助熔剂对Sr0.97Si2N2O2：0.03Eu2+荧光粉制备及发光性能的影响

在N₂气氛下,以Si₃N₄、SrCO₃和Eu₂O₃为原料,采用自还原高温固相合成法制备了Sr_0.97Si₂N₂O₂：0.03Eu²⁺荧光粉。在近紫外光激发下,该荧光粉发出明亮的黄绿光,发射峰位于533 nm处。采用XRD分析了不同助熔剂（NH₄F,NH₄Cl,Li₂CO₃,H₃BO₃）条件下的荧光粉晶相发育情况。通过SEM和荧光光谱研究了不同助熔剂对Sr_0.97Si₂N₂O₂：0.03Eu²⁺晶粒形貌及发光性能的影响。结果表明,随着助熔剂的添加,荧光粉团聚现象缓解、结晶度增强、分散性提高,且不同程度地提高了荧光粉的发光强度,其中以NH₄Cl的添加效果最佳。     

Co,Zn元素对YBa2Cu3O7-δ的不同的掺杂效应

对单相掺杂样品YBa₂Cu_3-xCo_xO_y (x=0.00,0.025,0.05,0.075,0.10,0.125,0.15,0.20,0.25,O.275,0.30,0.325,0.35,0.375,0.40)和YBa₂Cu_3-xZn_xO_y(x=O.025,0.05,0.075,0.10,0.15,0.20,0.30)作了室温下的 关键词：     

Vacuum Annealing Induced Room-Temperature Ferromagnetism in Co0.1Ti0.9O2-δ Films Prepared by Sol-Gel Method

The Co-doped TiO2 films （Co0.1Ti0.9O2-δ） are prepared on silicon substrates by sol-gel method and post annealing. TheCo0.1Ti0.9O2-δ film annealed in air is non-ferromagnetic at room temperature. After further annealed in a vacuum, the room-temperature ferromagnetism （RTFM） is observed. Experimental evidences show that the RTFM in the Co0.1Ti0.9O2-δ film may come from the Co-doped TiO2 matrix and is related to the oxygen vacancies created by vacuum annealing.     

Sol-gel法制备Er3+-Yb3+共掺杂Al2O3粉末光致发光特性

采用异丙醇铝[Al(OC₃H₇)₃]为前驱体,溶胶-凝胶(Sol-gel)法制备Er³⁺-Yb³⁺共掺杂Al₂O₃粉末.实验结果表明:900 ℃烧结的粉末为固溶Er³⁺、Yb³⁺的γ-(Al,Er,Yb)₂O₃相和少量θ-(Al,Er,Yb)₂O₃相的混合物.Er³⁺-Yb³⁺共掺杂Al₂O₃粉末具有中心波长为1.533 μm的光致发光(PL)特性.1 mol % Er³⁺和1 mol% Yb³⁺共掺杂的Al₂O₃粉末的PL强度较1 mol % Er³⁺掺杂提高2倍,半峰宽从53 nm增加到63 nm.随泵浦功率的提高,PL强度呈线性增加后渐呈饱和趋势.     

PrBa2Cu3O7-δ的制备和电子结构

采用固相反应法制备了正交单相PrBa₂Cu₃O_7-δ样品.运用标准直流四引线法测量了该样品的电阻,发现它随温度的变化呈半导体行为.通过XPS测量表明,样品中明显合有Pr⁴⁺.最后从能带结构讨论了PtBa₂Cu₃0_7-δ不超导的原因. 关键词：     

980 nm LD泵浦Er3+/Yb3+共掺Y2O3纳米粉所致热效应的研究

利用溶胶—凝胶方法制备了Er3+和Yb3+共掺杂的Y₂O₃纳米荧光粉。采用Er3+的2H_11/2→4I_15/2和4S_3/2→4I_15/2绿色上转换荧光强度比的方法,研究了由980 nm二极管激光器泵浦所导致的荧光粉样品表面温升现象。结果表明,随着泵浦功率的增加,样品表面温度大幅度上升, 当功率达到1 000 mW时,样品表面的温度达到820 K。该现象对分析稀土离子上转换过程中所出现的功率饱和现象起着重要的作用,并且在高温传感材料、医学生物细胞烧孔方面有着广阔应用前景。     

荧光粉Y3Mg2AlSi2O12∶Ce3+的合成及光谱性能研究

采用溶胶-凝胶法合成了Y₃Mg₂AlSi₂O₁₂∶Ce³⁺荧光粉。用X射线粉晶衍射(XRD)仪对其进行了物相分析,用电子扫描电镜(SEM)观察了该荧光粉的形貌,同时测定了激发光谱及发射光谱。结果表明,Y₃Mg₂AlSi₂O₁₂∶Ce³⁺的晶体结构与Y₃Al₅O₁₂(钇铝石榴石)一致,形貌也表现出等轴粒状的特点。发射谱为峰值位于580 nm处的宽带发射,是Ce³⁺的 4f⁶5d¹-4f⁷特征跃迁发射。激发谱表现为340 nm和468 nm的双峰带,可以被蓝光有效的激发。Ce³⁺的浓度对发光强度有明显的影响,当Ce³⁺的摩尔分数为0.06时,发光强度最大。最后考察了成分取代而导致的Y₃Mg₂AlSi₂O₁₂∶Ce³⁺的物相转变和对发光性能的影响。     

纳米晶Gd2O3 ∶ Eu3+的制备与发光性质

利用共沉淀法制备了纳米晶Gd₂O₃ : Eu³⁺发光粉体。 在不同掺杂浓度、不同煅烧温度的系列样品中,均观测到Eu³⁺离子的特征发射。样品的晶相与发射性质的研究表明:所制备的样品经800~1 300 ℃热处理后,晶相为立方相,1 400 ℃时开始向单斜相转变。荧光强度与Eu³⁺离子掺杂浓度关系研究表明:在不同掺杂浓度中,Eu³⁺离子浓度为4%时其相对发射强度最强。在三个不同的煅烧温度中,经800 ℃煅烧的样品其发光效果最好。此外还观察到电荷转移激发态以及基质、Gd³⁺与Eu³⁺之间的能量传递。激发谱包含三部分,即电荷转移带、Eu³⁺的4f内壳层电子跃迁和Gd³⁺的激发谱。     

Er3+/Yb3+共掺TeO2-Li2O-B2O3-GeO2玻璃系统的光谱性质和热稳定性研究

制备了Er³⁺/Yb³⁺共掺的70TeO₂-5Li₂O-(25-x)B₂O₃-xGeO₂（x=0,5,10,15,20 mol%）系列玻璃, 研究了玻璃的热稳定性能, 测试了玻璃的吸收光谱、荧光光谱以及Er3+离子4I13/2能级荧光寿命, 并根据McCumber理论计算了Er³⁺离子4I13/2→4I15/2跃迁的受激发射截面. 结果表明：随着GeO₂含量的增加, 玻璃的热稳定性逐渐提高, 荧光谱线半高宽（FWHM）保持在70 nm左右, 而荧光强度和Er3+离子4I13/2能级荧光寿命逐渐提高, 研究表明这种玻璃系统是一种具有应用潜能的宽带光纤放大器用的基质材料.     

0212型Ca3Cu2O4+δCl2-y化合物高温高压合成与研究

 利用“顶角氧掺杂”机制，即以二价氧部分替代顶角一价氯，用Ag₂O做氧源，在高温高压下制备了单相的Ca₃Cu₂O_4+δCl_2-y样品。X射线衍射分析发现，随着Ag₂O含量的增加，Ca₃Cu₂O_4+δCl_2-y样品的晶格常数a逐渐变小，c逐渐增大，体现了空穴掺杂的本质。进行了电阻率和磁化率测量，没有发现超导性，可能是空穴载流子没有达到合适的浓度所致。     

BaIn6Y2O13∶Yb3+, Er3+的制备及上转换发光性质的研究

采用高温固相法合成了不同Yb3+和Er3+掺杂浓度的BaIn₆Y₂O₁₃上转换发光材料。XRD数据显示,所合成的BaIn₆Y₂O₁₃∶Yb3+, Er3+属于六方晶系,引入激活剂并没有改变基质的晶体结构。利用971 nm半导体激光器激发样品,测量样品在不同激发光密度下上转换发射光谱和发射光功率,计算了上转换能量效率。数据表明在激发密度不变,激活剂浓度增加时,上转换光绿红比减小;激活剂浓度不变激发光密度增加时,发射光绿红比增大。分析表明是由于Er3+之间的交叉弛豫增强导致绿红比随激活剂掺杂浓度的增加而减小;Yb3+和Er3+之间的能量传递和Er3+的激发态吸收增强导致绿红比随激发密度的增加而增大。随着激发功率增加, 在较低激发功率时, 上转换绿光发射强度与激发功率的二次方成正比; 在较高激发功率时, 上转换绿光发射强度与激发功率的一次方成正比, 与报道的结果一致。能量效率存在极大值, 分别为0.38%(Yb3+掺杂浓度3%, Er3+掺杂浓度1%)和0.06%(Yb3+掺杂浓度9%, Er3+掺杂浓度3%), 产生极值的一个原因是4I_13/2亚稳态能级寿命较长, 聚集了大量电子, 使基态电子急剧减少, 导致上转换泵浦效率降低。     

B离子对SiO2基质凝胶中Eu3+特征光谱的加强作用

使用正硅酸乙酯、硼酸和硝酸铝为前驱体，硝酸铕为掺杂剂，以溶胶-凝胶法制备了Eu单掺和Eu、B共掺的SiO2干凝胶，并成功地在钠钙玻璃上制备了光洁度很好的掺杂SiO₂多层薄膜.利用荧光光谱、红外光谱（IR）、X射线衍射（XRD）等技术研究了B离子、退火温度对样品发光性能的影响.荧光光谱显示发光体能产生很强的红色发光，经500℃以上退火处理，产生6条谱带，分别归属于Eu³⁺的⁵D₀→⁷F_J（J=0, 1, 2, 3, 4）的电子跃迁, ⁵D₀→⁷F₁的跃迁分裂为两个峰.实验结果表明，B离子的加入，由于在材料中形成了Si-O-B键，使Eu³⁺的配位环境的对称性降低，加强了Eu³⁺的红光发射.退火处理改变了材料的网络结构，降低了水和羟基的含量有助于提高发光强度，但退火温度太高（850℃），发生了荧光猝灭效应，源于稀土离子发生位置迁移形成的团簇.XRD测试结果显示材料是非晶态的.     

Zn元素替代对MgGa2O4∶Cr3+的结构和发光性能的影响

采用高温固相法按化学式Zn_xMg_(1-x)Ga₂O₄∶Cr3+(x=0,0.2,0.6,0.8,1.0)配比原料制备了一系列红色长余辉发光材料。X射线衍射(XRD)分析表明样品物相均为面心立方结构。光致发光特性表明样品的红光发射峰均由以Cr3+为发光中心的电子2E—4A₂跃迁所致,Cr3+的激发带与基质发射带之间有大面积重叠,两者间存在有效的能量传递。余辉衰减曲线与热释光谱分析表明,不同Zn掺入量的样品余辉衰减快慢不同,是由于其中存在的陷阱能级深度不同,且陷阱能级越深,其余辉时间越长。     

Extended Measurement of the v2 (1- ←0+) Band of H3O+ by Mid-Infrared Diode Laser Spectroscopy

Twenty-five new R-branch lines of the v2（1^-← 0^＋） band of H3O^＋ are measured using diode laser velocity modulation spectroscopy between 1070 and 1230 cm^-1. The H3O^＋ ions are produced in a high voltage ac discharge with water diluted in helium. The observed lines together with all the previously published measurements are fit to the standard vibration-rotational Hamiltonian of an oblate symmetric top, yielding a set of improved molecular constants. All the sextic centrifugal distortion constants for both 0^＋ and 1^- states are determined precisely. The observed R（13, 0） transition is shifted about -0.129 cm^-1 from its calculated value, indicating that a near degeneracy exists between the （13, 0）^＋ and （13, 3）^- ground-state rotation-inversion levels.     

Growth and Characterization of a New Superconductor GaBa2Ca3Cu4O11+δ

We successfully grow a new superconductor GaBa₂Ca₃Cu₄O_11+δ(Ga-1234) with a transition temperature of 113 K, using the Walker-type high-pressure synthesis apparatus. X-ray diffraction measurements on the powderized samples show a mixture of the Ga-1234 phase and the Ca_0.85CuO₂ phase, and the former is dominant. Under the scanning electron microscope, plate-like crystals of the Ga-based 1234 phase with shiny surfaces can be seen.The...     

冷压与热压处理对YBa2Cu3O7-δ的结构相变和超导电性的影响

 本文研究了冷压（2.2~5.2 GPa）与热压（2.2 GPa,2.50~950 ℃）对YBa₂Cu₃O_7-δ的正交→四方相转变区和超导电性的影响。冷压保持其正交结构,但破坏了超导性,在98 K（失超点）到室温呈半导体特性,再在空气中烧结,可恢复液氮温区的零电阻状态。以Cu锅密封样品,热压处理至950 ℃,不发生Cu的析出。热压处理后,98 K（失超点）到室温呈半导体特性,再经通氧烧结,于86 K出现零电阻。热压处理过程,从450~950 ℃为正交→四方转变区。950 ℃为转变结束温度,大大高于氧气、空气、氮气、真空状态的温度。400 ℃附近为起始转变温度,低于氮气、氧气气氛的温度。因此相变区加宽。T_0-t结束温度升高,与Cu锅的抑制还原作用有密切关系。如降低高压淬火速率（<<10² ℃/s）,或随后辅以氧气氛中的后处理,将有利于获得既有高密度又有高T_c的YBa₂Cu₃O_7-δ超导体。     

EDTA络合溶胶-凝胶法制备Y2O2S:Eu3+,Mg2+,Ti4+红色长余辉材料

采用EDTA(乙二胺四乙酸)络合溶胶-凝胶法制备了Y2O2S:Eu3+,Mg2+,Ti4+粉体。采用X射线衍射仪、扫描电子显微镜和荧光分光光度计对不同温度合成的样品性能进行测试与表征。结果表明:当硫化温度低于1 000℃时,样品为Y2O3与Y2O2S的混合相;当温度在1 050～1 100℃时,样品为纯相的Y2O2S;当温度升高到1 150℃时,再次出现Y2O3的相。硫化温度在950～1 100℃时,产物的粒径为50～300 nm。用波长为330 nm的紫外光激发样品时,626 nm处的发射对应于Eu3+的5D0-7F2跃迁。硫化温度为1 100℃时,样品的余辉时间最佳,为95 min(≥1 mcd/m2)。相比于以乙酰丙酮为络合剂的溶胶-凝胶法,EDTA络合溶胶-凝胶法制备的样品的发光性能具有较大提高。     

Y2Ba4CuMoOy的添加和Mo替代Cu位对YBa2Cu3O7-δ超导体性能的影响（英文）

本文用固相反应法制备了YBa2(Cu1-xMox)3O7-δ+x mol Y2Ba4CuMoOy(x=0.00～0.08)的一系列多晶样品.利用X射线衍射法、标准四端引线法分别对样品的物相进行了表征和超导转变温度进行了系统的测量,发现随着掺杂量的增加,样品的晶体结构有从正交相向四方相转变的趋势,超导转变温度呈金属状态到半导体状态转变的趋势,并伴有两步转变过程;同时也观察到了超导转变温度降低且转变宽度增加的现象.然而,导致低Tc和宽T的可能原因是逐渐出现的非超导相Mo2411和样品的微观结构不均匀性.通过进一步的比较观察得到,样品超导转变温度出现两步转变最可能的原因不仅与非超导相Mo2411的增加有关而且与低Tc相的形成有关.     

基于低温光声光谱技术的YBa2Cu3O7-δ超导转变过程

利用低温光声系统实时采集高Tc超导材料超导转变过程光声信号,是高Tc超导材料超导机理研究的一种新的实验方法。选取YBa₂Cu₃O_7-8超导体作为试样,分别构建常态→超导态（试样降温过程）和超导态→常态（试样升温过程）,得到转变过程光声信号对比图,并依据光声光谱图对试样失超现象作出可能的解释。     

Effects of N-doping concentration on the electronic structure and optical properties of N-doped β-Ga2O3

The electronic structures and the optical properties of N-doped β-Ga2O3 with different N-doping concentrations are studied using the first-principles method.We find that the N substituting O（1） atom is the most stable structure for the smallest formation energy.After N-doping,the charge density distribution significantly changes,and the acceptor impurity level is introduced above the valence band and intersects with the Fermi level.The impurity absorption edges appear to shift toward longer wavelengths with an increase in N-doping concentration.The complex refractive index shows metallic characteristics in the N-doped β-Ga2O3.