Electron and lattice structure of ultra thin Ag films on Si(1 1 1) and Si(0 0 1)

We studied the low temperature (T ? 130 K) growth of Ag on Si(0 0 1) and Si(1 1 1) flat surfaces prepared by Si homo epitaxy with the aim to achieve thin metallic films. The band structure and morphology of the Ag overlayers have been investigated by means of XPS, UPS, LEED, STM and STS. Surprisingly a (√3 × √3)R30° LEED structure for Ag films has been observed after deposition of 2-6 ML Ag onto a Si(1 1 1)(√3 × √3)R30°Ag surface at low temperatures. XPS investigations showed that these films are solid, and UPS measurements indicate that they are metallic. However, after closer STM studies we found that these films consists of sharp Ag islands and (√3 × √3)R30°Ag flat terraces in between. On Si(0 0 1) the low-temperature deposition yields an epitaxial growth of Ag on clean Si(0 0 1)-2 × 1 with a twinned Ag(1 1 1) structure at coverage’s as low as 10 ML. Furthermore the conductivity of few monolayer Ag films on Si(1 0 0) surfaces has been studied as a function of temperature (40-300 K).     

The dense α-√3 × √3Pb/Si(1 1 1) phase: A comprehensive STM and SPA-LEED study of ordering, phase transitions and interactions

The T-θ phase diagram for the system Pb/Si(1 1 1) was determined in the coverage range 6/5 ML < θ < 4/3 ML from complementary STM and SPA-LEED experiments. This coverage is within the range where a “Devil’s Staircase” (DS) has been realized. The numerous DS phases answer conflicting information in the Pb/Si(1 1 1) literature and update the previously published phase diagram. The measurements reveal the thermal stability of the different linear DS phases with the transition temperature found to be a function of phase period. Because of additional complexity in the experimental system (i.e. two-dimensionality and 3-fold symmetry) the linear DS phases transform at higher temperature into commensurate phases of 3-fold symmetry HIC (historically named “hexagonal incommensurate phase”). Different types of HIC phases have been discovered differing in the size of the supercell built out of √3 × √3 domains separated by domain walls of the √7 × √3 phase. The detailed structures of these HIC phases (coverage, binding site, twist angle, etc.) have been deduced from the comparison of STM images and diffraction patterns. After heating the system to even higher temperature the HIC phase transforms into the disordered phase. For sufficiently high coverage a SIC (“striped incommensurate phase” which is also built from √3 × √3 domains but meandering √7 × √3 domain walls) is observed which also disorders at high temperatures.     

Comparative investigation of the c(2 × 2)-Si/Cu(0 1 1) and (√3 × √3)R30°-Cu2Si/Cu(1 1 1) surface alloys using DFT

The electronic structure of the c(2 × 2)-Si/Cu(0 1 1) surface alloy has been investigated and compared to the structures seen in the three phases of the (√3 × √3)R30°Cu₂Si/Cu(1 1 1) system, using LCAO-DFT. The weighted surface energy increase between the alloyed Cu(0 1 1) and Cu(1 1 1) surfaces is 126.7 meV/Si atom. This increase in energy for the (0 1 1) system when compared to the (1 1 1) system is assigned to the transition from a hexagonal to a rectangular local bonding environment for the Si ion cores, with the hexagonal environment being energetically more favorable. The Si 3s state is shown to interact covalently with the Cu 4s and 4p states whereas the Si 3p state, and to a lesser extent the Si 3d state, forms a mixture of covalent and metallic bonds with the Cu states. The Cu 4s and 4p states are shown to be altered by approximately the same amount by both the removal of Cu ion cores and the inclusion of Si ion cores during the alloying of the Cu(0 1 1) surface. However, the Cu 3d states in the surface and second layers of the alloy are shown to be more significantly altered during the alloying process by the removal of Cu ion cores from the surface layer rather than by the addition of Si ion cores. This is compared to the behavior of the Cu 3d states in the surface and second layers of the each phase of the (√3 × √3)R30°-Cu₂Si/Cu(1 1 1) alloy and consequently the loss of Cu-Cu periodicity during alloying of the Cu(0 1 1) surface is conjectured as the driving force for changes to the Cu 3d states. The accompanying changes to the Cu 4s and 4p states in both the c(2 × 2)-Si/Cu(0 1 1) and (√3 × √3)R30°-Cu₂Si/Cu(1 1 1) alloys are quantified and compared. The study concludes with a brief quantitative study of changes in the bond order of the Cu-Cu bonds during alloying of both Cu(0 1 1) and Cu(1 1 1) surfaces.     

Structural investigation of the c(√2 × 5√2)R45° surface alloy formed by Ti deposition on Cu(0 0 1)

The alloying process of Ti deposited on Cu(0 0 1) was studied by means of XPS, LEIS, XPD and LEED intensity analysis. With the sample held at 570 K, a linear decrease of the Cu LEIS signal as a function of the amount of Ti deposited is observed in the early stages of deposition until a constant value is reached. At the onset of the plateau a c(√2 × 5√2)R45° LEED pattern starts to be visible. XPD and LEED intensity measurements were performed for the c(√2 × 5√2)R45° phase prepared depositing ca. 1.5 monolayer of Ti. The angle-scanned XPD curves measured for the phase c(√2 × 5√2)R45° reveal that Ti atoms substitute Cu atoms in the fcc lattice of the substrate. The polar XPD curves show that at least the first four layers of the substrate are involved in the alloying process. We found that the (3 1 0) plane of the Cu₄Ti alloy (D1_a type-structure) fits, without significant contraction or expansion of the lattice parameters, the c(√2 × 5√2)R45° structure. The intensity versus energy curves of the diffracted beams were calculated on the basis of this structural model using the tensor LEED method. The results of the LEED intensity analysis provide a further evidence of the formation of a slab of Cu₄Ti(3 1 0) layers.     

Fabrication and scanning tunneling microscopy studies of the Si(1 1 1)-(√31 × √31)-In surface

We report on the fabrication of single phase of the Si(1 1 1)-(√31 × √31)-In reconstruction surface, observed by scanning tunneling microscopy (STM) at room temperature. By depositing specific amounts of indium atoms while heating the Si(1 1 1)-(7 × 7) substrate at a critical temperature, the single phase of Si(1 1 1)-(√31 × √31)-In surfaces could be routinely obtained over the whole surface with large domains. This procedure is certified by our high-resolution STM images in the range of 5-700 nm. Besides, the high resolution STM images of the Si(1 1 1)-(√31 × √31)-In surface were also presented.     

Observation of a (√3 × √3)-R30° reconstruction on GaN(0 0 0 1) by RHEED and LEED

A new reconstruction of √3 × √3-R30° has been observed on a GaN film grown on a 6H-SiC (0 0 0 1)-√3 × √3 surface using RHEED and LEED experimental techniques. The experimental LEED PF shows that the GaN film is Ga-terminated hexagonal. The surface is a mixture of two structures with a single bilayer height difference between them. One is a √3 × √3-R30° reconstruction with Ga-adatoms occupying the T4 sites. Another is a Ga-terminated 1 × 1 with no extra Ga on top. The area ratio of the √3 × √3 part to the 1 × 1 part is slightly larger than 1. The first principle total energy calculations and Tensor-LEED I-V curves simulations further confirm this structure model.     

Adsorption induced faceting and superstructural phase diagram of the Sb/Si(5 5 12) interface

The planar high index Si(5 5 12) surface consists of trenches formed by the several proximal surface planes, that can be employed as templates for the adsorption of low dimensional nanostructures. This paper reports the results of an extensive UHV study of the adsorption of Sb, in the sub-monolayer coverage regime, onto the Si(5 5 12) surface. The evolution of the surface phases, surface morphology and electronic structure is monitored by Auger Electron Spectroscopy (AES), Low Energy Electron Diffraction (LEED) and Electron Energy Loss Spectroscopy (EELS). A careful control of substrate temperatures and Sb coverages formed at a low flux rate of 0.06 ML/min enable us to extract a complete adsorption phase diagram of the important interface, for the first time. The phase diagram clearly demonstrates the conversion of the large Si(5 5 12) unit cell into facets of planes of smaller (2 2 5), (3 3 7) and (1 1 3) base units. The study also reveals the formation of various superstructural phases formed by steering the kinetic parameters.     

Investigation of the (√3 × √3)R30°-Cu2Si/Cu(1 1 1) surface alloy using DFT

The electronic structure of the FCC, HCP and 2-fold bridge phases of the (√3 × √3)R30°-Cu₂Si/Cu(1 1 1) surface alloy have been investigated using LCAO-DFT. Analysis of the total electron density, partial density-of-states (PDOS) and crystal orbital overlap population (COOP) curves for the system have shown a surprising similarity between the intra- and inter-layer Si-Cu bond for each phase. Low hybridization between the Si 3s and 3p orbitals results in a low directionality of the Si-Cu bond within each of phase. The Si 3s orbitals are shown to form covalent bonds with their surrounding Cu atoms whereas the Si 3p and 3d orbitals are shown to form combinations of covalent and metallic bonds. The Si-Cu interaction is shown clearly to extend to the second layer of the alloy in deference to previous studies of Si/Cu alloys.     

A structural parallel between Ge- and Si-induced 4 × 4 and 3 × 3 reconstructions on SiC(0 0 0 1) drawn from comparative RHEED oscillations

The initial Ge growth stages on a (√3 × √3)R30°-reconstructed SiC(0 0 0 1) surface (√3) have been studied using a complete set of surface techniques such as reflection high energy electron diffraction (RHEED), low energy electron diffraction (LEED), atomic force microscopy (AFM) and photoemission and compared with similar Si surface enrichments in place of Ge. The investigations essentially focus on the wetting growth-regimes that are favoured by the use of the √3 surface as a starting substrate, this surface being the closest to a smooth and ideally truncated Si-terminated face of hexagonal SiC(0 0 0 1). Depending on temperature and Ge or Si coverages, varying surface organizations are obtained. They range from unorganized layer by layer growths to relaxed Ge(1 1 1) or Si(1 1 1) island growths, through intermediate attempts of coherent and strained Ge or Si surface layers, characterized by 4 × 4 and 3 × 3 surface reconstructions, respectively. RHEED intensity oscillation recordings, as a function of Ge or Si deposited amounts, have been particularly helpful to pinpoint the limited (by the high lattice mismatch) existence domains of these interesting coherent phases, either in terms of formation temperature or surface coverages. Prominently comparable data for these two Ge- and Si-related reconstructions allow us to propose an atomic model for the still unexplained Ge-4 × 4 one. It is based on a same local organization in trimer and ad-atom units for the Ge excess as admitted for the Si-excess of the 3 × 3 surface, the higher strain nevertheless favouring arrangements, for the Ge-units, in 4 × 4 arrays instead of 3 × 3 Si ones. Admitting such models, 1.25 and 1.44 monolayers of Ge and Si, should, respectively, be able to lie coherently on SiC, with respective lattice mismatches near 30% and 25%. The experimental RHEED-oscillations values are compatible with such theoretical ones. Moreover, these RHEED coverage determinations (for layer completion, for instance) inform us in turn about the initial Si richness of the starting √3 reconstruction and help us to discriminate between earlier contradictory atomic models proposed in the literature.     

Ultra-thin Si overlayers on the TiO2 (1 1 0)-(1 × 2) surface: Growth mode and electronic properties

The growth of thin subnanometric silicon films on TiO₂ (1 1 0)-(1 × 2) reconstructed surfaces at room temperature (RT) has been studied in situ by X-ray and ultra-violet photoelectron spectroscopies (XPS and UPS), Auger electron and electron-energy-loss spectroscopies (AES and ELS), quantitative low energy electron diffraction (LEED-IV), and scanning tunneling microscopy (STM). For Si coverage up to one monolayer, a heterogeneous layer is formed. Its composition consists of a mixture of different suboxides SiO_x (1 < x ? 2) on top of a further reduced TiO₂ surface. Upon Si coverage, the characteristic (1 × 2) LEED pattern from the substrate is completely attenuated, indicating absence of long-range order. Annealing the SiO_x overlayer results in the formation of suboxides with different stoichiometry. The LEED pattern recovers the characteristic TiO₂ (1 1 0)-(1 × 2) diagram. LEED I-V curves from both, substrate and overlayer, indicate the formation of nanometric sized SiO_x clusters.     

Surface phase transition and electronic structure of c(5√2 × √2)R45°-Pb/Cu(1 0 0)

The c(5√2 × √2)R45°-Pb/Cu(1 0 0) surface phase is investigated by means of angle resolved ultraviolet photoemission and low energy electron diffraction in the temperature range between 300 and 550 K. We identify and characterize a temperature-induced surface phase transition at 440 K from the room temperature c(5√2 × √2) R45° phase to a (√2 × √2)R45° structure with split superstructure spots. The phase transition is fully reversible and takes place before the two-dimensional melting of the structure at 520 K. The electronic structure of the split (√2 × √2)R45° phase is characterized by a metallic free-electron like surface band. This surface band is backfolded with c(5√2 × √2)R45° periodicity phase at room temperature, giving rise to a surface band gap at the Fermi energy. We propose that a gain in electronic energy explains in part the stability of the c(5√2 × √2)R45° phase.     

Electronic structure study of reconstructed Au-SiC(0 0 0 1) surfaces

A study of surface and interface properties of reconstructed Au-SiC(0 0 0 1) surfaces is reported. Two reconstructions were prepared on SiC(0 0 0 1), a √3 × √3R30° and a Si-rich 3 × 3, before Au deposition and subsequent annealing at different temperatures. For the Si-rich 3 × 3 surface the existence of three stable reconstructions 2√3 × 2√3R30°, 3 × 3 and 5 × 5 are revealed after deposition of Au layers, 4-8 Å thick, and annealing at progressively higher temperatures between 500 and 950 °C. For the 2√3 surface two surface shifted Si 2p components are revealed and the Au 4f spectra clearly indicate silicide formation. The variation in relative intensity for the different core level components with photon energy suggests formation of an ordered silicide layer with some excess Si on top. Similar core level spectra and variations in relative intensity with photon energy are obtained for the 3 × 3 and 5 × 5 phases but the amount of excess Si on top is observed to be smaller and an additional weak Si 2p component becomes discernable.For the √3 surface the evolution of the core level spectra after Au deposition and annealing is shown to be distinctly different than for the Si-rich 3 × 3 surface and only one stable reconstruction, a 3 × 3 phase, is observed at similar annealing temperatures.     

STM study of acetylene reaction with Si(1 1 1): observation of a carbon-induced Si(1 1 1)√3×√3R30° reconstruction

The first stages of acetylene reaction with the Si(1 1 1)7 × 7 reconstructed surface kept at 600 °C are studied by recording scanning tunneling microscopy (STM) images during substrate exposure at a C₂H₂ pressure of 2 × 10⁻⁴ Pa (2 × 10⁻² mbar). We observed the progressive substitution of the 7 × 7 reconstruction with a carbon induced Si(1 1 1)√3×√3R30° reconstruction characterized by an atomic distance of 0.75 ± 0.02 nm, very close to that of the silicon 7 × 7 adatoms. This means that a carbon enrichment of the silicon outermost layers occurs giving rise to the formation of a Si-C phase different from the √3×√3R30° reconstruction typical of Si terminated hexagonal SiC(0 0 0 1) surface with an atomic distance of 0.53 nm. To explain STM images, we propose a reconstruction model which involves carbon atoms in T₄ and/or S₅ sites, as occurring for B doped Si(1 1 1) surface. Step edges and areas around the silicon surface defects are the first regions involved in the reaction process, which spreads from the upper part of the step edges throughout the terraces. Step edges therefore, progressively flakes and this mechanism leads, for the highest exposures, to the formation of large inlets which makes completely irregular the straight edge typical of the Si(1 1 1)7 × 7 terraces. These observations indicate that there occurs an atomic diffusion like that driving the meandering effect. Finally, the formation of a few crystallites is shown also at the lowest acetylene exposures. This is the first STM experiment showing the possibility to have carbon incorporation in a Si(1 1 1) matrix for higher amounts than expected, at least up to 1/6 of silicon atomic layer.     

Methanethiolate structural phases on Cu{1 1 1} observed using a novel fibre-optic low-energy electron diffraction instrument

We have used a novel fibre-optic low-energy electron diffraction (FO-LEED) instrument, capable of low flux measurements that minimise electron beam damage to surface overlayers, to study methanethiolate (CH₃-S-) structural phases formed on Cu{1 1 1} at temperatures between 110 and 300 K. Three structural phases were seen: a (√3 × √3)R30° phase that forms at 110-140 K; a (4 × 4) phase which was observed transiently at 110 K; and a pseudo-{1 0 0} reconstructed phase which forms at room temperature. We discuss these in the context of previous studies of this system, and demonstrate the ability of the FO-LEED instrument to record high-quality LEED patterns and intensity data from a strongly beam-sensitive surface.     

Deduction of a three-phase model for the (√3 × √3)R30°-Cu2Si/Cu(1 1 1) surface alloy

The (√3 × √3)R30°-Cu₂Si/Cu(1 1 1) surface alloy that forms during high temperature dosing of silane (SiH₄) on Cu(1 1 1) has been investigated using LCAO-DFT. Simulated STM images have shown that experimental images may be interpreted as a mixed phase system consisting of Si ion cores bound in HCP, FCC and twofold bridge sites with a ratio of 25:25:50 rather than previously proposed models where the Si ion cores were bound in only FCC and HCP sites. The new model is shown to be consistent with previously published NIXSW studies.     

Structure and electronic properties of gold adsorbed on Ti(0 0 0 1)

The Au/Ti(0 0 0 1) adsorption system was studied by low energy electron diffraction (LEED) and photoemission spectroscopy with synchrotron radiation after step-wise Au evaporation onto the Ti(0 0 0 1) surface. For adsorption of Au at 300 K, no additional superstructures were observed and the (1 × 1) pattern of the clean surface simply became diffuse. Annealing of gold layers more than 1 ML thick resulted in the formation of an ordered Au-Ti surface alloy. Depending on the temperature and annealing time, three surface reconstructions were observed by LEED: (√3 × √3) R30°, (2 × 2) and a one-dimensional incommensurate (√3 × √3) rectangular pattern. The Au 4f core level and valence band photoemission spectra provided evidence of a strong chemical interaction between gold and titanium. The data indicated formation of an intermetallic interface and associated valence orbital hybridization, together with diffusion of gold into the bulk. Au core-level shifts were found to be dependent on the surface alloy stoichiometry.     

Growth of (√3 × √3)-Ag and (1 1 1) oriented Ag islands on Ge/Si(1 1 1) surfaces

We have studied the growth of Ag on Ge/Si(1 1 1) substrates. The Ge/Si(1 1 1) substrates were prepared by depositing one monolayer (ML) of Ge on Si(1 1 1)-(7 × 7) surfaces. Following Ge deposition the reflection high energy electron diffraction (RHEED) pattern changed to a (1 × 1) pattern. Ge as well as Ag deposition was carried out at 550 °C. Ag deposition on Ge/Si(1 1 1) substrates up to 10 ML has shown a prominent (√3 × √3)-R30° RHEED pattern along with a streak structure from Ag(1 1 1) surface. Scanning electron microscopy (SEM) shows the formation of Ag islands along with a large fraction of open area, which presumably has the Ag-induced (√3 × √3)-R30° structure on the Ge/Si(1 1 1) surface. X-ray diffraction (XRD) experiments show the presence of only (1 1 1) peak of Ag indicating epitaxial growth of Ag on Ge/Si(1 1 1) surfaces. The possibility of growing a strain-tuned (tensile to compressive) Ag(1 1 1) layer on Ge/Si(1 1 1) substrates is discussed.     

Substitutional adsorption geometry for Pb(1 1 1)-(√3 × √3)R30°-K

Intermixed structures for alkalis (larger than Li) on close-packed substrates have previously been observed only on Al(1 1 1). This study shows that K forms an ordered intermixed structure on Pb(1 1 1). The structures of clean Pb(1 1 1) and Pb(1 1 1)-(√3 × √3)R30°-K were studied using dynamical low-energy electron diffraction (LEED). The clean Pb(1 1 1) surface at 47 K was found to be a relaxed version of the bulk structure, in agreement with an earlier study of the same surface [Y.S. Li, F. Jona, P.M. Marcus, Phys. Rev. B 43 (1991) 6337]. At room temperature, adsorption of K on this surface results in a (√3 × √3)R30° structure, which was shown using dynamical LEED to consist of K atoms substituted in surface vacancies. The K-Pb bond length was found to be 3.62 ± 0.3 Å, with no significant change to the Pb interlayer spacings.     

Mixed water/OH structures on Pd(1 1 1)

Chemisorbed O and water react on Pd(1 1 1) at low temperatures to form a mixed OH/H₂O layer with a (√3 × √3)R30° registry. Reaction requires at least two water molecules to each O before the (2 × 2)O islands are consumed, the most stable OH/water structure being a (OH + H₂O) layer containing 0.67 ML of oxygen, formed by the reaction 3H₂O + O → 2(H₂O + OH). This structure is stabilised compared to pure water structures, decomposing at 190 K as OH recombines and water desorbs. The (√3 × √3)R30° − (OH + H₂O) phase cannot be formed by O/H reaction and is distinct from the (√3 × √3)R30° structure formed by O/H coadsorption below 200 K. Mixed OH/water structures do not react with coadsorbed H below 190 K on Pd(1 1 1), preventing this phase catalyzing the low temperature H₂/O₂ reaction which only occurs at higher temperatures.     

Structural and statistical analysis of Yb/Si(1 1 1) and Eu/Si(1 1 1) reconstructions

We have performed the structural and statistical analysis of Yb/Si(1 1 1) and Eu/Si(1 1 1) surfaces in the submonolayer regime utilizing low-energy electron diffraction and scanning tunneling microscopy (STM). The almost identical series of one-dimensional chain structures (e.g., 3 × 2/3 × 1, 5 × 1, 7 × 1, 9 × 1, and 2 × 1 phases) are found in order of increasing metal coverage for both adsorbed systems, however, only the Eu/Si system reveals the ‘√3’-like reconstruction before the 2 × 1 endpoint phase. The atomic models of chain structures are proposed and discussed. In particular, our results suggest the odd-order n×1 (n=5,7,9,…) intermediate reconstructions to incorporate the Seiwatz chains and honeycomb chains with the proportion of m:1, where . The statistical analysis of STM images is carried out to examine the correlation of atomic rows on Eu/Si and Yb/Si surfaces. It is found that Eu stabilizes more ordered row configuration compared to Yb, which can be explained in terms of indirect electronic interaction of atomic chains or/and different magnetic properties of adsorbed species.