Comparative study on structural and optical properties of ZnO thin films prepared by PLD using ZnO powder target and ceramic target

Zinc oxide thin films have been obtained in O₂ ambient at a pressure of 1.3 Pa by pulsed laser deposition (PLD) using ZnO powder target and ceramic target. The effect of temperature on structural and optical properties of ZnO thin films was investigated systematically by XRD, SEM, FTIR and PL spectra. The results show that the best structural and optical properties can be achieved for ZnO thin film fabricated at 700 °C using powder target and at 400 °C using ceramic target, respectively. The PL spectrum reveals that the efficiency of UV emission of ZnO thin film fabricated by using powder target is low, and the defect emission of ZnO thin film derived from Zn_i and O_i is high.     

Optical properties and structural characteristics of ZnO thin films grown on a-plane sapphire substrates by plasma-assisted molecular beam epitaxy

We investigated structural and optical properties of ZnO thin films grown on (112?0) a-plane sapphire substrates using plasma-assisted molecular beam epitaxy. Negligible biaxial stress in ZnO thin films is due to the use of (112?0) a-plane sapphire substrates and slow substrate cooling. The 14 K photoluminescence spectrum shows a blueshift of energy positions compared with ZnO single crystal. A donor with binding energy of 43 meV and an acceptor with binding energy of ～170 meV are identified by well-resolved photoluminescence spectra. A characteristic emission band at 3.320 eV (so-called A-line) is studied. Based on analysis from photoluminescence spectra, the origin of the A-line, it seems, is more likely an (e, A°) transition, in which defect behaves as an acceptor. The room-temperature photoluminescence is dominated by the FX at 3.307 eV, which is an indication of strongly reduced defect density in ZnO thin films.     

Phase mixture and anti-reflection window in visible of annealed beryllium-nitride thin films on silicon crystal

Beryllium-nitride (Be₃N₂) thin films were grown on silicon Si(1 1 1) substrates by pulsed laser deposition in a RIBER LDM-32 system, and characterized with in/ex situ XPS and SIMS. The structure of the films was analyzed with XRD. The films were further analyzed for surface topographic information with SEM and profilometry, and for optical properties with optical spectroscopy. It was observed that the material, prepared at room temperature and annealed at 700 °C for 2 h, had undergone a partial phase transition to a mixture of amorphous and crystalline phases, and the thin films showed a large anti-reflection window in the visible. Therefore, the annealed Be₃N₂ thin films would be potentially useful for stable electronic packaging with desired photonic features.     

Optical properties of PMN–PT thin films prepared using pulsed laser deposition

(1 ? x)Pb(Mg_1/3Nb_2/3)O₃–xPbTiO₃ (PMN–PT) thin films have been deposited on quartz substrates using pulsed laser deposition (PLD). Crystalline microstructure of the deposited PMN–PT thin films has been investigated with X-ray diffraction (XRD). Optical transmission spectroscopy and Raman spectroscopy are used to characterize optical properties of the deposited PMN–PT thin films. The results show that the PMN–PT thin films of perovskite structure have been formed, and the crystalline and optical properties of the PMN–PT thin films can be improved as increasing the annealing temperature to 750 °C, but further increasing the annealing temperature to 950 °C may lead to a degradation of the crystallinity and the optical properties of the PMN–PT thin films. In addition, a weak second harmonic intensity (SHG) has been observed for the PMN–PT thin film formed at the optimum annealing temperature of 750 °C according to Maker fringe method. All these suggest that the annealing temperature has significant effect on the structural and optical properties of the PMN–PT thin films.     

Characteristics of ZnO:In thin films prepared by RF magnetron sputtering

In-doped ZnO (ZnO:In) transparent conductive thin films were deposited on glass substrates by RF magnetron sputtering. The effect of substrate temperature on the structural, electrical and optical properties of the ZnO:In thin films was investigated. It was found that higher temperature improves the crystallinity of the films and promotes In substitution easily. ZnO:In thin films with the best crystal quality were fabricated at 300 °C, which exhibit a larger grain size of 29 nm and small tensile strain of 0.9%. The transmittance of all the films was revealed to be over 85% in the visible range independence of the substrate temperatures and the lowest resistivity of ZnO:In thin films is 2.4×10⁻³ Ω cm.     

Photoluminescence studies of ZnO thin films on R-plane sapphire substrates grown by sol–gel method

Zinc oxide (ZnO) thin films on R-plane sapphire substrates were grown by the sol–gel spin-coating method. The optical properties of the ZnO thin films were investigated using photoluminescence. In the UV range, the asymmetric near-band-edge emission was observed at 300 K, which consisted of two emissions at 3.338 and 3.279 eV. Eight peaks at 3.418, 3.402, 3.360, 3.288, 3.216, 3.145, 3.074, and 3.004 eV, which respectively correspond to the free exciton (FX), bound exciton, transverse optical (TO) phonon replica of FX recombination, and first-order longitudinal optical phonon replica of FX and the TO (1LO+TO), 2LO+TO, 3LO+TO, 4LO+TO, and 5LO+TO, were obtained at 12 K. From the temperature-dependent PL, it was found that the emission peaks at 3.338 and 3.279 eV corresponded to the FX and TO, respectively. The activation energy of the FX and TO emission peaks was found to be about 39.3 and 28.9 meV, respectively. The values of the fitting parameters of Varshni's empirical equation were α=4×10^?3 eV/K and β=4.9×10³ K, and the S factor of the ZnO thin films was 0.658. With increasing temperature, the exciton radiative lifetime of the FX and TO emissions increased. The temperature-dependent variation of the exciton radiative lifetime for the TO emission was slightly higher than that for the FX emission.     

Preparation and characterization of highly conducting and transparent Al doped CdO thin films by pulsed laser deposition

Highly conducting and transparent aluminum doped CdO thin films were deposited using pulsed laser deposition technique. The effect of growth temperature on structural, electrical, and optical properties was studied. It is observed that the film orientation changes from preferred (1 1 1) plane to (2 0 0) plane with increase in growth temperature. The electrical resistivity of the films was found to increase with increase in growth temperature. The low resistivity of 4.3 × 10⁻⁵ Ω cm and high transparency (∼85%) was obtained for the film grown at 150 °C. The band gap of the films varies from 2.74 eV to 2.84 eV.     

Effect of laser incident energy on the structural,morphological and optical properties of Cu2ZnSnS4 (CZTS) thin films

The polycrystalline Cu₂ZnSnS₄ (CZTS) thin films have been prepared by pulsed laser deposition (PLD) method at room temperature. The laser incident energy was varied from 1.0 at the interval of 0.5–3.0 J/cm². The effect of laser incident energy on the structural, morphological and optical properties of CZTS thin films was studied by means of X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and optical absorption. The studies reveal that an improvement in the structural, morphological and optical properties of CZTS thin films with increasing laser incident energy up to 2.5 J/cm². However, when the laser incident energy was further increased to 3.0 J/cm², leads to degrade the structural, morphological and optical properties of the CZTS thin films.     

Photoluminescence of chemical solution-derived amorphous ZnO layers prepared by low-temperature process

Growth characteristic and optical properties of the amorphous ZnO thin films prepared on soda-lime–silica glass substrates by chemical solution process at 100 and 200 °C were investigated by using X-ray diffraction analysis, scanning probe microscope, ultraviolet spectrophotometer, and photoluminescence. The films exhibited an amorphous pattern even when finally heat treated at 100–200 °C for 60 min. The photoluminescence spectrum of amorphous ZnO films shows a strong near-band-edge emission, while the visible emission is nearly quenched.     

Effect of phosphorus irradiation on the structural,electrical, and optical characteristics of ZnO thin films

Phosphorus irradiation at a low energy (50 keV) and at a dosage of 8×10¹⁴ ions/cm² was carried out on 〈002〉 ZnO films grown by using a pulsed laser deposition technique (Sample A). Subsequent rapid thermal annealing at 650 °C and 750 °C was performed to remove defects resulting from the irradiation (samples B and C, respectively). Atomic force microscopy was used to determine the root mean square roughness, which was 10.07, 8.66, and 9.31 nm for samples A, B, and C, respectively. Low-temperature photoluminescence measurements revealed increased deep-level defect peaks following irradiation; however, the subsequent annealing minimized the defects. Although the dominant donor-bound exciton peak verifies the n-type conductivity of the films, the free–electron–to–acceptor and donor-to-acceptor pair peaks in the irradiated samples confirm an increase in acceptor concentration.     

Structural and optical properties of Mn-doped ZnO nanocrystalline thin films with the different dopant concentrations

The transparent nanocrystalline thin films of undoped zinc oxide and Mn-doped (Zn_1−xMn_xO) have been deposited on glass substrates via the sol–gel technique using zinc acetate dehydrate and manganese chloride as precursor. The as-deposited films with the different manganese compositions in the range of 2.5–20 at% were pre-heated at 100 °C for 1 h and 200 °C for 2 h, respectively, and then crystallized in air at 560 °C for 2 h. The structural properties and morphologies of the undoped and doped ZnO thin films have been investigated. X-ray diffraction (XRD) spectra, scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) were used to examine the morphology and microstructure of the thin films. Optical properties of the thin films were determined by photoluminescence (PL) and UV/Vis spectroscopy. The analyzed results indicates that the obtained films are of good crystal quality and have smooth surfaces, which have a pure hexagonal wurtzite ZnO structure without any Mn related phases. Room temperature photoluminescence is observed for the ZnO and Mn-doped ZnO thin films.     

High quality nitrogen-doped zinc oxide thin films grown on ITO by sol–gel method

Highly transparent N-doped ZnO thin films were deposited on ITO coated corning glass substrate by sol–gel method. Ammonium nitrate was used as a dopant source of N with varying the doping concentration 0, 0.5, 1.0, 2.0 and 3.0 at%. The DSC analysis of prepared NZO sols is observed a phase transition at 150 °C. X-ray diffraction pattern showed the preferred (002) peak of ZnO, which was deteriorated with increased N concentrations. The transmittance of NZO thin films was observed to be ~88%. The bandgap of NZO thin films increased from 3.28 to 3.70 eV with increased N concentration from 0 to 3 at%. The maximum carrier concentration 8.36×10¹⁷ cm⁻³ and minimum resistivity 1.64 Ω cm was observed for 3 at% N doped ZnO thin films deposited on glass substrate. These highly transparent ZnO thin films can be used as a window layer in solar cells and optoelectronic devices.     

Phase growth control in low temperature PLD Co: TiO2 films by pressure

This paper reports on the structural and optical properties of Co-doped TiO₂ thin films grown onto (0001)Al₂O₃ substrates by non-reactive pulsed laser deposition (PLD) using argon as buffer gas. It is shown that by keeping constant the substrate temperature at as low as 310 °C and varying only the background gas pressure between 7 Pa and 70 Pa, it is possible to grow either epitaxial rutile or pure anatase thin films, as well as films with a mixture of both polymorphs. The optical band gaps of the films are red shifted in comparison with the values usually reported for undoped TiO₂, which is consistent with n-type doping of the TiO₂ matrix. Such band gap red shift brings the absorption edge of the Co-doped TiO₂ films into the visible region, which might favour their photocatalytic activity. Furthermore, the band gap red shift depends on the films’ phase composition, increasing with the increase of the Urbach energy for increasing rutile content.     

Growth and characterization of indium oxide films

In₂O₃ films have been deposited using chemical spray pyrolysis technique at different substrate temperatures that varied in the range, 250–450 °C. The structural and morphological properties of the as-deposited films were studied using X-ray diffractometer and scanning electron microscope as well as atomic force microscope, respectively. The films formed at a temperature of 400 °C showed body-centered cubic structure with a strong (2 2 2) orientation. The structural parameters such as the crystallite size, lattice strain and texture coefficient of the films were also calculated. The films deposited at a temperature of 400 °C showed an optical transmittance of >85% in the visible region. The change of resistivity, mobility, carrier concentration and activation energies with the deposition temperature was studied. The highest figure of merit for the layers grown at 400 °C was 1.09 × 10⁻³ Ω⁻¹.     

Effect of electron beam on structural,linear and nonlinear properties of nanostructured Fluorine doped ZnO thin films

Electron beam induced effects on Fluorine doped ZnO thin films (FZO) grown by chemical spray pyrolysis deposition technique were studied. The samples were exposed to 8 MeV electron beam at different dose rate ranging from 1 kGy to 4 kGy. All films exhibit a polycrystalline nature which shows an increase in crystallanity with irradiation dosages. The electron beam irradiation effectively controls the films surface morphology and its linear optical characteristics. Z-Scan technique was employed to evaluate the sign and magnitude of nonlinear refractive index and nonlinear absorption coefficient using a continuous wave laser at 632.8 nm as light source. Enhancement in the third order nonlinear optical properties was were noted due to electron beam irradiation. Tailoring the physical and NLO properties by electron beam, the FZO thin films becomes a promising candidate for various optoelectronic applications such as phase change memory devices, optical pulse compression, optical switching and laser pulse narrowing.     

ArF excimer laser deposition of wide-band gap solid electrolytes for thin film batteries

High quality solid electrolyte thin films was grown by pulsed laser deposition (PLD) using a high photon energy ArF excimer laser. Various amorphous thin films were successfully deposited on glass substrates from oxide targets; such as Li₃PO₄, LiBO₂, Li₂SiO₃, Li₂CO₃, Li₂SO₄, Li₂ZrO₃, LiAlO₂, Li₂WO₄ and Ohara glass ceramics. The morphology, optical property and ionic conductivity of these films were examined by optical microscope, UV–VIS spectroscopy and impedance analysis. Dramatic improvement of the film morphology was observed by using a high photon energy laser, while the broken film with many droplets was obtained by using lower ones. Ionic conductivity of the films was examined by impedance spectroscopy and dc polarization method. For example, an ionic conductivity of a Li₃PO₄ film was 4.6 × 10^? 6 S cm^? 1 at 25 °C with activation energy of 0.57 eV. Electronic conductivity measurements revealed that most of the films were pure lithium ion conductors, while a Li₂WO₄ film was a mixed conductor.     

Structural,electrical and optical properties of sol–gel AZO thin films

Transparent conductive Al-doped zinc oxide (AZO) thin films were prepared by a sol–gel method and their structural, electrical and optical properties were systematically investigated. A minimum resistivity of 4.2 × 10⁻³ Ω cm was obtained for the 650 °C-annealed films doped with 1.0 at.% Al. All films had the preferential c-axis oriented texture according to the X-ray diffraction (XRD) results. Optical transmittance spectra of the films showed a high transmittance of over 85% in the visible region and the optical band gap of the AZO films broadened with increasing doping concentration.     

The growth of ZnO:Ga:Cu as new TCO film of advanced electrical,optical and structural quality

Because of having similarities in many physical as well as chemical properties to those of Zn, Cu has been strategically used as an effective dopant e.g., Al, Ga, F, etc., to change the optical, electrical and the micro-structural properties of ZnO thin films for obtaining its favorable opto-electronic performance as a transparent conducting oxide suitable for devices. Present study demonstrates the growth of transparent conducting ZnO:Ga:Cu thin films, by low power RF magnetron sputtering at a low substrate temperature (100 °C). Highly crystalline ZnO:Ga:Cu film with preferred c-axis orientation has been obtained demonstrating a high magnitude of transmission ~85% in the visible range and a high electrical conductivity ~40 S cm^–1, facilitated by large crystallite size (~29 nm), introducing reduced grain boundary scattering. XPS O 1S spectrum reveals the presence of a significant fraction of oxygen atoms effectively increasing the optical transparency. Incorporation of Ga and Cu ions into the ZnO matrix promotes violation of the local translational symmetry as suggested by the relaxation of Raman selection rules for the network, evident by the presence of strong (B₁^high–B₁^low) modes which are typically Raman inactive. The consequences of Cu doping has been compared with identically prepared ZnO and ZnO:Ga films.     

Temperature dependent photoluminescence processes in ZnO thin films grown on sapphire by pulsed laser deposition

Temperature dependence of the photoluminescence (PL) transitions in the range of 10–300 K was studied for ZnO thin films grown on sapphire by pulsed laser deposition. The low temperature PL spectra were dominated by recombination of donor bound excitons (B_X) and their phonon replicas. With increasing temperature, free exciton (F_X) PL and the associated LO phonon replicas increased in intensity at the expense of their bound counterparts. The B_X peak with line width of ∼6 meV at 10 K exhibited thermal activation energy of ∼17 meV, consistent with the exciton-defect binding energy. The separation between the F_X and B_X peak positions was found to reduce with increasing temperature, which was attributed to the transformation of B_X into the shallower donor bound exciton complexes at consecutive lower energy states with increasing temperature, which are possible in ZnO. The energy separation between F_X peak and its corresponding 1-LO phonon replica showed stronger dependence on temperature than that of 2-LO phonon replica. However, their bound counterparts did not exhibit this behavior. The observed temperature dependence of the energy separation between the free exciton and it is LO phonon replicas are explained by considering the kinetic energy of free exciton. The observed PL transitions and their temperature dependence are consistent with observations made with bulk ZnO crystals implying high crystalline and optical quality of the grown films.     

Adsorption properties of Mg–Al layered double hydroxides thin films grown by laser based techniques

Powdered layered double hydroxides (LDHs) have been widely studied due to their applications as catalysts, anionic exchangers or host materials for inorganic and/or organic molecules. Assembling nano-sized LDHs onto flat solid substrates forming thin films is an expanding area of research due to the prospects of novel applications as sensors, corrosion-resistant coatings, components in optical and magnetic devices.Continuous and adherent thin films were grown by laser techniques (pulsed laser deposition – PLD and matrix assisted pulsed laser evaporation – MAPLE) starting from targets of Mg–Al LDHs. The capacity of the grown thin films to retain a metal (Ni) from contaminated water has been also explored. The thin films were immersed in an Ni(NO₃)₂ aqueous solutions with Ni concentrations of 10^?3% (w/w) (1 g/L) and 10^?4% (w/w) (0.1 g/L), respectively. X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) combined with energy dispersive X-ray analysis (EDX) were the techniques used to characterize the prepared materials.