Structural transformations of Fe81B13Si4C2 amorphous alloy induced by heating

Thermal stability and crystallization of the Fe₈₁B₁₂Si₄C₂ alloy were investigated in the temperature range 25-700 °C by the XRD and Mössbauer analysis. It was shown that on heating the as-prepared amorphous Fe₈₁B₁₂Si₄C₂ alloy undergoes thermal stabilization through a series of structural transformations involving the process of stress-relieving (temperature range 200-400 °C), followed by a loss of ferromagnetic properties (Curie temperature at 420 °C) and finally crystallization (temperature range 450-530 °C). The process of crystallization begins by formation of two crystal phases: Fe₃B and subsequently Fe₂B, as well as a solid solution α-Fe(Si). With increase in annealing temperature, the completely crystallized alloy involved only two phases, Fe₂B and solid solution α-Fe(Si).XRD patterns established a difference in phase composition and size of the formed crystallites during crystallization depending on the side (fishy or shiny) of the ribbon. The first nuclei of the phase α-Fe₃Si were found on the shiny side by XRD after heat treatment even at 200 °C but the same phase on the fishy side of ribbon was noticed after heat treatment at 450 °C. The largest difference between the contact and free surface was found for the Fe₂B phase crystallized by heating at 700 °C, showing the largest size of crystallites of about 130 nm at 700 °C on the free (shiny) surface.     

Structure,magnetic properties and magnetostriction of Fe81Ga19 thin films

The structure, magnetic properties and magnetostriction of Fe₈₁Ga₁₉ thin films have been investigated by using X-ray diffraction analysis, scanning electron microscope (SEM), vibrating sample magnetometer and capacitive cantilever method. It was found that the grain size of as-deposited Fe₈₁Ga₁₉ thin films is 50–60 nm and the grain size increases with increase in the annealing temperature. The remanence ratio (M_r/M_s) of the thin films slowly decreases with increase in the annealing temperature. However, the coercivity of the thin films goes the opposite way with increase in the annealing temperature. A preferential orientation of the Fe₈₁Ga₁₉ thin film fabricated under an applied magnetic field exists along 〈1 0 0〉 direction due to the function of magnetic field during sputtering. An in-plane-induced anisotropy of the thin film is well formed by the applied magnetic field during the sputtering and the formation of in-plane-induced anisotropy results in 90° rotations of the magnetic domains during magnetization and in the increase of magnetostriction for the thin film.     

Effect of heat treatment on structure, magnetization and magnetostriction of Fe81Ga19 melt-spun ribbons

Structure, magnetization and magnetostriction of melt-spun Fe₈₁Ga₁₉ ribbons were investigated both before and after heat treatment. The matrix of melt-spun Fe₈₁Ga₁₉ ribbons kept a body-centered-cubic (bcc) structure (A2) at room temperature. [1 0 0] preferred orientation was formed during melt-spinning process and became stronger with the increase of the ribbon thickness. For the ribbons with a thickness of 110 μm, maximum saturation magnetostrictive strain of −189 ppm along ribbon length was obtained in the samples heat treated at 800 °C for 3 h and then quenched into water. This value was about 16% larger than that of melt-spun ones, which could be contributed to the single disordered A2 structure and the enhancement of [1 0 0]-oriented texture. However, when the ribbon samples were cooled at 2 and 0.5 °C/min after heat treatment at 800 °C for 3 h, a minor quantity of ordered D0₃ and L1₂ phase was found to precipitate in the A2 matrix, respectively, which resulted in the reduction of both magnetization and magnetostrictive strain.     

Preparation and magnetic properties of BaFe12O19/Ni0.8Zn0.2Fe2O4 nanocomposite ferrite

Nanocomposite of hard (BaFe₁₂O₁₉)/soft ferrite (Ni_0.8Zn_0.2Fe₂O₄) have been prepared by the sol–gel process. The nanocomposite ferrite are formed when the calcining temperature is above 800 °C. It is found that the magnetic properties strongly depend on the presintering treatment and calcining temperature. The “bee waist” type hysteresis loops for samples disappear when the presintering temperature is 400 °C and the calcination temperature reaches 1100 °C owing to the exchange-coupling interaction. The remanence of BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite with the mass ratio of 5:1 is higher than a single phase ferrite. The specific saturation magnetization, remanence magnetization and coercivity are 63 emu/g, 36 emu/g and 2750 G, respectively. The exchange-coupling interaction in the BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite is discussed.     

Evidence of existence of metastable SrFe12O19 nanoparticles

The existence of metastable hexaferrite is reported. Synthesis of strontium hexaferrite, SrFe₁₂O₁₉, at 400 °C was realized under controlled oxygen atmosphere. Such technique allows obtaining of SrFe₁₂O₁₉ at lower temperatures than those by traditional methods (above 800 °C). Phase transformation occurred during a measurement of magnetization vs. temperature (heating up to 625 °C). The heat treatment induces a change from SrFe₁₂O₁₉ to γ-Fe₂O₃ (as the main phase), and SrFeO_2.74 to Sr₂Fe₂O₅. Together with these phase transformations, an increment in the amount of SrCO₃ is detected. Magnetic study of the samples, before and after the heating, supports the structural analysis conclusions.     

Effects of annealing temperature on structure and magnetic properties of CoAl0.2Fe1.8O4/SiO2 nanocomposites

CoAl_0.2Fe_1.8O₄/SiO₂ nanocomposites were prepared by sol–gel method. The effects of annealing temperature on the structure and magnetic properties of the samples were studied by X-ray diffraction, transmission electron microscopy, vibrating sample magnetometer and Mössbauer spectroscopy. The results show that the CoAl_0.2Fe_1.8O₄ in the samples exhibits a spinel structure after being annealed. As annealing temperature increases from 800 to 1200 °C, the average grain size of CoAl_0.2Fe_1.8O₄ in the nanocomposites increases from 5 to 41 nm while the lattice constant decreases from 0.8397 to 0.8391 nm, the saturation magnetization increases from 21.96 to 41.53 emu/g. Coercivity reaches a maximum of 1082 Oe for the sample annealed at 1100 °C, and thereafter decreases with further increasing annealing temperature. Mössbauer spectra show that the isomer shift decreases, hyperfine field increases and the samples transfer from mixed state of superparamagnetic and magnetic order to the completely magnetic order with annealing temperature increasing from 800 to 1200 °C.     

Synthesis and magnetic properties of hard magnetic (CoFe2O4)-soft magnetic (Fe3O4) nano-composite ceramics by SPS technology

CoFe₂O₄/Fe₃O₄ nano-composite ceramics were synthesized by Spark Plasma Sintering. The X-ray diffraction patterns show that all samples are composed of CoFe₂O₄ and Fe₃O₄ phases when the sintering temperature is below 900 °C. It is found that the magnetic properties strongly depend on the sintering temperature. The two-step hysteresis loops for samples sintered below 500 °C are observed, but when sintering temperature reaches 500 °C, the step disappears, which indicates that the CoFe₂O₄ and Fe₃O₄ are well exchange coupled. As the sintering temperature increases from 500 to 800 °C, the results of X-ray diffractometer indicate the constriction of crystalline regions due to the ion diffusion at the interfaces of CoFe₂O₄/Fe₃O₄ phases, which have great impact on the magnetic properties.     

Improvement of the magnetic properties of Nd9.5Fe81Zr3B6.5 nanocomposite magnets by semi-melt spinning

Nd_9.5Fe₈₁Zr₃B_6.5 ribbons are prepared by single roller melt-spinning technique at 1150 °C which is in the solid and liquid coexistence zone. The phase evolution and magnetic properties were studied by X-ray diffraction, differential scanning calorimetry, transmission electron microscopy observations, and magnetization measurements. The experimental results show that in comparison to the ribbons quenching at higher temperature, the thickness of ribbons prepared at 1150 °C are insensitive to the wheel speed and an uniform nanoscale structure with fine grains can be obtained directly from the semi-melt and the exchange coupling interaction between the grains was enhanced for the nanocomposite permanent alloy which can contributed to excellent magnetic properties.     

Simple recipe to synthesize single-domain BaFe12O19 with high saturation magnetization

We report a new synthesis route for preparation of single-domain barium hexaferrite (BaFe₁₂O₁₉) particles with high saturation magnetization. Nitric acid, known as a good oxidizer, is used as a mixing medium during the synthesis. It is shown that formation of BaFe₁₂O₁₉ phase starts at 800 °C, which is considerably lower than the typical ceramic process and develops with increasing temperature. Both magnetization measurements and scanning electron microscope micrographs reveal that the particles are single domain up to 1000 °C at which the highest coercive field of 3.6 kOe was obtained. The best saturation magnetization of ≈60 emu/g at 1.5 T was achieved by sintering for 2 h at 1200 °C. Annealing at temperatures higher than 1000 °C increased the saturation magnetization, on the other hand, decreased the coercive field which was due to the formation of multi-domain particles with larger grain sizes. It is shown that the best sintering to obtain fine particles of BaFe₁₂O₁₉ occurs at temperatures 900-1000 °C. Finally, magnetic interactions between the hard BaFe₁₂O₁₉ phase and impurity phases were investigated using the Stoner-Wohlfarth model.     

Annealing effects on structural, optical and electrical properties of e-beam evaporated CuIn0.5Ga0.5Te2 thin films

CuIn_0.5Ga_0.5Te₂ (CIGT) thin films have been prepared by e-beam evaporation from a single crystal powder synthesized by direct reaction of constituent elements in a stoichiometric proportion. Post-depositional annealing has been carried out at 300 and 350 °C. The compositions of the films were determined by energy dispersive X-ray analysis (EDXA) and it was found that there was a remarkable fluctuation in atomic percentage of the constituent elements following to the post-depositional annealing. X-ray diffraction analysis (XRD) has shown that as-grown films were amorphous in nature and turned into polycrystalline structure following to the annealing at 300 °C. The main peaks of CuIn_0.5Ga_0.5Te₂ and some minor peaks belonged to a binary phase Cu₂Te appeared after annealing at 300 °C, whereas for the films annealed at 350 °C single phase of the CuIn_0.5Ga_0.5Te₂ chalcopyrite structure was observed with the preferred orientation along the (1 1 2) plane. The effect of annealing on and near surface regions has been studied using X-ray photoelectron spectroscopy (XPS). The results indicated that there was a considerable variation in surface composition following to the annealing process. The transmission and reflection measurements have been carried out in the wavelength range of 200-1100 nm. The absorption coefficients of the films were found to be in the order of 10⁴ cm⁻¹ and optical band gaps were determined as 1.39, 1.43 and 1.47 eV for as-grown and films annealed at 300 and 350 °C, respectively. The temperature dependent conductivity and photoconductivity measurements have been performed in the temperature range of −73 to 157 °C and the room temperature resistivities were found to be around 3.4 × 10⁷ and 9.6 × 10⁶ (Ω cm) for the as-grown and annealed films at 350 °C, respectively.     

Thermal stability, oxygen non-stoichiometry and transport properties of LaNi0.6Fe0.4O3

Thermal stability, oxygen non-stoichiometry and electrical conductivity of LaNi_0.6Fe_0.4O_3−δ were investigated in the temperature region of 20-1000 °C in Ar/O₂ gas flows at oxygen partial pressures between 0.5 and 21,000 Pa. Diffusion mobility was measured in Ar/O₂ gas flow at pO₂ = 18 Pa. Crystal structure of this compound was found to be stable at the mentioned experimental conditions. LaNi_0.6Fe_0.4O_3−δ is a p-type semiconductor with metallic type conductivity above 150 °C at the investigated pO₂ range. Two different (fast and slow) oxygen exchange areas on the temperature-pO₂ diagram were established, which are due to two different oxygen anion positions in the double B-site mixed perovskite structure. Oxygen non-stoichiometry in the fast oxygen exchange region reaches about 0.005 of oxygen atomic index. Chemical diffusion and oxygen surface exchange coefficients do not vary at 600-800 °C, but show visible increase above 800-850 °C.     

Immiscibility in the NiFe2O4-NiCr2O4 spinel binary

The solid solution behavior of the Ni(Fe_1−nCr_n)₂O₄ spinel binary is investigated in the temperature range 400-1200 °C. Non-ideal solution behavior, as exhibited by non-linear changes in lattice parameter with changes in n, is observed in a series of single-phase solids air-cooled from 1200 °C. Air-annealing for 1 year at 600 °C resulted in partial phase separation in a spinel binary having n=0.5. Spinel crystals grown from NiO, Fe₂O₃ and Cr₂O₃ reactants, mixed to give NiCrFeO₄, by Ostwald ripening in a molten salt solvent, exhibited single-phase stability down to about 750 °C (the estimated consolute solution temperature, T_cs). A solvus exists below T_cs. The solvus becomes increasingly asymmetric at lower temperatures and extrapolates to n values of 0.2 and 0.7 at 300 °C. The extrapolated solvus is shown to be consistent with that predicted using a primitive regular solution model in which free energies of mixing are determined entirely from changes in configurational entropy at room temperature.     

Characteristics of spherical-shaped Li4Ti5O12 anode powders prepared by spray pyrolysis

Spherical-shaped Li₄Ti₅O₁₂ anode powders with a mean size of 1.5 μm were prepared by spray pyrolysis. The precursor powders obtained by spray pyrolysis had no peaks of crystal structure of Li₄Ti₅O₁₂. The powders post-treated at temperatures of 800 and 900 °C had the single phase of spinel Li₄Ti₅O₁₂. The powders post-treated at a temperature of 1000 °C had main peaks of the Li₄Ti₅O₁₂ phase and small impurity peaks of Li₂Ti₃O₇. The spherical shape of the precursor powders was maintained after post-treatment at temperatures below 800 °C. The Brunauer-Emmett-Teller (BET) surface areas of the Li₄Ti₅O₁₂ anode powders post-treated at temperatures of 700, 800 and 900 °C were 4.9, 1.6 and 1.5 m²/g, respectively. The initial discharge capacities of Li₄Ti₅O₁₂ powders were changed from 108 to 175 mAh/g when the post-treatment temperatures were changed from 700 to 1000 °C. The maximum initial discharge capacity of the Li₄Ti₅O₁₂ powders was obtained at a post-treatment temperature of 800 °C, which had good cycle properties below current densities of 0.7 C.     

Properties of Fe–Ga based powders prepared by mechanical alloying

Alloys of Fe–Ga with starting compositions of 17, 19, 21, 23, and 25 at% Ga and Fe₈₁Ga₁₇Z₂ (Z=Si, Sn) have been prepared by mechanical alloying. Samples were milled in a SPEX Model 8000 mill with a ball to sample weight ratio of about 4:1. Phase formation as a function of milling time has been investigated for the 19 at% Ga sample and suggests that milling times of 12 h produce fully alloyed samples. Alloys have been studied by electron microprobe, X-ray diffraction, vibrating sample magnetometery and ⁵⁷Fe Mössbauer effect spectroscopy. Fully milled powders have measured compositions of Fe_100−xGa_x with x=15.7, 17.0, 19.0, 22.4, and 24.0 and Fe_83.1Ga_15.2Z_1.7 (for both Z=Si and Sn). X-ray diffraction showed the presence of a disordered bcc phase with no indication of an ordered D0₃ phase. However, the latter is difficult to observe with X-ray diffraction because of the low intensity of the fcc superlattice peaks. A bimodal Fe hyperfine field distribution as obtained from Mössbauer effect spectra indicated the presence of two discrete Fe environments. The results suggested a lower degree of Ga clustering than has been previously observed in Fe–Ga alloys, of similar composition, prepared by melt spinning. The microstructure is similar to that of Fe–Ga thin films prepared by combinatorial sputtering. Some samples have also been studied after annealing at 800 °C for 8 h. No changes were observed in X-ray diffraction patterns after annealing. However, Mössbauer effect studies show the formation of D0₃ and L1₂ order in annealed samples analogous to the phases observed in melt spun ribbons of similar composition.     

Phase transition in multiferroic YMnO3 and its solid solution YMn(0.93)Fe(0.07)O3

Ceramics of YMnO₃ and its Fe substituted YMn_(0.93)Fe_(0.07)O₃ solid solution were synthesized by solid state reaction of the oxides at 1200 °C. Hexagonal phase was identified in both cases by X-ray powder diffraction. Rietveld refinement of cell parameters showed an increase of the parameter values for the solid solution. Dielectric permittivity measurements versus temperature showed a phase transition at 655 °C for yttrium manganite, however, for the solid solution no phase transition was detected on heating up to 700 °C. Dielectric loss measurements showed higher slope changes and better defined local maxima for the solid solution than for the pure phase.     

Morphology and magnetic properties of Co0.8Fe2.2O4 films prepared by the chemical solution deposition

Co_0.8Fe_2.2O₄ ferrite thin films have been prepared on Si(0 0 1) substrates by the chemical solution deposition. Structural characteristics indicate all films are single phase with spinel structure and the space group and the mean grain size increases from 8 to 30 nm with the increase of annealing temperature. The magnetic properties of Co_0.8Fe_2.2O₄ thin films are highly dependent on annealing temperature. The sample annealed at 800 °C possesses high saturation magnetization, moderate coercivity and squareness ratio, making it a promising application candidate in high-density record and magneto-optical materials.     

Synthesis and characterization of lithium ferrite by oxalate precursor route

Nanocrystalline lithium ferrite (LiFe₅O₈) powders have been synthesized by oxalate precursor route. The effects of Fe³⁺/Li⁺ mole ratio, and annealing temperature on the formation, crystalline size, morphology and magnetic properties were systematically studied. The Fe³⁺/Li⁺ mole ratio was controlled from 5 to 3.33 while the annealing temperature was controlled from 600 to 1100 °C. The resultant powders were investigated by differential thermal analyzer (DTA), X-ray diffractometer (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). DTA results showed that LiFe₅O₈ phase started to form at around 520 °C. XRD indicated that LiFe₅O₈ phase always contained α-Fe₂O₃ impurity and the hematite phase formation increased by increasing the annealing temperature ?850 °C for different Fe³⁺/Li⁺ mole ratios 5, 4.55 and 3.85. Moreover, lithium ferrite phase was formed with high conversion percentage at critical annealing temperature 750–800 °C. Single well crystalline LiFe₅O₈ phase was obtained at Fe³⁺/Li⁺ mole ratio 3.33 and annealing temperatures from 800 to 1000 °C. Maximum saturation magnetization (68.7 emu/g) was achieved for the formed lithium ferrite phase at Fe³⁺/Li⁺ mole ratio 3.33 and annealing temperature 1000 °C.     

A study of the properties and microstructure of Ni81Fe19 ultrathin films with MgO

The anisotropic magnetoresistance (AMR) of a Ta (5 nm)/MgO (3 nm)/Ni₈₁Fe₁₉ (10 nm)/MgO (2 nm)/Ta (3 nm) film with MgO-Nano Oxide Layer (NOL) increases dramatically from 1.05% to 3.24% compared with a Ta (5 nm)/Ni₈₁Fe₁₉ (10 nm)/Ta (3 nm) film without the MgO-NOL layer after annealing at 380 °C for 2 h. Although the MgO destroys the NiFe (1 1 1) texture, it enhances the specular electron scattering of the conduction electrons at the NOL interface and suppresses the interface reactions and diffusion at the Ta/NiFe and NiFe/Ta interfaces. The NiFe (1 1 1) texture was formed after the annealing, resulting in a higher AMR ratio. X-ray photoelectron spectroscope results show that Mg and Mg²⁺ were present in the MgO_x films.     

Multiferroic TbMnO3 nanoparticles

We report on the synthesis of TbMnO₃ nanoparticles by chemical co-precipitation route and their structural, chemical bonding, magnetic and dielectric properties. It is shown that the interesting multiferroic properties of this system as reflected by the concurrent occurrence of magnetic and dielectric transitions are retained in the nanoparticles (size∼40 nm). However, the nanoparticle constitution and properties are seen to depend significantly on the calcination temperature. While the nanoparticles obtained by calcination at 800 °C correspond very well with the reported properties of single phase TbMnO₃ (all the key magnetic and dielectric features near 7, 27 and 41 K, albeit with reduced dielectric constant) the nanoparticles obtained by calcination at 900 °C develop a Tb deficient skin which softens the transitions, reducing the dielectric constant further.     

Effect of nanoscale thin films of Dy2Fe14B on the magnetic hysteresis characteristics of melt-spun ribbons of Nd2Fe14B

The effectiveness of nanoscale Dy₂Fe₁₄B thin films on coercivity and energy product of melt-spun ribbons of Nd₂Fe₁₄B at high temperatures was investigated. It is hypothesized that the nanoscale Dy-thin film will act as an obstacle for the nucleation of reverse domains and also maximize the energy of domain walls and thereby improve the magnetic performance at high temperatures. Pulsed laser deposition (PLD) of amorphous Dy₂Fe₁₄B layers on Nd₂Fe₁₄B melt-spun ribbons was performed for a nominal thickness of 40 nm. The coated ribbons were then annealed in environmentally controlled quartz furnace at two different cycles (750 °C for 15 min and 900 °C for 2 h) to cause crystallization. Magnetic hysteresis tests conducted at 300 and 400 K revealed that there is small but consistent improvement in the magnetic properties of the coated ribbons annealed at 750 °C for 15 min. However, higher temperature annealing (900 °C for 2 h) drastically reduced the magnetic properties. The incomplete recrystallization of amorphous structure at 750 °C for 15 min and large grain growth and formation of non-magnetic phases at 900 °C for 2 h are believed to be responsible for not meeting the expected magnetic performance.