Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33, 用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体. 采用这些固溶体作载体, 以Fe2O3为活性组分, 用浸渍法制备了一系列催化剂. BET结果显示, 将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积. TPR结果显示, 载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能. XRD结果表明, Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况, 老化前后催化剂的晶相结构基本无明显变化. 特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时, Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

整体式Co3O4/YSZ—γ-Al2O3＋CYZ催化剂上的甲烷催化燃烧

用质量比为3：2的YSZ-γ-Al2O3和CeO2-Y2O3-ZrO2的混合物（以YSZA＋CYZ表示）作载体，制备了不同Co3O4含量的整体式甲烷燃烧催化剂，同时制备了分别以YSZA和CYZ为载体的催化剂作为对比。研究了它们老化前后的反应性能，并用BET，XPS，XRD，TPR等研究了催化剂的比表面、表面状态、晶相结构和还原性能．结果表明，YSZ-γ-Al2O3和CeO2-Y2O3-ZrO2混合载体能有效地抑制CoAl2O4的生成，并能充分发挥各自的优点，因此负载一定量的钴后表现出很高的甲烷催化燃烧活性和抗老化性，尤其是含8wt％Co3O4的样品性能最佳，有望成为实用的甲烷燃烧催化剂之一．     

整体式Co3O4/YSZ-Y-Al2O3+CYZ催化剂上的甲烷催化燃烧

用质量比为32的YSZ-γ-Al2O3和CeO2-Y2O3-ZrO2的混合物(以YSZA+CYZ表示)作载体,制备了不同Co3O4含量的整体式甲烷燃烧催化剂,同时制备了分别以YSZA和CYZ为载体的催化剂作为对比,研究了它们老化前后的反应性能,并用BET,XPS,XRD,TPR等研究了催化剂的比表面、表面状态、晶相结构和还原性能.结果表明,YSZ-γ-Al2O3和CeO2-Y2O3-ZrO2混合载体能有效地抑制CoAl2O4的生成,并能充分发挥各自的优点,因此负载一定量的钴后表现出很高的甲烷催化燃烧活性和抗老化性,尤其是含8 wt%Co3O4的样品性能最佳,有望成为实用的甲烷燃烧催化剂之一.     

Fe2O3/YSZ-γ-Al2O3催化剂在甲烷催化燃烧中的催化性能研究

以Fe2O3为活性组分，γ-Al2O3，ZrO2-γ—Al2O3及YSZ—γ—Al2O3(YSZ是用Y2O3稳定ZrO2的催化剂载体)为载体，制备了3种甲烷燃烧催化剂．其中以YSZ—γ—Al2O3为载体的催化剂催化性能最好．XPS检测发现．ZrO2和Y2O3的存在可以增加和稳定Fe2O3的表面浓度，同时也可减弱Fe2O3与γ—Al2O3之间的相互作用．Fe2O3质量分数为10％的Fe2O3／YSZ—γ—Al2O3催化剂具有最佳的催化活性．XRD测试结果表明．该催化剂的活性与Fe2O3在载体上的分散状况有关．     

Ce0.45Zr0.45Y0.07La0.03O1.95/La-Ba-Al2O3质量比对整体式铁基催化剂上稀薄甲烷燃烧的影响

采用共沉淀法和胶溶法分别制备了高性能的储氧材料Ce0.45Zr0.45Y0.07La0.03O1.95(OSM)和耐高温高比表面的La-Ba-Al2O3,并以它们为载体,制备了一系列整体式铁基催化剂.考察了该系列催化剂对甲烷稀薄燃烧的催化性能.并用低温N2吸附-脱附,储氧量(OSC)测试,X射线衍射(XRD)和H2程序升温还原(H2-TPR)等测试手段考察了不同Ce0.45Zr0.45Y0.07La0.03O1.95/La-Ba-Al2O3质量比对催化剂特性的影响.活性测试结果表明,当Ce0.45Zr0.45Y0.07La0.03O1.95/La-Ba-Al2O3质量比为1:1时新鲜和老化催化剂的活性均最好,新鲜催化剂可在50000h-1的高空速条件下使含量为1%(体积分数)的甲烷在446℃起燃,553℃完全转化;低温氮气吸附-脱附测试结果和H2-TPR表明,不同的Ce0.45Zr0.45Y0.07La0.03O1.95/La-Ba-Al2O3质量比使催化剂表现出不同的织构性能和还原性能;XRD测试结果表明,OSM以均一固溶体存在,Fe高度分散在载体上.综合以上表征手段得出:合适的Ce0.45Zr0.45Y0.07La0.03O1.95/La-Ba-Al2O3质量比导致催化剂具有优异的稀薄甲烷催化燃烧活性和热稳定性.     

ZrO2、Y2O3对CH4燃烧催化剂Fe2O3/γ-Al2O3的改性作用

γ-Ａｌ2Ｏ3作为催化剂载体具有较大的比表面积,机械强度高,孔结构适宜,但不耐高温。近年来,氧化锆载体以其耐高温等[1]独特性质引起多方面的关注[2-4],它能与所负载的金属产生强烈的电子相互作用,影响催化剂的吸附、氧化和还原性能。但是ＺｒＯ2比表面积较小,且随焙烧温度的升高急剧下降,如单独作为催化剂载体,其应用受到很大限制。若将ＺｒＯ2分散到γ-Ａｌ2Ｏ3表面上,可制得兼备两者优点的复合载体。当ＺｒＯ2中加入Ｙ2Ｏ3,能产生特殊的氧空穴[5],具有氧离子传导功能和导电性;与活性组分相结合能在很大程度上提高反应速度。我们用Ｙ…     

Ce1-xNixO2/Al2O3/FeCrAl催化剂的制备及其甲烷催化燃烧性能

以FeCrA l合金薄片为基体,A l2O3为过渡载体,Ce1-xN ixO2(x=0.1-0.3)、CeO2和N iO为活性组分,制备了Ce1-xN ixO2/A l2O3/FeCrA l、CeO2/A l2O3/FeCrA l和N iO/A l2O3/FeCrA l金属基整体式催化剂,在固定床微型反应器中评价了催化剂的甲烷催化燃烧性能,用SEM、XRD、TPR等方法对催化剂的物相、表面形貌和氧化还原性进行了表征.结果表明,Ce1-xN ixO2在催化剂表面的分散性比CeO2和N iO要好;Ce1-xN ixO2/A l2O3/FeCrA l(x=0.1-0.3)催化剂具有好的催化活性和高温稳定性,CeO2/A l2O3/FeCrA l和N iO/A l2O3/FeCrA l催化剂有好的初活性但高温稳定性较差;活性组分与A l2O3和FeCrA l金属基体之间存在较强的相互作用.     

CeO2-MOx（M=La^3＋,Ca^2＋）改性Pd/γ-Al2O3催化甲烷燃烧性能

采用沉积-沉淀法制备了固溶体CeO2-MOx=(M=La3+,Ca2+)改性的Pd/γ-Al2O3催化剂,利用XRD、Raman和XPS对催化剂进行了表征.结果表明,金属(M)离子进入CeO2的晶格,形成CeO2-MOx固溶体,Raman谱上463cm-1处对应于Ce-O键的F2g对称伸缩振动强度降低.其中,样品Pd/γ-Al2O3CeO2-CaO在615 cm-1处出现一小峰,样品Pd/γ-Al2O3-CeO2-La2O3在320cm-1处出现的肩峰,都表明固溶体CeO2-MOx的形成使O2-亚晶格结构对称性降低.XPS分析表明,固溶体改性的Pd/γ-Al2O3催化剂中Pd的3d5/2结合能比正常价态的PdO的结合能高出0.5-0.6 eV,形成了一种高度离子化的.与载体具有强相互作用的Pd物种.催化甲烷燃烧实验证明,固溶体CeO2-MOx(M=La3+,Ca2+)改性的Pd/γ-Al2O3催化剂的低温活性和稳定性均高于未经改性的Pd/γ-Al2O3催化剂和仅用CeO2改性的Pd/γAl2O3催化剂,在空速为50000 h-1时,可使1%CH4-99%空气(体积分数)混合气中甲烷的10%转化温度降至254℃,转化率100%时的转化温度降至340℃.     

BaO对Pd/Al2O3上CH4催化燃烧性能的影响

以醋酸钯为前身盐, BaO-Al2O3复合氧化物为载体制备了系列负载型钯催化剂. BET和XRD表征结果表明,复合氧化物在制备过程中发生固相反应所生成的BaAl2O4 可以阻止γ-Al2O3向α相的转变,显著增强Al2O3的热稳定性.以甲烷燃烧为模型反应的评价结果表明, BaO的引入提高了催化剂上甲烷燃烧反应的活性和稳定性.     

掺杂Mn对CeO2-ZrO2-Al2O3材料性质的影响

采用共沉淀法制备了一系列Mn掺杂摩尔分数为0～5%的CeO2-ZrO2-Al2O3(CZA)复合氧化物, 并采用BET, OSC, XRD, XPS, H2-TPR等方法对所制备的材料进行了表征. 结果表明, 所制备的材料均形成了稳定的CZA固溶体, 尤其是Mn掺杂0.5%的材料在600和1000 ℃焙烧后均表现出最好的织构性能. OSC和H2-TPR的结果表明, Mn掺杂量≤1%时, 氧在材料中的体相移动是材料储氧和被还原的速控步骤, 并且Mn的掺杂量为0.2%时, 储氧量最大, 材料的还原温度也最低; Mn掺杂量>1%时, Mn物种对材料储氧和被还原的作用显著. XPS结果表明, Mn在焙烧过程中会迁移向表面, 结合H2-TPR结果可知, 新鲜样品表面的MnOx物种主要为Mn2O3, 而老化样品主要为Mn3O4.     

Pd/γ-Al2O3三效催化剂中CeO2-ZrO2-La2O3的作用

用浸渍法制备了CeO2-ZrO2-La2O3复合氧化物,用XRD,TG-DTA,拉曼光谱、H2-TPR和BET表面积测定等方法对合成的样品进行了表征,研究了在单钯Pd/γ-Al2O3催化剂中添加CeO2-ZrO2-La2O3对催化剂活性和热稳定性的影响.结果表明,在Pd/γ-Al2O3中加入三元复合氧化物有利于提高三效催化剂的热稳定性,有利于阻止γ-Al2O3在高温时的相变以稳定Al2O3结构,防止在高温条件下催化剂表面积的损失.在Pd的负载量为1 g*L-1条件下,测定了Pd/CeO2-ZrO2-La2O3/γ-Al2O3/蜂窝陶瓷催化剂对CO,C3H6和NO净化的三效活性,研究了催化剂的结构和三效催化活性之间的关系.结果表明,CeO2-ZrO2-La2O3的存在能明显提高Pd基催化剂对CO,C3H6和NO的三效净化活性,扩大催化剂的操作窗口,提高在富氧条件下对NOx的还原性能.     

Catalytic methanol decomposition to carbon monoxide and hydrogen over Pd/CeO2-ZrO2-La2O3 with different Ce/Zr molar ratios

The catalytic behaviors of Pd (1.4 wt%) catalysts supported on CeO2-ZrO2-La2O3 mixed oxides with different Ce/Zr molar ratios were investigated for methanol decomposition. Nitrogen adsorption-desorption (BET), X-ray photoelectron spectroscopy (XPS), H2 temperature-programmed reduction (H2-TPR), X-ray diffraction (XRD) and Pd dispersion analysis were used for their characterization. Pd/Ce0.76Zr0.18 La0.06 O1.97 catalyst showed the highest BET surface area, best Pd dispersion capability and strongest metal-support interaction. Moreover, XPS showed that there was lattice defect oxygen or mobile oxygen. According to the result of O 1s measurements the lattice defect oxygen or mobile oxygen helped to maintain Pd in a partly oxidized state and increased the activity for methanol decomposition. The Pd/Ce0.76Zr0.18La0.06O1.97 catalyst exhibited the best activity. A 100% conversion of methanol was achieved at around 260℃, which was about 20-40 ℃ lower than other catalysts     

Comparative Study of CuO Species on CuO/Al2O3, CuO/CeO-Al2O3 andCuO/La2O-Al2O3 Catalysts for CO Oxidation

CuO/Al2O3, CuO/CeO2-Al2O3, and CuO/La2O3-Al2O3 (denoted as Cu/Al, Cu/CeAl, and Cu/LaAl) catalysts were prepared by an impregnation method. CuO species and CuO/Al2O3 thermal solid-solid interaction were characterized by in situ XRD, Raman spectroscopy and H2-TPR techniques. For the Cu/Al catalyst, a CuAl2O4 phase exists between the CuO and Al2O3 layer and the CuO phase exists on the surface in both highly dispersed and bulk forms. For the Cu/CeAl catalyst, there is highly dispersed and bulk CuO on the surface, but most of the CuO has transferred into the internal layer of CeO2 as bulk CuO and CuAl2O4. For the Cu/LaAl catalyst, only bulk CuO is present on the surface of the catalyst and no CuAl2O4 is formed. The catalytic activity order for CO oxidation is Cu/CeAl>Cu/Al>Cu/LaAl. The highly dispersed CuO on the catalyst surface may be the active phase for CO oxidation. The results show that the addition of CeO2 not only promotes both the transference of CuO and the formation of CuAl2O4 but also favors the CO oxidation due to the association of highly dispersed CuO with CeO2, while La2O3 hinders the transference of CuO and the formation of CuAl2O4.     

CuO／CeO2和CuO／Al2O3催化剂的催化性能

本文以ＣＯ氧化为模式反应考察了ＣｅＯ２和Ａｌ２Ｏ３负载氧化铜催化剂的氧化活性，运用ＸＲＤ和ＴＰＲ技术研究了催化剂的还原性能和物相结构，结果表明：载体性质对负载ＣｕＯ催化剂的ＣＯ氧化活性有很大影响，ＣｕＯ／ＣｅＯ２催化剂活性明显高于ＣｕＯ／Ａｌ２Ｏ３催化剂．催化剂的还原特性随载体不同而不同．同时发现，热处理对催化剂铜物种的存在形式，晶粒大小、还原特性及其催化活性有明显影响，ＣｕＯ／Ａｌ２Ｏ３催化剂活性下降的主要因素是生成了活性较低的ＣｕＡｌ２Ｏ４相，而ＣｕＯ／ＣｅＯ２催化剂活性下降是由于ＣｕＯ和ＣｅＯ２发生烧结，晶粒变大     

Praseodymium Oxide Modified CeO2/Al2O3 Catalyst for Selective Catalytic Reduction of NO by NH3

A series of CeO₂/Al₂O₃ catalysts was modified with praseodymium oxide using an extrusion method. The catalytic activities of the obtained catalysts were measured for the selective catalytic reduction of NO with NH₃ to screen suitable addition of praseodymium oxide. These samples were characterized by XRD, N₂‐BET, NH₃‐TPD, NO‐TPD, Py‐IR, H₂‐TPR, Raman spectra and XPS, respectively. Results showed the optimal catalyst with the Pr/Ce molar ratio of 0.10 exhibited more than 90% NO conversion in a wide temperature range of 290–425°C under GHSV of 5000 h^?1. The number of Lewis acid sites and the chemisorbed oxygen concentration of the catalysts would increase with the Pr incorporation, which was favorable for the excellent catalytic performance. In addition, the Pr incorporation inhibited growth of the Al₂O₃ crystal particles and led to the lattice expansion of CeO₂, which increased catalytic activity. The results implied that the higher chemisorbed oxygen concentrations and the more Lewis acid sites were conductive to obtain the excellent SCR activity.     

复合沉淀剂制备的CeO2-ZrO2-Al2O3材料及其负载的单Pd三效催化剂

采用了一种由氨水和碳酸铵组成的复合沉淀剂来制备CeO₂-ZrO₂-Al₂O₃ （CZA）复合氧化物。作为对比,分别采用氨水和碳酸铵为沉淀剂制备了另外两个CZA复合氧化物。系统地研究了各CZA材料在织构、结构、氧化还原性能、热老化行为之间的区别,以及其负载的单Pd三效催化剂的催化性能。结果表明,不同的沉淀剂制得的材料中其CeO₂-ZrO₂ （CZ）和Al₂O₃之间的相互作用不同。用氨水做沉淀剂时,得到的材料中CZ和Al₂O₃之间的相互作用很小,导致其热稳定性较差。在碳酸铵做沉淀剂的情况下,CZ和Al₂O₃之间具有很强的相互作用,可以提高材料的热稳定性,但同时,CZ固溶体的均一性被严重破坏,使得材料的氧化还原性能不理想。而复合沉淀剂的使用可以有效地平衡CZ和Al₂O₃之间的相互作用,导致得到的CZA材料具有优异的织构、结构性能及良好的热稳定性。因此,其负载的单Pd催化剂表现出最为优异的氧化还原性能和三效催化活性。     

Pt/Al2O3和Pt/CeO2/Al2O3催化甲烷部分氧化制合成气反应

研究了Pt/Al₂O₃和Pt/CeO₂/Al₂O₃对甲烷部分氧化制合成气反应的催化活性,发现Pt/CeO₂/Al₂O₃显示了更高的甲烷转化率和合成气选择性.用H₂-TPR、H₂-TPD、SEM-EDX和XRD等技术对催化剂进行了表征.CeO₂和Pt相互作用促进Pt在催化剂表面的分散,抑制Pt在催化剂表面的迁移;降低了催化剂的燃烧活性,提高了催化剂的部分氧化活性和选择性,可避免因催化剂床层局部温度过高而导致催化剂活性下降或失活,提高了催化剂的稳定性.同时,CeO₂通过促进水汽变换反应使反应体系迅速达到平衡,提高了催化剂对H₂的选择性.     

水热改性对NiMo/γ-Al2O3加氢脱氮催化剂结构及性能的影响

The influence of hydrothermal modification on the structure and hydrodenitrogenation (HDN) activity of NiMo/γ-Al₂O₃catalyst was studied in the range 140～180 ℃. The experimental results indicated that the hydrodenitrogenation reaction rate of pyridine was accelerated using the NiMo/γ-Al₂O₃catalyst synthesized via hydrothermal route due to the change of the structure, the increase of the amount of Mo and Ni and the rise of the specific surface area. The change of the structure of catalysts was enhanced at higher hydrothermal temperature, producing NiMo/γ-Al₂O₃catalyst with better HDN activity.     

镧、锰掺杂改性CeO2-ZrO2-Al2O3固溶体的性能

采用共沉淀法制备了一系列La, Mn共掺杂的CeO2-ZrO2-A12O3(CZA)复合氧化物, 采用BET, XRD, H2-TPR, XPS和XRF等方法对样品进行表征. 结果表明, 全部样品均形成了稳定的CZA固溶体, 经600 ℃焙烧后表现出良好的织构性能, 1000 ℃老化后, La, Mn共掺杂样品具有最佳的高温稳定性; H2-TPR测试表明, La, Mn之间存在正协同效应, 共掺杂的样品具有最佳的低温还原性能和高温稳定性; XPS结果表明, 掺杂La可有效抑制在焙烧过程中Mn向表面的迁移, 从而保持较高的表面吸附氧浓度.