Effect of Co underlayer on soft magnetic properties and microstructure of FeCo thin films

High saturation magnetization soft magnetic FeCo (=Fe₆₅Co₃₅) films were prepared using a thin Co underlayer. The FeCo/Co films exhibited a well-defined in-plane uniaxial anisotropy with easy axis coercivity (H_ce) of 10 Oe and hard axis coercivity (H_ch) of 3 Oe, and a half reduction of H_c with H_ce=4.8 Oe and H_ch=1.0 Oe was obtained when the composition was adjusted to 25 at% Co. The effective permeability of the films remains flat around 250 to 800 MHz. The saturation magnetostriction was 5.2×10⁻⁵ and the intrinsic stress was 0.8 GPa in FeCo single layer, both were slightly reduced by Co underlayer. The Co underlayer changed the preferred orientation of the FeCo films from (2 0 0) to (1 1 0) but more significantly, reduced the average grain size from ∼74 to ∼8.2 nm. It also reduced the surface roughness from 2.351 to 0.751 nm. The initial stage and interface diffusion properties were examined by TEM and XPS.     

Soft magnetic properties of FeCo films with Co underlayer

Bilayered Fe₆₅Co₃₅ (=FeCo)/Co films were prepared by facing targets sputtering with 4πM_s∼24 kg. The soft magnetic properties of FeCo films were induced by a Co underlayer. H_c decreased rapidly when the Co underlayer was 2 nm or more. The films showed well-defined in-plane uniaxial anisotropy with the typical values of H_ce=10 Oe and H_ch=3 Oe, respectively. High frequency characteristics of the films show the films can work at 0.8 GHz with real permeability as high as 250.     

Thickness dependence of microwave magnetic properties in electrodeposited Fe-Co soft magnetic films with in-plane anisotropy

In this work, the thickness effect of Fe₅₂Co₄₈ soft magnetic films with in-plane anisotropy on static and microwave magnetic properties was investigated. The hysteresis loop results indicated that the static in-plane uniaxial anisotropy field increased from almost 0-60 Oe with increasing film thickness from 100 to 540 nm and well-defined in-plane uniaxial magnetic anisotropy can be obtained as the thickness reached 540 nm or larger. Based on Landau-Lifshitz-Gilbert (LLG) equation, the microwave complex permeability spectra were analyzed and well fitted. The LLG curve-fitting results indicated that the initial permeability increased from 106 to 142 and the resonant frequency was shifted from 4.95 to 4.29 GHz as the film thickness was varied from 540 to 1500 nm. Moreover, it was found that there was a discrepancy between the static and the dynamically determined anisotropy field, which can be explained by introducing an additional effective isotropic ripple field. The decreased ripple field was suggested to result in a significant decrease of damping coefficient from 0.109 to 0.038.     

Effect of oxygen pressure on microstructure and magnetic properties of strontium hexaferrite (SrFe12O19) film prepared by pulsed laser deposition

The effects of oxygen pressure during deposition on microstructure and magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films grown on Si (100) substrate with Pt (111) underlayer by pulsed laser deposition have been investigated. X-ray diffraction pattern confirms that the films have c-axis perpendicular orientation. The c-axis dispersion (Δθ₅₀) increases and c-axis lattice parameter decreases with increasing oxygen pressure. The films have hexagonal shape grains with diameter of 150-250 nm as determined by atomic force microscopy. The coercivities in perpendicular direction are higher than those in in-plane direction, which shows the films have perpendicular magnetic anisotropy. The saturation magnetization and anisotropy field for the film deposited in oxygen pressure of 0.13 mbar are comparable to those of the bulk strontium hexaferrite. Higher oxygen pressure leads to the films having higher coercivity and squareness. The coercivity in perpendicular and in-plane directions of the film deposited in oxygen pressure of 0.13 mbar are 2520 Oe and 870 Oe, respectively.     

Studies on high-moment soft magnetic FeCo/Co thin films

The dependences of soft magnetic properties and microstructures of the sputtered FeCo (=FeFeCo薄膜 溅射条件 软磁性 高饱和磁化强度FeCo film, sputtering conditions, high saturation magnetization, soft magnetic properties2005-10-263/7/2006 12:00:00 AMThe dependences of soft magnetic properties and microstructures of the sputtered FeCo （=Fe65Co35） films on Co underlayer thickness tCo, FeCo thickness tFeCo, substrate temperature Ts and taxget-substrate spacing dT-s are studied. FeCo single layer generally shows a high coercivity with no obvious magnetic anisotropy. Excellent soft magnetic properties with saturation magnetization μ0Ms of 2.35 T and hard axis coercivity Hch of 0.25 kA/m in FeCo films can be achieved by introducing a Co underlayer. It is shown that sandwiching a Co underlayer causes a change in orientation and reduction in grain size from 70 nm to about 10 nm in the FeCo layer. The magnetic softness can be explained by the Hoffmann＇s ripple theory due to the effect of grain size. The magnetic anisotropy can be controlled by changing dT-S, and a maximum of 14.3 kA/m for anisotropic field Hk is obtained with dT-S=18.0 cm.     

Magnetic properties of strontium hexaferrite films prepared by pulsed laser deposition

The magnetic properties of strontium hexaferrite (SrFe₁₂O₁₉) films fabricated by pulsed laser deposition on the Si(100) substrate with Pt(111) underlayer have been studied as a function of film thickness (50–700 nm). X-ray diffraction patterns confirm that the films have c-axis perpendicular orientation. The coercivities in perpendicular direction are higher than those for in-plane direction which indicates the films have perpendicular magnetic anisotropy. The coercivity was found to decrease with increasing of thickness, due to the increasing of the grain size and relaxation in lattice strain. The 200 nm thick film exhibits hexagonal shape grains of 150 nm and optimum magnetic properties of M_s=298 emu/cm³ and H_c=2540 Oe.     

Microstructure and magnetic properties of nanocomposite FePt/MgO and FePt/Ag films

An in-plane magnetic anisotropy of FePt film is obtained in the MgO 5 nm/FePt t nm/MgO 5 nm films (where t=5, 10 and 20 nm). Both the in-plane coercivity (H_c∥) and the perpendicular magnetic anisotropy of FePt films are increased when introducing an Ag-capped layer instead of MgO-capped layer. An in-plane coercivity is 3154 Oe for the MgO 5 nm/FePt 10 nm/MgO 5 nm film, and it can be increased to 4846 Oe as a 5 nm Ag-capped layer instead of MgO-capped layer. The transmission electron microscopy (TEM)-energy disperse spectrum (EDS) analysis shows that the Ag mainly distributed at the grain boundary of FePt, that leads the increase of the grain boundary energy, which will enhance coercivity and perpendicular magnetic anisotropy of FePt film.     

Magnetic anisotropy properties of CoZrNb thin films deposited on PET substrate by magnetron sputtering

Soft magnetism and magnetic anisotropy properties of CoZrNb thin films deposited on polyethylene terephthalate (PET) substrate by magnetron sputtering were investigated. As the film thickness increases, the coercivity of films decreases from 7 to 4 Oe. It exhibits an in-plane uniaxial magnetic anisotropy as the thickness of CoZrNb thin films increases. An easy axis is observed in CoZrNb films along the direction transverse to the rolling direction of the polymer web.     

Strongly in-plane magnetized FePt thin film on ultrathin Fe underlayer

The effect of ultrathin Fe underlayer on the strong in-plane magnetization of FePt magnetic thin film was investigated. This FePt thin film could be attained using the ultrathin Fe underlayer with 1 nm thickness. The in-plane coercivity of FePt film with 20 nm thickness grown on ultrathin Fe underlayer was high up to 7400 Oe. However, its out-of-plane coercivity was extremely low to 350 Oe compared to those of FePt thin films in other conventional studies. This result indicates that FePt thin film was strongly in-plane magnetized by ultrathin Fe underlayer. The strong ordering phase transformation kinetics and the high texturing to in-plane direction of the FePt thin film by ultrathin Fe underlayer were confirmed by Kinetics Monte Carlo (KMC) simulation and XRD measurement result, respectively. It is also supposed that they are associated with the reduction of an interface free energy between the film and the substrate with an introduction of ultrathin underlayer.     

Perpendicular magnetic anisotropy of ultrathin FeCo alloy films on Pd(0 0 1) surface: First principles study

Using the full potential linearized augmented plane wave (FLAPW) method, thickness dependent magnetic anisotropy of ultrathin FeCo alloy films in the range of 1 monolayer (ML) to 5 ML coverage on Pd(0 0 1) surface has been explored. We have found that the FeCo alloy films have close to half metallic state and well-known surface enhancement in thin film magnetism is observed in Fe atom, whereas the Co has rather stable magnetic moment. However, the largest magnetic moment in Fe and Co is found at 1 ML thickness. Interestingly, it has been observed that the interface magnetic moments of Fe and Co are almost the same as those of surface elements. The similar trend exists in orbital magnetic moment. This indicates that the strong hybridization between interface FeCo alloy and Pd gives rise to the large magnetic moment. Theoretically calculated magnetic anisotropy shows that the 1 ML FeCo alloy has in-plane magnetization, but the spin reorientation transition (SRT) from in-plane to perpendicular magnetization is observed above 2 ML thickness with huge magnetic anisotropy energy. The maximum magnetic anisotropy energy for perpendicular magnetization is as large as 0.3 meV/atom at 3 ML film thickness with saturation magnetization of . Besides, the calculated X-ray magnetic circular dichroism (XMCD) has been presented.     

Mǒsbauer study of the field induced uniaxial anisotropy in electro-deposited FeCo alloy films

Thin ferromagnetic films with in-plane magnetic anisotropy are promising materials for obtaining high microwave permeability.The paper reports a Mo¨ssbauer study of the field induced in-plane uniaxial anisotropy in electro-deposited FeCo alloy films.The FeCo alloy films were prepared by the electro-deposition method with and without an external magnetic field applied parallel to the film plane during deposition.Vibrating sample magnetometry and Mo¨ssbauer spectroscopy measurements at room temperature indicate that the film deposited in external field shows an in-plane uniaxial anisotropy with an easy direction coinciding with the external field direction and a hard direction perpendicular to the field direction,whereas the film deposited without external field does not show any in-plane anisotropy.Mo¨ssbauer spectra taken in three geometric arrangements show that the magnetic moments are almost constrained in the film plane for the film deposited with applied magnetic field.Also,the magnetic moments tend to align in the direction of the applied external magnetic field during deposition,indicating that the observed anisotropy should be attributed to directional ordering of atomic pairs.     

Effects of the Hf content on the microstructure and magnetic properties of Co-Hf-Ta thin films

Effects of the Hf content in Co-Hf-Ta thin films on the microstructure and magnetic properties were investigated in this study. It was found that appropriate Hf addition can effectively refine the Co grain size. Co grain sizes sharply decreased from 50 nm down to 2.3 nm with increasing the Hf content from 1.02 at.% to 2.81 at.%, leading to the reduced magneto-crystalline anisotropy. The Co-Hf-Ta thin films with small Co grains reveal low anisotropy field, low coercivity, and high resistivity. By optimizing the Hf content, the film with Hf concentration of 2.81 at.% exhibits excellent soft magnetic properties: high saturation magnetization (4πM_S ∼ 13.6 kG), and low coercivity (H_C ∼ 0.6 Oe). The effective permeability of the film reaches 800 and remains constant up to 1 GHz.     

Tunable resonance frequency of FeNi films by oblique sputtering

FeNi thin films were fabricated by radio frequency magnetron sputtering on Si(1 1 1). Dynamic properties at remanence of the films were systematically investigated in a wide frequency range from 100 MHz to 5 GHz. The results show that both thickness of FeNi films and oblique angle have important effects on the magnetic properties of the films, the magnetic resonant frequency of the films can also be adjusted by the two factors. The in-plane uniaxial magnetic anisotropy field can be adjusted from 82 Oe to 220 Oe by increasing the oblique angle. As a consequence, the magnetic resonant frequency of the films increased from 2.7 GHz to 4.2 GHz.     

Microstructure and magnetic properties studies of SmCo5 thin films grown on MgO and glass substrates

In this work, SmCo₅ thin films are deposited on single crystal MgO (1 0 0) and amorphous glass substrates with a Cr underlayer at 400 °C by sputtering. A comparison study shows that the microstructures and magnetic properties are different in the two SmCo₅ films on the MgO (1 0 0) and glass substrates, respectively. An epitaxial growth of Cr-(2 0 0)〈1 1 0〉/SmCo₅-(1 1 2¯ 0)〈0 0 0 1〉 is achieved on the MgO (1 0 0) single crystal substrate with an average grain size of 20 nm for SmCo₅. On the amorphous glass substrate, no significant crystallographic texture is found in the Cr underlayer. After the deposition of SmCo₅, a weak texture of (1 1 2¯ 0) is observed with an average grain size of 8 nm. High remanence ratio value in this film is probably due to strong exchange coupling. Both SmCo₅ films show high in-plane coercivity, high in-plane anisotropy and remanence enhancement.     

Thickness dependence of magnetic anisotropic properties of FeCoNd films

The magnetic FeCoNd films with thickness (t) from 50 to 166 nm were fabricated by RF magnetron co-sputtering at ambient condition. The amorphous structures of all of the films were investigated by X-ray diffraction and transmission electron microscopy. A spin reorientation transition from in-plane single domain state to out-of-plane stripe domain state was observed as a function of t. When t is below a critical thickness, magnetic moments lie in the film plane corresponding to in-plane single domain state because of the strong demagnetization energy. However, when t is increased, out-of-plane stripe domain structure was developed due to a dominated perpendicular magnetic anisotropy. Scanning electron microscopy data indicate that the perpendicular anisotropy, which is responsible for the formation of stripe domains, may result from the shape effect of the columnar growth of the FeCo grains.     

Co-based nanogranular thin films on flexible substrate for gigahertz applications

The Co-based granular thin films were deposited on the flexible substrate (Kapton) by magnetron sputtering. The films comprise of Co nanocrystallites and small amount of amorphous (Al,O)-rich inter-granular phase and have the electric resistivities in the range 50–120 μΩ cm, depending on the composition and thickness. The as-deposited films with thickness <80 nm have low coercivity (<20 Oe along hard direction), high permeability (up to 500) and resonance frequency up to 2.5 GHz. Compared to the rigid films, the flexible films have relatively higher coercivity and lower resonance frequency. A comparison between Co-based granular films and FeTaN continuous films has also been discussed.     

Influence of the nitrogen contents on the permeability characteristics and soft magnetic properties of FeHfN films

High permeability magnetic films can enhance the inductance of thin-film inductors in DC-DC converters. In order to obtain high permeability, the uniaxial anisotropy and coercivity should be as low as possible. This study employed dc reactive magnetron sputtering to fabricate nanocrystalline FeHfN thin films. The influence of the nitrogen flow on the composition, microstructure, and permeability characteristics, as well as magnetic properties was investigated. Increasing the nitrogen content can alter FeHfN films from amorphous-like to crystalline phases. The magnetic properties and permeability depend on variations in the microstructure. With the optimum N₂/Ar flow ratio of 4.8% (N₂ flow: 1.2 sccm), low anisotropy (H_K = 18 Oe), low coercivity (H_C = 1.1 Oe) and high permeability (μ′ > 600 at 50 MHz) were obtained for fabrication of a nanocrystalline FeHfN film with a thickness of around 700 nm. Such as-fabricated FeHfN films with a permeability of over 600 should be a promising candidate for high-permeability ferromagnetic material applications.     

Preparation of strontium hexaferrite film by pulsed laser deposition with in situ heating and post annealing

Strontium hexaferrite (SrFe₁₂O₁₉) films have been fabricated by pulsed laser deposition on Si(1 0 0) substrate with Pt(1 1 1) underlayer through in situ and post annealing heat treatments. C-axis perpendicular oriented SrFe₁₂O₁₉ films have been confirmed by X-ray diffraction patterns for both of the in situ heated and post annealed films. The cluster-like single domain structures are recognized by magnetic force microscopy. Higher coercivity in perpendicular direction than that for the in-plane direction shows that the films have perpendicular magnetic anisotropy. High perpendicular coercivity, around 3.8 kOe, has been achieved after post annealing at 500 °C. Higher coercivity of the post annealed SrFe₁₂O₁₉ films was found to be related to nanosized grain of about 50–80 nm.     

Preparation, and magnetic and electromagnetic properties of La-doped strontium ferrite films

SrLa_xFe_12−xO₁₉ films (x=0-1.0) with large magneto-crystalline anisotropy were synthesized on SiO₂ substrate by sol-gel and self-propagating high-temperature synthesis technique. The films were characterized by various experimental techniques including X-ray diffraction analysis, Field Emission Scanning Electron Microscope, Atomic Force Microscopy, Vibrating Sample Magnetometry and vector network analyzer. The results show that La ions completely enter into strontium ferrite lattice without changing the ferrite appearance; its grain size is approximately 40-80 nm, its length is 100 nm; the magnetoplumbite structure is proved through testing a concertina form of the crystal grain; the maximum coercivity is 5986 Oe at x=0.2; La-doped films possess a wider microwave absorption frequency range with better gross loss angle tangent (tan δ>0.1), from 9 to 10.5 GHz at x=0.2, where the maximum value of tan δ reaches 0.2709. The La-doped films reach smaller nanometer size, better magnetic properties and microwave absorption properties with the doping of lanthanum.     

Four-fold magnetic anisotropy in a Co film on MgO(0 0 1)

The development of devices based on magnetic tunnel junctions has raised new interests on the structural and magnetic properties of the interface Co/MgO. In this context, we have grown ultrathin Co films (≤30 Å) by molecular-beam epitaxy on MgO(0 0 1) substrates kept at different temperatures (T_S). Their structural and magnetic properties were correlated and discussed in the context of distinct magnetic anisotropies for Co phases reported in the literature. The sample characterization has been done by reflection high energy electron diffraction, magneto-optical Kerr effect and ferromagnetic resonance. The main focus of the work is on a sample deposited at T_S=25 °C, as its particular way of growth has enabled a bct Co structure to settle on the substrate, where it is not normally obtained without specific seed layers. This sample presented the best crystallinity, softer magnetic properties and a four-fold in-plane magnetic anisotropy with Co〈1 1 0〉 easy directions. Concerning the samples prepared at T_S=200 and 500° C, they show fcc and polycrystalline structures, respectively and more intricate magnetic anisotropy patterns.