Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Theoretical study of the triplet excited state of PtPOP and the exciplexes M-PtPOP (M = Tl, Ag) in solution and comparison with ultrafast X-ray scattering results

The [Pt₂(H₂P₂O₅)₄]⁴⁻ ions in the ground and excited states and the excited-state complexes M-[Pt₂(H₂P₂O₅)₄]³⁻ and M₂-[Pt₂(H₂P₂O₅)₄]²⁻ (M = Ag, Tl) were studied in solution with various density functional theory (DFT) functionals from Gaussian 09 and Amsterdam Density Functional (ADF) programs. Calculated results were compared with ultrafast X-ray solution scattering data. Time dependent DFT (TD-DFT) calculations with the B3PW91 functional and unrestricted open shell calculations with the mPBE functional produce good agreement with the experimental results. Compared to gas phase calculations, the surrounding solvent is found to play an important role to shorten the Pt-Pt and M-Pt (M = Ag, Tl) bond lengths, lowering the molecular orbital energies and influences the molecular orbital transitions upon excitation, which stabilizes the excited transient molecules in solution.     

Investigation on The Thermal Properties of Fe2O(SO4)2. Part II

Fe₂O(SO₄)₂ is a secondary product of the decomposition of FeSO₄⋅H₂O. Part I of this study presents results on the synthesis of Fe₂O(SO₄)₂ in gaseous environment containing either low or high concentration of oxygen. In this paper the existence of differences between the structures of Fe₂O(SO₄)₂ and Fe₂(SO₄)₃ is proved on the basis of a detailed thermal study of Fe₂O(SO₄)₂ upon dynamic heating (differential thermal analysis) and upon isothermal heating (thermal-analytic balance) in various gaseous environments as well as by presenting kinetic data on the processes of decomposition of both compounds. This revised version was published online in July 2006 with corrections to the Cover Date.     

Syntheses and characterization of two oxoborates, (Pb3O)2(BO3)2MO4 (M=Cr, Mo)

Two oxoborates, (Pb₃O)₂(BO₃)₂MO₄ (M=Cr, Mo), have been prepared by solid-state reactions below 700 °C. Single-crystal XRD analyses showed that the Cr compound crystallizes in the orthorhombic group Pnma with a=6.4160(13) Å, b=11.635(2) Å, c=18.164(4) Å, Z=4 and the Mo analog in the group Cmcm with a=18.446(4) Å, b=6.3557(13) Å, c=11.657(2) Å, Z=4. Both compounds are characterized by one-dimensional chains formed by corner-sharing OPb₄ tetrahedra. BO₃ and CrO₄ (MoO₄) groups are located around the chains to hold them together via Pb–O bonds. The IR spectra further confirmed the presence of BO₃ groups in both structures and UV–vis diffuse reflectance spectra showed band gaps of about 1.8 and 2.9 eV for the Cr and Mo compounds, respectively. Band structure calculations indicated that (Pb₃O)₂(BO₃)₂MoO₄ is a direct semiconductor with the calculated energy gap of about 2.4 eV.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

M5(PO4)3F (M=Ca, Sr, Ba)中Sm3+的电荷迁移态及Sm3+和Eu3+的电荷迁移能量关系

采用高温固相反应合成了M_5-2xSm_xNa_x(PO₄)₃F(M=Ca,Sr,Ba)荧光体,研究了其在真空紫外-可见光范围的发光特性。发现在Ca₅(PO₄)₃F中Sm³⁺的电荷迁移带约在191 nm,在Sr₅(PO₄)₃F中约在199 nm,而在Ba₅(PO₄)₃F中约在204 nm,随着被取代碱土离子半径的增大电荷迁移能量逐渐减小。比较了M₅(PO₄)₃F (M=Ca,Sr,Ba)中Sm³⁺和Eu³⁺电荷迁移能量的关系。     

Gases Released During the Conversion of NH4Zr2(PO4)3 to HZr2(PO4)3

Gases released during the conversion of NH₄Zr₂(PO₄)₃ to HZr₂(PO₄)₃ were identified using an apparatus in which gases released from a sample placed in a thermogravimetric analyzer were directly introduced to a gas cell of an IR spectrometer. Such acidic gases as N₂O and NO were detected besides the basic NH₃ gas, and their formation mechanism was discussed.This revised version was published online in November 2005 with corrections to the Cover Date.     

Solid-solid interactions in pure and Li2O-doped manganese and magnesium mixed oxides system

The solid-solid interactions between manganese and magnesium oxides in absence and in presence of small amounts of Li₂O have been investigated. The molar ratios between manganese and magnesium oxides in the form of Mn₂O₃ and MgO were varied between 0.05:1 to 0.5:1. The mixed solids were calcined in air at 400-1000°C. The techniques employed were DTA, XRD and H₂O₂ decomposition at 20-40°C.The results obtained revealed that solid-solid interactions took place between the reacting solids at 600-1000°C yielding magnesium manganates (Mg₂MnO₄, Mg₆MnO₈, MgMnO₄ besides unreacted portions of MgO, Mn₂O₃ and Mn₃O₄). Li₂O-doping (0.75-6 mol%) of the investigated system followed by calcination at 600 and 800°C decreased progressively the intensity of the diffraction lines of Mn₂O₃ (Bixbyite) with subsequent increase in the lattice parameter 'a' of MgO to an extent proportional to the amount of Li₂O added. This finding might suggest that the doping process enhanced the dissolution of Mn₂O₃ in MgO forming solid solution. This treatment led also to the formation of Li₂MnO₃. Furthermore, the doping with 3 and 6 mol% Li₂O conducted at 800°C resulted in the conversion of Mn₂O₃ into Mn₃O₄, a process that took place at 1000°C in absence of Li₂O. The produced Li₂MnO₃ phase remained stable by heating at up to 1000°C. Furthermore, Li₂O doping of the investigated system at 400-1000°C resulted in a progressive measurable increase in the particle size of MgO.The catalytic activity measurements showed that the increase in the molar ratio of Mn₂O₃ in the samples precalcined at 400-800°C was accompanied by a significant increase in the catalytic activity of the treated solids. The maximum increase in the catalytic activity expressed as reaction rate constant measured at 20°C (k _20°C) attained 3.14, 2.67 and 3.25-fold for the solids precalcined at 400, 600 and 800°C, respectively. Li₂O-doping of the samples having the formula 0.1 Mn₂O₃/MgO conducted at 400-600°C brought a progressive significant increase in its catalytic activity. The maximum increase in the value of k _20°C due to Li₂O attained 1.93 and 2.75-fold for the samples preheated at 400 and 600°C, respectively and opposite effect was found for the doped samples preheated at 800°C.This revised version was published online in November 2005 with corrections to the Cover Date.     

Interaction Between Two Similar Plane Parallel Double Layers for (NH4)2Fe(SO4)2 or (NH4)2Cu(SO4)2 Type Complex Salt Electrolytes at Positive Surface Potential

Interaction energies between two similar plane parallel double layers for (NH₄)₂Fe(SO₄)₂ or (NH₄)₂Cu(SO₄)₂ type complex salt electrolytes at positive surface potential were expanded in a power series and accurate numeral results were given for 0.1 ≤ y _e  < y ₀ ≤ 20. The general expressions were given for the interaction energies of A _ν +B _ν′ +C_ν? type complex salt electrolytes at y > 0. The interaction energies for simple salts NaCl, CaCl₂, Na₂SO₄, FeCl₃, Na₃PO₄, Mg₃(PO₄)₂, Al₂(SO₄)₃, and complex salts (NH₄)₂Fe(SO₄)₂ or (NH₄)₂Cu(SO₄)₂ at y ₀ = 1 were compared. There was hardly difference between these simple salts and this complex salt for the interaction energies. The interaction energy for complex salt (NH₄)₂Fe(SO₄)₂ was close to that for simple salt Na₃PO₄.

Supplemental files are available for this article. Go to the publisher's online edition of the Journal of Dispersion Science and Technology to view the free supplemental file.     

Near infrared study of aqueous lanthanide perchlorates

The near infrared spectra of water in aqueous solutions of La(ClO₄)₃, Pr(ClO₄)₃, Nd(ClO₄)₃, Gd(ClO₄)₃, Er(ClO₄)₃, Yb(ClO₄)₃, Lu(ClO₄)₃, and NaClO₄ have been measured in the concentration range from 0.3 to 2.5 mol-dm^–3, at 25°C. The relative contents of free OH groups in the 1.0, 1.6, and 2.2M solutions have been calculated from extinction coefficients for water at 1160 nm. They increase with increasing salt concentration and are greater in solutions of the lighter lanthanide perchlorates at any fixed molarity. The results are discussed in terms of the stoichiometry and structure of hydrated cations of trivalent lanthanides.     

Synthesis of o-LiMnO2 by Microwave Irradiation and StudyIts Heat Treatment and Lithium Exchange

Microwave irradiation of a suspension of γ-MnOOH in a 4 mol dm⁻³ LiOH solution brought about a rapid formation of semicrystalline orthorhombic LiMnO₂ (o-LiMnO₂) within 30 min at 120°C. Cubic Li_1.6Mn_1.6O₄ was obtained by heating o-LiMnO₂ at 400°C; lithium could be topotactically extracted from Li_1.6Mn_1.6O₄ with acid to form cubic H_1.6Mn_1.6O₄.     

Structure Study of Bi2.5Na0.5Ta2O9 and Bi2.5Nam−1.5NbmO3m+3 (m=2-4) by Neutron Powder Diffraction and Electron Microscopy

The crystal structures of Bi_2.5Na_0.5Ta₂O₉ and Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=3,4) have been investigated by the Rietveld analysis of their neutron powder diffraction patterns (λ=1.470 Å). These compounds belong to the Aurivillius phase family and are built up by (Bi₂O₂)²⁺ fluorite layers and (A_m-1B_mO_3m+1)^2- (m=2-4) pseudo-perovskite slabs. Bi_2.5Na_0.5Ta₂O₉ (m=2) and Bi_2.5Na_2.5Nb₄O₁₅ (m=4) crystallize in the orthorhombic space group A2₁am, Z=4, with lattice constants of a=5.4763(4), b=5.4478(4), c=24.9710 (15) and a=5.5095(5), b=5.4783(5), c=40.553(3) Å, respectively. Bi_2.5Na_1.5Nb₃O₁₂ (m=3) has been refined in the orthorhombic space group B2cb, Z=4, with the unit-cell parameters a=5.5024(7), b=5.4622(7), and c=32.735(4) Å. In comparison with its isostructural Nb analogue, the structure of Bi_2.5Na_0.5Ta₂O₉ is less distorted and bond valence sum calculations indicate that the Ta-O bonds are somewhat stronger than the Nb-O bonds. The cell parameters a and b increase with increasing m for the compounds Bi_2.5Na_m-1.5Nb_mO_3m+3 (m=2-4), causing a greater strain in the structure. Electron microscopy studies verify that the intergrowth of mixed perovskite layers, caused by stacking faults, also increases with increasing m.     

Phase relations, crystal chemistry, and dielectric properties in sections of the La2O3-CaO-MgO-TiO2 system

Subsolidus phase equilibria and crystal chemistry were studied for the La₂O₃-MgO-TiO₂ system and for the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃ in the quaternary La₂O₃-CaO-MgO-TiO₂ system. Dielectric properties (relative permittivity and temperature coefficient of resonant frequency, τ_f) were measured at 5-10 GHz and mapped onto the phase equilibria relations to reveal the compositions of temperature-stable (τ_f=0) compounds and mixtures. Phase equilibria relations were obtained by X-ray powder diffraction analysis of approximately 80 specimens prepared by solid-state reactions in air at ∼1450°C. Six ternary phases were found to form in the La₂O₃-MgO-TiO₂ system, including the three previously reported compounds LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, and “La₆MgTi₄O₁₈”; and the new phases La₁₀MgTi₉O₃₄, La₉Mg_0.5Ti_8.5O₃₁, and a perovskite-type solid solution (1−x)LaMg_1/2Ti_1/2O₃-xLa_2/3TiO₃ (0?x?0.5). The phase previously reported as “La₆MgTi₄O₁₈” was found to form off-composition, apparently as a point compound, at La₆Mg_0.913Ti_4.04O₁₈. Indexed experimental X-ray powder diffraction patterns are given for LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, La₆Mg_0.913Ti_4.04O₁₈, La₁₀MgTi₉O₃₄, and La₉Mg_0.5Ti_8.5O₃₁. LaMg_1/2Ti_1/2O₃ exhibits a slightly distorted perovskite structure with ordered B-cations (P2₁/n; a=5.5608(2) Å, b=5.5749(3) Å, c=7.8610(5) Å, β=90.034(4)°). La₅Mg_0.5Ti_3.5O₁₅ (Pm1; a=5.5639(1), c=10.9928(5) Å) and La₆Mg_0.913Ti_4.04O₁₈ (R3m; a=5.5665(1), c=39.7354(9) Å) are n=5 and n=6 members, respectively, of the (111) perovskite-slab series A_nB_n−1O_3n. The new phases La₁₀MgTi₉O₃₄ (a=5.5411(2), b=31.3039(9), c=3.9167(1) Å) and La₉Mg_0.5Ti_8.5O₃₁ (a=5.5431(2), b=57.055(1), c=3.9123(1) Å) are n=5 and n=4.5 members, respectively, of the (110) perovskite-slab series A_nB_nO_3n+2, which exhibit orthorhombic subcells; electron diffraction revealed monoclinic superlattices with doubled c-parameters for both compounds. Extensive perovskite-type solid solutions form in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃. The La₂O₃-MgO-TiO₂ system contains two regions of temperature-stable (τ_f=0) compositions. The quaternary La₂O₃-CaO-MgO-TiO₂ system contains an extensive single-phase perovskite-type volume through which passes a surface of temperature-stable compositions with permittivities projected to be in the 40-50 range. Traces of this surface occur as lines of τ_f=0 perovskite-type phases in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃.     

g-C_3N_4/CaTi_2O_5复合材料制备及其光催化性能

利用类石墨氮化碳(g-C_3N_4)和亚稳相钙钛氧化物(CaTi_2O_5)固相法制备C_3N_4/CaTi_2O_5复合材料。利用X射线衍射(XRD)、金相显微镜、扫描电子显微镜(SEM)及附带能谱分析仪(EDS)和N2吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计(UV-Vis)测试了样品的光吸收性能,研究C_3N_4与CaTi_2O_5物质的量之比(nC_3N_4/nCaTi_2O_5)对C_3N_4/CaTi_2O_5复合样品的物相结构和微观形貌的影响,同时考察C_3N_4/CaTi_2O_5复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明:相比纯C_3N_4和CaTi_2O_5样品,C_3N_4/CaTi_2O_5复合样品在可见光下具有较高的光催化性能,随着nC_3N_4/nCaTi_2O_5增加,样品的光催化降解率随之增加而后降低,当nC_3N_4/nCaTi_2O_5=1∶1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

Thermal decomposition of Me3SnO2PCl2, Me2Sn(O2PCl2)2 and Ph3SnO2PCl2

TG and DTA studies on Me₃SnO₂PCl₂, Me₂Sn(O₂PCl₂)₂ and Ph₃SnO₂PCl₂ were carried out under dynamic argon atmosphere. The results show that the decomposition proceeds in different stages leading to the formation of Sn₃(PO₄)₂ as a stable product. This compound was characterized by IR spectroscopy. Decomposition schemes involving reductive elimination reactions were proposed.     

The Phase Relations in the System In2O3–TiO2–MgO at 1100 and 1350°C

The phase relations in the system In₂O₃–TiO₂–MgO at 1100 and 1350°C are determined by a classical quenching method. In this system, there are four pseudobinary compounds, In₂TiO₅, MgTi₂O₅ (pseudobrookite type), MgTiO₃ (ilmenite type), and Mg₂TiO₄ (spinel type) at 1100°C. At 1350°C, in addition to these compounds there exist a spinel-type solid solution Mg_2−xIn_2xTi_1−xO₄ (0≤x≤1) and a compound In₆Ti₆MgO₂₂ with lattice constants a=5.9236(7) Å, b=3.3862(4) Å, c=6.3609(7) Å, β=108.15(1)°, and q=0.369, which is isostructural with the monoclinic In₃Ti₂FeO₁₀ in the system In₂O₃–TiO₂–MgO. The relation between the lattice constants of the spinel phase and the composition nearly satisfies Vegard's law. In₆Ti₆MgO₂₂ extends a solid solution range to In₂₀Ti₁₇Mg₃O₆₇ with lattice constants of a=5.9230(5) Å, b=3.3823(3) Å, c=6.3698(6) Å, β=108.10(5)°, and q=0.360. The distributions of constituent cations in the solid solutions are discussed in terms of their ionic radius and site preference effect.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Microstructures of Some Bi-W-Nb-O Phases

Microstructures of three Bi-W-Nb-O phases have been examined by using high-resolution transmission electron microscopy. Bi₁₇W₂Nb₃O₃₉ and Bi₁₇WNb₃O₃₆ have incommensurate superstructures derived from the defect fluorite-type δ-Bi₂O₃ and can be regarded as intermediate phases between the type II solid solutions in the Bi-Nb-O and Bi-W-O systems. Bi₈W₂Nb₂O₂₃ has a Bi₂WO₆-like subunit cell with a stepped superstructure. Formation mechanisms of various superstructures are discussed.