is attributed to E₁(TO) phonon mode. The shoulder at about 382 cm⁻¹ appearing in the films whose substrates were sputter-etched for shorter time (10-20 min) originates from A₁(TO) phonon mode. The results of photoluminescence (PL) spectra reveal that the optical band gap (Eg) of the ZnO films increases from 3.10 eV to 3.23 eV with the increase of the sputter-etching time of the substrate.     

Substrate temperature dependence of properties of ZnO thin films deposited by LP-MOCVD

ZnO films were prepared on (0002) sapphire by metal-organic chemical vapor deposition (MOCVD) with fixed Zn and O gas flow rates. The film properties displayed complex dependencies on temperature over the range 330–460 °C. All films were preferentially oriented along the (0002) direction and the integrated intensity of the (0002) peak increased with increasing substrate temperature, indicative of an increasing deposition rate. Furthermore, high substrate temperatures promoted the growth of columnar grains, and improved the crystallinity, as the decreasing FWHM of the (0002) ZnO peak suggests. However, it was not the highest temperature sample, but the sample deposited at 390 °C that had the best UV band emission characteristics, with no defect-related luminescence in the photoluminescence (PL) spectra, as well as the highest transmission and sharpest absorption edge in the transmittance spectra. PACS 81.15.Gh; 78.55.Et; 68.55.Jk; 61.10.Kw     

A study of the optical properties of titanium oxide films prepared by dc reactive magnetron sputtering

TiO₂ thin films were deposited on the glass substrates by dc reactive magnetron sputtering technique at different sputtering pressures (2 × 10⁻³ to 2 × 10⁻² mbar). The films prepared at low pressures have an anatase phase, and the films prepared at high pressures have an amorphous phase. The optical properties were studied by measuring the transmittance and the ellipsometric spectra. The optical constants of the films in the visible range were obtained by fitting the transmittance combined with the ellipsometry measurements using the classical model with one oscillator. The refractive index of the films decreases from 2.5 until 2.1 as the sputtering pressure increases from 2 × 10⁻³ to 2 × 10⁻² mbar. The films prepared at the pressure higher than 6 × 10⁻³ mbar show a volume inhomogeneity. This volume inhomogeneity has been calculated by fitting the transmittance and the ellipsometric spectra. The volume inhomogeneity of the film prepared at the highest sputtering pressure is about 10%. Although the films prepared at high pressures show a large volume inhomogeneity, they have low extinction coefficients. It is suggested that the anatase phase results in more light scattering than amorphous phase does, and then a high extinction coefficient.     

Effect of intrinsic stress on the optical properties of nanostructured ZnO thin films grown by rf magnetron sputtering

In this paper we report the effect of deposition temperature on the structural and optical properties of ZnO thin films prepared by rf magnetron sputtering. The films grown at lower deposition temperatures were in a state of large compressive stress, whereas the films grown at higher temperature (450 °C) were almost stress free. In the absorption spectra, the ZnO excitonic and the Zn surface plasmon resonance (SPR) peaks have been observed. A redshift in the optical band gap of ZnO films has also been observed with the increase in the deposition temperature. The shift in the band gap calculated from the size effect did not match with the observed shift values and the observed shift has been attributed to the compressive stress present in the films.     

Physical properties of ZnO thin films deposited by spray pyrolysis technique

Thin films of ZnO have been prepared on glass substrates at different thicknesses by spray pyrolysis technique using 0.2 M aqueous solution of zinc acetate. X-ray diffraction reveals that the films are polycrystalline in nature having hexagonal wurtzite type crystal structure. The resistivity at room temperature is of the order 10⁻² Ω cm and decreased as the temperature increased. Films are highly transparent in the visible region. The dependence of the refractive index, n, and extinction coefficient, k, on the wavelength for a sprayed film is also reported. Optical bandgap, E_g, has been reported for the films. A shift from E_g = 3.21 eV to 3.31 eV has been observed for deposited films.     

The influence of titanium on the properties of zinc oxide films deposited by radio frequency magnetron sputtering

TiO₂-doped zinc oxide thin films were deposited on glass substrates by radio frequency (RF) magnetron sputtering with TiO₂-doped ZnO targets in an argon atmosphere. The structural properties of TiO₂-doped ZnO films doped with different TiO₂ contents were investigated. The experimental results show that polycrystalline TiO₂-doped ZnO films had the (0 0 2) preferred orientation. The deposition parameters such as the working pressure and substrate temperature of TiO₂-doped ZnO films were also investigated. The crystalline structure of the TiO₂-doped ZnO films gradually improved as the working pressure was lowered and the substrate temperature was raised. The lowest electrical resistivity for the TiO₂-doped ZnO films was obtained when the Ti addition was 1.34 wt%; its value was 2.50 × 10⁻³ Ω cm, smaller than that found in previous studies. The transmittance of the TiO₂-doped ZnO films in the visible wavelength range was more than 80%. The optical energy gap was related to the carrier concentration, and was in the range of 3.30-3.48 eV.     

Comparison of the optical properties of undoped and Ga-doped ZnO thin films deposited using RF magnetron sputtering at room temperature

The optical properties of undoped zinc oxide (ZnO) thin films of various thicknesses were compared with those of Ga-doped (GZO) thin films. Transparent, high-quality undoped ZnO and GZO films were deposited successfully using radio-frequency (RF) sputtering at room temperature. The films were polycrystalline with a hexagonal structure and a strongly preferred orientation along the c-axis. The films had an average optical transmission >85% in the visible part of the electromagnetic spectrum. The undoped ZnO thin films were more transparent than the GZO thin films. In the photoluminescence (PL) spectrum, ZnO film has higher quality than GZO as a result of decrease in the green emission intensity.     

Structural and photoluminescent properties of ZnO films deposited by radio frequency reactive sputtering

Zinc oxide films with c-axis preferred orientation were deposited on silicon (100) substrates by radio frequency (RF) reactive sputtering. The properties of the sam- ples were characterized by X-ray diffractometer, X-ray photoelectron spectroscopy and fluorescent-spectrophotometer. The effect of sputtering power and substrate temperature on the structural and photoluminescent (PL) properties of the ZnO films was investigated. The results indicated that when the sputtering power is 100 W and the substrate temperature is 300-400℃, it is suitable for the growth of high c-axis orientation and small strain ZnO films. A violet peak at about 380 nm and a blue band at about 430 nm were observed in the room temperature photolumines- cence spectra, and the origin of blue emission was investigated.     

Indium zinc oxide thin films deposited by sputtering at room temperature

The deposition of amorphous indium zinc oxide (IZO) thin films on glass substrates with n-type carrier concentrations between 10¹⁴ and 3 × 10²⁰ cm⁻³ by sputtering from single targets near room temperature was investigated as a function of power and process pressure. The resistivity of the films with In/Zn of ∼0.7 could be controlled between 5 × 10⁻³ and 10⁴ Ω cm by varying the power during deposition. The corresponding electron mobilities were 4-18 cm² V⁻¹ s⁻¹.The surface root-mean-square roughness was <1 nm under all conditions for film thicknesses of 200 nm. Thin film transistors with 1 μm gate length were fabricated on these IZO layers, showing enhancement mode operation with good pitch-off characteristics, threshold voltage 2.5 V and a maximum transconductance of 6 mS/mm. These films look promising for transparent thin film transistor applications.     

Effect of annealing on the properties of N-doped ZnO films deposited by RF magnetron sputtering

N-doped ZnO films were deposited by RF magnetron sputtering in N₂/Ar gas mixture and were post-annealed at different temperatures (T_a) ranging from 400 to 800 °C in O₂ gas at atmospheric pressure. The as-deposited and post-annealed films were characterized by their structural (XRD), compositional (SIMS, XPS), optical (UV-vis-NIR spectrometry), electrical (Hall measurements), and optoelectronic properties (PL spectra). The XRD results authenticate the improvement of crystallinity following post-annealing. The weak intensity of the (0 0 2) reflection obtained for the as-deposited N-doped ZnO films was increased with the increasing T_a to become the preferred orientation at higher T_a (800 °C). The amount of N-concentration and the chemical states of N element in ZnO films were changed with the T_a, especially above 400 °C. The average visible transmittance (400-800 nm) of the as-deposited films (26%) was increased with the increasing T_a to reach a maximum of 75% at 600 °C but then decreased. In the PL spectra, A⁰X emission at 3.321 eV was observed for T_a = 400 °C besides the main D⁰X emission. The intensity of the A⁰X emission was decreased with the increasing T_a whereas D⁰X emission became sharper and more optical emission centers were observed when T_a is increased above 400 °C.     

Violet and blue-green luminescence from Ti-doped ZnO films deposited by RF reactive magnetron sputtering

Pure and Ti-doped zinc oxide (TZO) films are deposited using radio frequency (RF) reactive magnetron sputtering at different RF powers. Micro-structural and optical properties in doped ZnO films are systematically investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electronic microscopy (SEM), and a fluorescence spectrophotometer. The results indicate that ZnO films show stronger preferred orientation toward the c$c$-axis and smoother surface roughness after Ti doping. As for TZO films, the full width at half maxima (FWHM) of (002) diffraction peaks decreased first and then increased, reaching a minimum of about 0.92° at 150 W, while the residual compressive stress of the TZO film prepared at 150 W became the largest. The photoluminescent (PL) spectra measured at room temperature reveal a violet, a blue and two green emissions. Intense violet and blue-green luminescence is obtained for the sample deposited at higher RF power. The origin of these emissions is discussed.     

Ferromagnetism in Eu-doped ZnO films deposited by radio-frequency magnetic sputtering

This paper reports that Eu-doped ZnO films were successfully deposited on silicon (100) by radio-frequency magnetic sputtering. The x-ray diffraction patterns indicate that Eu substitutes for Zn in the lattice. Ferromagnetic loops were obtained by using superconducting quantum interference device at 10 K and room temperature. No discontinuous change was found in both of the zero-field-cooled and field-cooled curves. The observed ferromagnetism in Eu-doped ZnO can be attributed to a single magnetic phase. The saturation magnetisation decreased remarkably for the Eu-doped ZnO prepared by introducing 5% of oxygen in the sputtering gas or by the post annealing in O2, suggesting that the defects play key roles in the development of ferromagnetism in Eu-doped ZnO films.     

Characteristics of ZnO:In thin films prepared by RF magnetron sputtering

In-doped ZnO (ZnO:In) transparent conductive thin films were deposited on glass substrates by RF magnetron sputtering. The effect of substrate temperature on the structural, electrical and optical properties of the ZnO:In thin films was investigated. It was found that higher temperature improves the crystallinity of the films and promotes In substitution easily. ZnO:In thin films with the best crystal quality were fabricated at 300 °C, which exhibit a larger grain size of 29 nm and small tensile strain of 0.9%. The transmittance of all the films was revealed to be over 85% in the visible range independence of the substrate temperatures and the lowest resistivity of ZnO:In thin films is 2.4×10⁻³ Ω cm.     

衬底温度对反应磁控溅射W掺杂ZnO薄膜的微观结构及光电性能的影响

采用直流脉冲反应磁控溅射方法生长W掺杂ZnO（WZO）透明导电氧化物薄膜并研究了衬底温度对薄膜微观结构、组分、表面形貌以及光电性能的影响.实验结果表明,WZO薄膜具有良好的（002）晶面择优取向,且适当的衬底温度是制备优质WZO薄膜的关键因素.随着衬底温度升高,薄膜表面粗糙度先增大后减小;衬底温度较高时,薄膜的结构致密,结晶质量好,电子迁移率高.当衬底温度为325℃时,WZO薄膜获得最低电阻率9.25×10^-3Ω·cm,方块电阻为56.24Ω/□,迁移率为11.8 cm² V^-1·s^-1,其在可见光及近红外区域（400—1500 nm）范围的平均透过率达到85.7%.     

Effects of temperature-induced stress on the structural,electrical, and optical properties of ZnO:Ga thin films grown on Si substrates

Crystalline ZnO:Ga thin films with highly preferential c-axis oriented crystals were prepared on Si(001) substrates at different temperatures using the reactive magnetron sputtering technique. Effects of temperature-induced stress in ZnO:Ga films were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), electrical transport, and spectroscopic ellipsometry measurements. XRD results showed that the films were highly c-axis (out-of-plane) oriented and crystallinity improved with growth temperature. The residual compressive stress in films grown at low temperature relaxes with substrate temperature and becomes tensile stress with further increases in growth temperature. Resistivity of the films decreases with increasing stress, while the carrier concentration and mobility increase as the stress increases. The mechanism of the stress-dependent bandgap of ZnO:Ga films grown at different temperatures is suggested in the present work.     

Optical inhomogeneity of ZnS films deposited by thermal evaporation

Zinc sulfide (ZnS) films with optical thickness (reference wavelength is 620 nm) ranging from 310 to 1240 nm were deposited on quartz substrates at room temperature by a thermal evaporation system. The structure and morphology of the films were investigated by X-ray diffraction, atomic force microscopy, respectively. The optical properties of the films were determined by in situ transmittance measurements and wideband spectra photometric measurements, respectively. The experimental results show that the films exhibit cubic structure, and the intensity of the (2 2 0) diffraction peak enhances with the increase of optical thickness. Surface grain size and surface roughness increase monotonously with increasing film thickness. Refractive indices and extinction coefficients calculated by in situ transmittance measurements are well consistent with those calculated by wideband spectra photometric measurements. Both the refractive index and packing density of the film increase as the increase of film thickness, which confirms the film is positive inhomogeneous and has an expanding columnar structure. Extinction coefficients of the films increase with increasing film thickness, which results from the increase of surface roughness.     

Direct current magnetron sputter-deposited ZnO thin films

Zinc oxide (ZnO) is a very promising electronic material for emerging transparent large-area electronic applications including thin-film sensors, transistors and solar cells. We fabricated ZnO thin films by employing direct current (DC) magnetron sputtering deposition technique. ZnO films with different thicknesses ranging from 150 nm to 750 nm were deposited on glass substrates. The deposition pressure and the substrate temperature were varied from 12 mTorr to 25 mTorr, and from room temperature to 450 °C, respectively. The influence of the film thickness, deposition pressure and the substrate temperature on structural and optical properties of the ZnO films was investigated using atomic force microscopy (AFM) and ultraviolet-visible (UV-Vis) spectrometer. The experimental results reveal that the film thickness, deposition pressure and the substrate temperature play significant role in the structural formation and the optical properties of the deposited ZnO thin films.     

Optical properties of hexagonal boron nitride thin films deposited by radio frequency bias magnetron sputtering

The optical properties of hexagonal boron nitride (h-BN) thin films were studied in this paper. The films were characterized by Fourier transform infrared spectroscopy, UV--visible transmittance and reflection spectra. h-BN thin films with a wide optical band gap E_g (5.86 eV for the as-deposited film and 5.97 eV for the annealed film) approaching h-BN single crystal were successfully prepared by radio frequency (RF) bias magnetron sputtering and post-deposition annealing at 970~K. The optical absorption behaviour of h-BN films accords with the typical optical absorption characteristics of amorphous materials when fitting is made by the Urbach tail model. The annealed film shows satisfactory structure stability. However, high temperature still has a significant effect on the optical absorption properties, refractive index n, and optical conductivity σ of h-BN thin films. The blue-shift of the optical absorption edge and the increase of E_g probably result from stress relaxation in the film under high temperatures. In addition, it is found that the refractive index clearly exhibits different trends in the visible and ultraviolet regions. Previous calculational results of optical conductivity of h-BN films are confirmed in our experimental results.     

Effect of Mn doping on the nanostructure and optical properties of ZnO films synthesized by magnetron sputtering

We investigated the microstructure and optical properties of Zn_1−xMn_xO films synthesized by the magnetron sputtering technique. Structural analyses suggest that Mn occupied the Zn sites successfully and did not change the wurtzite structure of ZnO. In addition, nanoscale columnar grain arrays were found in the Mn-doped ZnO films. The experimental results indicate that moderate Mn doping could enhance the photoluminescence emission of ZnO. The possible origin of the emissions from our samples was also explored.