Comparative study of structural and magnetic properties of NiZnCu ferrite powders prepared via chemical coprecipitation method with different coprecipitators

We prepared NiZnCu ferrite powders with nominal composition Ni_0.4−xZn_0.6Cu_xFe₂O₄ (x=0-0.2) via chemical coprecipitation method with NaOH and Na₂CO₃ as coprecipitators. The structural and magnetic properties of these compounds were studied and compared. It is found that all the specimens exhibit single-phase structure after annealing. The saturation magnetization of specimens with NaOH as coprecipitator is lower than that with Na₂CO₃ as coprecipitator. It is also found that the growth of grains is hindered for specimens using Na₂CO₃ as coprecipitator.     

Tape casting of cobalt ferrite from nonaqueous slurry

This paper describes the fabrication of CoFe₂O₄ thick films using the tape casting method from nonaqueous slurry. CoFe₂O₄ particles with average size of ∼800 nm were prepared by the solid-state reaction method. Sediment volumes and viscosity were tested to study the effects of dispersant in reducing aggregations in slurry. Slurry with 0.25 wt% dispersant amounts and 41.3 wt% solid content showed the optimal stability and rheological properties. A tape velocity of 8 cm/s was used in this study considering the non-Newtonian flow behavior at low shear rate. CoFe₂O₄ ceramic films sintered at 1150 °C for 2 h have dense structure (relative density of 94%) and exhibited ferromagnetic properties with in-plane saturation magnetization of ∼324 emu/cm³.     

Microstructure and magnetic properties of low-temperature sintered CoTi-substituted barium ferrite for LTCC application

In this article, the influences of the BaCu(B₂O₅) (BCB) additive on sintering behavior, structure and magnetic properties of iron deficient M-type barium ferrite Ba(CoTi)_xFe_11.8−2xO₁₉ (BaM) have been investigated. It is found that the maximum sintered densities of BaM change from 86% to 94% as the BCB content varies from 1 to 4 wt%. Single-phase BaM can be detected by the XRD analysis in the sample with 3 wt% BCB sintered at 900 °C, and the microstructure is hexagonal platelets with few intragranular pores. This is attributed to the formation of the BCB liquid phase. Meanwhile, the experimental results illuminate that the CoTi ions prefer to occupy the 4f2 and 2b sites and the magnetic properties depend on the amount of CoTi-substitution. In addition, the chemical compatibility between BaM and silver paste is also investigated; it can be seen that BaM is co-fired well with the silver paste and no other second phase is observed. Especially, the 3 wt% BCB-added Ba(CoTi)_0.9Fe₁₁O₁₉ sintered at 900 °C has good properties with the sintered density of 4.9 g/cm³, saturation magnetization of 49.7 emu/g and coercivity of 656.6 Oe. These results indicate that it is cost effective in the production of Low Temperature Co-fired Ceramics (LTCC) multilayer devices.     

Perpendicularly oriented barium ferrite thin films with low microwave loss,prepared by pulsed laser deposition

Barium ferrite(Ba M) thin films are deposited on platinum coated silicon wafers by pulsed laser deposition(PLD).The effects of deposition substrate temperature on the microstructure,magnetic and microwave properties of Ba M thin films are investigated in detail.It is found that microstructure,magnetic and microwave properties of Ba M thin film are very sensitive to deposition substrate temperature,and excellent Ba M thin film is obtained when deposition temperature is 910℃ and oxygen pressure is 300 m Torr(1 Torr = 1.3332×10~2Pa).X-ray diffraction patterns and atomic force microscopy images show that the best thin film has perpendicular orientation and hexagonal morphology,and the crystallographic alignment degree can be calculated to be 0.94.Hysteresis loops reveal that the squareness ratio(M_r/M_s) is as high as 0.93,the saturated magnetization is 4004 Gs(1 Gs = 10~4T),and the anisotropy field is 16.5 kOe(1 Oe = 79.5775 A·m~(-1)).Ferromagnetic resonance measurements reveal that the gyromagnetic ratio is 2.8 GHz/kOe,and the ferromagnetic resonance linewith is108 Oe at 50 GHz,which means that this thin film has low microwave loss.These properties make the Ba M thin films have potential applications in microwave devices.     

Room temperature single-step electrosynthesized copper ferrite thin films and study of their magnetic properties

A single-step electrosynthesis of copper ferrite thin films from aqueous bath (which avoids anodization step for an incorporation of oxygen species into deposit) has been carried out at room temperature. Observed tetrahedral structured nanocrystalline copper ferrite thin films showed smooth, uniform and compact surface morphology. After annealing, increase in dielectric constant and reduced dielectric loss were observed. The saturation magnetization for annealed films was 292 emu/cm³ comparable to that of other reported ferrites.     

Dielectric,electrical transport and magnetic properties of Er3+substituted nanocrystalline cobalt ferrite

Erbium substituted cobalt ferrite (CoFe_2−xEr_xO₄; x=0.0–0.2, referred to CFEO) materials were synthesized by sol-gel auto-combustion method. The effect of erbium (Er³⁺) substitution on the crystal structure, dielectric, electrical transport and magnetic properties of cobalt ferrite is evaluated. CoFe_2−xEr_xO₄ ceramics exhibit the spinel cubic structure without any impurity phase for x≤0.10 whereas formation of the ErFeO₃ orthoferrite secondary phase was observed for x≥0.15. All the CFEO samples demonstrate the typical hysteresis (M–H) behavior with a decrease in magnetization as a function of Er content due to weak superexchange interaction. The frequency (f) dependent dielectric constant (ε′) revealed the usual dielectric dispersion. The ε′–f dispersion (f=20 Hz to 1 MHz) fits to the modified Debye's function with more than one ion contributing to the relaxation. The relaxation time and spread factor derived are ∼10⁻⁴ s and ∼0.61(±0.04), respectively. Electrical and dielectric studies indicate that ε′ increases and the dc electrical resistivity decreases as a function of Er content (x≤0.15). Complex impedance analyses confirm only the grain interior contribution to the conduction process. Temperature dependent electrical transport and room temperature ac conductivity (σ_ac) analyses indicate the semiconducting nature and small polaron hopping.     

The structural and magnetic powders prepared by properties of barium ferrite the sol-gel method

In this paper,M-type hexagonal barium ferrite powders are synthesized using the sol-gel method.A dried precursor heated in air is analyzed in the temperature range from 50 to 1200 C using thermo-gravimetric analysis and differential scanning calorimetry.The effects of the additives and the cacinating temperature on the magnetic properties are investigated,and the results show that single-phase barium ferrite powders can be formed.After heat-treating at 950 C for 4h with 3 wt% additive,the coercivity and saturation magnetization are found to be 440 Oe and 57.9 emu/g,respectively.     

稀土掺杂对钴铁氧体电子结构和磁性能影响的理论研究

尖晶石型铁氧体是十分重要的磁性材料之一, 具有独特的物理性质、化学特性、磁学特性和电子特性. 其中尖晶石型钴铁氧体具有较好的电磁性质而被广泛应用. 本文基于密度泛函理论(DFT) 的第一性原理平面波赝势法, 结合广义梯度近似(GGA+U), 研究了CoRE_0.125Fe_1.875O₄ (RE = Nd, Eu, Gd)体系的电子结构和磁性能. 结果表明随着稀土元素从Nd到Gd掺杂体系晶胞的晶格常数呈递减趋势. 磁性能依赖于稀土离子(RE³⁺)4f轨道未配对的电子数, 掺杂Eu和Gd能够提高钴铁氧体体系的磁矩, 主要因为它们3+价态离子具有较多未配对的4f电子, 因而对磁性能的影响较大. 然而Nd 的掺杂对体系磁性能的影响很小, 这是由于它的离子半径较大, 导致晶格发生畸变.     

Synthesis, characterization and magnetic properties on nanocrystalline BaFe12O19 ferrite

Single phase BaM (BaFe₁₂O₁₉) ferrites are prepared by using sol–gel method. The preparing conditions of samples are investigated in detail, such as acid/nitrate ratio, the value of pH and annealing temperature. The best conditions on preparing BaFe₁₂O₁₉, which can be obtained on a Fe/Ba ratio of 12, the citric acid contents R = 3, the starting pH of solution is 9, and annealing temperature 950 °C. The thermal decomposition behavior of the dried gel was examined by TG–DSC, the structure and properties of powders were measured respectively by XRD techniques. The magnetic properties of barium ferrites are emphatically researched about the changing crystallite size and annealing temperature by the vibrating sample magnetometer (VSM). Magnetic measurement shows that the barium ferrite samples annealed at 1000 °C has the maximal coercive field of 5691.91 Oe corresponding to the maximal remnant magnetization of 35.60 emu/g and the sample synthesized at 1000 °C has the maximal saturation magnetization of 60.75 emu/g.     

Enhancement of magnetic and dielectric properties of low temperature sintered NiCuZn ferrite by Bi2O3-CuO additives

With a series of 1.0 wt%Bi$_{2}$O$_{3}$-$x$ wt% CuO ($x =0.0$, 0.2, 0.4, 0.6, and 0.8) serving as sintering additives, Ni$_{0.23}$Cu$_{0.32}$Zn$_{0.45}$Fe$_{2}$O$_{4}$ ferrites are successfully synthesized at a low temperature (900 $^\circ$C) by using the solid state reaction method. The effects of the additives on the phase formation, magnetic and dielectric properties as well as the structural and gyromagnetic properties are investigated. The x-ray diffraction (XRD) results indicate that the added Bi$_{2}$O$_{3}$-CuO can lower the synthesis temperature significantly without the appearing of the second phase. The scanning electron microscope (SEM) images confirm that Bi$_{2}$O$_{3}$ is an important factor that determines the sintering behaviors, while CuO affects the grain size and densification. With CuO content $x=0.4$ or 0.6, the sample shows high saturation magnetization, low coercivity, high real part of magnetic permeability, dielectric permittivity, and small ferromagnetic resonance linewidth ($\Delta H$). The NiCuZn ferrites are a promising new generation of high-performance microwave devices, such as phase shifters and isolators.     

Structure and magnetic properties of Ni0.5Zn0.5Mn0.5-xMoxFe1.5O4 ferrites prepared by sol-gel auto-combustion method

A series of Mo doped Ni-Mn-Zn ferrites compounds with the formula Ni_0.5Zn_0.5Mn_0.5-xMo_xFe_1.5O₄ (x = 0, 0.025, 0.05, 0.075 and 0.1) were first synthesized by sol-gel auto-combustion method. The X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy (FTIR), and vibrating sample magnetometer (VSM) analysis were carried out to characterize the microstructural and magnetic properties of ferrites. Rietveld refinement of X-ray diffraction data confirmed the formation of cubic spinel structure and the emergence of FeMoO₄ phase with the substitution of Mo⁶⁺ contents. The grain size increased remarkably due to the formation of the liquid phase. The saturation magnetization (M_s) increased while the coercivity (H_c) decreased from 67.3 to 12.1 Oe due to the decrease of magneto-crystalline anisotropy constant. The initial permeability (μ_i) increased significantly from 34 (x = 0) to 114 (x = 0.075) and later decreased for x = 0.1. In our experiment, Ni_0.5Zn_0.5Mn_0.425Mo_0.075Fe_1.5O₄ ferrite presented the best microstructure and soft magnetic properties.     

Effect of doping MnO2 on magnetic properties for M-type barium ferrite

The crystalline structure and magnetic properties of M-type barium ferrite doped with small amounts of MnO₂ (0, 0.25, 0.5, 0.75, 1.0, 1.5, and 2.0 wt%, respectively) have been investigated by means of XRD, SEM and VSM. The results show that the crystalline structures of barium ferrite are still M-type hexagonal structure and Mn ions are distributed homogeneously in both the grains and the grain boundaries. The saturation magnetization and magnetocrystalline anisotropy constants both reach the highest values when x=0.75 wt%. The displacement of Fe ions from 4f₁ to 2b site is mainly responsible for the appearance of the maximum values.     

Effect of deposition temperature on orientation and electrical properties of (K0.5Na0.5)NbO3 thin films by pulsed laser deposition

Lead-free ferroelectric K_0.5Na_0.5NbO₃ (KNN) thin films have been prepared on Pt/TiO₂/SiO₂/Si substrates by pulsed laser deposition process. The structures, crystal orientations and electrical properties of thin films have been investigated as a function of deposition temperature from 680 °C to 760 °C. It is found that the deposition temperature plays an important role in the structures, crystal orientations and electrical properties of thin films. The crystallization of thin films improves with increasing deposition temperature. The thin film deposited at 760 °C exhibits strong (0 0 1) preferential orientation, large dielectric constant of 930 and the remnant polarization of 8.54 μC/cm².     

Crystal orientation dependence of the in-plane dielectric properties for Ba(Sn0.15Ti0.85)O3 thin films

Barium tin titanate Ba(Sn_0.15Ti_0.85)O₃ (BTS) thin films with (1 0 0), (1 1 0) and (1 1 1) orientation were grown on (1 0 0), (1 1 0) and (1 1 1) LaAlO₃ (LAO) single-crystal substrates through sol–gel process, respectively. The in-plane dielectric properties of the films were measured on interdigital capacitor (IDC). Films with the (1 1 1) orientation had larger relative dielectric constant and larger tunability against the dc bias electric field than (1 0 0)- and (1 1 0)-oriented films. This difference in dielectric properties in these three kinds of oriented BTS films may be attributed due to change in the direction and magnitude of electric polarization in orientation engineered BTS films. This work clearly reveals the dielectric properties of BTS films exhibited a strong sensitivity to crystal orientation.     

Development of nanocrystalline Mn-Zn ferrites for high frequency transformer applications

Microwave-Hydrothermal (M-H) method has been successfully used for the synthesis of nanocrystalline Mn-Zn ferrites which are used for high-frequency applications. As synthesized powders were characterized using X-ray diffraction (XRD) and transmission electron microscopy (TEM). The nanopowders were annealed at 600 °C/20 min using the microwave sintering method. The frequency dependence of dielectric constant (ε′) was measured in the range of 10 Hz-1.3 GHz and initial permeability (μ_i) was measured in the range of 10 Hz-1 MHz. The total power loss (P_t) was measured on the annealed samples at 100 kHz and 200 mT condition. Conductor-embedded-ferrite transformers were fabricated and output power (P_o), efficiency (η) and temperature rise (ΔT) were measured at sinusoidal voltage of 25 V at 1 MHz. The transformer efficiency (η) was found to be high and surface rise of temperature (ΔT) is very low.     

Effects of impurity Na ions on the structural and magnetic properties of Ni-Zn-Cu ferrite powders: An improvement for chemical coprecipitation method

Ni-Zn-Cu ferrite powders with nominal composition Ni_0.4−xZn_0.6Cu_xFe₂O₄ (x=0.00-0.20) were prepared via chemical coprecipitation method. X-ray diffractometer, vibrating sample magnetometer, scanning electron microscopy, inductively coupled plasma-atomic emission spectrometry and energy dispersive spectrum were used to study the effects of impurity Na⁺ ions on the structural and magnetic properties. As a result, it was found that the impurity Na⁺ ions affect the crystalline structures and magnetic properties greatly. Moreover, the heterogeneous distribution of impurity Na⁺ ions and the formation of Na compounds retard the phase formation and the grain growth of specimens. Our study also reveals that for the chemical coprecipitation method, a second washing process introduced after drying can eliminate the impurity Na⁺ ions effectually and thus helps in the formation of single-phase structure and the growth of grains, which is very important for the improvement of magnetic properties and the preparation of ferrites via chemical coprecipitation method.     

Synthesis and characterisation of Gd-doped BaTiO3 thin films prepared by laser ablation for optoelectronic applications

The results of gadolinium (Gd)-doped barium titanate (BaTiO₃) thin films prepared by laser ablation on glass and silicon substrates are reported. Rutherford backscattering (RBS) analyses carried out on glass samples indicated the substitution of barium (Ba) by gadolinium (Gd) after annealing, leading to a film with composition Ba_0.76TiGd_0.01O_2.5. There is a reduction in the thickness from 2.21 to 2.02 microns for as-deposited and annealed films. The films on silicon showed a higher degree of crystallinity compared to that of glass substrates due to increased annealing temperature. The average grain size calculated using the X-ray diffraction (XRD) pattern from silicon substrates was 30 nm. The film has a tetragonal structure with a “c/a” ratio of 1.03 signifying that the incorporation of Gd in BaTiO₃ led to the elongation of the c-axis. The percentage transmittance reduced from 80 to 50% due to annealing and this is probably due to structural changes in the film. Swanepoel envelope method employed on the interference fringes of the transmittance pattern led to the determination of the variation of the refractive index with wavelength. Sellmier single oscillator model was applied to determine the optical constants of the films on glass substrates. Bandgap analyses carried out showed the reduction in bandgap with annealing and also the possibility that Gd incorporation has modified the film chemistry leading to the existence of direct (4.35 eV) and indirect (3.88 eV) allowed transitions in the annealed films. Dielectric property measurement carried out under ambient conditions gave a relaxation time τ of 1.6×10⁻⁴ s and conduction by small polaron with the onset of polaron conduction set at about 7 kHz. It is conjectured that these properties, especially the high refractive index and the high bandgaps, can make Gd-doped BaTiO₃ a good candidate for optoelectronic applications.     

Critical behaviours and magnetic properties of three-dimensional bond and anisotropy dilution Blume——Capel model in the presence of an applied field

This paper studies the critical behaviours and magnetic properties of three-dimensional bond and anisotropy dilution Blume--Capel model (BCM) in the presence of an applied field within the effective field theory. The trajectory of tricritical point, reentrant transitions and degenerate patterns of anisotropy are obtained both for the bond and the anisotropy dilutions. The global phase diagrams demonstrate unusually reentrant phenomena. The temperature dependences of magnetization curves undergo remarkable spin glass behaviour at low temperatures, and transform from ferromagnetism to paramagnetism at high temperature in applied fields. Temperature dependence of magnetic susceptibility curve is in qualitative agreement with experimental result.     

Analysis of general multipolar images on dielectric layers for the calculation of DEP force

An axisymmetric field problem of a sphere and a multi-layered planer dielectric body is investigated based on the multipolar expansion method. First, the multipolar potential, produced by the sphere and expressed in the spherical coordinate system, is re-written in the cylindrical coordinate system as an integral of Bessel function. Then the field problem is solved with the boundary conditions at the planer interface of the dielectrics, and the obtained potential is written back to spherical harmonics, which can be regarded as “image multipoles” inside the dielectric body. The “images” influences back the “multipoles” on the sphere, and the field can be determined by solving these relations in self-consistent manner. DEP force exerted on the particle is calculated as the multipolar interaction, as well as the capacitance for the case involving a conducting sphere and a conducting plane.     

Heat generation ability in AC magnetic field and their computer simulation for Ti tube filled with ferrite powder

The heat generation ability of needle-type materials was studied for the application of thermal coagulation therapy in an AC magnetic field. Although the Ti tube without the MgFe₂O₄ powder or Ti rod showed poor heat generation abilities in an AC magnetic field, the temperature was significantly increased by the presence of ferrite powder in the Ti tube. We confirmed using a computer simulation that the eddy loss of the Ti tube was increased by the enhanced magnetic flux density due to the ferrite powder in the Ti tube. The heat generation of the ferrite filled Ti tube was increased by utilization of the quenched MgFe₂O₄ powder from elevated temperature. The relative magnetic permeability of the quenched ferrite was enhanced with the decrease in the inverse ratio of the cubic spinel structure. The heat generation ability was increased with the increase in the relative magnetic permeability of the Ti tube with ferrite powder. The calculated joule loss based on the experimental results showed an agreement with those using the computer simulation.