Room temperature visible light emission from Si/SiO2 multilayers: Roles of interface electronic states and silicon phase

We have studied luminescence properties and microstructure of 20 patterns Si/SiO₂ multilayers. The photoluminescence spectra consist of two gaussian bands in the visible-infrared spectral region. It has been demonstrated that the strong PL band is caused by the radiative recombination in the Si/SiO₂ interfaces states, whereas the weaker band originates from radiative recombination in the nanosized Si layers. The peak shift of this latter band shows a discontinuity that corresponds to a crystalline-to-amorphous phase change when the Si layers are thinner than 30 Å. The peak energy as a function of the layer thickness is interpreted using a quantum confinement model in the case of amorphous Si layers.     

SiO2/Si衬底上石墨烯的制备与结构表征

在分子束外延(MBE)设备中,利用直接沉积C原子的方法在覆盖有SiO₂的Si衬底(SiO₂/Si)上生长石墨烯,并通过Raman光谱和近边X射线吸收精细结构谱等实验技术对不同衬底温度(500℃,600℃,700℃,900℃,1100℃,1200℃)生长的薄膜进行结构表征.实验结果表明,在衬底温度较低时生长的薄膜是无定形碳,在衬底温度高于700℃时薄膜具有石墨烯的特征,而且石墨烯的结晶质量随着衬底温度的升高而改善,但过高的衬底温度会使石墨烯质量降低.衬底温度为1100℃时结晶质量最好.衬底温度较低时C原子活性较低,难以形成有序的C-sp²六方环.而衬底温度过高时(1200℃),衬底表面部分SiO₂分解,C原子与表面的Si原子或者O原子结合而阻止石墨烯的形成,并产生表面缺陷导致石墨烯结晶变差.     

Preparation and characterization of novel Pd/SiO2 and Ca-Pd/SiO2 egg-shell catalysts with porous hollow silica

Novel egg-shell structured monometallic Pd/SiO₂ and bimetallic Ca-Pd/SiO₂ catalysts were prepared by an impregnation method using porous hollow silica (PHS) as the support and PdCl₂ and Ca(NO₃)₂·4H₂O as the precursors. It was found from transmission electron microscope (TEM), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) that Pd was loaded on PHS with a particle size of 5-12 nm in Pd/SiO₂ samples and the Pd particle size in Ca-Pd/SiO₂ was smaller than that in Pd/SiO₂ since Ca could prevent Pd particles from aggregating. X-ray photoelectron spectroscopy (XPS) analyses exhibited that Pd 3d_5/2 binding energies of Pd/SiO₂ and Ca-Pd/SiO₂ were 0.2 and 0.9 eV lower than that of bulk Pd, respectively, as a result of the shift of the electron cloud from Pd to oxygen in Pd/SiO₂ and to both oxygen and Ca in Ca-Pd/SiO₂. The activity of Ca-Pd/SiO₂ egg-shell catalyst for CO hydrogenation and the selectivity to methanol, with a value of 36.50 mmol_CO mol⁻¹_Pd s⁻¹ and 100%, respectively, were much higher than those of the catalysts prepared with traditional silica gel as the support, owing to the porous core-shell structure of the PHS support.     

Electroluminescence from Si／SiO2 films deposited on p—Si substrates

The structure of Au/Si/SiO₂/p-Si has been fabricated using the magnetron sputtering technique. It has a very good rectifying behaviour. Visible electroluminescence (EL) has been observed from the Au/Si/SiO₂/p-Si structure at a forward bias of 5V or larger. A broad band with one peak around 650－660 nm appears in all the EL spectra of the structure. The effects of the thickness of the Si layer in the Si/SiO₂ films and of the input electrical power on EL spectra are studied systematically.     

Structural and optical properties of Si/SiO2 multi-quantum wells

Structural and optical properties of Si/SiO₂ multi-quantum wells (MQW) were investigated by means of Raman scattering and photoluminescence (PL) spectroscopy. The MQW structures were fabricated on a quartz substrate by remote plasma enhanced chemical vapour deposition (RPECVD) of alternating amorphous Si and SiO₂ layers. After layer deposition the samples were subjected to heat treatments, i.e. rapid thermal annealing (RTA) and furnace annealing. Distinct PL signatures of confined carriers evidenced formation of Si-nanocrystals (nc-Si) in annealed samples. Analyses of Raman spectra also show presence of nc-Si phase along with amorphous-Si (a-Si) phase in the samples. The strong influence of the annealing parameters on the formation of nc-Si phase suggests broad possibilities in engineering MQW with various optical properties. Interestingly, conversion of the a-Si phase to the nc-Si phase saturates after certain time of furnace annealing. On the other hand, thinner Si layers showed a disproportionately lower crystalline volume fraction. From the obtained results we could assume that an interface strain prevents full crystallization of the Si layers and that the strain is larger for thinner Si layers. The anomalous dependence of nc-Si Raman scattering peak position on deposited layer thickness observed in our experiments also supports the above assumption.     

First-principles study of the segregation of boron dopants near the interface between crystalline Si and amorphous SiO2

We investigate the stability of boron dopants near the interface between crystalline Si and amorphous SiO₂ through first-principles density functional calculations. An interstitial B is found to be more stable in amorphous SiO₂ than in Si, so that B dopants tend to segregate to the interface. When defects exist in amorphous SiO₂, the stability of B is greatly enhanced, especially around Si floating bond defects, while it is not significantly affected near Si–Si dimers, which are formed by O-vacancy defects.     

Suppression of boron segregation by interface Ge atoms at SiGe/SiO2 interface

We investigate the migration pathway and barrier for B diffusion at SiGe/SiO₂ interface through first-principles density functional calculations. Similar to the diffusion mechanism reported for Si/SiO₂ interface, a substitutional B, which initially forms a B-self-interstitial complex in SiGe, diffuses to the interface and then to the oxide in form of an interstitial B. At the defect-free interface, where bridging O atoms are inserted to remove interface dangling bonds, it is energetically more favorable for the interstitial B to intervene in the Ge–O bridge bond rather than the Si–O bridge bond at the interface. As a result of the B intervention, interface Ge atoms significantly enhance the stability of B-related defects in the interface region and thereby act as traps for B dopants. At the interface with the Ge–O bridge bond, the overall migration barrier for B diffusion from SiGe to SiO₂ is estimated to be about 3.7 eV, much higher than the reported value of about 2.1 eV at Si/SiO₂ interface. Our results provide a clue to understanding the experimental observation that B segregation toward the oxide is suppressed in SiGe/SiO₂ interface.     

Further indication of a low quartz structure at the SiO2/Si interface from coincidence Doppler broadening spectroscopy

Results from coincidence Doppler broadening (CDB) measurements on various Si samples and Brazilian quartz having low quartz structure are presented with the aim to give further strong indication of the existence of a low quartz structure, but not of Si divacancies as frequently considered, at the SiO₂/Si interface.     

Si/SiO2 multilayers: synthesis by reactive magnetron sputtering and photoluminescence emission

This paper relates a complete study of Si/SiO₂ multilayer (ML) structures. First, we suggest an original way of synthesis based on reactive magnetron sputtering of a pure silica target. The photoluminescence spectra of these MLs consist of two Gaussian bands in the visible-near infrared spectral region. The stronger one (I band) is fixed at about 780 nm and probably due to interface states. The weaker one (Q band) is tuneable with the Si sublayer thickness and originates from a radiative recombination within the nanosized Si layers. For this latter band the peak position is a function of the Si sublayer thickness and shows a discontinuity at 30 Å. This corresponds to an Si phase change. For thicknesses above 30 Å, the sublayers are composed of nanocrystalline silicon whereas below 30 Å the sublayers are made of amorphous silicon. We develop a model based on a quantum well to which we have added an interfacial region between Si and SiO₂. It is characterised by an interfacial potential of 0.3 eV. This model depicts the simultaneous behaviour of Q and I bands for an Si sublayer thickness below 30 Å.     

XPS investigation of diffusion of two-layer ZrO2/SiO2 and SiO2/ZrO2 sol–gel films

Two-layer ZrO₂/SiO₂ and SiO₂/ZrO₂ films were deposited on K9 glass substrates by sol–gel dip coating method. X-ray photoelectron spectroscopy (XPS) technique was used to investigate the diffusion of ZrO₂/SiO₂ and SiO₂/ZrO₂ films. To explain the difference of diffusion between ZrO₂/SiO₂ and SiO₂/ZrO₂ films, porous ratio and surface morphology of monolayer SiO₂ and ZrO₂ films were analyzed by using ellipsometry and atomic force microscopy (AFM). We found that for the ZrO₂/SiO₂ films there was a diffusion layer with a certain thickness and the atomic concentrations of Si and Zr changed rapidly; for the SiO₂/ZrO₂ films, the atomic concentrations of Si and Zr changed relatively slowly, and the ZrO₂ layer had diffused through the entire SiO₂ layer. The difference of diffusion between ZrO₂/SiO₂ and SiO₂/ZrO₂ films was influenced by the microstructure of SiO₂ and ZrO₂.     

Influence of Si/SiO2 interface properties on electrical performance and breakdown characteristics of ultrathin stacked oxide/nitride dielectric films

In this work, the influence of Si/SiO₂ interface properties, interface nitridation and remote-plasma-assisted oxidation (RPAO) thickness (<1 nm), on electrical performance and TDDB characteristics of sub-2 nm stacked oxide/nitride gate dielectrics has been investigated using a constant voltage stress (CVS). It is demonstrated that interfacial plasma nitridation improves the breakdown and electrical characteristics. In the case of PMOSFETs stressed in accumulation, interface nitridation suppresses the hole traps at the Si/SiO₂ interface evidenced by less negative V_t shifts. Interface nitridation also retards hole tunneling between the gate and drain, resulting in reduced off-state drain leakage. In addition, the RPAO thickness of stacked gate dielectrics shows a profound effect in device performance and TDDB reliability. Also, it is demonstrated that TDDB characteristics are improved for both PMOS and NMOS devices with the 0.6 nm-RPAO layer using Weibull analysis. The maximum operating voltage is projected to be improved by 0.3 V difference for a 10-year lifetime. However, physical breakdown mechanism and effective defect radius during stress appear to be independent of RPAO thickness from the observation of the Weibull slopes. A correlation between trap generation and dielectric thickness changes based on the C-V distortion and oxide thinning model is presented to clarify the trapping behavior in the RPAO and bulk nitride layer during CVS stress.     

Anneal temperature dependence of Si/SiO2 superlattices photoluminescence

Photoluminescence spectroscopy, Fourier transform infrared spectroscopy, X-ray reflectometry and high resolution electron microscopy have been used to interpret the photoluminescence properties of annealed (3/19 nm) Si/SiO₂ multilayers grown by reactive magnetron sputtering. The multilayers show an emission in the visible and near-infrared range after heat treatment from 900°C which tends to decrease from 1200°C. Three different origins for the photoluminescence activity have been found. An anneal temperature of 1200°C is necessary to optimise the silicon crystallisation within the silicon sublayers.     

Effect of laser annealing on crystallinity of the Si layers in Si/SiO2 multiple quantum wells

We report on continuous-wave laser induced crystallisation processes occurring in Si/SiO₂ multiple quantum wells (MQW), prepared by remote plasma enhanced chemical vapour deposition of amorphous Si and SiO₂ layers on quartz substrates. The size and the volume fraction of the Si nanocrystals in the layers were estimated employing micro-Raman spectroscopy. It was found that several processes occur in the Si/SiO₂ MQW system upon laser treatment, i.e. amorphous to nanocrystalline conversion, Si oxidation and dissolution of the nanocrystals. The speed of these processes depends on laser power density and the wavelength, as well as on the thickness of Si-rich layers. At optimal laser annealing conditions, it was possible to achieve ∼100% crystallinity for 3, 5 and 10 nm thickness of deposited amorphous Si layers. Crystallization induced variation of the light absorption in the layers can explain the complicated process of Si nanocrystals formation during the laser treatment.     

Preparation and characterization of amine-functionalized SiO2/TiO2 films for formaldehyde degradation

This paper investigated the gaseous formaldehyde degradation by the amine-functionalized SiO₂/TiO₂ photocatalytic films for improving indoor air quality. The films were synthesized via the co-condensation reaction of methyltrimethoxysilane (MTMOS) and 3-aminopropyltrimethoxysilane (APTMS). The physicochemical properties of prepared photocatalysts were characterized with N₂ adsorption/desorption isotherms measurement, X-ray diffraction (XRD) and Fourier Transform Infrared spectroscopy (FT/IR). The effect of amine-functional groups and the ratio of MTMOS/APTMS precursors on the formaldehyde adsorption and photocatalytic degradation were investigated. The results showed that the formaldehyde adsorption and photocatalytic degradation of the APTMS-functionalized SiO₂/TiO₂ film was higher than that of SiO₂/TiO₂ film due to the surface adsorption on amine sites and the relatively high of the specific surface area of the APTMS-functionalized SiO₂/TiO₂ film (15 times higher than SiO₂/TiO₂). The enhancement of the formaldehyde degradation of the film can be attributed to the synergetic effect of adsorption and subsequent photocatalytic decomposition. The repeatability of photocatalytic film was also tested and the degradation efficiency was 91.0% of initial efficiency after seven cycles.     

Preparation and characterization of SiO2/ZrO2/Ag multicoated microspheres

A new type of multicoated silica/zirconia/silver (SiO₂/ZrO₂/Ag) core-shell composite microspheres is synthesized in this paper. In the process, ZrO₂-decorated silica (SiO₂/ZrO₂) core-shell composites were firstly fabricated by the modification of zirconia on silica microspheres through the hydrolysis of zirconium precursor. Subsequently, on SiO₂/ZrO₂ composite cores, silver nanoparticles were introduced via ultrasonic irradiation and acted as “Ag seeds” for the formation of integrate silver shell by further reduction of silver ions using formaldehyde as reducer. The resulting samples were characterized by transmission electron microscopy, X-ray diffraction, Fourier-transform infrared, energy-dispersive X-ray, and UV-vis spectroscopy, indicating that zirconia and silver layers were successfully coated on the surfaces of silica microspheres.     

Influence of patterning on the nucleation of Ge islands on Si and SiO2 surfaces

Surface patterning is expected to influence the nucleation site of deposited nanostructures. In the present study, clean Si and SiO₂ surfaces were patterned by a nanolithographic process using a Focused Ion Beam (FIB). Ge was evaporated in ultra high vacuum at 873 K on these substrates, resulting in the formation of island arrays. Based on scanning tunneling microscopy and atomic force microscopy images, a statistical analysis was performed in order to highlight the effect of patterning on the size distribution of islands compared to a non-patterned surface. We find that the self-organization mechanism on patterned substrates results in a very good arrangement and positioning of Ge nanostructures, depending on growth conditions and holes distance, both on Si and SiO₂ surfaces.     

Silicon nanoparticles formation in annealed SiO/SiO2 multilayers

We present a study on amorphous SiO/SiO₂ superlattice performed by grazing-incidence small-angle X-ray scattering (GISAXS). Amorphous SiO/SiO₂ superlattices were prepared by high-vacuum evaporation of 3 nm thin films of SiO and SiO₂ (10 layers each) onto Si(1 0 0) substrate. After the deposition, samples were annealed at 1100 °C for 1 h in vacuum, yielding to Si nanocrystals formation. Using a Guinier approximation, the shape and the size of the crystals were obtained. The size of the growing nanoparticles in the direction perpendicular to the film surface is well controlled by the bilayer thickness. However, their size varies more significantly in the direction parallel to the film surface.     

Ag-Au合金/SiO$lt;sub$gt;2$lt;/sub$gt;复合薄膜的制备与表征

以AgNO₃,HAuCl₄和正硅酸乙酯为主要原料,利用溶胶-凝胶法和旋涂技术,通过热处理和紫外光辐射还原得到了不同n_Ag/n_Au（1∶0,2∶1,1∶2,0∶1）的Ag-Au合金/SiO₂复合薄膜.从扫描电子显微镜和X射线衍射谱的结果可以看出得到的薄膜均匀性好,复合薄膜中合金颗粒的尺寸为10 nm左右.利用紫外-可见分光光谱仪研究了复合薄膜的光吸收性能,结果表明,随着n_Ag/n_Au的降低,吸收峰的位置也由最初的Ag纳米粒子的等离子共振吸收峰430 nm附近,逐渐红移到Au纳米粒子的等离子共振吸收峰605和880 nm附近.从光吸收谱可以看出,n_Ag∶n_Au＝2∶1和1∶2的两个样品分别在515,730 nm附近和550,730 nm附近出现表面等离子共振吸收峰.这表明Au-Ag合金固溶体的形成. 关键词： 2')" href="#">Ag-Au合金/SiO₂ 紫外辐射 光吸收性能     

The effect of Si surface nitridation on the interfacial structure and electrical properties of (La2O3)0.5(SiO2)0.5 high-k gate dielectric films

Thermal stability, interfacial structures and electrical properties of amorphous (La₂O₃)_0.5(SiO₂)_0.5 (LSO) films deposited by using pulsed laser deposition (PLD) on Si (1 0 0) and NH₃ nitrided Si (1 0 0) substrates were comparatively investigated. The LSO films keep the amorphous state up to a high annealing temperature of 900 °C. HRTEM observations and XPS analyses showed that the surface nitridation of silicon wafer using NH₃ can result in the formation of the passivation layer, which effectively suppresses the excessive growth of the interfacial layer between LSO film and silicon wafer after high-temperature annealing process. The Pt/LSO/nitrided Si capacitors annealed at high temperature exhibit smaller CET and EOT, a less flatband voltage shift, a negligible hysteresis loop, a smaller equivalent dielectric charge density, and a much lower gate leakage current density as compared with that of the Pt/LSO/Si capacitors without Si surface nitridation.     

Immobilization of glucose oxidase using CoFe2O4/SiO2 nanoparticles as carrier

Aminated-CoFe₂O₄/SiO₂ magnetic nanoparticles (NPs) were prepared from primary silica particles using modified StÖber method. Glucose oxidase (GOD) was immobilized on CoFe₂O₄/SiO₂ NPs via cross-linking with glutaraldehyde (GA). The optimal immobilization condition was achieved with 1% (v/v) GA, cross-linking time of 3 h, solution pH of 7.0 and 0.4 mg GOD (in 3.0 mg carrier). The immobilized GOD showed maximal catalytic activity at pH 6.5 and 40 °C. After immobilization, the GOD exhibited improved thermal, storage and operation stability. The immobilized GOD still maintained 80% of its initial activity after the incubation at 50 °C for 25 min, whereas free enzyme had only 20% of initial activity after the same incubation. After kept at 4 °C for 28 days, the immobilized and free enzyme retained 87% and 40% of initial activity, respectively. The immobilized GOD maintained approximately 57% of initial activity after reused 7 times. The K_M (Michaelis-Menten constant) values for immobilized GOD and free GOD were 14.6 mM and 27.1 mM, respectively.