1.
N-Phenyl-3,3-Bis[4-(p-aminophenoxy)phenyl] phthalimidine ( II ) was used as a monomer with various aromatic dicarboxylic acids and tetracarboxylic dianhydrides to synthesize polyamides and polyimides, respectively. The diamine II was derived by a nucleophilic substitution of N-phenyl-3,3-bis(4-hydroxyphenyl) phthalimidine with p-chloronitrobenzene in the presence of K2CO3 and then hydro-reduced. Polyamides IV a-g having inherent viscosities of 0.55–1.64 dL/g were prepared by the direct polycondensation of the diamine II with various aromatic diacids using triphenyl phosphite and pyridine as condensing agents. All the aromatic polyamides were amorphous and readily soluble in various polar solvents such as N,N-dimethylacetamide (DMAc), N,N-dimethylformamide, dimethylsulfoxide, and N-methyl-2-pyrrolidone (NMP). Transparent and flexible films of these polymers could be cast from the DMAc solutions. These aromatic polyamides had glass transition temperatures in the range of 293–319°C and 10% weight loss occurred up to 480°C. The polyimides were synthesized from diamine II and various aromatic dianhydrides via the two-stage procedure that included ring-opening polyaddition in DMAc to give poly(amic acid)s, followed by thermal or chemical conversion to polyimides. Most of the aromatic polyimides obtained by chemical cyclization were found to be soluble in NMP, m-cresol, and o-chlorophenol. These polyimides showed almost no weight loss up to 500°C in air or nitrogen atmosphere. © 1994 John Wiley & Sons, Inc.  相似文献   

2.
3,3-Bis[4-(4-aminophenoxy)phenyl]phthalide ( II ) was used as a monomer with various aromatic dicarboxylic acids and dianhydrides to synthesize polyamides and polyimides, respectively. The diamine II was derived by a nucleophilic substitution of phenolphthalein with p-chloronitrobenzene in the presence of K2CO3. Polyamides IV a-g having inherent viscosities of 0.77–2.46 dL/g were prepared by the direct polycondensation of diamine II with diacids III a-g using triphenyl phosphite and pyridine as condensing agents. The polyamides were readily soluble in a variety of solvents such as N, N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), and N-methyl-2-pyrrolidinone (NMP) and afforded transparent and flexible films from the polymer solutions. These polymers had glass transition temperatures (Tgs) in the 227–307°C range and 10% weight loss temperatures occurred up to 450°C. Polyimides VI a-e based on diamine II and various aromatic dianhydrides V a-e were synthesized by the two-stage procedure that included ring-opening, followed by thermal or chemical conversion to polyimides. Most of the polyimides obtained by chemical cyclodehydration procedure were found to soluble in DMF, NMP, o-chlorophenol, and m-cresol. The Tgs of these polyimides were in the 260–328°C range and showed almost no weight loss up to 500°C under air and nitrogen atmosphere. © 1994 John Wiley & Sons, Inc.  相似文献   

3.
1,6-Bis(4-aminophenoxy)naphthalene ( I ) was used as a monomer with various aromatic tetracarboxylic dianhydrides to synthesize polyimides via a conventional two-stage procedure that included ring-opening polyaddition in a polar solvent such as N,N-dimethylacetamide (DMAc) to give poly(amic acid)s, followed by thermal cyclodehydration to polyimides. The diamine ( I ) was prepared through the nucleophilic displacement of 1,6-dihydroxynaphthal-ene with p-chloronitrobenzene in the presence of K2CO3, followed by catalytic reduction. Depending on the dianhydrides used, the poly(amic acid)s obtained had inherent viscosities of 0.73–2.31 dL/g. All the poly(amic acid)s could be solution cast and thermally converted into transparent, flexible, and tough polyimide films. The polyimide films had a tensile modulus range of 1.53–1.84 GPa, a tensile strength range of 95–126 MPa, and an elongation range at break of 9–16%. The polyimide derived from 4,4′-sulfonyldiphthalic anhydride (SDPA) had a better solubility than the other polyimides. These polyimides had glass transition temperatures between 248–286°C (DSC). Thermogravimetric analyses established that these polymers were fairly stable up to 500°C, and the 10% weight loss temperatures were recorded in the range of 549–595°C in nitrogen and 539–590°C in air atmosphere. © 1995 John Wiley & Sons, Inc.  相似文献   

4.
Novel aromatic polyimides containing symmetric, bulky di-tert-butyl substituents unit were synthesized from 1,4-bis(4-aminophenoxy)2,5-di-tert-butylbenzene (BADTB) and various aromatic tetracarboxylic dianhydrides by the conventional two-stage procedure that included ring-opening polyaddition in a polar solvent such as N,N-dimethylacetamide to give poly(amic acid)s, followed by cyclodehydration to polyimides. The diamine was prepared through the nucleophilic displacement of 2,5-di-tert-butylhydroquinone with p-chloronitrobenzene in the presence of K2CO3, followed by catalytic reduction. Depending on the dianhydrides used, the poly(amic acid)s obtained had inherent viscosities of 0.83–1.88 dL g−1. Most of the polyimides formed transparent, flexible, and tough films. Tensile strength and elongation at break of the BADTB-based polyimide films ranged from 68–93 MPa and 7–11%, respectively. The polyimide derived from 4,4′-hexafluoro-isopropylidenebisphathalic anhydride had better solubility than the other polyimides. These polyimides had glass transition temperatures between 242–298°C and 10% mass loss temperatures were recorded in the range of 481–520°C in nitrogen. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 1527–1534, 1997  相似文献   

5.
A novel spirobichroman unit containing dietheramine, 6,6′-bis(4-aminophenoxy)-4,4,4′,4′,7,7′-hexamethyl-2,2′-spirobichroman ( 3 ), was prepared by the nucleophilic substitution of 6,6′-dihydroxy-4,4,4′,4′,7,7′-hexamethyl-2,2′-spirobichroman with p-chloronitrobenzene in the presence of K2CO3 followed by hydrazine catalytic reduction of the intermediate dinitro compound. A series of polyimides were synthesized from diamine 3 and various aromatic dianhydrides by a conventional two-stage procedure through the formation of poly(amic-acid)s followed by thermal imidization. The intermediate poly(amic-acid)s had inherent viscosities of 1.00–2.78 dL/g. All the poly-(amic-acid)s could be thermally cyclodehydrated into flexible and tough polyimide films, and some polyimides were soluble in polar solvents such as N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide (DMAc), and N,N-dimethylformamide (DMF). These polyimides had glass transition temperatures (Tg) in the range of 236–256°C, and 10% weight loss occurred up to 450°C. Furthermore, a series of polyamides and poly(amide-imide)s with inherent viscosities of 0.71–2.29 dL/g were prepared by direct polycondensation of the diamine 3 with various aromatic dicarboxylic acids and imide ring-containing dicarboxylic acids by means of triphenyl phosphite and pyridine. All the polyamides and poly(amide-imide)s were readily soluble in polar solvents such as DMAc, and tough and flexible films could be cast from their DMAc solutions. These polymers had glass transition temperatures in the range of 137–228°C and 10% weight loss temperatures in the range of 419–443°C in air and 404–436°C in nitrogen, respectively. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 1487–1497, 1997  相似文献   

6.
1,3-Diaminoadamantane (I) was used as a monomer with various aromatic dicarboxylic acyl chlorides and dianhydrides to synthesize polyamides and polyimides, respectively. Polyamides having inherent viscosities of 0.10–0.27 dL/g were prepared by low-temperature solution polycondensation. The polyamides were soluble in a variety of solvents such as N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), pyridine, dioxane, and nitrobenzene. These polyamides had glass transition temperatures in the 179–187°C range and 5% weight loss temperatures occurred at up to 354°C. Polyimides based on diamine I and various aromatic dianhydrides were synthesized by the two-stage procedure that included ring-opening to form polyamic acids, followed by thermal conversion to polyimides. The polyamic acids had inherent viscosities of 0.14–0.38 dL/g. The glass transition temperature of these polyimides were in the 245–303°C range and showed almost no weight loss up to 350°C under air and nitrogen atmosphere. © 1996 John Wiley & Sons, Inc.  相似文献   

7.
The novel diamine, 1,7-bis(4-aminophenoxy)naphthalene (1,7-BAPON), was synthesized and used to prepared polyimides. 1,7-BAPON was synthesized through the nucleophilic displacement of 1,7-dihydroxynaphthalene with p-fluoronitrobenzene in the presence of K2CO3 followed by catalytic-reduction. Polyimides were prepared from 1,7-BAPON and various aromatic tetracarboxylic dianhydrides by the usual two-step procedure that included ring-opening polyaddition to give poly(amic acid)s, followed by cyclodehydration to polyimides. The poly(amic acid)s had inherent viscosities of 0.74-2.48 dL/g. Most of the polyimides formed tough, creasible films. These polyimides had glass transition temperatures between 247–278°C and their 10% weight loss temperatures were recorded in the range of 515–575°C in nitrogen atmosphere. © 1995 John Wiley & Sons, Inc.  相似文献   

8.
A new cardo diamine monomer, 5,5-bis[4-(4-aminophenoxy)phenyl]-4,7-methanohexahydroindane (II), was prepared in two steps with high yield. The monomer was reacted with six different aromatic tetracarboxylic dianhydrides in N,N-dimethylacetamide (DMAc) to obtain the corresponding cardo polyimides via the poly(amic acid) precursors and thermal or chemical imidization. All the poly(amic acid)s could be cast from their DMAc solutions and thermally converted into transparent, flexible, and tough polyimide films which were further characterized by x-ray and mechanical analysis. All of the polymers were amorphous and the polyimide films had a tensile strength range of 89–123 MPa, an elongation at break range of 6–10%, and a tensile modulus range of 1.9–2.5 GPa. Polymers Vc, Ve, and Vf exhibited good solubility in a variety of solvents such as N-methyl-2-pyrrolidinone (NMP), DMAc, N,N-dimethylformamide (DMF), dimethyl sulfoxide (DMSO), pyridine, γ-butyrolactone, and even in tetrahydrofuran and chloroform. These polyimides showed glass-transition temperatures between 274 and 299°C and decomposition temperatures at 10% mass loss temperatures ranging from 490 to 521°C and 499 to 532°C in nitrogen and air atmospheres, respectively. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 2815–2821, 1999  相似文献   

9.
Novel aromatic polyimides containing bis(phenoxy)naphthalene units were synthesized from 1,5-bis(4-aminophenoxy)naphthalene (APN) and various aromatic tetracarboxylic dianhydrides by the usual two-step procedure that included ring-opening polyaddition in a polar solvent such as N,N-dimethylacetamide (DMAc) to give poly(amic acid)s, followed by cyclodehydration to polyimides. The poly(amic acid)s had inherent viscosities between 0.72 and 1.94 dL/g, depending on the tetracarboxylic dianhydrides used. Excepting the polyimide IVb obtained from 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA), all other polyimides formed brown, flexible, and tough films by casting from the poly(amic acid) solutions. The polyimide synthesized from BPDA was characterized as semicrystalline, whereas the other polyimides showed amorphous patterns as shown by the x-ray diffraction studies. Tensile strength, initial moduli, and elongation at break of the APN-based polyimide films ranged from 105–135 MPa, 1.92–2.50 GPa, and 6–7%, respectively. These polyimides had glass transition temperatures between 228 and 317°C. Thermal analyses indicated that these polymers were fairly stable, and the 10% weight loss temperatures by TGA were recorded in the range of 543–574°C in nitrogen and 540–566°C in air atmosphere, respectively. © 1993 John Wiley & Sons, Inc.  相似文献   

10.
A dicarboxylic acid ( I ) was prepared from the condensation of 9,9-bis[4-(4-aminophenoxy) phenyl] fluorene and trimellitic anhydride. A new family of poly(amide-imide)s having inherent viscosities of 0.75-1.04 dL/g was prepared by the triphenyl phosphite activated polycondensation from the diimide-diacid I with various aromatic diamines in a medium consisting of N-methyl-2-pyrrolidone (NMP), pyridine, and calcium chloride. Most of the resulting polymers showed an amorphous nature and were readily soluble in polar solvents such as NMP and N,N-dimethylacetamide. All the soluble poly(amide-imide)s afforded transparent, flexible, and tough films. The glass transition temperatures of these polymers were in the range of 262–325°C and the 10% weight loss temperatures were above 525°C in air. © 1994 John Wiley & Sons, Inc.  相似文献   

11.
A novel bis(ether anhydride) monomer, 9,9‐bis[4‐(3,4‐dicarboxyphenoxy)phenyl]fluorene dianhydride (4), was synthesized from the nitrodisplacement of 4‐nitrophthalonitrile by the bisphenoxide ion of 9,9‐bis(4‐hydroxyphenyl)fluorene (1), followed by alkaline hydrolysis of the intermediate tetranitrile and dehydration of the resulting tetracarboxylic acid. A series of poly(ether imide)s bearing the fluorenylidene group were prepared from the bis(ether anhydride) 4 with various aromatic diamines 5a–i via a conventional two‐stage process that included ring‐opening polyaddition to form the poly(amic acid)s 6a–i followed by thermal cyclodehydration to the polyimides 7a–i. The intermediate poly(amic acid)s had inherent viscosities in the range of 0.39–1.57 dL/g and afforded flexible and tough films by solution‐casting. Except for those derived from p‐phenylenediamine, m‐phenylenediamine, and benzidine, all other poly(amic acid) films could be thermally transformed into flexible and tough polyimide films. The glass transition temperatures (Tg) of these poly(ether imide)s were recorded between 238–306°C with the help of differential scanning calorimetry (DSC), and the softening temperatures (Ts) determined by thermomechanical analysis (TMA) stayed in the range of 231–301°C. Decomposition temperatures for 10% weight loss all occurred above 540°C in an air or a nitrogen atmosphere. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1403–1412, 1999  相似文献   

12.
A novel, trifluoromethyl‐substituted, bis(ether amine) monomer, 1,4‐bis(4‐amino‐2‐trifluoromethylphenoxy)naphthalene, was synthesized through the nucleophilic displacement of 2‐chloro‐5‐nitrobenzotrifluoride with 1,4‐dihydroxynaphthalene in the presence of potassium carbonate in dimethyl sulfoxide, followed by catalytic reduction with hydrazine and Pd/C in ethanol. A series of new fluorine‐containing polyimides with inherent viscosities of 0.57–0.91 dL/g were prepared by reacting the diamine with six commercially available aromatic dianhydrides via a conventional, two‐step thermal or chemical imidization method. Most of the resulting polyimides were soluble in strong polar solvents such as N‐methylpyrrolidone and N,N‐dimethylacetamide (DMAc). All the polyimides afforded transparent, flexible, and strong films with good tensile properties. These polyimides exhibited glass‐transition temperatures (Tg's) (by DSC) and softening temperatures (by thermomechanical analysis) in the ranges of 252–315 and 254–301 °C, respectively. Decomposition temperatures for 5% weight loss all occurred above 500 °C in both air and nitrogen atmospheres. The dielectric constants of these polyimides ranged from 3.03 to 3.71 at 1 MHz. In addition, a series of new, fluorinated polyamides with inherent viscosities of 0.32–0.62 dL/g were prepared by the direct polycondensation reaction the diamine with various aromatic dicarboxylic acids by means of triphenyl phosphite and pyridine. All the polyamides were soluble in polar solvents such as DMAc and could be solution‐cast into tough and flexible films. These polyamides had Tg's between 228 and 256 °C and 10% weight‐loss temperatures above 400 °C in nitrogen or air. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2377–2394, 2004  相似文献   

13.
Jiang  Jianwen  Huang  Shuiping  Liu  Yuan  Sheng  Shouri  Huang  Zhenzhong  Song  Caisheng 《中国化学》2010,28(1):102-110
9,9‐Bis(4‐hydroxyphenyl)xanthene (BHPX) was synthesized in 82% yield from xanthenone in a one‐pot, two‐step synthetic procedure. A new diacyl chloride monomer, 9,9‐bis[4‐(chloroformylphenoxy)phenyl]xanthene (BCPX), was synthesized in three steps from the nucleophilic fluorodisplacement of 4‐fluorobenzonitrile with the dipotassium bisphenolate of BHPX, followed by alkaline hydrolysis of the intermediate bis(ether nitrile), and then chlorination with thionyl chloride. Several novel aromatic polyamides containing ether and bulky xanthene groups with the inherent viscosities (0.72–0.98 dL/g) were prepared by the low temperature polycondensation of BCPX with various aromatic diamines in N,N‐dimethylacetamide (DMAc) solution containing pyridine (Py). All new polyamides were amorphous and readily soluble in various polar solvents such as DMAc, N,N‐dimethylformamide (DMF), N‐methyl‐2‐pyrrolidone (NMP) and Py. These polymers showed relatively high glass transition temperatures between 236 and 298°C, decomposition temperatures at 10% weight loss ranging from 490 to 535°C and 483 to 515°C in nitrogen and air, respectively, and char yields at 700°C in nitrogen higher than 50%. Transparent, flexible, and tough films of these polymers cast from DMAc solutions exhibited tensile strengths ranging from 82 to 106 MPa, elongations at break from 10% to 25%, and initial moduli from 2.0 to 2.8 GPa.  相似文献   

14.
New aromatic polyimides containing a biphenyl-2,2′-diyl or 1,1′-binaphthyl-2,2′-diyl unit were prepared by a conventional two-step method starting from 2,2′-bis(p-aminophenoxy) biphenyl or 2,2′-bis(p-aminophenoxy)-1,1′-binaphthyl and aromatic tetracarboxylic dianhydrides. The polyimides having inherent viscosities of 0.69–0.99 and 0.51–0.59 dL/g, respectively, were obtained. Some of these polymers were readily soluble in a variety of organic solvents including N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), dimethyl sulfoxide, and pyridine. Transparent, flexible, and pale yellow to brown films of these polymers could be cast from the DMAc or NMP polyamic acid solutions. These aromatic polyimides containing biphenyl and binaphthyl units had glass transition temperatures in the range of 200–235 and 286–358°C, respectively. They began to lose weight around 380°C, with 10% weight loss being recorded at about 470°C in air. © 1993 John Wiley & Sons, Inc.  相似文献   

15.
1,1-Bis[4-(4-carboxyphenoxy)phenyl]cyclohexane (III) and 1,1-bis[4-(4-aminophenoxy)phenyl]cyclohexane (V) were prepared in two main steps starting from the aromatic nucleophilic substitution of p-fluorobenzonitrile and p-chloronitrobenzene, respectively, with 1,1-bis(4-hydroxyphenyl)cyclohexane in the presence of potassium carbonate in N,N-dimethylformamide (DMF). Using triphenyl phosphite and pyridine as condensing agents, two series of polyamides with cyclohexylidene cardo groups were directly polycondensated from dicarboxylic acid III with various aromatic diamines or from diamine V with various aromatic dicarboxylic acids in an N-methyl-2-pyrrolidone (NMP) solution containing dissolved calcium chloride. The polyamides exhibited inherent viscosities in the range of 0.45 to 1.78 dL/g. Almost all of the polymers were readily soluble in polar aprotic solvents such as NMP and N,N-dimethylacetamide (DMAc) and could afford transparent, flexible, and tough films by solution casting. The glass transition temperatures (Tg) of these aromatic polyamides were in the range of 180–243°C by DSC, and the 10% weight loss temperatures in nitrogen and air were all above 450°C. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 3575–3583, 1999  相似文献   

16.
The diamine 1,4-bis(4-aminophenoxy)-2,5-di-tert-butylbenzene, containing symmetric, bulky di-tert-butyl substituents and a flexible ether unit, was synthesized and used to prepare a series of polyamides by the direct polycondensation with various aromatic dicarboxylic acids in N-methyl-2-pyrrolidinone (NMP) using triphenyl phosphite and pyridine as condensing agents. All the polymers were obtained in quantitative yields with inherent viscosities of 0.32–1.27 dL g−1. Most of these polyamides, except II a , II d , and II e , showed an amorphous nature and dissolved in polar solvents and less polar solvents. Polyamides derived from 4,4′-sulfonyldibenzoic acid, 4,4′-(hexafluoro-isopropylidene)dibenzoic acid, and 5-nitroisophthalic acid were even soluble in a common organic solvent such as THF. Most polyamide films could be obtained by casting from their N,N-dimethylacetamide (DMAc) solutions. The polyamide films had a tensile strength range of 49–78 MPa, an elongation range at break of 3–5%, and a tensile modulus range of 1.57–2.01 GPa. These polyamides had glass transition temperatures ranging between 253 and 276°C, and 10% mass loss temperatures were recorded in the range 402–466°C in nitrogen atmosphere. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 1069–1074, 1998  相似文献   

17.
Aromatic polyamides were synthesized from 4,5-bis(4-aminophenyl)-2-phenyloxazole (APO) or 4,5-bis[4(4-aminophenoxy)phenyl]-2-phenyloxazole (APPO) containing 2-phenyl-4,5-oxazolediyl units with several aromatic carboxylic dichlorides by a low-temperature solution polycondensation method. The polyamides were obtained quantitatively, and their inherent viscosities ranged from 0.48 to 1.25 dL g?1. The glass transition temperatures (T gs) were displayed between 234 to 311°C, and the residual weight at 600°C (Res.wt600) exceeded 52% in nitrogen atmosphere. The polyamides showed good solubility in several aprotic polar solvents, such as N,N-dimethylacetoamide (DMAc), N-methyl-2-pyrrolidone (NMP), and dimethyl sulfoxide (DMSO). Aromatic polyimides were derived from APO or APPO with aromatic carboxylic dianhydrides through polyamic acids. The inherent viscosities of the polyamic acids, which were 0.53 to 1.02 dL g?1, T gs of the polyimides were observed between 259 to 361°C and their Res.wts600 were above 70%. The polyamides and polyimides were amorphous and afforded thin, flexible and tough films. We also prepared a nanocomposite of the polyamide derived from APPO with organophilic montmorillonite clay.  相似文献   

18.
A new N‐phenylated amide (N‐phenylamide) unit containing aromatic diamine, N,N′‐bis(3‐aminobenzoyl)‐N,N′‐diphenyl‐1,4‐phenylenediamine, was prepared by the condensation of N,N′‐diphenyl‐1,4‐phenylenediamine with 3‐nitrobenzoyl chloride, followed by catalytic reduction. Two series of organosoluble aromatic poly(N‐phenylamide‐imide)s and poly(N‐phenylamide‐amide)s with inherent viscosities of 0.58–0.82 and 0.56–1.21 dL/g were prepared by a conventional two‐stage method and the direct phosphorylation polycondensation, respectively, from the diamine with various aromatic dianhydrides and aromatic dicarboxylic acids. All polyimides and polyamides are amorphous and readily soluble in many organic solvents such as N,N‐dimethylacetamide and N‐methyl‐2‐pyrrolidone. These polymers could be solution cast into transparent, tough, and flexible films with high tensile strengths. These polyimides and polyamides had glass‐transition temperatures in the ranges of 230–258 and 196–229 °C, respectively. Decomposition temperatures of the polyimides for 10% weight loss all occurred above 500 °C in both nitrogen and air atmospheres. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2564–2574, 2002  相似文献   

19.
5,5-Bis[4-(4-carboxyphenoxy)phenyl]hexahydro-4,7-methanoindan ( 3a ) and 5,5-bis[4-(4-aminophenoxy)phenyl]hexahydro-4,7-methanoindan ( 3b ) were prepared in two main steps starting from the aromatic nucleophilic halogen-displacement of p-fluorobenzonitrile and p-chloronitrobenzene, respectively, with 5,5-bis(4-hydroxyphenyl)hexahydro-4,7-methanoindan in the presence of potassium carbonate in N,N-dimethylformamide (DMF). Using triphenyl phosphite and pyridine as condensing agents, two series of polyamides having polyalicyclic cardo units were directly polycondensated from dicarboxylic acid 3a with various aromatic diamines, or from diamine 3b with various aromatic dicarboxylic acids in the N-methyl-2-pyrrolidone (NMP) solution containing dissolved calcium chloride. High molecular weight polyamides with inherent viscosities between 0.73 and 1.44 dL/g were obtained. All polymers were readily soluble in polar aprotic solvents such as NMP and N,N-dimethylacetamide (DMAc) and afforded transparent, flexible, and tough films by solution casting. The glass-transition temperatures (Tg) of these aromatic polyamides were in the range of 219–253°C by DSC, and the 10% weight loss temperatures in nitrogen and air were above 467 and 465°C, respectively. A comparative study of some polyamides with an isomeric repeat unit is also presented. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 4510–4520, 1999  相似文献   

20.
A new triphenylamine‐containing diamine monomer, 4,4′‐diamino‐4″‐tert‐butyltriphenylamine, was successfully synthesized by the cesium fluoride‐mediated N,N‐diarylation of 4‐tert‐butylaniline with 4‐fluoronitrobenzene, followed by the reduction of the nitro group. The obtained diamine monomer was reacted with various aromatic dicarboxylic acids and tetracarboxylic dianhydrides to produce two series of novel triphenylamine‐based polyamides and polyimides with pendent tert‐butyl substituents. Most of the polymers were readily soluble in polar organic solvents, such as N‐methyl‐2‐pyrrolidone and N,N‐dimethylacetamide (DMAc), and could be solution cast into tough and flexible polymer films. These polymers showed high glass transition temperatures between 282 and 320 °C, and they were fairly stable up to a temperature above 450 °C (for polyamides) or 500 °C (for polyimides). These polymers exhibited UV absorption maxima around 308 to 361 nm. The photoluminescence spectra of the polyamides in DMAc exhibited a peak emission wavelength in the blue at 421–433 nm. Cyclic voltammograms of polyamides and polyimides showed an oxidation wave at 1.0–1.1 V versus Ag/AgCl in an acetonitrile solution. All the polyamides and polyimides exhibited excellent reversibility of electrochromic characteristics by continuous several cyclic scans between 0.0 and 1.1–1.3 V, with a color change from the original pale yellowish neutral form to the green or blue oxidized forms. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4579–4592, 2006  相似文献   